JP2021053946A - 透明ガスバリア性吸水積層体 - Google Patents
透明ガスバリア性吸水積層体 Download PDFInfo
- Publication number
- JP2021053946A JP2021053946A JP2019179454A JP2019179454A JP2021053946A JP 2021053946 A JP2021053946 A JP 2021053946A JP 2019179454 A JP2019179454 A JP 2019179454A JP 2019179454 A JP2019179454 A JP 2019179454A JP 2021053946 A JP2021053946 A JP 2021053946A
- Authority
- JP
- Japan
- Prior art keywords
- water
- layer
- absorbing agent
- transparent gas
- absorbing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明による透明ガスバリア性吸水積層体は、様々な分野の製品に適用することができ、例えば、車載用のネジ、シャフト、金属板、等の金属製品、及び電気部品等を防錆する為の包装材料や、食品や医薬品等の水分による劣化を抑制する為の包装材料として好適に用いることができる。
金属製品内容物への防錆を目的として、常温で揮発して防錆効果を発揮する気化性の高い防錆剤を樹脂に含有させた包装用積層体が、特許文献1〜3で提案されているが、外装による密閉が必要であったり、気化した防錆剤が内容物に付着した場合に、内容物が劣化したり機能的障害を生じたり等、防錆効果以外の影響が懸念され、除去するにも手間が煩雑であるために用途が限定されており、揮発性の防錆剤を用いない防錆積層体が望まれている。
食品や医薬品の包装には、PTP包装、ブリスター包装が広く使われているが、従来は防湿性が不十分なものが多くあり、それを補うために、アルミニウム箔ピロー袋を外袋として用いて乾燥剤を同梱している。しかしながら、外袋開封後の防湿性が不十分であり、乾燥剤の誤飲事故が多い。
PTPまたはブリスター包装材料の防湿性を改良する為に、包装材料に乾燥剤やバリア層を含ませることが、特許文献4で提案されているが、包装材料の透明性が不十分であり、内容物の変質状態を確認するための視認性に劣るものであった。
すなわち、本発明は、以下の点を特徴とする。
1.少なくとも、基材層と、シーラント層とを有する透明ガスバリア性吸水積層体であって、
該基材層は、透明ガスバリア性フィルムを含み、
該シーラント層は、吸水剤とヒートシール性樹脂とを含み、
該吸水剤は、無機吸水剤および/または有機吸水剤を含有し、
該吸水剤を含有する層中の、該吸水剤の含有量が、0.5質量%以上、70質量%以下である、
透明ガスバリア性吸水積層体。
2.前記吸水剤が、無機吸水剤および/または有機吸水剤であり、
該無機吸水剤は、ゼオライト、活性白土、有機金属構造体からなる群から選ばれる1種または2種以上である、
該有機吸水剤は、ポリ(メタ)アクリル酸、ポリ(メタ)アクリル酸アルカリ金属塩、ポリ(メタ)アクリル酸アルカリ土類金属塩、ポリ酢酸ビニル、ポリビニルアルコールからなる群から選ばれる1種または2種以上を含有する、
上記1記載の、透明ガスバリア性吸水積層体。
3.全光線透過度が60%以上、99%以下である、
上記1または2に記載の、透明ガスバリア性吸水積層体。
4.前記無機吸水剤の1次粒子の数平均粒子径が、1nm以上、400nm以下であり、
前記無機吸水剤の前記シーラント層中での2次粒子を含めた数平均粒子径が、20μm以下である、
上記1〜3の何れかに記載の、透明ガスバリア性吸水積層体。
5.前記有機吸水剤の屈折率が、1.3以上、2.0未満であり、
前記ヒートシール性樹脂の屈折率が、1.3以上、2.0未満であり、
前記有機吸水剤の屈折率と、前記ヒートシール性樹脂の屈折率との差の絶対値が、0以上、1.0以下である、
上記1〜4の何れかに記載の、透明ガスバリア性吸水積層体。
6.上記1〜5の何れかに記載の透明ガスバリア性吸水積層体を用いて作製された、透明ガスバリア性吸水包装材料。
また、各図においては省略されているが、各層の間に接着剤層を設けることもできる。
さらに、必要に応じて、各層間の接着強度(密着強度)を強固にするために、各層の積層面に、コロナ放電処理、オゾン処理、プラズマ処理、グロー放電処理、サンドブラスト処理等のなどの物理的な表面処理や、化学薬品を用いた酸化処理などの化学的な表面処理
を予め施しておくこともできる。
