JP2011068130A - Textile seal, textile sheet, seal, adhesive sheet, and method of manufacturing the same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a new technology in a seal and an adhesive sheet. <P>SOLUTION: The seal 10 comprises a substrate 100 and an adhesive 200. The substrate is, for example, a textile. Further, the substrate is provided with a separator 300 covering the adhesive 200. The textile seal is provided with an anchor material between the textile 100 and the adhesive 200, and furthermore, a complementary sheet and a second adhesive between the adhesive 200 and the separator 300. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

  The present invention relates to a fabric seal, a fabric sheet, a seal, an adhesive sheet, and a method for producing the same.

  Conventionally, it has been desired to develop products using textiles. For example, in the silk fabric industry, while the kimono market cannot be expected to grow significantly, an effective measure for reducing the demand for silk fabric is desired. In addition, new technologies for sealing and adhesive sheets are desired.

  An object of an aspect of the present invention is to provide a technique that can be applied to the development of products using fabrics. Moreover, it aims at providing the technique which can promote utilization of a silk fabric. Moreover, it aims at providing the new technique in a seal | sticker and an adhesive sheet.

  According to an aspect of the present invention, a fabric seal including a fabric and an adhesive material is provided.

  According to another aspect of the present invention, there is provided a fabric sheet comprising a fabric and means for attaching the fabric to another object.

  According to another aspect of the present invention, there is provided a method for producing a fabric seal or fabric sheet, comprising the steps of providing a fabric and providing the fabric with means for attaching the fabric to another object. The

  According to another aspect of the present invention, a woven fabric, an adhesive material disposed on one surface of the woven fabric, and affixed to the one surface of the woven fabric via the adhesive material, wherein at least a part of the adhesive material is There is provided a fabric seal comprising a separator that can be removed from the one side of the fabric while remaining on the one side of the fabric.

  According to another aspect of the present invention, the base material, the auxiliary sheet, the separator, the first adhesive material disposed between the base material and the auxiliary sheet, and between the auxiliary sheet and the separator. And a second adhesive material disposed on the surface.

  According to another aspect of the present invention, a base material, a supplementary sheet, a first adhesive material disposed between the base material and the supplementary sheet, and a surface opposite to the first adhesive material And an adhesive sheet provided with a second pressure-sensitive adhesive material disposed on one surface of the auxiliary sheet.

It is a cross-sectional schematic diagram which shows a fabric seal (woven fabric sheet). It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the whole shape of a fabric seal. It is a figure which shows the example of the anchor process with respect to a textile fabric. It is a figure which shows the example of the anchor process with respect to a textile fabric. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows the example of the structure | tissue structure of a textile fabric typically. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically the example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows the example of arrangement | positioning of an adhesive material. It is a figure which shows the example of arrangement | positioning of an adhesive material. It is a figure which shows the example of arrangement | positioning of an adhesive material. It is a figure which shows the example of the form of a separator. It is a figure which shows the example of the form of a separator. It is a figure which shows the example of the form of a separator. It is a figure which shows the example of the form of a separator. It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows the example which attached the fabric seal (woven fabric sheet) to the target object. It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows typically the example of an embodiment provided with the auxiliary sheet | seat in which the folding kei was formed. It is a figure which shows typically the form example provided with the adhesive material of multiple layers. It is a schematic diagram which shows the example which peels a textile fabric from a target object by delamination. It is a schematic diagram which shows the example which peels a textile fabric from a target object. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the manufacturing process of a textile fabric seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows typically an example of the expanded cross-section of a textile seal. It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows another example of a fabric seal | sticker (woven fabric sheet). It is a figure which shows the example of arrangement | positioning of a supplement (reinforcement part). It is a figure which shows an example of the process for providing UV curable resin to a textile fabric. It is a figure which shows another example of the process for providing UV curable resin to a textile fabric. It is a figure which shows another example for the partial process of a textile fabric. It is a figure which shows another example for the partial process of a textile fabric. It is a figure which shows another example for the partial process of a textile fabric. It is a figure which shows another example for the partial process of a textile fabric. It is a figure which shows another example for the partial process of a textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows the example of the form which strengthened the cutting part of the textile fabric. It is a figure which shows an example of the surface in a fabric seal (woven fabric sheet). It is a figure which shows another example of the surface in a fabric seal (woven fabric sheet). It is a figure which shows another example of the surface in a fabric seal (woven fabric sheet). It is a figure which shows the example by which the fabric seal | sticker (woven fabric sheet) was applied as a thousand company bill and an exchange bill. It is a figure which shows the example by which the textile seal (woven fabric sheet) was applied as a label for alcoholic beverage containers. It is a figure which shows the example in which the textile seal (woven fabric sheet) was applied as another container label.

  Embodiments of the present invention will be described below with reference to the drawings. In each drawing referred to in the following description, in order to make the drawing easy to see, the dimensions of each constituent member are changed or partly omitted as necessary.

