JP2022083923A - 負極活物質原料の製造方法 - Google Patents
負極活物質原料の製造方法 Download PDFInfo
- Publication number
- JP2022083923A JP2022083923A JP2020195563A JP2020195563A JP2022083923A JP 2022083923 A JP2022083923 A JP 2022083923A JP 2020195563 A JP2020195563 A JP 2020195563A JP 2020195563 A JP2020195563 A JP 2020195563A JP 2022083923 A JP2022083923 A JP 2022083923A
- Authority
- JP
- Japan
- Prior art keywords
- silicon
- raw material
- negative electrode
- electrode active
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
さらに、シリコンクラスレートIIについては、Na22.56Si136、Na17.12Si136、Na18.72Si136、Na7.20Si136、Na11.04Si136、Na1.52Si136、Na23.36Si136、Na24.00Si136、Na20.48Si136、Na16.00Si136、Na14.80Si136を製造したことが記載されている。
このようにして得られた反応生成物は固い塊状をなしているため、当該反応生成物を負極活物質の製造に供するためには高出力の粉砕機を用いて粉砕する必要があった。つまり、当該反応生成物は、そのまま負極活物質原料として使用することができず、負極活物質原料とするためには高出力の粉砕機を含む大規模な製造設備を必要とする。したがって、当該反応生成物は負極活物質の工業的な生産に適するとはいい難い問題があった。
また、粉砕および再加熱を経て得られた反応生成物からは結晶性シリコンに由来するピークが認められなかったことから、初回加熱後の反応生成物を粉砕することによりシリコンとナトリウムとが十分に混ざり合い、その結果、シリコンおよびナトリウムからナトリウムシリサイドが生じる反応が好適に進行したと推測される。つまり、加熱、粉砕および再加熱の3工程のうち粉砕工程は、シリコンおよびナトリウムからナトリウムシリサイドが生じる反応を進行させるために有効といい得る。
粉末状の水素化ナトリウムと粉末状のシリコンとを炭化水素系分散媒中で混合してNa-Si混合原料を得る混合工程と、
前記Na-Si混合原料をナトリウムシリサイドの融点未満の温度で加熱して前記ナトリウムシリサイドを得る反応工程と、を具備する、負極活物質原料の製造方法である。
粉末状の水素化ナトリウムと粉末状のシリコンとを炭化水素系分散媒中で混合してNa-Si混合原料を得る混合工程と、
前記Na-Si混合原料をナトリウムシリサイドの融点未満の温度で加熱して前記ナトリウムシリサイドを得る反応工程と、を具備する。
以下、本発明の製造方法をその要素毎に説明する。
このうち混合工程の意義は、ナトリウムシリサイドが生成する反応が好適に進行するように、ナトリウムとシリコンとが十分に混合されたNa-Si混合原料を得ることにある。本発明の製造方法においては、粉末状の水素化ナトリウムと粉末状のシリコンとを用い、これらを炭化水素系分散媒中で混合する。なお、Na-Si混合原料は粉末状の水素化ナトリウムおよび粉末状のシリコンを必須とし、炭化水素系分散媒を含まなくても良いし、炭化水素系分散媒が残存していても良い。
つまり、本発明の製造方法においては、混合工程に用いた炭化水素系分散媒は、反応工程前に除去するのが好ましい。さらに換言すると、本発明の製造方法は、混合工程後かつ反応工程前に、炭化水素系分散媒を除去する工程を具備するのが好ましい。
本発明の製造方法に要するコストを考慮すると、炭化水素系分散媒の除去は揮発により行うのが好ましい。したがって、炭化水素系分散媒としては、反応工程における加熱温度よりも低い温度で揮発し得るものを用いるのが好ましく、比較的低温で揮発し得るものを用いるのが特に好ましいといい得る。
炭化水素系分散媒の粘度の好ましい範囲として、50mPa・s以下、10mPa・s以下または1mPa・s以下の各範囲が挙げられる。炭化水素系分散媒の粘度につき、下限値は特に限定されず、0mPa・sを超えればよい。
このうちシリコンの平均粒子径は、一般的なレーザー回折式粒度分布測定装置で測定した場合における、D50で表すことができる。
また、水素化ナトリウムの平均粒子径は、画像解析により測定可能である。具体的には、顕微鏡写真を画像解析することにより得られた水素化ナトリウムの投影面積を基に、当該投影面積と同じ投影面積を有する球体の直径を算出し、当該直径を水素化ナトリウムの粒子径とみなせば良い。そして当該水素化ナトリウムの粒子径を複数取得し、その平均値を算出すれば良い。
なお、粉末状の水素化ナトリウムとして市販品を用いる場合には、そのカタログ値を水素化ナトリウムの平均粒子径とみなし得る。
粉末状の水素化ナトリウムおよび粉末状のシリコンに対する炭化水素系分散媒の量の好ましい範囲として、粉末状の水素化ナトリウムおよび粉末状のシリコンの質量の合計を100質量部としたときに、20質量部以上の範囲内、50質量部以上の範囲内、75質量部以上の範囲内、または100質量部以上の範囲内の各範囲が例示される。なお、粉末状の水素化ナトリウムおよび粉末状のシリコンに対する炭化水素系分散媒の量の好ましい範囲には特に上限はないが、コスト面を考慮すると、1000質量部以下であるのが好ましい。
