JP2011201325A - 合板及び化粧合板 - Google Patents
合板及び化粧合板 Download PDFInfo
- Publication number
- JP2011201325A JP2011201325A JP2011158003A JP2011158003A JP2011201325A JP 2011201325 A JP2011201325 A JP 2011201325A JP 2011158003 A JP2011158003 A JP 2011158003A JP 2011158003 A JP2011158003 A JP 2011158003A JP 2011201325 A JP2011201325 A JP 2011201325A
- Authority
- JP
- Japan
- Prior art keywords
- plywood
- resin
- layer
- thin plates
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】木質薄板を積層してなる合板であって、
(1)隣接する木質薄板どうしはいずれも接着されており、
(2)少なくとも最上層及び最下層の木質薄板は、熱硬化性樹脂と繊維質材料とを含む接着材層を介して、それぞれ隣接する木質薄板と接着されている、
ことを特徴とする合板。
【選択図】なし
Description
(1)隣接する木質薄板どうしはいずれも接着されており、
(2)少なくとも最上層及び最下層の木質薄板は、熱硬化性樹脂と繊維質材料とを含む接着材層を介して、それぞれ隣接する木質薄板と接着されている、
ことを特徴とする合板。
2.前記繊維質材料が、1)ポリエステル、ナイロン、レーヨン、ポリプロピレン、芳香族ポリアミド又はガラスからなる不織布、2)ポリエステル、ケブラー、ナイロン、ガラス、レーヨン、綿及びアセテートの少なくとも1種からなる織物、3)クラフト紙、和
紙又はクレープ紙、並びに、4)ポリエステル、ナイロン、レーヨン、ポリプロピレン、芳香族ポリアミド又はガラスからなるチョップドファイバー、からなる群から選択される少なくとも1種である、上記項1に記載の合板。
3.前記熱硬化性樹脂が、フェノール樹脂、ユリア樹脂、メラミン樹脂、ダップ樹脂、不飽和ポリエステル樹脂、アルキド樹脂及びエポキシ樹脂からなる群から選択される少なくとも1種である、上記項1又は2に記載の合板。
4.前記木質薄板の材質が、植林材、針葉樹及び雑木材からなる群から選択される少なくとも1種である、上記項1〜3のいずれかに記載の合板。
5.合板表面に、熱可塑性樹脂を含む表面保護層をさらに有する、上記項1〜4のいずれかに記載の合板。
6.合板表面に、熱硬化性樹脂と繊維質材料とを含む表面保護層をさらに有する、上記項1〜4のいずれかに記載の合板。
7.上記項1〜6のいずれかに記載の合板に化粧シートを積層してなる化粧合板。
以下、本発明合板及び化粧合板について詳細に説明する。
本発明合板は、木質薄板を積層してなる合板であって、
(1)隣接する木質薄板どうしはいずれも接着されており、
(2)少なくとも最上層及び最下層の木質薄板は、熱硬化性樹脂と繊維質材料とを含む接着材層を介して、それぞれ隣接する木質薄板と接着されている、
ことを特徴とする。
それぞれ隣接する木質薄板と接着されている。
本発明化粧合板は、前記合板に化粧シートを積層してなる。
発明では、環境問題、被印刷面との接着性等を考慮すると、ポリエステル、イソシアネートとポリオールからなるポリウレタン、ポリアクリル、ポリアミド系樹脂等の1種又は2種以上混合したものである。なお、ワイピングインキについても、上記で説明した絵柄層に用いるインキと同じインキで形成することができる。
紫外線、電子線等を用いることが望ましい。紫外線源としては、超高圧水銀灯、高圧水銀灯、低圧水銀灯、カーボンアーク灯、ブラックライト蛍光灯、メタルハライドランプ灯の光源が使用できる。紫外線の波長としては、190〜380nm程度の波長域を使用することができる。また、電子線源としては、例えば、コッククロフトワルト型、バンデグラフト型、共振変圧器型、絶縁コア変圧器型、直線型、ダイナミトロン型、高周波型等の各種電子線加速器を用いることができる。用いる電子線としては、一般に100〜1000keV程度、好ましくは100〜300keVのものを使用することができる。電子線の照射量は、通常2〜15Mrad程度とすればよい。
MLH材(広葉樹であるが、樹木種類を問わない仕様)をロータリーレースで裁断し、下記5枚の木質薄板を作製した。
第2層用薄板:3.4mm
第3層用薄板:3.4mm
第4層用薄板:3.4mm
第5層用薄板:1.3mm
これらの薄板を130℃で乾燥し、含水率を10%以下とした。
樹種を針葉樹(カラ松)に変えた以外は、実施例1と同様にして合板を製造した。
針葉樹(カラ松)をロータリーレースで裁断し、下記5枚の木質薄板を作製した。
第2層用薄板:3.4mm
第3層用薄板:3.4mm
第4層用薄板:3.4mm
第5層用薄板:1.3mm
これらの薄板を130℃で乾燥し、含水率を10%以下とした。
針葉樹(カラ松)をロータリーレースで裁断し、下記5枚の木質薄板を作製した。
第2層用薄板:3.4mm
第3層用薄板:3.4mm
第4層用薄板:3.4mm
第5層用薄板:1.3mm
これらの薄板を130℃で乾燥し、含水率を10%以下とした。
実施例及び比較例で製造した合板の第1層側と、床材用化粧シート(0.16mm厚、大日本印刷株式会社製)とをPUR系(湿気硬化型)接着剤を約40g/m2(硬化時)用いてラミネートした。
床用化粧材の鉛筆硬度を測定した。試験は、JIS K5400に従って行った。
床用化粧材(1尺×6尺)を、温度5℃、湿度30%で1週間放置後、更に温度40℃、湿度90%で1週間放置した。次いで、床用化粧材の反り・ねじれの有無を肉眼により確認した。
と評価した。
Claims (7)
- 木質薄板を積層してなる合板であって、
(1)隣接する木質薄板どうしはいずれも接着されており、
(2)少なくとも最上層及び最下層の木質薄板は、熱硬化性樹脂と繊維質材料とを含む接着材層を介して、それぞれ隣接する木質薄板と接着されている、
ことを特徴とする合板。 - 前記繊維質材料が、1)ポリエステル、ナイロン、レーヨン、ポリプロピレン、芳香族ポリアミド又はガラスからなる不織布、2)ポリエステル、ケブラー、ナイロン、ガラス、レーヨン、綿及びアセテートの少なくとも1種からなる織物、3)クラフト紙、和紙又はクレープ紙、並びに、4)ポリエステル、ナイロン、レーヨン、ポリプロピレン、芳香族ポリアミド又はガラスからなるチョップドファイバー、からなる群から選択される少なくとも1種である、請求項1に記載の合板。
- 前記熱硬化性樹脂が、フェノール樹脂、ユリア樹脂、メラミン樹脂、ダップ樹脂、不飽和ポリエステル樹脂、アルキド樹脂及びエポキシ樹脂からなる群から選択される少なくとも1種である、請求項1又は2に記載の合板。
- 前記木質薄板の材質が、植林材、針葉樹及び雑木材からなる群から選択される少なくとも1種である、請求項1〜3のいずれかに記載の合板。
- 合板表面に、熱可塑性樹脂を含む表面保護層をさらに有する、請求項1〜4のいずれかに記載の合板。
- 合板表面に、熱硬化性樹脂と繊維質材料とを含む表面保護層をさらに有する、請求項1〜4のいずれかに記載の合板。
- 請求項1〜6のいずれかに記載の合板に化粧シートを積層してなる化粧合板。