JP2023005273A - hair treatment agent - Google Patents
hair treatment agent Download PDFInfo
- Publication number
- JP2023005273A JP2023005273A JP2021107064A JP2021107064A JP2023005273A JP 2023005273 A JP2023005273 A JP 2023005273A JP 2021107064 A JP2021107064 A JP 2021107064A JP 2021107064 A JP2021107064 A JP 2021107064A JP 2023005273 A JP2023005273 A JP 2023005273A
- Authority
- JP
- Japan
- Prior art keywords
- hair
- agent
- treatment agent
- mass
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は毛髪処理剤に関する。 The present invention relates to hair treatment agents.
毛髪にすべり、しなやかさ、まとまり感などを付与する目的で、従来からヘアリンスやヘアトリートメントなどが使用されている。一般的にヘアリンスやヘアトリートメントは、カチオン性界面活性剤、油剤、シリコーン誘導体、タンパク質加水分解物などのコンディショニング成分を含有し、これらの成分が毛髪表面に吸着することにより、コンディショニング効果を発揮させていた。 Hair rinses, hair treatments, and the like have been conventionally used for the purpose of imparting slipperiness, suppleness, manageability, and the like to hair. In general, hair rinses and hair treatments contain conditioning ingredients such as cationic surfactants, oils, silicone derivatives, and protein hydrolysates, and these ingredients adsorb to the hair surface to exert their conditioning effects. rice field.
しかしながら、従来のヘアリンスやヘアトリートメントは、ヘアカラー、パーマを繰り返した毛髪に対するコンディショニング効果が弱く、またシャンプーによってコンディショニング効果が失われやすかった。 However, conventional hair rinses and hair treatments have a weak conditioning effect on hair that has been repeatedly colored and permed, and the conditioning effect tends to be lost by shampooing.
ヘアカラーやパーマなどの処理を行った毛髪に対するコンディショニング効果の向上、およびコンディショニング効果の持続性を高める技術として、アニオン性物質（ポリマー、タンパク質加水分解物など）とカチオン性物質（ポリマー、界面活性剤など）とを組み合わせるなどして毛髪にイオン性のコンプレックスを形成する技術が提案されている（例えば、特許文献１～５）。
しかしながら、これらの技術においても、損傷の激しい毛髪や傷みの激しい毛先に対しては、コンディショニング効果が不十分であった。
As a technology to improve the conditioning effect on hair that has been treated with hair coloring, perming, etc., and to increase the durability of the conditioning effect, anionic substances (polymers, protein hydrolysates, etc.) and cationic substances (polymers, surfactants, etc.) etc.) have been proposed to form an ionic complex in the hair (for example, Patent Documents 1 to 5).
However, even with these techniques, the conditioning effect is insufficient for severely damaged hair and severely damaged hair tips.
近年、ブリーチ処理後にヘアカラー処理をするヘアデザイン技術が流行しており、従来よりも毛髪の損傷が激しくなっている。そのため従来の毛髪処理剤では、損傷の激しい毛髪に対しては、コンディショニング効果が不十分であった。
また上記ヘアデザイン技術の流行と共に、毛髪のすべり感、しなやかさ、まとまりなどのコンディショニング効果を付与できる毛髪処理剤が希求されており、特に損傷の激しい毛髪に対しても優れたコンディショニング効果を付与できる毛髪処理剤が求められていた。
本発明は上記事情に鑑みなされたものであって、その目的は、毛髪に優れたコンディショニング効果を付与できる毛髪処理剤を提供することである。
In recent years, a hair design technique in which hair coloring is performed after bleaching has become popular, and hair damage is becoming more serious than before. Therefore, conventional hair treatment agents have insufficient conditioning effects on severely damaged hair.
In addition, along with the popularity of the above-mentioned hair design technology, there is a demand for a hair treatment agent that can impart conditioning effects such as smoothness, suppleness, and manageability to hair, and that can impart excellent conditioning effects, particularly to severely damaged hair. A hair treatment agent has been desired.
The present invention has been made in view of the above circumstances, and an object thereof is to provide a hair treatment agent capable of imparting an excellent conditioning effect to hair.
上記課題を解決し得た本発明の毛髪処理剤は以下の構成を有する。
［１］下記（Ａ１）および下記（Ｂ１）を容器Ａ内に含有する処理剤Ｘ；または
下記（Ａ１）を容器Ｂ内に含有する第１剤と、下記（Ｂ１）を容器Ｃ内に含有する第２剤とを含有する処理剤Ｙ；
を含む毛髪処理剤。
（Ａ１）ポリクオタニウム－６４
（Ｂ１）ジカルボン酸ビスエトキシジグリコール
The hair treatment agent of the present invention, which has solved the above problems, has the following constitution.
[1] Treatment agent X containing (A1) and (B1) below in container A; or First agent containing (A1) below in container B and (B1) below in container C A processing agent Y containing a second agent to
A hair treatment agent containing.
(A1) Polyquaternium-64
(B1) Bisethoxydiglycol dicarboxylate
［２］ 前記処理剤Ｘ、または前記第１剤に含まれる前記ポリクオタニウム－６４の含有量は、１質量％以下（０質量％は含まない）である［１］に記載の毛髪処理剤。 [2] The hair treatment agent according to [1], wherein the content of the polyquaternium-64 contained in the treatment agent X or the first agent is 1% by mass or less (not including 0% by mass).
［３］ 前記処理剤Ｘ、または前記第２剤に含まれる前記（Ｂ１）ジカルボン酸ビスエトキシジグリコールの含有量は、１５質量％以下（０質量％は含まない）である［１］または［２］に記載の毛髪処理剤。 [3] The content of the (B1) bisethoxydiglycol dicarboxylate contained in the treatment agent X or the second agent is 15% by mass or less (not including 0% by mass) [1] or [ 2].
［４］ 前記毛髪処理剤は、更に下記（Ｃ１）および下記（Ｃ２）を容器Ｄ内に含有する処理剤Ｚを含むものである［１］～［３］のいずれか１項に記載の毛髪処理剤。
（Ｃ１）アミノ変性シリコーン
（Ｃ２）ジカルボン酸ジエステル
[4] The hair treatment agent according to any one of [1] to [3], further comprising a treatment agent Z containing the following (C1) and the following (C2) in a container D. .
(C1) amino-modified silicone (C2) dicarboxylic acid diester
［５］ 前記処理剤Ｚに含まれる前記（Ｃ１）アミノ変性シリコーンの含有量は、１０質量％以下（０質量％は含まない）、
前記（Ｃ２）ジカルボン酸ジエステルの含有量は、７質量％以下（０質量％は含まない）である［４］に記載の毛髪処理剤。
[5] The content of the (C1) amino-modified silicone contained in the treatment agent Z is 10% by mass or less (not including 0% by mass),
The hair treatment agent according to [4], wherein the content of the (C2) dicarboxylic acid diester is 7% by mass or less (not including 0% by mass).
［６］ 前記処理剤Ｘ、または前記第１剤は、更に下記（Ａ２）および／または下記（Ａ３）を含有する［１］～［５］のいずれか１項に記載の毛髪処理剤。
（Ａ２）カチオン化タンパク質
（Ａ３）カチオン性界面活性剤
[6] The hair treatment agent according to any one of [1] to [5], wherein the treatment agent X or the first agent further contains (A2) and/or (A3) below.
(A2) cationized protein (A3) cationic surfactant
［７］ 前記処理剤Ｘ、または前記第２剤は、更に下記（Ｂ２）を含有する［１］～［６］のいずれか１項に記載の毛髪処理剤。
（Ｂ２）アニオン性多糖類
[7] The hair treatment agent according to any one of [1] to [6], wherein the treatment agent X or the second agent further contains the following (B2).
(B2) anionic polysaccharide
以下のいずれかの塗布方法を含む［１］～［７］のいずれかに記載の毛髪処理剤の使用方法。
前記処理剤Ｘを毛髪に塗布する；
前記処理剤Ｘを毛髪に塗布した後、前記処理剤Ｚを塗布する；
前記第１剤を毛髪に塗布した後、前記第２剤を毛髪に塗布する；
前記第１剤を毛髪に塗布した後、前記第２剤を毛髪に塗布し、その後、処理剤Ｚを塗布する；
前記第２剤を毛髪に塗布した後、前記第１剤を毛髪に塗布する；
前記第２剤を毛髪に塗布した後、前記第１剤を毛髪に塗布し、その後、処理剤Ｚを塗布する；
前記第１剤、および前記第２剤を混合して混合剤を調製した後、該混合剤を毛髪に塗布する；または
前記第１剤、および前記第２剤を混合して混合剤を調製した後、該混合剤を毛髪に塗布し、その後、前記処理剤Ｚを塗布する；
A method of using the hair treatment agent according to any one of [1] to [7], including any of the following application methods.
Applying the treatment agent X to the hair;
After the treatment agent X is applied to the hair, the treatment agent Z is applied;
After applying the first agent to the hair, the second agent is applied to the hair;
After applying the first agent to the hair, the second agent is applied to the hair, and then the treatment agent Z is applied;
After applying the second agent to the hair, apply the first agent to the hair;
After applying the second agent to the hair, the first agent is applied to the hair, and then the treatment agent Z is applied;
After preparing a mixture by mixing the first agent and the second agent, the mixture is applied to the hair; or the first agent and the second agent are mixed to prepare a mixture After that, the mixture is applied to the hair, and then the treatment agent Z is applied;
本発明の毛髪処理剤は、ブリーチ処理やヘアカラー、パーマ等の化学的処理（以降、ブリーチ処理等という）が複数回施され、損傷が激しい毛髪に対して、優れた毛髪のすべり感、しなやかさ、まとまり（以下、コンディショニング効果という）を付与できる。 The hair treatment agent of the present invention provides excellent smoothness and suppleness to hair that has undergone multiple chemical treatments such as bleaching, hair coloring, and perming (hereinafter referred to as bleaching treatment, etc.) and is severely damaged. It is possible to impart coherence (hereinafter referred to as conditioning effect).
本発明の毛髪処理剤の適用対象となる毛髪は、好ましくはブリーチ処理等が施された毛髪、より好ましくは２回、または３回のブリーチ処理等が施された毛髪、さらに好ましくは４回以上のブリーチ処理等が施された毛髪である。
ホワイトブリーチなど、ブリーチ処理等を複数回繰り返した毛髪は、従来のヘアカラー処理された染髪やパーマ処理された毛髪と比べて毛髪の損傷が激しい。そのため従来の毛髪処理剤ではこのような損傷が激しい毛髪に対して十分なコンディショニング効果が得られなかった。
Hair to which the hair treatment agent of the present invention is applied is preferably hair that has been bleached, more preferably hair that has been bleached twice or three times, and still more preferably hair that has been bleached four times or more. hair that has undergone bleaching treatment or the like.
