JP2018505291A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2018505291A5 JP2018505291A5 JP2017558619A JP2017558619A JP2018505291A5 JP 2018505291 A5 JP2018505291 A5 JP 2018505291A5 JP 2017558619 A JP2017558619 A JP 2017558619A JP 2017558619 A JP2017558619 A JP 2017558619A JP 2018505291 A5 JP2018505291 A5 JP 2018505291A5
- Authority
- JP
- Japan
- Prior art keywords
- measured
- capacitor film
- film
- astm
- polyetherimide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000003990 capacitor Substances 0.000 claims 30
- 239000004697 Polyetherimide Substances 0.000 claims 21
- 229920001601 polyetherimide Polymers 0.000 claims 21
- 150000002148 esters Chemical class 0.000 claims 15
- 229920005623 miscible polymer blend Polymers 0.000 claims 10
- 238000005227 gel permeation chromatography Methods 0.000 claims 9
- 150000003457 sulfones Chemical class 0.000 claims 7
- HEDRZPFGACZZDS-UHFFFAOYSA-N chloroform Chemical compound ClC(Cl)Cl HEDRZPFGACZZDS-UHFFFAOYSA-N 0.000 claims 6
- 230000037303 wrinkles Effects 0.000 claims 4
- IISBACLAFKSPIT-UHFFFAOYSA-N Bisphenol A Chemical compound C=1C=C(O)C=CC=1C(C)(C)C1=CC=C(O)C=C1 IISBACLAFKSPIT-UHFFFAOYSA-N 0.000 claims 3
- 210000001736 Capillaries Anatomy 0.000 claims 3
- BVKZGUZCCUSVTD-UHFFFAOYSA-L Carbonate dianion Chemical compound [O-]C([O-])=O BVKZGUZCCUSVTD-UHFFFAOYSA-L 0.000 claims 3
- 239000004793 Polystyrene Substances 0.000 claims 3
- 125000003118 aryl group Chemical group 0.000 claims 3
- 150000004985 diamines Chemical class 0.000 claims 3
- 239000011521 glass Substances 0.000 claims 3
- 238000005259 measurement Methods 0.000 claims 3
- 238000000847 optical profilometry Methods 0.000 claims 3
- 239000004417 polycarbonate Substances 0.000 claims 3
- 229920000515 polycarbonate Polymers 0.000 claims 3
- 238000006116 polymerization reaction Methods 0.000 claims 3
- 229920002223 polystyrene Polymers 0.000 claims 3
- 238000000518 rheometry Methods 0.000 claims 3
- 230000003746 surface roughness Effects 0.000 claims 3
- 229940018564 M-PHENYLENEDIAMINE Drugs 0.000 claims 2
