JP2017211434A - 積層フィルム、及び画像表示装置 - Google Patents
積層フィルム、及び画像表示装置 Download PDFInfo
- Publication number
- JP2017211434A JP2017211434A JP2016102808A JP2016102808A JP2017211434A JP 2017211434 A JP2017211434 A JP 2017211434A JP 2016102808 A JP2016102808 A JP 2016102808A JP 2016102808 A JP2016102808 A JP 2016102808A JP 2017211434 A JP2017211434 A JP 2017211434A
- Authority
- JP
- Japan
- Prior art keywords
- film
- polarizer
- adhesive layer
- meth
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明は、粘着剤層、偏光フィルム、及び輝度向上フィルムをこの順に含む積層フィルムであって、前記偏光フィルムは、ポリビニルアルコール系樹脂を含有する偏光子の少なくとも片面に保護フィルムを有する偏光フィルムであり、前記偏光子の厚みが10μm以下であり、かつ、単体透過率が43.0%以上であり、前記輝度向上フィルムの偏光度が90%以上あり、前記保護フィルムの厚みが25μm以下であり、かつ、透湿度が200g/(m2・day)以下であることを特徴とする積層フィルムである。
である。
【選択図】図1
Description
前記偏光フィルムは、ポリビニルアルコール系樹脂を含有する偏光子の少なくとも片面に保護フィルムを有する偏光フィルムであり、
前記偏光子の厚みが10μm以下であり、かつ、単体透過率が43.0%以上であり、
前記輝度向上フィルムの偏光度が90%以上あり、
前記保護フィルムの厚みが25μm以下であり、かつ、透湿度が200g/(m2・day)以下であることを特徴とする積層フィルムに関する。
前記積層フィルムを、85℃で500時間放置した後の前記偏光子の吸収軸方向の加熱収縮率が、0.5%以下であることが好ましい。
前記接着剤層のバルク吸水率が10重量%以下であることが好ましい。
前記積層フィルムが、粘着剤層、保護フィルム、偏光子、及び輝度向上フィルムをこの順に含むか、又は、粘着剤層、偏光子、保護フィルム、及び輝度向上フィルムをこの順に含むことが好ましい。
本発明の積層フィルムは、粘着剤層、偏光フィルム、及び輝度向上フィルムをこの順に含み、
前記偏光フィルムは、ポリビニルアルコール系樹脂を含有する偏光子の少なくとも片面に保護フィルムを有する偏光フィルムであり、
前記偏光子の厚みが10μm以下であり、かつ、単体透過率が43.0%以上であり、
前記輝度向上フィルムの偏光度が90%以上あり、
前記保護フィルムの厚みが25μm以下であり、かつ、透湿度が200g/(m2・day)以下であることを特徴とする。
(1−1)偏光子
本発明で用いる偏光子は、ポリビニルアルコール系樹脂を含有し、厚みが10μm以下であり、かつ、単体透過率が43.0%以上であるものであればよい。
特許第4751486号明細書、
特許第4751481号明細書、
特許第4815544号明細書、
特許第5048120号明細書、
国際公開第2014/077599号パンフレット、
国際公開第2014/077636号パンフレット、
等に記載されている薄型偏光子又はこれらに記載の製造方法から得られる薄型偏光子を挙げることができる。
とにより延伸による破断等の不具合なく延伸することが可能となる。
本発明で用いる保護フィルムを形成する材料としては、透明性を有し、かつ、透湿度が200g/(m2・day)以下にすることができる材料であればよく、特に限定されない。
前記偏光子と保護フィルムとは、通常、接着剤層を介して密着している。
バルク吸水率(%)=[{(浸漬後の接着層の重量)−(浸漬前の接着層の重量)}/(浸漬前の接着層の重量)]×100
前記ラジカル重合硬化型接着剤は、硬化性化合物としてのラジカル重合性化合物を含む。ラジカル重合性化合物は、活性エネルギー線により硬化する化合物であってもよく、熱により硬化する化合物であってもよい。活性エネルギー線としては、例えば、電子線、紫外線、可視光線等が挙げられる。