なお、本発明においては、フィルムとシートとは同義として扱い、吸水は、気体および/または液体の水を吸収することを指す。
本発明の透明ガスバリア性吸水積層体は、少なくとも、基材層と、シーラント層とを有する、透明で、ガスバリア性と吸水とを有する積層体である。
該基材層がガスバリア性フィルムを含むことによって、水分の浸透を抑制することができ、該シーラント層が、吸水剤を含有することによって、水分を吸着し、ヒートシール性樹脂を含有することによって、ヒートシール性を発揮することができる。
また透明ガスバリア性吸水積層体に支持性が不足している場合には、さらに、補強層を含むことができる。
透明ガスバリア性吸水積層体の全光線透過度は、60%以上、99%以下が好ましい。上記範囲よりも低いと透明性が劣る傾向になり、内容物の視認が困難になり易い。上記範囲よりも高くすることは困難であり、生産工程や品質管理が複雑になって生産性が劣り易い。
ここで、全光線透過度とは、JIS K 7361(プラスチックの光学的特性試験法)に規定された方法によって、色彩情報測定機器等を用いて測定される、光線の透過率のことである。
上記において、一般的な添加剤としては、例えば、アンチブロッキング剤、滑剤、架橋剤、酸化防止剤、紫外線吸収剤、光安定剤、充填剤、補強剤、帯電防止剤、顔料、改質用樹脂等を含有することができる。
基材層は透明ガスバリア性フィルムを含む。
透明ガスバリア性フィルムは、透明性とガスバリア性と支持性とを有することが好ましい。
透明ガスバリア性フィルムとしては、例えば、透明なガスバリア性樹脂からなる透明基材フィルム、透明無機蒸着層付き樹脂フィルム等が挙げられる。
基材層は、1層で構成されていてもよく、同じ又は異なる組成の任意の積層手段によって積層された2層以上の多層で構成されていてもよい。
基材層は、透明ガスバリア性フィルム以外の素材からなる層を含んでいてもよく、例えば、基材層に支持性が不足している場合には、透明な補強フィルムからなる補強層を含むことができる。
また、基材層の片面若しくは両面に、印刷層を設けることもできる。
基材層の厚さは、当業者が適宜に設定することができるが、積層体に適切な強度や腰を付与する目的から、基材層の厚さは、5μm以上、100μm以下が好ましく、7μm以上、50μm以下がより好ましい。
透明基材フィルムは、ガスバリア性樹脂からなり、基材層を構成する透明な樹脂フィルムである。
透明基材フィルムは、気体の透過を抑制し、包装体を作製した際に、包装体外部から包装体内部の内容物収容部への酸素や水蒸気の侵入を抑え、内容物収容部から外側へのガス成分の拡散を抑えることができる。
透明基材フィルムは、1層で構成されていてもよく、同じ又は異なる組成の任意の積層手段によって積層された2層以上の多層で構成されていてもよい。
透明基材フィルムは、さらに、支持性を有することが好ましく、未延伸フィルム、あるいは一軸方向または二軸方向に延伸した延伸フィルム等のいずれのものでも使用することができる。
また、透明基材フィルムは、無機蒸着層の無機蒸着層支持フィルムを兼ねていてもよい。このような場合には、無機蒸着層付きの基材フィルムの無機蒸着層がシーラント層側に積層されて用いられることが好ましい。
ガスバリア性樹脂としては、例えば、ポリ塩化ビニリデン系樹脂(PVDC)、ポリエステル系樹脂、ポリアミド系樹脂(特にナイロンMXD6等の芳香族ポリアミド)、エチレン−酢酸ビニル共重合体(酢酸ビニルがおよそ79wt%〜92wt%)を完全ケン化したエチレン含有率25モル%〜50モル%のエチレン−ビニルアルコール共重合体(EVOH)、ポリビニルアルコール、ポリアクリロニトリル、その他等が挙げられる。
透明無機蒸着層付き樹脂フィルムは、透明な無機蒸着層と、該無機蒸着層を支持する透明な支持樹脂フィルムからなり、基材層を構成する透明なフィルムである。
支持樹脂フィルムには、無機蒸着層の形成工程に耐えられるような、機械的、物理的、化学的、その他等において優れた性質を有し、特に強度を有して強靭であり、かつ、耐熱性を有する樹脂からなる樹脂フィルムを用いることが好ましい。
支持樹脂フィルムに含有される好適な樹脂としては、例えば、ポリエチレンテレフタレート(PET)、ポリブチレンテレフタレート(PBT)等のポリエステル系樹脂;各種ナイロン等のポリアミド系樹脂;ポリエチレン系樹脂、ポリプロピレン系樹脂、環状ポリオレフィン樹脂、ポリスチレン系樹脂、アクリロニトリル−スチレン共重合体(AS樹脂
)、アクリロニトリル−ブタジエン−スチレン共重合体(ABS樹脂)、ポリブデン樹脂フィルム等のポリオレフィン系樹脂;ポリ塩化ビニル系樹脂、ポリカーボネート系樹脂、ポリイミド系樹脂、ポリアミドイミド系樹脂、ポリアリールフタレート樹脂、シリコーン系樹脂、ポリスルホン系樹脂、ポリフェニレンスルフィド系樹脂、ポリエーテルスルホン系樹脂、ポリウレタン系樹脂、セルロース系樹脂、ポリ(メタ)アクリル系樹脂、ポリ塩化ビニリデン、アセタール系樹脂、フッ素系樹脂、その他等を挙げることができる。これらの樹脂は、1種または2種以上を混合して用いてもよく、種類の異なる樹脂を含有する多層で用いてもよい。