- WZCQRUWWHSTZEM-UHFFFAOYSA-N M-Phenylenediamine Chemical compound NC1=CC=CC(N)=C1 WZCQRUWWHSTZEM-UHFFFAOYSA-N 0.000 claims 2
- CBCKQZAAMUWICA-UHFFFAOYSA-N P-Phenylenediamine Chemical compound NC1=CC=C(N)C=C1 CBCKQZAAMUWICA-UHFFFAOYSA-N 0.000 claims 2
- 210000001138 Tears Anatomy 0.000 claims 2
- 229910052782 aluminium Inorganic materials 0.000 claims 2
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminum Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 2
- 239000000203 mixture Substances 0.000 claims 2
- 239000002904 solvent Substances 0.000 claims 2
- MQJKPEGWNLWLTK-UHFFFAOYSA-N Di(p-aminophenyl)sulphone Chemical compound C1=CC(N)=CC=C1S(=O)(=O)C1=CC=C(N)C=C1 MQJKPEGWNLWLTK-UHFFFAOYSA-N 0.000 claims 1
- 229910052799 carbon Inorganic materials 0.000 claims 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 1
- 229910052739 hydrogen Inorganic materials 0.000 claims 1
- 239000001257 hydrogen Substances 0.000 claims 1
- UFHFLCQGNIYNRP-UHFFFAOYSA-N hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 claims 1
- 229910052760 oxygen Inorganic materials 0.000 claims 1
- 239000001301 oxygen Substances 0.000 claims 1
- MYMOFIZGZYHOMD-UHFFFAOYSA-N oxygen Chemical compound O=O MYMOFIZGZYHOMD-UHFFFAOYSA-N 0.000 claims 1
- 230000003068 static Effects 0.000 claims 1
Claims (9)
- ポリエーテルイミドおよびポリ(カーボネート−アリレートエステル)を含む混和性ポリマーブレンドを含む、一軸延伸高収率押出成形キャパシターフィルムであって、
前記ポリエーテルイミドは、芳香族二無水物と、m−フェニレンジアミン、p−フェニレンジアミンまたはこれらの組合せを含むジアミンとの重合から誘導される単位を含み、
前記ポリエーテルイミドは、置換または無置換芳香族一級モノアミンにより末端封鎖されており、
前記ポリ(カーボネート−アリレートエステル)は、互いに異なるビスフェノールカーボネート繰り返し単位およびアリレートエステル繰り返し単位を含み、
前記高収率押出成形キャパシターフィルムは、該キャパシターフィルムを製造するために使用される押出機に入る前の混和性ポリマーブレンドの総重量に対して、該押出機に入る該混和性ポリマーブレンドの約90重量%以上を含む、一軸延伸高収率押出成形キャパシターフィルム。 - 請求項1に記載のキャパシターフィルムであって、
前記ポリエーテルイミドが、ポリスチレン標準品を使用するゲル浸透クロマトグラフィー(GPC)によって決定すると、約20,000Da〜約400,000Daの重量平均分子量を有し、
前記ポリエーテルイミドが、340℃におけるキャピラリーレオメトリーによって測定すると、100sec −1 の粘度と5,000sec −1 の粘度との比が約11未満であり、
前記ポリエーテルイミドが、ASTM D638に準拠して決定すると、約380,000psi(2,618MPa)以上の引張弾性率を有し、
前記ポリ(カーボネート−アリレートエステル)が、ポリカーボネート標準品を使用するGPCによって測定すると、約2,000Da〜約100,000Daの重量平均分子量を有し、
