JP3482408B2 - Vacuum insulation and refrigerators using vacuum insulation - Google Patents
Vacuum insulation and refrigerators using vacuum insulationInfo
- Publication number
- JP3482408B2 JP3482408B2 JP2002064972A JP2002064972A JP3482408B2 JP 3482408 B2 JP3482408 B2 JP 3482408B2 JP 2002064972 A JP2002064972 A JP 2002064972A JP 2002064972 A JP2002064972 A JP 2002064972A JP 3482408 B2 JP3482408 B2 JP 3482408B2
- Authority
- JP
- Japan
- Prior art keywords
- heat insulating
- insulating material
- vacuum heat
- nylon film
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、真空断熱材、およ
び真空断熱材を使用した冷蔵庫に関するものである。TECHNICAL FIELD The present invention relates to a vacuum heat insulating material and a refrigerator using the vacuum heat insulating material.
【０００２】[0002]
【従来の技術】近年、地球環境保護が大きく叫ばれるな
か、家電製品の省エネルギー化は緊急に取り組むべき重
要な課題となってきている。この解決方法の一つとし
て、無駄な熱の授受を防ぐ目的での真空断熱材の適用が
ある。2. Description of the Related Art In recent years, with the great demand for protection of the global environment, energy saving of home electric appliances has become an important issue to be urgently addressed. As one of the solutions, there is application of a vacuum heat insulating material for the purpose of preventing wasteful heat transfer.
【０００３】真空断熱材は、発泡樹脂や繊維材等を芯材
として外被材内に入れた断熱材で、断熱材内部を真空に
保つことにより気体の熱伝導率を著しく低下させたもの
であり、その断熱性能を長期に渡って維持するために
は、断熱材内部を真空に保ち続ける必要がある。しか
し、外被材にピンホールが生じると外部からのガス侵入
が起こるために断熱性能が大きく悪化してしまうという
課題がある。The vacuum heat insulating material is a heat insulating material in which a foamed resin, a fiber material or the like is used as a core material and is put in an outer covering material, and the heat conductivity of gas is remarkably lowered by keeping the inside of the heat insulating material in vacuum. However, in order to maintain the heat insulating performance for a long period of time, it is necessary to keep the inside of the heat insulating material vacuum. However, there is a problem that when a pinhole is formed in the outer covering material, gas infiltration from the outside occurs, so that the heat insulation performance is significantly deteriorated.
【０００４】そこで、真空断熱材の外被材のラミネート
構成において、耐傷性のよいナイロンフィルムを外被材
の最外層に追加ラミネートすることによって外部からの
耐磨耗性や耐傷性等を強化した技術が、特開昭６１−２
７３９２号公報に開示されている。Therefore, in the laminated structure of the jacket material of the vacuum heat insulating material, a nylon film having good scratch resistance is additionally laminated on the outermost layer of the jacket material to enhance abrasion resistance and scratch resistance from the outside. The technology is JP-A-61-2.
It is disclosed in Japanese Patent No. 7392.
【０００５】また、真空断熱材以外の包装用材料とし
て、強度や耐湿性を上げることを目的とした電子部品用
包装袋で、ナイロンを用いて耐突き刺し性を向上させた
技術が特開平９−１９３３０５号から特開平９−１９３
３０７号公報に開示されている。Further, as a packaging material other than the vacuum heat insulating material, a technique for improving puncture resistance by using nylon in a packaging bag for electronic parts for the purpose of increasing strength and moisture resistance is disclosed in Japanese Patent Laid-Open No. 9- From 193305 to JP-A-9-193
No. 307 publication.
【０００６】この発明の積層フィルムは、半導体デバイ
スなどの電子部品を湿気や静電気から保護するための電
子部品用包装袋（電子部品収納容器用包装袋を含む）の
用途に使用されるもので、電子部品が製造されてから実
装されるまでの間の保護が目的であり、１〜２年程度の
防湿効果の持続性を考慮したものである。The laminated film of the present invention is used for an electronic component packaging bag (including an electronic component storage container packaging bag) for protecting electronic components such as semiconductor devices from moisture and static electricity. The purpose is to protect the electronic components from the time they are manufactured to the time they are mounted, and the durability of the moisture-proof effect for about 1 to 2 years is taken into consideration.
【０００７】また、特開２０００−５２５１５号公報に
開示されているように、突き刺し強度が必要となるトレ
イ入り商品の外装フィルムなどにも、熱溶着フィルムと
共押ししたナイロンフィルムが、ガスバリア層となるプ
ラスチックフィルムと貼り合わせて用いられている。Further, as disclosed in Japanese Patent Application Laid-Open No. 2000-52515, a nylon film co-pressed with a heat-welding film serves as a gas barrier layer even for an exterior film of a tray-containing product which requires puncture strength. It is used by pasting it with a plastic film.
【０００８】[0008]
【発明が解決しようとする課題】すなわち、通常の包装
材では内容物の保護が主な目的であり、その保管期間も
せいぜい数年間である。これに対し、真空断熱材の外被
材は、真空断熱材内部の真空度が断熱性能に直接的に関
わるものである。特に、冷蔵庫に搭載する真空断熱材は
１０年以上に渡って使用されることを考慮すると、わず
かなピンホールも許されず、外被材の耐突き刺し性の向
上は真空断熱材の断熱性能維持を考える上で大変重要で
ある。That is, the main purpose of ordinary packaging materials is to protect the contents, and the storage period is at most several years. On the other hand, in the vacuum heat insulating material, the degree of vacuum inside the vacuum heat insulating material is directly related to the heat insulating performance. In particular, considering that the vacuum insulation material to be installed in the refrigerator will be used for more than 10 years, even pinholes are not allowed, and the improvement of the puncture resistance of the jacket material is to maintain the insulation performance of the vacuum insulation material. It is very important in thinking.
【０００９】従来の外被材仕様でも、真空断熱材の芯材
として発泡樹脂のように硬度や密度の小さい芯材を使用
した場合にはピンホールが生じることはなかった。しか
し、冷蔵庫への広範な適用等のためには真空断熱材も比
較的大きなものが必要になり、重量が増加して外部から
の突き刺しに対して強化する必要がある。Even in the conventional jacket material specification, pinholes did not occur when a core material having a low hardness and a small density such as foamed resin was used as the core material of the vacuum heat insulating material. However, for a wide range of applications such as refrigerators, a relatively large vacuum heat insulating material is required, which increases the weight and needs to be strengthened against external piercing.
