JP2017048080A - 破砕剤組成物 - Google Patents
破砕剤組成物 Download PDFInfo
- Publication number
- JP2017048080A JP2017048080A JP2015171691A JP2015171691A JP2017048080A JP 2017048080 A JP2017048080 A JP 2017048080A JP 2015171691 A JP2015171691 A JP 2015171691A JP 2015171691 A JP2015171691 A JP 2015171691A JP 2017048080 A JP2017048080 A JP 2017048080A
- Authority
- JP
- Japan
- Prior art keywords
- agent
- crushing
- hydrate
- agent composition
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】金属酸化物と金属粉末とから成るテルミット剤、水和物及びバインダーを含み、テルミット剤1g当たりの酸素バランスが−0.35〜−0.12g/gであり、バインダーの含有率が1.5質量%以下であることを特徴とする破砕剤組成物。
【選択図】なし
Description
(1)金属酸化物と金属粉末とから成るテルミット剤、水和物及びバインダーを含み、テルミット剤1g当たりの酸素バランスが−0.35〜−0.12であり、バインダーの含有率が1.5質量%以下であることを特徴とする破砕剤組成物、
(2)金属酸化物が、酸化第二銅、酸化第二鉄又はこれらの混合物であり、金属粉末が、アルミニウム、マグネシウム又はこれらの混合物であることを特徴とする(1)に記載の破砕剤組成物、
(3)水和物が、硫酸アルミニウム・18水和物、硫酸亜鉛・7水和物、硫酸マグネシウム・7水和物、カリウム明礬・12水和物、及びアンモニウム明礬・12水和物から成る群から選択される1種以上であることを特徴とする(1)又は(2)のいずれか一項に記載の破砕剤組成物、
(4)バインダーが、DSCで発熱ピークを示さないことを特徴とする(1)乃至(3)のいずれか一項に記載の破砕剤組成物、
に関する。
本発明は、製造作業時及び使用時の安全性並びに利便性に配慮した破砕剤に関する。
本発明の破砕剤は、テルミット剤の酸素バランスを制限すること等により、各種感度が低減し、製造時及び使用時の安全性が高く、火薬類取締法及び消防法上の制約を受けないという利点がある。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.24のテルミット剤69.5%(酸化第二銅/アルミニウムの質量比率 60/40)、アンモニウム明礬・12水和物(和光純薬工業(株)製)30%、予めエタノールに溶解させたエチルセルロース(和光純薬工業(株)製)0.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.19のテルミット剤64.5%(酸化第二銅/アルミニウムの質量比率 64/36)、アンモニウム明礬・12水和物(和光純薬工業(株)製)35%、予めエタノールに溶解させたポリビニルピロリドン(和光純薬工業(株)製)0.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.32のテルミット剤64.5%(酸化第二銅/アルミニウムの質量比率 52/48)、アンモニウム明礬・12水和物(和光純薬工業(株)製)35%、予めエタノールに溶解させたポリビニルピロリドン(和光純薬工業(株)製)0.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.15のテルミット剤64.5%(酸化第二銅/アルミニウムの質量比率 68/32)、アンモニウム明礬・12水和物(和光純薬工業(株)製)35%、予めエタノールに溶解させたポリビニルピロリドン(和光純薬工業(株)製)0.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(日本化学産業(株)製)/アルミニウム(東洋アルミニウム(株)製)から成る、酸素バランス−0.05のテルミット剤49.5%(酸化第二銅/アルミニウムの質量比率 77/23)、カリウム明礬・12水和物(和光純薬工業(株)製)49%、予めエタノールに溶解させたヒドロキシプロピルメチルセルロース(和光純薬工業(株)製)1.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.24のテルミット剤49.5%(酸化第二銅/アルミニウムの質量比率 60/40)、アンモニウム明礬・12水和物(和光純薬工業(株)製)49%、予めエタノールに溶解させたポリビニルピロリドン(和光純薬工業(株)製)1.