JP2019094243A - マグネシアセメント組成物およびその用途 - Google Patents
マグネシアセメント組成物およびその用途 Download PDFInfo
- Publication number
- JP2019094243A JP2019094243A JP2017227005A JP2017227005A JP2019094243A JP 2019094243 A JP2019094243 A JP 2019094243A JP 2017227005 A JP2017227005 A JP 2017227005A JP 2017227005 A JP2017227005 A JP 2017227005A JP 2019094243 A JP2019094243 A JP 2019094243A
- Authority
- JP
- Japan
- Prior art keywords
- magnesia cement
- magnesium oxide
- cement composition
- bet specific
- specific surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
酸化マグネシウムとして、BET比表面積の異なる酸化マグネシウムを2種以上用い、
リン酸カルシウムとして、第二リン酸カルシウムを用いる、
ことを特徴とするマグネシアセメント組成物である。
(a1)BET比表面積の異なる酸化マグネシウムを2種以上
(a2)第二リン酸カルシウム
を含有するA剤と、
次の成分
(b1)塩化マグネシウム
(b2)水
を含有するB剤とを、
含有することを特徴とするマグネシアセメントキットである。
酸化マグネシウム(BET比表面積の異なる酸化マグネシウムの総量)18〜35質量部
第二リン酸カルシウム 2〜8質量部
塩化マグネシウム6水和物 13〜30質量部
A剤:
(a1)BET比表面積の異なる酸化マグネシウムを2種以上
(a2)第二リン酸カルシウム
B剤:
(b1)塩化マグネシウム
(b2)水
マグネシアセメント水性混練物の物性:
以下の表1に記載の組成のA剤とB剤を調製した。これらA剤およびB剤を混合してマグネシアセメント組成物を含有する水性混練物を調製した。これら水性混練物の可使時間と硬化時間を以下の方法で測定した。また、酸化マグネシウムの平均BET比表面積を以下のようにして測定した。それらの結果を表1に示した。
温度が15℃の室内で、A剤とB剤を混合した直後を起点として、粘度が20,000mPa・sを超えるまでの時間を、次の判定基準に当てはめて可使時間の判定を行った。粘度の測定は、JIS Z 8803(液体の粘度測定方法)に準じ、BII形粘度計 モデルBHII(東機産業(株)製)を使用して、回転数20rpmで行った。
(評価) (内容)
○ : 20分以上
△ : 10分以上〜20分未満
× : 10分未満
温度が20℃の室内で、試料の水性混合物を直径100mmの円形の塩化ビニル製型枠に厚み5mmになるように流し込み、水平になるように静置する。24時間経過後にデュロメータータイプD硬度計を使用して、試験体の表面の硬度を測定し、次の判定基準に当てはめて硬化性の判定を行った。
(評価) (内容)
○ : 60以上
△ : 40以上〜60未満
× : 40未満
まず、各酸化マグネシウムのBET比表面積は、JIS R 1626(ファインセラミックス粉体の気体吸着BET法による比表面積の測定方法)に準じ、流動式比表面積自動測定装置(フローソーブ2300型:(株)島津製作所製)を用いて測定した。その後、各組成で使用する酸化マグネシウムのみを混合した後の混合物について、上記測定法でBET比表面積を測定したものを平均BET比表面積とした。
マグネシアセメント硬化物の物性:
以下の表2に記載の組成のA剤とB剤を調製した。これらA剤およびB剤を混合してマグネシアセメント組成物を含有する水性混練物を調製した。これらを温度が20℃の室内で、以下に示すデュロメーター硬度測定方法および曲げ強さ測定方法の各試験体の形状に注型した硬化体を用いて、このマグネシアセメント硬化物のデュロメーター硬度と、曲げ強さを測定した。また、マグネシアセメント組成物に含有される酸化マグネシウムの平均BET比表面積を実施例1と同様にして測定した。それらの結果を表2に示した。
デュロメーター硬度は、JIS K 7215(プラスチックのデュロメーター硬さ試験方法)に準じ、デュロメーター タイプD硬度計((株)上島製作所製)を用い、気乾35日のデュロメーター硬度と、気乾7日の後、水中浸漬28日のデュロメーター硬度を測定した。なお、保持率(%)は、以下の計算式により算出した。
試験体:直径100mm、厚さ5mmの円形状
保持率(%)=(気乾7日の後、水中浸漬28日の硬度/気乾35日の硬度)×100
曲げ強さは、JIS K 7171(プラスチック曲げ特性の求め方)に準じ、以下の注型して作製した試験体とオートグラフAG−50kN Xplus((株)島津製作所製)を用い、以下の条件で曲げ強さを測定した。
試験体:幅15mm×厚み8mm×長さ160mm
支点間距離:128mm
試験速度:1.0mm/min
マグネシアセメントキット:
