JP2012173369A - カラーフィルタ用着色樹脂組成物 - Google Patents
カラーフィルタ用着色樹脂組成物 Download PDFInfo
- Publication number
- JP2012173369A JP2012173369A JP2011032717A JP2011032717A JP2012173369A JP 2012173369 A JP2012173369 A JP 2012173369A JP 2011032717 A JP2011032717 A JP 2011032717A JP 2011032717 A JP2011032717 A JP 2011032717A JP 2012173369 A JP2012173369 A JP 2012173369A
- Authority
- JP
- Japan
- Prior art keywords
- pigment
- color filter
- acid
- compound
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
【課題】本発明の目的は、耐熱性、耐光性、耐溶剤性に優れたカラーフィルタ用着色組成物および上記特性に優れたカラーフィルタを提供することである。
【解決手段】着色剤と、光重合開始剤と、有機溶剤と、アルカリ可溶性樹脂と、光重合性化合物と、熱架橋性成分とからなるカラーフィルタ用着色樹脂組成物であって、着色剤が、有機顔料と、キサンテン系酸性染料が四級アンモニウム塩化合物で造塩された化合物(A)とからなり、熱架橋性成分が三官能以上の多官能エポキシ樹脂であることを特徴とするカラーフィルタ用着色樹脂組成物によって解決される。
【選択図】なし
【解決手段】着色剤と、光重合開始剤と、有機溶剤と、アルカリ可溶性樹脂と、光重合性化合物と、熱架橋性成分とからなるカラーフィルタ用着色樹脂組成物であって、着色剤が、有機顔料と、キサンテン系酸性染料が四級アンモニウム塩化合物で造塩された化合物(A)とからなり、熱架橋性成分が三官能以上の多官能エポキシ樹脂であることを特徴とするカラーフィルタ用着色樹脂組成物によって解決される。
【選択図】なし
Description
本発明は、カラー液晶表示装置、カラー撮像管素子等に用いられるカラーフィルタの製造に使用されるカラーフィルタ用着色組成物、及びこれを用いて形成されてなるフィルタセグメントを備えるカラーフィルタに関するものである。
カラー液晶表示装置は、2枚の偏光板に挟まれた液晶層が、1枚目の偏光板を通過した光の偏光度合いを制御して、2枚目の偏光板を通過する光量をコントロールすることにより表示を行う表示装置であり、ツイストネマチック(TN)型液晶を用いるタイプが主流となっている。液晶表示装置は、2枚の偏光板の間にカラーフィルタを設けることによりカラー表示が可能となった。そのため液晶表示装置は、テレビやパソコンモニタ用途への展開が進んでいる。
その他の代表的な液晶表示装置の方式としては、一対の電極を片側の基板上に設けて基板に平行な方向に電解を印加するイン・プレーン・スイッチング(IPS)方式、負の誘電異方性をもつネマチック液晶を垂直配向させるヴァーティカリー・アライメント(VA)方式、また一軸性の位相差フィルムの光軸を互いに直交させ、光学補償を行なっているオプティカリー・コンベンセンド・ベンド(OCB)方式等があり、それぞれが実用化されている。
一般的にカラーフィルタは、ガラス等の透明な基板の表面に形成された、赤色フィルタ層(R)、緑色フィルタ層(G)および青色フィルタ層(B)からなる微細な帯(ストライプ)状のフィルタセグメント(画素)を平行又は交差して配置したもの、あるいは微細なフィルタセグメントを縦横一定の配列で配置したものからなっている。フィルタセグメントは、数ミクロン〜数100ミクロンと微細であり、しかも色相毎に所定の配列で整然と配置されている。
カラー液晶表示装置に用いられているカラーフィルタの上には、一般に液晶を駆動させるための透明電極が蒸着あるいはスパッタリングにより形成され、さらにその上に液晶を一定方向に配向させるための配向膜が形成されている。これらの透明電極及び配向膜の性能を充分に得るには、その形成工程を一般に200℃以上、好ましくは230℃以上の高温で行う必要がある。
カラーフィルタに要求される品質項目としては、コントラスト比と明度が挙げられる。コントラスト比が低いカラーフィルタを用いると、液晶が制御した偏光度合いを乱してしまい、光を遮断しなければならないとき(OFF状態)に光が漏れたり、光を透過しなければならないとき(ON状態)に透過光が減衰したりするため、ぼやけた画面となってしまう。そのため高品質な液晶表示装置を実現するためには、高コントラスト化が不可欠である。
また、明度が低いカラーフィルタを用いると、光の透過率が低いため、暗い画面となってしまい、明るい画面とするためには、光源であるバックライトの数を増量する必要がある。そのため消費電力の増大を抑制する観点から、カラーフィルタの高明度化がトレンドとなっている。
さらに、前述のようにカラー液晶装置がテレビやパソコンモニタ等に用いられるようになったことから、カラーフィルタに対して高コントラスト化、高明度化とともに、広い色再現領域や高い信頼性の要求も高くなっている。
またC−MOS(Complementary Metal Oxide Semiconductor:相補型金属酸化膜半導体)、CCD(Charge Coupled Device:電荷結合素子)などに代表されるカラー撮像管素子は、その受光素子上に赤色フィルタ層(R)、緑色フィルタ層(G)および青色フィルタ層(B)の加法混合の原色のフィルタセグメントを具備するカラーフィルタをそれぞれ配設して色分解するのが一般的である。また、原色のカラーフィルタに比べ高感度が得られるため、赤色、緑色、青色の補色に相当する、シアン、マゼンタ、イエロー(CMY)のフィルタセグメントを具備するカラーフィルタもよく用いられている。補色のカラーフィルタは、フラッシュなどの補助光源を利用しにくいビデオカメラ等で採用される場合が多い。
近年においては、カラー撮像管素子に用いられるカラーフィルタにおいても高透過率すなわち明度や、高い信頼性といった要求が高まっている。
近年においては、カラー撮像管素子に用いられるカラーフィルタにおいても高透過率すなわち明度や、高い信頼性といった要求が高まっている。
カラーフィルタの製造方法には、着色剤として染料、造塩染料を使った染色法、染料分散法や、着色剤として顔料を使った顔料分散法、印刷法、電着法などがある。このうち染色法、あるいは染色分散法は着色剤が染料であることから、耐熱性や耐光性にやや劣る欠点がある。よってカラーフィルタの着色剤としては耐熱性や耐光性に優れる顔料が用いられ、製造方法としては形成方法の精度や安定性から顔料分散法を用いる場合が多い。
顔料分散法は、樹脂中に着色剤である顔料粒子を分散させたものに感光剤や添加剤などを混合・調合することによってカラーレジスト化し、このカラーレジストを基板上にスピンコーターなどの塗布装置により塗膜形成し、アライナーやステッパー等によりマスクを介して選択的に露光を行い、アルカリ現像、熱硬化処理をすることによりパターニングし、この操作を繰り返すことによってカラーフィルタを作製する方法である。
一般に顔料粒子に微細化処理を行い、その微細化された顔料を極限まで一次粒子に近づけた顔料分散体を作成することによって、顔料による光の散乱が抑制され、高コントラスト化が達成できる。また分散体の透明度も向上するため、分散体の分光スペクトルが高透過率を持ち、高明度化が実現する。この分散体をカラーレジストに用いることにより、高コントラスト、高明度をもつカラーフィルタが得られる。
しかし、顔料を着色剤として用いたカラーフィルタは、顔料粒子による光の散乱等により、液晶によって制御された偏光度合いを乱してしまい、その結果、カラー液晶表示装置の輝度やコントラストの低下を招きやすいという問題がある。
上記の課題を解決するために、着色剤として顔料ではなく染料を樹脂等に溶解させる技術が提案されている(例えば特許文献1参照)。
またフタロシアニン系染料とキサンテン系染料とを含有するカラーフィルタ用インクも検討されている。特に直接染料、酸性染料を組み合わせたものであったが、発色性は良好であったものの耐熱性、耐光性に劣り、満足の行くものとはいえなかった。(例えば特許文献2参照)
また銅フタロシアニン系酸性染料等のアミン塩、銅フタロシアニン系酸性染料のスルホンアミド化合物をカラーフィルタ用着色剤に用いることも提案されている。しかしながらここで開示される造塩化合物は、溶剤溶解性が劣り、また十分な耐熱性、耐光性を有するものではなかった。(例えば特許文献3、4参照)
キサンテン系染料の分光は、銅フタロシアニン顔料や、シアニン顔料と比較した場合、400〜450nm付近において高い透過率を有するため、上記顔料や他の青色色素と併用して青色カラーフィルタを作成した場合、色バランスを崩さない、より高明度な青色カラーフィルタが得られることが提案されている。(例えば特許文献5、6参照)
また、有機溶剤可溶性酸性染料、光重合開始剤、重合性化合物、エポキシ基を有する共重合体及び有機溶剤を少なくとも含む染料含有ネガ型硬化性組成物が提案されている。しかし、有機溶剤可溶性酸性染料単独では、耐熱性、耐光性に劣り、アルカリ可溶性樹脂を用いない場合には、現像性の制御が困難であり、現像残渣の問題を解消することができない。(例えば特許文献7)
またフタロシアニン系染料とキサンテン系染料とを含有するカラーフィルタ用インクも検討されている。特に直接染料、酸性染料を組み合わせたものであったが、発色性は良好であったものの耐熱性、耐光性に劣り、満足の行くものとはいえなかった。(例えば特許文献2参照)
また銅フタロシアニン系酸性染料等のアミン塩、銅フタロシアニン系酸性染料のスルホンアミド化合物をカラーフィルタ用着色剤に用いることも提案されている。しかしながらここで開示される造塩化合物は、溶剤溶解性が劣り、また十分な耐熱性、耐光性を有するものではなかった。(例えば特許文献3、4参照)
キサンテン系染料の分光は、銅フタロシアニン顔料や、シアニン顔料と比較した場合、400〜450nm付近において高い透過率を有するため、上記顔料や他の青色色素と併用して青色カラーフィルタを作成した場合、色バランスを崩さない、より高明度な青色カラーフィルタが得られることが提案されている。(例えば特許文献5、6参照)
また、有機溶剤可溶性酸性染料、光重合開始剤、重合性化合物、エポキシ基を有する共重合体及び有機溶剤を少なくとも含む染料含有ネガ型硬化性組成物が提案されている。しかし、有機溶剤可溶性酸性染料単独では、耐熱性、耐光性に劣り、アルカリ可溶性樹脂を用いない場合には、現像性の制御が困難であり、現像残渣の問題を解消することができない。(例えば特許文献7)
本発明の目的は、耐熱性、耐光性、耐溶剤性に優れたカラーフィルタにすることができるカラーフィルタ用の着色樹脂組成物を提供することである。
本発明者らは、前記諸問題を解決するために鋭意研究を重ねた結果、カラーフィルタ用着色組成物の着色剤として、キサンテン系酸性染料と四級アンモニウム塩化合物(のカウンタ成分)とからなる造塩化合物(A)および顔料を含む着色剤を使用することによって、高い明度と広い色再現領域が可能となり、さらに熱架橋性成分として、三官能以上の多官能エポキシ樹脂を使用することにより、耐熱性、耐光性、耐溶剤性においても優れていること見出し、この知見に基づいて本発明をなしたものである。
すなわち、本発明は、着色剤と、光重合開始剤と、有機溶剤と、アルカリ可溶性樹脂と、光重合性化合物と、熱架橋性成分とからなるカラーフィルタ用着色樹脂組成物であって、着色剤が、有機顔料とキサンテン系酸性染料が四級アンモニウム塩化合物で造塩された化合物[A]とからなり、熱架橋性成分が三官能以上の多官能エポキシ樹脂であることを特徴とするカラーフィルタ用着色樹脂組成物に関する。
また、本発明は、キサンテン系酸性染料がC.I.アシッド レッドに分類されることを特徴とする上記カラーフィルタ用着色樹脂組成物に関する。
また、本発明は、キサンテン系酸性染料がC.I.アシッド レッド 52、および、C.I.アシッド レッド 289のいずれか1つであることを特徴とする上記カラーフィルタ用着色樹脂組成物に関する。
また、本発明は、四級アンモニウム塩化合物が、下記一般式(1)で表されることを特徴とする上記カラーフィルタ用着色樹脂組成物に関する。
一般式(1)
Y−は無機または有機のアニオンを表す。)
また、本発明は、少なくとも1つの赤色フィルタセグメント、少なくとも1つの緑色フィルタセグメントおよび少なくとも1つの青色フィルタセグメントを備えるカラーフィルタにおいて、少なくとも1つのフィルタセグメントが、上記カラーフィルタ用着色樹脂組成物により形成されてなるカラーフィルタに関する。
本発明においては、着色剤が、有機顔料と側鎖にカチオン性基を有する樹脂と、アニオン性染料とを反応させて得られた造塩化合物を含有し、さらに熱架橋性成分として、三官能以上の多官能エポキシ樹脂を使用することにより、耐熱性、耐光性、耐溶剤性においても優れたカラーフィルタを得ることができる。
以下、本発明を詳細に説明する。
なお、以下に挙げる「C.I.」は、カラーインデックス(C.I.)を意味する。
本発明のカラーフィルタ用着色組成物は、アルカリ可溶性樹脂と、光重合性化合物と、光重合開始剤と、有機溶剤と、着色剤として有機顔料、およびキサンテン系酸性染料と四級アンモニウム塩化合物(のカウンタ成分)とからなる造塩化合物(A)と、熱架橋性成分として三官能以上の多官能エポキシ樹脂と、を含むカラーフィルタ用着色組成物である。
<着色剤>
本発明のカラーフィルタ用着色組成物の着色剤としては、キサンテン系酸性染料と四級アンモニウム塩化合物とからなる造塩化合物(A)および有機顔料を含むものである。
本発明のカラーフィルタ用着色組成物の着色剤としては、キサンテン系酸性染料と四級アンモニウム塩化合物とからなる造塩化合物(A)および有機顔料を含むものである。
造塩化合物(A)と有機顔料とを併用、混合することで、前述のように多くのバックライトがもつ特徴的なピークをもつ425〜500nm付近において、分光スペクトルが高い透過率を有することが可能になり、高い明度と広い色再現性を得ることが出来る。さらに酸性染料を造塩化することで、高い耐熱性、耐光性、耐溶剤性を併せて持つことが出来る。
(キサンテン系酸性染料と四級アンモニウム塩化合物とからなる造塩化合物(A))
造塩化合物(A)について説明する。キサンテン系酸性染料と四級アンモニウム塩化合物とからなる造塩化合物(A)に用いる、キサンテン系酸性染料は、赤色、紫色を呈するものであり、染料の形態を有するものである。
造塩化合物(A)について説明する。キサンテン系酸性染料と四級アンモニウム塩化合物とからなる造塩化合物(A)に用いる、キサンテン系酸性染料は、赤色、紫色を呈するものであり、染料の形態を有するものである。