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(日本化学産業(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.02のテルミット剤54.7%(酸化第二銅/アルミニウムの質量比率 80/20)、硫酸マグネシウム・7水和物アンモニウム明礬・12水和物(和光純薬工業(株)製)45%、予めエタノールに溶解させたヒドロキシプロピルメチルセルロース(和光純薬工業(株)製)0.3%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス±0のテルミット剤64.5%(酸化第二銅/アルミニウムの質量比率 82/18)、アンモニウム明礬・12水和物(和光純薬工業(株)製)35%、予めエタノールに溶解させたポリビニルピロリドン(和光純薬工業(株)製)0.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
酸化第二銅(古河ケミカルズ(株)製)/アルミニウム(和光純薬工業(株)製)から成る、酸素バランス−0.38のテルミット剤64.5%(酸化第二銅/アルミニウムの質量比率 47/53)、アンモニウム明礬・12水和物(和光純薬工業(株)製)35%、予めエタノールに溶解させたポリビニルピロリドン(和光純薬工業(株)製)0.5%をSUS製容器内において竹べらで混合し、目開き2.8mmの篩を通した後、常温で一昼夜風乾して破砕剤組成物を調製した。
縦横200mm、高さ500mmのコンクリートブロックにおいて、最小抵抗線100mm、穿孔長200mmの装薬孔に各破砕剤を装薬し、砂でタンピングした後、専用点火具で着火し、コンクリートブロックが破砕される最少薬量を測定した。
火薬学会規格ES−21(1)及びES−22に各々規定の落つい感度試験及び摩擦感度試験により、落つい感度及び摩擦感度を測定した。
火薬学会規格ES−25で規定されている静電気感度試験に準じて静電気感度を測定した。静電気感度試験装置((株)日本テクナート製)を用い、試料状態は開放状態、電極間隙長は0.1mmで測定した。
消防法に基づく危険物第2類の判定試験である小ガス炎着火試験を行い、火炎を接触させてから着火するまでの時間を測定した。着火時間≦3秒以内であれば第一種可燃性固体、3秒<着火時間≦10秒であれば第二種可燃性固体、不着火又は燃焼不継続であれば非危険物となる。第一種可燃性固体及び第二種可燃性固体の指定数量は各々100kg、500kgであり、指定数量以上の貯蔵・取扱にあっては消防法に基づく特定場所での許可が必要となる。
消防法に基づく危険物第5類の判定試験である圧力容器試験を行い、100〜200℃の範囲で40±5℃/minで昇温した時の9.0mm又は1.0mmのオリフィス板を取り付けた圧力容器の破裂板の破裂の有無を観察した。各破砕剤組成物は消防法別表第一の第五類の品名欄に掲げる物品ではないため、消防法上は危険物第5類にならないが、9.0mm、1.0mmのオリフィス板で破裂板が50%以上の確率で破裂した場合、それぞれ第一種自己反応性物質、第2種自己反応性物質と同等の加熱分解の激しさの危険性を有することになる。
消防法に基づく危険物第5類の判定試験である熱分析試験を行った。熱分析装置(DSC8230型:理学製)を用いて標準物質(2,4−ジニトロトルエン及び過酸化ベンゾイル)、各破砕剤組成物の発熱開始温度及び発熱量を測定し、標準物質から求められた危険性の基準と比較して爆発の危険性について確認した。
これらの試験結果を表1に示す。
これに対し、比較例1の破砕剤組成物は、酸素バランスが−0.12g/gよりもプラス側であるため、破砕性能は比較的優れているものの、静電気感度が高く、小ガス炎着火試験では第二種可燃性固体に該当し、圧力容器試験及び熱分析試験では第一種自己反応性物質と同等の危険性を示す結果となった。
比較例2の破砕剤組成物は、酸素バランスが−0.29g/gであるが、バインダー含有率が1.5%よりも多いため、各種感度が低く、危険物非該当であるものの、破砕性能が実施例に比べて劣る結果となった。
比較例3の破砕剤組成物は、酸素バランスが−0.12g/gよりもプラス側であるため、静電気感度が高く、破砕性能が劣る結果となった。
比較例5の破砕剤組成物は、酸素バランスが−0.35g/gよりもマイナス側であるため、各種感度は比較的低く、危険物非該当であるものの、優れた破砕性能が得られないことが確認された。
Claims (4)
- 金属酸化物と金属粉末とから成るテルミット剤、水和物及びバインダーを含み、テルミット剤1g当たりの酸素バランスが−0.35〜−0.12g/gであり、バインダーの含有率が、1.5質量%以下であることを特徴とする破砕剤組成物。
- 金属酸化物が、酸化第二銅、酸化第二鉄又はこれらの混合物であり、金属粉末が、アルミニウム、マグネシウム又はこれらの混合物であることを特徴とする請求項1に記載の破砕剤組成物。
- 水和物が、硫酸アルミニウム・18水和物、硫酸亜鉛・7水和物、硫酸マグネシウム・7水和物、カリウム明礬・12水和物、及びアンモニウム明礬・12水和物から成る群から選択される1種以上であることを特徴とする請求項1又は請求項2のいずれか一項に記載の破砕剤組成物。
- バインダーが、DSCで発熱ピークを示さないことを特徴とする請求項1乃至請求項3のいずれか一項に記載の破砕剤組成物。