  FIG. 1 is a view showing a fabric seal (fabric sheet) 10. In FIG. 1, a fabric seal (fabric sheet) 10 includes a fabric 100, an adhesive material (attachment material, bonding material, adhesive material) 200, and a separator (release layer, release sheet, mount, protective sheet) 300.

  In one embodiment, the adhesive material 200 is disposed on one side of the fabric 100. The separator 300 is disposed on the one surface of the fabric 100 through the adhesive material 200. That is, in one embodiment, the fabric seal 10 has at least a three-layer structure including the fabric 100, the adhesive material 200, and the separator 300. An adhesive material 200 is disposed between the fabric 100 and the separator 300. The fabric 100 is disposed on one side of the adhesive material 200, and the separator 300 is disposed on the other side.

  As will be described later, the fabric seal (fabric sheet) 10 is not limited to a substantially three-layer structure. Alternatively or additionally, the substantial number of layers of the fabric seal (fabric sheet) 10 is 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15 16, 17, 18, 19, 20, or more. In other words, the fabric seal (woven fabric sheet) 10 includes layers 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14 in addition to a single layer of the fabric 100. , 15, 16, 17, 18, 19, or more layers.

  In one embodiment, it is possible to remove (peel) at least a portion of the separator 300 from one side of the fabric 100 while leaving the adhesive material 200 on one side of the fabric 100. In the fabric seal 10 from which the separator 300 is removed, at least a part of the adhesive material 200 is exposed. The fabric seal 10 can be attached to the object 500 through the exposed adhesive material 200. For example, by bringing the adhesive material 200 having adhesiveness into contact with the object 500, the fabric seal 10 from which the separator 300 has been removed can be attached to the object 500 using the adhesive force of the adhesive material 200.

  In one embodiment, the fabric 100 may have at least one of a color, a pattern, a character, a design, and the like. In the fabric 100 attached to the object 500, at least one of its color, shadow, pattern, character, pattern, and the like can be observed. The fabric 100 can typically include a silk fabric, a wool fabric, a cotton fabric, a hemp fabric, a chemical fiber fabric, and the like. In addition, the fabric 100 can include a pre-dyed fabric and / or a post-dyed fabric.

  In the fabric seal 10 attached to the object 500, the fabric 100 has a first surface 102 disposed on the space side and a second surface 104 disposed on the object 500 side. In one example, the fabric 100 is observed from the side opposite to the object 500. In this case, the first surface 102 of the fabric 100 faces the observation side space. In another example, the fabric 100 is observed through an object 500 that has substantial transparency and / or has an observation window. That is, the second surface 104 of the fabric 100 is observed from the object 500 side. In this case, the second surface 104 of the fabric 100 faces the observation side space through the object 500. In yet another example, both sides of the fabric 100 are observed. That is, the first surface 102 of the fabric 100 is observed from the opposite side of the object 500, and the second surface 104 of the fabric 100 is observed through the object 500 having substantial transparency and / or having an observation window. Is done. In one embodiment, the adhesive material 200 is disposed on the second surface 104 of the fabric 100. That is, the adhesive material 200 is disposed between the fabric 100 and the object 500.

  In one embodiment, by attaching the fabric seal (fabric sheet) 10 to the object 500, the appearance characteristics and functional characteristics of the fabric seal 10 can be imparted to the object 500. For example, at least one appearance such as the color, shading, pattern, character, and design of the fabric 100 is imparted to the object 500. Alternatively, the fabric seal 10 contributes to the development of functions other than the appearance of the object 500 to which the fabric seal 10 is attached. The use of the fabric 100 is promoted by increasing the number of objects 500 to which the fabric seal 10 is attached. For example, when the fabric 100 is a silk fabric, the silk fabric 100 contributes to the eye-catching appearance of the object 500 to which the fabric seal 10 (silk fabric seal 10) is attached. Alternatively, the silk fabric seal 10 contributes to the development of functions other than the appearance of the object 500 to which the silk fabric seal 10 is attached. The use of the silk fabric 100 is promoted by increasing the number of objects 500 to which the silk fabric seal 10 is attached.

  In another embodiment, a seal (adhesive sheet) 10 including a base material 100 other than a fabric, an adhesive material (attachment material) 200, and a separator (release layer, release sheet, mount, protective sheet) 300 is provided. it can. Examples of the substrate 100 other than the woven fabric include cloth other than the woven fabric and Japanese paper. The substrate 100 can include a permeable material, a liquid-absorbing material, or a porous material. Here, the cloth is a plate-like or sheet-like member made of fiber (natural fiber, chemical fiber) or the like, and includes various types. For example, the fabric includes woven fabric, non-woven fabric, felt, knitted fabric, lace, and the like. Various materials can be used as the material of the cloth, for example, cotton, silk, hemp, mohair, wool, cashmere, chemical fiber (for example, acetate, cupra, rayon, recycled polyester, nylon, polyurethane, polyester, Fistop) Etc.). Examples of the nonwoven material include nylon fiber, polyolefin fiber, silk fiber, rayon fiber, vinylon fiber, glass fiber, and aramid fiber. As the base material 100, the above materials may be used alone or in combination. The cloth and the material thereof are not limited to the above example.