前記カチオン重合硬化型接着剤は、硬化性化合物としてのカチオン重合性化合物を含む。カチオン重合性化合物としては、例えば、エポキシ基及び/又はオキセタニル基を有する化合物が挙げられる。エポキシ基を有する化合物は、分子内に少なくとも2個のエポキシ基を有する化合物が好ましく用いられる。エポキシ基を有する化合物としては、例えば、少なくとも2個のエポキシ基と少なくとも1個の芳香環を有する化合物(芳香族系エポキシ化合物)、分子内に少なくとも2個のエポキシ基を有し、そのうちの少なくとも1個は脂環式環を構成する隣り合う2個の炭素原子との間で形成されている化合物(脂環式エポキシ化合物)等が挙げられる。
本発明で使用する粘着剤層は、特に限定されるものではなく、公知の粘着剤組成物から形成される粘着剤層を使用することができる。
本発明で使用する輝度向上フィルムは、偏光度が90%以上であり、95%以上であることが好ましい。本発明においては、偏光度が90%以上の輝度向上フィルムを用いるため、ムラ視認性を軽減することができる。輝度向上フィルムはバックライトからの光を偏光に変換するため、偏光フィルムには偏光が入射される。すなわち、高温高湿環境により偏光フィルムの偏光度が劣化しても、高い偏光度を有する輝度向上フィルムを通過して偏光が入射されるため、偏光フィルムの偏光度劣化の影響が小さく、表示ムラの発生を抑制できるものである。
本発明の画像表示装置は、前記積層フィルムを有することを特徴とする。本発明の積層フィルムは、液晶表示セルのバックライト側偏光フィルムとして好適に用いることができる。
非晶性PET基材に9μm厚のPVA層が製膜された積層体を延伸温度130℃の空中補助延伸によって延伸積層体を生成し、次に、延伸積層体をヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度0.3%の水溶液に浸漬して着色積層体を生成し、さらに着色積層体を延伸温度65℃のホウ酸水中延伸によって総延伸倍率が5.94倍になるように非晶性PET基材と一体に延伸された5μm厚のPVA層を含む光学フィルム積層体を生成した。このような2段延伸によって非晶性PET基材に製膜されたPVA層のPVA分子が高次に配向され、染色によって吸着されたヨウ素がポリヨウ素イオン錯体として一方向に高次に配向された高機能偏光膜を構成する、厚さ5μmのPVA層(偏光子)(1)を含む光学フィルム積層体を生成した。得られた光学フィルム積層体のPVA層の透過率は43.3%であり、ホウ酸含有量は23重量%であった。
ヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度を0.2%に変更した以外は、製造例1と同様にして、厚さ5μmのPVA層(偏光子)(2)を含む光学フィルム積層体を生成した。得られた光学フィルム積層体のPVA層の透過率は44.0%であり、ホウ酸含有量は23重量%であった。
ヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度を0.23%に変更した以外は、製造例1と同様にして、厚さ5μmのPVA層(偏光子)(3)を含む光学フィルム積層体を生成した。得られた光学フィルム積層体のPVA層の透過率は43.7%であり、ホウ酸含有量は23重量%であった。
ヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度を0.23%に変更した以外は、製造例1と同様にして、厚さ5μmのPVA層(偏光子)(4)を含む光学フィルム積層体を生成した。得られた光学フィルム積層体のPVA層の透過率は42.8%であり、ホウ酸含有量は23重量%であった。
平均重合度2400、ケン化度99.9モル%の厚み20μmのポリビニルアルコールフィルムを、30℃の温水中に60秒間浸漬し膨潤させた。次いで、ヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度0.3%の水溶液に浸漬し、3.5倍まで延伸させながらフィルムを染色した。その後、65℃のホウ酸エステル水溶液中で、トータルの延伸倍率が6倍となるように延伸を行った。延伸後に、40℃のオーブンにて3分間乾燥を行い、厚さ7μmの偏光子(5)を得た。得られた偏光子の透過率は43.3%であり、ホウ酸含有量は23重量%であった。