本発明においては、これらの中でも、特に、ポリエステル系樹脂および/またはポリアミド系樹脂を含有することが好ましい。
透明な無機蒸着層を形成する無機化合物としては、無機酸化物、無機窒化物、無機炭化物等が挙げられる。
無機元素としては、リン(P)元素や金属元素が好ましく、金属元素の具体例としては、例えば、アルミニウム(Al)、ケイ素(Si)、マグネシウム(Mg)、カルシウム(Ca)、カリウム(K)、スズ(Sn)、ナトリウム(Na)、ホウ素(B)、チタン(Ti)、鉛(Pb)、ジルコニウム(Zr)、イットリウム(Y)、亜鉛(Zn)、バナジウム(V)、バリウム(Ba)、クロム(Cr)等が挙げられ、上記の無機元素の1種または2種以上を組み合わせて用いることができる。
上記の中でも、金属酸化物が特に好ましく用いられる。
上記において、X=0の場合は金属であり、また、Xの範囲の上限は、完全に酸化した場合の値である。
すなわち、Xの値の範囲は0よりも大きく、上限値は、例えば、ケイ素は2、アルミニウムは1.5、マグネシウムは1、カルシウムは1、カリウムは0.5、スズは2、ナトリウムは0.5、ホウ素は1、5、チタンは2、鉛は1、ジルコニウムは2、イットリウムは1.5である。
アルミニウム元素からなる無機化合物の具体例としては、Xが1.0〜2.0の範囲の酸化アルミニウムが好ましく、珪素元素からなる無機化合物の具体例としては、Xが0.5〜1.5の範囲の酸化珪素が好ましい。
無機蒸着層は、これらの無機化合物の1種または2種以上を組み合わせて用いてもよい。
無機蒸着層は、1層であってもよく、2層以上であってもよい。1層の場合には、1種の無機化合物で形成されていてもよく、2種以上の無機化合物の混合物で形成されていてもよい。2層の場合には、同一または異なる組成の層が積層されていてもよく、各層は、1種または2種以上の無機化合物から形成されていてもよい。
更に、具体的に説明すると、上記のPVD法では、例えば、巻き取り式蒸着機を使用し、真空チャンバーの中で、巻き出しロールから出た無機蒸着層支持フィルムを蒸着チャンバーの中に入れ、ここで、るつぼで熱せられた蒸着源を蒸発させ、更に、必要ならば、酸素吹き出し口より酸素等を噴出させながら、冷却したコーティングドラム上の樹脂フィルムの上に、マスクを介して無機蒸着層を形成し、次いで無機蒸着層が形成されたガスバリアフィルムを巻き取りロールに巻き取ることによって、本発明にかかる無機蒸着層を有する樹脂フィルムを製造することができる。
更に詳しくは、上記のPVD法においては、酸化アルミニウムからなる無機蒸着層の厚さは、200Å〜1000Åが好ましく、300Å〜500Å位がより好ましい。
また、上記のCVD法においては、酸化珪素からなる無機蒸着層の厚さは、50Å〜500Åが好ましく、100Å〜300Åがより好ましい。
上記範囲よりも厚いと、無機蒸着層にクラック等が入りやすくなり、ガスバリア性が低下するという危険性があると共に、工程時間が長くなり生産性が低下する為に好ましくない。また、上記範囲よりも薄いと、十分なガスバリア性を奏することが困難になり易い。
シーラント層は、吸水剤とヒートシール性樹脂とを含有する1層で構成されていてもよく、吸水剤を含有する吸水層と、ヒートシール性樹脂を含有してヒートシール性に優れるヒートシール層との多層で構成されていてもよい。
シーラント層は、吸水剤とヒートシール性樹脂とを含有するシーラントフィルムから形成された層であることが好ましい。
シーラントフィルムに支持性が不足している場合には、シーラントフィルムに補強層を含むことができる。
シーラントフィルムは、片面または両面がヒートシール性を有することが好ましく、その為には、シーラントフィルムの片面表面にヒートシール層が積層されていてもよく、両面表面にヒートシール層が積層されていてもよい。
シーラントフィルムの表面にヒートシール性があれば、他の層と積層する際の界面接着性が高くなり、ヒートシール性を高くすることができる。
そして、シーラント層を構成する各層は、接着剤層を介して積層されていてもよい。
吸水層は、吸水剤を含有する層であり吸水剤を分散させるための熱可塑性樹脂を含有する。また、吸水層は、ヒートシール性の熱可塑性樹脂を含有していてもよく、十分なヒートシール性を有していれば、同時にヒートシール層にもなり得る。
吸水層の厚みに特に制限は無いが、10μm以上、100μm以下が好ましい。上記範