Hair that has undergone multiple bleaching treatments, such as white bleaching, is more severely damaged than conventional hair dyed or permed hair. For this reason, conventional hair treatment agents cannot provide sufficient conditioning effects on such severely damaged hair.
本発明の毛髪処理剤は、（Ａ１）ポリクオタニウム－６４と（Ｂ１）ジカルボン酸ビスエトキシジグリコールを必須成分とする。両成分を必須成分とすることで損傷の激しい毛髪に対して優れたコンディショニング効果、すなわち、毛髪のすべり感、しなやかさ、まとまりを付与できる。更に処理剤Ｚを使用することで、本発明の毛髪処理剤で付与されたコンディショニング効果の持続性、すなわち、毛髪処理剤で処理した後、毛髪を複数回シャンプーしてもコンディショニング効果を維持できる。 The hair treatment agent of the present invention comprises (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate as essential components. By using both components as essential components, it is possible to impart excellent conditioning effects to severely damaged hair, that is, smoothness, suppleness and manageability of hair. Furthermore, by using the treatment agent Z, the conditioning effect imparted by the hair treatment agent of the present invention can be maintained, that is, the conditioning effect can be maintained even when the hair is shampooed multiple times after treatment with the hair treatment agent.
以下、本発明の毛髪処理剤について説明する。
本発明の毛髪処理剤は、下記処理剤Ｘ、または処理剤Ｙを含む。
処理剤Ｘ：同一の容器Ａ内に（Ａ１）ポリクオタニウム－６４、および（Ｂ１）ジカルボン酸ビスエトキシジグリコールを含有する（１剤型処理剤ということがある）。
処理剤Ｙ：第１剤と第２剤とを含む構成であり、第１剤は容器Ｂ内に（Ａ１）ポリクオタニウム－６４を含有し、第２剤は容器Ｃ内に（Ｂ１）ジカルボン酸ビスエトキシジグリコールを含有する。なお、第１剤と第２剤は夫々、異なる容器に含まれている（２剤型処理剤ということがある）。
本発明のコンディショニング効果は、毛髪処理時に（Ａ１）ポリクオタニウム－６４と（Ｂ１）ジカルボン酸ビスエトキシジグリコールが同時に毛髪に塗布されている状態になれば得られる。したがって塗布前は（Ａ１）ポリクオタニウム－６４と（Ｂ１）ジカルボン酸ビスエトキシジグリコールが共に同じ容器Ａで保存されていてもよいし（１剤型処理剤）、（Ａ１）ポリクオタニウム－６４と（Ｂ１）ジカルボン酸ビスエトキシジグリコールが混ざらないように別々の容器Ｂと容器Ｃに分けて保存されていてもよい（２剤型処理剤）。
The hair treatment agent of the present invention is described below.
The hair treatment agent of the present invention contains treatment agent X or treatment agent Y below.
Treatment agent X: (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate are contained in the same container A (sometimes referred to as a one-component treatment agent).
Processing agent Y: A configuration containing a first agent and a second agent, the first agent containing (A1) polyquaternium-64 in container B, and the second agent containing (B1) bis dicarboxylate in container C Contains ethoxydiglycol. The first agent and the second agent are contained in different containers (sometimes referred to as a two-agent treatment agent).
The conditioning effect of the present invention can be obtained when (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate are simultaneously applied to the hair during hair treatment. Therefore, both (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate may be stored in the same container A (single-component treatment agent) before application, or (A1) polyquaternium-64 and (B1) ) The dicarboxylic acid bisethoxydiglycol may be divided and stored in separate containers B and C so as not to be mixed (two-component treatment agent).
（Ａ１）ポリクオタニウム－６４
（Ａ１）ポリクオタニウム－６４は、下記式（Ｉ）で示されるホスホリルコリン基を有する重合体である。
(A1) Polyquaternium-64 is a polymer having a phosphorylcholine group represented by the following formula (I).
ポリオクタニウムは複数の種類が存在するが、本発明者らが検討した結果、ポリオクタニウム－６４とジカルボン酸ビスエトキシジグリコールとの組み合わせのみが損傷の激しい毛髪に対して優れたヘアコンディショニング効果を発揮する。
本発明では「ＬＩＰＩＤＵＲＥ－Ｃ」（日油社製）などの各種市販のポリクオタニウム－６４を使用できる。
There are multiple types of polyoctanium, but as a result of investigations by the present inventors, only the combination of polyoctanium-64 and bisethoxydiglycol dicarboxylate has an excellent hair conditioning effect on severely damaged hair. demonstrate.
Various commercially available polyquaternium-64 such as "LIPIDURE-C" (manufactured by NOF CORPORATION) can be used in the present invention.
（Ａ１）ポリオクタニウム－６４の含有量を多くするとコンディショニング効果、特に毛髪のすべり感向上に寄与する。一方、（Ａ１）ポリオクタニウム－６４の含有量が多すぎると毛髪が柔らかくなり過ぎて絡まりやすくなり、コンディショニング効果、すなわち、毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりが悪くなる傾向を示す。
（Ａ１）ポリクオタニウム－６４の含有量は処理剤Ｘ、または第１剤中に占める割合が好ましくは０．０００５質量％以上、より好ましくは０．００２５質量％以上、さらに好ましくは０．００５質量％以上であって、好ましくは１質量％以下、より好ましくは０．５質量％以下、さらに好ましくは０．２質量％以下である。
(A1) Increasing the content of polyoctanium-64 contributes to the conditioning effect, particularly to the smoothness of the hair. On the other hand, if the content of (A1) polyoctanium-64 is too high, the hair becomes too soft and tends to get tangled, and the conditioning effect, that is, the smoothness of the hair, the suppleness of the hair, and the tendency of the hair to be set poorly. show.
(A1) The content of polyquaternium-64 is preferably 0.0005% by mass or more, more preferably 0.0025% by mass or more, and still more preferably 0.005% by mass in the processing agent X or the first agent. Above, it is preferably 1% by mass or less, more preferably 0.5% by mass or less, and still more preferably 0.2% by mass or less.
（Ｂ１）ジカルボン酸ビスエトキシジグリコール
（Ｂ１）ジカルボン酸ビスエトキシジグリコールは、下記式（ＩＩ）で示される化合物である。
［化２］
Ｒ２Ｏ－ＣＯ－Ｒ１－ＣＯ－ＯＲ２・・・（ＩＩ）
（式中、Ｒ１は炭素数２～１０の直鎖、分岐鎖又は環状の炭化水素基を表し、Ｒ２はエトキシジグリコール基を表す。）
ジカルボン酸ビスエトキシジグリコールの具体例としては、例えばシクロヘキサンジカルボン酸ビスエトキシジグリコール、コハク酸ビスエトキシジグリコール、アジピン酸ビスエトキシジグリコール、セバシン酸ビスエトキシジグリコール、フタル酸ビスエトキシジグリコール、テレフタル酸ビスエトキシジグリコール、アゼライン酸ビスエトキシジグリコールが挙げられる。
特にシクロヘキサンジカルボン酸ビスエトキシジグリコールが好ましい。シクロヘキサンジカルボン酸ビスエトキシジグリコールとしては「Ｎｅｏｓｏｌｕｅ－Ａｑｕｌｉｏ」（日本精化社製）などの各種市販品を用いることができる。
（Ｂ１）ジカルボン酸ビスエトキシジグリコールは、単独、または２種以上使用してもよい。
(B1) Bisethoxydiglycol dicarboxylate (B1) Bisethoxydiglycol dicarboxylate is a compound represented by the following formula (II).
[Chemical 2]
R 2 O—CO—R 1 —CO—OR 2 (II)
(In the formula, R 1 represents a linear, branched or cyclic hydrocarbon group having 2 to 10 carbon atoms, and R 2 represents an ethoxydiglycol group.)
Specific examples of bisethoxydiglycol dicarboxylates include bisethoxydiglycol cyclohexanedicarboxylate, bisethoxydiglycol succinate, bisethoxydiglycol adipate, bisethoxydiglycol sebacate, bisethoxydiglycol phthalate, and terephthalate. acid bisethoxydiglycol, azelate bisethoxydiglycol;
Cyclohexanedicarboxylic acid bisethoxydiglycol is particularly preferred. As the bisethoxydiglycol cyclohexanedicarboxylate, various commercial products such as "Neosolue-Aqulio" (manufactured by Nippon Fine Chemical Co., Ltd.) can be used.
(B1) Dicarboxylic acid bisethoxydiglycol may be used alone or in combination of two or more.
（Ｂ１）ジカルボン酸ビスエトキシジグリコールの含有量を多くするとコンディショニング効果を向上できる。一方、（Ｂ１）ジカルボン酸ビスエトキシジグリコールの含有量が多くなり過ぎると毛髪に（Ａ１）ポリクオタニウム－６４、および／または（Ｂ１）ジカルボン酸ビスエトキシジグリコール（以下、有効成分ということがある）が多く吸着し過ぎて髪がベタついて、コンディショニング効果が悪くなる傾向を示す。
（Ｂ１）ジカルボン酸ビスエトキシジグリコールの含有量は、処理剤Ｘ、または第２剤中に占める割合（２種以上の場合は合計）が好ましくは０．０５質量％以上、より好ましくは０．１質量％以上、さらに好ましくは０．５質量％以上であって、好ましくは１５質量％以下、より好ましくは１０質量％以下、さらに好ましくは４質量％以下である。
The conditioning effect can be improved by increasing the content of (B1) bisethoxydiglycol dicarboxylate. On the other hand, if the content of (B1) bisethoxydiglycol dicarboxylate is too high, (A1) polyquaternium-64 and/or (B1) bisethoxydiglycol dicarboxylate (hereinafter sometimes referred to as an active ingredient) may be added to the hair. Too much is adsorbed and the hair becomes sticky, and the conditioning effect tends to be poor.
The content of (B1) bisethoxydiglycol dicarboxylate is preferably 0.05% by mass or more, more preferably 0.05% by mass or more, more preferably 0.05% by mass or more (total when two or more are used) in the treatment agent X or the second agent. It is 1% by mass or more, more preferably 0.5% by mass or more, preferably 15% by mass or less, more preferably 10% by mass or less, and even more preferably 4% by mass or less.
処理剤Ｘ、第１剤において、（Ａ１）ポリクオタニウム－６４以外の残部成分は、溶媒であり、溶媒としては水、エタノールなど公知の毛髪処理剤用の溶媒を使用でき、好ましくは水である。
また第２剤において、（Ｂ１）ジカルボン酸ビスエトキシジグリコール以外の残部成分は、溶媒としては水、エタノールなど公知の毛髪処理剤用の溶媒を使用でき、好ましくは水である。
処理剤Ｘ、第１剤、第２剤は後記する成分（Ａ２）、成分（Ａ３）、成分（Ｂ２）などの有効添加成分や各種公知の添加剤を含有していてもよい。
また毛髪処理剤は処理剤Ｘ；または第１剤と第２剤からなる処理剤Ｙで構成されていてもよいが、更に処理剤Ｚを有する構成であってもよい。
In the treatment agent X, the first agent, the remaining component other than (A1) polyquaternium-64 is a solvent, and as the solvent, a known solvent for hair treatment agents such as water and ethanol can be used, preferably water.