平均重合度2400、ケン化度99.9モル%の厚み30μmのポリビニルアルコールフィルムを、30℃の温水中に60秒間浸漬し膨潤させた。次いで、ヨウ素/ヨウ化カリウム(重量比=0.5/8)の濃度0.3%の水溶液に浸漬し、3.5倍まで延伸させながらフィルムを染色した。その後、65℃のホウ酸エステル水溶液中で、トータルの延伸倍率が6倍となるように延伸を行った。延伸後に、40℃のオーブンにて3分間乾燥を行い、厚さ12μmの偏光子(6)を得た。得られた偏光子の透過率は43.5%であり、ホウ酸含有量は23重量%であった。
ヒドロキシエチルアクリルアミド(HEAA、logP=−0.56、ホモポリマーのTg=123℃、興人社製)10重量部、テトラヒドロフルフリル(メタ)アクリレート(FA−THFM、logP=1.13、ホモポリマーのTg=45℃、日立化成(株)製)10重量部、トリシクロデカンジメタノールジアクリレート(商品名:ライトアクリレートDCP−A、logP=3.05、ホモポリマーのTg=134℃、共栄社化学(株)製)80重量部、2−メチル−1−(4−メチルチオフェニル)−2−モルフォリノプロパン−1−オン(商品名:IRGACURE907、logP=2.09、BASF社製)3重量部、ジエチルチオキサントン(商品名:KAYACURE DETX−S、logP=5.12、日本化薬(株)製)3重量部を混合して50℃で1時間撹拌し、活性エネルギー線により硬化し得る硬化型接着剤を得た。
グルタルイミド環単位を有するメタクリル樹脂ペレットを、100.5kPa、100℃で12時間乾燥させ、単軸の押出機にてダイス温度270℃でTダイから押出してフィルム状に成形した。さらに当該フィルムを、その搬送方向に、樹脂のTgより10℃高い雰囲気下で延伸し、次いでフィルム搬送方向と直交する方向に樹脂のTgより7℃高い雰囲気下で延伸して、アクリル系樹脂から構成される保護フィルムを得た。得られたフィルムの透湿度は、150g/(m2・day)であり、厚みは20μmであった。
製造例1で得られた光学フィルム積層体の偏光膜の表面に、製造例7で製造した硬化型粘着剤を塗布し、コロナ処理した厚さ20μmのアクリルフィルムを貼合せた。その後、アクリルフィルム側から、IRヒーターを用いて50℃に加温し、可視光線をアクリルフィルム側に照射して前記硬化型接着剤を硬化させた後、70℃で3分間熱風乾燥して、非晶性PET基材/偏光子/接着剤層(厚み:1μm)/アクリルフィルムからなる積層体を得た。得られた積層体から、非晶性PET基材を剥離して、アクリル面に、厚さ5μmのアクリル系接着剤層を介して、輝度向上フィルム(商品名:APF−V4、偏光度:92%、3M製)を貼り合わせた。得られた積層体の偏光子面に、厚さ20μmの粘着剤層(商品名:No.58、日東電工(株)製)を貼り合せ、積層フィルムを得た。なお、この積層フィルムの構成(粘着剤層/偏光子/保護フィルム/輝度向上フィルム)を構成Aという。
製造例1で得られた光学フィルム積層体の偏光膜の表面に、製造例7で製造した硬化型粘着剤を塗布し、コロナ処理した厚さ20μmのアクリルフィルムを貼合せた。その後、アクリルフィルム側から、IRヒーターを用いて50℃に加温し、可視光線をアクリルフィルム側に照射して前記硬化型接着剤を硬化させた後、70℃で3分間熱風乾燥して、非晶性PET基材/偏光子/接着剤層(厚み:1μm)/アクリルフィルムからなる積層体を得た。得られた積層体の偏光子面に、厚さ5μmのアクリル系接着剤層を介して、輝度向上フィルム(商品名:APF−V4、偏光度:92%、3M製)を貼り合わせた。得られた積層体から、非晶性PET基材を剥離して、アクリルフィルム面に、厚さ20μmの粘着剤層(商品名:No.58、日東電工(株)製)を貼り合せ、積層フィルムを得た。なお、この積層フィルムの構成(粘着剤層/保護フィルム/偏光子/輝度向上フィルム)を構成Bという。
製造例5で得られた偏光子(5)の片面に、製造例7で製造した硬化型粘着剤を塗布し、コロナ処理した厚さ20μmのアクリルフィルムを貼合せた。その後、アクリルフィルム側から、IRヒーターを用いて50℃に加温し、可視光線をアクリルフィルム側に照射して前記硬化型接着剤を硬化させた後、70℃で3分間熱風乾燥して、偏光子/接着剤層(厚み:1μm)/アクリルフィルムからなる積層体を得た。得られた積層体のアクリルフィルム面に、厚さ5μmのアクリル系接着剤層を介して、輝度向上フィルム(商品名:APF−V4、偏光度:92%、3M製)を貼り合わせた。得られた積層体の偏光子面に、厚さ20μmの粘着剤層(商品名:No.58、日東電工(株)製)を貼り合せ、積層フィルムを得た。