  In addition, the cloth is denim, fleece, velvet, toweling, suede, corduroy, linen, satin, cotton satin, gauze, double gauze, gingham, cotton voile, cotton twill, organge, yanagi (yoryu), oblique weaving, Crepe, flannel, pile, velvet, flannel, betting, velor, canvas, blanket, rasha, carako, stretch broad, exposed, sheeting, chiffon, shantung, georgette, new moss, broad, voile, muslin, linen mask, waffle weave , Calling, yellow Hachijo, Shiose, upper cloth, cocoon, chirimen (shrinking), Nishijin, Hadane, Fuji silk, Honshu, meisen, cotton candy, yukata, rinzu, silk thread, Core yarn, shearing, chambray, stretch, slab, ripple, plain fabric, twill fabric Or a satin fabric. These may be used alone or in combination. The cloth and the material thereof are not limited to the above example.

The object 500 to which the fabric seal (woven fabric sheet) 10 is attached can be any object having an attachment surface. Examples of the object 500 include stationery and auxiliary tools (for example, writing tools, notebooks, memo paper, notebooks, recording tools, staplers, scissors, sticky notes, envelopes, postcards, letter papers, storage tools, etc.), containers and boxes (for example, Food containers, bottles, glass containers, glasses, cans, tin containers, resin bottles, paper boxes, paper cups, wooden boxes, cloth boxes, trash cans, etc., mobile devices and their accessories (for example, mobile phones, mobile terminals, mobile games) Machine, etc.), electrical products and accessories (for example, various home appliances, personal computers, audio equipment, video equipment, photographing equipment, game equipment, communication equipment, lighting equipment, lamps, etc.), recording media and accessories ( For example, DVD (Digital Versatile Disc), MD (Magnetic Disk), CD (Compact Disk), BD (Blue-ray Disk), FD (Floppy Disk (registered trademark)), flash memory, Tape, cassette tape, etc.), machinery (eg, cameras, watches, musical instruments, telephones, etc.), clothing / garment accessories and accessories (eg, clothes, underwear, shoes, belts, handkerchiefs, bags, ties, glasses, etc.) Hair ornaments, hairpins, jewelry, etc.), ornaments (eg, frames, ornaments, jewelry, glass plates), cosmetics and accessories (eg, mirrors, cosmetic containers, cosmetic packages, etc.), kitchenware ( For example, dishes, cooking utensils, pans, storage utensils, cooking aids, etc.), medical products (eg, drug packages, masks, bandages, bandages, aids, etc.), articles related to shrines and temples (eg, fortune, amulet, ema) , Godshelves, bills, thousand company tags (tags, title tags, color tags, exchange tags, exchange bills), other lucky charms), and other daily necessities (eg, toys, dolls, crafts, pet supplies, restrooms) Equipment / Toiletries, Cleaning Tools, Exercise Equipment, Exercise Equipment, Learning Tools, Fans, Fans, etc.), Vehicles and Accessories (eg, Bus, Taxi, Train, Ship, Airplane, Truck, Car, Bicycle, etc.), Stage Sets and stage equipment (stage tools, stage costumes, stage decorations, etc.), structures and decorations for stadiums and dojos, banners (table climbers, carp streamers, etc.), table decoration supplies, transportation network components, architecture Things / Buildings, Public Facilities, Vending Machines / Cash Handling Devices (eg, vending machines, cash dispensers, etc.), signboards, walls (wall materials), floors (floor materials), ceilings (ceiling materials), windows (windows) Members, frame members), shelves, furniture, tables, chairs, bedding, books, newspapers, magazines, brochures, calendars, business cards, business cards, etc. In particular, it is known to be used for maiko, geisha, geisha, geisha, performing arts parties and the like. Also called color tags, exchange tags, exchange bills, flower business cards. ), Name tag, paper, wrapping paper, various tickets, menu table, various cards, plants, flowers (fresh flowers, artificial flowers), human body (cheek, nose, mouth, forehead, heel, ear, chin, head, neck, shoulder, Arm, wrist, chest, back, palm, back of hand, finger, hand nail, waist, buttocks, leg, knee, ankle, instep, toe, palm of palm, toenail, etc.) , Construction site partitions, guide plates, etc. The fabric seal 10 can be applied as a specific seal in which the object 500 is specified or as a free seal in which the object 500 and its use are not specified. The fabric seal (fabric sheet) 10 includes, for example, souvenir goods seals, wrapping seals, decoration seals, outdoor seals, bonding tapes, sticky notes, labels (product labels, information labels, price tags, etc.), stickers, emblems, insignia (emblems) ), Puzzles, pennants, flame retardant sheets, fire prevention sheets, quasi-drugs, shrines and temples related items (Omikuji, Amulet, Ema, Shinto Shelf, bills, Sensha bills (stickers, title tags, color tags, exchange tags, exchange bills) ), Other auspicious items), Sensha bill (used as a business card substitute, etc. Especially, it is known to be used for Maiko, Geiko, Geisha, Geisha, entertainment related parties, etc. Color tags, exchange tags, exchange bills, It is also called a flower business card.) Can be widely applied as a decorative material. The object 500 to which the fabric seal (fabric sheet) 10 is attached and the application object of the fabric seal (fabric sheet) 10 are not limited to the above examples. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  In one embodiment, the silk fabric 100 can be used as the fabric 100. In this case, by attaching the silk fabric seal (silk fabric sheet) 10 to the object 500, the appearance characteristics and functional characteristics of the silk fabric 100 can be imparted to the object 500.

