JP2019196485A - アクリル系樹脂粒子、塗料組成物及び光学材料 - Google Patents
アクリル系樹脂粒子、塗料組成物及び光学材料 Download PDFInfo
- Publication number
- JP2019196485A JP2019196485A JP2019104363A JP2019104363A JP2019196485A JP 2019196485 A JP2019196485 A JP 2019196485A JP 2019104363 A JP2019104363 A JP 2019104363A JP 2019104363 A JP2019104363 A JP 2019104363A JP 2019196485 A JP2019196485 A JP 2019196485A
- Authority
- JP
- Japan
- Prior art keywords
- volume
- particle diameter
- cumulative
- particle
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
α>γ>η ・・・式1
30%≦体積基準の粒子径のCV値≦40% ・・・式2
A≦0.75 ・・・式3
1.1≦B≦1.6 ・・・式4
α=体積基準の累積10%粒子径/個数基準の累積10%粒子径
γ=体積基準の累積50%粒子径/個数基準の累積50%粒子径
η=体積基準の累積90%粒子径/個数基準の累積90%粒子径
A=体積基準の累積10%粒子径/体積基準の累積50%粒子径
B=体積基準の累積90%粒子径/体積基準の累積50%粒子径
α>β>γ>δ>η ・・・式5
β=体積基準の累積25%粒子径/個数基準の累積25%粒子径
δ=体積基準の累積75%粒子径/個数基準の累積75%粒子径
C≦0.85 ・・・式6
1.1≦D≦1.4 ・・・式7
C=体積基準の累積25%粒子径/体積基準の累積50%粒子径
D=体積基準の累積75%粒子径/体積基準の累積50%粒子径
体積基準の平均粒子径は、10万個のアクリル系樹脂粒子の体積基準の累積50%粒子径である。
アクリル系樹脂粒子の粒子径のCV値(変動係数)を、下記式に基づいて算出する。
アクリル系樹脂粒子の体積基準のCV値(%)
=100×(アクリル系樹脂粒子の体積基準の粒度分布の標準偏差)
/アクリル系樹脂粒子の体積基準の平均粒子径)
メチルメタクリレート95重量部、エチレングリコールジメタクリレート5重量部及び過酸化ベンゾイル0.4重量部を含む単量体組成物、脱イオン水200重量部、酸可溶性の難水溶性無機化合物からなる分散安定剤としてのトリリン酸カルシウム6重量部、並びに、ラウリル硫酸ナトリウム0.1重量部を混合機(特殊機化工業株式会社製 商品名「TKホモミキサー」)に供給して4500rpmで10分間に亘って混合して、単量体組成物が脱イオン水中に均一に分散した分散液を得た。
混合機の回転数を7000rpmとしたこと以外は実施例1と同様の要領で分級前の架橋ポリメチルメタクリレート粒子を得た。
メチルメタクリレート及びエチレングリコールジメタクリレートの代わりに、ブチルメタクリレート35重量部、ブチルアクリレート35重量部及びエチレングリコールジメタクリレート30重量部を用いたこと、混合機の回転数を6500rpmとしたこと以外は実施例1と同様の要領で分級前の架橋アクリル系樹脂粒子を得た。
実施例1で製造された分級前の架橋ポリメチルメタクリレート粒子を用いた。
実施例2で製造された分級前の架橋ポリメチルメタクリレート粒子を用いた。
実施例3で製造された分級前の架橋アクリル系樹脂粒子を用いた。
実施例1で得られた分級後の架橋ポリメチルメタクリレート粒子をターボクラシファイヤー(日清エンジニアリング社製 商品名「型式TC−15」)に投入して、粒子径が12μmを超える架橋ポリメチルメタクリレート粒子を除去した。
光拡散シートを目視観察し、樹脂粒子が集中している部分と樹脂粒子の少ない部分の存在、所謂、塗工ムラの存在を確認した。塗工ムラの観察できなかった場合を「良」、塗工ムラが観察された場合を「不良」とした。
染色物摩擦堅牢度試験機(大栄科学精器製作所社製)を用いた。光拡散シートから縦12cm×横5cmの平面長方形状の試験片を2枚切り出した。染色物摩擦堅牢度試験機の試料台上に、試験片をその光拡散層が上となるように載置、固定した。染色物摩擦堅牢度試験機の摩擦子に光拡散層を上向きにして別の試験片を固定し、更に、その上に500gの分銅(試験片への接触面積は4cm2)を乗せて30往復/分の速さで試験片の長辺方向と平行に10cmの距離を20回往復させて擦過し、光拡散層の傷つき性を評価した。光拡散層の傷が肉眼で確認できなかった場合を「良」、傷が確認できた場合を「不良」とした。