製造例2で得られた光学フィルム積層体を用い、コロナ処理した厚さ13μmのCOPフィルムを用いた以外は、実施例1と同様にして積層フィルムを得た。
製造例3で得られた光学フィルム積層体を用いた以外は、実施例1と同様にして積層フィルムを得た。
輝度向上フィルムにAPF−V3を用いた以外は、実施例1と同様にして積層フィルムを得た。
用いた偏光子、保護フィルム、粘着剤層、輝度向上フィルムを表1に記載のものに変更した以外は、実施例1と同様にして積層フィルムを形成した。
実施例及び比較例で使用したPVA層(偏光子)の厚みは、デジタルマイクロメーター(KC-351C、アンリツ社製)を用いて測定した。
実施例及び比較例で使用したPVA層(偏光子)の単体透過率Tは、紫外可視分光光度計(V7100、日本分光(株)製)を用いて測定した。これらの透過率は、JIS Z8701の2度視野(C光源)により測定して視感度補正を行なったY値である。
実施例及び比較例で使用したPVA層(偏光子)を加熱乾燥(120℃、2時間)し、その後、粉砕して、重量1gの評価用サンプルを得た。95℃の水500mLに、該評価用サンプル1gをすべて溶解させた。得られた水溶液に、マンニトール10gと、ブロモチモールブルー溶液(BTB溶液)2mLを加えて、サンプル溶液を調製した。このサンプル溶液に、中和点を迎えるまで、0.1mol/Lの水酸化ナトリウムを滴下し、その滴下量から、下記式に基づき、ホウ酸含有量(重量%)を算出した。
保護フィルムの透湿度の測定は、JIS Z0208の透湿度試験(カップ法)に準じて測定した。直径60mmに切断したサンプルを約15gの塩化カルシウムを入れた透湿カップにセットし、40℃、90%の恒温機に入れ、24時間放置した前後の塩化カルシウムの重量増加を測定することで透湿度(g/m2・day)を求めた。
実施例及び比較例で使用した粘着剤を用いて、厚さ25μmの粘着剤層を形成した。得られた厚さ25μmの粘着剤層を10mm巾×30mmに切断したものをサンプルとした。このサンプルの上部の10mm×10mmを、ベーク板に貼着し、50℃、50atmで15分間のオートクレーブ処理をした後、室温(23℃)で1時間放置した。その後、サンプルに、500gの荷重を負荷(垂下方向への引張り剪断応力の負荷)し、1時間後のサンプルのズレ量(μm)を測定した。
実施例及び比較例で使用した硬化型接着剤を、実施例と同様の条件で硬化させて、厚み100μmの評価用硬化物(重量:M1g)を作製した。該評価用硬化物を、23℃の純水に24時間浸漬させ、その後、取り出して表面の水を拭き取った後、浸漬後の該評価用硬化物の重量(M2g)を測定した。浸漬前の評価用硬化物の重量M1gと、浸漬後の評価用硬化物の重量M2から、以下の式によりバルク吸水率を算出した。
輝度向上フィルムの単体透過率T、平行透過率Tp、直交透過率Tcを紫外可視分光光度計(日本分光(株)製のV7100)を用いて測定した。これらの透過率は、JIS Z8701の2度視野(C光源)により測定して視感度補正を行なったY値である。輝度向上フィルムの偏光度Pを上記の透過率を用い、次式により求めた。
偏光度P(%)={(Tp−Tc)/(Tp+Tc)}1/2×100
実施例、比較例で得られた積層フィルムを、偏光子の延伸方向が0°になるように、100mm×100mmのサイズにカットし、厚み1mmのガラス板上に、粘着剤層を介して貼り合わせて測定サンプルとし、偏光フィルムの四隅に印をつけた。(株)ミツトヨ製の画像測定機(クイックビジョン)により、偏光フィルムの四隅の印間の長さL0を測定した。測定したサンプルを、85℃の加熱オーブン中に500時間投入したのち、再度、偏光フィルムの四隅の印間の長さL500を測定した。寸法変化率は次式により算出した。
寸法変化率(%)={(L500−L0)/L0}×100
実施例及び比較例で得られた積層フィルムの外観検査において、糊打痕の発生を目視で確認した。1m2あたりの糊打痕の発生数をカウントした。
厚さ0.3mmの無アルカリガラスの一方に、実施例及び比較例で得られた積層フィルム、他方に、厚さ12μmのPVAフィルムを用いた偏光板(商品名:GRT1794KUHC3、透過率:43.0%、日東電工(株)製)を、それぞれの偏光子の吸収軸が直交になるように貼り合わせて、60℃、R.H.90%の環境下に500時間投入した。取り出した後、暗室でバックライト輝度(7000cd/cm2又は10000cd/cm2)の上での面内スジ状ムラを目視にて確認した。