  The silk fabric 100 has a structure in which warp yarns (warp yarns) and weft yarns (weft yarns) each made of silk yarn are interlaced. In general, warp yarns are arranged along the length of the fabric during weaving, and weft yarns are arranged along the width direction. The repetition of the predetermined pattern of crossings constitutes a fabric structure. In general, in a woven fabric, a unit structure constituting the woven structure is repeated. Note that the basic minimum organization is sometimes called a complete organization. In addition, the intersection between the warp and the weft may be referred to as a texture point. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the raw yarn (silk yarn, raw yarn) used for the silk fabric 100 includes natural fibers made from silkworms. Morphological characteristics such as the double structure, cross-sectional shape, and curvilinearity of the tissue of natural silk contribute to the appearance and functional characteristics of silk fabric 100 such as texture, dyeability, and gloss. The texture of the silk fabric 100 can include at least one element such as elastic smoothness, hardness, resilience (strain), tension (bending strength), and thickness (bulge). The texture generally differs between the pre-kneaded fabric and the post-kneaded fabric based on the fiber structure. Silk yarn is glossy, color, dyeable, stretchable, hygroscopic / breathable, low-charged, wrinkle-proof, flame retardant, UV-cut, antibacterial, oxidation-resistant, and substance-absorbing It can have functions such as gas absorptivity and metal adsorption. In another embodiment, a silk fabric can be formed using a composite material combining a natural fiber silk thread and another material. Additionally, a predetermined treatment can be applied to the silk thread or silk fabric 100.

  In one embodiment, at least part of the silk thread of the silk fabric 100 can be made of a material other than silk. For example, silk yarn can be used for the warp or weft, and materials other than silk (for example, chemical fiber, paper-based color yarn (for example, gold thread, silver thread)) can be used for the weft thread or warp.