赤色、紫色を呈するとは、C.I.アシッド レッド、C.I.アシッド バイオレット等の酸性染料、C.I.ダイレクト レッド、C.I.ダイレクト バイオレット等の直接染料に属するものである。ここで直接染料は、スルホン酸基を有することから本発明においては酸性染料と同義とみなす。
さらに造塩化合物(A)は、これらのキサンテン系酸性染料(直接染料も含む)とカウンタイオンとして働くカウンタ成分である四級アンモニウム塩化合物とで造塩、変性した造塩染料に属するものである。
さらに造塩化合物(A)は、これらのキサンテン系酸性染料(直接染料も含む)とカウンタイオンとして働くカウンタ成分である四級アンモニウム塩化合物とで造塩、変性した造塩染料に属するものである。
[キサンテン系酸性染料]
キサンテン系染料の酸性染料について説明する。キサンテン系染料の酸性染料としては、C.I.アシッド レッド 51(エリスロシン(食用赤色3号))、C.I.アシッド レッド 52(アシッドローダミン)、C.I.アシッド レッド 87(エオシンG(食用赤色103号))、C.I.アシッド レッド 92(アシッドフロキシンPB(食用赤色104号))、C.I.アシッド レッド 289、C.I.アシッド レッド 388、ローズベンガルB(食用赤色5号)、アシッドローダミンG、C.I.アシッド バイオレット 9、C.I.アシッド バイオレット 9、C.I.アシッド バイオレット 30などC.I.アシッド レッドに分類されるものであるを用いることが好ましい。
キサンテン系染料の酸性染料について説明する。キサンテン系染料の酸性染料としては、C.I.アシッド レッド 51(エリスロシン(食用赤色3号))、C.I.アシッド レッド 52(アシッドローダミン)、C.I.アシッド レッド 87(エオシンG(食用赤色103号))、C.I.アシッド レッド 92(アシッドフロキシンPB(食用赤色104号))、C.I.アシッド レッド 289、C.I.アシッド レッド 388、ローズベンガルB(食用赤色5号)、アシッドローダミンG、C.I.アシッド バイオレット 9、C.I.アシッド バイオレット 9、C.I.アシッド バイオレット 30などC.I.アシッド レッドに分類されるものであるを用いることが好ましい。
中でもC.I.アシッド レッド 52、C.I.アシッド レッド 87、C.I.アシッド レッド 92、C.I.アシッド レッド 289、C.I.アシッド レッド 388を用いることが好ましい。
本発明に用いるキサンテン系酸性染料は、透過スペクトルにおいて650nmの領域で透過率が90%以上であり、600nmの領域で透過率が75%以上、550nmの透過率が5%以下、400nmの領域で透過率が70%以上であるものが好ましい。より好ましくは、650nmの領域で透過率が95%以上であり、600nmの領域で透過率が80%以上、550nmの透過率が10%以下、400nmの領域で透過率が75%以上である。
またキサンテン系酸性染料としては、発色性の優れる点でローダミン系酸性染料を用いることが好ましい。
[四級アンモニウム塩化合物]
次いで、キサンテン系酸性染料のカウンタ成分としての四級アンモニウム塩化合物について説明する。四級アンモニウム塩化合物は、アンモニウム基を有することで酸性染料のカウンタになるものである。
次いで、キサンテン系酸性染料のカウンタ成分としての四級アンモニウム塩化合物について説明する。四級アンモニウム塩化合物は、アンモニウム基を有することで酸性染料のカウンタになるものである。
造塩化合物(A)のカウンタ成分である四級アンモニウム塩化合物の好ましい形態は、無色、または白色を呈するものである。
ここで無色、または白色とはいわゆる透明な状態を意味し、可視光領域の400〜700nmの全波長領域において、透過率が95%以上、好ましくは98%以上となっている状態と定義されるものである。すなわち染料成分の発色を阻害しない、色変化を起こさないものである必要がある。
四級アンモニウム塩化合物のカチオン成分であるカウンタ部分の分子量は190〜900の範囲であることが好ましい。ここでカチオン部分とは、下記一般式(1)中の(NR1R2R3R4)+の部分に相当する。分子量が190よりも小さいと耐光性、耐熱性が低下してしまうことがあり、さらに溶剤への溶解性が低下してしまうことがある。また分子量が900よりも大きくなると分子中の発色成分の割合が低下してしまうことがあり、発色性が低下し、明度も低下してしまうことがある。より好ましくはカウンタ部分の分子量が240〜850の範囲である。特に好ましいのは、カウンタ部分の分子量が350〜800の範囲である。
ここで分子量は構造式を基に計算を行ったものであり、Cの原子量を12、Hの原子量を1、Nの原子量を14とした。
また、四級アンモニウム塩化合物として以下一般式(1)で表されるものが用いられる。
一般式(1)
(一般式(1)中、R1〜R4は、それぞれ独立に、炭素数1〜20のアルキル基、または、ベンジル基を示し、R1、R2、R3、および、R4の少なくとも2つ以上がCの数が5〜20個である。Y-は無機または有機のアニオンを表す。)
R1〜R4の少なくとも2つ以上のCの数を5〜20個とすることで、溶剤に対する溶解性が良好なものとなることがある。Cの数が5より小さいアルキル基が3つ以上になると溶剤に対する溶解性が悪くなり、塗膜異物が発生しやすくなってしまうことがある。またCの数が20を超えてしまうアルキル基が存在すると造塩化合物(A)の発色性が損なわれてしまうことがある。
具体的には、テトラメチルアンモニウムクロライド(カチオン部分の分子量が74)、テトラエチルアンモニウムクロライド(カチオン部分の分子量が122)、モノステアリルトリメチルアンモニウムクロライド(カチオン部分の分子量が312)、ジステアリルジメチルアンモニウムクロライド(カチオン部分の分子量が550)、トリステアリルモノメチルアンモニウムクロライド(カチオン部分の分子量が788)、セチルトリメチルアンモニウムクロライド(カチオン部分の分子量が284)、トリオクチルメチルアンモニウムクロライド(カチオン部分の分子量が368)、ジオクチルジメチルアンモニウムクロライド(カチオン部分の分子量が270)、モノラウリルトリメチルアンモニウムクロライド(カチオン部分の分子量が228)、ジラウリルジメチルアンモニウムクロライド(カチオン部分の分子量が382)、トリラウリルメチルアンモニウムクロライド(カチオン部分の分子量が536)、トリアミルベンジルアンモニウムクロライド(カチオン部分の分子量が318)、トリヘキシルベンジルアンモニウムクロライド(カチオン部分の分子量が360)、トリオクチルベンジルアンモニウムクロライド(カチオン部分の分子量が444)、トリラウリルベンジルアンモニウムクロライド(カチオン部分の分子量が612)、ベンジルジメチルステアリルアンモニウムクロライド(カチオン部分の分子量が388)、及びベンジルジメチルオクチルアンモニウムクロライド(カチオン部分の分子量が248)、ジアルキル(アルキルがC14〜C18)ジメチルアンモニウムクロライド(硬化牛脂)(カチオン部分の分子量が438〜550)等を用いることが好ましい。
アニオンを構成するY-の成分は、無機または有機のアニオンであればよいが、ハロゲンであることが好ましく、通常は塩素である。
具体的な四級アンモニウム塩化合物の製品としては、花王社製のコータミン24P、コータミン86Pコンク、コータミン60W、コータミン86W、コータミンD86P、サニゾールC、サニゾールB−50等、ライオン社製のアーカード210−80E、2C−75、2HT−75、2HTフレーク、2O−75I、2HP−75、2HPフレーク等があげられ、中でもコータミンD86P(ジステアリルジメチルアンモニウムクロライド)、アーカード2HT−75(ジアルキル(アルキルがC14〜C18)ジメチルアンモニウムクロライド)が好ましいものである。
[造塩化処理]
キサンテン系酸性染料と四級アンモニウム塩化合物との造塩化合物は、従来知られている方法により合成することができる。特開平11−72969号公報などに具体的な手法が開示されている。
キサンテン系酸性染料と四級アンモニウム塩化合物との造塩化合物は、従来知られている方法により合成することができる。特開平11−72969号公報などに具体的な手法が開示されている。
一例をあげると、キサンテン系酸性染料を水に溶解した後、四級アンモニウム塩化合物を添加、攪拌しながら造塩化処理を行なえばよい。ここでキサンテン系酸性染料中のスルホン酸基(−SO3H)の部分と四級アンモニウム塩化合物のアンモニウム基(NH4 +)の部分が結合した造塩化合物が得られる。また水の代わりに、メタノール、エタノールも造塩化時に使用可能な溶媒である。
顔料と造塩化合物(A)との使用割合は、顔料100重量部に対し造塩化合物(A)1〜80重量部が好ましい。より好ましくは5〜60重量部である。造塩化合物(A)の添加量が1重量部よりも少ないと再現可能な色度領域が狭くなり、また80重量部を越えると色相が変化してしまうため好ましくないことがある。
<有機顔料>
本発明のカラーフィルタ用着色組成物は、有機顔料を添加し、カラーフィルタ用着色組成物として使用する。
本発明のカラーフィルタ用着色組成物は、有機顔料を添加し、カラーフィルタ用着色組成物として使用する。
有機顔料としては、有機顔料のみまたは、有機顔料と無機の顔料を、単独または2種類以上混合して用いることができる。顔料は、発色性が高く、且つ耐熱性の高い顔料、特に耐熱分解性の高い顔料が好ましく用いられる。以下に、カラーフィルタ用着色組成物に使用可能な有機顔料の具体例を、カラーインデックス番号で示す。
赤色フィルタセグメントを形成するための赤色着色組成物には、例えばC.I.ピグメント レッド 7、9、14、41、48:1、48:2、48:3、48:4、57:1、81、81:1、81:2、81:3、81:4、122、123、146、150、168、169、176、177、178、180、184、185、187、192、200、202、208、210、215、216、217、220、223、224、226、227、228、240、242、246、254、255、264、268、270、272、273、274,276、277、278、279、280、281、282、283、284、285、286、または287等の赤色顔料を用いることができる。また赤色着色組成物には、C.I.ピグメント オレンジ 38、43、71、または73等の橙色顔料及び/またはC.I.ピグメント イエロー 1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、138、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、193、194、198、199、213、214、218、219、220、または221等の黄色顔料を併用することができる。
緑色フィルタセグメントを形成するための緑色着色組成物には、例えばC.I.ピグメント グリーン7、10、36、37、58等の緑色顔料を用いることができる。また緑色着色組成物には、C.I.ピグメント イエロー1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、138、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、193、194、198、199、213、214、218、219、220、または221等の黄色顔料を併用することができる。
青色フィルタセグメントを形成するための青色着色組成物には、例えばC.I.ピグメント ブルー 1、1:2、1:3、2、2:1、2:2、3、8、9、10、10:1、11、12、15、15:1、15:2、15:3、15:4、15:6、16、18、19、22、24、24:1、53、56、56:1、57、58、59、60、61、62、64等の青色顔料を用いることができる。また青色着色組成物には、C.I.ピグメント バイオレット 1、19、23、27、29、30、32、37、40、42、50等の紫色顔料を併用することができる。
シアン色フィルタセグメントを形成するためのシアン色着色組成物には、例えばC.I.ピグメント ブルー 15:1、15:2、15:4、15:3、15:6、16、81等の青色顔料を単独でまたは混合して用いることができる。
マゼンタ色フィルタセグメントを形成するためのマゼンタ色着色組成物には、例えばC.I.ピグメント バイオレット 1、19、C.I.ピグメント レッド 144、146、177、169、81等の紫色顔料および赤色顔料を単独でまたは混合して用いることができる。マゼンタ色組成物には、黄色顔料を併用することができる。
[顔料の微細化]
本発明の着色組成物に使用する顔料、さらにオプションとして用いる顔料は、ソルトミリング処理を行い微細化することができる。顔料の一次粒子径は、着色剤担体中への分散が良好なことから、20nm以上であることが好ましい。また、コントラスト比が高いフィルタセグメントを形成できることから、100nm以下であることが好ましい。特に好ましい範囲は、25〜85nmの範囲である。なお、顔料の一次粒子径は、顔料のTEM(透過型電子顕微鏡)による電子顕微鏡写真から一次粒子の大きさを直接計測する方法で行った。具体的には、個々の顔料の一次粒子の短軸径と長軸径を計測し、平均をその顔料粒子の粒径とした。次に、100個以上の顔料粒子について、それぞれの粒子の体積を求めた粒径の立方体と近似して求め、体積平均粒径を平均一次粒子径としている。
本発明の着色組成物に使用する顔料、さらにオプションとして用いる顔料は、ソルトミリング処理を行い微細化することができる。顔料の一次粒子径は、着色剤担体中への分散が良好なことから、20nm以上であることが好ましい。また、コントラスト比が高いフィルタセグメントを形成できることから、100nm以下であることが好ましい。特に好ましい範囲は、25〜85nmの範囲である。なお、顔料の一次粒子径は、顔料のTEM(透過型電子顕微鏡)による電子顕微鏡写真から一次粒子の大きさを直接計測する方法で行った。具体的には、個々の顔料の一次粒子の短軸径と長軸径を計測し、平均をその顔料粒子の粒径とした。次に、100個以上の顔料粒子について、それぞれの粒子の体積を求めた粒径の立方体と近似して求め、体積平均粒径を平均一次粒子径としている。
ソルトミリング処理とは、顔料と水溶性無機塩と水溶性有機溶剤との混合物を、ニーダー、2本ロールミル、3本ロールミル、ボールミル、アトライター、サンドミル等の混練機を用いて、加熱しながら機械的に混練した後、水洗により水溶性無機塩と水溶性有機溶剤を除去する処理である。水溶性無機塩は、破砕助剤として働くものであり、ソルトミリング時に無機塩の硬度の高さを利用して顔料が破砕される。顔料をソルトミリング処理する際の条件を最適化することにより、一次粒子径が非常に微細であり、また、分布の幅がせまく、シャープな粒度分布をもつ顔料を得ることができる。