In the second agent, the remaining components other than (B1) bisethoxydiglycol dicarboxylate may be water, ethanol or other known solvents for hair treatment agents, preferably water.
The processing agent X, the first agent, and the second agent may contain effective additive components such as component (A2), component (A3), and component (B2) described later, and various known additives.
The hair treatment agent may be composed of the treatment agent X; or the treatment agent Y consisting of the first agent and the second agent, or may further include the treatment agent Z.
本発明の毛髪処理剤は（Ａ１）ポリクオタニウム－６４、および（Ｂ１）ジカルボン酸ビスエトキシジグリコールを併用することで上記所望の効果が得られるが、更に下記（１）～（３）よりなる群から選ばれる少なくとも１種の有効添加成分を含有させると、コンディショニング効果やコンディショニング効果の持続性を、より一層向上できるため好ましい。
（１）（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステル（処理剤Ｚ）
（２）（Ａ２）カチオン化タンパク質、および／または（Ａ３）カチオン性界面活性剤
（３）（Ｂ２）アニオン性多糖類
The hair treatment agent of the present invention can obtain the desired effects by using (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate in combination. It is preferable to contain at least one effective additive component selected from the following because the conditioning effect and the durability of the conditioning effect can be further improved.
(1) (C1) amino-modified silicone and (C2) dicarboxylic acid diester (treatment agent Z)
(2) (A2) cationic protein and/or (A3) cationic surfactant (3) (B2) anionic polysaccharide
（１）処理剤Ｚ
処理剤Ｚは、（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステルを含有する。（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステルは併用する必要があり、（Ａ１）ポリクオタニウム－６４と（Ｂ１）ジカルボン酸ビスエトキシジグリコールと共に使用すると、コンディショニング効果とコンディショニング効果の持続性を向上できる。
上記処理剤Ｚの添加効果は、（Ａ１）ポリクオタニウム－６４および（Ｂ１）ジカルボン酸ビスエトキシジグリコールと共に毛髪に塗布されている状態になれば得られる。毛髪に塗布する前の（Ｃ１）アミノ変性シリコーンおよび（Ｃ２）ジカルボン酸ジエステルは、（Ａ１）ポリクオタニウム－６４や（Ｂ１）ジカルボン酸ビスエトキシジグリコールと混ざらないように容器Ｂや容器Ｃとは別の容器Ｄで保存することが望ましい。
(1) Treatment agent Z
The treatment agent Z contains (C1) an amino-modified silicone and (C2) a dicarboxylic acid diester. (C1) Amino-modified silicone and (C2) dicarboxylic acid diester must be used in combination, and when used together with (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate, the conditioning effect and the durability of the conditioning effect can be obtained. can improve.
The effect of adding the treatment agent Z can be obtained when it is applied to the hair together with (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate. (C1) amino-modified silicone and (C2) dicarboxylic acid diester before application to the hair are separated from container B and container C so as not to mix with (A1) polyquaternium-64 and (B1) bisethoxydiglycol dicarboxylate. It is desirable to store in container D of
（Ｃ１）アミノ変性シリコーン
（Ｃ１）アミノ変性シリコーンは毛髪への吸着性に優れており、ダメージケアやコンディショニング効果、持続性の向上に効果を有する成分である。
（Ｃ１）アミノ変性シリコーンとしては、例えばアミノエチルアミノプロピルシロキサン・ジメチルシロキサン共重合体などのアモジメチコン；アミノエチルアミノプロピルメチルシロキサン・ジメチルシロキサン共重合体などの（アミノエチルアミノプロピルメチコン／ジメチコン）コポリマー；高重合ジメチルシロキサン・メチル（アミノプロピル）シロキサン共重合体などのアミノプロピルジメチコン等が挙げられる。
アミノ変性シリコーンとしては、「ＤＯＷＳＩＬ ＳＭ ８９０４ ＣＯＳＭＥＴＩＣ ＥＭＵＬＳＩＯＮ」、「ＤＯＷＳＩＬ ＢＹ２２－０７９」、「ＤＯＷＳＩＬ ＦＺ－４６７１」、「ＤＯＷＳＩＬ ＦＺ－４６７２」、「ＤＯＷＳＩＬ ＳＳ－３５５１」（ダウ・東レ社製）などの各種市販品を用いることができる。
（Ｃ１）アミノ変性シリコーンは、単独または２種以上使用してもよい。
(C1) Amino-Modified Silicone (C1) Amino-modified silicone is a component that has excellent adsorptivity to hair and is effective for damage care, conditioning effects, and improvement of durability.
(C1) Amino-modified silicone includes, for example, amodimethicone such as aminoethylaminopropylsiloxane/dimethylsiloxane copolymer; (aminoethylaminopropylmethicone/dimethicone) copolymer such as aminoethylaminopropylmethylsiloxane/dimethylsiloxane copolymer; ; and aminopropyl dimethicone such as highly polymerized dimethylsiloxane/methyl(aminopropyl)siloxane copolymer.
Examples of amino-modified silicone include "DOWSIL SM 8904 COSMETIC EMULSION", "DOWSIL BY22-079", "DOWSIL FZ-4671", "DOWSIL FZ-4672", "DOWSIL SS-3551" (manufactured by Dow Toray Industries, Inc.). Various commercial products can be used.
(C1) Amino-modified silicone may be used alone or in combination of two or more.
（Ｃ１）アミノ変性シリコーンの含有量を多くするとコンディショニング効果、および持続性を向上できる。一方、（Ｃ１）アミノ変性シリコーンの含有量が多すぎると、毛髪に吸着し過ぎて髪をすいたときの引っかかりが大きくなる等、コンディショニング効果や持続性が減少する傾向を示す。
（Ｃ１）アミノ変性シリコーンの含有量は、処理剤Ｚに占める割合（２種以上の場合は合計）が好ましくは０．１質量％以上、より好ましくは１質量％以上、さらに好ましくは２質量％以上であって、好ましくは１０質量％以下、より好ましくは７質量％以下、さらに好ましくは５質量％以下である。
(C1) If the content of amino-modified silicone is increased, the conditioning effect and durability can be improved. On the other hand, if the content of (C1) amino-modified silicone is too high, it will tend to be too much adsorbed on the hair, resulting in greater tangling when the hair is brushed, resulting in reduced conditioning effect and durability.
(C1) The content of the amino-modified silicone is preferably 0.1% by mass or more, more preferably 1% by mass or more, and still more preferably 2% by mass in terms of the proportion of the amino-modified silicone in the treatment agent Z (in the case of two or more types, the total). It is preferably 10% by mass or less, more preferably 7% by mass or less, and even more preferably 5% by mass or less.
（Ｃ２）ジカルボン酸ジエステル
（Ｃ２）ジカルボン酸ジエステルは毛髪への有効成分の浸透促進に有効な成分であり、ダメージ回復効果、コンディショニング効果、持続性の向上に効果を有する成分である。
（Ｃ２）ジカルボン酸ジエステルとしては、例えばアジピン酸ジイソプロピル、アジピン酸ジイソブチル、アジピン酸ジエトキシエチル、アジピン酸ジグリセリル混合脂肪酸エステル等のアジピン酸ジエステル；コハク酸ジエトキシエチル、コハク酸ジオクチル等のコハク酸ジエステル；セバシン酸ジエチル等のセバシン酸ジエステルが挙げられる。
（Ｃ２）ジカルボン酸ジエステルとして各種市販品を用いることができる。
（Ｃ２）ジカルボン酸ジエステルは、単独または２種以上使用できる。
(C2) Dicarboxylic acid diester (C2) Dicarboxylic acid diester is a component effective in promoting the permeation of the active ingredient into the hair, and is a component having effects for damage recovery effect, conditioning effect, and improvement of durability.
Dicarboxylic acid diesters (C2) include, for example, adipic acid diesters such as diisopropyl adipate, diisobutyl adipate, diethoxyethyl adipate, and diglyceryl adipate mixed fatty acid ester; succinic acid such as diethoxyethyl succinate and dioctyl succinate; Diester; includes diesters of sebacate such as diethyl sebacate.
Various commercial products can be used as (C2) dicarboxylic acid diester.
(C2) Dicarboxylic acid diesters can be used alone or in combination of two or more.
（Ｃ２）ジカルボン酸ジエステルの含有量を多くするとコンディショニング効果、および持続性を向上できる。一方、（Ｃ２）ジカルボン酸ジエステルの含有量が多すぎると、毛髪に多く吸着し過ぎてベタつきが出て、コンディショニング効果や持続性が減少する傾向を示す。
（Ｃ２）ジカルボン酸ジエステルの含有量は、処理剤Ｚに占める割合（２種以上の場合は合計）が好ましくは０．０１質量％以上、より好ましくは０．１質量％以上、さらに好ましくは０．５質量％以上であって、好ましくは７質量％以下、より好ましくは５質量％以下、さらに好ましくは２質量％以下である。
(C2) When the content of dicarboxylic acid diester is increased, the conditioning effect and durability can be improved. On the other hand, if the content of (C2) dicarboxylic acid diester is too high, it will be too much adsorbed on the hair, resulting in stickiness and tending to reduce the conditioning effect and durability.
The content of the dicarboxylic acid diester (C2) is preferably 0.01% by mass or more, more preferably 0.1% by mass or more, and still more preferably 0 as a proportion of the amount of the dicarboxylic acid diester in the treatment agent Z (in the case of two or more types, the total). 5% by mass or more, preferably 7% by mass or less, more preferably 5% by mass or less, and even more preferably 2% by mass or less.
（２）（Ａ２）カチオン化タンパク質、および／または（Ａ３）カチオン性界面活性剤
（Ａ２）カチオン化タンパク質と（Ａ３）カチオン性界面活性剤の少なくとも１方、好ましくは両方を含有させると、コンディショニング効果を向上できる。
（Ａ２）カチオン化タンパク質、および／または（Ａ３）カチオン性界面活性剤は、処理剤Ｘ、または第１剤に含有させることが好ましい。
(2) containing at least one of (A2) a cationic protein and/or (A3) a cationic surfactant, and preferably both of (A2) a cationic protein and (A3) a cationic surfactant, conditioning can improve effectiveness.
(A2) cationized protein and/or (A3) cationic surfactant is preferably contained in the treatment agent X or the first agent.