◎:10000cd/cm2のバックライトを用いた場合であってもスジ状ムラなし。
〇:7000cd/cm2のバックライトを用いた場合にスジ状ムラなし。
△:7000cd/cm2のバックライトを用いた場合にスジ状ムラ一部にあり。
×:7000cd/cm2のバックライトを用いた場合にスジ状ムラ全面にあり。
得られた積層フィルムを100mm×100mmのサイズに切り出しサンプルを作製した。得られたサンプルをガラス板に貼り合わせ、ヒートサイクル試験(−40℃〜85℃/30分)を200サイクル行い、クラック発生の有無を目視で確認した。
〇:クラック発生なし。
×:クラック発生あり。
iPad(登録商標)Air(Apple社製)パネルのTFT側の偏光板を剥がして、実施例、比較例の偏光板を貼り合わせた後に、白表示状態時の輝度をSR−UL1(TOPCON CORPORATION)を用いて暗室で測定を行った。
厚さ0.3mmの無アルカリガラスの一方に、実施例及び比較例で得られた積層フィルム、他方に、厚さ12μmのPVAフィルムを用いた偏光板(商品名:GRT1794KUHC3、日東電工(株)製)を、それぞれの偏光子の吸収軸が直交になるように貼り合わせて、85℃の環境下に500時間投入した。取り出した後、QVA606−PRO−AE10((株)ミツトヨ製)を用いて反り量を測定した。
〇:反りが発生しないか、又は、問題とならない程度の反りが発生した。
×:顕著な反りが発生した。
(積層フィルムの構成)
構成A:粘着剤層/偏光子/保護フィルム/輝度向上フィルム
構成B:粘着剤層/保護フィルム/偏光子/輝度向上フィルム
(偏光子)
偏光子(1)〜(6):製造例1〜6で得られた偏光子(1)〜(6)
(輝度向上フィルム)
APF−V4:輝度向上フィルムの商品名、偏光度:92%、3M製
APF−V3:輝度向上フィルムの商品名、偏光度:95%、3M製
DBEF−QV2:輝度向上フィルムの商品名、偏光度:88%、3M製
AF−film:輝度向上フィルムの商品名、偏光度:62%、Extend製
(保護フィルム)
アクリル系:製造例8で得られたアクリル系保護フィルム、透湿度:150g/(m2・day)、厚み:20μm
COP:シクロオレフィン系保護フィルム、透湿度:30g/(m2・day)、厚み:13μm、商品名:ZF14−013、日本ゼオン製
TAC系保護フィルム、透湿度:800g/(m2・day)、厚み:25 μm、商品名:TJ25UL、富士フィルム製
(粘着剤層)
No.58:商品名、クリープ値:120μm、日東電工(株)製
2 偏光フィルム
2a 偏光子
2b 保護フィルム
2c 保護フィルム
3 輝度向上フィルム
4 粘着剤層
Claims (6)
- 粘着剤層、偏光フィルム、及び輝度向上フィルムをこの順に含む積層フィルムであって、
前記偏光フィルムは、ポリビニルアルコール系樹脂を含有する偏光子の少なくとも片面に保護フィルムを有する偏光フィルムであり、
前記偏光子の厚みが10μm以下であり、かつ、単体透過率が43.0%以上であり、
前記輝度向上フィルムの偏光度が90%以上あり、
前記保護フィルムの厚みが25μm以下であり、かつ、透湿度が200g/(m2・day)以下であることを特徴とする積層フィルム。 - 前記偏光子のホウ酸含有量が、18〜24重量%であることを特徴とする請求項1に記載の積層フィルム。
- 前記粘着剤層のクリープ値が100〜150μmであり、
前記積層フィルムを、85℃で500時間放置した後の前記偏光子の吸収軸方向の加熱収縮率が、0.5%以下であることを特徴とする請求項1又は2に記載の積層フィルム。 - 前記偏光子と保護フィルムが接着剤層を介して積層されており、
前記接着剤層のバルク吸水率が10重量%以下であることを特徴とする請求項1〜3のいずれかに記載の積層フィルム。 - 前記偏光フィルムが、偏光子の片面のみに保護フィルムを有する偏光フィルムであり、
前記積層フィルムが、粘着剤層、保護フィルム、偏光子、及び輝度向上フィルムをこの順に含むか、又は、粘着剤層、偏光子、保護フィルム、及び輝度向上フィルムをこの順に含むことを特徴とする請求項1〜4のいずれかに記載の積層フィルム。 - 請求項1〜5のいずれかに記載の積層フィルムを有することを特徴とする画像表示装置。