JP2015081753A - 無機繊維耐火断熱ライニング施工方法及び炉 - Google Patents
無機繊維耐火断熱ライニング施工方法及び炉 Download PDFInfo
- Publication number
- JP2015081753A JP2015081753A JP2013221266A JP2013221266A JP2015081753A JP 2015081753 A JP2015081753 A JP 2015081753A JP 2013221266 A JP2013221266 A JP 2013221266A JP 2013221266 A JP2013221266 A JP 2013221266A JP 2015081753 A JP2015081753 A JP 2015081753A
- Authority
- JP
- Japan
- Prior art keywords
- inorganic fiber
- furnace
- heat insulation
- construction method
- lining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
無機繊維耐火断熱ライニングから、酸化物前駆体を含有する液状物質液が含浸されていない部分を切断してサンプルとし、このサンプルの重量(g)と加熱面側の面積とを測定し、面比重を次式により求める。
5個のサンプルについて測定した面比重の平均値を添着前の面比重r1とする。含浸後の無機繊維耐火断熱ライニングを1250℃で2時間焼成した後、含浸部分を切り出し同様の方法で面比重r2を測定する。r2とr1の差(r2−r1)を添着量(g/m2)とする。
結晶質のムライトファイバーからなるブランケット(商品名:三菱樹脂株式会社 MAFTEC MLS、厚さ25mm、嵩密度96kg/m3、Al2O3:72質量%、SiO2:28質量%)から300mm×300mmの正方形の板状物を切り出し、これを16枚積層した後、圧縮し、高さ300mm×幅300mm×長さ300mmのブロック(商品名:新日本サーマルセラミックス Z‐BLOK1600)を用いた。これをブロックライニング工法により熱延加熱炉の天井へ施工した。
実施例1において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を2.5%、施工速さを1.05m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例1において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を15%、施工速さを0.04m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。評価結果を表1に示す。
実施例1において、酸化物前駆体の調製原料としてマグネシウム塩(酢酸マグネシウム四水和物)、前記アルミナゾル及び水を用い、酸化物前駆体を含有する液状物質の焼成後の酸化物質量比(MgO/Al2O3)を28:72としたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
結晶質のムライトファイバーからなるブランケット(商品名:三菱樹脂株式会社 MAFTEC MLS、厚さ25mm、嵩密度96kg/m3、Al2O3:72質量%、SiO2:28質量%)の一方の面側に接着剤(商品名:新日本サーマルセラミックス株式会社 サーモプレグCW)を塗布し、熱延加熱炉のスキッドパイプへ巻きつけて固定した。実施例1と同様の液状物質を、リシンガンを用いて施工速さ0.35m2/minで吹き付けた。
ムライトファイバー(商品名:三菱樹脂株式会社 MAFTEC MLS)とアルミナ粒子を水中に分散させ、凝集材及び結合材としてコロイダルシリカとカチオン性スターチを添加し、リング状の金型へ真空成形した後、乾燥してリング状モールド(商品名:新日本サーマルセラミックス SCボールド1600スキッドポスト 嵩密度250kg/m3 高さ50×内径230×外径340mm)を作製し、熱延加熱炉のスキッドポストへ施工した。実施例1と同様の液状物質を、リシンガンを用いて施工速さ0.35m2/minで吹き付けた。
実施例1において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を1.5%、施工速さを1.65m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例1において施工速さを0.05m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例3において、酸化物前駆体にシリカゾル、前述のアルミナゾル及び水を用い、酸化物前駆体を含有する液状物質の焼成後の酸化物質量比(SiO2/Al2O3)を28:72としたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例3において、酸化物前駆体にアルミナゾル及び水を用い、酸化物換算成分濃度15wt%の液状物質を吹き付けたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例5において、酸化物前駆体を含有する液状物質を用いなかったこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例5において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を10%、施工速さを1.05m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例5において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を1.5%、施工速さを1.65m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例6において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を10%、施工速さを1.05m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す。
実施例6において、酸化物前駆体を含有する液状物質の酸化物換算成分濃度を1.5%、施工速さを1.65m2/minとしたこと以外は同様にして無機繊維耐火断熱ライニングを得た。含浸厚み及び添加量の測定結果並びに評価結果を表1に示す
表1の通り、実施例1〜6はいずれも耐スケール性に優れる。ブロックを用いた実施例1〜4においても、目地開きは生じない。
Claims (5)
- 無機繊維断熱成形体を炉内に配置する工程と、
酸化物前駆体を含有する液状物質を該無機繊維断熱成形体の炉内加熱面側に付着させる工程と
を有する無機繊維耐火断熱ライニング施工方法において、
該液状物質を該無機繊維断熱成形体の炉内加熱面側から炉壁面側の深さ方向の少なくとも3〜30mmの領域に含浸させ、前記酸化物前駆体の添着量を焼成後の酸化物換算で50〜2000g/m2とすることを特徴とする無機繊維耐火断熱ライニング施工方法。 - 前記酸化物前駆体がCaO前駆体及びMgO前駆体の少なくとも一方と、Al2O3前駆体とを含むことを特徴とする請求項1に記載の無機繊維耐火断熱ライニング施工方法。
- スプレーまたは刷毛塗りによって前記酸化物前駆体の液状物質を前記無機繊維断熱成形体に付着させることを特徴とする請求項1または2に記載の無機繊維耐火断熱ライニング施工方法。
- 液状物質が着色されていることを特徴とする請求項1〜3のいずれかに記載の無機繊維耐火断熱ライニング施工方法。
- 請求項1〜4のいずれか1項に記載の無機繊維耐火断熱ライニング施工方法によって形成された無機繊維耐火ライニングを有する炉。