JP2020105349A - 多彩塗料組成物 - Google Patents
多彩塗料組成物 Download PDFInfo
- Publication number
- JP2020105349A JP2020105349A JP2018245094A JP2018245094A JP2020105349A JP 2020105349 A JP2020105349 A JP 2020105349A JP 2018245094 A JP2018245094 A JP 2018245094A JP 2018245094 A JP2018245094 A JP 2018245094A JP 2020105349 A JP2020105349 A JP 2020105349A
- Authority
- JP
- Japan
- Prior art keywords
- emulsion
- resin
- glass transition
- paint
- transition temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記エマルジョン塗料は、顔料と、樹脂エマルジョンと、親水性コロイド形成物質と、を含み、前記樹脂エマルジョンのガラス転移温度TgAが前記バインダー樹脂のガラス転移温度TgBよりも小さいことを特徴とする。
本発明の多彩塗料組成物は、エマルジョン塗料をゲル化膜でカプセル化してなる着色ゲル状粒子と、バインダー樹脂と、を含んでいる。
エマルジョン塗料は、顔料と、樹脂エマルジョンと、親水性コロイド形成物質と、を含んでいる。そして、樹脂エマルジョンと、バインダー樹脂とは、互いにガラス転移温度Tgが異なる樹脂を用いる。
着色ゲル状粒子は、エマルジョン塗料をゲル化膜によってカプセル化(粒子化)してなるものであり、顔料と、樹脂エマルジョンと、親水性コロイド形成物質とを少なくとも含む。
顔料としては、無機系顔料及び有機系顔料のいずれでもよく、また、これらを混合したものであっても良い。
無機系顔料としては、例えば酸化チタン、酸化マグネシウム、酸化バリウム、酸化カルシウム、酸化亜鉛、酸化ジルコニウム、酸化イットリウム、酸化インジウム、チタン酸ナトリウム、酸化ケイ素、酸化ニッケル、酸化マンガン、酸化クロム、酸化鉄、酸化銅、酸化セリウム、酸化アルミニウムなどの金属酸化物系顔料;酸化鉄−酸化マンガン、酸化鉄−酸化クロム(例えば大日精化株式会社製の「ダイピロキサイドカラーブラック#9595」、アサヒ化成工業株式会社製の「Black6350」)、酸化鉄−酸化コバルト−酸化クロム(例えば大日精化株式会社製の「ダイピロキサイドカラーブラウン#9290」、「ダイピロキサイドカラーブラック#9590」)、酸化銅−酸化マグネシウム(例えば大日精化株式会社製の「ダイピロキサイドカラーブラック#9598」)、酸化マンガン−酸化ビスマス(例えばアサヒ化成工業株式会社製の「Black6301」)、酸化マンガン−酸化イットリウム(例えばアサヒ化成工業株式会社製の「Black6303」)などの複合酸化物顔料;シリコン、アルミニウム、鉄、マグネシウム、マンガン、ニッケル、チタン、クロム、カルシウムなどの金属系顔料;さらに鉄−クロム、ビスマス−マンガン、鉄−マンガン、マンガン−イットリウムなどの合金系顔料;パール顔料、マイカ顔料、マイカコーティングパール顔料、アルミニウム粉、ステンレス粉等の光輝性顔料;カオリン、硫酸バリウム、含水ケイ酸マグネシウム、炭酸カルシウム等の体質顔料が挙げられる。これらは単独で又は2種以上を組み合せて用いることができる。
樹脂エマルジョンとしては、ガラス転移温度Tgがバインダー樹脂と異なる樹脂エマルジョンを用いる。例えば、樹脂エマルジョンのガラス転移温度TgAが、バインダー樹脂のガラス転移温度TgBよりも低いものを用いる。より具体的には、樹脂エマルジョンとして、ガラス転移温度TgAが−25℃以上、0℃以下の範囲の樹脂を用いる。
親水性コロイド形成物質としては、例えばセルロース誘導体、ポリエチレンオキサイド、ポリビニルアルコール、カゼイン、デンプン、ガラクトマンノン、グアルゴム、ローカストビーンゴムなどの天然高分子などを含有する水溶液が挙げられる。これらは1種類単独で又は2種類以上を組み合せて用いてもよい。上記水溶液の中ではグアルゴムの水溶液が特に好ましい。水溶液の濃度は特に限定されるものではなく、例えば0.5〜5.0質量%であればよい。