  In one embodiment, the silk fabric 100 may include at least one of a pre-dyed fabric (pre-kneaded fabric) and a post-dyed fabric (post-kneaded fabric). The production of a pre-dyed fabric includes processes such as twisting, refining / dying, weaving, and finishing. The production of post-dyed fabric includes, for example, processes such as twisting, weaving, refining / finishing, and dyeing / finishing. In the twisting process, the twist direction (right twist, left twist) and the strength of the twist (sweet twist, parallel twist, strong twist) are appropriately set. The twisted yarn structure can include, for example, at least one of a single twisted yarn, a plied yarn, a piece twisted yarn, a decorative twisted yarn, and a wall twisted yarn. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric structure of the silk fabric 100 may have at least one of a plain weave, a twill weave (twill weave), a satin weave, and a change texture (change plain weave, change twill weave, change satin weave). . Plain weave, oblique weave, and satin weave are called Mihara organization. The oblique weave includes a double-faced oblique weave, a one-sided oblique weave, a three-face oblique weave, a four-face oblique weave, a five-face oblique weave, and / or six or more oblique cloths. The satin weave includes fresh satin weave, weft satin weave, 5 satin weave, 6 satin weave, 7 satin weave, and / or 8 or more satin weaves. Change plain weave is woven weave, woven weave, yokoune weave, change ridge weave, Yoshino weave, fresh Yoshino weave, yoko Yoshino weave, Shijira weave (Awa Shijira), Nanako weave, It includes a modified weave weave, a knot weave, and / or a facing weave. Changed weave fabrics: Stretch fabrics, Steep fabrics, Slow fabrics, Magari fabrics, Torn fabrics, Turkish satin (4 sheets), Herringbone, Overlapping fabrics, Ajiro Seibun weave, Yamagata Seibun weave, Yamagata Seibun weaving, Yamagata Seibun weave, rhombus Seibun weaving, Flying oblique weaving, Yoriyomonbun weaving, Tateyoyoori weaving weaving, Yokoyoori weaving weaving, It includes a twisted weave, a day / night oblique weave, a blurred oblique weave, and / or a decorative oblique weave. The changing satin weave includes irregular satin weaving, Hiroge satin, layered satin weaving, mikage satin weaving, day and night satin weaving, and / or blurred satin weaving. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the woven structure of the silk fabric 100 may be a woven weave (brighton woven, special woven weave, sponge woven), gray cyan woven, hack woven, imitation woven, and plain woven as required. At least one of the following. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric texture of the silk fabric 100 can include a partial reinforcing tissue, if desired. The partial reinforcing structure can include an edge reinforcing structure (end-processed tissue) that reinforces at least a part of the silk fabric 100 near the edge or substantially the entire periphery of the edge. The partial reinforcing tissue can include so-called selvedge weave. The partial reinforcing structure can be provided on at least a part of the silk fabric 100. For example, a woven fabric (for example, an ear) different from other parts can be provided on a part or the entire periphery near the edge of the silk fabric 100. In addition, a woven fabric (for example, an ear) different from other portions can be provided in the vicinity of the corner of the silk fabric 100. The partial reinforcement structure in the silk fabric 100 may have a dense structure and / or a thick thread structure as compared to other parts. The partial reinforcing structure is advantageous for improving the appearance and reinforcing the silk fabric. For example, the partial reinforcing structure is advantageous in preventing fraying of the end face (edge) in the silk fabric 100. As the partial reinforcing structure, for example, plain weave, ridge weave, and / or oblique weave can be used. The ear tissue can include at least one of a plain weave ear, a yolk woven ear, a Nanako weave ear, a twill ear weave, a pillow ear, and a bag ear. Alternatively or additionally, at least a portion of the partial reinforcing tissue can be provided at a portion other than the edge. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the pattern of the silk fabric 100 in the pre-dyed fabric is represented based on the combination of the fabric texture and the warp / weft color yarn arrangement (color effect). Silk fabric 100 patterns include, for example, pin head (end and end cross, fine deer lattice), hairline, two and two check, shark skin, hound tooth, shepherd check, glen check, bird's eye, and At least one of the star checks can be included. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric texture of the silk fabric 100 can include a layered tissue. The layered structure consists of a single layered structure using two or more types of warp or weft, double weaving using two types of warp and weft, and multilayer weaving using three or more types of warp and weft. At least one of the following. The one-ply structure includes a weft double weave using two types of weft yarns and / or a warp double weave using two types of warp yarns. The weft double weave includes a weft double backing weave, a weft double-sided weave, and / or a shined weft double weave. Warp double weaves include warp double backing weaves, warp double double weaves, and / or lined double weaves. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the double weave can include a bonded double weave. In the case of weaving two woven fabrics on the front and back sides, the bonded double weaving is a single woven fabric in which two woven fabrics are brought into close contact with each other using part of the front and back yarns. The binding double weave includes ordinary binding double weaving, back warp binding double weaving, back weft binding double weaving, and / or double binding double weaving. The double weave can also include a centrally bonded double weave. In the center-bound double weave, another thread is used for binding. Center-bound double weave is center warp-bound double weave, center weft-bound double weave, center-bound double-weave, weft-bound back warp-bound double weave, and / or warp Including double weft with double weft. The double weave can also include a backing double weave. The backed double weave includes a weft backed double weave and / or a warp backed double weave. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the multi-woven can include 3, 4, 5, or 6 or more layers. Multiple weaves include a bonded multi-layer weave, a central warp-bound multi-layer weave, and / or a central weft-bound multi-layer weave. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric structure of the silk fabric 100 is a bag weave, an air-weaving fabric, a weave weave, a mesh weave, a Toriko weave, a picket, a fold weave, a Bedford cord weave, a crepon, an oblique cord weave, a crest cord weave, and a contact weave. It may include at least one knotted double weave. The bag weave usually includes a bag, a side bag, and / or a multiple bag weave. The wind woven includes a double two-color wind woven, a double three-color wind woven, a double four-color wind woven, a triple three-color wind woven, and / or a triple nine-color wind woven. The weaving weave includes weft weaving, weaving weaving, and / or weft weaving weaving. Trico weave includes warp trico weave and / or weft trico weave. Picks include simple picks, shinned picks, fast back picks, loose back picks, and / or crest picks. Bedford cord weave includes plain bedford cord weave, oblique table bedford cord weave, and / or bedded cord weave. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric texture of the silk fabric 100 can include a pile weave including a weft pile and / or a fresh pile weave. The weft pile weave includes bevel, cole heaven and / or weave plush. The rarities include rarities by plains, rarities by oblique lines, and / or rarities by both sides. The call sky includes a flat land call sky, a scalloped call sky, and / or a double-sided call sky. The horizontal plush includes double sided positive plush. Warp pile fabric includes towel tissue, velvet tissue, double velvet tissue, and / or plush. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric texture of the silk fabric 100 can include entangled tissue. The entangled tissue can include at least one of a spider, a spear, and a bran. A kite includes a kannon kite, a two-fold kite, a three-print kite, a crest kite, a literary kite, and / or a musou. A kite includes a flat kite, a twill kite, a kite, a kite, a slant kite, a kite, a checkered kite, a three-clad kite, a four-clad kite, a vertical kite, a square kite, and / or a mud. The twills include three twills, one raku twills, and / or nobles twills. Luo includes mesh, brood, horo, and / or bunra. The same applies to woven fabrics other than silk fabric.