囲よりも薄いと吸水効果を充分に発揮し難く、上記範囲よりも厚くても吸水効果はそれほど向上せず、積層体の剛性が強くなりすぎて、包装材料の用途としての使い勝手が悪くなり易い。
具体的には、吸水剤を熱可塑性樹脂に相対的に高濃度でメルトブレンドしてマスターバッチを調整し、次いで、所望の吸水層中の濃度になるように、マスターバッチと他の成分とをドライブレンドして用いることが好ましい。
メルトブレンドされる熱可塑性樹脂としては、1種であっても2種以上であってもよい。
吸水剤のマスターバッチ中の含有量は、20質量%以上、90質量%以下が好ましく、30質量%以上、70質量%以下がより好ましい。上記の範囲であれば、吸水層中に必要かつ十分な量の吸水剤を分散した状態で含有させることが容易である。
該吸水剤は、無機吸水剤および/または有機吸水剤を含有することが好ましい。
無機吸水剤は、気体の水分または液体の水分を吸収する無機化合物であり、ゼオライト、活性白土、有機金属構造体(MOF:Metal Organic Frameworks)からなる群から選ばれる1種または2種以上を含有することが好ましい。また、他の吸水剤を併用することもできる。
ここで、細孔径は、A型ゼオライトは0.3〜0,5nmのものが好ましく、CHA型ゼオライトは0.38nm前後のものが好ましく、MFI型ゼオライトは0.55nm前後のものが好ましく。
比表面積は、MFI型ゼオライトは300〜400m2/gのものが好ましい。
上記のゼオライトは、水以外にも、その細孔径に応じた分子サイズ、比表面積に応じた量のガスを吸収できる。例えば、CHA型ゼオライトは、低級炭化水素、二酸化炭素を、MFI型ゼオライトは、二酸化炭素、低級炭化水素、低級アルデヒド類、低級有機酸、低級アルコールを吸着する能力に優れる。
活性白土は比表面積の大きいものが好ましく、比表面積に特に制限は無いが、比表面積50〜400m2/g、細孔径4〜7nmのものが入手し易い。pH(5%サスペンジョン)は2.5〜9が好ましく、3〜7がより好ましい。
上記の金属有機構造体は、一般的な活性炭やゼオライトと比較して、より小さな細孔径と、より大きな比表面積を有する多孔質構造を有することができる。
ン酸鉄、テレフタル酸アルミニウム、テレフタル酸ジルコン、2−メチルイミダゾール亜鉛、ギ酸マグネシウム、ベンゼン−1,3,5−トリ安息香酸亜鉛、2,6−ナフタレン−ジカルボン酸亜鉛、アミノベンゼン−1,4−ジカルボン酸アルミニウム、2,5−ジオキシドベンゼン−1,4−ジカルボキレートマグネシウム、4,4−ジオキシドビフェニル−3,3−ジカルボキシレートマグネシウム)等が挙げられ、これらの群から選ばれる1種または2種以上を用いることができる。
Langmuir比表面積の場合は、500m2/g以上、5000m2/g以下が好ましく、1200m2/g以上、2400m2/g以下がより好ましい。
BET比表面積は例えば、トリメシン酸銅が1500m2/g、テレフタル酸アルミニウムが950m2/g、フマル酸アルミニウムが1000m2/g、トリメシン酸アルミニウムが1100m2/g、トリメシン酸ジルコンが2060m2/g、ギ酸マグネシウムが400m2/g、ベンゼン−1,3,5−トリ安息香酸亜鉛が3600m2/gのものがある。
Langmuir比表面積は例えば、トリメシン酸銅が2000m2/g、テレフタル酸アルミニウムが1500m2/g、フマル酸アルミニウムが1200m2/g、トリメシン酸アルミニウムが1500m2/g、トリメシン酸ジルコンが2390m2/g、ギ酸マグネシウムが500m2/g、ベンゼン−1,3,5−トリ安息香酸亜鉛が5000m2/gのものがある。
上記の有機金属構造体は、水以外にも、その細孔径に応じた分子サイズ、比表面積に応じた量のガスを吸着できる。例えばトリメシン酸銅は、低級炭化水素(特にメタン)と二酸化炭素を、テレフタル酸アルミニウムは、メタン、水、二酸化炭素を吸着する能力に優れ、フマル酸アルミニウムとトリメシン酸ジルコンは、水を吸着する能力に優れ、トリメシン酸アルミニウム、低級炭化水素(特にメタン)と水を吸着する能力に優れる。
また、1次粒子は凝集して2次粒子を生じていることが多い為、ジェットミル等の公知の粉砕手段によって微粒子化してから用いることが好ましく、透明吸水性フィルム中における、2次粒子を含む数平均粒子径が、1nm以上、20μm以下であることが好ましい。上記範囲より小さくすることは1次粒子の数平均粒子径の下限であるために困難であり、上記範囲よりも大きいと、透明吸水性フィルムの透明性を得ることが困難になり易い。
有機吸水剤は、気体の水分または液体の水分を吸収する有機樹脂であり、ポリ(メタ)アクリル酸、ポリ(メタ)アクリル酸アルカリ金属塩、ポリ(メタ)アクリル酸アルカリ土類金属塩、ポリ酢酸ビニル、ポリビニルアルコールからなる群から選ばれる1種または2種以上を含有することが好ましい。また、他の吸水剤を併用することもできる。