水溶性無機塩としては、塩化ナトリウム、塩化バリウム、塩化カリウム、硫酸ナトリウム等を用いることができるが、価格の点から塩化ナトリウム(食塩)を用いるのが好ましい。水溶性無機塩は、処理効率と生産効率の両面から、顔料の全重量を基準(100重量%)として、50〜2000重量%用いることが好ましく、300〜1000重量%用いることが最も好ましい。
水溶性有機溶剤は、顔料及び水溶性無機塩を湿潤する働きをするものであり、水に溶解(混和)し、かつ用いる無機塩を実質的に溶解しないものであれば特に限定されない。ただし、ソルトミリング時に温度が上昇し、溶剤が蒸発し易い状態になるため、安全性の点から、沸点120℃以上の高沸点溶剤が好ましい。例えば、2−メトキシエタノール、2−ブトキシエタノール、2−(イソペンチルオキシ)エタノール、2−(ヘキシルオキシ)エタノール、ジエチレングリコール、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコール、トリエチレングリコールモノメチルエーテル、液状のポリエチレングリコール、1−メトキシ−2−プロパノール、1−エトキシ−2−プロパノール、ジプロピレングリコール、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、液状のポリプロピレングリコール等が用いられる。水溶性有機溶剤は、顔料の全重量を基準(100重量%)として、5〜1000重量%用いることが好ましく、50〜500重量%用いることが最も好ましい。
顔料をソルトミリング処理する際には、必要に応じて樹脂を添加してもよい。用いられる樹脂の種類は特に限定されず、天然樹脂、変性天然樹脂、合成樹脂、天然樹脂で変性された合成樹脂等を用いることができる。用いられる樹脂は、室温で固体であり、水不溶性であることが好ましく、かつ上記有機溶剤に一部可溶であることがさらに好ましい。樹脂の使用量は、顔料の全重量を基準(100重量%)として、5〜200重量%の範囲であることが好ましい。
(その他の着色剤)
また本発明の着色組成物には、効果に支障を来たさない範囲でその他の有機顔料を添加することができる。
また本発明の着色組成物には、効果に支障を来たさない範囲でその他の有機顔料を添加することができる。
有機顔料の場合は、ジオキサジン系顔料、アントラキノン系顔料、アゾ系顔料、キナクリドン系顔料を併用することが好ましい。中でもジオキサジン系顔料を併用することが好ましい。ジオキサジン系顔料としては、C.I.ピグメント バイオレット 23を用いることが好ましい。本発明の着色組成物にジオキサジン系顔料を併用することで、さらに耐熱性、耐光性、耐溶剤性に優れ、安定した高品質な着色組成物とすることができる。
またこれらを併用して、用いることができる有機顔料も前記述べたように、ソルトミリング等の方法により微細化し用いることが好ましい。
<熱架橋性成分>
本発明における三官能以上の多官能エポキシ化合物とは、1分子中に3個以上のエポキシ環を有する化合物である。エポキシ環は、バインダー樹脂のカルボキシル基と熱架橋することができる。
<熱架橋性成分>
本発明における三官能以上の多官能エポキシ化合物とは、1分子中に3個以上のエポキシ環を有する化合物である。エポキシ環は、バインダー樹脂のカルボキシル基と熱架橋することができる。
本発明に使用できる三官能以上の多官能エポキシ化合物としては、ノボラック型エポキシ樹脂、脂環式エポキシ化合物などが挙げられる。
ノボラック型エポキシ樹脂とは、下記一般式(2)で表される化合物で、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂に分類される。
ノボラック型エポキシ樹脂としては、具体的には、EOCN−1020、EOCN−102S、EOCN−103S、EOCN−104S、EOCN−4500、EOCN−4600、XD−1000、XD−1000−L、XD−1000−2L、NC−3000、NC−3000−H(以上、日本化薬社製)、YDPN−638、YDCN−700−2、YDCN−700−3、YDCN−700−5、YDCN−700−7、YDCN−700−10、YDCN−704、YDCN−704A(以上、新日鐵化学社製)、N−660、N−665、N−670、N−673、N−680、N−690、N−695、N−665−EXP、N−672−EXP、N−655−EXP−S、N−662−EXP−S(以上、DIC社製)などが挙げられる。
脂環式エポキシ樹脂とは、例えば、下記一般式(3)で表される化合物である。脂環式エポキシ樹脂としては、EHPE3150(ダイセル化学工業社製)などが挙げられる。
これ以外の三官能以上の多官能エポキシ樹脂としては、三官能のエポキシ樹脂であるテクモアVG3101(プリンテック社製)、四官能のエポキシ樹脂であるTETRAD−C、TETRAD−X(以上、三菱ガス化学社製)などが挙げられる。
三官能以上の多官能エポキシ樹脂の添加量としては、アルカリ可溶性樹脂のカルボン酸量D1に対して、エポキシ量F1との比率(D1/F1)が0.5以上1.5以下であることが好ましい。D1/F1が0.5より小さいと、ベーク後の黄変により、カラーフイルタの品質が損われたり、着色組成物の経時安定性が保てない場合がある。D1/F1が1.5より大きいと、耐溶剤性の改善効果が制限されることがある。
<アルカリ可溶性樹脂>
アルカリ可溶性樹脂は、着色剤、特に造塩化合物を分散するもの、もしくは造塩化合物を染色、浸透させるものである。アルカリ可溶性樹脂としては、可視光領域の400〜700nmの全波長領域において分光透過率が好ましくは80%以上、より好ましくは95%以上の樹脂であることが好ましい。アルカリ可溶性樹脂とは、酸性基含有エチレン性不飽和単量体を共重合した樹脂である。また、さらに光感度を向上させるために、エチレン性不飽和二重結合を有する活性エネルギー線硬化性樹脂を用いることもできる。
アルカリ可溶性樹脂は、着色剤、特に造塩化合物を分散するもの、もしくは造塩化合物を染色、浸透させるものである。アルカリ可溶性樹脂としては、可視光領域の400〜700nmの全波長領域において分光透過率が好ましくは80%以上、より好ましくは95%以上の樹脂であることが好ましい。アルカリ可溶性樹脂とは、酸性基含有エチレン性不飽和単量体を共重合した樹脂である。また、さらに光感度を向上させるために、エチレン性不飽和二重結合を有する活性エネルギー線硬化性樹脂を用いることもできる。
特に側鎖にエチレン性不飽和二重結合を有する活性エネルギー線硬化性樹脂をカラーフィルタ用アルカリ現像型レジストに用いることで、造塩化合物(A)を塗布した後の塗膜異物が発生せず、レジスト材中の造塩化合物(A)の安定性が改善され好ましい。側鎖にエチレン性不飽和二重結合を有さない直鎖状の樹脂を用いた場合は、樹脂と染料の混在する液中で染料が樹脂にトラップされにくく自由度を持っていることで染料成分が凝集・析出しやすいが、側鎖にエチレン性不飽和二重結合を有する活性エネルギー線硬化性樹脂を用いることで、樹脂と染料の混在する液中で染料が樹脂にトラップされ易いため、染料成分が凝集・析出しにくく、また、さらに活性エネルギー線で露光し膜を形成する際に樹脂が3次元架橋されることで染料分子が固定され、その後の現像工程で溶剤が除去されても染料成分が凝集・析出しにくくなると推定される。
アルカリ可溶性樹脂の重量平均分子量(Mw)は、着色剤(B)を好ましく分散させるためには、10,000〜100,000の範囲が好ましく、より好ましくは10,000〜80,000の範囲である。また数平均分子量(Mn)は5,000〜50,000の範囲が好ましく、Mw/Mnの値は10以下であることが好ましい。
アルカリ可溶性樹脂をカラーフィルタ用感光性着色組成物として使用する場合には、顔料及び造塩化合物の分散性、浸透性、現像性、及び耐熱性の観点から、着色剤吸着基及び現像時のアルカリ可溶基として働くカルボキシル基、着色剤担体及び溶剤に対する親和性基として働く脂肪族基及び芳香族基のバランスが、顔料及び造塩化合物の分散性、浸透性、現像性、さらには耐久性にとって重要であり、酸価20〜300mgKOH/gの樹脂を用いることが好ましい。酸価が、20mgKOH/g未満では、現像液に対する溶解性が悪く、微細パターン形成するのが困難であることがある。300mgKOH/gを超えると、微細パターンが残らなくなることがある。
アルカリ可溶性樹脂は、成膜性および諸耐性が良好なことから、着色剤の全重量を基準(100重量%)として、30重量%以上の量で用いることが好ましく、着色剤濃度が高く、良好な色特性を発現できることから、500重量%以下の量で用いることが好ましい。
酸性基含有エチレン性不飽和モノマーを共重合したアルカリ可溶性樹脂としては、例えば、カルボキシル基、スルホン基等の酸性基を有する樹脂が挙げられる。アルカリ可溶性樹脂として具体的には、酸性基を有するアクリル樹脂、α−オレフィン/(無水)マレイン酸共重合体、スチレン/スチレンスルホン酸共重合体、エチレン/(メタ)アクリル酸共重合体、又はイソブチレン/(無水)マレイン酸共重合体等が挙げられる。中でも、酸性基を有するアクリル樹脂、およびスチレン/スチレンスルホン酸共重合体から選ばれる少なくとも1種の樹脂、特に酸性基を有するアクリル樹脂は、耐熱性、透明性が高いため、好適に用いられる。
エチレン性不飽和二重結合を有する活性エネルギー線硬化性樹脂としては、たとえば以下に示す(a)や(b)の方法により不飽和エチレン性二重結合を導入した樹脂が挙げられる。
[方法(a)]
方法(a)としては、例えば、エポキシ基を有する不飽和エチレン性単量体と、他の1種類以上の単量体とを共重合することによって得られた共重合体の側鎖エポキシ基に、不飽和エチレン性二重結合を有する不飽和一塩基酸のカルボキシル基を付加反応させ、更に、生成した水酸基に、多塩基酸無水物を反応させ、不飽和エチレン性二重結合およびカルボキシル基を導入する方法がある。
方法(a)としては、例えば、エポキシ基を有する不飽和エチレン性単量体と、他の1種類以上の単量体とを共重合することによって得られた共重合体の側鎖エポキシ基に、不飽和エチレン性二重結合を有する不飽和一塩基酸のカルボキシル基を付加反応させ、更に、生成した水酸基に、多塩基酸無水物を反応させ、不飽和エチレン性二重結合およびカルボキシル基を導入する方法がある。
エポキシ基を有する不飽和エチレン性単量体としては、例えば、グリシジル(メタ)アクリレート、メチルグリシジル(メタ)アクリレート、2−グリシドキシエチル(メタ)アクリレート、3,4エポキシブチル(メタ)アクリレート、及び3,4エポキシシクロヘキシル(メタ)アクリレートが挙げられ、これらは、単独で用いても、2種類以上を併用してもかまわない。次工程の不飽和一塩基酸との反応性の観点で、グリシジル(メタ)アクリレートが好ましい。
不飽和一塩基酸としては、(メタ)アクリル酸、クロトン酸、o−、m−、p−ビニル安息香酸、(メタ)アクリル酸のα位ハロアルキル、アルコキシル、ハロゲン、ニトロ、シアノ置換体等のモノカルボン酸等が挙げられ、これらは、単独で用いても、2種類以上を併用してもかまわない。
多塩基酸無水物としては、テトラヒドロ無水フタル酸、無水フタル酸、ヘキサヒドロ無水フタル酸、無水コハク酸、無水マレイン酸等が挙げられ、これらは単独で用いても、2種類以上を併用してもかまわない。カルボキシル基の数を増やす等、必要に応じて、トリメリット酸無水物等のトリカルボン酸無水物を用いたり、ピロメリット酸二無水物等のテトラカルボン酸二無水物を用いて、残った無水物基を加水分解すること等もできる。また、多塩基酸無水物として、不飽和エチレン性二重結合を有する、エトラヒドロ無水フタル酸、又は無水マレイン酸を用いると、更に不飽和エチレン性二重結合を増やすことができる。
方法(a)の類似の方法として、例えば、カルボキシル基を有する不飽和エチレン性単量体と、他の1種類以上の単量体とを共重合することによって得られた共重合体の側鎖カルボキシル基の一部に、エポキシ基を有する不飽和エチレン性単量体を付加反応させ、不飽和エチレン性二重結合およびカルボキシル基を導入する方法がある。
[方法(b)]
方法(b)としては、水酸基を有する不飽和エチレン性単量体を使用し、他のカルボキシル基を有する不飽和一塩基酸の単量体や、他の単量体とを共重合することによって得られた共重合体の側鎖水酸基に、イソシアネート基を有する不飽和エチレン性単量体のイソシアネート基を反応させる方法がある。
方法(b)としては、水酸基を有する不飽和エチレン性単量体を使用し、他のカルボキシル基を有する不飽和一塩基酸の単量体や、他の単量体とを共重合することによって得られた共重合体の側鎖水酸基に、イソシアネート基を有する不飽和エチレン性単量体のイソシアネート基を反応させる方法がある。
水酸基を有する不飽和エチレン性単量体としては、2−ヒドロキシエチル(メタ)アクリレート、2−若しくは3−ヒドロキシプロピル(メタ)アクリレート、2−若しくは3−若しくは4−ヒドロキシブチル(メタ)アクリレート、グリセロール(メタ)アクリレート、又はシクロヘキサンジメタノールモノ(メタ)アクリレート等のヒドロキシアルキル(メタ)アクリレート類が挙げられ、これらは、単独で用いても、2種類以上を併用してもかまわない。また、上記ヒドロキシアルキル(メタ)アクリレートに、エチレンオキシド、プロピレンオキシド、及び/又はブチレンオキシド等を付加重合させたポリエーテルモノ(メタ)アクリレートや、(ポリ)γ−バレロラクトン、(ポリ)ε−カプロラクトン、及び/又は(ポリ)12−ヒドロキシステアリン酸等を付加した(ポリ)エステルモノ(メタ)アクリレートも使用できる。塗膜異物抑制の観点から、2−ヒドロキシエチル(メタ)アクリレート、又はグリセロール(メタ)アクリレートが好ましい。
イソシアネート基を有する不飽和エチレン性単量体としては、2−(メタ)アクリロイルオキシエチルイソシアネート、又は1,1−ビス〔(メタ)アクリロイルオキシ〕エチルイソシアネート等が挙げられるが、これらに限定することなく、2種類以上併用することもできる。
<有機溶剤>
本発明の着色組成物には、着色剤を充分に着色剤担体中に分散、浸透させ、ガラス基板等の基板上に乾燥膜厚が0.2〜5μmとなるように塗布してフィルタセグメントを形成することを容易にするために有機溶剤を含有させることができる。
本発明の着色組成物には、着色剤を充分に着色剤担体中に分散、浸透させ、ガラス基板等の基板上に乾燥膜厚が0.2〜5μmとなるように塗布してフィルタセグメントを形成することを容易にするために有機溶剤を含有させることができる。