【００１０】更には、無機繊維をボード状に成形する
と、硬度が増すとともに、成形時にかかる力のためにボ
ードの表面の繊維が折れる等の現象が起こり、これによ
って鋭くなった繊維がボードの表面に多数存在するよう
になる。これを真空断熱材の芯材に使用したときには、
繊維の先端が外被材を内側から突き刺すという現象が起
こる。このような繊維による内側からの突き刺しは繊維
径が太くなると多発する傾向にあり、芯材の密度を大き
くすると、芯材重量が大きくなることに加えて、より硬
度が増すために、さらに内側からの突き刺しによるピン
ホールが生じやすくなる。Furthermore, when the inorganic fibers are molded into a board shape, the hardness increases and the fibers on the surface of the board are broken due to the force applied during molding. As a result, sharpened fibers cause the surface of the board to become sharp. There will be many in. When this is used as the core material for vacuum insulation,
The phenomenon that the tip of the fiber pierces the jacket material from the inside occurs. The piercing from the inside by such fibers tends to occur frequently when the fiber diameter becomes thick, and when the density of the core material is increased, the weight of the core material is increased and the hardness is further increased. Pinholes are more likely to occur due to piercing.
【００１１】すなわち、無機繊維をボード状に成形した
芯材を用いた真空断熱材を冷蔵庫に適用する場合には、
芯材の硬度が高い上、芯材一枚あたりのサイズおよび重
量が大きくなるために、従来のラミネート構造ではピン
ホールの発生を防ぐことができなくなってきた。That is, when a vacuum heat insulating material using a core material formed by molding inorganic fibers into a board is applied to a refrigerator,
Since the hardness of the core material is high and the size and weight of each core material are large, it has become impossible to prevent the occurrence of pinholes in the conventional laminated structure.
【００１２】本発明は、外被材のラミネート仕様を変え
ることにより、無機繊維のボード状芯材を冷蔵庫用の真
空断熱材に適用するような厳しい条件でも、硬度やサイ
ズや重量の相互作用によるピンホールを生じることがな
く、長期に渡り断熱性能を保つ真空断熱材を提供し、更
にこの真空断熱材を使用した省エネルギーの冷蔵庫を提
供することを目的とする。According to the present invention, by changing the laminating specifications of the jacket material, the hardness, size, and weight interact due to the interaction of the inorganic fiber board-like core material in a vacuum heat insulating material for a refrigerator. An object of the present invention is to provide a vacuum heat insulating material that does not cause pinholes and keeps its heat insulating performance for a long period of time, and further to provide an energy-saving refrigerator using this vacuum heat insulating material.
【００１３】[0013]
【課題を解決するための手段】本発明の請求項１に記載
の発明は、芯材と、ラミネートで構成された外被材とを
備え、前記芯材が無機繊維を成形したボード状であり、
前記外被材のラミネート構成が、外側から順に、第１の
延伸ナイロンフィルム、第２の延伸ナイロンフィルム、
金属箔からなるガスバリア層、熱溶着層であり、前記第
１、第２の延伸ナイロンフィルム間に接着層があり、か
つ密度が１５０ｋｇ／ｍ３以上である真空断熱材であ
る。The invention according to claim 1 of the present invention comprises a core material and an outer covering material composed of a laminate.
The core material is a board-shaped molded inorganic fiber,
The laminate structure of the covering material is, in order from the outside, a first
Stretched nylon film, second stretched nylon film,
A gas barrier layer made of a metal foil and a heat-welding layer,
Is there an adhesive layer between the first and second stretched nylon films?
It is a vacuum heat insulating material having a density of 150 kg / m3 or more .
【００１４】[0014]
【００１５】[0015]
【００１６】 発泡樹脂を芯材として用いたときにピン
ホールの発生が起こらない従来のラミネート構成であっ
ても、真空断熱材の密度が１５０ｋｇ／ｍ３以上になる
ような無機繊維を成形したボード状芯材を用いた場合
は、成形時に折れて鋭くなった繊維が芯材表面に存在す
ることに加え、芯材重量や硬度が大きくなるために、ピ
ンホールが発生する。しかし、ナイロンは、耐衝撃性、
耐屈曲性や引張強度など様々な機械的特性に優れた材料
であり、延伸ナイロンフィルムは無延伸ナイロンフィル
ムに比べガスバリア性や耐突き刺し性により優れてお
り、外被材に延伸ナイロンフィルムを２層以上使用する
ことによって芯材の硬度やサイズや重量の条件が厳しく
なった場合でもピンホールの発生を、より確実に防ぐこ
とができる。[0016] Even with a conventional laminate structure in which pinholes do not occur when a foamed resin is used as a core material, a board formed with inorganic fibers such that the vacuum heat insulating material has a density of 150 kg / m 3 or more. When the core material is used, pinholes occur because the fibers that are broken and sharpened at the time of molding are present on the surface of the core material, and the weight and hardness of the core material increase. However, nylon is impact resistant,
Material with various mechanical properties such as flex resistance and tensile strength
The stretched nylon film is superior to the non-stretched nylon film in terms of gas barrier property and puncture resistance, and the hardness, size and weight of the core material can be improved by using two or more layers of stretched nylon film as the outer covering material. Even if the situation becomes severe, it is possible to more reliably prevent the occurrence of pinholes.
【００１７】[0017]
【００１８】[0018]
【００１９】[0019]
【００２０】外被材にナイロンフィルムを２層以上ラミ
ネートすることによって、耐突き刺し性を向上させると
ともに、ガスバリア層の外側にのみナイロンフィルムを
ラミネートすることにより、ガス侵入の影響が大きい熱
溶着層端部の断面の厚さを増やすことがなく、真空断熱
材のサイズが冷蔵庫用途のように大きくなった場合にお
いても外被材のガスバリア性を保持することができる。
また、ナイロンフィルムを２層重ねると、ナイロンフィ
ルム間の接着層により内側からの突き刺しが緩和され、
１層で２層分の厚みを設定する場合よりも突き刺し強度
を大きくできる。The piercing resistance is improved by laminating two or more layers of nylon film on the outer covering material, and the nylon film is laminated only on the outer side of the gas barrier layer, so that the end of the heat-welding layer is greatly affected by gas intrusion. The gas barrier property of the covering material can be maintained even when the size of the vacuum heat insulating material is increased as in a refrigerator application without increasing the thickness of the cross section of the portion.
Also, when two layers of nylon film are stacked, the piercing from the inside is alleviated by the adhesive layer between the nylon films,
The piercing strength can be increased as compared with the case of setting the thickness for two layers with one layer.
【００２１】 本発明の請求項２に記載の発明は、少な
くとも、第１のナイロンフィルムの内側、または、第２
のナイロンフィルムの外側に蒸着を施したことを特徴と
する真空断熱材である。The invention according to claim 2 of the present invention is at least the inner side of the first nylon film or the second nylon film.
It is a vacuum heat insulating material characterized by vapor deposition on the outside of the nylon film.
【００２２】ナイロンフィルムのいずれかに蒸着層が存
在することにより、外被材の内側からの突き刺しによっ
て熱溶着層およびガスバリア層にピンホールが生じた場
合でも、ナイロンフィルムに施した蒸着によりガスの透
過をより確実に防ぐことができる。Due to the presence of the vapor-deposited layer on any of the nylon films, even if pinholes are formed in the heat-welding layer and the gas barrier layer by being pierced from the inside of the outer covering material, the vapor deposition on the nylon film prevents the formation of gas. Permeation can be prevented more reliably.