さらに、後述するように、本発明の製造方法により得られた本発明の負極活物質原料には結晶性Siが含まれないかまたは殆ど含まれない。このため本発明の製造方法では、既述した従来の製造方法、すなわちナトリウムとシリコンとを反応させて溶融塩状のナトリウムシリサイドを生成する方法とは異なり、反応系を過剰にナトリウムリッチにする必要がない。
なお、本明細書でいう濾別とは、水素化ナトリウムおよびシリコンを、炭化水素系分散媒等の洗浄用溶媒および除去対象であるコート材から分離することを意味し、濾紙等の濾材を用いてこれらを分離しても良いし、既知の固液分離や分液の技術を用いてこれらを分離しても良い。
・混合工程
粉末状の水素化ナトリウムとして、パラフィンでコートされたものを用いた。当該粉末は65.7質量%の水素化ナトリウムを含有し、パラフィンを含む当該粉末の平均粒子径は10μmであり、その質量は252.6gである。
粉末状のシリコンとしては、平均粒子径5μmのシリコン粉末185gを用いた。
炭化水素系分散媒として500mlのヘキサンを用い、上記の粉末状のシリコンおよび粉末状の水素化ナトリウムに当該炭化水素系分散媒を投入し、メカニカルスターラーにて窒素雰囲気下、25℃で10分間攪拌した。これにより、粉末状の水素化ナトリウムと粉末状のシリコンとが均一または略均一に混合されたNa-Si混合原料を得た。
混合工程で得られたNa-Si混合原料は、粉末状の水素化ナトリウム、粉末状のシリコンおよび炭化水素系分散媒を含み、さらに、粉末状の水素化ナトリウムにはコート材たるパラフィンが残存していると考えられる。実施例1の製造方法における洗浄工程では、炭化水素系分散媒およびパラフィンをNa-Si混合原料から除去するための洗浄工程を行った。
炭化水素系分散媒の除去後、粉末状の水素化ナトリウムおよび粉末状のシリコンを含む濾過残渣に500mlの洗浄用溶媒を加え、攪拌機にて窒素雰囲気下、25℃で10分間攪拌し、その後粉末状の水素化ナトリウムおよび粉末状のシリコンを濾別する洗浄を2回繰り返した。なお、洗浄用溶媒としては、炭化水素系分散媒と同じヘキサンを用いた。
洗浄工程後のNa-Si混合原料全量を反応容器に配置し、当該反応容器内にアルゴンガスを100ml/分の速度で流通させつつ、マッフル炉で600℃、10時間加熱することで、ナトリウムとシリコンとを反応させた。加熱後、冷却を経て得られた反応生成物は、互いに凝集した粒子状をなしているように視認された。ナトリウムシリサイドの融点は800℃付近であるために、実施例1の製造方法における反応工程では、ナトリウムとシリコンとの反応で生成したナトリウムシリサイドは溶融塩状にならなかったものと推測される。
アルゴン雰囲気下のグローブボックス内にて、スパチュラを用いて上記の反応生成物を反応容器から掻き取り、乳鉢で軽く解砕した。解砕後の反応生成物を実施例1の負極活物質原料とした。
なお、実施例1の負極活物質原料の質量は330gであったため、実施例1の製造方法における収率は、質量基準で約94%であった。
粉末状のシリコン140gとブロック状のナトリウム125±1gとを反応容器に入れ、当該反応容器内にアルゴンガスを100ml/分の速度で流通させつつ、マッフル炉で880℃、1時間加熱した後に冷却し、固い塊状の反応生成物を得た。アルゴン雰囲気下のグローブボックス内にて、反応容器をハンマーで叩いて当該反応生成物を取り出し、続いて当該反応生成物をハンマーにて粉砕した後、粉砕機にてさらに粉砕した。粉砕機としては大阪ケミカル株式会社製のワンダークラッシャーWC-3を用い、粉砕時間はメモリ5にて20秒間であった。
なお、比較例1の負極活物質原料の質量は250gであったため、比較例1の製造方法における収率は、質量基準で約94%であった。
比較例2の製造方法は、再加熱を行わなかったこと以外は比較例1の製造方法と同じである。比較例2の製造方法により比較例2の負極活物質原料を得た。
実施例1の負極活物質原料、比較例1の負極活物質原料および比較例2の負極活物質原料につき、粉末X線回折装置にてX線回折測定を行った。実施例1の負極活物質原料のX線回折チャートを図1に示し、比較例1の負極活物質原料および比較例2の負極活物質原料のX線回折チャートを図2に示す。なお、図1には、ナトリウムシリサイドに由来するピークの位置(図中のNaSi)を併記した。また、図2にはナトリウムシリサイドに由来するピークの位置(図中のNaSi)、および、シリコンに由来するピークの位置(図中のSi)を併記した。
このことから、シリコンと塊状のナトリウムとを単に加熱するだけの比較例2の負極活物質原料の製造方法では、ナトリウムおよびシリコンからナトリウムシリサイドが生じる反応は十分に進行しないことが裏付けられる。また、比較例1の負極活物質原料では結晶性シリコンに由来するピークが認められなかったことから、初回の加熱後に解砕および再加熱を行うことで、ナトリウムおよびシリコンからナトリウムシリサイドが生じる反応が十分に進行することが裏付けられる。
この結果から、本発明の製造方法が負極活物質原料の工業的な生産に好適であることが裏付けられる。
Claims (2)
- 粉末状の水素化ナトリウムと粉末状のシリコンとを炭化水素系分散媒中で混合してNa-Si混合原料を得る混合工程と、
前記Na-Si混合原料をナトリウムシリサイドの融点未満の温度で加熱して前記ナトリウムシリサイドを得る反応工程と、を具備する、負極活物質原料の製造方法。 - 前記混合工程後かつ前記反応工程前に、前記Na-Si混合原料を洗浄し前記水素化ナトリウムおよび前記シリコンを濾別する洗浄工程を具備する、請求項1に記載の負極活物質原料の製造方法。