JP2013256692A - 銅製錬スラグからの銅の回収方法 - Google Patents
銅製錬スラグからの銅の回収方法 Download PDFInfo
- Publication number
- JP2013256692A JP2013256692A JP2012133136A JP2012133136A JP2013256692A JP 2013256692 A JP2013256692 A JP 2013256692A JP 2012133136 A JP2012133136 A JP 2012133136A JP 2012133136 A JP2012133136 A JP 2012133136A JP 2013256692 A JP2013256692 A JP 2013256692A
- Authority
- JP
- Japan
- Prior art keywords
- slag
- copper
- mat
- smelting
- magnetite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】銅製錬により発生したスラグを保持した保持炉内において、その保持炉内に設けた攪拌装置によりスラグを攪拌し、スラグ中の銅粒子を沈降させる。攪拌に際しては、1cm/sより大きな流速の旋回流を生じさせるように攪拌することが好ましい。
【選択図】 なし
Description
先ず、マグネタイト濃縮層の存在と銅粒子の沈降状態について以下のように調査した。
内径17mmのアルミナ製タンマン管の底に銅製錬の実操業で発生したマット20gを装填し、その上に同じく実操業で発生したスラグ40gを載せた。次いで、タンマン管を黒鉛るつぼ内に立てた状態で入れ、この黒鉛坩堝に耐熱ボードで蓋をし、電気炉内に立てた状態で設置した。
タンマン管に装填したスラグ40gとマット20gに対して攪拌処理を施さなかったこと以外は、実施例1と同じ方法で過熱し冷却した。冷却後のタンマン管を、実施例1と同じ方法で輪切りにし、スラグとマットの界面を光学顕微鏡で観察した。
Claims (3)
- 銅製錬により発生したスラグを保持した保持炉内において、該保持炉内に設けた攪拌装置により該スラグを攪拌し、該スラグ中の銅粒子を沈降させることを特徴とする銅製錬スラグからの銅の回収方法。
- 1cm/sより大きな流速の旋回流を生じさせるように攪拌することを特徴とする請求項1記載の銅製錬スラグからの銅の回収方法。
- 上記保持炉内におけるスラグとマットの界面付近に上記攪拌装置の先端部を位置させて攪拌することを特徴とする請求項1又は2記載の銅製錬スラグからの銅の回収方法。