【００２３】 本発明の請求項３に記載の発明は、請求
項１または請求項２の真空断熱材を搭載した冷蔵庫であ
る。The invention according to claim 3 of the present invention is a refrigerator equipped with the vacuum heat insulating material according to claim 1 or 2 .
【００２４】無機繊維を成形したボード状芯材を使用し
た真空断熱材を冷蔵庫に適用する場合、一枚あたりのサ
イズや重量が大きくなることにより、ピンホール発生の
リスクが非常に高くなるが、本発明によって、ピンホー
ルを発生させることなく長期間断熱性能を保つ真空断熱
材を得ることができるため、長期間省エネルギーを保つ
冷蔵庫を提供することができる。When a vacuum heat insulating material using a board-shaped core material made of inorganic fibers is applied to a refrigerator, the risk of pinholes is extremely high due to the increase in size and weight per sheet, According to the present invention, it is possible to obtain a vacuum heat insulating material that keeps heat insulating performance for a long time without generating pinholes, and thus it is possible to provide a refrigerator that saves energy for a long time.
【００２５】[0025]
【発明の実施の形態】以下、本発明の真空断熱材の実施
の形態について説明する。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the vacuum heat insulating material of the present invention will be described below.
【００２６】 本発明は、芯材と、ラミネートで構成さ
れた外被材とを備え、前記芯材が無機繊維を成形したボ
ード状であり、前記外被材のラミネート構成が、外側か
ら順に、第１の延伸ナイロンフィルム、第２の延伸ナイ
ロンフィルム、金属箔からなるガスバリア層、熱溶着層
であり、前記第１、第２の延伸ナイロンフィルム間に接
着層があり、かつ密度が１５０ｋｇ／ｍ３以上であるこ
とを特徴とする真空断熱材である。The present invention comprises a core material and a laminate.
An outer cover material, wherein the core material is a board-shaped molded inorganic fiber , and the laminated structure of the outer cover material is outside.
In order from the first stretched nylon film, the second stretched nylon film
Ron film, gas barrier layer made of metal foil, heat welding layer
And between the first and second stretched nylon films
It has a layer and has a density of 150 kg / m3 or more.
It is a vacuum heat insulating material characterized by .
【００２７】無機繊維としては、グラスウール、グラス
ファイバー、アルミナ繊維、シリカアルミナ繊維、シリ
カ繊維、ロックウール、炭化ケイ素繊維等特に指定する
ものではない。また、ボード状に加熱加圧成形する時に
は、取り扱い性向上のためバインダーを使用しても良
い。バインダーを使用すると、ボード化した芯材の硬度
が大きくなるためにピンホール発生のリスクは大きくな
るが、本発明のラミネート構成ではバインダーによって
芯材硬度が高くなった場合でもピンホールの発生を防ぐ
ことができる。As the inorganic fiber, glass wool, glass fiber, alumina fiber, silica-alumina fiber, silica fiber, rock wool, silicon carbide fiber and the like are not particularly specified. In addition, a binder may be used to improve handleability when the board is heated and pressed. When a binder is used, the risk of pinholes is increased because the hardness of the core material made into a board is increased, but in the laminated structure of the present invention, the occurrence of pinholes is prevented even when the core material hardness is increased by the binder. be able to.
【００２８】ナイロンフィルムは、耐衝撃性、耐屈曲性
や引張強度など様々な機械的特性に優れており、前記外
被材に使用するナイロンの種類としては、ナイロン−
６、ナイロン−６．６、ＭＸＤナイロン等があり、特に
指定するものではないが、芳香族系ナイロンを使用する
とガスバリア性をより向上させることができる。Nylon films are excellent in various mechanical properties such as impact resistance, flex resistance and tensile strength, and as the type of nylon used for the covering material, nylon-
6, nylon-6.6, MXD nylon and the like, which are not particularly specified, but the gas barrier property can be further improved by using aromatic nylon.
【００２９】また、ナイロンフィルムの形態としては、
単層ナイロンフィルム、異種のナイロンを共押出し加工
した多層ナイロンフィルムなどがあるが、特に指定する
ものではない。前記外被材のガスバリア層としては、金
属箔が最も適しているが、金属または金属酸化物、ある
いはダイヤモンドライクカーボンを蒸着したプラスチッ
クフィルム等を用いることもでき、ガス透過を低減する
目的で用いるものであれば特に指定するものではない。Further, as the form of the nylon film,
There are single-layer nylon films, multi-layer nylon films obtained by co-extruding different types of nylon, etc., but it is not particularly specified. As the gas barrier layer of the jacket material, a metal foil is most suitable, but a metal or metal oxide, or a plastic film deposited with diamond-like carbon can also be used, and is used for the purpose of reducing gas permeation. If so, there is no particular designation.
【００３０】上記金属箔としては、アルミニウム、ステ
ンレス、鉄等を用いることができるが、特に指定するも
のではない。As the metal foil, aluminum, stainless steel, iron or the like can be used, but it is not particularly specified.
【００３１】プラスチックフィルムへの金属蒸着の材料
は、アルミニウム、コバルト、ニッケル、亜鉛、銅、
銀、あるいはそれらの混合物等を用いることができる
が、特に指定するものではない。Materials for metal deposition on a plastic film include aluminum, cobalt, nickel, zinc, copper,
Silver, a mixture thereof, or the like can be used, but it is not particularly specified.
【００３２】また、前記プラスチックフィルム上への金
属酸化物蒸着の材料は、シリカ、アルミナ等を用いるこ
とができるが、特に指定するものではない。As the material for depositing the metal oxide on the plastic film, silica, alumina or the like can be used, but it is not particularly specified.
【００３３】前記外被材の熱溶着層は、外被材を構成す
るフィルムの中で最もガス透過度が大きい部分であり、
熱溶着層の性質は真空断熱材の経時断熱性能に大きく影
響する。熱溶着層の厚さは、減圧封止工程における封止
品質の安定性や、熱溶着部端面からのガス侵入の抑制
や、ガスバリア層として金属箔を使用した場合における
熱伝導による表面からのヒートリークを考慮すると、２
５μｍ〜６０μｍが適している。熱溶着層の材料として
は、無延伸ポリプロピレンフィルム、高密度ポリエチレ
ンフィルム、直鎖状低密度ポリエチレンフィルム等を用
いることができ、特に指定するものではないが、耐突き
刺し性に優れた無延伸ポリプロピレンフィルムを用いる
のがより効果的である。また、外被材の外層にさらに表
面保護層を設けることも可能である。The heat-welding layer of the jacket material is a portion having the highest gas permeability in the film constituting the jacket material,
The properties of the heat-welded layer have a great influence on the temporal heat insulation performance of the vacuum heat insulating material. The thickness of the heat-welding layer is the stability of the sealing quality in the reduced pressure sealing process, the suppression of gas intrusion from the end face of the heat-welding portion, and the heat from the surface due to heat conduction when a metal foil is used as the gas barrier layer. 2 considering the leak
5 μm to 60 μm is suitable. As the material of the heat-welding layer, an unstretched polypropylene film, a high-density polyethylene film, a linear low-density polyethylene film or the like can be used, and although not particularly specified, an unstretched polypropylene film excellent in puncture resistance. Is more effective. It is also possible to further provide a surface protective layer on the outer layer of the outer covering material.