（Ａ２）カチオン化タンパク質
（Ａ２）カチオン化タンパク質は、特に有効成分の毛髪への付着性（吸着性）向上に寄与する成分である。
カチオン化タンパク質とは、タンパク質または加水分解タンパク質をカチオン化した化合物である。カチオン化タンパク質としては、カチオン化加水分解ケラチン、カチオン化加水分解コラーゲン、カチオン化加水分解コメタンパク、カチオン化加水分解シルク、カチオン化加水分解カゼインが例示される。
具体的には、塩化Ｎ－［２－ヒドロキシ－３－（トリメチルアンモニオ）プロピル］加水分解ケラチン、塩化Ｎ－［２－ヒドロキシ－３－（トリメチルアンモニオ）プロピル］加水分解コラーゲン、塩化Ｎ－［２－ヒドロキシ－３－（トリメチルアンモニオ）プロピル］加水分解コメタンパク、塩化Ｎ－［２－ヒドロキシ－３－（トリメチルアンモニオ）プロピル］加水分解シルク等がある。また、セテアラミドエチルジエトニウム加水分解コメタンパク等の誘導体等が挙げられる。
これらの（Ａ２）カチオン化タンパク質は、単独または２種以上使用できる。
(A2) Cationized protein (A2) A cationized protein is a component that particularly contributes to improving the adhesion (adsorbability) of the active ingredient to the hair.
A cationized protein is a compound obtained by cationizing a protein or hydrolyzed protein. Examples of cationized proteins include cationized hydrolyzed keratin, cationized hydrolyzed collagen, cationized hydrolyzed rice protein, cationized hydrolyzed silk, and cationized hydrolyzed casein.
Specifically, N-[2-hydroxy-3-(trimethylammonio)propyl]hydrolyzed keratin chloride, N-[2-hydroxy-3-(trimethylammonio)propyl]hydrolyzed collagen chloride, N-chloride [2-hydroxy-3-(trimethylammonio)propyl]hydrolyzed rice protein, N-[2-hydroxy-3-(trimethylammonio)propyl]hydrolyzed silk chloride and the like. In addition, derivatives such as cetearamidoethyldiethonium hydrolyzed rice protein are also included.
These (A2) cationized proteins can be used singly or in combination of two or more.
（Ａ２）カチオン化タンパク質の含有量を多くすると有効成分の毛髪への付着性が増してコンディショニング効果を向上できる。一方、（Ａ２）カチオン化タンパク質の含有量が多すぎると毛髪に吸着する付着性向上成分が多くなり過ぎて、髪をすいたときの引っかかりが大きくなり、しなやかさが悪くなる等、コンディショニング効果が悪くなる傾向を示す。
（Ａ２）カチオン化タンパク質の含有量は処理剤Ｘ、または第１剤中に占める割合（２種以上の場合は合計）が好ましくは０．００５質量％以上、より好ましくは０．０３質量％以上、さらに好ましくは０．１質量％以上であって、好ましくは２質量％以下、より好ましくは１．５質量％以下、さらに好ましくは１質量％以下である。
(A2) When the content of the cationized protein is increased, the adhesion of the active ingredient to the hair is increased, and the conditioning effect can be improved. On the other hand, if the content of (A2) the cationized protein is too high, the amount of the adhesion-improving component that is adsorbed to the hair will be too large, and the hair will be caught more when combed, and the suppleness will be worsened, resulting in poor conditioning effects. It tends to get worse.
(A2) The content of the cationized protein is preferably 0.005% by mass or more, more preferably 0.03% by mass or more as a proportion of the cationized protein in the treatment agent X or the first agent (in the case of two or more types, the total). , more preferably 0.1% by mass or more, preferably 2% by mass or less, more preferably 1.5% by mass or less, and even more preferably 1% by mass or less.
（Ａ３）カチオン性界面活性剤
（Ａ３）カチオン性界面活性剤は、髪のすべり感向上に寄与する成分であり、コンディショニング効果向上に寄与する成分である。
（Ａ３）カチオン性界面活性剤としては、例えばアルキルトリメチルアンモニウムハライド、ジアルキルジメチルアンモニウムハライド、アルキルジメチルベンジルアンモニウムハライド、第三級脂肪族アミノ塩等が挙げられる。具体的にはラウリルトリメチルアンモニウムクロライド、ミリスチルトリメチルアンモニウムクロライド、セチルトリメチルアンモニウムクロライド、セチルトリメチルアンモニウムメチルサルフエート、パルミチルトリメチルアンモニウムクロライド、ステアリルトリメチルアンモニウムクロライド、エイコシルトリメチルアンモニウムクロライドなどのモノアルキル第四級アンモニウム塩；ジパルミチルジメチメルアンモニウムクロライド、ジステアリルジメチルアンモニウムクロライド等のジ長鎖アルキル第四級アンモニウム塩等が挙げられる。これらのなかでもモノアルキル第四級アンモニウム塩が好ましい。
（Ａ３）カチオン性界面活性剤は、単独または２種以上使用してもよい。
(A3) Cationic surfactant (A3) The cationic surfactant is a component that contributes to improving the smoothness of the hair, and is a component that contributes to improving the conditioning effect.
(A3) Cationic surfactants include, for example, alkyltrimethylammonium halides, dialkyldimethylammonium halides, alkyldimethylbenzylammonium halides, tertiary aliphatic amino salts and the like. Specifically, monoalkyl quaternary ammoniums such as lauryltrimethylammonium chloride, myristyltrimethylammonium chloride, cetyltrimethylammonium chloride, cetyltrimethylammonium methylsulfate, palmityltrimethylammonium chloride, stearyltrimethylammonium chloride and eicosyltrimethylammonium chloride. Salts; di-long-chain alkyl quaternary ammonium salts such as dipalmityldimethylammonium chloride and distearyldimethylammonium chloride; Among these, monoalkyl quaternary ammonium salts are preferred.
(A3) Cationic surfactants may be used alone or in combination of two or more.
（Ａ３）カチオン性界面活性剤の含有量を多くすると、コンディショニング効果を向上できる。一方、（Ａ３）カチオン性界面活性剤の含有量が多すぎると、毛髪が柔らかくなり過ぎて、まとまりが悪くなる傾向を示す。
（Ａ３）カチオン性界面活性剤の含有量は、処理剤Ｘ、または第１剤に占める割合（２種以上の場合は合計）が好ましくは０．０１質量％以上、より好ましくは０．１質量％以上、さらに好ましくは０．２質量％以上であって、好ましくは３質量％以下、より好ましくは２質量％以下、さらに好ましくは１．５質量％以下である。
(A3) The conditioning effect can be improved by increasing the content of the cationic surfactant. On the other hand, if the content of the cationic surfactant (A3) is too high, the hair tends to be too soft and unmanageable.
(A3) The content of the cationic surfactant is preferably 0.01% by mass or more, more preferably 0.1% by mass in terms of the proportion of the cationic surfactant in the treatment agent X or the first agent (in the case of two or more types, the total). % or more, more preferably 0.2 mass % or more, preferably 3 mass % or less, more preferably 2 mass % or less, still more preferably 1.5 mass % or less.
（３）（Ｂ２）アニオン性多糖類
（Ｂ２）アニオン性多糖類は、コンディショニング効果、特に毛髪のまとまり向上に有効な成分である。
（Ｂ２）アニオン性多糖類としては、例えば、カラギーナン、キサンタンガム、グアーガム、アルギン酸ナトリウム、およびデキストランの多価カルボキシメチルエーテルのナトリウム塩であるカルボキシメチルデキストランナトリウム等が挙げられる。これらのなかでもカルボキシメチルデキストランナトリウムが好ましい。
（Ｂ２）アニオン性多糖類は各種市販品を用いることができる。
（Ｂ２）アニオン性多糖類は、単独または２種以上使用できる。
(3) (B2) Anionic Polysaccharides (B2) Anionic polysaccharides are effective ingredients for conditioning effects, particularly for improving the manageability of hair.
(B2) Examples of anionic polysaccharides include carrageenan, xanthan gum, guar gum, sodium alginate, and carboxymethyldextran sodium, which is a sodium salt of polyvalent carboxymethyl ether of dextran. Among these, sodium carboxymethyldextran is preferred.
(B2) Various commercial products can be used as the anionic polysaccharide.
(B2) Anionic polysaccharides can be used singly or in combination of two or more.
（Ｂ２）アニオン性多糖類の含有量を多くするとコンディショニング効果を向上できる。一方、（Ｂ２）アニオン性多糖類の含有量が多すぎると、処理剤の粘度が高くなり過ぎて毛髪に均一に塗布しづらくなり、有効成分を十分に吸着させることができなくなり、コンディショニング効果が悪化する傾向を示す。
（Ｂ２）アニオン性多糖類の含有量は、処理剤Ｘ、または第１剤に占める割合（２種以上は合計）が好ましくは０．００１質量％以上、より好ましくは０．０１質量％以上、さらに好ましくは０．１質量％以上であって、好ましくは１５質量％以下、より好ましくは５質量％以下、さらに好ましくは２質量％以下である。
(B2) The conditioning effect can be improved by increasing the content of the anionic polysaccharide. On the other hand, if the content of the anionic polysaccharide (B2) is too high, the viscosity of the treatment agent becomes too high, making it difficult to apply it uniformly to the hair, making it impossible to sufficiently adsorb the active ingredient, resulting in poor conditioning effects. Shows a tendency to worsen.
(B2) The content of the anionic polysaccharide is preferably 0.001% by mass or more, more preferably 0.01% by mass or more, in the proportion of the treatment agent X or the first agent (the total of two or more types), It is more preferably 0.1% by mass or more, preferably 15% by mass or less, more preferably 5% by mass or less, and even more preferably 2% by mass or less.
本発明の毛髪処理剤には、上記の各種有効添加成分以外にも必要に応じて公知の毛髪処理剤に配合されている各種公知の添加剤を配合してもよい。
公知の添加剤としては例えば、植物油（オリーブ油、ホホバ油、シア脂等）、脂肪酸、炭化水素（スクワラン、流動パラフィン等）、高級アルコールなどの油脂類、界面活性剤（アニオン性界面活性剤、両性界面活性剤、ノニオン性界面活性剤）、糖類（ソルビトール等）、フッ素系化合物類、消臭剤、防腐剤、キレート剤、ｐＨ調整剤、溶剤、抗炎症剤、増粘剤、香料、色素等を挙げることができ、これらを適宜配合することができる。
In the hair treatment agent of the present invention, in addition to the various effective additive components described above, various known additives that are blended in known hair treatment agents may be blended, if necessary.
Known additives include, for example, vegetable oils (olive oil, jojoba oil, shea butter, etc.), fatty acids, hydrocarbons (squalane, liquid paraffin, etc.), fats and oils such as higher alcohols, surfactants (anionic surfactants, amphoteric surfactants, nonionic surfactants), sugars (sorbitol, etc.), fluorine compounds, deodorants, preservatives, chelating agents, pH adjusters, solvents, anti-inflammatory agents, thickeners, fragrances, pigments, etc. and these can be appropriately blended.