前記ポリ(カーボネート−アリレートエステル)が、25℃においてクロロホルム中で測定すると、約0.3dl/g〜約1.5dl/gの固有粘度を有し、
前記キャパシターフィルムが、
約170℃を超えるガラス転移温度を有し、
3.2ミリメートル(mm)の厚さの試料において、264psi(1.8MPa)でASTM D648に準拠して測定すると、約150℃以上の熱変形温度を有し、
1kHz、23℃および50%相対湿度(RH)においてASTM D150に準拠して測定すると、約3〜約5の比誘電率を有し、
1kHz、23℃および50%RHにおいて測定すると、約0%〜約1の誘電正接を有しており、23℃において、ASTM D149に準拠して測定すると、約500V/ミクロン〜約800V/ミクロンの破壊強度を有しており、
特定の測定エリア全体にわたる前記フィルムの平均厚さに対して、フィルム厚さの約+/−10%未満のフィルム厚さのばらつきを有するしわのない領域を有し、
光学式形状測定法によって測定すると、平均フィルム厚さに対して、約+/−3%未満の平均表面粗さ(Ra)を有する、キャパシターフィルム。 - 請求項1に記載のキャパシターフィルムであって、
前記ポリエーテルイミドが、ポリスチレン標準品を使用するゲル浸透クロマトグラフィー(GPC)によって決定すると、約20,000Da〜約400,000Daの重量平均分子量を有し、
前記ポリエーテルイミドが、340℃におけるキャピラリーレオメトリーによって測定すると、100sec −1 の粘度と5,000sec −1 との粘度との比が約10未満であり、
前記ポリエーテルイミドが、ASTM D638に準拠して決定すると、約380,000psi(2,618MPa)以上の引張弾性率を有し、
前記ポリ(カーボネート−アリレートエステル)が、ポリカーボネート標準品を使用するGPCによって測定すると、約2,000Da〜約100,000Daの重量平均分子量を有し、
前記ポリ(カーボネート−アリレートエステル)は、25℃においてクロロホルム中で測定すると、約0.3dl/g〜約1.5dl/gの固有粘度を有し、
前記キャパシターフィルムが、
約190℃を超えるガラス転移温度を有し、
3.2ミリメートル(mm)の厚さの試料において、264psi(1.8MPa)でASTM D648に準拠して測定すると、約170℃以上の熱変形温度を有し、
1kHz、23℃および50%RHにおいてASTM D150に準拠して測定すると、約3〜約5の比誘電率を有し、
1kHz、23℃および50%RHにおいて測定すると、約0.1%〜約0.5%の誘電正接を有し、
23℃において、ASTM D149に準拠して測定すると、約600V/ミクロン〜約800V/ミクロンの破壊強度を有し、
特定の測定エリア全体にわたる前記フィルムの平均厚さに対して、フィルム厚さの約+/−10%未満のフィルム厚さのばらつきを有するしわのない領域を有し、
光学式形状測定法によって測定すると、平均フィルム厚さに対して、約+/−3%未満の平均表面粗さ(Ra)を有する、キャパシターフィルム。 - ASTM D1894に準拠して測定すると、金属化表面上の、アルミニウム上の、および/またはそれ自体上の動摩擦係数が約0.75未満であること、
ASTM D1894に準拠して測定すると、金属化表面上の、アルミニウム上の、および/またはそれ自体上の静摩擦係数が約0.75未満であること、
1kHzにおける前記キャパシターフィルムの比誘電率が、約0℃〜約170℃で本質的に変化しないままであり、該比誘電率は、約0℃〜約170℃の温度範囲内で、最高の比誘電率の値に対して、約20%未満変動すること、
1kHzにおける前記キャパシターフィルムの誘電正接が、約0℃〜約170℃で本質的に変化しないままであり、約0.1%〜約1%であること、
前記キャパシターフィルムの誘電正接が、23℃および50%RHにおいて、1kHz〜100kHzで測定すると、約0.1%〜約1%であること、
約0℃〜約170℃の前記キャパシターフィルムの破壊強度差が、ASTM D149に準拠して測定すると、23℃における破壊強度値の約40%未満であること、
1kHzおよび約0℃〜約170℃におけるキャパシタンス差が、23℃におけるキャパシタンス値に対して、約+/−5%未満であること、
100cm 2 のエリアにおいて、約20ミクロン超の直径を有する、2つ未満の炭化封入体を含むこと、
約10m〜約10,000mのフィルム長さおよび約300mm〜約3,000mmのフィルム幅を有する請求項1に記載のキャパシターフィルムであって、該フィルムの全表面積の少なくとも約80%にしわがないこと、
約1.25未満の炭素/(酸素+水素)(C/(O+H))比を有すること、