Claims (15)
- 体積基準の累積10%粒子径を個数基準の累積10%粒子径で除した値α、体積基準の累積50%粒子径を個数基準の累積50%粒子径で除した値γ、及び、体積基準の累積90%粒子径を個数基準の累積90%粒子径で除した値ηが下記式1を満し且つ体積基準の粒子径のCV値が式2を満たすと共に、体積基準の累積10%粒子径を体積基準の累積50%粒子径で除した値Aが式3を満たし且つ体積基準の累積90%粒子径を体積基準の累積50%粒子径で除した値Bが式4を満たしており、更に、体積基準の累積25%粒子径を個数基準の累積25%粒子径で除した値β及び体積基準の累積75%粒子径を個数基準の累積75%粒子径で除した値δが下記式5を満たしていることを特徴とするアクリル系樹脂粒子。
α>γ>η ・・・式1
30%≦体積基準の粒子径のCV値≦40% ・・・式2
A≦0.75 ・・・式3
1.1≦B≦1.6 ・・・式4
α>β>γ>δ>η ・・・式5 - 体積基準の累積10%粒子径を個数基準の累積10%粒子径で除した値α、体積基準の累積50%粒子径を個数基準の累積50%粒子径で除した値γ、及び、体積基準の累積90%粒子径を個数基準の累積90%粒子径で除した値ηが下記式1を満し且つ体積基準の粒子径のCV値が式2を満たすと共に、体積基準の累積10%粒子径を体積基準の累積50%粒子径で除した値Aが式3を満たし且つ体積基準の累積90%粒子径を体積基準の累積50%粒子径で除した値Bが式4を満たしており、更に、体積基準の累積25%粒子径を体積基準の累積50%粒子径で除した値Cが式6を満たしていることを特徴とするアクリル系樹脂粒子。
α>γ>η ・・・式1
30%≦体積基準の粒子径のCV値≦40% ・・・式2
A≦0.75 ・・・式3
1.1≦B≦1.6 ・・・式4
C≦0.85 ・・・式6 - 体積基準の累積10%粒子径を個数基準の累積10%粒子径で除した値α、体積基準の累積50%粒子径を個数基準の累積50%粒子径で除した値γ、及び、体積基準の累積90%粒子径を個数基準の累積90%粒子径で除した値ηが下記式1を満し且つ体積基準の粒子径のCV値が式2を満たすと共に、体積基準の累積10%粒子径を体積基準の累積50%粒子径で除した値Aが式3を満たし且つ体積基準の累積90%粒子径を体積基準の累積50%粒子径で除した値Bが式4を満たしており、更に、体積基準の累積75%粒子径を体積基準の累積50%粒子径で除した値Dが式7を満たしていることを特徴とするアクリル系樹脂粒子。
α>γ>η ・・・式1
30%≦体積基準の粒子径のCV値≦40% ・・・式2
A≦0.75 ・・・式3
1.1≦B≦1.6 ・・・式4
1.1≦D≦1.4 ・・・式7 - 前記αが1.8〜3.2であることを特徴とする請求項1〜3の何れか1項に記載のアクリル系樹脂粒子。
- 前記γが1.4〜2.8であることを特徴とする請求項1〜4の何れか1項に記載のアクリル系樹脂粒子。
- 前記ηが1.4〜2.8であることを特徴とする請求項1〜5の何れか1項に記載のアクリル系樹脂粒子。
- 体積基準の累積50%粒子径が1〜50μmであることを特徴とする請求項1〜6の何れか1項に記載のアクリル系樹脂粒子。
- メチルアクリレート、エチルアクリレート、プロピルアクリレート、n−ブチルアクリレート、イソブチルアクリレート、メチルメタクリレート、エチルメタクリレート、プロピルメタクリレート、n−ブチルメタクリレート及びイソブチルメタクリレートから選ばれた少なくとも一つのモノマーを含むアクリル系モノマーの重合体であることを特徴とする請求項1〜7の何れか1項に記載のアクリル系樹脂粒子。
- 前記アクリル系モノマーは、ビニル基を複数個有する多官能モノマーを更に含むことを特徴とする請求項8に記載のアクリル系樹脂粒子。
- 艶消し塗料用の粒子であることを特徴とする請求項1〜9の何れか1項に記載のアクリル系樹脂粒子。
- 建築物の外装塗料用の粒子であることを特徴とする請求項1〜9の何れか1項に記載のアクリル系樹脂粒子。
- 光学材料用の粒子であることを特徴とする請求項1〜9の何れか1項に記載のアクリル系樹脂粒子。
- 請求項1〜9の何れか1項に記載のアクリル系樹脂粒子とバインダー樹脂とを含むことを特徴とする塗料組成物。
- 基材上に光拡散層が積層一体化されてなる光学材料であって、上記光拡散層は、請求項1〜9の何れか1項に記載のアクリル系樹脂粒子とバインダー樹脂とを含むことを特徴とする光学材料。
- 光学材料が光拡散シートであることを特徴とする請求項14に記載の光学材料。