JP2022533283A - 負極材料、当該材料を含む極片、電気化学装置及び電子装置 - Google Patents
負極材料、当該材料を含む極片、電気化学装置及び電子装置 Download PDFInfo
- Publication number
- JP2022533283A JP2022533283A JP2021533503A JP2021533503A JP2022533283A JP 2022533283 A JP2022533283 A JP 2022533283A JP 2021533503 A JP2021533503 A JP 2021533503A JP 2021533503 A JP2021533503 A JP 2021533503A JP 2022533283 A JP2022533283 A JP 2022533283A
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- present application
- oxygen
- electrode material
- containing silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本出願の第1の形態は、酸素含有シリコン材料を含み、
前記酸素含有シリコン材料のラマンスペクトルにおいて、IAは、ラマンスペクトルにおけるピーク位置が140cm-1±10cm-1であるピークに対応するピーク強度を表し、IDは、ラマンスペクトルにおけるピーク位置が470cm-1±10cm-1であるピークに対応するピーク強度を表し、IEはラマンスペクトルにおけるピーク位置が510cm-1±10cm-1であるピークに対応するピーク強度を表し、
前記負極材料は0<IA/ID<2、且つ0≦IE /IA<5を満たす、負極材料を提供する。
前記負極材料は0<IA/ID<2、且つ0≦IE/IA<5を満たす、負極材料を提供する。
<負極材料の製造>
ステップA:原料であるアモルファス酸化ケイ素を破砕し、分級処理した後、酸化ケイ素粉末即ち酸素含有シリコン材料が得られる。その中で、原料であるアモルファス酸化ケイ素の平均粒子径は1mm~100mmで、酸化ケイ素の化学式はSiOxであり、0.5<x<1.6である。
上記負極材料、黒鉛、導電剤を攪拌して混合し、混合物Aが得られる。その中で、攪拌時間は120min以上、攪拌機の公転速度は10~30r/minである。
<正極片の製造>
活物質LiCoO2、導電性カーボンブラック、バインダーを、質量比95~98:1.5~5:1.5~5で有機溶媒系に十分攪拌して均一に混合した後、Al箔上に塗布して乾燥し、冷間プレスを行い、正極片が得られ、極片を74mm×867mmの片材に切断して用いる。その中で、バインダーとして、ポリフッ化ビニリデンを用いて、有機溶媒として、N-メチルピロリドンを用いる。
溶媒EC、DMC、DECを、体積比1:1:1で混合し、混合液が得られ、そしてFECとLiPF6を加え、混合して電解液が得られる。ここで、電解液におけるFECの質量濃度は、15~20wt%であり、電解液におけるLiPF6のモル濃度は0.5~2mol/Lである。
セパレータとして、ポリエチレン(PE)多孔質ポリマーフィルムを用いて、セパレータを正極と負極との間に介在して隔離の役割を果たすように、上記製造した正極片、セパレータ、負極片をこの順に積層し、巻き取りして、電極組立体が得られた。電極組立体を包材外装に入れ、調製された電解液を注入して封止し、化成、脱ガス、トリミング等のプロセスを行うことで、リチウムイオン電池が得られる。
<表面に炭素が存在していない負極材料のリチウムイオン電池の製造>
<負極材料の製造>
原料であるアモルファス酸化ケイ素を、まず機械破砕処理して、そして気流粉砕機で気流粉砕を行うことで、酸化ケイ素粉末が得られ、そして分級を行い、Dv50が5.5μmの酸化ケイ素粉末即ち酸素含有シリコン材料が得られる。
上記負極材料、黒鉛、導電剤を真空攪拌機(番号:MSK-SFM-10)で攪拌して混合し、混合物Aが得られ、その中で、攪拌時間は120minであり、攪拌機の公転速度は20r/minである。
活物質LiCoO2、導電性カーボンブラック、バインダーを、質量比96.7:1.7:1.6で有機溶媒系NMPに十分攪拌して均一に混合した後、固形分の含有量が75wt%の正極スラリーが得られた。正極スラリーを、Al箔上に塗布して乾燥し、冷間プレスを行うことで、塗布の厚さが110μmの正極片が得られ、極片を74mm×867mmの片材に切断して用いる。
溶媒EC、DMC、DECを体積比1:1:1で混合し、混合液が得られた。そしてフルオロエチレンカーボネート(FEC)とLiPF6を加え、混合して電解液が得られた。ここで、電解液におけるFECの質量濃度は10wt%であり、電解液におけるLiPF6のモル濃度は1mol/Lである。
セパレータとして、厚さが15μmのPE多孔質ポリマーフィルムを用いて、セパレータを正極と負極との間に介在して隔離の役割を果たすように、上記製造した正極片、セパレータ、負極片をこの順に積層し、巻き取りして、電極組立体が得られた。電極組立体を包材外装に入れ、調製された電解液を注入して封止し、化成、脱ガス、トリミング等のプロセスを行うことで、リチウムイオン電池が得られる。
<表面に炭素が存在する負極材料のリチウムイオン電池の製造>
<負極材料の製造>