【００３４】表面保護層としては、ポリエチレンテレフ
タレートフィルム、ポリプロピレンフィルムの延伸加工
品などが利用でき、ポリエチレンテレフタレートフィル
ムを用いると水蒸気バリア性を向上させることができ
る。As the surface protective layer, a polyethylene terephthalate film, a stretched product of a polypropylene film, or the like can be used. When a polyethylene terephthalate film is used, the water vapor barrier property can be improved.
【００３５】また、外被材の袋形状は、四方シール袋、
ガゼット袋、三方シール袋、ピロー袋、センターテープ
シール袋等があるが、特に指定するものではない。The bag shape of the outer cover material is a four-sided seal bag,
There are gusset bags, three-sided seal bags, pillow bags, center tape seal bags, etc., but they are not specified.
【００３６】また、真空断熱材の初期断熱性能および経
時断熱性能をより一層向上させる場合は、ガス吸着剤や
水分吸着剤等のゲッター物質を使用することも可能であ
る。Further, in order to further improve the initial heat insulation performance and the time-dependent heat insulation performance of the vacuum heat insulating material, a getter substance such as a gas adsorbent or a water adsorbent can be used.
【００３７】その吸着機構は、物理吸着、化学吸着、お
よび吸蔵、収着等のいずれでもよいが、非蒸発型ゲッタ
ーとして作用する物質が良好である。The adsorption mechanism may be physical adsorption, chemical adsorption, occlusion, sorption, or the like, but a substance that acts as a non-evaporable getter is preferable.
【００３８】具体的には、合成ゼオライト、活性炭、活
性アルミナ、シリカゲル、ドーソナイト、ハイドロタル
サイト等の物理吸着剤である。Specifically, it is a physical adsorbent such as synthetic zeolite, activated carbon, activated alumina, silica gel, dawsonite and hydrotalcite.
【００３９】化学吸着剤としては、アルカリ金属やアル
カリ土類金属の酸化物や、アルカリ金属やアルカリ土類
金属の水酸化物等が利用でき、特に、酸化リチウム、水
酸化リチウム、酸化カルシウム、水酸化カルシウム、酸
化マグネシウム、水酸化マグネシウム、酸化バリウム、
水酸化バリウムが効果的に作用する。As the chemical adsorbent, oxides of alkali metals and alkaline earth metals, hydroxides of alkali metals and alkaline earth metals, and the like can be used, and in particular, lithium oxide, lithium hydroxide, calcium oxide, water and the like. Calcium oxide, magnesium oxide, magnesium hydroxide, barium oxide,
Barium hydroxide works effectively.
【００４０】また、硫酸カルシウム、硫酸マグネシウ
ム、硫酸ナトリウム、炭酸ナトリウム、炭酸カリウム、
塩化カルシウム、炭酸リチウム、不飽和脂肪酸、鉄化合
物等も効果的に作用する。Calcium sulfate, magnesium sulfate, sodium sulfate, sodium carbonate, potassium carbonate,
Calcium chloride, lithium carbonate, unsaturated fatty acids, iron compounds, etc. also act effectively.
【００４１】また、バリウム、マグネシウム、カルシウ
ム、ストロンチウム、チタン、ジルコニウム、バナジウ
ム等の物質を単独、もしくは合金化したゲッター物質を
適用するのがより効果的である。Further, it is more effective to apply a getter substance, which is a single substance of barium, magnesium, calcium, strontium, titanium, zirconium, vanadium or the like, or is an alloy thereof.
【００４２】さらには、このような前記ゲッター物質を
少なくとも窒素、酸素、水分、二酸化炭素を吸着除去す
るため、種々混合して適用することも可能である。 真
空断熱材の製造方法は、まず外被材を作製し、その後外
被材中に芯材を挿入し内部を減圧し封止してもよく、あ
るいは、減圧槽中に芯材とロール状あるいはシート状の
ラミネートフィルムからなる外被材を設置し、ロール状
あるいはシート状の外被材を芯材に沿わせた状態にして
から外被材を熱溶着することにより、真空断熱材を作製
してもよく、特に指定するものではない。Further, in order to adsorb and remove at least nitrogen, oxygen, water, and carbon dioxide, it is possible to apply various kinds of the getter substances as described above. The manufacturing method of the vacuum heat insulating material may be as follows. First, the outer covering material is produced, and then the core material is inserted into the outer covering material and the inside is depressurized and sealed. A vacuum heat insulating material is produced by installing a jacket material made of a sheet-shaped laminate film, placing the roll-shaped or sheet-shaped jacket material along the core material, and then heat-welding the jacket material. However, it is not specified.
【００４３】次に、本発明の真空断熱材を使用した冷蔵
庫について説明する。Next, a refrigerator using the vacuum heat insulating material of the present invention will be described.
【００４４】真空断熱材を冷蔵庫に適用した場合、冷蔵
庫の外箱と内箱とからなる空間の、外箱側または内箱側
に真空断熱材を貼付し、残りの空間に樹脂発泡体を充填
するのが一般的であるが、真空断熱材と発泡樹脂体とを
一体発泡した断熱体を冷蔵庫の外箱と内箱の間の空間に
配設しても良い。これらの適用は冷蔵庫本体の他、ドア
部、仕切り板部等にもでき、特に指定するものではない
が、広範囲に使用するほど使用電力量が低減できるもの
であり、機械室と内箱との間、あるいは冷凍室の周囲に
前記真空断熱材を用いることは、温度差が大きいため特
に断熱効率に優れ、より低電力量で冷蔵庫を運転でき
る。When the vacuum heat insulating material is applied to the refrigerator, the vacuum heat insulating material is attached to the outer box side or the inner box side of the space consisting of the outer box and the inner box of the refrigerator, and the remaining space is filled with the resin foam. In general, a heat insulating body obtained by integrally foaming a vacuum heat insulating material and a foamed resin body may be arranged in the space between the outer box and the inner box of the refrigerator. These applications can be applied not only to the refrigerator body but also to the door part, partition plate part, etc., and although not particularly specified, the power consumption can be reduced as the product is used over a wider area. The use of the vacuum heat insulating material in the space or around the freezer has a large temperature difference, so that the heat insulating efficiency is particularly excellent and the refrigerator can be operated with a lower electric power amount.
【００４５】空間に充填する樹脂発泡体は、例えば硬質
ウレタンフォーム、フェノールフォームやスチレンフォ
ーム等を使用することができるが、特に指定するもので
はない。The resin foam filled in the space may be, for example, hard urethane foam, phenol foam, styrene foam or the like, but is not particularly specified.