以下の組成のA剤(20kg)とB剤(10kg)からなるマグネシアセメントキットを調製した。なお、酸化マグネシウムの平均BET比表面積は、36.7m2/gであった。
BET比表面積が6.4m2/gの酸化マグネシウム※1 15.0%
BET比表面積が20.0m2/gの酸化マグネシウム※3 10.0%
BET比表面積が98.9m2/gの酸化マグネシウム※2 10.0%
第二リン酸カルシウム 6.0%
充填剤※4 58.0%
減水剤※5 0.5%
消泡剤※6 0.5%
(合計) 100.0%
<B剤>
塩化マグネシウム6水和物 49.7%
水 43.0%
水性樹脂※8 7.0%
消泡剤※7 0.3%
(合計) 100.0%
※1〜7は実施例1と同じ
※8:アクリルエマルション、サイビノール(登録商標)UC−203、サイデン化学(株)製
マグネシアセメントキット:
以下の組成のA剤(20kg)、B剤(10kg)、C剤(0.3kg)からなるマグネシアセメントキットを調製した。なお、酸化マグネシウムの平均BET比表面積は、38.6m2/gであった。
BET比表面積が6.4m2/gの酸化マグネシウム※1 23.0%
BET比表面積が98.9m2/gの酸化マグネシウム※2 12.0%
第二リン酸カルシウム 6.0%
充填剤※4 58.0%
減水剤※5 0.5%
消泡剤※6 0.5%
(合計) 100.0%
<B剤>
塩化マグネシウム6水和物 49.7%
水 43.0%
水性樹脂※9 7.0%
消泡剤※7 0.3%
(合計) 100.0%
<C剤>
顔料 25.0%
水 74.4%
湿潤分散剤※10 0.6%
(合計) 100.0%
※1〜7は実施例1と同じ
※9:アクリルエマルション、リポテックス(登録商標)MI−500、ライオン(株)製
※10:アクリル系共重合物、DISPERBYK−2010、ビックケミー・ジャパン(株)製
床への塗工:
実施例1の組成4と同様のマグネシアセメントを含有する水性混練物を調製し、これを縦300mm×横300mm×厚み50mmのコンクリート板に3mmの厚さになるように塗布し、水平になるように静置してマグネシアセメント硬化物の試験体を得た。これを20℃、28日間養生した。この試験体について表3に記載の試験を行った。その結果もあわせて表3に記載した。
アンモニア吸収試験:
実施例1の組成4と同様のマグネシアセメントを含有する水性混練物を調製し、これを100mm×100mmの型枠に3mmの厚さになるように流し込み、水平になるように静置してマグネシアセメント硬化物を得た。このマグネシアセメント硬化物を3Lテドラーバックに挿入して密封処理をした。その中に濃度を40〜50ppmに調整したアンモニアガスを2L封入した。所定時間経過後に、北川式ガス検知管を用いてアンモニアガス濃度を測定した。その結果を表4に示した。
成型タイルの作製:
実施例1の組成4と同様のマグネシアセメントを含有する水性混練物を調製し、これをタイルの型枠に入れ、硬化させて成型タイルを得た。
以 上
Claims (11)
- 酸化マグネシウム、リン酸カルシウムおよび塩化マグネシウムを含有するマグネシアセメント組成物であって、
酸化マグネシウムとして、BET比表面積の異なる酸化マグネシウムを2種以上用い、
リン酸カルシウムとして、第二リン酸カルシウムを用いる、
ことを特徴とするマグネシアセメント組成物。 - BET比表面積の異なる酸化マグネシウムが、BET比表面積が1m2/g以上〜15m2/g未満の酸化マグネシウム、BET比表面積が15m2/g以上〜60m2/g未満の酸化マグネシウム、BET比表面積が60m2/g以上〜120m2/gの酸化マグネシウムからなる群から選ばれる2種以上である請求項1記載のマグネシアセメント組成物。
- 酸化マグネシウムの平均BET比表面積が30〜70m2/gである請求項1または2記載のマグネシアセメント組成物。
- 酸化マグネシウムと塩化マグネシウムが、酸化マグネシウムと塩化マグネシウム6水和物の質量比として1:0.5〜1.0で含有するものである請求項1〜3の何れかに記載のマグネシアセメント組成物。
- 第二リン酸カルシウムの含有量が、酸化マグネシウムの含有量の3質量%以上である請求項1〜4の何れかに記載のマグネシアセメント組成物。
- 更に、充填材、顔料、減水剤、消泡剤、湿潤分散剤、粘性調整剤、ダレ防止剤、水性樹脂および骨材からなる群から選ばれる配合剤の1種または2種以上を含有するものである請求項1〜5の何れかに記載のマグネシアセメント組成物。
- 次の成分
(a1)BET比表面積の異なる酸化マグネシウムを2種以上
(a2)第二リン酸カルシウム
を含有するA剤と、
次の成分
(b1)塩化マグネシウム
(b2)水
を含有するB剤とを、
含有することを特徴とするマグネシアセメントキット。 - 請求項1〜6の何れかに記載のマグネシアセメント組成物を含有する水性混練物を硬化させることを特徴とするマグネシアセメントの硬化物。
- 請求項1〜6の何れかに記載のマグネシアセメント組成物を含有する水性混練物を硬化させることを特徴とするマグネシアセメントの硬化方法。
- 請求項1〜6の何れかに記載のマグネシアセメント組成物を含有する水性混練物を、床面に塗布し、硬化させることを特徴とする床面の施工方法。
- アンモニアを請求項8記載のマグネシアセメントの硬化物に吸収させることを特徴とするアンモニア吸収方法。