有機溶剤としては、例えば乳酸エチル、ベンジルアルコール、1,2,3−トリクロロプロパン、1,3−ブタンジオール、1,3−ブチレングリコール、1,3−ブチレングリコールジアセテート、1,4−ジオキサン、2−ヘプタノン、2−メチル−1,3−プロパンジオール、3,5,5−トリメチル−2−シクロヘキセン−1−オン、3,3,5−トリメチルシクロヘキサノン、3−エトキシプロピオン酸エチル、3−メチル−1,3−ブタンジオール、3−メトキシ−3−メチル−1−ブタノール、3−メトキシ−3−メチルブチルアセテート、3-メトキシブタノール、3−メトキシブチルアセテート、4−ヘプタノン、m−キシレン、m−ジエチルベンゼン、m−ジクロロベンゼン、N,N−ジメチルアセトアミド、N,N−ジメチルホルムアミド、n−ブチルアルコール、n−ブチルベンゼン、n−プロピルアセテート、o−キシレン、o−クロロトルエン、o−ジエチルベンゼン、o−ジクロロベンゼン、p−クロロトルエン、p−ジエチルベンゼン、sec−ブチルベンゼン、tert−ブチルベンゼン、γ―ブチロラクトン、イソブチルアルコール、イソホロン、エチレングリコールジエチルエーテル、エチレングリコールジブチルエーテル、エチレングリコールモノイソプロピルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノエチルエーテルアセテート、エチレングリコールモノターシャリーブチルエーテル、エチレングリコールモノブチルエーテル、エチレングリコールモノブチルエーテルアセテート、エチレングリコールモノプロピルエーテル、エチレングリコールモノヘキシルエーテル、エチレングリコールモノメチルエーテル、エチレングリコールモノメチルエーテルアセテート、ジイソブチルケトン、ジエチレングリコールジエチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールモノイソプロピルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノメチルエーテル、シクロヘキサノール、シクロヘキサノールアセテート、シクロヘキサノン、ジプロピレングリコールジメチルエーテル、ジプロピレングリコールメチルエーテルアセテート、ジプロピレングリコールモノエチルエーテル、ジプロピレングリコールモノブチルエーテル、ジプロピレングリコールモノプロピルエーテル、ジプロピレングリコールモノメチルエーテル、ダイアセトンアルコール、トリアセチン、トリプロピレングリコールモノブチルエーテル、トリプロピレングリコールモノメチルエーテル、プロピレングリコールジアセテート、プロピレングリコールフェニルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノブチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルプロピオネート、ベンジルアルコール、メチルイソブチルケトン、メチルシクロヘキサノール、酢酸n−アミル、酢酸n−ブチル、酢酸イソアミル、酢酸イソブチル、酢酸プロピル、二塩基酸エステル等が挙げられる。
中でも、本発明の顔料、造塩化合物(A)の分散、溶解が良好なことから、乳酸エチル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート等のグリコールアセテート類、ベンジルアルコール等の芳香族アルコール類やシクロヘキサノン等のケトン類を用いることが好ましい。
有機溶剤は、1種を単独で、若しくは2種以上を混合して用いることができる。また有機溶剤は、着色組成物を適正な粘度に調節し、目的とする均一な膜厚のフィルタセグメントを形成できることから、着色剤の全重量を基準(100重量%)にして、800〜4000重量%の量で用いることが好ましい。
<分散>
本発明の着色組成物は、有機顔料およびキサンテン系酸性染料と四級アンモニウム塩化合物(のカウンタ成分)とからなる造塩化合物(A)とを含む着色剤を、前記アルカリ可溶性樹脂と、必要に応じて溶剤とからなる着色剤担体中に、好ましくは色素誘導体などの分散助剤と一緒に、三本ロールミル、二本ロールミル、サンドミル、ニーダー、又はアトライター等の各種分散手段を用いて微細に分散して製造することができる。また、本発明の着色組成物は、有機顔料、造塩化合物(A)、その他の着色剤等を別々に着色剤担体に分散したものを混合して製造することもできる。
本発明の着色組成物は、有機顔料およびキサンテン系酸性染料と四級アンモニウム塩化合物(のカウンタ成分)とからなる造塩化合物(A)とを含む着色剤を、前記アルカリ可溶性樹脂と、必要に応じて溶剤とからなる着色剤担体中に、好ましくは色素誘導体などの分散助剤と一緒に、三本ロールミル、二本ロールミル、サンドミル、ニーダー、又はアトライター等の各種分散手段を用いて微細に分散して製造することができる。また、本発明の着色組成物は、有機顔料、造塩化合物(A)、その他の着色剤等を別々に着色剤担体に分散したものを混合して製造することもできる。
(分散助剤)
着色剤を着色剤担体中に分散する際には、適宜、色素誘導体、樹脂型分散剤、界面活性剤等の分散助剤を用いることができる。分散助剤は、着色剤の分散に優れ、分散後の着色剤の再凝集を防止する効果が大きいので、分散助剤を用いて着色剤を顔料担体中に分散してなる着色組成物を用いた場合には、分光透過率の高いカラーフィルタが得られる。
着色剤を着色剤担体中に分散する際には、適宜、色素誘導体、樹脂型分散剤、界面活性剤等の分散助剤を用いることができる。分散助剤は、着色剤の分散に優れ、分散後の着色剤の再凝集を防止する効果が大きいので、分散助剤を用いて着色剤を顔料担体中に分散してなる着色組成物を用いた場合には、分光透過率の高いカラーフィルタが得られる。
本発明において、造塩化合物(A)は、有機顔料の分散助剤としての役割を果たすこともでき好ましい組み合わせである。
色素誘導体としては、有機顔料、アントラキノン、アクリドンまたはトリアジンに、塩基性置換基、酸性置換基、または置換基を有していても良いフタルイミドメチル基を導入した化合物があげられる。
本発明においては、中でも顔料誘導体が好ましく、その構造は、下記一般式(4)で示される化合物である。
本発明においては、中でも顔料誘導体が好ましく、その構造は、下記一般式(4)で示される化合物である。
P−Ln 式(4)
(ただし、
P:n価の、有機顔料残基、アントラキノン残基、アクリドン残基またはトリアジン残基
L:塩基性置換基、酸性置換基、または置換基を有していても良いフタルイミドメチル基
n:1〜4の整数である)
(ただし、
P:n価の、有機顔料残基、アントラキノン残基、アクリドン残基またはトリアジン残基
L:塩基性置換基、酸性置換基、または置換基を有していても良いフタルイミドメチル基
n:1〜4の整数である)
Pの有機顔料残基を構成する有機顔料としては、例えば、ジケトピロロピロール系顔料;アゾ、ジスアゾ、ポリアゾ等のアゾ系顔料;銅フタロシアニン、ハロゲン化銅フタロシアニン、無金属フタロシアニン等のフタロシアニン系顔料;アミノアントラキノン、ジアミノジアントラキノン、アントラピリミジン、フラバントロン、アントアントロン、インダントロン、ピラントロン、ビオラントロン等のアントラキノン系顔料;キナクリドン系顔料;ジオキサジン系顔料;ペリノン系顔料;ペリレン系顔料;チオインジゴ系顔料;イソインドリン系顔料;イソインドリノン系顔料;キノフタロン系顔料;スレン系顔料;金属錯体系顔料等が挙げられる。
色素誘導体としては、例えば、特開昭63−305173号公報、特公昭57−15620号公報、特公昭59−40172号公報、特公昭63−17102号公報、特公平5−9469号公報等に記載されているものを使用でき、これらは単独で又は2種類以上を混合して用いることができる。
色素誘導体の配合量は、分散性向上の点から、着色剤全量を基準(100重量%)として、好ましくは0.5重量%以上、さらに好ましくは1重量%以上、最も好ましくは3重量%以上である。また、耐熱性、耐光性の観点から、着色剤の全量を基準(100重量%)として、好ましくは40重量%以下、最も好ましくは35重量%以下である。
樹脂型分散剤は、着色剤に吸着する性質を有する顔料親和性部位と、着色剤担体と相溶性のある部位とを有し、着色剤に吸着して着色剤の着色剤担体への分散を安定化する働きをするものである。樹脂型分散剤として具体的には、ポリウレタン、ポリアクリレート等のポリカルボン酸エステル、不飽和ポリアミド、ポリカルボン酸、ポリカルボン酸(部分)アミン塩、ポリカルボン酸アンモニウム塩、ポリカルボン酸アルキルアミン塩、ポリシロキサン、長鎖ポリアミノアマイドリン酸塩、水酸基含有ポリカルボン酸エステルや、これらの変性物、ポリ(低級アルキレンイミン)と遊離のカルボキシル基を有するポリエステルとの反応により形成されたアミドやその塩等の油性分散剤、(メタ)アクリル酸−スチレン共重合体、(メタ)アクリル酸−(メタ)アクリル酸エステル共重合体、スチレン−マレイン酸共重合体、ポリビニルアルコール、ポリビニルピロリドン等の水溶性樹脂や水溶性高分子化合物、ポリエステル系、変性ポリアクリレート系、エチレンオキサイド/プロピレンオキサイド付加化合物、燐酸エステル系等が用いられ、これらは単独で又は2種以上を混合して用いることができるが、必ずしもこれらに限定されるものではない。
市販の樹脂型分散剤としては、ビックケミー・ジャパン社製のDisperbyk−101、103、107、108、110、111、116、130、140、154、161、162、163、164、165、166、170、171、174、180、181、182、183、184、185、190、2000、2001、2020、2025、2050、2070、2095、2150、2155またはAnti−Terra−U、203、204、またはBYK−P104、P104S、220S、6919、またはLactimon、Lactimon−WSまたはBykumen等、日本ルーブリゾール社製のSOLSPERSE−3000、9000、13000、13240、13650、13940、16000、17000、18000、20000、21000、24000、26000、27000、28000、31845、32000、32500、32550、33500、32600、34750、35100、36600、38500、41000、41090、53095、55000、76500等、チバ・ジャパン社製のEFKA−46、47、48、452、4008、4009、4010、4015、4020、4047、4050、4055、4060、4080、4400、4401、4402、4403、4406、4408、4300、4310、4320、4330、4340、450、451、453、4540、4550、4560、4800、5010、5065、5066、5070、7500、7554、1101、120、150、1501、1502、1503、等、味の素ファインテクノ社製のアジスパーPA111、PB711、PB821、PB822、PB824等が挙げられる。
界面活性剤としては、ラウリル硫酸ナトリウム、ポリオキシエチレンアルキルエーテル硫酸塩、ドデシルベンゼンスルホン酸ナトリウム、スチレン−アクリル酸共重合体のアルカリ塩、ステアリン酸ナトリウム、アルキルナフタリンスルホン酸ナトリウム、アルキルジフェニルエーテルジスルホン酸ナトリウム、ラウリル硫酸モノエタノールアミン、ラウリル硫酸トリエタノールアミン、ラウリル硫酸アンモニウム、ステアリン酸モノエタノールアミン、スチレン−アクリル酸共重合体のモノエタノールアミン、ポリオキシエチレンアルキルエーテルリン酸エステル等のアニオン性界面活性剤;ポリオキシエチレンオレイルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンアルキルエーテルリン酸エステル、ポリオキシエチレンソルビタンモノステアレート、ポリエチレングリコールモノラウレート等のノニオン性界面活性剤;アルキル4級アンモニウム塩やそれらのエチレンオキサイド付加物等のカオチン性界面活性剤;アルキルジメチルアミノ酢酸ベタイン等のアルキルベタイン、アルキルイミダゾリン等の両性界面活性剤が挙げられ、これらは単独で又は2種以上を混合して用いることができるが、必ずしもこれらに限定されるものではない。
樹脂型分散剤、界面活性剤を添加する場合には、着色剤の全量を基準(100重量%)とし、好ましくは0.1〜55重量%、さらに好ましくは0.1〜45重量%である。樹脂型分散剤、界面活性剤の配合量が、0.1重量%未満の場合には、添加した効果が得られ難く、配合量が55重量%より多いと、過剰な分散剤により分散に影響を及ぼすことがある。
本発明の着色組成物は、さらに光重合性単量体および/または光重合開始剤を添加し、カラーフィルタ用感光性着色組成物として使用することが出来る。
<光重合性化合物>
本発明の光重合性化合物には、紫外線や熱などにより硬化して透明樹脂を生成するモノマーもしくはオリゴマーが含まれ、これらを単独で、または2種以上混合して用いることができる。モノマーの配合量は、着色剤の全重量を基準(100重量%)として、5〜400重量%であることが好ましく、光硬化性および現像性の観点から10〜300重量%であることがより好ましい。
<光重合性化合物>
本発明の光重合性化合物には、紫外線や熱などにより硬化して透明樹脂を生成するモノマーもしくはオリゴマーが含まれ、これらを単独で、または2種以上混合して用いることができる。モノマーの配合量は、着色剤の全重量を基準(100重量%)として、5〜400重量%であることが好ましく、光硬化性および現像性の観点から10〜300重量%であることがより好ましい。
紫外線や熱などにより硬化して透明樹脂を生成するモノマー、オリゴマーとしては、例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、β−カルボキシエチル(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、トリプロピレングリコールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、1,6−ヘキサンジオールジグリシジルエーテルジ(メタ)アクリレート、ビスフェノールAジグリシジルエーテルジ(メタ)アクリレート、ネオペンチルグリコールジグリシジルエーテルジ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、トリシクロデカニル(メタ)アクリレート、エステルアクリレート、メチロール化メラミンの(メタ)アクリル酸エステル、エポキシ(メタ)アクリレート、ウレタンアクリレート等の各種アクリル酸エステルおよびメタクリル酸エステル、(メタ)アクリル酸、スチレン、酢酸ビニル、ヒドロキシエチルビニルエーテル、エチレングリコールジビニルエーテル、ペンタエリスリトールトリビニルエーテル、(メタ)アクリルアミド、N−ヒドロキシメチル(メタ)アクリルアミド、N−ビニルホルムアミド、アクリロニトリル等が挙げられるが、必ずしもこれらに限定されるものではない。
