JP4463844B2 - 自己融着糸条 - Google Patents
自己融着糸条 Download PDFInfo
- Publication number
- JP4463844B2 JP4463844B2 JP2007278402A JP2007278402A JP4463844B2 JP 4463844 B2 JP4463844 B2 JP 4463844B2 JP 2007278402 A JP2007278402 A JP 2007278402A JP 2007278402 A JP2007278402 A JP 2007278402A JP 4463844 B2 JP4463844 B2 JP 4463844B2
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- filaments
- fused
- resin
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明者らは、さらに検討を重ねて本発明を完成した。
(1) 熱可塑性樹脂からなるフィラメント複数本を引きそろえて加撚および/または製紐し、ついで、送り込みローラーと巻き取りローラーとの速度比((巻き取りローラーの速度)/(送り込みローラーの速度))1.0未満で加熱下延伸することにより、隣接するフィラメントを実質的に融着させて製造されることを特徴とする融着糸条、
(2) 上記の隣接するフィラメントを実質的に融着させたのち、ついで、送り込みローラーと巻き取りローラーとの速度比((巻き取りローラーの速度)/(送り込みローラーの速度))1.0より高い倍率で加熱下延伸することにより製造されることを特徴とする(1)に記載の融着糸条、
(3) 熱可塑性樹脂が、ポリアミド系樹脂、ポリエステル系樹脂、フッ素系樹脂またはポリオレフィン系樹脂であることを特徴とする上記(1)又は(2)に記載の融着糸条、
(4) 熱可塑性樹脂からなるフィラメントが、20g/d以上の引張強度を有するフィラメントであることを特徴とする上記(1)又は(2)に記載の融着糸条、
(5) 上記の送り込みローラーと巻き取りローラーとの速度比1.0未満で加熱下延伸する際の温度が、熱可塑性樹脂からなるフィラメントの融点より高いことを特徴とする上記(1)〜(4)のいずれかに記載の融着糸条、
(6) 上記の送り込みローラーと巻き取りローラーとの速度比1.0より高い倍率での加熱下延伸後に、さらに、外周を合成樹脂で被覆することを特徴とする上記(2)〜(5)のいずれかに記載の融着糸条の製造方法、
(7) 上記の熱可塑性樹脂からなるフィラメント複数本は、芯糸を取り囲むように引きそろえてさらに加撚するかまたは芯糸のまわりに製紐してある、上記(1)〜(6)のいずれかに記載の融着糸条、
(8) 熱可塑性樹脂からなるフィラメント複数本を含み、融着のための媒体が含まれておらず、隣接するフィラメントが互いに実質的に融着していることを特徴とする、上記(1)〜(7)のいずれかに記載の融着糸条、及び、
(9) 熱可塑性樹脂からなるフィラメント複数本を含有し、隣接するフィラメントが実質的に融着している糸条であって、その糸条の太さが、上記糸条と同じ熱可塑性樹脂からなる同数のフィラメントを含有する同数のヤーンを含み、隣接するフィラメントが融着していない糸条の太さの±10%の範囲内であり、その糸条の引張強度が、上記融着していない糸条の引張強度以上であることを特徴とする上記(8)に記載の融着糸条、
に関する。
本発明の自己融着糸条は、隣接するフィラメントを実質的に完全融着しているため、水を抱き込みにくく、水切れ性に優れている。このことから、特に本発明の自己融着糸条はレジャーや漁業用釣糸、水産資材として好適に用いることができる。
加えて、本発明の自己融着糸条においては、複数種類のフィラメントを用いたり、芯糸を糸条の中心に挿入したりすることによって、例えば比重を任意に設定するなど、単独のフィラメントでは得られない効果を発揮させることができる。又は、単糸デニールを細くしなくても、初期の強力を維持できるため、耐磨耗性に優れた糸条の製造ができるようになった。
