JP4487171B2 - 感光性樹脂組成物およびそれを用いた感光性樹脂印刷用原版 - Google Patents
感光性樹脂組成物およびそれを用いた感光性樹脂印刷用原版 Download PDFInfo
- Publication number
- JP4487171B2 JP4487171B2 JP2003295855A JP2003295855A JP4487171B2 JP 4487171 B2 JP4487171 B2 JP 4487171B2 JP 2003295855 A JP2003295855 A JP 2003295855A JP 2003295855 A JP2003295855 A JP 2003295855A JP 4487171 B2 JP4487171 B2 JP 4487171B2
- Authority
- JP
- Japan
- Prior art keywords
- latex
- photosensitive resin
- polymer
- weight
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明における(A)成分として用いられる水分散ラテックスとは重合体粒子を分散質として水中に分散したものである。また少なくとも2種類以上の水分散ラテックスより得られる疎水性重合体とは、この水分散ラテックスから水を取り除いて得られる疎水性重合体そのものであり、本発明においては2種類以上用いられることが必要である。
なお、実施例における特性値は以下の測定方法によって得られた値である。
(1)硬度:JIS−K6301に準ずるスプリング式硬さ試験(A形)法により20℃で測定した値である。
(2)反発弾性率:φ10m/m(重さ4.16g)の鋼鉄製ボールを20cm地の高さより落下させ、跳ね戻る高さ(a)を読みとり、(a/20)×100%表示とした。
(3)膨潤率:印刷版を水あるいはエタノールに20℃で1時間あるいは24時間浸漬させた後の重量増加率(%)を測定した。
(4)光散乱率:分光光度計(U−3210、日立製作所(株)製、150φ積分球付属装置付き)を用いて、感光性樹脂組成物のλ=365nmでの散乱率を測定した。
(A)成分であるブタジエンラテックス(Nipol LX111NF 不揮発分55% 日本ゼオン(株)製)22重量部、アクリロニトリル−ブタジエンラテックス(Nipol SX1503 不揮発分43% 日本ゼオン(株)製)5重量部、(B)成分である親水性重合体(PFT-3 不揮発分25% 共栄社化学(株)製)5重量部、(C)成分であるオリゴブタジエンアクリレート(ABU−2S 共栄社化学(株)製)10重量部、(D)成分である光重合開始剤0.45重量部、(E)成分である凝集防止剤0.3重量部(ノイゲンSDX−60 第一工業製薬(株)製)、架橋剤としてラウリルメタクリレート3重量部、ジメチロールトリシクロデカンジアクリレート0.9重量部、重合禁止剤としてハイドロキノンモノメチルエーテル0.03重量部、その他の添加剤としてカルボン酸系共重合体0.04重量部をトルエン15重量部とともに容器中で混合してから、調合直後と1時間後のドープの状態を観察した。次に加圧ニーダーを用いて105℃で混練し、その後トルエンと水を減圧除去した。得られた感光性樹脂組成物を厚さ125μmのポリエチレンテレフタレートフィルム上にポリエステル系接着層をコーテイングしたフィルムと、同じポリエチレンテレフタレートフィルム上に粘着防止層(ポリビニルアルコール)をコーテイングしたフィルムで挟み(接着層、粘着防止層が感光性樹脂組成物と接触するように)、ヒートプレス機で105℃、100kg/cm2の圧力で1分間加圧することにより、厚さ1.7mmの感光性樹脂原版を作成した。得られた原版を剥離し、網点200線1%〜95%、最小独立点直径100μm、最小凸文字1ポイント、最小抜き文字1ポイント、ベタ画像、ステップガイドを含む検査ネガをあて、365nmにおける照度17.5W/m2(Anderson&Vreeland社製ランプFR20T12−BL−9−BP)を用いて裏露光と表露光をおこないネガフィルムを除去し、アルキルナフタレンスルホン酸ソーダ4重量%を含有する40℃の中性水で8分間現像し、60℃で20分間乾燥した。
調合直後及び1時間経過後のドープの状態は均一であり、変わり無かった。得られた印刷版のショアA硬度は58、反発弾性は65%、1時間後の水膨潤率は1.5%、エタノール膨潤率は3.7%、24時間後の水膨潤率は3.5%、エタノール膨潤率は5.8%、365nmの光散乱率は17.3%であった。
実施例1において、(A)成分であるブタジエンラテックス(Nipol LX111NF 不揮発分55% 日本ゼオン(株)製)20重量部、アクリロニトリル−ブタジエンラテックス(Nipol LX550 不揮発分45% 日本ゼオン(株)製)6重量部、(B)成分である親水性重合体(PFT-3 不揮発分25% 共栄社化学(株)製)6重量部、(C)成分であるオリゴブタジエンアクリレート(ABU−2S 共栄社化学(株)製)11重量部を用いた以外は実施例1と同様にして、フレキソ刷版を作製した。得られた印刷版は、実施例1と同様の画像再現性と耐刷性を示した。
実施例1において、(E)成分である凝集防止剤(ノイゲンSDX−60 第一工業製薬(株)製)1重量部を除いた以外は実施例1と同様にして、ドープを調合した。ところが、得られたドープは調合直後にラテックス粒子間で急激な凝集が起こり、1時間経過後には固液分離したため、その時点で製造を中止した。
実施例1において、(A)成分であるアクリロニトリル−ブタジエンラテックス(Nipol SX1503 不揮発分43% 日本ゼオン(株)製)5重量部を除いた以外は実施例1と同様にして、フレキソ刷版を作製した。得られた印刷版は、20分間現像してもレリーフ深度が0.8mmに達することはなく、現像不良であった。
実施例1において、(B)成分である親水性重合体(PFT-3 不揮発分25% 共栄社化学(株)製)5重量部を除いた以外は実施例1と同様にして、フレキソ刷版を作製した。得られた印刷版は、20分間現像してもレリーフ深度が0.8mmに達することはなく、現像不良であった。
実施例1において、(C)成分であるオリゴブタジエンアクリレート(ABU−2S 共栄社化学(株)製)のかわりに液状ポリブタジエン(B−2000 日本石油化学(株)製)13重量部を用いた以外は実施例1と同様にして、フレキソ刷版を作製した。得られた印刷版は、20分間現像してもレリーフ深度が0.8mmに達することはなく、現像不良であった。
Claims (2)
- (A)ポリブタジエンラテックス、スチレン−ブタジエン共重合体ラテックス、アクリロニトリル−ブタジエン共重合体ラテックス、メチルメタクリレート−ブタジエン共重合体ラテックス、ポリイソプレンラテックスから選ばれる少なくとも2種類以上の水分散ラテックスから得られる疎水性重合体、(B)ポリブタジエン骨格を有する親水性重合体、(C)ブタジエン骨格を有する親水性重合体、(D)光重合性化合物としてブタジエン重合体又はイソプレン重合体の末端および/または側鎖にエチレン性不飽和基が結合した光重合性オリゴマー、および(E)凝集防止剤としてラテックスに含有するもの以外に炭素数が12〜15のノニオン系界面活性剤を含有し、水分散ラテックスから得られる疎水性重合体が、(C)成分であるオリゴマーの光重合性化合物中に分散した形態であることを特徴とする感光性樹脂組成物。
- 支持体上に、請求項1に記載の感光性樹脂組成物からなる感光層を塗設して構成されることを特徴とする感光性樹脂印刷用原版