<光重合開始剤>
本発明のカラーフィルタ用着色組成物には、該組成物を紫外線照射により硬化させ、フォトリソグラフ法によりフィルタセグメントを形成する場合は、光重合開始剤等を加えて溶剤現像型あるいはアルカリ現像型着色レジスト材の形態で調整することができる。光重合開始剤を使用する際の配合量は、着色剤の全量を基準として、5〜200重量%であることが好ましく、光硬化性および現像性の観点から10〜150重量%であることがより好ましい。
本発明のカラーフィルタ用着色組成物には、該組成物を紫外線照射により硬化させ、フォトリソグラフ法によりフィルタセグメントを形成する場合は、光重合開始剤等を加えて溶剤現像型あるいはアルカリ現像型着色レジスト材の形態で調整することができる。光重合開始剤を使用する際の配合量は、着色剤の全量を基準として、5〜200重量%であることが好ましく、光硬化性および現像性の観点から10〜150重量%であることがより好ましい。
光重合開始剤としては、4−フェノキシジクロロアセトフェノン、4−t−ブチル−ジクロロアセトフェノン、ジエトキシアセトフェノン、1−(4−イソプロピルフェニル)−2−ヒドロキシ−2−メチルプロパン−1−オン、1−ヒドロキシシクロヘキシルフェニルケトン、2−メチル−1−[4−(メチルチオ)フェニル]−2−モルフォリノプロパン−1−オン、2−(ジメチルアミノ)−2−[(4−メチルフェニル)メチル]−1−[4−(4−モルフォリニル)フェニル]−1−ブタノン、又は2−ベンジル−2−ジメチルアミノ−1−(4−モルフォリノフェニル)−ブタン−1−オン等のアセトフェノン系化合物;ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、又はベンジルジメチルケタール等のベンゾイン系化合物;ベンゾフェノン、ベンゾイル安息香酸、ベンゾイル安息香酸メチル、4−フェニルベンゾフェノン、ヒドロキシベンゾフェノン、アクリル化ベンゾフェノン、4−ベンゾイル−4’−メチルジフェニルサルファイド、又は3,3’,4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン等のベンゾフェノン系化合物;チオキサントン、2−クロルチオキサントン、2−メチルチオキサントン、イソプロピルチオキサントン、2,4−ジイソプロピルチオキサントン、又は2,4−ジエチルチオキサントン等のチオキサントン系化合物;2,4,6−トリクロロ−s−トリアジン、2−フェニル−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−メトキシフェニル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−トリル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−ピペロニル−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4−ビス(トリクロロメチル)−6−スチリル−s−トリアジン、2−(ナフト−1−イル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(4−メトキシ−ナフト−1−イル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4−トリクロロメチル−(ピペロニル)−6−トリアジン、又は2,4−トリクロロメチル−(4’−メトキシスチリル)−6−トリアジン等のトリアジン系化合物;1,2−オクタンジオン,1−〔4−(フェニルチオ)−,2−(O−ベンゾイルオキシム)〕、又はO−(アセチル)−N−(1−フェニル−2−オキソ−2−(4’−メトキシ−ナフチル)エチリデン)ヒドロキシルアミン等のオキシムエステル系化合物;ビス(2,4,6−トリメチルベンゾイル)フェニルホスフィンオキサイド、又は2,4,6−トリメチルベンゾイルジフェニルホスフィンオキサイド等のホスフィン系化合物;9,10−フェナンスレンキノン、カンファーキノン、エチルアントラキノン等のキノン系化合物; ボレート系化合物; カルバゾール系化合物;イミダゾール系化合物;あるいは、チタノセン系化合物等が用いられる。
これらの光重合開始剤は1種または必要に応じて任意の比率で2種以上混合して用いることができる。これらの光重合開始剤は、カラーフィルタ用着色組成物中の着色剤の全量を基準(100重量%)として、5〜200重量%であることが好ましく、光硬化性及び現像性の観点から10〜150重量%であることがより好ましい。
<増感剤>
さらに、本発明のカラーフィルタ用着色組成物には、増感剤を含有させることができる。増感剤としては、カルコン誘導体、ジベンザルアセトン等に代表される不飽和ケトン類、ベンジルやカンファーキノン等に代表される1,2−ジケトン誘導体、ベンゾイン誘導体、フルオレン誘導体、ナフトキノン誘導体、アントラキノン誘導体、キサンテン誘導体、チオキサンテン誘導体、キサントン誘導体、チオキサントン誘導体、クマリン誘導体、ケトクマリン誘導体、シアニン誘導体、メロシアニン誘導体、オキソノ−ル誘導体等のポリメチン色素、アクリジン誘導体、アジン誘導体、チアジン誘導体、オキサジン誘導体、インドリン誘導体、アズレン誘導体、アズレニウム誘導体、スクアリリウム誘導体、ポルフィリン誘導体、テトラフェニルポルフィリン誘導体、トリアリールメタン誘導体、テトラベンゾポルフィリン誘導体、テトラピラジノポルフィラジン誘導体、フタロシアニン誘導体、テトラアザポルフィラジン誘導体、テトラキノキサリロポルフィラジン誘導体、ナフタロシアニン誘導体、サブフタロシアニン誘導体、ピリリウム誘導体、チオピリリウム誘導体、テトラフィリン誘導体、アヌレン誘導体、スピロピラン誘導体、スピロオキサジン誘導体、チオスピロピラン誘導体、金属アレーン錯体、有機ルテニウム錯体、又はミヒラーケトン誘導体、α−アシロキシエステル、アシルフォスフィンオキサイド、メチルフェニルグリオキシレート、ベンジル、9,10−フェナンスレンキノン、カンファーキノン、エチルアンスラキノン、4,4’−ジエチルイソフタロフェノン、3,3’,又は4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン、4,4’−ジエチルアミノベンゾフェノン等が挙げられる。
さらに、本発明のカラーフィルタ用着色組成物には、増感剤を含有させることができる。増感剤としては、カルコン誘導体、ジベンザルアセトン等に代表される不飽和ケトン類、ベンジルやカンファーキノン等に代表される1,2−ジケトン誘導体、ベンゾイン誘導体、フルオレン誘導体、ナフトキノン誘導体、アントラキノン誘導体、キサンテン誘導体、チオキサンテン誘導体、キサントン誘導体、チオキサントン誘導体、クマリン誘導体、ケトクマリン誘導体、シアニン誘導体、メロシアニン誘導体、オキソノ−ル誘導体等のポリメチン色素、アクリジン誘導体、アジン誘導体、チアジン誘導体、オキサジン誘導体、インドリン誘導体、アズレン誘導体、アズレニウム誘導体、スクアリリウム誘導体、ポルフィリン誘導体、テトラフェニルポルフィリン誘導体、トリアリールメタン誘導体、テトラベンゾポルフィリン誘導体、テトラピラジノポルフィラジン誘導体、フタロシアニン誘導体、テトラアザポルフィラジン誘導体、テトラキノキサリロポルフィラジン誘導体、ナフタロシアニン誘導体、サブフタロシアニン誘導体、ピリリウム誘導体、チオピリリウム誘導体、テトラフィリン誘導体、アヌレン誘導体、スピロピラン誘導体、スピロオキサジン誘導体、チオスピロピラン誘導体、金属アレーン錯体、有機ルテニウム錯体、又はミヒラーケトン誘導体、α−アシロキシエステル、アシルフォスフィンオキサイド、メチルフェニルグリオキシレート、ベンジル、9,10−フェナンスレンキノン、カンファーキノン、エチルアンスラキノン、4,4’−ジエチルイソフタロフェノン、3,3’,又は4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン、4,4’−ジエチルアミノベンゾフェノン等が挙げられる。
さらに具体的には、大河原信ら編、「色素ハンドブック」(1986年、講談社)、大河原信ら編、「機能性色素の化学」(1981年、シーエムシー)、池森忠三朗ら編、及び「特殊機能材料」(1986年、シーエムシー)に記載の増感剤が挙げられるがこれらに限定されるものではない。また、その他、紫外から近赤外域にかけての光に対して吸収を示す増感剤を含有させることもできる。
増感剤は、必要に応じて任意の比率で二種以上用いてもかまわない。増感剤を使用する際の配合量は、着色組成物中に含まれる光重合開始剤の全重量を基準(100重量%)として、3〜60重量%であることが好ましく、光硬化性、現像性の観点から5〜50重量%であることがより好ましい。
<アミン系化合物>
また、本発明のカラーフィルタ用着色組成物には、溶存している酸素を還元する働きのあるアミン系化合物を含有させることができる。
また、本発明のカラーフィルタ用着色組成物には、溶存している酸素を還元する働きのあるアミン系化合物を含有させることができる。
このようなアミン系化合物としては、トリエタノールアミン、メチルジエタノールアミン、トリイソプロパノールアミン、4−ジメチルアミノ安息香酸メチル、4−ジメチルアミノ安息香酸エチル、4−ジメチルアミノ安息香酸イソアミル、安息香酸2−ジメチルアミノエチル、4−ジメチルアミノ安息香酸2−エチルヘキシル、及びN,N−ジメチルパラトルイジン等が挙げられる。
<レベリング剤>
本発明の着色組成物には、透明基板上での組成物のレベリング性をよくするため、レベリング剤を添加することが好ましい。レベリング剤としては、主鎖にポリエーテル構造又はポリエステル構造を有するジメチルシロキサンが好ましい。主鎖にポリエーテル構造を有するジメチルシロキサンの具体例としては、東レ・ダウコーニング社製FZ−2122、ビックケミー社製BYK−333などが挙げられる。主鎖にポリエステル構造を有するジメチルシロキサンの具体例としては、ビックケミー社製BYK−310、BYK−370などが挙げられる。主鎖にポリエーテル構造を有するジメチルシロキサンと、主鎖にポリエステル構造を有するジメチルシロキサンとは、併用することもできる。レベリング剤の含有量は通常、着色組成物の全重量を基準(100重量%)として、0.003〜0.5重量%用いることが好ましい。
本発明の着色組成物には、透明基板上での組成物のレベリング性をよくするため、レベリング剤を添加することが好ましい。レベリング剤としては、主鎖にポリエーテル構造又はポリエステル構造を有するジメチルシロキサンが好ましい。主鎖にポリエーテル構造を有するジメチルシロキサンの具体例としては、東レ・ダウコーニング社製FZ−2122、ビックケミー社製BYK−333などが挙げられる。主鎖にポリエステル構造を有するジメチルシロキサンの具体例としては、ビックケミー社製BYK−310、BYK−370などが挙げられる。主鎖にポリエーテル構造を有するジメチルシロキサンと、主鎖にポリエステル構造を有するジメチルシロキサンとは、併用することもできる。レベリング剤の含有量は通常、着色組成物の全重量を基準(100重量%)として、0.003〜0.5重量%用いることが好ましい。
レベリング剤として特に好ましいものとしては、分子内に疎水基と親水基を有するいわゆる界面活性剤の一種で、親水基を有しながらも水に対する溶解性が小さく、着色組成物に添加した場合、その表面張力低下能が低いという特徴を有し、さらに表面張力低下能が低いにも拘らずガラス板への濡れ性が良好なものが有用であり、泡立ちによる塗膜の欠陥が出現しない添加量において十分に帯電性を抑止できるものが好ましく使用できる。このような好ましい特性を有するレベリング剤として、ポリアルキレンオキサイド単位を有するジメチルポリシロキサンが好ましく使用できる。ポリアルキレンオキサイド単位としては、ポリエチレンオキサイド単位、ポリプロピレンオキサイド単位があり、ジメチルポリシロキサンは、ポリエチレンオキサイド単位とポリプロピレンオキサイド単位とを共に有していてもよい。
また、ポリアルキレンオキサイド単位のジメチルポリシロキサンとの結合形態は、ポリアルキレンオキサイド単位がジメチルポリシロキサンの繰り返し単位中に結合したペンダント型、ジメチルポリシロキサンの末端に結合した末端変性型、ジメチルポリシロキサンと交互に繰り返し結合した直鎖状のブロックコポリマー型のいずれであってもよい。ポリアルキレンオキサイド単位を有するジメチルポリシロキサンは、東レ・ダウコーニング株式会社から市販されており、例えば、FZ−2110、FZ−2122、FZ−2130、FZ−2166、FZ−2191、FZ−2203、FZ−2207が挙げられるが、これらに限定されるものではない。
レベリング剤には、アニオン性、カチオン性、ノニオン性、または両性の界面活性剤を補助的に加えることも可能である。界面活性剤は、2種以上混合して使用しても構わない。
レベリング剤に補助的に加えるアニオン性界面活性剤としては、ポリオキシエチレンアルキルエーテル硫酸塩、ドデシルベンゼンスルホン酸ナトリウム、スチレン−アクリル酸共重合体のアルカリ塩、アルキルナフタリンスルホン酸ナトリウム、アルキルジフェニルエーテルジスルホン酸ナトリウム、ラウリル硫酸モノエタノールアミン、ラウリル硫酸トリエタノールアミン、ラウリル硫酸アンモニウム、ステアリン酸モノエタノールアミン、ステアリン酸ナトリウム、ラウリル硫酸ナトリウム、スチレン−アクリル酸共重合体のモノエタノールアミン、ポリオキシエチレンアルキルエーテルリン酸エステルなどが挙げられる。
レベリング剤に補助的に加えるアニオン性界面活性剤としては、ポリオキシエチレンアルキルエーテル硫酸塩、ドデシルベンゼンスルホン酸ナトリウム、スチレン−アクリル酸共重合体のアルカリ塩、アルキルナフタリンスルホン酸ナトリウム、アルキルジフェニルエーテルジスルホン酸ナトリウム、ラウリル硫酸モノエタノールアミン、ラウリル硫酸トリエタノールアミン、ラウリル硫酸アンモニウム、ステアリン酸モノエタノールアミン、ステアリン酸ナトリウム、ラウリル硫酸ナトリウム、スチレン−アクリル酸共重合体のモノエタノールアミン、ポリオキシエチレンアルキルエーテルリン酸エステルなどが挙げられる。
レベリング剤に補助的に加えるカオチン性界面活性剤としては、アルキル4級アンモニウム塩やそれらのエチレンオキサイド付加物が挙げられる。レベリング剤に補助的に加えるノニオン性界面活性剤としては、ポリオキシエチレンオレイルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンアルキルエーテルリン酸エステル、ポリオキシエチレンソルビタンモノステアレート、ポリエチレングリコールモノラウレートなどの;アルキルジメチルアミノ酢酸ベタインなどのアルキルベタイン、アルキルイミダゾリンなどの両性界面活性剤、また、フッ素系やシリコーン系の界面活性剤が挙げられる。