例えば、アクリル酸重合体、メタクリル酸重合体、アクリル酸−メタクリル酸共重合体、アクリル酸−マレイン酸共重合体、メタクリル酸−マレイン酸共重合体、アクリル酸−メタクリル酸−マレイン酸共重合体、等が挙げられる。
例えば、ポリ(メタ)アクリル酸ナトリウム塩、ポリ(メタ)アクリル酸リチウム塩等が挙げられる。
例えば、ポリ(メタ)アクリル酸カルシウム塩等が挙げられる。
本発明において、屈折率は、JIS K 7142:2008に従って、フィルム化されて、Abbe屈折計を使って、波長589nmの光で測定された値である。
ヒートシール層は、ヒートシール性樹脂を含有し、十分なヒートシール性を有する層であり、有機吸水剤を含有していてもよく、含有していなくてもよいが、有機吸水剤を含有しない場合の方がヒートシール性が高く、好ましい。
吸水層中に含有される熱可塑性樹脂は、有機吸水剤の分散性に優れ、包装材料の用途に耐え得るものであれば特に制限は無い。
また、熱可塑性樹脂は、ヒートシール性樹脂であってもよく、或いは、ヒートシール性樹脂を含有することもできる。
熱可塑性樹脂としては、ポリオレフィン系樹脂を含有することが好ましい。
ポリオレフィン系樹脂の具体例としては、低密度ポリエチレン(LDPE)、中密度ポリエチレン(MDPE)、高密度ポリエチレン(HDPE)、直鎖状(線状)低密度ポリエチレン(LLDPE)、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸エチル共重合体、エチレン−アクリル酸共重合体、エチレン−メタクリル酸共重合体、エチレン−メチルメタクリル酸共重合体、エチレン−プロピレン共重合体等及びこれらの樹脂の混合物が挙げられる。
上記の中でも、ポリエチレン系の樹脂が好ましく、ポリエチレン系の樹脂の中でも、LDPE、LLDPE、汎用PE、PE系共重合体等がより好ましく、LLDPEが更に好ましい。
吸水層が有機吸水剤を含有する場合、熱可塑性樹脂の屈折率は、1.3以上、2.0未満が好ましく、ヒートシール性樹脂の屈折率との差の絶対値が、0以上、1.0以下であることが好ましい。屈折率が上記範囲より高くても低くても、ヒートシール性樹脂との屈折率差が上記範囲内になることが困難であり、屈折率差が上記範囲よりも大きいと透明吸水性フィルムの透明性を得ることが困難になり易い。
ヒートシール性樹脂は、熱によって溶融して融着し得るものであれば、特に制限無く、公知のヒートシール性樹脂を用いることができる。
ヒートシール性熱可塑性樹脂の具体例としては、ポリエチレン、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖状(線状)低密度ポリエチレン、メタロセンポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体、アイオノマー樹脂、エチレン−(メタ)アクリル酸エチル共重合体、エチレン−(メタ)アクリル酸共重合体、エチレン−プロピレン共重合体、メチルペンテンポリマー、ポリエチレンまたはポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタクリル酸、無水マレイン酸、フマル酸その他等の不飽和カルボン酸で変性したポリオレフィン系樹脂、エチレン−(メタ)アクリル酸エステル−不飽和カルボン酸の三元共重合体樹脂、環状ポリオレフィン樹脂、環状オレフィンコポリマー、ポリエチレンテレフタレート(PET)、ポリアクリロニトリル(PAN)などが挙げられる。
これらの中でも、ポリオレフィン系樹脂が好ましく、ポリエチレン系樹脂がより好ましく、低密度ポリエチレン(LDPE)、直鎖状(線状)低密度ポリエチレン(LLDPE)がさらに好ましい。
吸水層が有機吸水剤を含有する場合、ヒートシール性樹脂の屈折率は、1.3以上、2.0未満が好ましく、有機吸水剤の屈折率との差の絶対値が、0以上、1.0以下であることが好ましい。屈折率が上記範囲より高くても低くても、ヒートシール性樹脂との屈折率差が上記範囲内になることが困難であり、屈折率差が上記範囲よりも大きいと透明吸水性フィルムの透明性を得ることが困難になり易い。
例えば、各種ポリエチレン系樹脂の屈折率は約1.5であり、各種(メタ)アクリル系樹脂の屈折率は約1.5であり、各種PET系樹脂の屈折率は約1.5〜約1.7である。
接着剤層に用いられる接着剤に特に制限は無く、DL(ドライラミネート)用接着剤、EC(エクストルージョンコート)用接着剤、ノンソルベントラミネート用接着剤、任意のアンカーコート剤等を用いることができる。
また、接着剤は、熱硬化型、紫外線硬化型、電子線硬化型等のいずれであってよく、水
