JP2019219659A - 光学用粘着シート - Google Patents
光学用粘着シート Download PDFInfo
- Publication number
- JP2019219659A JP2019219659A JP2019111384A JP2019111384A JP2019219659A JP 2019219659 A JP2019219659 A JP 2019219659A JP 2019111384 A JP2019111384 A JP 2019111384A JP 2019111384 A JP2019111384 A JP 2019111384A JP 2019219659 A JP2019219659 A JP 2019219659A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- adhesive sheet
- adhesive layer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記粘着層(A)の65℃90%RHで3日間静置後の含水率が0.10〜0.25質量%であり、且つ
前記粘着層(A)の65℃90%RHにおける透湿度が350〜1000g/m2・dayである、
光学用粘着シート。
本発明は、その一態様として、スチレン系ブロック共重合体を含有する粘着層(A)を含み、前記粘着層(A)の65℃90%RHで3日間静置後の含水率が0.10〜0.25質量%であり、且つ前記粘着層(A)の65℃90%RHにおける透湿度が350〜1000g/m2・dayである、光学用粘着シート(本明細書において、「本発明の光学用粘着シート」と示すこともある。)に関する。以下に、これについて説明する。
粘着層(A)を含む本発明の光学用粘着シートは、光学的に透明な部材を備えた電気製品、電子製品、若しくは光学機器、例えば携帯電話、スマートフォン、パソコン、電子ペーパー、タブレット型パーソナルコンピューターおよびゲーム機などの画像表示装置(例えば液晶ディスプレイ、OLEDディスプレイ、エレクトロウェッティング方式ディスプレイ)を製造する際に、表面を保護するためのカバーパネルとタッチパネルモジュールとを接着したり、カバーパネルとディスプレイパネルモジュールとを接着したり、タッチパネルモジュールとディスプレイパネルモジュールとを接着したりするのに好適に用いることができる。本発明の光学用粘着シートはこれら以外の光学フィルムなどの光学用途にも適用可能である。
(1−1)実施例1
スチレン系ブロック共重合体としてスチレン−(エチレン−プロピレン)−スチレン型ブロック共重合体(SEPS、商品名:セプトン2063、スチレン含有量:13質量%(St13%)、クラレ社製)60質量部、軟化剤としてポリイソブチレン(商品名:日石ポリブテンHV−300、数平均分子量:1400、JXTGエネルギー社製)13質量部、及び粘着付与剤としてスチレン−芳香族炭化水素系共重合体(商品名:FMR0150、軟化点:145℃、三井化学社製)27質量部を、トルエン中で撹拌して均一に溶解させて、粘着剤組成物(固形分濃度:35質量%)を得た。
表1及び表2に示す配合組成(組成の単位は質量%である)に従って、実施例1と同様にして光学用粘着シートを得た。実施例1で使用した成分以外の成分は以下のとおりである。
(a1)スチレン−(エチレン−プロピレン)−スチレン型ブロック共重合体(SEPS、商品名:セプトン2002、スチレン含有量:30質量%(St30%)、クラレ社製)
(a2)スチレン−(エチレン−ブチレン)−スチレン型ブロック共重合体(SEBS、商品名:タフテックH1062、スチレン含有量:18質量%(St18%)、旭化成社製)
(a3)スチレン−(エチレン−ブチレン)−スチレン型ブロック共重合体(SEBS、商品名:タフテックH1041、スチレン含有量:30質量%(St30%)、旭化成社製)
(a4)酸変性スチレン−(エチレン−ブチレン)−スチレン型ブロック共重合体(SEBS(酸変性)、商品名:タフテックC5025、酸価:4mgCH3ONa/g、スチレン含有量:12質量%(St1%)、旭化成社製)。
(b1)3−グリシドキシプロピルトリメトキシシラン(商品名:KBM403、信越シリコーン社製)。
表2に示す配合組成(組成の単位は質量%である)に従って、実施例1と同様にして光学用粘着シートを得た。実施例1〜14で使用した成分以外の成分は以下のとおり作製した。
(2−1)含水率
光学用粘着シート(実施例1〜17及び比較例1〜3)を23℃50%RHで3日以上静置した後、1.3cm×4cmに裁断し、セパレータ2を剥離してその質量(α(単位:g))を測定した。セパレータ2を剥離した塗膜の面に、厚さ25μmのアルミニウム箔を貼り合せ、65℃90%RHで3日静置した。セパレータ1を剥離し、カールフィッシャー法による水分測定装置(平沼微量水分測定装置、AQ−2000)と水分気化装置(平沼水分気化装置、EV−2000)を用いて、120℃10分間加熱した際に発生した水分量(γ(単位:g))を測定した。また、剥離したセパレータ1を再度23℃50%RHで3日以上静置して質量(β(単位:g))を測定した。