本発明の毛髪処理剤は各種形態を採用でき、例えば、クリーム、ローション、乳液、ゲルなどの剤型等にすることができ、頭髪用化粧料に幅広く使用・応用できる。 The hair treatment agent of the present invention can take various forms such as cream, lotion, milky lotion and gel, and can be widely used and applied to hair cosmetics.
本発明の毛髪処理剤の好適な使用方法について説明する。
本発明の毛髪処理剤は、ア）まずシャンプーで毛髪の汚れを落とした後、十分に水気を取り除いて髪を湿潤状態とすることが好ましい（以下、予洗ということがある）。
処理剤Ｘを用いた１剤型処理剤の場合は、イ）処理剤Ｘを毛髪に塗布し、毛髪全体に処理剤Ｘを伸ばしながらなじませる。
ウ）その後、毛髪処理剤をお湯ですすぎ流すことが好ましい（以下、湯洗ということがある）。
A preferred method of using the hair treatment agent of the present invention will be described.
With regard to the hair treatment agent of the present invention, it is preferable that a) the hair is first washed with shampoo, and then water is sufficiently removed to bring the hair to a moist state (hereinafter sometimes referred to as pre-washing).
In the case of a one-component type treatment agent using treatment agent X, a) apply treatment agent X to the hair, and apply treatment agent X to the entire hair while spreading it.
c) After that, it is preferable to rinse the hair treatment agent with hot water (hereinafter sometimes referred to as hot water washing).
処理剤Ｘに加えて処理剤Ｚを使用する場合、ア）予洗後、イ）処理剤Ｘを毛髪に塗布し、毛髪全体に処理剤Ｘを伸ばしながらなじませた後、処理剤Ｘを除去することなく、すなわち、処理剤Ｘをすすぎ流すことなく、エ）処理剤Ｚを毛髪に塗布し、毛髪全体に処理剤Ｚを伸ばしながらなじませる。
ウ）その後、湯洗することが好ましい。
When the treatment agent Z is used in addition to the treatment agent X, a) after pre-washing, b) the treatment agent X is applied to the hair, and after the treatment agent X is spread and blended throughout the hair, the treatment agent X is removed. without rinsing the treatment agent X, d) apply the treatment agent Z to the hair, and apply the treatment agent Z to the hair while spreading the treatment agent Z over the entire hair.
c) After that, it is preferable to wash with hot water.
第１剤と第２剤とを用いた２剤型処理剤の場合は、第１剤と第２剤の塗布順序は特に限定されず、第１剤と第２剤の両方が毛髪に塗布された状態となればよい。したがって、下記Ｉ～ＩＩＩのいずれの使用形態であってもよい。
Ｉ：ア）予洗後、カ－１）第１剤を毛髪に塗布し、毛髪全体に第１剤を伸ばしながらなじませた後、第１剤を除去することなく、すなわち、第１剤をすすぎ流すことなく、カ－２）第２剤を毛髪に塗布し、毛髪全体に第２剤を伸ばしながらなじませる。
ＩＩ：ア）予洗後、カ－３）第２剤を毛髪に塗布し、毛髪全体に第２剤を伸ばしながらなじませた後、第２剤を除去することなく、すなわち、第２剤をすすぎ流すことなく、カ－４）第１剤を毛髪に塗布し、毛髪全体に第１剤を伸ばしながらなじませる。
ＩＩＩ：ア）予洗後、カ－５）第１剤と第２剤とを混合した混合剤を調製した後、カ－６）該混合剤を毛髪に塗布し、毛髪全体に混合剤を伸ばしながらなじませる。
ウ）上記カ－２）、カ－４）、カ－６）の後、湯洗することが好ましい。
In the case of a two-component treatment agent using the first and second agents, the application order of the first and second agents is not particularly limited, and both the first agent and the second agent are applied to the hair. It should be in good condition. Therefore, it may be used in any of the following forms I to III.
I: A) After pre-washing, C-1) Apply the first agent to the hair, spread the first agent over the entire hair and let it blend in, and then rinse the first agent without removing the first agent. Without rinsing, apply Car-2) 2nd agent to the hair, and apply the 2nd agent to the entire hair while spreading it.
II: a) After pre-washing, c-3) Apply the second agent to the hair, spread the second agent over the entire hair and let it blend in, and then rinse the second agent without removing the second agent. 4) Apply the 1st agent to the hair without washing it off, and apply the 1st agent to the hair while spreading it all over the hair.
III: a) After pre-washing, c-5) After preparing a mixture by mixing the first agent and the second agent, c-6) applying the mixture to the hair and stretching the mixture over the entire hair. Get used to it.
C) It is preferable to wash with hot water after the above-mentioned C-2), C-4) and C-6).
２剤型処理剤に加えて更に処理剤Ｚを使用する場合、
上記Ｉ：ア）→カ－１）→カ－２）の後、または
上記ＩＩ：ア）→カ－３）→カ－４）の後、または
上記ＩＩＩ：ア）→カ－５）→カ－６）の後、
ウ）湯洗することなく、すなわち、第１剤と第２剤が毛髪に塗布された状態で、キ）処理剤Ｚを毛髪に塗布し、毛髪全体に処理剤Ｚを伸ばしながらなじませる。
その後、ウ）湯洗することが好ましい。
When using a processing agent Z in addition to the two-component processing agent,
After the above I: A) → C-1) → C-2), or after the above II: A) → C-3) → C-4), or above III: A) → C-5) → F After -6),
c) without rinsing with hot water, i.e., in a state in which the first agent and the second agent are applied to the hair, g) apply the treatment agent Z to the hair, and apply the treatment agent Z to the hair while spreading it all over the hair.
After that, c) it is preferable to wash with hot water.
本発明では処理剤を塗布した状態で毛髪を例えば５～３０分間放置してもよい。放置時間を設けることで各成分の髪への浸透・吸着がより促進され、コンディショニング効果、及び持続性を向上できる。
このような放置は、例えばイとウの間、イとエの間、カ－１とカ－２の間、カ－２とウの間、カ－２とキの間、カ－３とカ－４の間、カ－４とウの間、カ-４とキの間、カ－６とウの間、カ－６とキの間において行うことが好ましい。処理剤の塗布が複数ある場合は各処理剤の塗布間で放置してもよいし、あるいはいずれかの処理剤の塗布間で放置してもよい。
In the present invention, the hair may be left for, for example, 5 to 30 minutes while the treatment agent is applied. By setting the standing time, the penetration and adsorption of each component to the hair is further promoted, and the conditioning effect and durability can be improved.
Such neglect is, for example, between A and C, between A and D, between Car 1 and Car 2, between Car 2 and C, between Car 2 and Ki, between Car 3 and Car It is preferable to perform between -4, between Ka-4 and C, between Ka-4 and Ki, between Ka-6 and C, and between Ka-6 and Ki. When a plurality of processing agents are applied, the substrate may be left between the applications of each processing agent, or may be left between the applications of any one of the processing agents.
更に毛髪のダメージが強い場合は各処理剤を毛髪になじませた後で、スチーマーやローラーボール等を用いて加温放置した後、お湯で処理剤をすすぎ流してもよい。加温放置することで、各成分の浸透、および吸着がより促進され、コンディショニング効果やその持続効果を向上させることができる。加温放置する場合の加熱温度は、例えば３０℃～６０℃である。また該温度で放置する時間は、例えば５分～３０分である。 Further, if the hair is severely damaged, after applying each treatment agent to the hair, the treatment agent may be rinsed off with hot water after being left to heat with a steamer or a roller ball. By leaving it warm, the permeation and adsorption of each component are further promoted, and the conditioning effect and its sustained effect can be improved. The heating temperature when left to heat is, for example, 30°C to 60°C. Also, the time for standing at this temperature is, for example, 5 minutes to 30 minutes.
以下、実施例を挙げて本発明をより具体的に説明するが、本発明はもとより下記実施例によって制限を受けるものではなく、前・後記の趣旨に適合し得る範囲で適当に変更を加えて実施することも勿論可能であり、それらはいずれも本発明の技術的範囲に包含される。 Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited by the following examples, and can be modified appropriately within the scope that can conform to the gist of the above and later descriptions. It is of course possible to implement them, and all of them are included in the technical scope of the present invention.
（ブリーチ処理）
パーマ処理、ヘアカラー処理、ブリーチ処理などの化学的処理を一切行っていない毛束を準備した。粉末ブリーチ剤（中野製薬株式会社製キャラデコ トーナー ブリーチパウダー ＥＸ）と過酸化水素系酸化剤（中野製薬株式会社製キャラデコ オキサイド Ｎ０６）とを１：３（質量比）となるように混合したブリーチ剤を毛髪に質量比１：１の割合で塗布した後、３５℃で３０分間保持した後、４５質量％ラウリル硫酸トリエタノールアミン溶液で毛髪を洗浄した。続いて湯洗によりラウリル酸トリエタノールアミン溶液を洗い落とし、その後、毛髪をドライヤーで完全に乾燥させた。この処理（ブリーチ→ラウリル硫酸トリエタノールアミン溶液洗浄→湯洗→乾燥）を３回繰り返した。得られたブリーチ後の毛束を用いて評価用試料を作製した。
なお、各評価用試料の作製に使用したブリーチ後の毛束は長さ２０ｃｍ、重さ１５ｇである。
(Bleach processing)
Hair tresses were prepared without any chemical treatments such as perm treatment, hair coloring treatment, and bleaching treatment. A bleaching agent obtained by mixing a powder bleaching agent (Caradeco Toner Bleach Powder EX manufactured by Nakano Pharmaceutical Co., Ltd.) and a hydrogen peroxide-based oxidizing agent (Caradeco Oxide N06 manufactured by Nakano Pharmaceutical Co., Ltd.) at a ratio of 1:3 (mass ratio). After applying to the hair at a mass ratio of 1:1, the hair was kept at 35° C. for 30 minutes, and then washed with a 45% by mass triethanolamine lauryl sulfate solution. Subsequently, the triethanolamine laurate solution was washed off by washing with hot water, and then the hair was completely dried with a dryer. This treatment (bleaching→washing with triethanolamine lauryl sulfate→washing with hot water→drying) was repeated three times. An evaluation sample was prepared using the obtained bundle of hair after bleaching.
The hair bundle after bleaching used to prepare each evaluation sample had a length of 20 cm and a weight of 15 g.