<硬化剤、硬化促進剤>
また本発明の着色組成物には、熱硬化性樹脂の硬化を補助するため、必要に応じて、硬化剤、硬化促進剤などを含んでいてもよい。硬化剤としては、フェノール系樹脂、アミン系化合物、酸無水物、活性エステル、カルボン酸系化合物、スルホン酸系化合物などが有効であるが、特にこれらに限定されるものではなく、熱硬化性樹脂と反応し得るものであれば、いずれの硬化剤を使用してもよい。また、これらの中でも、1分子内に2個以上のフェノール性水酸基を有する化合物、アミン系硬化剤が好ましく挙げられる。前記硬化促進剤としては、例えば、アミン化合物(例えば、ジシアンジアミド、ベンジルジメチルアミン、4−(ジメチルアミノ)−N,N−ジメチルベンジルアミン、4−メトキシ−N,N−ジメチルベンジルアミン、4−メチル−N,N−ジメチルベンジルアミン等)、4級アンモニウム塩化合物(例えば、トリエチルベンジルアンモニウムクロリド等)、ブロックイソシアネート化合物(例えば、ジメチルアミン等)、イミダゾール誘導体二環式アミジン化合物及びその塩(例えば、イミダゾール、2−メチルイミダゾール、2−エチルイミダゾール、2−エチル−4−メチルイミダゾール、2−フェニルイミダゾール、4−フェニルイミダゾール、1−シアノエチル−2−フェニルイミダゾール、1−(2−シアノエチル)−2−エチル−4−メチルイミダゾール等)、リン化合物(例えば、トリフェニルホスフィン等)、グアナミン化合物(例えば、メラミン、グアナミン、アセトグアナミン、ベンゾグアナミン等)、S−トリアジン誘導体(例えば、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン、2−ビニル−2,4−ジアミノ−S−トリアジン、2−ビニル−4,6−ジアミノ−S−トリアジン・イソシアヌル酸付加物、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン・イソシアヌル酸付加物等)などを用いることができる。これらは1種単独で使用してもよく、2種以上を併用してもよい。前記硬化促進剤の含有量としては、熱硬化性樹脂全量に対し、0.01〜15重量%が好ましい。
また本発明の着色組成物には、熱硬化性樹脂の硬化を補助するため、必要に応じて、硬化剤、硬化促進剤などを含んでいてもよい。硬化剤としては、フェノール系樹脂、アミン系化合物、酸無水物、活性エステル、カルボン酸系化合物、スルホン酸系化合物などが有効であるが、特にこれらに限定されるものではなく、熱硬化性樹脂と反応し得るものであれば、いずれの硬化剤を使用してもよい。また、これらの中でも、1分子内に2個以上のフェノール性水酸基を有する化合物、アミン系硬化剤が好ましく挙げられる。前記硬化促進剤としては、例えば、アミン化合物(例えば、ジシアンジアミド、ベンジルジメチルアミン、4−(ジメチルアミノ)−N,N−ジメチルベンジルアミン、4−メトキシ−N,N−ジメチルベンジルアミン、4−メチル−N,N−ジメチルベンジルアミン等)、4級アンモニウム塩化合物(例えば、トリエチルベンジルアンモニウムクロリド等)、ブロックイソシアネート化合物(例えば、ジメチルアミン等)、イミダゾール誘導体二環式アミジン化合物及びその塩(例えば、イミダゾール、2−メチルイミダゾール、2−エチルイミダゾール、2−エチル−4−メチルイミダゾール、2−フェニルイミダゾール、4−フェニルイミダゾール、1−シアノエチル−2−フェニルイミダゾール、1−(2−シアノエチル)−2−エチル−4−メチルイミダゾール等)、リン化合物(例えば、トリフェニルホスフィン等)、グアナミン化合物(例えば、メラミン、グアナミン、アセトグアナミン、ベンゾグアナミン等)、S−トリアジン誘導体(例えば、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン、2−ビニル−2,4−ジアミノ−S−トリアジン、2−ビニル−4,6−ジアミノ−S−トリアジン・イソシアヌル酸付加物、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン・イソシアヌル酸付加物等)などを用いることができる。これらは1種単独で使用してもよく、2種以上を併用してもよい。前記硬化促進剤の含有量としては、熱硬化性樹脂全量に対し、0.01〜15重量%が好ましい。
<その他の添加剤成分>
本発明の着色組成物には、組成物の経時粘度を安定化させるために貯蔵安定剤を含有させることができる。また、透明基板との密着性を高めるためにシランカップリング剤等の密着向上剤を含有させることもできる。
本発明の着色組成物には、組成物の経時粘度を安定化させるために貯蔵安定剤を含有させることができる。また、透明基板との密着性を高めるためにシランカップリング剤等の密着向上剤を含有させることもできる。
貯蔵安定剤としては、例えば、ベンジルトリメチルクロライド、ジエチルヒドロキシアミンなどの4級アンモニウムクロライド、乳酸、シュウ酸などの有機酸およびそのメチルエーテル、t−ブチルピロカテコール、テトラエチルホスフィン、テトラフェニルフォスフィンなどの有機ホスフィン、亜リン酸塩等が挙げられる。貯蔵安定剤は、着色剤の全量を基準(100重量%)として、0.1〜10重量%の量で用いることができる。
密着向上剤としては、ビニルトリス(β−メトキシエトキシ)シラン、ビニルエトキシシラン、ビニルトリメトキシシラン等のビニルシラン類、γ−メタクリロキシプロピルトリメトキシシラン等の(メタ)アクリルシラン類、β−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、β−(3,4−エポキシシクロヘキシル)メチルトリメトキシシラン、β−(3,4−エポキシシクロヘキシル)エチルトリエトキシシラン、β−(3,4−エポキシシクロヘキシル)メチルトリエトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシラン等のエポキシシラン類、N−β(アミノエチル)γ−アミノプロピルトリメトキシシラン、N−β(アミノエチル)γ−アミノプロピルトリエトキシシラン、N−β(アミノエチル)γ−アミノプロピルメチルジエトキシシシラン、γ−アミノプロピルトリエトキシシラン、γ−アミノプロピルトリメトキシシラン、N−フェニル−γ−アミノプロピルトリメトキシシラン、N−フェニル−γ−アミノプロピルトリエトキシシラン等のアミノシラン類、γ−メルカプトプロピルトリメトキシシラン、γ−メルカプトプロピルトリエトキシシラン等のチオシラン類等のシランカップリング剤が挙げられる。密着向上剤は、着色組成物中の着色剤の全量を基準(100重量%)として、0.01〜10重量%、好ましくは0.05〜5重量%の量で用いることができる。
<粗大粒子の除去>
本発明の着色組成物は、遠心分離、焼結フィルタ、メンブレンフィルタ等の手段にて、5μm以上の粗大粒子、好ましくは1μm以上の粗大粒子、さらに好ましくは0.5μm以上の粗大粒子および混入した塵の除去を行うことが好ましい。このように着色組成物は、実質的に0.5μm以上の粒子を含まないことが好ましい。より好ましくは0.3μm以下であることが好ましい。
本発明の着色組成物は、遠心分離、焼結フィルタ、メンブレンフィルタ等の手段にて、5μm以上の粗大粒子、好ましくは1μm以上の粗大粒子、さらに好ましくは0.5μm以上の粗大粒子および混入した塵の除去を行うことが好ましい。このように着色組成物は、実質的に0.5μm以上の粒子を含まないことが好ましい。より好ましくは0.3μm以下であることが好ましい。
<カラーフィルタ>
次に、本発明のカラーフィルタについて説明する。本発明のカラーフィルタは、少なくとも1つの赤色フィルタセグメント、少なくとも1つの緑色フィルタセグメント、および少なくとも1つの青色フィルタセグメントを具備し、前記少なくとも1つのフィルタセグメントは、本発明のカラーフィルタ用着色組成物を用いて形成される。
次に、本発明のカラーフィルタについて説明する。本発明のカラーフィルタは、少なくとも1つの赤色フィルタセグメント、少なくとも1つの緑色フィルタセグメント、および少なくとも1つの青色フィルタセグメントを具備し、前記少なくとも1つのフィルタセグメントは、本発明のカラーフィルタ用着色組成物を用いて形成される。
赤色フィルタセグメントは、赤色顔料と着色剤担体を含む通常の赤色着色組成物を用いて形成することができる。赤色着色組成物には、例えばC.I.ピグメント レッド 7、14、41、48:1、48:2、48:3、48:4、57:1、81、81:1、81:2、81:3、81:4、122、146、168、169、177、178、184、185、187、200、202、208、210、242、246、254、255、264、270、272、273、274,276、277、278、279、280、281、282、283、284、285、286、又は287等の赤色顔料が用いられる。また赤色を呈する塩基性染料、酸性染料の造塩化合物を使用することもできる。
また赤色着色組成物には、C.I.ピグメント オレンジ 43、71、又は73等の橙色顔料及び/またはC.I.ピグメント イエロー 1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、138、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、193、194、198、199、213、214、218、219、220、又は221等の黄色顔料を併用することができる。また橙色及び/または黄色を呈する塩基性染料、酸性染料の造塩化合物を使用することもできる。
緑色フィルタセグメントは、緑色顔料と着色剤担体を含む通常の緑色着色組成物を用いて形成することができる。緑色顔料としては、例えばC.I.ピグメント グリーン7、10、36、37、58等が用いられる。
また緑色着色組成物には、黄色顔料を併用することができる。併用可能な黄色顔料としては、C.I.ピグメント イエロー1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、138、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、193、194、198、199、213、214、218、219、220、又は221等の黄色顔料を挙げることができる。また黄色を呈する塩基性染料、酸性染料の造塩化合物を併用することもできる。
<カラーフィルタの製造方法>
本発明のカラーフィルタは、印刷法またはフォトリソグラフィー法により、製造することができる。
本発明のカラーフィルタは、印刷法またはフォトリソグラフィー法により、製造することができる。
印刷法によるフィルタセグメントの形成は、印刷インキとして調製した着色組成物の印刷と乾燥を繰り返すだけでパターン化ができるため、カラーフィルタの製造法としては、低コストで量産性に優れている。さらに、印刷技術の発展により高い寸法精度および平滑度を有する微細パターンの印刷を行うことができる。印刷を行うためには、印刷の版上にて、あるいはブランケット上にてインキが乾燥、固化しないような組成とすることが好ましい。また、印刷機上でのインキの流動性の制御も重要であり、分散剤や体質顔料によるインキ粘度の調整を行うこともできる。
フォトリソグラフィー法によりフィルタセグメントを形成する場合は、上記溶剤現像型あるいはアルカリ現像型着色レジスト材として調製した着色組成物を、透明基板上に、スプレーコートやスピンコート、スリットコート、ロールコート等の塗布方法により、乾燥膜厚が0.2〜5μmとなるように塗布する。必要により乾燥された膜には、この膜と接触あるいは非接触状態で設けられた所定のパターンを有するマスクを通して紫外線露光を行う。その後、溶剤またはアルカリ現像液に浸漬するかもしくはスプレーなどにより現像液を噴霧して未硬化部を除去して所望のパターンを形成したのち、同様の操作を他色について繰り返してカラーフィルタを製造することができる。さらに、着色レジスト材の重合を促進するため、必要に応じて加熱を施すこともできる。フォトリソグラフィー法によれば、上記印刷法より精度の高いカラーフィルタが製造できる。
現像に際しては、アルカリ現像液として炭酸ナトリウム、水酸化ナトリウム等の水溶液が使用され、ジメチルベンジルアミン、トリエタノールアミン等の有機アルカリを用いることもできる。また、現像液には、消泡剤や界面活性剤を添加することもできる。
なお、紫外線露光感度を上げるために、上記着色レジストを塗布乾燥後、水溶性あるいはアルカリ水溶性樹脂、例えばポリビニルアルコールや水溶性アクリル樹脂等を塗布乾燥し酸素による重合阻害を防止する膜を形成した後、紫外線露光を行うこともできる。
なお、紫外線露光感度を上げるために、上記着色レジストを塗布乾燥後、水溶性あるいはアルカリ水溶性樹脂、例えばポリビニルアルコールや水溶性アクリル樹脂等を塗布乾燥し酸素による重合阻害を防止する膜を形成した後、紫外線露光を行うこともできる。
本発明のカラーフィルタは、上記方法の他に電着法、転写法などにより製造することができるが、本発明の着色組成物はいずれの方法にも用いることができる。なお、電着法は、基板上に形成した透明導電膜を利用して、コロイド粒子の電気泳動により各色フィルタセグメントを透明導電膜の上に電着形成することでカラーフィルタを製造する方法である。また、転写法は剥離性の転写ベースシートの表面に、あらかじめフィルタセグメントを形成しておき、このフィルタセグメントを所望の基板に転写させる方法である。
透明基板あるいは反射基板上に各色フィルタセグメントを形成する前に、あらかじめブラックマトリクスを形成することができる。ブラックマトリクスとしては、クロムやクロム/酸化クロムの多層膜、窒化チタニウムなどの無機膜や、遮光剤を分散した樹脂膜が用いられるが、これらに限定されない。また、前記の透明基板あるいは反射基板上に薄膜トランジスター(TFT)をあらかじめ形成しておき、その後に各色フィルタセグメントを形成することもできる。また本発明のカラーフィルタ上には、必要に応じてオーバーコート膜や透明導電膜などが形成される。
以下に、本発明を実施例に基づいて説明するが、本発明はこれによって限定されるものではない。なお、特にことわりがない限り、「部」とは「重量部」を意味する。
また、アクリル樹脂の重量平均分子量(Mw)は、TSKgelカラム(東ソー社製)を用い、RI検出器を装備したGPC(東ソー社製、HLC−8120GPC)で、展開溶媒にTHF(テトラヒドロフラン)を用いて測定したポリスチレン換算の重量平均分子量(Mw)である。