  In one embodiment, the fabric structure of the silk fabric 100 is spelled, freshly nished, horizontal nishiki, donko, shuchin, shoha, futsu, and tangle weave. Woven), velvet, main grain weave, woven weave, and cocoon. These 12 items are included in Nishijin Ori's designated varieties. Freshly nishiki includes flat shinnishiki and / or obliquely shinnishiki. Yoko Nishiki includes latitude brocade, Yamato brocade (Kinki brocade), kara-ori and / or brocade. The insulator includes an insulator band and / or an insulator back. The introduction includes an introduction and / or introduction zone. The same applies to woven fabrics other than silk fabric.

  In one embodiment, in addition to the above, the silk fabric 100 is made of lion, lantern, habutae, rinzu, summon, meisen, oshima, spell It can include various woven fabrics such as Nishiki and Hakataori. Chirimen is a woven fabric made by plain weaving silk, and is manufactured by alternately weaving warp yarns having substantially no twist and weft yarns having a strong twist, and then refining. The surface of the fabric has fine wrinkles (unevenness). The unevenness of the grain leads to irregular reflection of light. Shibo can contribute to the richness of the silk fabric 100 texture and dyed color. Crimping is excellent in wrinkle resistance. The same applies to woven fabrics other than silk fabric.

  In one embodiment, at least one of the woven fabric structure, the twisted yarn structure, the yarn thickness, and the density of the silk fabric 100 can be selected according to the use of the silk fabric seal 10 or the like. For example, an option having a relatively high strength on at least the surface side of the silk fabric 100 can be employed. Or the option suitable for application | coating of a chemical | medical agent can be employ | adopted to the at least back surface side of the silk fabric 100. FIG. Or according to the request | requirement of an external appearance, the classification of a textile structure can be selected. The same applies to woven fabrics other than silk fabric.

  Additionally, the silk thread and / or silk fabric 100 may be subjected to a predetermined treatment to improve and / or add a predetermined function in the silk fabric seal 10. These functions include, for example, strength (such as tensile strength), abrasion resistance, weather resistance (such as yellowing and embrittlement suppression), moisture permeability, waterproofness, water resistance (water repellency), chemical resistance, washability, and appearance. Properties (such as gloss), wrinkle resistance, thermal properties, heat retention, cold insulation, flexibility, and flame retardancy. The same can be done when using a fabric other than silk fabric. Moreover, it can do similarly when using cloth other than textiles and Japanese paper instead of textiles.

  2A, 2B, 2F, 2G, 2H, and 2I are diagrams showing examples of the overall shape of the fabric seal 10 using the fabric 100. FIG.

  In FIG. 2A, the fabric seal 10 generally has a substantially rectangular shape. The fabric 100 and the separator (mounting board) 300 may have substantially the same shape and / or the same size as each other. 2A, the fabric 100 and the separator 300 have a short axis along the X axis and a long axis along the Y axis. In one embodiment, the Y axis is substantially along the warp yarn 121 (or weft yarn 122) of the fabric 100 and the X axis is substantially along the weft yarn 122 (or warp yarn 121) of the fabric 100. The minor axis of the fabric 100, the minor axis of the separator 300, the weft yarn 122 (or warp yarn 121) of the fabric 100, and one symmetry axis of the fabric 100 are substantially parallel to the X axis. The major axis of the fabric 100, the major axis of the separator 300, the warp yarn 121 (or weft yarn 122) of the fabric 100, and one symmetry axis of the fabric 100 are substantially parallel to the X axis. In one embodiment, the fabric 100 has a shape with an axis substantially along the warp or weft. In the present embodiment, the separator 300 has a shape having an axis substantially along the warp or weft. Such a relationship between the fabric structure (warp and weft) and the predetermined axis in the fabric seal 10 contributes to the excellent appearance of the fabric seal 10. In other embodiments, the fabric 100 and the separator 300 can have a shape with an axis that intersects the warp or weft. For example, the crossing angle can be about 5, 10, 15, 20, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, or 85 degrees.