本発明の製造方法で使用される熱可塑性樹脂としては、例えば、ポリアミド系樹脂、ポリエステル系樹脂、フッ素系樹脂またはポリオレフィン系樹脂などが挙げられる。
ポリアミド系樹脂としては、具体的に、例えば、ナイロン6、ナイロン66、ナイロン12、ナイロン6,10などの脂肪族ポリアミドもしくはその共重合体、または芳香族ジアミンとジカルボン酸により形成される半芳香族ポリアミドもしくはその共重合体などが挙げられる。
ポリオレフィン系樹脂としては、具体的に、例えば、ポリエチレンまたはポリプロピレン等が挙げられる。
上記高強力フィラメントとして、具体的には、例えば、超高分子量ポリエチレンフィラメント、全芳香族ポリアミドフィラメント、ヘテロ環高性能フィラメントまたは全芳香族ポリエステルフィラメント等が挙げられる。なかでも、屈曲性高分子からなる超高分子量ポリエチレンフィラメントが好ましい。
超高分子量ポリエチレンフィラメントの製造方法は、たとえば特開昭55−5228号公報、特開昭55−107506号公報などに開示されており、これら公知の方法を用いてよい。また、超高分子量ポリエチレンフィラメントとして、ダイニーマ(登録商標)(商品名 東洋紡績株式会社製)やスペクトラ(商品名 ハネウエル社製)等の市販品を用いてもよい。
上記金属粒子を含有するフィラメントは、例えば、単軸または二軸混練機などを用いて金属粒子を溶融混練することにより、金属を含有する熱可塑性樹脂を作成し、かかる熱可塑性樹脂から広く実施されている溶融紡糸方法などを用いて製造することができる。
本発明においては、上述した熱可塑性樹脂からなるフィラメント複数本を引きそろえ、所望により加撚および/または製紐する。
フィラメント複数本を引きそろえる際には、所望により、芯糸を中心にして、その周りを取り囲むようにフィラメントを引きそろえてもよい。
複数本のフィラメントに撚りをかける方法としては、特に限定されないが、例えば、リング撚糸機、ダブルツイスターまたはイタリー式撚糸機など公知の撚糸機を用いて行うことができる。本工程における撚りの程度は特に限定されないが、撚係数Kが約0.2〜1.5程度、より好ましくは約0.3〜1.2程度、さらに好ましくは約0.4〜0.8程度となるように撚りをかけることが好適である。なお、撚係数Kは次式:K=t×D1/2(但し、t:撚り数(回/m)、D:繊度(tex)を表す。)より算出される。前記式における繊度は、JIS L 1013(1999)に従って測定する。
延伸処理の方法は、例えば空気中で加熱しながら延伸する等の自体公知の方法が採用され得る。延伸は、1段で行ってもよいし、2段以上で行ってもよい。延伸時の温度は、フィラメントの種類もしくは径の大きさまたは延伸速度によって異なるので一概には言えないが、例えば、通常、フィラメントの融点−約10℃以上の温度である。延伸時の温度の上限は、特に限定されない。より具体的には、フィラメントが超高分子量ポリエチレンフィラメントの場合、延伸時の温度は、約150℃以上(好ましくは約150℃〜170℃)である。
延伸処理の方法は、液体または気体中で加熱しながら延伸する等の自体公知の方法が採用され得る。延伸は、1段で行ってもよいし、2段以上で行ってもよい。本延伸処理は、約1.0より高い延伸倍率で行うことを特徴とする。実際にどのような延伸倍率で行うかは、フィラメントの種類、原料となるフィラメントに対し既に延伸処理がされているか否か、または既に延伸処理がされている場合はどの程度の延伸倍率で延伸されているのか等の事情に応じて、適宜選択すればよい。例えば市販のフィラメントのように、前工程において原料として、既に延伸倍率1.0よりも高い倍率で延伸されているフィラメントを用いる場合は、本工程(延伸倍率1.0より高い倍率での加熱下延伸)の延伸倍率は通常約1.01〜5程度、好ましくは約1.01〜3程度、より好ましくは約2.2〜3程度が好適である。一方、前工程において未延伸フィラメントを用いる場合は、本工程での延伸倍率は通常約1.01〜15程度、好ましくは約2〜10程度、より好ましくは約4〜8程度が好適である。ここで、「未延伸フィラメント」とは、製造工程において全く延伸されていないフィラメントもしくは市販のフィラメントの製造時の延伸倍率に満たない延伸倍率で延伸されているフィラメントをいう。