まず、実施例および比較例に用いたアルカリ可溶性樹脂、微細化顔料、造塩化合物(A)、顔料分散体、キサンテン系化合物含有樹脂溶液、赤色レジスト材、緑色レジスト材の製造方法から説明する。
<アルカリ可溶性樹脂1、2の製造方法>
(アルカリ可溶性樹脂1の調製)
セパラブル4口フラスコに温度計、冷却管、窒素ガス導入管、撹拌装置を取り付けた反応容器にシクロヘキサノン70.0部を仕込み、80℃に昇温し、反応容器内を窒素置換した後、滴下管よりn−ブチルメタクリレート13.3部、2−ヒドロキシエチルメタクリレート4.6部、メタクリル酸4.3部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亞合成株式会社製「アロニックスM110」)7.4部、2,2’−アゾビスイソブチロニトリル0.4部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、重量平均分子量(Mw)26000のアクリル樹脂の溶液を得た。室温まで冷却した後、樹脂溶液約2gをサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20重量%になるようにメトキシプロピルアセテートを添加してアルカリ可溶性樹脂1を調製した。
(アルカリ可溶性樹脂1の調製)
セパラブル4口フラスコに温度計、冷却管、窒素ガス導入管、撹拌装置を取り付けた反応容器にシクロヘキサノン70.0部を仕込み、80℃に昇温し、反応容器内を窒素置換した後、滴下管よりn−ブチルメタクリレート13.3部、2−ヒドロキシエチルメタクリレート4.6部、メタクリル酸4.3部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亞合成株式会社製「アロニックスM110」)7.4部、2,2’−アゾビスイソブチロニトリル0.4部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、重量平均分子量(Mw)26000のアクリル樹脂の溶液を得た。室温まで冷却した後、樹脂溶液約2gをサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20重量%になるようにメトキシプロピルアセテートを添加してアルカリ可溶性樹脂1を調製した。
(アルカリ可溶性樹脂2の調製)
温度計、冷却管、窒素ガス導入管、滴下管及び撹拌装置を備えたセパラブル4口フラスコにシクロヘキサノン207部を仕込み、80℃に昇温し、フラスコ内を窒素置換した後、滴下管より、メタクリル酸20部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亜合成社製アロニックスM110)20部、メタクリル酸メチル45部、2−ヒドロキシエチルメタクリレート8.5部、及び2,2'−アゾビスイソブチロニトリル1.33部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、共重合体樹脂溶液を得た。
次に得られた共重合体溶液全量に対して、窒素ガスを停止し乾燥空気を1時間注入しながら攪拌したのちに、室温まで冷却した後、2−メタクリロイルオキシエチルイソシアネート(昭和電工社製カレンズMOI)6.5部、ラウリン酸ジブチル錫0.08部、シクロヘキサノン26部の混合物を70℃で3時間かけて滴下した。
樹脂溶液約2gをサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20重量%になるようにシクロヘキサノンを添加してアルカリ可溶性樹脂2を調製した。重量平均分子量(Mw)は18000であった。
温度計、冷却管、窒素ガス導入管、滴下管及び撹拌装置を備えたセパラブル4口フラスコにシクロヘキサノン207部を仕込み、80℃に昇温し、フラスコ内を窒素置換した後、滴下管より、メタクリル酸20部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亜合成社製アロニックスM110)20部、メタクリル酸メチル45部、2−ヒドロキシエチルメタクリレート8.5部、及び2,2'−アゾビスイソブチロニトリル1.33部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、共重合体樹脂溶液を得た。
次に得られた共重合体溶液全量に対して、窒素ガスを停止し乾燥空気を1時間注入しながら攪拌したのちに、室温まで冷却した後、2−メタクリロイルオキシエチルイソシアネート(昭和電工社製カレンズMOI)6.5部、ラウリン酸ジブチル錫0.08部、シクロヘキサノン26部の混合物を70℃で3時間かけて滴下した。
樹脂溶液約2gをサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20重量%になるようにシクロヘキサノンを添加してアルカリ可溶性樹脂2を調製した。重量平均分子量(Mw)は18000であった。
<微細化顔料の製造方法>
(青色微細顔料1の作製)
フタロシアニン系青色顔料C.I.ピグメント ブルー 15:6(東洋インキ製造株式会社製「LIONOL BLUE ES」、比表面積60m2/g)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の青色微細顔料1を得た。青色微細顔料1の比表面積は80m2/gであった。
(青色微細顔料1の作製)
フタロシアニン系青色顔料C.I.ピグメント ブルー 15:6(東洋インキ製造株式会社製「LIONOL BLUE ES」、比表面積60m2/g)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の青色微細顔料1を得た。青色微細顔料1の比表面積は80m2/gであった。
(青色微細顔料2の作製)
トリフェニルメタン系青色顔料C.I.ピグメント ブルー 1(BASF社製「Fanal Blue D 6340」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の青色微細顔料2を得た。青色微細顔料2の比表面積は65m2/gであった。
トリフェニルメタン系青色顔料C.I.ピグメント ブルー 1(BASF社製「Fanal Blue D 6340」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の青色微細顔料2を得た。青色微細顔料2の比表面積は65m2/gであった。
(紫色微細顔料1の作製)
ジオキサジン系紫色顔料C.I.ピグメント バイオレット 23(東洋インキ製造株式会社製「LIONOGEN VIOLET RL」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の紫色微細顔料1を得た。紫色微細顔料1の比表面積は95m2/gであった。
ジオキサジン系紫色顔料C.I.ピグメント バイオレット 23(東洋インキ製造株式会社製「LIONOGEN VIOLET RL」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の紫色微細顔料1を得た。紫色微細顔料1の比表面積は95m2/gであった。
(赤色微細顔料1の作製)
ジケトピロロピロール系赤色顔料C.I.ピグメント レッド 254(チバ・ジャパン社製「IRGAZIN RED 2030」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の赤色微細顔料1を得た。赤色微細顔料1の比表面積は70m2/gであった。
ジケトピロロピロール系赤色顔料C.I.ピグメント レッド 254(チバ・ジャパン社製「IRGAZIN RED 2030」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の赤色微細顔料1を得た。赤色微細顔料1の比表面積は70m2/gであった。
(黄色微細顔料1の作製)
イソインドリン系黄色顔料C.I.ピグメント イエロー 139(チバ・ジャパン社製「イルガフォアイエロー 2R−CF」)500部、塩化ナトリウム500部、およびジエチレングリコール250部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、120℃で8時間混練した。次に、この混練物を5リットルの温水に投入し、70℃に加熱しながら1時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウム及びジエチレングリコールを除いた後、80℃で一昼夜乾燥し、490部の黄色微細顔料1を得た。黄色微細顔料1の比表面積は70m2/gであった。
イソインドリン系黄色顔料C.I.ピグメント イエロー 139(チバ・ジャパン社製「イルガフォアイエロー 2R−CF」)500部、塩化ナトリウム500部、およびジエチレングリコール250部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、120℃で8時間混練した。次に、この混練物を5リットルの温水に投入し、70℃に加熱しながら1時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウム及びジエチレングリコールを除いた後、80℃で一昼夜乾燥し、490部の黄色微細顔料1を得た。黄色微細顔料1の比表面積は70m2/gであった。
(緑色微細顔料1の作製)
フタロシアニン系緑色顔料C.I.ピグメント グリーン 36(東洋インキ製造株式会社製「リオノールグリーン 6YK」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の緑色微細顔料1を得た。緑色微細顔料1の比表面積は75m2/gであった。
フタロシアニン系緑色顔料C.I.ピグメント グリーン 36(東洋インキ製造株式会社製「リオノールグリーン 6YK」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の緑色微細顔料1を得た。緑色微細顔料1の比表面積は75m2/gであった。
(黄色微細顔料2の作製)
ニッケル錯体系黄色顔料C.I.ピグメント イエロー 150(ランクセス社製「E−4GN」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の黄色微細顔料2を得た。黄色微細顔料2の比表面積は65m2/gであった。
ニッケル錯体系黄色顔料C.I.ピグメント イエロー 150(ランクセス社製「E−4GN」)200部、塩化ナトリウム1400部、およびジエチレングリコール360部をステンレス製1ガロンニーダー(井上製作所製)に仕込み、80℃で6時間混練した。次にこの混練物を8リットルの温水に投入し、80℃に加熱しながら2時間攪拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、85℃で一昼夜乾燥し、190部の黄色微細顔料2を得た。黄色微細顔料2の比表面積は65m2/gであった。
<造塩化合物(A)の製造方法>
(造塩化合物(A−1))
下記の手順でC.I.アシッド レッド 289とジステアリルジメチルアンモニウムクロライド(コータミンD86P)(カチオン部分の分子量が550)とからなる造塩化合物(A−1)を作製した。
7〜15モル%の水酸化ナトリウム溶液中に、C.I.アシッド レッド 289を溶解させ十分に混合・攪拌を行い、70〜90℃に加熱した後、コータミンD86Pを少しずつ滴下していく。またコータミンD86Pは水に溶解し水溶液として用いても良い。コータミンD86Pを滴下した後、70〜90℃で60分攪拌し十分に反応を行う。反応の終点確認としては濾紙に反応液を滴下して、にじみがなくなったところを終点として、造塩化合物が得られたことと判断できる。攪拌しながら室温まで放冷した後、吸引濾過を行い、水洗後、濾紙上に残った造塩化合物を乾燥機にて水分を除去して乾燥して、C.I.アシッド レッド 289とジステアリルジメチルアンモニウムクロライドとの造塩化合物、造塩化合物(A−1)を得た。
(造塩化合物(A−1))
下記の手順でC.I.アシッド レッド 289とジステアリルジメチルアンモニウムクロライド(コータミンD86P)(カチオン部分の分子量が550)とからなる造塩化合物(A−1)を作製した。
7〜15モル%の水酸化ナトリウム溶液中に、C.I.アシッド レッド 289を溶解させ十分に混合・攪拌を行い、70〜90℃に加熱した後、コータミンD86Pを少しずつ滴下していく。またコータミンD86Pは水に溶解し水溶液として用いても良い。コータミンD86Pを滴下した後、70〜90℃で60分攪拌し十分に反応を行う。反応の終点確認としては濾紙に反応液を滴下して、にじみがなくなったところを終点として、造塩化合物が得られたことと判断できる。攪拌しながら室温まで放冷した後、吸引濾過を行い、水洗後、濾紙上に残った造塩化合物を乾燥機にて水分を除去して乾燥して、C.I.アシッド レッド 289とジステアリルジメチルアンモニウムクロライドとの造塩化合物、造塩化合物(A−1)を得た。
(造塩化合物(A−2))
下記の手順でC.I.アシッド レッド 52とジアルキル(アルキルがC14〜C18)ジメチルアンモニウムクロライド(アーカード2HT−75)(カチオン部分の分子量が438〜550)とからなる造塩化合物(A−2)を作製した。
下記の手順でC.I.アシッド レッド 52とジアルキル(アルキルがC14〜C18)ジメチルアンモニウムクロライド(アーカード2HT−75)(カチオン部分の分子量が438〜550)とからなる造塩化合物(A−2)を作製した。
7〜15モル%の水酸化ナトリウム溶液中に、C.I.アシッド レッド 52を溶解させ十分に混合・攪拌を行い、70〜90℃に加熱した後、アーカード2HT−75を少しずつ滴下していく。またアーカード2HT−75は水に溶解し水溶液として用いても良い。アーカード2HT−75を滴下した後、70〜90℃で60分攪拌し十分に反応を行う。反応の終点確認としては濾紙に反応液を滴下して、にじみがなくなったところを終点として、造塩化合物が得られたことと判断できる。攪拌しながら室温まで放冷した後、吸引濾過を行い、水洗後、濾紙上に残った造塩化合物を乾燥機にて水分を除去して乾燥して、C.I.アシッド レッド 52とジアルキル(アルキルがC14〜C18)ジメチルアンモニウムクロライドとの造塩化合物、造塩化合物(A−2)を得た。
[実施例1〜6]
(実施例1;着色組成物(DB−1)の作製)
下記の混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5.0μmのフィルタで濾過し顔料分散体(DB−1)を作製した。
造塩化合物(A−1) : 4.0部
微細化顔料(P−1) : 7.0部
アルカリ可溶性樹脂1 :40.0部