エマルジョン塗料は、上述した顔料、樹脂エマルジョン、および親水性コロイド形成物質に加えて、更に必要に応じて、含水ケイ酸マグネシウムなどの体質顔料、増粘剤、分散剤、消泡剤、防腐剤及びレベリング剤等の添加剤をさらに含んでいてもよい。
ゲル化膜は、エマルジョン塗料をカプセル化するものであり、エマルジョン塗料を閉じ込めるものである。ゲル化膜は、親水性コロイド形成物質を含むエマルジョン塗料と、ゲル化剤を含む分散媒とを混合し、ディソルバなどの分散機で撹拌しながらエマルジョン塗料を分散させて、分散媒中のゲル化剤と親水性コロイド形成物質とを反応させることにより得られる。
分散媒としては、ゲル化剤を含む水性の分散媒が用いられる。ゲル化剤としては、例えば、マグネシウムモンモリロナイト粘土、ナトリウムペンタクロロフェノール、重ホウ酸アンモニウムなどのホウ酸塩、タンニン酸、乳酸チタン、塩化カルシウムなどを含有する水溶液が挙げられる。
バインダー樹脂としては、ガラス転移温度Tgが樹脂エマルジョンと異なる樹脂を用いる。例えば、バインダー樹脂のガラス転移温度TgBが、樹脂エマルジョンのガラス転移温度TgAよりも高いものを用いる。より具体的には、バインダー樹脂として、ガラス転移温度TgBが10℃以上、50℃以下の範囲の樹脂を用いる。
上述したような多彩塗料組成物を製造する際には、エマルジョン塗料をカプセル化させた着色ゲル状粒子と、バインダー樹脂とをディソルバなどの分散機で撹拌することにより得られる。この時の多彩塗料組成物を構成する着色ゲル状粒子に含まれるエマルジョン塗料の固形分と、バインダー樹脂の固形分との含有比率は、0.5以上、5.0以下であることが好ましい。
本発明の多彩塗料組成物から形成された模様塗膜(塗膜)は、着色ゲル状粒子に含まれる樹脂エマルジョンおよびバインダー樹脂として、互いにガラス転移温度Tgが異なる樹脂材料、例えば、樹脂エマルジョンのガラス転移温度TgAが、バインダー樹脂のガラス転移温度TgBよりも低いものを用いることにより、汚れを塗膜に付着させない、あるいは、付着した汚れを容易に落とすことができる耐汚染性の向上と、多彩塗料組成物を用いた塗膜を壁面に形成した後、外気温の変動等によって壁面が大きく伸縮しても、形成した塗膜のひび割れや剥離を防止できる下地追従性の向上とを、両立させることが可能になる。
下記に示す樹脂エマルジョン(A−1〜A−6)、及び、下記に示す親水性コロイド形成物質を表1に示す配合割合で配合し、撹拌混合することによりエマルジョン塗料(B−1〜B−6)を得た。表1において、各成分の配合割合の単位は質量部である。
樹脂エマルジョン:アニオン性高分子アクリル系樹脂エマルジョン
樹脂エマルジョンA−1 プライマルJP−130S(Tg:25℃)ダウコーティングマテリアルズ社製
樹脂エマルジョンA−2 プライマルAC2235(Tg:18℃)ダウコーティングマテリアルズ社製
樹脂エマルジョンA−3 プライマルB−15B(Tg:−2℃)ダウコーティングマテリアルズ社製
樹脂エマルジョンA−4 プライマルAC339(Tg:32℃)ダウコーティングマテリアルズ社製
樹脂エマルジョンA−5 エラステン2471(Tg:−23℃)ダウコーティングマテリアルズ社製
樹脂エマルジョンA−6 プライマルE−357(Tg:45℃)ダウコーティングマテリアルズ社製
親水性コロイド形成物質:非イオン性グアルゴム誘導体の1.5%水溶液
分散剤:アニオン性高分子分散液 オロタン731ダウコーティングマテリアルズ社製
一方、表4に示す結果によれば、比較例1〜6の塗膜は、樹脂エマルジョンのTgAとバインダー樹脂のTgBが同じため、耐汚染性または下地追従性の何れか一方が不合格となり、耐汚染性と下地追従性のいずれか一方しか充足できないという結果に留まった。
Claims (2)
- エマルジョン塗料がゲル化膜でカプセル化された少なくとも1色以上の着色ゲル状粒子と、バインダー樹脂と、を含む多彩塗料組成物であって、
前記エマルジョン塗料は、顔料と、樹脂エマルジョンと、親水性コロイド形成物質と、を含み、前記樹脂エマルジョンのガラス転移温度TgAが前記バインダー樹脂のガラス転移温度TgBよりも小さいことを特徴とする多彩塗料組成物。 - 前記樹脂エマルジョンのガラス転移温度TgAが、−25℃以上、0℃以下の範囲であり、かつ、前記バインダー樹脂のガラス転移温度TgBが、10℃以上、50℃以下の範囲であることを特徴とする請求項1に記載の多彩塗料組成物。