JP2552630B2 - Cement manufacturing method - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention burns the waste of products made of materials such as pachinko machines, slot machines, wood, metals, plastics, etc., and burns heavy oil or coal during cement production. The present invention relates to a resource-saving type cement manufacturing technology that suppresses the consumption of the main fuel of.

[0002]

2. Description of the Related Art A gaming machine such as a pachinko gaming machine or a slot machine has a rapid change in user's preference. Therefore, on the amusement hall side, a pachinko gaming machine or a slot machine is often replaced with a new type. ing. The pachinko game machines and slot machines that have been replaced are not used for reuse, are difficult to dismantle, and are in trouble for disposal.

[0003]

By the way, the disposal of the pachinko gaming machine and the slot machine is either to stack and store at a specific place or to simply incinerate. However, since the amount of discarded pachinko machines and slot machines is enormous, it is difficult to secure a stacking storage place.

Further, it is not easy to incinerate. In other words, even if it is incinerated, the incinerated ash must be finally landfilled, which causes a problem of landfill. Also, the iron used in pachinko machines and slot machines is incinerated once, and if an oxide film or soot adheres to the surface, the commercial value as scrap is significantly reduced, and iron after incineration is also landfilled. is the current situation.

Further, there is a concern that chlorine-containing wires contained in the waste will generate dioxin due to chlorine. Therefore, wood, metal, such as pachinko machines and slot machines,
It is an object of the present invention to provide an effective treatment technology for waste products that are made of materials such as plastic.

[0006] In particular, it is an object of the present invention to provide a technique which makes effective use of waste such as pachinko game machines and slot machines compatible with resource saving, and which is useful for preventing environmental destruction due to landfilling. Further, it is another object of the present invention to provide an effective technique that does not cause an operation failure of a rotary kiln or a calcining furnace when effectively utilizing wastes such as a pachinko game machine and a slot machine for cement production.

[0007]

[Means for Solving the Problems] That is, even if waste such as a pachinko gaming machine or a slot machine is incinerated, if it is used together with a main fuel such as heavy oil or coal at the time of cement production, Resources can be saved. However, it has been found that various problems occur when these waste materials are simply burned in a rotary kiln or a calcining furnace in a cement manufacturing apparatus.

First, in order to burn in a rotary kiln or a calcining furnace, metal components such as nails used in pachinko game machines, slot machines, etc. became a problem. That is, these metals have a great influence on the chemical composition of the cement, and it was necessary to remove the metal components prior to combustion. For that purpose, it is necessary to crush the product body.

By the way, after crushing, the metal content is removed,
When this crushed piece is put into a rotary kiln or a calcining furnace, scattering of the crushed product causes ventilation obstacles in the kiln, and the kiln is not completely burned and scattered upstream. And, if the combustion is continued as it is, the danger of deterioration of the combustion efficiency and the trouble of adhesion of the bank becomes extremely high. Therefore, as a result of earnestly conducting research on this point, that is, as a result of earnestly researching what should be considered in order to prevent the above problems from occurring, pachinko machines and slot machines. The present invention has been achieved by the finding that the problem can be solved by considering the size when crushed and the incineration input site of the cement manufacturing apparatus.

That is, the object of the present invention is to provide a cement production method for effectively utilizing cement in the production of cement by burning the waste of a product constructed by using materials such as wood, metal and plastic. A crushing process for crushing the crushed product, a removal process for removing the metal component from the crushed product, and a burning process for removing the metal component and introducing a crushed piece having a size of 13 to 30 mm into the rotary kiln inlet of the cement manufacturing apparatus and burning it. And a cement manufacturing method.

Further, a pachinko game machine and / or a slot formed by using a material such as wood, metal, or plastic.
A cement manufacturing method for effectively utilizing for cement production by burning waste of machine products, a crushing step of crushing the waste, a removal step of removing a metal content from the crushed material, and a metal content being removed, The method for producing cement is characterized in that a crushed piece having a maximum size of 6 mm is charged into a position of a rotary kiln burner in a cement manufacturing apparatus and is burned.

Further, there is provided a cement production method for effectively utilizing cement in the production of cement by burning the waste of a product made of wood, metal, plastic or the like, which comprises a crushing step of crushing the waste. , A metal removal process for removing metal from the crushed material, and a combustion process for removing metal and removing a crushed piece having a maximum size of 6 mm into a rising duct or a calcination furnace in a cement manufacturing apparatus and burning it. It is achieved by a method for producing cement.