原料であるアモルファス酸化ケイ素を、まず機械破砕処理して、そして気流粉砕機で気流粉砕を行うことで、粒度の範囲が0.2μm~30μmの酸化ケイ素粉末が得られ、そして分級を行い、Dv50が5.5μmの酸化ケイ素粉末即ち酸素含有シリコン材料が得られる。
CVD炉における酸化ケイ素粉末の昇温温度が1000℃であること以外は、実施例2と同じにする。
CVD炉における酸化ケイ素粉末の昇温温度が1300℃であること以外は、実施例2と同じにする。
CVD炉における酸化ケイ素粉末の昇温温度が1500℃であること以外は、実施例2と同じにする。
CVD炉における酸化ケイ素粉末に通す炭素源ガスがエチレンであること以外は、実施例2と同じにする。
CVD炉における酸化ケイ素粉末に通す炭素源ガスがトルエン(C7H8)であること以外は、実施例2と同じにする。
CVD炉における酸化ケイ素粉末に通す炭素源ガスがメタンとエチレンの混合ガスであること以外は、実施例2と同じにする。その中で、混合ガスにおけるメタンとエチレンの体積比は1:2である。
CVD炉における酸化ケイ素粉末に通す炭素源ガスがメタンとエチレンの混合ガスであること以外は、実施例2と同じにする。その中で、混合ガスにおけるメタンとエチレンの体積比は2:1である。
CVD炉における酸化ケイ素粉末の昇温温度が600℃であること以外は、実施例2と同じにする。
CVD炉における酸化ケイ素粉末の昇温温度が1800℃であること以外は、実施例2と同じにする。
酸化ケイ素粉末のDv50が2.0μmであること以外は、実施例2と同じにする。
酸化ケイ素粉末のDv50が15.0μmであること以外は、実施例2と同じにする。
以下の方法に従って各実施例及び各比較例で製造された負極材料、負極片、リチウムイオン電池を測定する:
負極材料及び負極片のラマン測定:
分光装置(Jobin Yvon LabRAM HR)で負極材料及びサイクルした後の負極片を測定した。光源は532nmであり、測定範囲は50cm-1~4000cm-1であり、充放電サイクルを行った後の負極片をDMCで洗浄して測定する。
レーザー粒度分布測定装置(MasterSizer 2000)によって粒度分布を測定した。50mlの清浄なビーカーに0.02gの負極材料粉末サンプルを加え、20mlの脱イオン水を加えて、更に2~3滴の1%の界面活性剤を滴下し、粉末を完全に水に分散し、120Wの超音波洗浄機で5分間の超音波をした後、負極材料の粒子径を測定する。
本出願の負極材料を含むリチウムイオン電池をサイクルして測定した。測定温度は25℃である。0.5Cにて定電流で4.45Vまで充電し、定電圧で0.025Cまで充電し、5分間静置した後、0.5Cにて3.0Vまで放電することにより得られた容量を初回容量とする。さらに0.5C充電/0.5C放電でサイクルして測定し、各サイクル後の容量と初回容量との比により、400回サイクルした後、容量減衰曲線が得られる。
マイクロメーターで半分充電された時の(即ち50%充電した状態(SOC))リチウムイオン電池の厚さを測定した。400回サイクルまでサイクルすると、電池は満充電された(即ち100%SOC)状態になり、さらに、この時の電池の厚さをマイクロメーターで測定した。当該測定した電池の厚さを、初回半分充電された時の(50%SOC)電池の厚さと比較して、この時の満充電された(100%SOC)電池膨張率が得られる。各実施例と比較例の製造パラメーター及び測定結果は以下の表1に示す:
酸素含有シリコン材料のDv50が大き過ぎ、例えば比較例4の15.0μmである場合、リチウムイオン電池のサイクル膨張率も著しく高まる。その理由は主に、大きい粒子がサイクル過程においてより割れやすく、露出される新鮮な界面が電解液と反応し続け、サイクルの減衰を加速させ、膨張を増加させる、ためである。このため、酸素含有シリコン材料のDv50は5.5μm~10μmに制御されるのが好ましい。
Claims (11)
- 酸素含有シリコン材料を含み、
前記酸素含有シリコン材料のラマンスペクトルにおいて、IAはラマンスペクトルにおけるピーク位置が140cm-1±10cm-1であるピークに対応するピーク強度を表し、IDはラマンスペクトルにおけるピーク位置が470cm-1±10cm-1であるピークに対応するピーク強度を表し、IEはラマンスペクトルにおけるピーク位置が510cm-1±10cm-1であるピークに対応するピーク強度を表し、
前記負極材料は0<IA/ID<2、且つ0≦IE/IA<5を満たす、負極材料。 - 前記負極材料は0<IA/ID<2、且つIE/IA=0を満たす、請求項1に記載の負極材料。
- 前記酸素含有シリコン材料の化学式はSiOxで表れ、0.5<x<1.6、前記酸素含有シリコン材料のDv50は5.5μm~10μmである、請求項1に記載の負極材料。
- 前記酸素含有シリコン材料の表面に炭素が存在し、前記酸素含有シリコン材料のラマンスペクトルにおいて、I1350とI1580とは0<I1350/I1580<2.5を満たす、請求項1に記載の負極材料。
- バインダー及び請求項1~4のいずれかに記載の負極材料を含む合剤層を含む、負極片。
- 前記合剤層は、さらに、天然黒鉛或いは人造黒鉛の少なくとも一種を含む黒鉛を含む、請求項5に記載の負極片。
- 前記負極片において、前記合剤層に占める前記酸素含有シリコン材料の質量は、1%~99%である、請求項5に記載の負極片。
- 請求項5~7のいずれかに記載の負極片を含む、電極組立体。
- 請求項8に記載の電極組立体を含む、電気化学装置。
- 前記電気化学装置の膨張率は5.9%~9.1%である、請求項9に記載の電気化学装置。
- 請求項9又は10に記載の電気化学装置を含む、電子装置。