CN102603440A - 一种用于爆炸焊接的低爆速粉状乳化炸药 - Google Patents
一种用于爆炸焊接的低爆速粉状乳化炸药 Download PDFInfo
- Publication number
- CN102603440A CN102603440A CN2012100991522A CN201210099152A CN102603440A CN 102603440 A CN102603440 A CN 102603440A CN 2012100991522 A CN2012100991522 A CN 2012100991522A CN 201210099152 A CN201210099152 A CN 201210099152A CN 102603440 A CN102603440 A CN 102603440A
- Authority
- CN
- China
- Prior art keywords
- explosive
- welding
- detonation velocity
- low detonation
- powdery emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于爆炸焊接的低爆速粉状乳化炸药，按重量计，由粉状乳化炸药60～85%，滑石粉、膨胀珍珠岩至少一种15～40%混合而成。所述的滑石粉的水分不高于0.5wt%，40目的细度占70—85wt%；膨胀珍珠岩的水分不高于0.5wt%，堆积密度为40～60kg/m3；本发明的密度为0.6～0.85g/cm3。本发明具有易于生产、性能稳定、猛度较高、爆炸焊接效果好的特点。
Description
技术领域
本发明涉及一种乳化炸药，特别涉及一种用于爆炸焊接的低爆速粉状乳化炸药。
背景技术
爆炸焊接技术是一种以炸药为能源的压力焊、熔化焊和扩散焊三位一体的金属焊接工艺：以炸药为能源，通过炸药爆轰产生的脉冲载荷，推动一种材料（复层）高速倾斜碰撞另一种材料（基层），由瞬间产生的高温高压实现两种金属的冶金结合。其产生的金属复合板的主要用途是替代价格昂贵的不锈钢和有色金属，用于石化、化工、船舶、车辆及耐热、耐磨和特殊要求的设备货构件，以达到降低工程造价的目的。由于焊接技术的特殊要求，其使用的专用炸药爆速为2.0×103—2.8×103m/s、猛度为9—11mm、密度为0.6g/cm3—0.85g/cm3,即为一般意义上的低爆速炸药。目前，市场上使用的低爆速炸药大致分为两种：第一种为单质猛炸药加稀释剂，如中国专利CN85103347A披露的采用定型的猛炸药加稀释剂加工而成，所用的猛炸药为梯恩梯、黑索今等军用猛炸药，这些炸药成本高，机械感度也高，生产过程危险性高；同时，梯恩梯是国家禁止在工业炸药中使用的炸药品种之一；再者，该炸药在爆炸过程中会产生大量的有害废气，污染环境。第二种是在膨化硝铵炸药中加入稀释剂，如加入珍珠岩粉、空心玻璃微球、矿物微粉等微粉颗粒，以降低爆速和猛度。这种炸药与第一种相比，具有质量稳定和环保等特点，但是存在猛度、威力均低，爆轰性能难以达到爆炸焊接炸药要求的缺点。中国专利CN1778777A披露了一种低爆速爆炸焊接炸药，采用铵油炸药与添加剂混合而成，该专利在加工时采用目前民爆行业已被淘汰的轮碾工艺，目前也无法实施，而且铵油炸药威力低，加入惰性物质后性能下降更快，从而出现性能不稳定现象，达不到爆炸焊接的猛度要求。
发明内容
本发明所要解决的技术问题是提供了一种用于爆炸焊接的低爆速粉状乳化炸药，具有易生产、性能稳定、猛度较高的特点，从而达到较好的爆炸焊接效果。
为解决上述技术问题，本发明一种用于爆炸焊接的低爆速粉状乳化炸药，按重量计，由下列原料制成：
普通粉状乳化炸药60～85%、
滑石粉、膨胀珍珠岩中的至少一种15～40%。
上述方案中，所述的滑石粉的水分不高于0.5 wt %，40目的细度占70—85wt%；膨胀珍珠岩的水分不高于0.5 wt %，堆积密度为40～60kg/m3。滑石粉太细，将会在生产过程中随旋风分离器分离出去，滑石粉细度高于40目，影响混合的均匀度，使产品性能受影响。滑石粉和珍珠岩的水份控制一定要不高于0.5 wt %，否则制备的低爆速炸药容易吸潮，结块，易失去爆轰性能。
本发明具有以下优点和特点：
1、易于生产。即以普通的粉状乳化炸药为主体，添加适量惰性物质如：滑石粉、膨胀珍珠岩一种或者两种，按一定的比例混合即可；粉状乳化炸药为市售，来源广泛，价格相对适中；
2、性能稳定。粉状乳化炸药相比铵油炸药威力高，由其制备的低爆速爆炸焊接炸药性能稳定，满足爆炸焊接炸药猛度9～11mm的要求，从而保障爆炸焊接效果。
具体实施方式
实施例1
取普通粉状乳化炸药160kg、滑石粉40 kg，混合均匀，即可得本发明一种用于爆炸焊接低爆速粉状乳化炸药，爆速2800m/s，猛度10.9mm，密度0.82 g/cm3。
实施例2
取普通粉状乳化炸药160kg、滑石粉30 kg、珍珠岩10 kg，混合均匀，即可得本发明一种用于爆炸焊接低爆速粉状乳化炸药，爆速2580m/s，猛度9.2mm，密度0.72 g/cm3。
实施例3
取普通粉状乳化炸药120kg、滑石粉60 kg、珍珠岩20 kg，混合均匀，即可得本发明一种用于爆炸焊接低爆速粉状乳化炸药，爆速2080m/s，猛度8.5mm，密度0.68 g/cm3。
实施例4
取普通粉状乳化炸药170kg、珍珠岩30 kg，混合均匀，即可得本发明一种用于爆炸焊接低爆速粉状乳化炸药，爆速2280m/s，猛度10.5mm，密度0.65 g/cm3。
实施例1—4中的滑石粉的水分不高于0.5 wt %，40目的细度占70—85wt%；膨胀珍珠岩的水分不高于0.5 wt %，堆积密度为40～60kg/m3。
普通粉状乳化炸药 (质量％)：是以硝酸铵75～88、有机油相材料2～6、乳化剂1～3、助溶剂1～3、水1～5组成，采用乳化方式将氧化剂和可燃物混合成均一的乳胶，再由喷雾制粉工艺将乳胶直接制成产品。该产品可广泛适用于露天及无可燃气和（或）矿尘爆炸危险的地下爆破工程。
由实施例1—4可见，本发明通过粉状乳化炸药和滑石粉、膨胀珍珠岩中的一种或者两种，简单的混合制备而成，其密度为0.6～0.85g/cm3，满足爆炸焊接炸药猛度9～11mm的要求，从而具有良好的爆炸焊接效果。
Claims (2)
1.一种用于爆炸焊接的低爆速粉状乳化炸药，按重量计，由下列原料制成：
普通粉状乳化炸药60～85%、
滑石粉、膨胀珍珠岩中的至少一种15～40%。
2.根据权利要求1所述的一种用于爆炸焊接低的爆速粉状乳化炸药，其特征是：所述的滑石粉的水分不高于0.5wt%， 40目的细度占70—85wt%；膨胀珍珠岩的水分不高于0.5 wt %，堆积密度为40～60kg/m3。