Further, there is provided a cement manufacturing method for burning waste of a product made of a material such as wood, metal, plastic or the like to effectively utilize it for cement production, which comprises a crushing step of crushing the waste. , A metal removal step for removing metal from the crushed material, and a combustion step for removing the metal content and charging a crushed piece having a maximum size of 1 mm at the position of the calciner burner in the cement manufacturing apparatus and burning it. It is achieved by a method for producing cement.

By the way, a method of crushing a product waste made of materials such as wood, metal, and plastic, and throwing it into a rotary kiln for cement firing, a rising duct, or a calcination furnace, and burning it as it is I have been talking about. For example, it has been described that crushed pieces having a size of 13 to 30 mm are put into a rotary kiln inlet of a cement manufacturing apparatus and burned in pieces. However, the mesh width of shredding equipment such as shredder is 1
Even when it was crushed after being adjusted to 3 to 30 mm and burned, sometimes the operation was not good. For example, depending on the degree of crushing of the product, even if the mesh width is 20 mm, if the product is a material that is easily crushed, the stable operation of the kiln may be adversely affected. In other words, the ratio of being blown up to the rising duct is usually 1% or less, but sometimes it is about 15%. In such a case, the blown-up crushed pieces partially drop and are also blown up and circulate, causing hunting of the entire kiln system.

In view of the above, in the case of charging at the inlet of the rotary kiln and burning it, the following means have been considered. First, we tried to make the crushing of wood constant by adjusting the size of the sieve mesh and the crusher. For example,
The larger the mesh width, the smaller the amount of fine powder in the crushed product.
However, in this case, large debris are mixed in, which hinders pneumatic transportation.

The fine powder can be removed by passing it through a classifying device such as a sieve or an air classifier, but the removed fine powder needs to be combusted at another combustion place, not at the rotary kiln inlet. In this method, the rotary kiln inlet is used. It is not possible to carry out combustion processing by itself. In addition, the equipment cost and running cost are naturally high. Therefore, in order to stably burn the composite structure at the inlet of the rotary kiln, it is necessary to consider a measure that prevents fine powder from rising.

As the method, it was considered to insert the nozzle into the rotary kiln as deeply as possible and to inject it into the rotary kiln so that the raw material is dipped into the raw material. However, in this method, the temperature in the vicinity of the charging port is as high as 900 to 1100 ° C., and therefore the deterioration of the injection nozzle is rapid. Also, when the nozzle is inserted deep into the kiln, it is often damaged due to the coating that occasionally drops. Therefore, it was not possible to adopt such a means.

[0018] Therefore, as a result of further studies, the fine powder is packed in a flammable bag such as paper or plastic so that the fine powder may be caught in the raw material before it is thrown into the kiln inlet. Thought. And this was tried. The experiment is 20 liters (or less
Bottom, liter is indicated by L. ) The crushed product was packed in a paper bag of ) , and it was thrown into the rotary kiln entrance intermittently.
As a result, it was confirmed that the rotary kiln can be continuously charged without disturbing the stable state. The feeding interval is better for maintaining the stable state of the rotary kiln for a small bag close to continuous feeding, but if it is too small, combustion of the bag itself is completed quickly and eventually fine powder is blown up to the rising duct. , Cause hunting,
High cost in the bag filling process. On the contrary, if the size of the bag is increased, the cost for the bag filling process can be suppressed, but the interval for charging the inlet of the rotary kiln becomes large, which becomes an obstacle to the stability of the kiln system. As a result of research, bags with a size of 1 to 50 L, preferably 5 to 30 L are used, and 100 m
When the crushed product crushed to a size of m or less was packed, charged into the rotary kiln inlet and burned, it was possible to burn continuously without impairing the stability of the rotary kiln. In this method, since it is not necessary to carry out pneumatic transportation, the size of the crushed product may be large as long as it can be packed in a bag. However, in order to remove the metal that affects the cement component, it was preferable to be crushed to a size of 100 mm or less.