性型、溶液型、エマルジョン型、分散型等のいずれの形態でもよく、また、その性状は、フィルム/シート状、粉末状、固形状等のいずれの形態でもよく、更に、接着機構については、化学反応型、溶剤揮発型、熱溶融型、熱圧型等のいずれの形態でもよい。
補強層は補強フィルムからなる層であり、透明ガスバリア性吸水積層体に支持性が不足している場合に含まれることが好ましい。
補強フィルムには、機械的、物理的、化学的、その他等において優れた性質を有し、特に、強度を有して強靱であり、かつ耐熱性を有する一般的な公知公用の補強用のフィルムを用いることができる。
補強フィルムとしては、各種の樹脂フィルムを用いることができる。
十分な支持性を得る為の補強フィルム用の樹脂フィルムとしては、ポリエチレンテレフタレート(PET)やポリエチレンナフタレート等のポリエステル系樹脂、ポリプロピレン等のポリオレフィン系樹脂、ナイロン等のポリアミド系樹脂、ポリアラミド系樹脂、ポリカーボネート系樹脂、ポリアセタール系樹脂、フッ素系樹脂、その他等の強靱な熱可塑性樹脂を用いて作製された樹脂フィルムが挙げられる。
そして、補強フィルムには、未延伸フィルム、あるいは一軸方向または二軸方向に延伸した延伸フィルム等のいずれのものでも使用することができる。
上記の中でも、ポリエステル系樹脂および/またはポリアミド系樹脂を含む樹脂フィルムが好ましく、二軸延伸PETフィルム、二軸延伸ナイロンフィルムが、より好ましく用いられる。
上記のような材料を使用して、透明ガスバリア性吸水積層体を製造する方法について説明する。下記に示した作製方法は1例であって、本発明を限定するものではない。
透明ガスバリア性吸水積層体を構成する各層の積層は、通常の包装材料を製造するときに使用するラミネートする方法、例えば、ウェットラミネーション法、ドライラミネーション法、無溶剤型ドライラミネーション法、押し出しラミネーション法、Tダイ共押し出し成形法、共押し出しラミネーション法、インフレーション法、その他等の任意の方法で行うことができる。
そして、上記の積層を行う際に、必要ならば、例えば、コロナ処理、オゾン処理等の前処理を各層の表面に施すことができる。また、例えば、イソシアネート系(ウレタン系)、ポリエチレンイミン系、ポリブタジェン系、有機チタン系等のアンカーコーティング剤、あるいはポリウレタン系、ポリアクリル系、ポリエステル系、エポキシ系、ポリ酢酸ビニル系、セルロース系、その他等のラミネート用接着剤等のアンカーコート剤等を任意に使用することができる。
バリア性吸水積層体を作製する場合について、一例を説明する。
先ず、シーラント層1用の樹脂と、該吸水層用の樹脂組成物と、シーラント層2用の樹脂とを、インフレーション製膜によって製膜及び積層して、ヒートシール層1/吸水層/ヒートシール層2、という層構成のシーラントフィルムを作製することができる。
二次加工の例としては、エンボス加工、塗装、接着、印刷、メタライジング(めっき等)、機械加工、表面処理(帯電防止処理、コロナ放電処理、プラズマ処理、フォトクロミズム処理、物理蒸着、化学蒸着、コーティング、等)等が挙げられる。また、透明ガスバリア性吸水積層体に、ラミネート加工(ドライラミネートや押し出しラミネート)、製袋加工、およびその他の後処理加工を施すこともできる。
本発明の透明ガスバリア性吸水包装材料は、本発明の透明ガスバリア性吸水積層体から作製された包装材料であり、透明ガスバリア性吸水積層体と同様な透明性、吸水性を有し、ヒートシール性に優れることができる。
透明ガスバリア性吸水包装材料は、必要に応じて、種々の機能を有する層をさらに含んでいてもよい。
本発明の透明ガスバリア性吸水包装材料は、シーラント層側が内容物に近くなるように包装して用いることが好ましい。この場合、ガスバリア性の基材層が外部からの水分の侵入を抑制し、吸水性のシーラント層が内容物収容空間内の湿度を下げて、内容物を効率的に低湿度環境下で収容することができる。
[基材層用フィルム]
・透明蒸着フィルム1:大日本印刷(株)社製酸化アルミニウム蒸着膜付きPETフィルム、IB−PET−PXB2。12μm厚
・アルミニウム箔1:東洋アルミニウム(株)社製。9μm厚。
・金属蒸着フィルム1:アルミニウム蒸着PETフィルム。12μm厚
・DL接着剤1:ロックペイント(株)社製ドライラミネート用接着剤、RU−004/H1。
下記の無機吸水剤を用いたが、すべて、1次数平均粒子径は1〜400nmであるが、凝集物を多く含んでいた為に、ジェットミルによって数平均粒子径が20μm以下になるように粉砕してから用いた。
・無機吸水剤1:BASF社製金属有機構造体、A520。フマル酸アルミニウム。細孔径1.1nmおよび0.5nm。
・無機吸水剤2:BASF社製金属有機構造体、A100。テレフタル酸アルミニウム。細孔径0.8nmおよび0.5nm。