  In FIG. 2B, the fabric seal 10 has a circular shape, a square shape, a diamond shape, or a star shape as a whole. The fabric 100 and the separator (mounting paper) 300 of the fabric seal 10 can have substantially the same shape and / or the same size. Alternatively or additionally, the fabric seal 10 can have a triangular shape, a pentagonal shape, a hexagonal shape, an elliptical shape, or other shapes. The contour of the fabric seal 10 can include at least one of a straight line, a curved line, and a zigzag line. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. The fabric 100 and the separator 300 can have a shape having an axis along the warp (or weft) along the Y axis or a weft (or warp) along the X axis, or an axis that intersects the warp or weft. Can have a shape with

  As shown in FIG. 2C, an example of the manufacturing process of the fabric seal 10 includes (a) a process of placing the adhesive material 200 on one surface of the fabric 100, and heat treatment, light treatment, and drying treatment for the adhesive material 200 as necessary. And / or other processing steps, (b) a step of placing the separator 300 on one surface of the fabric 100 via the adhesive material 200, and a predetermined processing (for example, cutting, edge portion) on the laminate as necessary. Processing, edge processing, etc.). The substrate or semi-finished product can be provided in the form of a sheet or a roll. The use of a scroll is advantageous for improving the production capacity. For example, a scroll made only of a predetermined base material is provided. For example, a scroll is provided in which a plurality of layers including at least one substrate are repeated in the radial direction. For example, at the time of bonding a predetermined base material and another base material, at least one base material can be used as a scroll.

  As shown in FIG. 2D, another example of the manufacturing process of the fabric seal 10 includes: (a) a step of placing the adhesive material 200 on one surface of the separator 300, heat treatment, light treatment, A process of performing a drying process and / or other processes, (b) a process of placing the separator 300 on one surface of the fabric 100 via the adhesive material 200, and a predetermined process (for example, cutting, Edge processing, edge processing, etc.). Alternatively, another example of the manufacturing process of the fabric seal 10 includes (a) a step of preparing a separator 300 in which an adhesive material 200 (layer of the adhesive material 200) is arranged on one side, and (b) a fabric through the adhesive material 200. A step of disposing a separator 300 on one surface of 100, and a step of performing predetermined processing (for example, cutting, edge processing, edge processing, etc.) on the laminate as necessary. The substrate or semi-finished product can be provided in the form of a sheet or a roll. The use of a scroll is advantageous for improving the production capacity. For example, a scroll made only of a predetermined base material is provided. For example, a scroll is provided in which a plurality of layers including at least one substrate are repeated in the radial direction. For example, at the time of bonding a predetermined base material and another base material, at least one base material can be used as a scroll. In one example, a scroll in which the lamination of the adhesive material 200 and the separator 300 is repeated in the radial direction (the scroll having a configuration in which the adhesive material 200 and the separator 300 are alternately laminated) can be prepared. Alternatively, a laminated sheet in which the separator 300, the adhesive material 200, and another cover sheet are laminated can be prepared. In cutting, the fabric 100, the adhesive material 200, and the separator 300 can be simultaneously cut or punched into a predetermined shape. In one example, the cutting shape can be set based on the result of image recognition of the pattern and characters of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  As shown in FIG. 2E, in at least one step of the manufacturing process of the fabric seal 10, a temporary separator (cover sheet, protective sheet) 1300 is temporarily attached at least temporarily as necessary for manufacturing and / or handling. It can be used. The temporary separator 1300 is used in a semi-finished product stage, for example. In one example, the temporary separator 1300 is affixed to a predetermined base material (for example, the separator 300) on which the adhesive material (200) is disposed, and is peeled off from the base material (300) leaving the adhesive material (200). Is possible. Moreover, in an example, the adhesive material (200) is arrange | positioned on the temporary separator 1300, and the temporary separator 1300 is affixed on a predetermined base material via the adhesive material (200). Moreover, in one example, while peeling the temporary separator 1300 from the adhesive material (200), the predetermined base material (300) on which the adhesive material (200) is disposed and another base material (for example, the fabric 100) are bonded together. It is done.

  In FIG. 2F, the fabric seal 10 generally has a shape having a contour that substantially conforms to the contour of the pattern or character that the fabric 100 has. The fabric 100 and the separator 300 may have substantially the same shape and / or the same size as each other. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. In one embodiment, the fabric 100 has at least one of letters, graphics, and patterns having an axis substantially along the warp or weft. In FIG. 2F, the Y-axis is substantially along the warp (or weft) of the fabric 100, and the X-axis is substantially along the weft (or warp) of the fabric 100. Character height axis, Character width axis, Character symmetry axis, Character vertical axis, Character horizontal axis, Character alignment axis, Symbol height axis, Symbol width axis, Symbol width The axis of symmetry, the vertical axis of the symbol, the horizontal axis of the symbol, and / or the axis of the arrangement direction of the symbols are along the X axis or the Y axis. These axes are substantially parallel to the warp (or weft) along the Y axis or the weft (or warp) along the X axis. Such a relationship between the fabric structure (warp and weft) and the characters, designs, and patterns in the fabric seal 10 contributes to the high appearance of the fabric seal 10. In one embodiment, the characters, designs, and / or patterns in the fabric 100 include at least one of a first design expressed based on the fabric texture and a second design expressed based on the post-weaving process. In other embodiments, the fabric 100 can have at least one of letters, designs, and patterns having an axis that substantially intersects the warp or weft. For example, the crossing angle can be about 5, 10, 15, 20, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, or 85 degrees. The manufacturing process of the fabric seal 10 shown in FIG. 2F is generally the same as that of FIGS. 2A and 2B. In one example, the cutting shape can be set based on the result of image recognition of the pattern and characters of the fabric 100.