Attempts have also been made to solidify instead of bagging. That is, in order to remove the metal that affects the cement component, it was crushed to a size of 100 mm or less and then solidified. For example, after crushing to a size of 100 mm or less, the plastic contained therein was heated to a temperature above the temperature at which it softened and melted, and the volume was reduced and solidified. According to this method, the bulk density after solidification increases 2.5 to 3 times, and even if the bulk density is the same, it is difficult to blow up in the air stream. Moreover, since the mass is 4 to 7 times, even if the size is 4 to 1/7, it is not blown up if the airflow velocity is the same. For example, the size is 5m
Even a thing about m was not blown up. It can be said that the maximum size when solidified is to burn out in the rotary kiln, but it is preferable to burn out at a position of about two-thirds of the effective length of the rotary kiln for effective heat utilization. From this point of view, it is preferable that the size be about 300 mm. More preferably 2
It was up to about 50 mm, more preferably about 200 mm.

From the above knowledge, the object of the present invention is a cement production method for effectively utilizing cement for the production of cement by burning the waste of the product made of materials such as wood, metal and plastic. Then, a crushing step of crushing the waste, a step of removing metal from the crushed material, and a crushed piece having a maximum size of 100 mm from which the metal is removed are packed in a bag of 1 to 50 L in size. , Put this bag into the rotary kiln entrance in the cement manufacturing equipment,
And a burning step of burning the cement.

[0021] Further, there is provided a cement manufacturing method for combusting waste of a product constituted by using materials such as wood, metal and plastic to effectively utilize for cement production, and a crushing step of crushing the waste. , Removal process to remove metal from crushed material, and maximum 100mm after metal removal
It is also achieved by a cement manufacturing method, characterized in that a crushed piece having a size of 5 to 300 mm is solidified to a volume of 5 to 300 mm, and the solidified product is put into a rotary kiln inlet of a cement manufacturing apparatus and burned. It

Further, according to the present invention as described above, the waste of the product constituted by using the material such as the pachinko machine, the slot machine, the wood, the metal, the plastic, etc. can be effectively treated. Become. In particular, both effective use of waste such as pachinko machines and slot machines and resource saving are compatible, and it is also useful for environmental conservation. It should be noted that generation of dioxin due to chlorine from the PVC-covered wire contained in the waste is not a concern because the combustion temperature is 860 ° C or higher. Further, when the wastes of the pachinko game machine and the slot machine are effectively used for cement production, the operation failure of the rotary kiln and the calcining furnace is not caused.

The present invention will be described below with reference to specific examples.

[0024]

1 to 5 show an embodiment of the present invention. FIG. 1 is a schematic view of a cement manufacturing apparatus, and FIGS. 2 to 5 are sizes of crushed materials to be put into a combustion means of the cement manufacturing apparatus. It is a graph which shows the height. In FIG. 1, 1 is a receiving hopper that receives waste products such as pachinko game machines and slot machines, 2 is a receiving crusher, 3 is a crusher, 4 is a metal removing machine, 5
Is a classifier, 6 is a storage hopper, 7 is a volume reducing and solidifying machine or a container filling machine, 8 is a quantitative feeder, 9 is a rotary kiln,
Reference numeral 10 is a calcination furnace, 11 is a duct, 12 is a cooler, 13 is a heat exchange stage, 14 is a main burner, and 15 is an auxiliary burner.

Then, a composite structure made of a material such as wood, metal or plastic such as a pachinko game machine or a slot machine carried by a truck is put into the receiving hopper 1. Then, if necessary, the crusher 2 such as a biaxial crusher receives and crushes. The maximum size of the receiving crusher 2 is about 500 mm. Then, it is crushed to a size of 100 mm or less by a crusher 3 equipped with a shear crusher such as a shredder with a rustle.

After that, the metal removing machine 4 removes iron and other non-ferrous metals. Next, secondary crushing is performed by the crusher 3 if necessary. After the secondary crushing, the metal removing machine 4 removes the metal as much as possible. The secondary crushed product is stored in the storage hopper 6 as it is or after the particle size is adjusted to a required particle size by the classifier 5. In the case of charging in bulk from here, it is directly sent to the rotary kiln 9 or the calcination furnace 10 via the constant quantity feeder 8. In this case, when air transportation is performed, the blown nozzle is cooled by the carrier air, and it is possible to prevent burnout of the nozzle and backfire due to combustion of crushed products in the nozzle.

Another route is to reduce the volume of the crushed product and solidify it. The volume-reducing and solidifying machine 7 may be one that uses frictional heat, one that applies heat from the outside, etc. The point is to add a crushed product of a composite structure such as a pachinko gaming machine from the plastic contained in it or from the outside. Melting of plastics,
Any material can be used as long as it can be solidified by softening. Then, the volume-solidified crushed product is put into the rotary kiln 9 via the constant quantity feeder 8. Also, instead of reducing the volume and solidifying, it may be packed in a container such as a paper bag.