（評価用試料の作製）
ブリーチ処理された毛髪を十分にお湯ですすぎ流した後（以下、予洗という）、毛髪処理剤を用いて以下のいずれかの処理を行った。
処理１：成分（Ａ１）と成分（Ｂ１）の両方を含有した処理剤Ｘ１．０ｇを毛束に塗布した後、流水で処理剤Ｘを十分に洗い流した。その後、毛束をドライヤーで完全に乾燥させた。
処理２：成分（Ａ１）を含有する処理剤Ａ（第１剤）１．０ｇを毛束に塗布した後、成分（Ｂ１）を含有する処理剤Ｂ（第２剤）２．０ｇ塗布した。塗布後、流水で処理剤Ａ、Ｂを十分に洗い流した。その後、毛束をドライヤーで完全に乾燥させた。
処理３：成分（Ｂ１）を含有する処理剤Ｂ（第２剤）２．０ｇ塗布した後、成分（Ａ１）を含有する処理剤Ａ（第１剤）１．０ｇを毛束に塗布した。塗布後、流水で十分に処理剤Ａ、Ｂを洗い流した。その後、毛束をドライヤーで完全に乾燥させた。
なお、処方例によっては処理剤Ａに成分（Ａ１）が含まれておらず、また処理剤Ｂには成分（Ｂ１）が含まれていないことがある。各処理に使用した処理剤の成分組成は表１～７に記載の通りである。
毛髪処理剤で処理して得られた各試料について、以下の基準で評価した。なお、実施例Ｎｏ．２－４を評価基準とした。
(Preparation of sample for evaluation)
After thoroughly rinsing the bleached hair with hot water (hereinafter referred to as pre-washing), one of the following treatments was performed using a hair treatment agent.
Treatment 1: After applying 1.0 g of the treatment agent X containing both the component (A1) and the component (B1) to the hair bundle, the treatment agent X was thoroughly washed away with running water. After that, the hair tress was completely dried with a dryer.
Treatment 2: After applying 1.0 g of treatment agent A (1st agent) containing component (A1) to the hair bundle, 2.0 g of treatment agent B (2nd agent) containing component (B1) was applied. After application, the treatment agents A and B were thoroughly washed away with running water. After that, the hair tress was completely dried with a dryer.
Treatment 3: After applying 2.0 g of treatment agent B (second agent) containing component (B1), 1.0 g of treatment agent A (first agent) containing component (A1) was applied to the hair bundle. After application, the treatment agents A and B were thoroughly washed away with running water. After that, the hair tress was completely dried with a dryer.
Depending on the formulation example, the processing agent A may not contain the component (A1), and the processing agent B may not contain the component (B1). The component compositions of the processing agents used in each treatment are shown in Tables 1-7.
Each sample obtained by treatment with a hair treatment agent was evaluated according to the following criteria. In addition, Example No. 2-4 was used as the evaluation criteria.
（毛髪のすべり感の評価方法）
専門パネラー１０名により以下の評価基準で官能評価し、評価点の合計値を求め、以下の基準で「毛髪のすべり感」について判定した。
［各パネラーの評価基準］
３点：すべり感が良い
２点：すべり感がやや良い
１点：すべり感が悪い
［すべり感の評価基準］
◎：２５点以上
○：２０点以上、２５点未満
△：１５点以上、２０点未満
×：１０点以上、１５点未満
(Method for evaluating slipperiness of hair)
Sensory evaluation was performed by 10 expert panelists according to the following evaluation criteria, the total value of the evaluation points was obtained, and the "hair smoothness" was determined according to the following criteria.
[Evaluation criteria for each panelist]
3 points: Good slip feeling 2 points: Slightly good slip feeling 1 point: Poor slip feeling [Evaluation criteria for slip feeling]
◎: 25 points or more ○: 20 points or more and less than 25 points △: 15 points or more and less than 20 points ×: 10 points or more and less than 15 points
（毛髪のしなやかさの評価方法）
専門パネラー１０名により以下の評価基準で官能評価し、評価点の合計値を求め、以下の基準で「毛髪のしなやかさ」について判定した。
［各パネラーの評価基準］
３点：しなやかさを感じる
２点：しなやかさをやや感じる
１点：しなやかさを感じない
［しなやかさの評価基準］
◎：２５点以上
○：２０点以上、２５点未満
△：１５点以上、２０点未満
×：１０点以上、１５点未満
(Method for evaluating suppleness of hair)
Sensory evaluation was carried out by 10 expert panelists according to the following evaluation criteria, the total value of the evaluation points was obtained, and the "flexibility of the hair" was determined according to the following criteria.
[Evaluation criteria for each panelist]
3 points: feeling suppleness 2 points: feeling suppleness a little 1 point: not feeling suppleness [evaluation criteria for suppleness]
◎: 25 points or more ○: 20 points or more and less than 25 points △: 15 points or more and less than 20 points ×: 10 points or more and less than 15 points
（毛髪のまとまりの評価方法）
専門パネラー１０名により以下の評価基準で官能評価し、評価点の合計値を求め、以下の基準で、「毛髪のまとまり」について判定した。
［各パネラーの評価基準］
３点：まとまりが良い
２点：まとまりがやや良い
１点：まとまりが悪い
［まとまりの評価基準］
◎：２５点以上
○：２０点以上、２５点未満
△：１５点以上、２０点未満
×：１０点以上、１５点未満
(Method for evaluating hair unity)
Sensory evaluation was carried out by 10 expert panelists according to the following evaluation criteria, the total value of the evaluation points was obtained, and the "settling of hair" was determined according to the following criteria.
[Evaluation criteria for each panelist]
3 points: good unity 2 points: somewhat good unity 1 point: poor unity [evaluation criteria for unity]
◎: 25 points or more ○: 20 points or more and less than 25 points △: 15 points or more and less than 20 points ×: 10 points or more and less than 15 points
（コンディショニング効果の持続性の評価用試料の作製）
ブリーチ処理された毛髪を予洗した後、毛髪処理剤を用いて以下のいずれかの処理を行って準備した試料を用いてコンディショニング効果の持続性を評価した。
処理１ａ：成分（Ａ１）と成分（Ｂ１）の両方を含有した処理剤Ｘ１．０ｇを毛束に塗布した後、成分（Ｃ１）を含有する処理剤Ｚ２．０ｇを塗布した。その後、水で十分に処理剤Ｘ、処理剤Ｚを洗い流した。その後、毛束をドライヤーで完全乾燥させた。その後、［シャンプー（中野製薬株式会社製ラデュラＮシャンプー ライトモイスト）→湯洗→タオルドライ→ドライヤー乾燥］を１０回繰り返した。
処理２ａ：成分（Ａ１）を含有する処理剤Ａ（第１剤）１．０ｇを毛束に塗布した後、成分（Ｂ１）を含有する処理剤Ｂ（第２剤）２．０ｇ塗布した。成分（Ｃ１）を含有する処理剤Ｚ２．０ｇ塗布した。塗布後、水で十分に処理剤Ａ、処理剤Ｂ、処理剤Ｚを洗い流した。その後、毛束をドライヤーで完全乾燥させた。その後、［シャンプー（中野製薬株式会社製ラデュラＮシャンプー ライトモイスト）→湯洗→タオルドライ→ドライヤー乾燥］を１０回繰り返した。
処理３ａ：成分（Ｂ１）を含有する処理剤Ｂ（第２剤）２．０ｇ塗布した後、成分（Ａ１）を含有する処理剤Ａ（第１剤）１．０ｇを毛束に塗布した。成分（Ｃ１）を含有する処理剤Ｚ２．０ｇ塗布した。塗布後、水で十分に処理剤Ａ、Ｂ、処理剤Ｚを洗い流した。その後、毛束をドライヤーで完全乾燥させた。その後、［シャンプー（中野製薬株式会社製ラデュラＮシャンプー ライトモイスト）→湯洗→タオルドライ→ドライヤー乾燥］を１０回繰り返した。
なお、処方例によっては処理剤Ｚに成分（Ｃ１）および／または（Ｃ２）が含まれていないことがある。各処理に使用した処理剤Ｚの成分組成は表８、表９に記載の通りである。
毛髪処理剤で処理して得られた各試料について、以下の基準で評価した。
(Preparation of sample for evaluation of durability of conditioning effect)
After pre-washing the bleached hair, the durability of the conditioning effect was evaluated using a sample prepared by performing one of the following treatments using a hair treatment agent.
Treatment 1a: After applying 1.0 g of treatment agent X containing both component (A1) and component (B1) to the hair bundle, 2.0 g of treatment agent Z containing component (C1) was applied. After that, the treatment agent X and the treatment agent Z were sufficiently washed away with water. After that, the hair tress was completely dried with a dryer. After that, [shampoo (Ladulla N Shampoo Light Moist manufactured by Nakano Pharmaceutical Co., Ltd.)→rinsing with hot water→drying with a towel→drying with a drier] was repeated 10 times.
Treatment 2a: After applying 1.0 g of treatment agent A (first agent) containing component (A1) to the hair bundle, 2.0 g of treatment agent B (second agent) containing component (B1) was applied. 2.0 g of processing agent Z containing component (C1) was applied. After the application, the treatment agents A, B, and Z were thoroughly washed away with water. After that, the hair tress was completely dried with a dryer. Thereafter, [shampoo (Ladulla N Shampoo Light Moist manufactured by Nakano Seiyaku Co., Ltd.)→rinsing with hot water→drying with a towel→drying with a drier] was repeated 10 times.
Treatment 3a: After applying 2.0 g of treatment agent B (second agent) containing component (B1), 1.0 g of treatment agent A (first agent) containing component (A1) was applied to the hair bundle. 2.0 g of processing agent Z containing component (C1) was applied. After application, the treatment agents A, B, and Z were thoroughly washed away with water. After that, the hair tress was completely dried with a dryer. Thereafter, [shampoo (Ladulla N Shampoo Light Moist manufactured by Nakano Seiyaku Co., Ltd.)→rinsing with hot water→drying with a towel→drying with a drier] was repeated 10 times.
Depending on the formulation example, the processing agent Z may not contain the components (C1) and/or (C2). Tables 8 and 9 show the component composition of the processing agent Z used in each treatment.
Each sample obtained by treatment with a hair treatment agent was evaluated according to the following criteria.
（コンディショニング効果の持続性の評価方法）
専門パネラー１０名により以下の評価基準で官能評価し、評価点の合計値を求め、以下の基準で「コンディショニング効果の持続性」について判定した。
（毛髪のすべり感の評価方法）
３点：コンディショニング効果が持続している
２点：コンディショニング効果がやや持続している
１点：コンディショニング効果が持続していない
［コンディショニング効果の持続性の評価基準］
◎：２５点以上
○：２０点以上、２５点未満
△：１５点以上、２０点未満
×：１０点以上、１５点未満
(Method for evaluating durability of conditioning effect)
Sensory evaluation was carried out by 10 expert panelists according to the following evaluation criteria, the total value of the evaluation points was obtained, and the "durability of the conditioning effect" was determined according to the following criteria.
(Method for evaluating slipperiness of hair)
3 points: Conditioning effect is sustained 2 points: Conditioning effect is somewhat sustained 1 point: Conditioning effect is not sustained [Evaluation criteria for sustainability of conditioning effect]
◎: 25 points or more ○: 20 points or more and less than 25 points △: 15 points or more and less than 20 points ×: 10 points or more and less than 15 points
表１～９において各成分の数値は、質量％を示し、成分が水溶液等の場合は純分換算したものである。 In Tables 1 to 9, the numerical value of each component indicates mass %, and when the component is an aqueous solution or the like, it is converted to a pure content.