【００４６】また、例えば硬質ウレタンフォームを発泡
する際に用いる発泡剤としては、特に指定するものでは
ないが、オゾン層保護、地球温暖化防止の観点から、シ
クロペンタン、イソペンタン、ｎ−ペンタン、イソブタ
ン、ｎ−ブタン、水（炭酸ガス発泡）、アゾ化合物、ア
ルゴン等が望ましく、特に断熱性能の点からシクロペン
タンが望ましい。The foaming agent used for foaming the rigid urethane foam is not particularly specified, but from the viewpoint of ozone layer protection and global warming prevention, cyclopentane, isopentane, n-pentane, isobutane. , N-butane, water (carbon dioxide gas foaming), azo compounds, argon and the like are preferable, and cyclopentane is particularly preferable from the viewpoint of heat insulating performance.
【００４７】また、使用する冷媒は、フロン１３４ａ、
イソブタン、ｎ−ブタン、プロパン、アンモニア、二酸
化炭素、水等があるが、特に指定するものではない。The refrigerant used is Freon 134a,
There are isobutane, n-butane, propane, ammonia, carbon dioxide, water, etc., but they are not particularly specified.
【００４８】以下、本発明の実施の形態について更に詳
しく説明する。The embodiments of the present invention will be described in more detail below.
【００４９】（実施の形態１）図１は本発明の第１の実
施例における真空断熱材の断面図、図２は図１の外被材
を示す要部断面図である。なお、図１については、一般
的な真空断熱材と特に変わるものではない。(Embodiment 1) FIG. 1 is a sectional view of a vacuum heat insulating material according to a first embodiment of the present invention, and FIG. 2 is a sectional view of an essential part showing the jacket material of FIG. Note that FIG. 1 is not particularly different from a general vacuum heat insulating material.
【００５０】１は真空断熱材であり、２は外被材、３は
芯材である。Reference numeral 1 is a vacuum heat insulating material, 2 is a jacket material, and 3 is a core material.
【００５１】外被材２は第１のナイロンフィルム４、ガ
スバリア層５、第２のナイロンフィルム６、熱溶着層７
を有するラミネートフィルムであり、２枚のラミネート
フィルムを三方シールにて製袋しており、第１と第２の
ナイロンフィルム４，６にはいずれも延伸されたナイロ
ン−６を用いて、その厚さは第１のナイロンフィルム４
は２５μｍ、第２のナイロンフィルム６は１５μｍであ
る。The jacket material 2 is a first nylon film 4, a gas barrier layer 5, a second nylon film 6, and a heat welding layer 7.
Is a laminated film having two sides, and two laminated films are formed into a bag by a three-sided seal. The stretched nylon-6 is used for the first and second nylon films 4 and 6, and the thickness thereof is The first nylon film 4
Is 25 μm and the second nylon film 6 is 15 μm.
【００５２】芯材３は、内側からの突き刺しを評価する
ために表面硬度を特に高めたグラスウールボードで、１
４０℃の乾燥炉で１時間乾燥したものを使用した。The core material 3 is a glass wool board whose surface hardness is particularly high in order to evaluate the sticking from the inside.
What was dried in a drying oven at 40 ° C. for 1 hour was used.
【００５３】この芯材３を製袋した外被材２中に挿入
し、内部を１０Ｐａまで減圧し、開口部を熱溶着により
封止した。真空断熱材の密度は１５０ｋｇ／ｍ3とし
た。This core material 3 was inserted into the bag-made jacket material 2, the inside pressure was reduced to 10 Pa, and the opening was sealed by heat welding. The density of the vacuum heat insulating material was 150 kg / m 3 .
【００５４】以上のようにして得た真空断熱材１の振動
試験を行い、試験前後の熱伝導率とピンホールの有無を
評価した。The vacuum heat insulating material 1 obtained as described above was subjected to a vibration test, and the thermal conductivity before and after the test and the presence or absence of pinholes were evaluated.
【００５５】試験に使用したフィルムの仕様と試験結果
を、実施例１および実施例２として表１に示す。なお、
表中のＮｙはナイロンフィルム、ガスバリア層としてＡ
ｌはアルミニウム箔、熱溶着層としてＣＰＰは無延伸ポ
リプロピレンフィルム、ＬＬＤＰＥは直鎖状低密度ポリ
エチレンフィルムである。The specifications of the film used in the test and the test results are shown in Table 1 as Example 1 and Example 2. In addition,
Ny in the table is a nylon film, A as a gas barrier layer
1 is an aluminum foil, CPP is a non-stretched polypropylene film as a heat-welding layer, and LLDPE is a linear low-density polyethylene film.
【００５６】（実施の形態２）図３は本発明の第２の実
施例における真空断熱材の要部断面図である。(Embodiment 2) FIG. 3 is a sectional view of a main part of a vacuum heat insulating material according to a second embodiment of the present invention.
【００５７】１ａは真空断熱材であり、２ａは外被材、
３は芯材である。1a is a vacuum heat insulating material, 2a is a jacket material,
3 is a core material.
【００５８】外被材２ａは第１のナイロンフィルム４
ａ、第２のナイロンフィルム６ａ、ガスバリア層５、熱
溶着層７をドライラミネートしたフィルムであり、２枚
のラミネートフィルムを三方シールにて製袋しており、
第１と第２のナイロンフィルム４ａ，６ａにはいずれも
延伸されたナイロン−６を用いて、その厚さは第１のナ
イロンフィルム４ａは１５μｍ、第２のナイロンフィル
ム６ａは２５μｍである。The outer cover material 2a is the first nylon film 4
a, a second nylon film 6a, a gas barrier layer 5, and a heat-welding layer 7 are dry laminated, and two laminated films are three-sidedly sealed to form a bag.
Stretched nylon-6 is used for both the first and second nylon films 4a and 6a, and the thickness is 15 μm for the first nylon film 4a and 25 μm for the second nylon film 6a.
【００５９】芯材３の材料と、減圧及び熱溶着による製
造方法については、実施の形態１と同様である。 以上
のようにして得た真空断熱材１ａの振動試験を行い、試
験前後の熱伝導率とピンホールの有無を評価した。The material of the core material 3 and the manufacturing method by pressure reduction and heat welding are the same as those in the first embodiment. The vacuum heat insulating material 1a obtained as described above was subjected to a vibration test, and the thermal conductivity before and after the test and the presence or absence of pinholes were evaluated.
【００６０】試験に使用したフィルムの仕様と試験結果
を、実施例３および実施例４として表１に示す。The specifications of the films used in the test and the test results are shown in Table 1 as Example 3 and Example 4.
【００６１】（実施の形態３）図４は本発明の第３の実
施例における真空断熱材の要部断面図である。(Embodiment 3) FIG. 4 is a sectional view of the essential parts of a vacuum heat insulating material according to a third embodiment of the present invention.
【００６２】１ｂは真空断熱材であり、２ｂは外被材、
３は芯材である。1b is a vacuum heat insulating material, 2b is a jacket material,
3 is a core material.