Next, the size of the crushed product and the place where the crushed product is put will be described. These relationships have been clarified for the first time by the present inventor.
First, the case where the pieces are thrown into the rotary kiln 9 at the entrance will be described. It is necessary to put the crushed product into the rotary kiln 9 and burn it. Crushed product is rotary kiln 9
If you climb up to the duct 11 that goes from the rotary kiln 9 to the calcining furnace 10 without entering, the airflow in the duct 11 rides toward the calcining furnace 10. Since the air flow in the duct 11 is not uniform, a part of it circulates. Draft fluctuations in the duct 11 occur, and finally fluctuations (hunting) occur from the rotary kiln 9 to the calcining furnace 10, which becomes a factor that hinders safe operation.

Therefore, it is preferable that the charge to the inlet of the rotary kiln 9 is as large as possible. However, when it is charged, it is necessary to make it large enough to allow pneumatic transportation because pneumatic transportation is effective. Therefore,
When an experiment was conducted on the relationship between pneumatic transportation and crushed products, the results shown in Fig. 2 were obtained. When pneumatically transported, the flow velocity in the duct 11 is usually 20 m / s or less, so the maximum diameter of the crushed product is 30 mm or less for plastic and 35 for wood.
It can be seen that it is preferable that the thickness is less than or equal to mm. Further, the state of soaring at the entrance of the rotary kiln 9 was the result shown in FIG. It can be seen that if the plastic is 11 mm or more and the wood is 13 mm or more, almost no scattering occurs.

That is, when the crushed product is charged from the inlet of the rotary kiln 9 and burned, it is necessary to have a size of 13 to 30 mm. A case where the calcination furnace 10 is charged separately will be described. When charging into the calcination furnace 10, unlike in the case of charging into the rotary kiln 9, it is necessary to burn the entire amount in the calcination furnace 10 so as not to drop to the rotary kiln 9 side. As described above, this is the duct 11 from the rotary kiln 9 to the calciner 10.
This is because when the crushed product circulates inside, hunting occurs in the entire system. Therefore, from Figure 3, the plastic is 6m
It can be seen that if m or less and wood is 7 mm or less, almost no fall occurs.

That is, the crushed product is treated with the rising duct 11
Alternatively, when it is put into the calcination furnace 10 and burned, it is necessary to have a size of 6 mm at the maximum. The size is preferably 5 mm at the maximum. Next, the case of burning in the same manner as coal or heavy oil which is the main fuel in a rotary kiln or a calciner burner will be described. In this case, the crushed product must have a burning rate equivalent to that of the main fuel. FIG. 4 shows a comparison of burning rates for wood and plastic among coal and crushed products. As is clear from FIG. 4, it was found that wood and plastic have a higher burning rate than coal, and a small specific surface area is required to obtain the same burning rate. Here, FIG. 5 shows the results of determining the sizes of wood and plastic for obtaining the same burning time as coal. It should be noted that the coal was based on an average diameter of 30 μm when pulverized coal used as fuel was used. Further, it is assumed that the plastic is crushed into squares with a thickness of 2 mm and the wood has a columnar shape.

The temperature in the kiln burner 14 is 1400 to
It was 1600 ° C., and it was found that wood should be crushed to 3 to 4 mm and plastic to 4 to 5 mm. Therefore,
The secondary crusher may be crushed with a mesh width of 4 to 5 mm and a maximum of 6 mm. The temperature in the calciner burner 15 is 800
Since it is ~ 1000 ° C, wood is 0.25-0.8m
m, plastic may be crushed to 1.5 to 2.2 mm. Therefore, the mesh width of the crusher is 0.5 mm, and the maximum is 1 m.
It may be crushed to about m.

The classifying device 5 may be used instead of changing the mesh width. In addition, 100 mm with metal removed
The crushed pieces having the following sizes were packed in a bag having a size of 1 to 50 L, and this bag was put into the inlet of the rotary kiln in the cement manufacturing apparatus and burned. Further, the crushed pieces having a size of 100 mm or less from which the metal content was removed were solidified by reducing the volume to 5 to 300 mm, and the solidified product was put into the rotary kiln inlet of the cement manufacturing apparatus and burned.