本発明において前記被覆に用いる合成樹脂(以下、「被覆樹脂」ともいう。)は、公知の樹脂を用いてよいが、本発明の自己融着糸条に密着できるものが好ましい。特に、屋外での長期使用に耐え、こすれ、曲げ疲労性等の耐久特性に優れたものが前記被覆樹脂としてより好ましい。下記に詳述する押出被覆により本発明の自己融着糸条の外周を被覆樹脂で被覆する場合、自己融着糸条がダイニーマである場合は、被覆樹脂としては、メルトインデックスが約0.1g/10分以上、より好ましくは、約0.1g/10分〜1000g/10分程度のものが好適である。コアとなる本発明の自己融着糸条の引張強度を損なわずに被覆するためには、上記範囲のメルトインデックスを有する被覆樹脂を用いることが好ましい。ここで、樹脂のメルトインデックスは、JIS K 7210(1976)「熱可塑性プラスチックの流れ試験方法」に従った方法にて、メルトインデクサ(宝工業株式会社製 L−202)で測定する。
このようにして上記自己融着糸条を被覆樹脂で被覆することにより、さらに水切れ性に優れた自己融着糸条を製造し得る。
製造した製紐糸A、融着糸B及び融着糸Cの強力(kg)及び伸度(%)を、万能試験機
オートグラフAG−100kNI(製品名、株式会社島津製作所製)を用いて測定した。測定結果を表1に示す。
製造した製紐糸A’、融着糸B’及び融着糸C’の引張強力(kg)、引張強度(g/d)及び伸度(%)を、実施例1と同様にして測定した。測定結果を表2に示す。
Claims (9)
- 熱可塑性樹脂からなるフィラメント複数本を引きそろえて加撚および/または製紐し、ついで、送り込みローラーと巻き取りローラーとの速度比((巻き取りローラーの速度)/(送り込みローラーの速度))1.0未満で加熱下延伸することにより隣接するフィラメントを実質的に融着させて製造されることを特徴とする融着糸条。
- 上記の隣接するフィラメントを実質的に融着させたのち、ついで、送り込みローラーと巻き取りローラーとの速度比((巻き取りローラーの速度)/(送り込みローラーの速度))1.0より高い倍率で加熱下延伸することにより製造されることを特徴とする請求項1に記載の融着糸条。
- 熱可塑性樹脂が、ポリアミド系樹脂、ポリエステル系樹脂、フッ素系樹脂またはポリオレフィン系樹脂であることを特徴とする請求項1又は請求項2に記載の融着糸条。
- 熱可塑性樹脂からなるフィラメントが、20g/d以上の引張強度を有するフィラメントであることを特徴とする請求項1又は請求項2に記載の融着糸条。
- 上記の送り込みローラーと巻き取りローラーとの速度比1.0未満で加熱下延伸する際の温度が、熱可塑性樹脂からなるフィラメントの融点より高いことを特徴とする請求項1〜4のいずれかに記載の融着糸条。
- 上記の送り込みローラーと巻き取りローラーとの速度比1.0より高い倍率での加熱下延伸後に、さらに、外周を合成樹脂で被覆することを特徴とする請求項2〜5のいずれかに記載の融着糸条。
- 上記の熱可塑性樹脂からなるフィラメント複数本は、芯糸を取り囲むように引きそろえてさらに加撚するかまたは芯糸のまわりに製紐してある、請求項1〜6のいずれかに記載の融着糸条。
- 熱可塑性樹脂からなるフィラメント複数本を含み、融着のための媒体が含まれておらず、隣接するフィラメントが互いに実質的に融着していることを特徴とする、請求項1〜7のいずれかに記載の融着糸条。
- 熱可塑性樹脂からなるフィラメント複数本を含有し、隣接するフィラメントが実質的に融着している糸条であって、その糸条の太さが、上記糸条と同じ熱可塑性樹脂からなる同数のフィラメントを含有する同数のヤーンを含み、隣接するフィラメントが融着していない糸条の太さの±10%の範囲内であり、その糸条の引張強度が、上記融着していない糸条の引張強度以上であることを特徴とする請求項8に記載の融着糸条。