【００６３】外被材２ｂは第１のナイロンフィルム４
ｂ、第２のナイロンフィルム６ｂ、ガスバリア層５、熱
溶着層７をドライラミネートしたフィルムであり、２枚
のラミネートフィルムを三方シールにて製袋しており、
第１と第２のナイロンフィルム４ｂ，６ｂにはいずれも
延伸されたナイロン−６を用いて、その厚さは第１のナ
イロンフィルム４ｂは１５μｍ、第２のナイロンフィル
ム６ｂは２５μｍであり、更に、第２のナイロンフィル
ム６ｂの外側にはアルミニウム蒸着５ｂが施してある。The outer cover material 2b is the first nylon film 4
b, the second nylon film 6b, the gas barrier layer 5, and the heat-welding layer 7 are dry laminated, and two laminated films are three-sided sealed to form a bag,
Stretched nylon-6 is used for both the first and second nylon films 4b and 6b, and the thickness is 15 μm for the first nylon film 4b and 25 μm for the second nylon film 6b. Aluminum vapor deposition 5b is applied to the outside of the second nylon film 6b.
【００６４】芯材３の材料と、減圧及び熱溶着による製
造方法については、実施の形態１と同様である。The material of the core material 3 and the manufacturing method by pressure reduction and heat welding are the same as those in the first embodiment.
【００６５】以上のようにして得た真空断熱材１ｂの振
動試験を行い、試験前後の熱伝導率とピンホールの有無
を評価した。The vacuum heat insulating material 1b thus obtained was subjected to a vibration test to evaluate the thermal conductivity before and after the test and the presence or absence of pinholes.
【００６６】試験に使用したフィルムの仕様と試験結果
を、実施例５および実施例６として表１に示す。なお、
表中のＶＭ−Ｎｙはアルミ蒸着ナイロンフィルムであ
る。The specifications of the films used in the test and the test results are shown in Table 1 as Example 5 and Example 6. In addition,
VM-Ny in the table is an aluminum vapor deposition nylon film.
【００６７】[0067]
【表１】 [Table 1]
【００６８】本発明の真空断熱材は、いずれにおいて
も、振動試験の後でも内側からの突き刺しによるピンホ
ールが生じることがなく、試験前の断熱性能を維持する
ことができた。以上のように、外被材のラミネート構成
を変更することによって、耐ピンホール性に優れた真空
断熱材を得ることができた。In any of the vacuum heat insulating materials of the present invention, pinholes due to piercing from the inside did not occur even after the vibration test, and the heat insulating performance before the test could be maintained. As described above, a vacuum heat insulating material having excellent pinhole resistance could be obtained by changing the laminate structure of the outer covering material.
【００６９】（実施の形態４）図５は本発明の第４の実
施例における冷蔵庫の本体部分の断面図である。(Fourth Embodiment) FIG. 5 is a sectional view of a main body portion of a refrigerator according to a fourth embodiment of the present invention.
【００７０】冷蔵庫本体８は、鋼板からなる外箱９と、
ＡＢＳ樹脂からなる内箱１０とで構成される空間の片面
に真空断熱材１を配設し、真空断熱材１以外の空間を硬
質ウレタンフォーム１１で発泡充填している。８ａは冷
蔵室、８ｂは冷凍室８である。また、１２は機械室で、
１３は圧縮機である。The refrigerator body 8 includes an outer box 9 made of a steel plate,
The vacuum heat insulating material 1 is arranged on one surface of the space formed by the inner box 10 made of ABS resin, and the space other than the vacuum heat insulating material 1 is foam-filled with the hard urethane foam 11. Reference numeral 8a is a refrigerating room, and 8b is a freezing room 8. 12 is a machine room,
Reference numeral 13 is a compressor.
【００７１】真空断熱材１は実施例１に示したものと同
様の構成であり、熱溶着部のひれ折りを行った上で設置
している。このように構成された冷蔵庫の消費電力量を
測定したところ、真空断熱材を装着しない冷蔵庫よりも
２０％低下しており、優れた断熱効果による省エネルギ
ーの達成を確認した。The vacuum heat insulating material 1 has the same structure as that shown in the first embodiment, and is installed after the heat-welded portion is folded. When the electric power consumption of the thus constructed refrigerator was measured, it was 20% lower than that of a refrigerator not equipped with a vacuum heat insulating material, and it was confirmed that energy saving was achieved by an excellent heat insulating effect.
【００７２】（比較例１）実施の形態２と比較するため
に、第２のナイロンフィルムを別の材料に変更してラミ
ネート構成を変えた外被材を使用した真空断熱材におい
て同様の試験を行った。COMPARATIVE EXAMPLE 1 In order to compare with the second embodiment, a similar test was conducted on a vacuum heat insulating material using an outer jacket material in which the second nylon film was changed to another material and the laminate constitution was changed. went.
【００７３】図６は本発明の比較例１における真空断熱
材の要部断面図である。FIG. 6 is a sectional view of a main part of the vacuum heat insulating material in Comparative Example 1 of the present invention.
【００７４】１ｃは真空断熱材であり、２ｃは外被材、
３は芯材である。1c is a vacuum heat insulating material, 2c is a jacket material,
3 is a core material.
【００７５】外被材２ｃは第１の保護層４ｃ、第２の保
護層６ｃ、ガスバリア層５、熱溶着層６をドライラミネ
ートしたフィルムであり、２枚のラミネートフィルムを
三方シールにて製袋しており、第１の保護層４ｃにはナ
イロン−６のフィルム、第２の保護層６ｃにはポリエチ
レンテレフタレートフィルム（ＰＥＴ）を用いている。The outer cover material 2c is a film obtained by dry laminating the first protective layer 4c, the second protective layer 6c, the gas barrier layer 5, and the heat-welding layer 6, and two laminated films are three-sided sealed to form a bag. Therefore, a nylon-6 film is used for the first protective layer 4c, and a polyethylene terephthalate film (PET) is used for the second protective layer 6c.
【００７６】芯材３の材料と、減圧及び熱溶着による製
造方法については、実施の形態１と同様である。The material of the core material 3 and the manufacturing method by pressure reduction and heat welding are the same as those in the first embodiment.
【００７７】以上のようにして得た真空断熱材１ｃの振
動試験を行い、試験前後の熱伝導率とピンホールの有無
を評価した。The vacuum heat insulating material 1c obtained as described above was subjected to a vibration test, and the thermal conductivity before and after the test and the presence or absence of pinholes were evaluated.
【００７８】試験に使用したフィルムの仕様と試験結果
を、比較例１、比較例２、および比較例３として表２に
示す。なお、表中の熱溶着層としてのＨＤＰＥは高密度
ポリエチレンフィルムである。The specifications of the film used in the test and the test results are shown in Table 2 as Comparative Example 1, Comparative Example 2 and Comparative Example 3. HDPE as the heat-welding layer in the table is a high-density polyethylene film.
【００７９】（比較例２）図７は本発明の比較例２にお
ける真空断熱材の要部断面図である。(Comparative Example 2) FIG. 7 is a sectional view of a main part of a vacuum heat insulating material in Comparative Example 2 of the present invention.
【００８０】１ｄは真空断熱材であり、２ｄは外被材、
３は芯材である。1d is a vacuum heat insulating material, 2d is a jacket material,
3 is a core material.
