JP2019519666A - 高力黄銅合金及び高力黄銅合金製品 - Google Patents
高力黄銅合金及び高力黄銅合金製品 Download PDFInfo
- Publication number
- JP2019519666A JP2019519666A JP2018535375A JP2018535375A JP2019519666A JP 2019519666 A JP2019519666 A JP 2019519666A JP 2018535375 A JP2018535375 A JP 2018535375A JP 2018535375 A JP2018535375 A JP 2018535375A JP 2019519666 A JP2019519666 A JP 2019519666A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- alloy
- brass alloy
- strength brass
- high strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【選択図】図9
Description
55〜65重量%のCuと、
1〜2.5重量%のMnと、
0.7〜2重量%のSnと、
0.2〜1.5重量%のFeと、
2〜4重量%のNiと、
2〜5重量%のAlと、
0.2〜2重量%のSiと、
最大2.0重量%のCoと、
不可避的不純物とともにある残余量のZnと、を有する高力黄銅合金によって達成される。
59〜65重量%のCu、特に59.5〜65重量%のCuと、
1.3〜2.3重量%のMn、特に1.4〜2.3重量%のMnと、
1.3〜1.65重量%のSn、特に1.4〜1.65重量%のSnと、
0.5〜1.5重量%のFe、特に0.5〜1.5重量%のFeと、
2.4〜3.4重量%のNi、特に2.55〜3.4重量%のNiと、
3.1〜4.1重量%のAl、特に3.4〜4.1重量%のAlと、
1.0〜2重量%のSi、特に1.05〜2重量%のSiと、
最大2.0重量%のCoと、
不可避的不純物とともにある残余量のZnと、を有する場合、さらにより改善され得る。
59〜62重量%のCu、特に59.5〜62重量%のCuと、
1.3〜1.65重量%のMn、特に1.4〜1.65重量%のMnと、
1.3〜1.65重量%のSn、特に1.4〜1.65重量%のSnと、
0.5〜1.0重量%のFe、特に0.6〜1.0重量%のFeと、
2.4〜3.4重量%のNi、特に2.55〜3.4重量%のNiと、
3.1〜4.1重量%のAl、特に3.4〜4.1重量%のAlと、
1.0〜1.7重量%のSi、特に1.05〜1.7重量%のSiと、
不可避的不純物とともにある残余量のZnと、を有する。
第1の検査シリーズにおいて、次の組成を有する合金の検査標品を注入し、押出成形した。
第2の検査シリーズにおいて、次の組成を有する合金の検査標品を注入及び押出成形した。
Claims (15)
- 55〜65重量%のCuと、
1〜2.5重量%のMnと、
0.7〜2重量%のSnと、
0.2〜1.5重量%のFeと、
2〜4重量%のNiと、
2〜5重量%のAlと、;
0.2〜2重量%のSiと、
2.0重量%のCo最大量と、
不可避的不純物とともにある残余量のZnと、を含む、高力黄銅合金であって、
前記Mn元素及びSn元素の合計が少なくとも1.7重量%であり、かつ最大で4.5重量%である、高力黄銅合金。 - 前記Mn元素及びSn元素が、1.25〜0.85のMn:Sn比で前記合金中に存在することを特徴とする、請求項1に記載の高力黄銅合金。
- 前記Mn元素:Sn元素の前記比が1.1〜0.92であることを特徴とする、請求項2に記載の高力黄銅合金。
- 59〜65重量%のCuと、
1.3〜1.65重量%のMnと、
1.3〜1.65重量%のSnと、
0.5〜1.0重量%のFeと、
2.4〜3.4重量%のNiと、
3.1〜4.1重量%のAlと、
1.0〜1.7重量%のSiと、
2.0重量%のCo最大量と、
不可避的不純物とともにある残余量のZnと、を含む、請求項1〜3のいずれか1項に記載の高力黄銅合金。 - 59〜62重量%のCuと、
1.3〜1.65重量%のMnと、
1.3〜1.65重量%のSnと、
0.5〜1.0重量%のFeと、
2.4〜3.4重量%のNiと、
3.1〜4.1重量%のAlと、
1.0〜1.7重量%のSiと、
不可避的不純物とともにある残余量のZnと、を含む、請求項3に記載の高力黄銅合金。 - 前記Co含有量が、0.9〜1.6重量%、特に0.9〜1.5重量%、特に好ましくは0.9〜1.1重量%であることを特徴とする、請求項4に記載の高力黄銅合金。
- 請求項1〜6のいずれか1項に記載の高力黄銅合金から製造された高力黄銅合金製品であって、主としてβ相でできていることを特徴とする、高力黄銅合金製品。
- α相の比率が10%未満であることを特徴とする、請求項5の前方参照における請求項7に記載の高力黄銅合金製品。
- α相の比率が35%未満であることを特徴とする、請求項4または6の前方参照における請求項7に記載の高力黄銅合金製品。
- Coが混合ケイ化物の形成に関与し、それゆえ、より高い比率のMnがマトリックス中に溶解したままである、請求項9に記載の高力黄銅合金製品。
- 金属間相の比率が5〜9%であることを特徴とする、請求項7〜10のいずれか1項に記載の高力黄銅合金製品。
- 導電率が10MS/m未満であることを特徴とする、請求項7〜11のいずれか1項に記載の高力黄銅合金製品。
- 前記高力黄銅合金製品の前記導電率が、8.2MS/m未満であることを特徴とする、請求項12に記載の高力黄銅合金製品。
- 前記合金製品が、好ましくは、酸性条件をほぼ確実に有する油環境での軸受における使用のための軸受部品であることを特徴とする、請求項7〜13のいずれか1項に記載の高力黄銅合金製品。
- 前記軸受部品が、ターボチャージャー軸受のための部品であることを特徴とする、請求項14に記載の高力黄銅合金製品。