As a result, good results were obtained.
The present invention can also be implemented in a rotary kiln for cement firing of the type shown in FIGS.

[0035]

[Effect] According to the present invention, it becomes possible to burn wastes such as pachinko game machines and slot machines which are difficult to dispose in a cement rotary kiln or a calcination furnace. In particular, the operation failure of the rotary kiln and calcination furnace is not caused. Further, since the incinerated ash generated is taken into the cement, the waste can be recycled. As a result, the amount of landfill waste can be reduced, which is also useful for environmental protection.

In addition, a part of the calorific value of cement burning can be substituted, which can contribute to resource saving.

[Brief description of drawings]

FIG. 1 is a schematic view of a cement manufacturing apparatus according to the present invention.

FIG. 2 is a graph showing the size of the crushed material that is put into the combustion means of the cement manufacturing device.

FIG. 3 is a graph showing the size of the crushed material to be put into the combustion means of the cement manufacturing device.

FIG. 4 is a graph showing the size of the crushed material to be injected into the combustion means of the cement manufacturing device.

FIG. 5 is a graph showing the size of the crushed material to be put into the combustion means of the cement manufacturing device.

[Fig. 6] Schematic diagram of rotary kiln for burning cement

[Figure 7] Schematic diagram of rotary kiln for cement firing

FIG. 8: Schematic diagram of rotary kiln for cement burning

FIG. 9: Schematic diagram of rotary kiln for cement burning

[Explanation of symbols]

 1 Receiving hopper 2 Receiving crusher 3 Crusher 4 Metal removing machine 5 Classifying device 8 Quantitative feeder 9 Rotary kiln 10 Calcination furnace 11 Duct 14 Main burner 15 Auxiliary burner

Continuation of front page (56) References JP-A-55-53622 (JP, A) JP-B-57-17867 (JP, B2)

Claims (6)

(57) [Claims] 1. A cement manufacturing method for burning waste of a product made of a material such as wood, metal, or plastic to effectively utilize it for cement production, which comprises a crushing step of crushing the waste. , The metal content from the crushed material
Removal process and metal parts are removed,
The crushed pieces with a size of mm are
A method for producing cement, comprising a combustion step of charging the tarry kiln at the inlet and burning it . 2. A cement manufacturing method for effectively utilizing cement for the production of cement by burning the waste of a product made of a material such as wood, metal or plastic, which comprises a crushing step of crushing the waste. , The metal content from the crushed material
The removal process and the maximum removal of metal are 10
1 mm to 50 liters of crushed pieces with a size of 0 mm
It is packed in a bag, and this bag is then
A method for producing cement, comprising a combustion step of charging at the kiln inlet and burning . 3. A cement production method for effectively utilizing cement in the production of cement by burning the waste of a product made of a material such as wood, metal or plastic, which comprises a crushing step of crushing the waste. , The metal content from the crushed material
The removal process and the maximum removal of metal are 10
Solidified volume reduction of crushed pieces of 0 mm to 5 to 300 mm
Then, the solidified product is used as a rotary in the cement manufacturing equipment.
A method for producing cement , which comprises a combustion process of charging the kiln at an inlet and burning it . 4. A pachinko gaming machine and / or slot machine configured using a material such as wood, metal, or plastic.
A method for producing cement, in which waste of thin products is burned for effective use in cement production, comprising a crushing step of crushing the waste, and a metal content from the crushed material.
Removal process and metal parts are removed, the maximum is 6m
you Keru rotor the size of the crushed pieces of m to cement manufacturing equipment
A combustion engineer that puts it in the position of the re-kiln burner and burns it.
A method for producing cement, which comprises: 5. A method for producing cement, which comprises effectively burning a waste product, which is made of a material such as wood, metal, or plastic, to produce a cement , and a crushing step of crushing the waste product. , The metal content from the crushed material
Removal process and metal parts are removed, the maximum is 6m
crushed pieces of m size in cement production equipment
Combustion work in which it is placed in a cooling duct or a calcination furnace and burned
A method for producing cement, which comprises: 6. A method for producing cement, which comprises effectively burning a waste product, which is made of a material such as wood, metal, or plastic, to produce a cement, which comprises crushing the waste. , The metal content from the crushed material
Removal process and metal parts are removed, maximum is 1m
A calcination furnace for cement production equipment
A method for producing cement, comprising a burning step of charging the burner at the position of a burner and burning it .