・無機吸水剤3:BASF社製金属有機構造体、A300。トリメシン酸アルミニウム。
細孔径0.7nmおよび0.6。
・無機吸水剤4:BASF社製金属有機構造体、Zr−300。トリメシン酸ジルコン。細孔径0.46nm、1.15nm、および1.8nm。
・無機吸水剤5:BASF社製金属有機構造体、C300。トリメシン酸銅。細孔径0.90nm又は0.3nm及び0.5nm。
・有機吸水剤1:東洋紡(株)社製ポリアクリル酸,タフチックHU720SF。数平均粒子径4μm、屈折率1.42。
・有機吸水剤2:日本触媒(株)社製ポリアクリル酸ナトリウム及び共重合体、アクアリックAS。数平均粒子径20μm以下、屈折率1.42、pH3.0。
・有機吸水剤3:日本触媒(株)社製ポリアクリル酸ナトリウム及び共重合体、アクアリックFH。数平均粒子径20μm以下、屈折率1.42、pH9.5。
・有機吸水剤4:日本触媒(株)社製ポリアクリル酸ナトリウム及び共重合体、アクアリックIH。数平均粒子径20μm以下、屈折率1.42、pH9.5。
・有機吸水剤5:日本触媒(株)社製ポリアクリル酸ナトリウム及び共重合体、アクアリックYS。数平均粒子径20μm以下、屈折率1.42、pH6.5〜9.0。
・有機吸水剤6:住友精化(株)社製ポリアクリル酸ナトリウム部分中和物、アクアキープSA60。数平均粒子径5μm、屈折率1.42。
・有機吸水剤7:住友精化(株)社製ポリアクリル酸ナトリウム部分中和物、アクアキープSH−P。屈折率1.42。
・LLDPE1:プライムポリマー(株)社製LLDPE、エボリューSP2020。密度0.916g/cm3、MFR2.0g/10分、屈折率1.54。
・LDPE1:三菱ケミカル(株)社製LDPE、LC600A。密度0.918g/cm3、MFR7g/10分、屈折率1.54。
マスターバッチを下記のように調製した。
[マスターバッチ1の調製]
LDPE1と、有機吸水剤1とを下記割合でメルトブレンドし、マスターバッチ1(MB1)を得た。
LDPE1 40質量部
無機吸水剤1 60質量部
表1の配合に従って、マスターバッチ1と同様に、メルトブレンドし、マスターバッチ2〜13(MB2〜13)を得た。
吸水層用にはMB1をそのまま吸水層用樹脂組成物として用いて、ヒートシール層1とヒートシール層2用にはLLDPE1を用いて、170℃でインフレーション製膜によって積層し、下記層構成の透明なシーラントフィルムを得た。
層構成:ヒートシール層1(15μm厚)/吸水層(30μm厚)/ヒートシール層2(15μm厚)
次に、透明蒸着フィルム1の無機蒸着層面と、上記で得たシーラントフィルムとを、DL接着剤1(塗布量3.0g/m2)を介したドライラミネーション(乾燥温度70℃)によって貼り合わせて、下記層構成の透明ガスバリア性吸水積層体を得て、各種評価を実施した。
層構成:基材層[基材フィルム(12μm厚)/無機蒸着層]/接着剤層(3.0g/m2)/シーラント層[ヒートシール層1(15μm厚)/吸水層(30μm厚)/ヒートシール層2(15μm厚)]
MB1とLLDPE1とを下記割合でドライブレンドして、吸水層用樹脂組成物として用いたこと以外は実施例1と同様に操作して、同様に透明なシーラントフィルム、透明ガスバリア性吸水積層体を得て、評価した。
MB1 50質量部
LLDPE1 50質量部
表2〜6の配合に従って、実施例1と同様に操作して、吸水層用樹脂組成物を準備し、透明なシーラントフィルムを得て、実施例1と同様に操作して透明ガスバリア性吸水積層体を得て、同様に評価を実施した。
表2〜6の配合に従って、実施例2と同様に操作して、吸水層用樹脂組成物を準備し、透明なシーラントフィルムを得て、実施例1と同様に操作して透明ガスバリア性吸水積層体を得て、同様に評価を実施した。
MB1とLLDPE1とを下記割合でドライブレンドして、吸水層用樹脂組成物として
用いて、170℃でインフレーション製膜を行って、1層のみからなる60μm厚の透明なシーラントフィルムを得て、実施例1と同様に操作して透明ガスバリア性吸水積層体を得て、同様に評価を実施した。
MB1 30質量部
LLDPE1 70質量部
MB1とLLDPE1とを下記割合でドライブレンドして、吸水層用樹脂組成物として用いて、170℃でインフレーション製膜を行って、1層のみからなる60μm厚の透明なシーラントフィルムを得て、実施例1と同様に操作して透明ガスバリア性吸水積層体を得て、同様に評価を実施した。
MB1 8.3質量部
LLDPE1 91.7質量部
MB7とLLDPE1とを下記割合でドライブレンドして、吸水層用樹脂組成物として用いて、170℃でインフレーション製膜を行って、1層のみからなる60μm厚の透明なシーラントフィルムを得て、実施例1と同様に操作して透明ガスバリア性吸水積層体を得て、同様に評価を実施した。