シクロヘキサノン :10.0部
プロピレングリコールモノメチルエーテルアセテート(PGMAC):38.0部
樹脂型分散剤 (チバ・ジャパン社製「EFKA4300」) : 1.0部
(実施例1;着色組成物(DB−1)の作製)
下記の混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5.0μmのフィルタで濾過し顔料分散体(DB−1)を作製した。
造塩化合物(A−1) : 4.0部
微細化顔料(P−1) : 7.0部
アルカリ可溶性樹脂1 :40.0部
シクロヘキサノン :10.0部
プロピレングリコールモノメチルエーテルアセテート(PGMAC):38.0部
樹脂型分散剤 (チバ・ジャパン社製「EFKA4300」) : 1.0部
(実施例2〜6)
以下、造塩化合物、微細化顔料を表2に示す組成に変更した以外は実施例1と同様にして、着色組成物(DB−2〜6)を作製した。
以下、造塩化合物、微細化顔料を表2に示す組成に変更した以外は実施例1と同様にして、着色組成物(DB−2〜6)を作製した。
(着色組成物の評価)
得られた着色組成物(DB−1〜6)について、保存安定性および塗膜異物に関する試験を下記の方法で行った。試験の結果を表2に示す。
得られた着色組成物(DB−1〜6)について、保存安定性および塗膜異物に関する試験を下記の方法で行った。試験の結果を表2に示す。
(保存安定性試験方法)
作製した着色組成物の25℃における粘度を、E型粘度計(東機産業社製TUE−20L型)を用い回転数20rpmで測定した。着色組成物の作製当日の初期粘度と、40℃の恒温室にて7日間保存後の促進経時粘度から、粘度変化率を算出し、保存安定性を下記の基準にて評価した。
作製した着色組成物の25℃における粘度を、E型粘度計(東機産業社製TUE−20L型)を用い回転数20rpmで測定した。着色組成物の作製当日の初期粘度と、40℃の恒温室にて7日間保存後の促進経時粘度から、粘度変化率を算出し、保存安定性を下記の基準にて評価した。
◎:1割未満
○:1割以上、2割未満
△:2割以上、5割未満
×:5割以上
以下、表1にその結果を示す。
○:1割以上、2割未満
△:2割以上、5割未満
×:5割以上
以下、表1にその結果を示す。
(塗膜異物試験方法)
調製直後の着色組成物にて試験基板を作製し、粒子の数をカウントすることで評価した。先ず、透明基板上に乾燥塗膜が約2.0μmとなるように着色組成物を塗布し、オーブンで230℃で20分加熱して試験基板を得た。その後、オリンパスシステム社製の金属顕微鏡「BX60」を用いて表面観察を行い(倍率は500倍)、透過により任意の5視野にて観測可能な粒子の数をカウントし、下記の基準にて評価した。評価結果において、◎と○は異物数が少なく良好であり、△は異物数が多いものの使用上問題ないレベル、×は異物による塗工ムラ(斑)が発生するため使用することはできない状態に相当する。
◎:〜5個未満
○:5個以上、20個未満
△:21個以上、100個未満
×:100個以上
以下、表1にその結果を示す。
調製直後の着色組成物にて試験基板を作製し、粒子の数をカウントすることで評価した。先ず、透明基板上に乾燥塗膜が約2.0μmとなるように着色組成物を塗布し、オーブンで230℃で20分加熱して試験基板を得た。その後、オリンパスシステム社製の金属顕微鏡「BX60」を用いて表面観察を行い(倍率は500倍)、透過により任意の5視野にて観測可能な粒子の数をカウントし、下記の基準にて評価した。評価結果において、◎と○は異物数が少なく良好であり、△は異物数が多いものの使用上問題ないレベル、×は異物による塗工ムラ(斑)が発生するため使用することはできない状態に相当する。
◎:〜5個未満
○:5個以上、20個未満
△:21個以上、100個未満
×:100個以上
以下、表1にその結果を示す。
<赤色、緑色レジスト材の製造方法>
(赤色レジスト材の調製)
下記の混合物を均一になるように攪拌混合した後、1.0μmのフィルタで濾過して、赤色レジスト材を得た。
顔料分散体(DP−4) :50.0部
顔料分散体(DP−5) :10.0部
アルカリ可溶性樹脂2 :11.0部
トリメチロールプロパントリアクリレート : 4.2部
(新中村化学社製「NKエステルATMPT」)
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) : 1.2部
増感剤(保土ヶ谷化学社製「EAB−F」) : 0.4部
エチレングリコールモノメチルエーテルアセテート :23.2部
(赤色レジスト材の調製)
下記の混合物を均一になるように攪拌混合した後、1.0μmのフィルタで濾過して、赤色レジスト材を得た。
顔料分散体(DP−4) :50.0部
顔料分散体(DP−5) :10.0部
アルカリ可溶性樹脂2 :11.0部
トリメチロールプロパントリアクリレート : 4.2部
(新中村化学社製「NKエステルATMPT」)
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) : 1.2部
増感剤(保土ヶ谷化学社製「EAB−F」) : 0.4部
エチレングリコールモノメチルエーテルアセテート :23.2部
(緑色レジスト材の調製)
下記の混合物を均一になるように攪拌混合した後、1.0μmのフィルタで濾過して、緑色レジスト材を得た。
顔料分散体(DP−6) :45.0部
顔料分散体(DP−7) :15.0部
アルカリ可溶性樹脂2:11.0部
トリメチロールプロパントリアクリレート : 4.2部
(新中村化学社製「NKエステルATMPT」)
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) : 1.2部
増感剤(保土ヶ谷化学社製「EAB−F」) : 0.4部
エチレングリコールモノメチルエーテルアセテート :23.2部
下記の混合物を均一になるように攪拌混合した後、1.0μmのフィルタで濾過して、緑色レジスト材を得た。
顔料分散体(DP−6) :45.0部
顔料分散体(DP−7) :15.0部
アルカリ可溶性樹脂2:11.0部
トリメチロールプロパントリアクリレート : 4.2部
(新中村化学社製「NKエステルATMPT」)
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) : 1.2部
増感剤(保土ヶ谷化学社製「EAB−F」) : 0.4部
エチレングリコールモノメチルエーテルアセテート :23.2部
(レジスト材の評価)
得られたレジスト材(R−1〜9)の塗膜の色特性、耐熱性、耐光性、耐溶剤性の各試験を下記の方法で行った。試験の結果を表2に示す。
得られたレジスト材(R−1〜9)の塗膜の色特性、耐熱性、耐光性、耐溶剤性の各試験を下記の方法で行った。試験の結果を表2に示す。
(塗膜異物試験方法)
透明基板上に乾燥塗膜が約2.5μmとなるようにレジスト材を塗布し、全面紫外線露光を行った後、オーブンで230℃20分加熱、放冷し評価基板を得た。評価はオリンパスシステム社製金属顕微鏡「BX60」を用いて表面観察を行った。倍率は500倍とし、透過にて任意の5視野で確認可能な粒子の数をカウントする。下記の評価結果において、◎、○は良好であり、△は異物が多いものの使用上問題ないレベルであり、×は異物による塗工ムラが発生してしまう。
◎:5個未満
○:5個以上、20個未満
△:20個以上、100個未満
×:100個以上
以下、表2にその結果を示す。
透明基板上に乾燥塗膜が約2.5μmとなるようにレジスト材を塗布し、全面紫外線露光を行った後、オーブンで230℃20分加熱、放冷し評価基板を得た。評価はオリンパスシステム社製金属顕微鏡「BX60」を用いて表面観察を行った。倍率は500倍とし、透過にて任意の5視野で確認可能な粒子の数をカウントする。下記の評価結果において、◎、○は良好であり、△は異物が多いものの使用上問題ないレベルであり、×は異物による塗工ムラが発生してしまう。
◎:5個未満
○:5個以上、20個未満
△:20個以上、100個未満
×:100個以上
以下、表2にその結果を示す。
(色特性の評価)
ガラス基板上にC光源においてx=0.150、y=0.060になるような膜厚にレジスト材を塗布し、この基板を230℃で20分加熱した。その後、得られた基板の明度(Y)を顕微分光光度計(オリンパス光学社製「OSP−SP200」)で測定した。
以下、表2にその結果を示す。
ガラス基板上にC光源においてx=0.150、y=0.060になるような膜厚にレジスト材を塗布し、この基板を230℃で20分加熱した。その後、得られた基板の明度(Y)を顕微分光光度計(オリンパス光学社製「OSP−SP200」)で測定した。
以下、表2にその結果を示す。
(塗膜耐熱性試験の方法)
透明基板上に乾燥塗膜が約2.5μmとなるようにレジスト材を塗布し、所定のパターンを有するマスクを通して紫外線露光を行った後、スプレーによりアルカリ現像液を噴霧して未硬化部を除去して所望のパターンを形成した。その後、オーブンで230℃20分加熱、放冷後、得られた塗膜のC光源での色度1(L*(1),a*(1),b*(1))を顕微分光光度計(オリンパス光学社製「OSP−SP200」)を用いて測定した。さらにその後、耐熱試験としてオーブンで250℃1時間加熱し、C光源での色度2(L*(2),a*(2),b*(2))を測定した。以下、表2にその結果を示す。
透明基板上に乾燥塗膜が約2.5μmとなるようにレジスト材を塗布し、所定のパターンを有するマスクを通して紫外線露光を行った後、スプレーによりアルカリ現像液を噴霧して未硬化部を除去して所望のパターンを形成した。その後、オーブンで230℃20分加熱、放冷後、得られた塗膜のC光源での色度1(L*(1),a*(1),b*(1))を顕微分光光度計(オリンパス光学社製「OSP−SP200」)を用いて測定した。さらにその後、耐熱試験としてオーブンで250℃1時間加熱し、C光源での色度2(L*(2),a*(2),b*(2))を測定した。以下、表2にその結果を示す。
測定した色差値を用いて、下記計算式により、色差ΔEab*を算出し、塗膜の耐熱性を下記の4段階で評価した。
ΔEab* = √((L*(2)- L*(1))2+ (a*(2)- a*(1)) 2+( b*(2)- b*(1)) 2)
◎:ΔEab*が1.5未満
○:ΔEab*が1.5以上、2.5未満
△:ΔEab*が2.5以上、5.0未満
×:ΔEab*が5.0以上
以下、表2にその結果を示す。
ΔEab* = √((L*(2)- L*(1))2+ (a*(2)- a*(1)) 2+( b*(2)- b*(1)) 2)
◎:ΔEab*が1.5未満
○:ΔEab*が1.5以上、2.5未満
△:ΔEab*が2.5以上、5.0未満
×:ΔEab*が5.0以上
以下、表2にその結果を示す。
(塗膜耐光性試験の方法)
塗膜耐熱性試験と同じ手順で試験用基板を作製し、C光源での色度1(L*(1),a*(1),b*(1))を顕微分光光度計(オリンパス光学社製「OSP−SP200」)を用いて測定した。その後、基板を耐光性試験機(TOYOSEIKI社製「SUNTEST CPS+」)に入れ、500時間放置した。基板を取り出した後、C光源での色度2(L*(2),a*(2),b*(2))を測定し、塗膜耐熱性試験と同様にして色差ΔEab*を算出し、耐熱性と同様の基準により塗膜の耐光性を評価した。以下、表2にその結果を示す。
塗膜耐熱性試験と同じ手順で試験用基板を作製し、C光源での色度1(L*(1),a*(1),b*(1))を顕微分光光度計(オリンパス光学社製「OSP−SP200」)を用いて測定した。その後、基板を耐光性試験機(TOYOSEIKI社製「SUNTEST CPS+」)に入れ、500時間放置した。基板を取り出した後、C光源での色度2(L*(2),a*(2),b*(2))を測定し、塗膜耐熱性試験と同様にして色差ΔEab*を算出し、耐熱性と同様の基準により塗膜の耐光性を評価した。以下、表2にその結果を示す。
(塗膜耐溶剤性試験の方法)
耐熱性試験と同じ手順で試験用基板を作製し、C光源での色度1(L*(1),a*(1),b*(1))を顕微分光光度計(オリンパス光学社製「OSP−SP200」)を用いて測定した。その後、基板をN−メチルピロリドンに30分間浸漬した。基板を取り出した後、C光源での色度2(L*(2),a*(2),b*(2))を測定し、塗膜耐熱性試験と同様にして色差ΔEab*を算出し、耐熱性と同様の基準により塗膜の耐溶剤性を評価した。以下、表にその結果を示す。
耐熱性試験と同じ手順で試験用基板を作製し、C光源での色度1(L*(1),a*(1),b*(1))を顕微分光光度計(オリンパス光学社製「OSP−SP200」)を用いて測定した。その後、基板をN−メチルピロリドンに30分間浸漬した。基板を取り出した後、C光源での色度2(L*(2),a*(2),b*(2))を測定し、塗膜耐熱性試験と同様にして色差ΔEab*を算出し、耐熱性と同様の基準により塗膜の耐溶剤性を評価した。以下、表にその結果を示す。
実施例9〜14のレジスト材(R−1〜6)は、保存安定性、耐溶剤性、現像性、耐熱性、耐光性が良好でカラーフィルタとして使用可能な範囲にあった。一方、比較例1,2のレジスト材(R−7、8)は耐溶剤性が悪く、比較例3のレジスト材(R−9)は保存安定性、現像性が悪いため、カラーフィルタとして使用可能な品位には達しなかった。これにより、着色剤が、有機顔料と、キサンテン系酸性染料が四級アンモニウム塩化合物で造塩された化合物(A)であり、熱架橋性成分が三官能以上の多官能エポキシ樹脂であるカラーフィルタ用着色樹脂組成物が、保存安定性、現像性に優れ、耐溶剤性、耐熱性、耐光性に優れたカラーフィルタを提供できることは明らかである。
Claims (5)
- 着色剤と、光重合開始剤と、有機溶剤と、アルカリ可溶性樹脂と、光重合性化合物と、熱架橋性成分とからなるカラーフィルタ用着色樹脂組成物であって、
着色剤が、有機顔料と、キサンテン系酸性染料が四級アンモニウム塩化合物で造塩された化合物(A)とからなり、
熱架橋性成分が、三官能以上の多官能エポキシ樹脂であることを特徴とするカラーフィルタ用着色樹脂組成物。 - キサンテン系酸性染料が、C.I.アシッド レッドに分類されるものであることを特徴とする請求項1に記載のカラーフィルタ用着色樹脂組成物。
- キサンテン系酸性染料が、C.I.アシッド レッド 52、および、C.I.アシッド レッド 289のいずれか1つであることを特徴とする請求項1または2に記載のカラーフィルタ用着色樹脂組成物。
- 少なくとも1つの赤色フィルタセグメント、少なくとも1つの緑色フィルタセグメントおよび少なくとも1つの青色フィルタセグメントを備えるカラーフィルタにおいて、少なくとも1つのフィルタセグメントが、請求項1〜4いずれかに記載のカラーフィルタ用着色樹脂組成物により形成されてなるカラーフィルタ。