（実施例１）
表１に示す第１剤である処理剤Ａ（処方例Ｉ－１～Ｉ－９；処方Ｉ－３１～３８）、表２に示す第２剤である処理剤Ｂ（処方例ＩＩ－４）、表３に示す処理剤Ｘ（処方例Ｉ－３とＩＩ－４を含むＩ・ＩＩ－１；処方Ｉ－８とＩＩ－８を含むＩ・ＩＩ－２）を表１０に示すように組み合わせて毛髪処理をした。なお、成分（Ａ１）を含有していない例は比較例である。各評価結果を表１０に示す。
(Example 1)
Treatment Agent A (Formulation Examples I-1 to I-9; Formulations I-31 to 38), which is the first agent shown in Table 1, and Treatment Agent B (Formulation Example II-4), which is the second agent shown in Table 2. , and the treatment agent X shown in Table 3 (I/II-1 including Formulation Examples I-3 and II-4; I/II-2 including Formulation Examples I-8 and II-8) were combined as shown in Table 10. I had my hair done. In addition, the example which does not contain a component (A1) is a comparative example. Each evaluation result is shown in Table 10.
実施例１では処理剤Ａ中の（Ａ１）ポリクオタニウム－６４の含有量が毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりに与える影響を検討した。
（Ａ１）ポリクオタニウム－６４を含有した処理剤Ａを用いた実験Ｎｏ．１～７ではいずれもコンディショニング効果に優れており、特に毛髪に優れたすべり感を付与できた。（Ａ１）ポリクオタニウム－６４が多くなると毛髪のすべり感が向上する傾向を示したが、含有量が多くなり過ぎると毛髪のすべり感が低下する傾向を示した。
（Ａ１）ポリクオタニウム－６４を含有した処理剤Ａを処理剤Ｂの後に塗布した実験Ｎｏ．１０；（Ａ１）ポリクオタニウム－６４を含有した処理剤Ａと処理剤Ｂを混合してから塗布した実験Ｎｏ．１１；（Ａ１）ポリクオタニウム－６４と（Ｂ１）シクロヘキサンジカルボン酸ビスエトキシジグリコールを含有した処理剤Ｘを塗布した実験Ｎｏ．１２は、いずれも毛髪に優れたすべり感などの優れたコンディショニング効果を付与することができた。これらの実施例からは塗布順序にかかわらず、所定の成分を毛髪に塗布できれば優れたコンディショニング効果が得られることがわかる。
一方、（Ａ１）ポリクオタニウム－６４を含有しない処理剤Ａを用いた実験Ｎｏ．８～９、１３～２０では毛髪にすべり感を付与できないなど、いずれもコンディショニング効果が悪かった。
In Example 1, the effect of the content of (A1) polyquaternium-64 in the treatment agent A on the smoothness of hair, the flexibility of hair, and the manageability of hair was examined.
(A1) Experiment No. using treatment agent A containing polyquaternium-64. All of Nos. 1 to 7 were excellent in conditioning effect, and were able to impart particularly excellent smoothness to the hair. When the content of (A1) polyquaternium-64 increased, the smoothness of the hair tended to improve, but when the content was too high, the smoothness of the hair tended to decrease.
(A1) Experiment No. in which treatment agent A containing polyquaternium-64 was applied after treatment agent B; 10; (A1) Experiment No. in which treatment agent A containing polyquaternium-64 and treatment agent B were mixed and then applied. 11; Experiment No. in which treatment agent X containing (A1) polyquaternium-64 and (B1) bisethoxydiglycol cyclohexanedicarboxylate was applied. All of No. 12 were able to impart excellent conditioning effects such as excellent slipperiness to the hair. These examples show that excellent conditioning effects can be obtained as long as the prescribed components can be applied to the hair, regardless of the order of application.
On the other hand, (A1) Experiment No. using treatment agent A not containing polyquaternium-64. With 8 to 9 and 13 to 20, the conditioning effect was poor, such as not being able to impart a slippery feel to the hair.
（実施例２）
表１に示す処理剤Ａ（処方例Ｉ－３）、および表２に示す処理剤Ｂ（処方例ＩＩ－１～ＩＩ－９、ＩＩ－３１～ＩＩ－３８）を表１１に示す組み合わせで毛髪処理をした。各評価結果を表１１に示す。
(Example 2)
Treatment agent A shown in Table 1 (formulation example I-3) and treatment agent B shown in table 2 (formulation examples II-1 to II-9, II-31 to II-38) were used in combination shown in table 11 to treat the hair. processed. Each evaluation result is shown in Table 11.
実施例２では処理剤Ｂ中の（Ｂ１）シクロヘキサンジカルボン酸ビスエトキシジグリコールの含有量が毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりに与える影響を検討した。
実験Ｎｏ．１－１～１－６はいずれも優れたコンディショニング効果が得られており、特に優れたすべり感を付与できた。（Ｂ１）シクロヘキサンジカルボン酸ビスエトキシジグリコールが多くなると毛髪のすべり感が向上する傾向を示したが、含有量が多くなり過ぎると毛髪のすべり感が低下する傾向を示した。
一方、（Ｂ１）シクロヘキサンジカルボン酸ビスエトキシジグリコールを含有しない処理剤Ｂを用いた実験Ｎｏ．１－７～１－１６では毛髪にすべり感などのコンディショニング効果を付与できなかった。
In Example 2, the effects of the content of (B1) bisethoxydiglycol cyclohexanedicarboxylate in treatment agent B on the smoothness of hair, the flexibility of hair, and the manageability of hair were examined.
Experiment no. All of Nos. 1-1 to 1-6 provided an excellent conditioning effect, and were able to impart a particularly excellent slipperiness. When the content of (B1) bisethoxydiglycol cyclohexanedicarboxylate increased, the smoothness of the hair tended to improve, but when the content was too high, the smoothness of the hair tended to decrease.
On the other hand, (B1) Experiment No. using treatment agent B not containing bisethoxydiglycol cyclohexanedicarboxylate. 1-7 to 1-16 could not impart a conditioning effect such as smoothness to the hair.
（実施例３）
表１に示す処理剤Ａ（処方例Ｉ－８、Ｉ－９）、および表２に示す処理剤Ｂ（処方例ＩＩ－８、ＩＩ－９）、処理剤Ｘ（処方Ｉ・ＩＩ－２）を表１２に示すように組み合わせて毛髪処理をした。各評価結果を表１２に示す。
(Example 3)
Treatment agent A (formulation examples I-8 and I-9) shown in Table 1, treatment agent B (formulation examples II-8 and II-9) shown in Table 2, and treatment agent X (formulations I and II-2) were combined as shown in Table 12 for hair treatment. Each evaluation result is shown in Table 12.
実施例３では処理剤Ａ中に（Ａ１）ポリクオタニウム－６４、および処理剤Ｂ中に（Ｂ１）シクロヘキサンジカルボン酸ビスエトキシジグリコールを含有しない場合のコンディショニング効果に与える影響を検討した。
（Ａ１）ポリクオタニウム－６４、および（Ｂ１）シクロヘキサンジカルボン酸ビスエトキシジグリコールを含有しない処理剤を用いた実験Ｎｏ．２－１～２－５では毛髪にすべり感、しなやかさ、まとまりを付与できなかった。
In Example 3, the influence on the conditioning effect when (A1) polyquaternium-64 in the treatment agent A and (B1) bisethoxydiglycol cyclohexanedicarboxylate in the treatment agent B is not included was investigated.
Experiment no. With 2-1 to 2-5, it was not possible to impart smoothness, suppleness and manageability to the hair.
（実施例４）
表１および表４に示す処理剤Ａ（処方例Ｉ－４、Ｉ－１０～Ｉ－１８）、および表２に示す処理剤Ｂ（処方例ＩＩ－４）を表１３に示すように組み合わせて毛髪処理をした。各評価結果を表１３に示す。
(Example 4)
Processing agents A (formulation examples I-4, I-10 to I-18) shown in Tables 1 and 4 and processing agent B (formulation examples II-4) shown in Table 2 were combined as shown in Table 13. I had my hair done. Each evaluation result is shown in Table 13.
実施例４では処理剤Ａ中の（Ａ２）カチオン化タンパク質、および（Ａ３）カチオン性界面活性剤が毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりに与える影響を検討した。
（Ａ２）カチオン化タンパク質、および／または（Ａ３）カチオン性界面活性剤を含有した処理剤Ａを用いた実験Ｎｏ．３－１～３－８では、毛髪にすべり感、しなやかさ、まとまりを付与でき、優れたコンディショニング効果が得られた。また（Ａ２）カチオン化タンパク質、および（Ａ３）カチオン性界面活性剤を含有しない処理剤Ａを用いた実験Ｎｏ．４、３－９）では、毛髪のしなやかさ、およびまとまりに対する効果が実験Ｎｏ.３－１～３－８よりも劣っていた。
In Example 4, the effects of (A2) the cationic protein and (A3) the cationic surfactant in the treatment agent A on the smoothness of the hair, the suppleness of the hair, and the manageability of the hair were investigated.
Experiment no. With 3-1 to 3-8, it was possible to impart smoothness, suppleness and manageability to the hair, and an excellent conditioning effect was obtained. Experiment No. 1 using (A2) cationized protein and (A3) treatment agent A containing no cationic surfactant. 4 and 3-9) were inferior to Experiment Nos. 3-1 to 3-8 in the effect on hair suppleness and manageability.
（実施例５）
表５に示す処理剤Ａ（処方例Ｉ－１９～Ｉ－２８）、および表２に示す処理剤Ｂ（処方例ＩＩ－４）を表１４に示すように組み合わせて毛髪処理をした。各評価結果を表１４に示す。
(Example 5)
Treatment agents A (formulation examples I-19 to I-28) shown in Table 5 and treatment agents B (formulation examples II-4) shown in Table 2 were combined as shown in Table 14 for hair treatment. Each evaluation result is shown in Table 14.
実施例５では処理剤Ａ中の（Ａ２）カチオン化タンパク質、および（Ａ３）カチオン性界面活性剤の含有量が毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりに与える影響を検討した。
（Ａ２）カチオン化タンパク質の含有量が０．０５％以上、１．５％以下の処理剤Ａを用いた実験Ｎｏ．４－２～４－４、（Ａ３）カチオン性界面活性剤の含有量が０．０２５％以上、１．７５％以下の処理剤Ａを用いた実験Ｎｏ．４－７～４－９では、毛髪のすべり感、しなやかさ、まとまりがより一層向上した。
In Example 5, the effects of the contents of (A2) cationic protein and (A3) cationic surfactant in treatment agent A on the smoothness of hair, the flexibility of hair, and the manageability of hair were examined.
(A2) Experiment No. using treatment agent A with a cationized protein content of 0.05% or more and 1.5% or less. 4-2 to 4-4, (A3) Experiment No. using the treatment agent A having a cationic surfactant content of 0.025% or more and 1.75% or less. In 4-7 to 4-9, the smoothness, suppleness and manageability of the hair were further improved.