MB7 8.3質量部
LLDPE1 91.7質量部
表8の配合に従って、実施例1と同様に操作して、吸水層用樹脂組成物を準備し、同様にシーラントフィルム、積層体を得て、同様に評価を実施した。
吸水層を含まない、LLDPE1のみからなる樹脂フィルム(60μm厚)を、170℃でインフレーション製膜してシーラントフィルムを得て、実施例1と同様に操作して積層体を作製し、同様に評価を実施した。
本願発明の実施例の吸水フィルムは、良好な製膜性、ヒートシール性、吸水性を示した。
一方、比較例1、2の不透明なガスバリア性フィルムを基材層に含むフィルムは透明性
が不十分な結果を示し、比較例3の吸水剤を含有しないフィルムは、吸水性が非常に不十分な結果を示し、比較例4の吸水剤を過剰に含有するフィルムは、製膜性とヒートシール性が不十分な結果を示した。
[製膜性]
シーラントフィルムの外観を肉眼で観察し、不良の有無を下記評価基準で評価した。
○:フィルムに皺、ぶつ、剥離が無かった。
×:フィルムに皺、ぶつ、剥離が有った。
積層体を100mm×100mmに切り分け、シーラント層面を重ね合せた後にヒートシールテスター(テスター産業社製:TP−701−A)を用いて、端部はヒートシールされずに二股に分かれている状態になるように1cm×10cmの領域をヒートシールし、さらに15mm幅で短冊状に切り分けて、ヒートシール強度測定用の試験片を作製した。
この試験片の二股に分かれている各端部を引張試験機に装着して、ヒートシール部を剥離するように引っ張って、ヒートシール強度(N/15mm幅)を測定して、下記合否基準で合否判定した。
(ヒートシール条件)
温度:160℃
圧力:1kgf/cm2
時間:1秒
(引張強度試験条件)
試験速度:300mm/分
荷重レンジ:50N
(合否判定基準)
○:30N/15mm以上であり、合格。
×:30N/15mm未満であり、不合格。
2枚のフィルムを縦100mm×横100mmの寸法に切断して重ねて3方をヒートシールし、文字を印刷した紙片を入れ、未ヒートシールの1方をヒートシールして75ccの空気を封入した。
そして、外側から内部の紙片上の文字が目視で視認できるか否か判断した。
積層体を縦210mm×横297mmの寸法に切断して包装袋を作製し、包装袋内部に温度・湿度データロガー(株)ティアンドデイ社製、TR−72wf)を入れ、包装袋内部の相対湿度を80%以上の空気に調整した後に密封して、25℃で放置し、初期値、7日後、10日後の湿度を測定した。
積層体を縦50mm×横50mmの寸法に切断し、JIS K 7361(プラスチックの光学的特性試験法)に準拠して色彩情報測定機器 ヘーズメーター(株式会社村上色彩技術研究所製 HM−150)により、全光線透過率およびヘイズを測定した。
2 透明ガスバリア性吸水包装材料
3 基材層
4 シーラント層
4a 吸水層
4b ヒートシール層
Claims (6)
- 少なくとも、基材層と、シーラント層とを有する透明ガスバリア性吸水積層体であって、
該基材層は、透明ガスバリア性フィルムを含み、
該シーラント層は、吸水剤とヒートシール性樹脂とを含み、
該吸水剤は、無機吸水剤および/または有機吸水剤を含有し、
該吸水剤を含有する層中の、該吸水剤の含有量が、0.5質量%以上、70質量%以下である、
透明ガスバリア性吸水積層体。 - 前記吸水剤が、無機吸水剤および/または有機吸水剤を含有し、
該無機吸水剤は、ゼオライト、活性白土、有機金属構造体からなる群から選ばれる1種または2種以上であり、
該有機吸水剤は、ポリ(メタ)アクリル酸、ポリ(メタ)アクリル酸アルカリ金属塩、ポリ(メタ)アクリル酸アルカリ土類金属塩、ポリ酢酸ビニル、ポリビニルアルコールからなる群から選ばれる1種または2種以上である、
請求項1記載の、透明ガスバリア性吸水積層体。 - 全光線透過度が60%以上、99%以下である、
請求項1または2に記載の、透明ガスバリア性吸水積層体。 - 前記無機吸水剤の1次粒子の数平均粒子径が、1nm以上、400nm以下であり、
前記無機吸水剤の前記シーラント層中での2次粒子を含めた数平均粒子径が、20μm以下である、
請求項1〜3の何れか1項に記載の、透明ガスバリア性吸水積層体。 - 前記有機吸水剤の屈折率が、1.3以上、2.0未満であり、
前記ヒートシール性樹脂の屈折率が、1.3以上、2.0未満であり、
前記有機吸水剤の屈折率と、前記ヒートシール性樹脂の屈折率との差の絶対値が、0以上、1.0以下である、
請求項1〜4の何れか1項に記載の、透明ガスバリア性吸水積層体。 - 請求項1〜5の何れか1項に記載の透明ガスバリア性吸水積層体を用いて作製された、透明ガスバリア性吸水包装材料。