【００８１】外被材２ｄは保護層４ｄ、ガスバリア層
５、熱溶着層６をドライラミネートしたフィルムであ
り、２枚のラミネートフィルムを三方シールにて製袋し
ており、保護層４にはポリエチレンテレフタレートフィ
ルム（ＰＥＴ）を用いている。The outer covering material 2d is a film obtained by dry laminating the protective layer 4d, the gas barrier layer 5 and the heat-welding layer 6, and two laminated films are formed into a bag by three-way sealing. A terephthalate film (PET) is used.
【００８２】芯材３の材料と、減圧及び熱溶着による製
造方法については、実施例１と同様である。The material of the core material 3 and the manufacturing method by pressure reduction and heat welding are the same as in the first embodiment.
【００８３】以上のようにして得た真空断熱材１ｄの振
動試験を行い、試験前後の熱伝導率とピンホールの有無
を評価した。The vacuum heat insulating material 1d thus obtained was subjected to a vibration test to evaluate the thermal conductivity and the presence or absence of pinholes before and after the test.
【００８４】試験に使用したフィルムの仕様と試験結果
を、比較例４、比較例５、および比較例６として表２に
示す。The specifications of the films used in the test and the test results are shown in Table 2 as Comparative Example 4, Comparative Example 5 and Comparative Example 6.
【００８５】[0085]
【表２】 [Table 2]
【００８６】真空断熱材のいずれの比較例においても、
振動試験によって内側からの突き刺しによるピンホール
が認められた。ナイロンフィルムを１層使用した場合
（比較例１）は、ナイロンフィルムを使用しなかった場
合（比較例２）に比べ、断熱性能の劣化は大きくなかっ
たが、生じたピンホールからのガス侵入により初期の断
熱性能を維持することはできなかった。In all the comparative examples of the vacuum heat insulating material,
A vibration test revealed a pinhole due to a piercing from the inside. When one layer of nylon film was used (Comparative Example 1), the heat insulation performance was not significantly deteriorated as compared with the case where no nylon film was used (Comparative Example 2), but due to gas intrusion from the generated pinhole. It was not possible to maintain the initial heat insulation performance.
【００８７】（比較例３）比較例１に用いた図６の外被
材と同じ仕様で、真空断熱材の密度が１４０ｋｇ／ｍ3
になるように成形した芯材を使用して同様の試験を行っ
た。(Comparative Example 3) With the same specifications as the jacket material of FIG. 6 used in Comparative Example 1, the vacuum heat insulating material has a density of 140 kg / m 3.
A similar test was conducted using a core material molded so that
【００８８】この仕様ではピンホールが発生せず、断熱
性能の低下も見られなかった。芯材の密度が低かったた
めと考えられる。According to this specification, no pinhole was generated and the heat insulating performance was not deteriorated. It is considered that the density of the core material was low.
【００８９】すなわち、芯材の密度が低い場合において
は、ナイロンフィルム層が１層である外被材でもピンホ
ールの発生を防ぐことができることから、密度が高い場
合においてこの発明の外被材の仕様が効果的であるとわ
かった。That is, when the density of the core material is low, the occurrence of pinholes can be prevented even with an outer jacket material having one nylon film layer. Therefore, when the density is high, the outer jacket material of the present invention can be used. The specification turned out to be effective.
【００９０】[0090]
【発明の効果】本発明は、芯材と、ラミネートで構成さ
れた外被材とを備え、前記芯材が無機繊維を成形したボ
ード状であり、前記外被材のラミネート構成が、外側か
ら順に、第１の延伸ナイロンフィルム、第２の延伸ナイ
ロンフィルム、金属箔からなるガスバリア層、熱溶着層
であり、前記第１、第２の延伸ナイロンフィルム間に接
着層があり、かつ密度が１５０ｋｇ／ｍ３以上であるこ
とを特徴とする真空断熱材である。The present invention comprises a core material and a laminate.
An outer cover material, wherein the core material is a board-shaped molded inorganic fiber , and the laminated structure of the outer cover material is outside.
In order from the first stretched nylon film, the second stretched nylon film
Ron film, gas barrier layer made of metal foil, heat welding layer
And between the first and second stretched nylon films
It has a layer and has a density of 150 kg / m3 or more.
It is a vacuum heat insulating material characterized by .
【００９１】耐突き刺し性に優れたフィルムであるナイ
ロンフィルムを外被材に２層以上ラミネートすることに
よって、真空断熱材の芯材として無機繊維を成形したボ
ード状芯材のように成形時に折れて鋭くなった繊維が表
面に存在し、かつ表面硬度が大きい芯材を使用した場合
や、その芯材のサイズや重量が冷蔵庫用のように大きく
なった場合においても、ピンホールの発生を防ぐことが
できる。By laminating two or more layers of a nylon film, which is a film having excellent puncture resistance, on the outer covering material, it is possible to fold at the time of forming like a board-shaped core material formed by molding inorganic fibers as a core material of a vacuum heat insulating material. Prevents pinholes from occurring even when a core material with sharp fibers is present on the surface and the surface hardness is large, or when the size and weight of the core material becomes large as in a refrigerator. You can
【００９２】[0092]
【００９３】芯材の密度が大きくなり、重量や硬度が大
きくなった場合においても、延伸ナイロンフィルムを使
用することでさらに耐突き刺し性が上がるために、硬
度、サイズ、重量など条件が厳しくなった場合でもピン
ホールの発生を防ぐことができる。Even when the density of the core material is increased and the weight and hardness are increased, the piercing resistance is further improved by using the stretched nylon film, so that the conditions such as hardness, size and weight become severe. Even in the case, it is possible to prevent the occurrence of pinholes.
【００９４】[0094]
【００９５】[0095]
【００９６】[0096]
【００９７】外被材のガスバリア層の外側にナイロンフ
ィルムを２層以上ラミネートすることによって、耐突き
刺し性を向上させるとともに、もっともガス侵入が多い
とされるシール層端部の断面の厚さを増やすことがない
ために、冷蔵庫用真空断熱材のようにサイズが大きくな
った場合でも、外被材のガスバリア性を保持することが
できる。また、ナイロンフィルム層を重ねることによっ
て、ナイロンフィルム間のドライラミネート層による力
の緩和が起こるために、ナイロンフィルムを１層にして
厚みを増した場合よりも突き刺しに対して強度が上が
る。By laminating two or more layers of nylon film on the outer side of the gas barrier layer of the outer covering material, the puncture resistance is improved and the thickness of the cross section of the end portion of the seal layer, which is considered to have the most gas intrusion, is increased. Therefore, even if the size of the vacuum heat insulating material for a refrigerator is increased, the gas barrier property of the outer covering material can be maintained. Further, by stacking the nylon film layers, the force is relaxed by the dry laminate layer between the nylon films, so that the strength against piercing is higher than in the case where the thickness of the nylon film is increased to one layer.