20ミクロンの厚さを有する試験片を使用し、ASTM D1938に準拠して測定すると、約0.5N/mm〜約3.0N/mmの縦方向のトラウザー引裂強度を有すること、
20ミクロンの厚さを有する試験片を使用し、ASTM D1938に準拠して測定すると、約0.5N/mm〜約3.0N/mmの横方向のトラウザー引裂強度を有すること、
前記キャパシターフィルムの総重量に対して、約1000ppm未満の溶媒を含むこと、
のうちの少なくとも一つを有する、請求項1に記載のキャパシターフィルム。 - 前記ポリエーテルイミドが、前記混和性ポリマーブレンド中に、約50重量%〜約99.9重量%の量で存在する、請求項1に記載のキャパシターフィルム。
- ポリエーテルイミドおよびポリ(カーボネート−アリレートエステル)を含む混和性ポリマーブレンドを含む、一軸延伸高収率押出成形キャパシターフィルムであって、
前記ポリエーテルイミドは、芳香族二無水物と、m−フェニレンジアミン、p−フェニレンジアミンまたはこれらの組合せを含むジアミンとの重合から誘導される単位を含み、
前記ポリエーテルイミドは、置換または無置換芳香族一級モノアミンにより末端封鎖されており、
前記ポリ(カーボネート−アリレートエステル)は、互いに異なるビスフェノールカーボネート繰り返し単位およびアリレートエステル繰り返し単位を含み、
前記高収率押出成形キャパシターフィルムは、溶媒不含であり、該キャパシターフィルムを製造するために使用される押出機に入る前の混和性ポリマーブレンドの総重量に対して、該押出機に入る該混和性ポリマーブレンドの約90重量%以上を含み、約0.1ミクロン〜約20ミクロンのフィルム厚さを有する、一軸延伸高収率押出成形キャパシターフィルム。 - 前記ポリエーテルイミドが、ポリエーテルイミドスルホンをさらに含む、請求項6に記載のキャパシターフィルム。
- ポリエーテルイミドスルホンおよびポリ(カーボネート−アリレートエステル)を含む混和性ポリマーブレンドを含む、一軸延伸高収率押出成形キャパシターフィルムであって、
前記ポリエーテルイミドスルホンは、芳香族二無水物と、ジアミノジフェニルスルホンを含むジアミンとの重合から誘導される単位を含み、
前記ポリエーテルイミドスルホンは、置換または無置換芳香族一級モノアミンにより末端封鎖されており、
前記ポリ(カーボネート−アリレートエステル)は、互いに異なるビスフェノールカーボネート繰り返し単位およびアリレートエステル繰り返し単位を含み、前記高収率押出成形キャパシターフィルムは、溶媒不含であり、該キャパシターフィルムを製造するために使用される押出機に入る前の混和性ポリマーブレンドの総重量に対して、該押出機に入る該混和性ポリマーブレンドの約90重量%以上を含む、一軸延伸高収率押出成形キャパシターフィルム。 - 請求項8に記載のキャパシターフィルムであって、
前記ポリエーテルイミドスルホンが、ポリスチレン標準品を使用するゲル浸透クロマトグラフィー(GPC)によって決定すると、約20,000Da〜約400,000Daの重量平均分子量を有し、
前記ポリエーテルイミドスルホンが、340℃におけるキャピラリーレオメトリーによって測定すると、100sec −1 の粘度と5,000sec −1 との粘度との比が約11未満であり、
前記ポリエーテルイミドスルホンが、ASTM D638に準拠して決定すると、約380,000psi(2,618MPa)以上の引張弾性率を有し、
前記ポリ(カーボネート−アリレートエステル)が、ポリカーボネート標準品を使用するGPCによって測定すると、約2,000Da〜約100,000Daの重量平均分子量を有し、
前記ポリ(カーボネート−アリレートエステル)が、25℃においてクロロホルム中で測定すると、約0.3dl/g〜約1.5dl/gの固有粘度を有し、
前記キャパシターフィルムが、
約170℃を超えるガラス転移温度を有し、
3.2ミリメートル(mm)の厚さの試料において、264psi(1.8MPa)でASTM D648に準拠して測定すると、約150℃以上の熱変形温度を有し、
1kHz、23℃および50%相対湿度(RH)においてASTM D150に準拠して測定すると、約3〜約5の比誘電率を有し、
1kHz、23℃および50%RHにおいて測定すると、約0%〜約1の誘電正接を有し、
23℃において、ASTM D149に準拠して測定すると、約500V/ミクロン〜約800V/ミクロンの破壊強度を有し、
特定の測定エリア全体にわたる前記フィルムの平均厚さに対して、フィルム厚さの約+/−10%未満のフィルム厚さのばらつきを有するしわのない領域を有し、
光学式形状測定法によって測定すると、平均フィルム厚さに対して、約+/−3%未満の平均表面粗さ(Ra)を有する、キャパシターフィルム。