（実施例６）
表４に示す処理剤Ａ（処方例Ｉ－１４）、および表２、表６に示す処理剤Ｂ（処方例ＩＩ－４、ＩＩ－１０～ＩＩ－１３）を表１５に示すように組み合わせて毛髪処理をした。各評価結果を表１５に示す。
(Example 6)
Processing agent A (formulation example I-14) shown in Table 4 and processing agent B (formulation examples II-4, II-10 to II-13) shown in Tables 2 and 6 were combined as shown in Table 15. I had my hair done. Each evaluation result is shown in Table 15.
実施例６では処理剤Ｂ中の（Ｂ２）アニオン性多糖類が毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりに与える影響を検討した。
（Ｂ２）アニオン性多糖類を含有していない処理剤Ｂを用いた実験Ｎｏ．３－５、５－４と（Ｂ２）アニオン性多糖類を含有した処理剤Ｂを用いた実験Ｎｏ．５－１～５－３を比較すると、（Ｂ２）アニオン性多糖類を含有することで、毛髪のすべり感、毛髪のしなやかさを付与し、特に毛髪に優れたまとまりを向上できた。
In Example 6, the effects of the (B2) anionic polysaccharide in the treatment agent B on the smoothness of the hair, the suppleness of the hair, and the manageability of the hair were investigated.
(B2) Experiment No. using treatment agent B containing no anionic polysaccharide. 3-5, 5-4 and (B2) Experiment Nos. using treatment agent B containing anionic polysaccharide. A comparison of 5-1 to 5-3 shows that the inclusion of (B2) an anionic polysaccharide imparts smoothness to the hair and flexibility to the hair, and particularly improves the manageability of the hair.
（実施例７）
表４に示す処理剤Ａ（処方例Ｉ－１４）、および表７に示す処理剤Ｂ（処方例ＩＩ－１４～ＩＩ－１９）を表１６に示すように組み合わせて毛髪処理をした。各評価結果を表１６に示す。
(Example 7)
The treatment agent A (formulation example I-14) shown in Table 4 and the treatment agent B (formulation examples II-14 to II-19) shown in Table 7 were combined as shown in Table 16 for hair treatment. Each evaluation result is shown in Table 16.
実施例７では処理剤Ｂ中の（Ｂ２）アニオン性多糖類の含有量が毛髪のすべり感、毛髪のしなやかさ、毛髪のまとまりに与える影響を検討した。
（Ｂ２）アニオン性多糖類の含有量が０．００１％以上１．５％以下の処理剤Ｂを用いた実験Ｎｏ．６－１～６－４）では、毛髪のすべり感、しなやかさ、まとまりのうち、少なくとも２点以上のコンディションが向上した。
In Example 7, the effects of the content of the anionic polysaccharide (B2) in the treatment agent B on the smoothness of the hair, the suppleness of the hair, and the manageability of the hair were examined.
(B2) Experiment No. using treatment agent B having an anionic polysaccharide content of 0.001% or more and 1.5% or less. In 6-1 to 6-4), at least two points of hair smoothness, suppleness and manageability were improved.
（実施例８）
表４に示す処理剤Ａ（処方例Ｉ－１４）、表６に示す処理剤Ｂ（処方例ＩＩ－１０）、表８に示す処理剤Ｚ（処方例ＩＩＩ－１～ＩＩＩ－９）、表３に示す処理剤Ｘ（処方例Ｉ・ＩＩ－１）を表１７に示すように組み合わせて毛髪処理をした。各評価結果を表１７に示す。
(Example 8)
Treatment Agent A shown in Table 4 (Formulation Example I-14), Treatment Agent B shown in Table 6 (Formulation Example II-10), Treatment Agent Z shown in Table 8 (Formulation Examples III-1 to III-9), Table 3 (Prescription Examples I and II-1) were combined as shown in Table 17 for hair treatment. Each evaluation result is shown in Table 17.
実施例８では処理剤Ｚの（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステルがコンディショニング効果、及びコンディショニング効果の持続性に与える影響を検討した。
（Ｃ１）アミノ変性シリコーン、または（Ｃ２）ジカルボン酸ジエステルの一方のみを含有した処理剤Ｚを用いた実験Ｎｏ．７－１～７－４と比べると、（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステルの両方を含有した処理剤Ｚを用いた実験Ｎｏ．７－５～７－８は、コンディショニング効果、及びその持続性のいずれも優れており、特にコンディショニング効果の持続性が極めて良好であった。
実験Ｎｏ．７－５、７－１０、７－１１は添加剤の処理剤の添加順序を変更した例であるが、いずれも優れた持続性を示した。
一方、（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステルのいずれも含有しない処理剤Ｚを用いた実験Ｎｏ．７－９はコンディショニング効果が持続性しなかった。
In Example 8, the effects of the (C1) amino-modified silicone and (C2) dicarboxylic acid diester of the treatment agent Z on the conditioning effect and the sustainability of the conditioning effect were examined.
Experiment No. using treatment agent Z containing only one of (C1) amino-modified silicone and (C2) dicarboxylic acid diester. Compared with 7-1 to 7-4, Experiment No. 1 using treatment agent Z containing both (C1) amino-modified silicone and (C2) dicarboxylic acid diester. 7-5 to 7-8 were excellent in both the conditioning effect and its durability, and in particular the durability of the conditioning effect was extremely good.
Experiment no. 7-5, 7-10, and 7-11 are examples in which the order of addition of the processing agent of the additive was changed, but all exhibited excellent durability.
On the other hand, experiment no. 7-9 did not sustain the conditioning effect.
（実施例９）
表４に示す処理剤Ａ（処方例Ｉ－１４）、および表６に示す処理剤Ｂ（処方例ＩＩ－１０）、および表９に示す処理剤Ｚ（処方例ＩＩＩ－１０～ＩＩＩ－１９）を表１８に示すように組み合わせて毛髪処理をした。各評価結果を表１８に示す。
(Example 9)
Treatment Agent A (Formulation Example I-14) shown in Table 4, Treatment Agent B (Formulation Example II-10) shown in Table 6, and Treatment Agent Z shown in Table 9 (Formulation Examples III-10 to III-19) were combined as shown in Table 18 for hair treatment. Each evaluation result is shown in Table 18.
実施例９では（Ｃ１）アミノ変性シリコーン、および（Ｃ２）ジカルボン酸ジエステルの含有量がコンディショニング効果、及びその持続性に与える影響を検討した。
（Ｃ１）アミノ変性シリコーンの含有量が１．２５％以上７．５％以下の処理剤Ｚを用いた実験Ｎｏ．８－２～８－４、および（Ｃ２）ジカルボン酸ジエステルの含有量が０．０３％以上２．５％以下の処理剤Ｚを用いた実験Ｎｏ．８－７～８－９では、コンディショニング効果、及び持続性のいずれにもより優れた効果を示した。
In Example 9, the effects of the contents of (C1) amino-modified silicone and (C2) dicarboxylic acid diester on the conditioning effect and its durability were investigated.
(C1) Experiment No. using treatment agent Z having an amino-modified silicone content of 1.25% or more and 7.5% or less. Experiment Nos. 8-2 to 8-4, and (C2) using treatment agent Z having a dicarboxylic acid diester content of 0.03% or more and 2.5% or less. 8-7 to 8-9 showed superior effects both in terms of conditioning effect and durability.
Claims (8)
下記（Ａ１）を容器Ｂ内に含有する第１剤と、下記（Ｂ１）を容器Ｃ内に含有する第２剤とを含有する処理剤Ｙ；
を含む毛髪処理剤。
（Ａ１）ポリクオタニウム－６４
（Ｂ１）ジカルボン酸ビスエトキシジグリコール A treatment agent X containing the following (A1) and the following (B1) in a container A; or a first agent containing the following (A1) in the container B and a second agent containing the following (B1) in the container C A processing agent Y containing an agent;
A hair treatment agent containing.
(A1) Polyquaternium-64
(B1) Bisethoxydiglycol dicarboxylate
（Ｃ１）アミノ変性シリコーン
（Ｃ２）ジカルボン酸ジエステル 4. The hair treatment agent according to any one of claims 1 to 3, further comprising a treatment agent Z containing the following (C1) and the following (C2) in a container D.
(C1) amino-modified silicone (C2) dicarboxylic acid diester
前記（Ｃ２）ジカルボン酸ジエステルの含有量は、７質量％以下（０質量％は含まない）である請求項４に記載の毛髪処理剤。 The content of the (C1) amino-modified silicone contained in the treatment agent Z is 10% by mass or less (not including 0% by mass),
5. The hair treatment agent according to claim 4, wherein the content of the (C2) dicarboxylic acid diester is 7% by mass or less (excluding 0% by mass).
（Ａ２）カチオン化タンパク質
（Ａ３）カチオン性界面活性剤 The hair treatment agent according to any one of claims 1 to 5, wherein the treatment agent X or the first agent further contains (A2) and/or (A3) below.
(A2) cationized protein (A3) cationic surfactant
（Ｂ２）アニオン性多糖類 The hair treatment agent according to any one of claims 1 to 6, wherein the treatment agent X or the second agent further contains the following (B2).
(B2) anionic polysaccharide
前記処理剤Ｘを毛髪に塗布する；
前記処理剤Ｘを毛髪に塗布した後、前記処理剤Ｚを塗布する；
前記第１剤を毛髪に塗布した後、前記第２剤を毛髪に塗布する；
前記第１剤を毛髪に塗布した後、前記第２剤を毛髪に塗布し、その後、処理剤Ｚを塗布する；
前記第２剤を毛髪に塗布した後、前記第１剤を毛髪に塗布する；または、
前記第１剤を毛髪に塗布した後、前記第２剤を毛髪に塗布し、その後、処理剤Ｚを塗布する；
前記第１剤、および前記第２剤を混合して混合剤を調製した後、該混合剤を毛髪に塗布する；または
前記第１剤、および前記第２剤を混合して混合剤を調製した後、該混合剤を毛髪に塗布し、その後、前記処理剤Ｚを塗布する； A method of using the hair treatment agent according to any one of claims 1 to 7, including any of the following application methods.
Applying the treatment agent X to the hair;
After the treatment agent X is applied to the hair, the treatment agent Z is applied;
After applying the first agent to the hair, the second agent is applied to the hair;
After applying the first agent to the hair, the second agent is applied to the hair, and then the treatment agent Z is applied;
After applying the second agent to the hair, the first agent is applied to the hair; or
After applying the first agent to the hair, the second agent is applied to the hair, and then the treatment agent Z is applied;
After preparing a mixture by mixing the first agent and the second agent, the mixture is applied to the hair; or the first agent and the second agent are mixed to prepare a mixture After that, the mixture is applied to the hair, and then the treatment agent Z is applied;