【００９８】本発明は、外被材のラミネート構成が、外
側から順に、第１のナイロンフィルム、第２のナイロン
フィルム、ガスバリア層、熱融着層の順であることに加
え、少なくとも、第１のナイロンフィルムの内側、また
は、第２のナイロンフィルムの外側に蒸着を施したこと
を特徴とする真空断熱材である。According to the present invention, in addition to the laminated constitution of the outer covering material, in order from the outside, the first nylon film, the second nylon film, the gas barrier layer and the heat fusion layer, and at least the first nylon film. The vacuum heat insulating material is characterized in that vapor deposition is applied to the inside of the nylon film or the outside of the second nylon film.
【００９９】外被材のガスバリア層の外側にナイロンフ
ィルムを２層以上ラミネートすることによって、耐突き
刺し性を向上させるとともに、もっともガス侵入が多い
とされるシール層端部の断面の厚さを増やすことがない
ために、真空断熱材のサイズが、冷蔵庫用途のように大
きくなった場合においても外被材のガスバリア性を保持
することができることに加え、外被材の内側からの突き
刺しによって熱溶着層およびガスバリア層にピンホール
が生じた場合でも、ナイロンフィルムに施した蒸着によ
り、ガスの透過を押さえることができる。By laminating two or more layers of nylon film on the outside of the gas barrier layer of the jacket material, the puncture resistance is improved and the thickness of the cross section of the end portion of the seal layer, which is considered to be the most gas invading, is increased. Therefore, even if the size of the vacuum heat insulating material is increased as in the case of refrigerators, the gas barrier property of the outer covering material can be maintained, and the heat welding by piercing from the inside of the outer covering material is performed. Even if pinholes are formed in the layer and the gas barrier layer, vapor permeation applied to the nylon film can suppress gas permeation.
【０１００】なお、いずれの発明においても、それが真
空断熱材の片面の外被材だけへの適用であっても、少な
くともその面は同様の効果を有する真空断熱材が得られ
る。In any of the inventions, even if it is applied to only one surface of the vacuum heat insulating material, a vacuum heat insulating material having the same effect on at least that surface can be obtained.
【０１０１】本発明は、上記発明のいずれかの真空断熱
材を使用した冷蔵庫である。The present invention is a refrigerator using the vacuum heat insulating material according to any one of the above inventions.
【０１０２】無機繊維をボード化した芯材を用いた真空
断熱材を冷蔵庫に適用する場合、芯材の硬度に加え、一
枚あたりのサイズや重量が大きくなるために、ピンホー
ル発生のリスクが非常に高くなるが、本発明の真空断熱
材によって、耐ピンホール性に優れ、長期信頼性に優れ
た真空断熱材を得ることができるため、真空断熱材を外
箱と内箱とからなる空間に配置し、残りの空間に発泡断
熱材を充填することにより、断熱性能に優れた省エネル
ギーの冷蔵庫を提供することができる。When a vacuum heat insulating material using a core material in which inorganic fiber is made into a board is applied to a refrigerator, the size and weight per sheet are increased in addition to the hardness of the core material, so that there is a risk of pinholes. Although it is extremely high, the vacuum heat insulating material of the present invention can provide a vacuum heat insulating material having excellent pinhole resistance and long-term reliability. Therefore, the vacuum heat insulating material is a space formed by an outer box and an inner box. It is possible to provide an energy-saving refrigerator excellent in heat insulating performance by arranging the same in a space and filling the remaining space with a foamed heat insulating material.
【図１】本発明の第１の実施例における真空断熱材の断
面図FIG. 1 is a sectional view of a vacuum heat insulating material according to a first embodiment of the present invention.
【図２】本発明の第１の実施例における真空断熱材の要
部断面図FIG. 2 is a sectional view of a main part of a vacuum heat insulating material according to the first embodiment of the present invention.
【図３】本発明の第２の実施例における真空断熱材の要
部断面図FIG. 3 is a sectional view of a main part of a vacuum heat insulating material according to a second embodiment of the present invention.
【図４】本発明の第３の実施例における真空断熱材の要
部断面図FIG. 4 is a sectional view of a main part of a vacuum heat insulating material according to a third embodiment of the present invention.
【図５】本発明の第４の実施例における冷蔵庫の本体部
分の断面図FIG. 5 is a sectional view of a main body portion of a refrigerator according to a fourth embodiment of the present invention.
【図６】本発明の比較例１における真空断熱材の要部断
面図FIG. 6 is a sectional view of a main part of a vacuum heat insulating material according to Comparative Example 1 of the present invention.
【図７】本発明の比較例２における真空断熱材の要部断
面図FIG. 7 is a sectional view of a main part of a vacuum heat insulating material according to Comparative Example 2 of the present invention.
１，１ａ，１ｂ 真空断熱材 ２，２ａ，２ｂ 外被材 ３ 芯材 ４，４ａ，４ｂ 第１のナイロンフィルム ５ ガスバリア層 ５ｂ 蒸着 ６，６ａ，６ｂ 第２のナイロンフィルム ７ 熱溶着層 ８ 冷蔵庫 ９ 外箱 １０ 内箱 1,1a, 1b Vacuum insulation 2,2a, 2b jacket material 3 core material 4,4a, 4b The first nylon film 5 gas barrier layer 5b evaporation 6,6a, 6b Second nylon film 7 Heat welding layer 8 refrigerator 9 outer box 10 inner box
Claims (3)
とを備え、前記芯材が無機繊維を成形したボード状であ
り、前記外被材のラミネート構成が、外側から順に、第
１の延伸ナイロンフィルム、第２の延伸ナイロンフィル
ム、金属箔からなるガスバリア層、熱溶着層であり、前
記第１、第２の延伸ナイロンフィルム間に接着層があ
り、かつ密度が１５０ｋｇ／ｍ３以上であることを特徴
とする真空断熱材。1. A core material and an outer jacket material formed of a laminate, wherein the core material is a board-like molded inorganic fiber, and the outer jacket material is laminated in order from the outside.
1st stretched nylon film, 2nd stretched nylon film
A gas barrier layer made of metal, a metal foil, and a heat welding layer.
There is an adhesive layer between the first and second stretched nylon films.
And a density of 150 kg / m3 or more, a vacuum heat insulating material.
内側、または、第２のナイロンフィルムの外側に蒸着を
施したことを特徴とする請求項１記載の真空断熱材。Wherein at least the inner first nylon film or a vacuum heat insulator of claim 1, wherein the subjected to evaporation to the outside of the second nylon film.
よって形成される空間に充填された発泡断熱材とを有
し、前記空間内において、前記外箱または前記内箱のい
ずれか一方の壁面に請求項１または請求項２記載の真空
断熱材を配設したことを特徴とする真空断熱材を使用し
た冷蔵庫。3. An outer box, an inner box, and a foam heat insulating material filled in a space formed by the outer box and the inner box, wherein the outer box or the inner box is filled with the foamed heat insulating material. A refrigerator using a vacuum heat insulating material, characterized in that the vacuum heat insulating material according to claim 1 or 2 is disposed on one of the wall surfaces.