JIS Z 0208(防湿包装材料の透湿度試験方法(カップ法))に準じて、温度65℃、湿度90%RHの条件で測定した。より具体的には、光学用粘着シート(実施例1〜17及び比較例1〜3)のセパレータ1及び2を剥離し、金属網に貼り合せた。塩化カルシウム約10gを入れた透湿カップ(内径60mm)の上に、金属網に貼り合わせた評価用単層シートを被せて周囲を封止した。その後、60℃90%RHに静置して評価を行った。結果を表1及び表2に示す。
光学用粘着シート(実施例1〜17及び比較例1〜3)をガラスとポリエチレンテレフタレートフィルムの間に積層したものを試験片とし、65℃環境下で水に浸水させ、240時間後の濁度を三波長蛍光灯下で観察した。試験片の端部と中央部とで濁度の差異が見られなかった場合を「○」、試験片の端部が薄く濁って見えた場合を「△」、試験片の端部が完全に白濁し、試験片越しに対象物を視認できなかった場合を「×」と評価した。結果を表1及び表2に示す。
光学用粘着シート(実施例1〜17及び比較例1〜3)をガラスとポリエチレンテレフタレートフィルムの間に積層したものを試験片とし、65℃環境下で水に浸水させ、240時間後のHazeを測定した。具体的には、光学用粘着シートをソーダガラス(0.7×56×86.6mm)上に貼り合せ、常温(23℃)にて分光色測計(コニカミノルタ製、CM−3700d)を用いて単層シート面からソーダガラス面へ透過させた光をSCI方式にて評価した際の、Hazeを測定した。試験片の端部と中央部のHazeの差異が0.5未満の場合を「◎」、試験片の端部と中央部のHazeの差異が0.5以上1未満の場合を「○」、試験片の端部と中央部のHazeの差異が1以上5未満の場合を「△」、試験片の端部と中央部のHazeの差異が5以上の場合を「×」と評価した。結果を表1及び表2に示す。
上記「(2−3)白化」の評価が「△」又は「×」の場合(白化が生じた場合)について、23℃50%RHで24時間静置した後、白化の有無を観察した。静置後に白化が消失していた場合を「○」、静置後も白化がみられた場合を「×」と評価した。結果を表1及び表2に示す。
2 透明導電性フィルム
3 透明導電性薄膜
4 透明プラスチックフィルム基材
5 機能層
6 静電容量方式タッチパネル
7 装飾パネル
8 光学用粘着シート
9 透明導電性フィルム
10 ハードコートフィルム
11 ITO層
12 PET基材層
13 HC層
14 ガラス
Claims (13)
- スチレン系ブロック共重合体を含有する粘着層(A)を含み、
前記粘着層(A)の65℃90%RHで3日間静置後の含水率が0.10〜0.25質量%であり、且つ
前記粘着層(A)の65℃90%RHにおける透湿度が350〜1000g/m2・dayである、
光学用粘着シート。 - 前記粘着層(A)における軟化剤の含有量が、前記粘着層(A)100質量%に対して0〜15質量%である、請求項1に記載の光学用粘着シート。
- 前記粘着層(A)が粘着付与剤を含有する、請求項1又は2に記載の光学用粘着シート。
- 前記粘着付与剤が、軟化点85℃以上であり且つ芳香族環を有する粘着付与剤であり、且つ前記粘着層(A)における前記粘着付与剤の含有量が、前記粘着層(A)100質量%に対して40質量%以下である、請求項3に記載の光学用粘着シート。
- 前記粘着層(A)におけるスチレン系ブロック共重合体の含有量が、前記粘着層(A)100質量%に対して45〜85質量%である、請求項1〜4のいずれかに記載の光学用粘着シート。
- 前記スチレン系ブロック共重合体中のスチレン含有量が10〜50質量%である、請求項1〜5のいずれかに記載の光学用粘着シート。
- 請求項1〜6のいずれかに記載の光学用粘着シート、及び前記光学用粘着シート上に配置されている被着体を含む、積層体。
- 請求項1〜6のいずれかに記載の光学用粘着シートと、前記光学用粘着シートの第1の表面に積層された第1の被着体と、前記光学用粘着シートの前記第1の表面とは反対の第2の表面に積層された第2の被着体とを含む、請求項7に記載の積層体。
- 前記第1の被着体が、反射防止フィルム、飛散防止フィルム、カバーパネル、金属若しくは金属酸化物薄膜付フィルム、金属又は金属酸化物薄膜付ガラス、超複屈折フィルム、又はタッチパネルモジュールであり、前記第2の被着体が、カバーパネル、金属又は金属酸化物薄膜付フィルム、金属若しくは金属酸化物薄膜付ガラス、超複屈折フィルム、タッチパネルモジュール、偏光板、又はディスプレイパネルモジュールである、請求項8に記載の積層体。
- 透明プラスチックフィルム基材の一方の面に、金属酸化物により形成された透明導電性薄膜を有し、他方の面に機能層を有する透明導電性フィルムの一方の面に、請求項1〜6のいずれかに記載の光学用粘着シートを有することを特徴とする粘着剤層付き透明導電性フィルム。
- 前記透明導電性フィルムの透明導電性薄膜上に、前記光学用粘着シートを有することを特徴とする請求項10に記載の粘着剤層付き透明導電性フィルム。
- 前記透明導電性フィルムの機能層上に、前記光学用粘着シートを有することを特徴とする請求項11に記載の粘着剤層付き透明導電性フィルム。
- 請求項10〜12のいずれか1項に記載の粘着剤層付き透明導電性フィルムを少なくとも1つ有することを特徴とするタッチパネル。