  In FIG. 2G, the fabric seal 10 generally has a scroll shape. In FIG. 2G, for example, the lamination of the separator 300, the adhesive material 200, and the fabric 100 is repeated along the radial direction. The scroll of the fabric seal 10 has a form in which the width (axial length) is larger than the diameter, a form in which the diameter and width (axial length) are the same, or a form in which the width (axial length) is small compared to the diameter. Can have. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The width and length of the scroll-like fabric seal 10 can be substantially matched to the original fabric size of the fabric 100. That is, the scroll of the fabric seal 10 can have a width and length that is substantially the same as the original fabric dimension of the fabric 100. Alternatively, the width and length of the scroll-like fabric seal 10 can be determined substantially independently of the original fabric dimensions of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. The original fabric dimension can take various numerical values. In one example of the original fabric dimensions when the fabric 100 is a silk fabric, the width is about 36, 37, 38, 40, 42, 72, or 91 cm and the length is about 4, 4.5, 5.7, 8, 8.5, 9, 9.8, 10, 11.4, 11.5, 12, 13.5, 18, 22, 22.8, 24, or 26 m. The above numerical value is an example, and the present invention is not limited to this.

  In one example, the manufacturing process of the scroll-shaped fabric seal 10 includes a step of unwinding the fabric 100 from the scroll, a step of disposing the adhesive material 200 on one surface of the fabric 100, and heat treatment and light treatment of the adhesive material 200 as necessary. A process of performing a drying process and / or other processes, a process of arranging the separator 300 on one surface of the fabric 100 via the adhesive material 200, and a process of winding the fabric 100 with the separator 300 attached thereto. Alternatively, the manufacturing process of the scroll-like fabric seal 10 includes a step of placing the adhesive material 200 on one side of the separator 300, a heat treatment, a light treatment, a drying treatment, and / or the like on the adhesive material 200 as necessary. A step of unwinding the fabric 100 from the scroll, a step of disposing the fabric 100 on one surface of the separator 300 via the adhesive material 200, and a step of winding the fabric 100 with the separator 300 attached thereto. . Further alternatively, the manufacturing process of the scroll-shaped fabric seal 10 includes a step of preparing a separator 300 having an adhesive material 200 (layer of the adhesive material 200) disposed on one side, a step of unwinding the fabric 100 from the scroll, an adhesive material The step of disposing the fabric 100 on one surface of the separator 300 through 200 and the step of winding the fabric 100 with the separator 300 attached thereto can be provided. In this case, a scroll in which the lamination of the adhesive material 200 and the separator 300 is alternately repeated in the radial direction (the scroll having a configuration in which the adhesive material 200 and the fabric 100 are alternately laminated) can be prepared. Cutting in the width direction is performed, for example, between a step of cutting the entire roll of the fabric 100 with the separator 300 over the entire diameter, a step of cutting the original fabric of the fabric 100 over the entire diameter, and from unwinding to winding. Any of the steps of continuously cutting the fabric 100 may be included. Further, by further cutting the scroll fabric 100 in a planar manner, a fabric seal 10 having a predetermined length and / or width and a fabric seal 10 having the configuration shown in FIG. 2A, FIG. 2B, or FIG. 2F can be obtained. it can. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In other embodiments, the separator 300 can be omitted from the roll of fabric seal 10 shown in FIG. 2G. In this case, in the scroll, the lamination of the fabric 100 and the adhesive material 200 is repeated along the radial direction. That is, the scroll of the fabric seal 10 has a configuration in which the adhesive material 200 and the fabric 100 are alternately stacked. The removal of the separator 300 is advantageous for cost reduction and scroll size reduction. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, in the process of disposing another substrate on one substrate via the adhesive 200, the adhesive can be softened by heat treatment, or at least a part can be melted by heat treatment. it can. With proper temperature control, a high quality fabric seal 10 can be obtained. In this case, the heat treatment temperature can be set according to, for example, the usage form and usage environment of the fabric seal (woven fabric sheet) 10, the structure of the fabric 100, the characteristics of the adhesive material 200 (softening temperature, melting temperature), and the like.

  In FIG. 2H, the fabric seal 10 has a folded quay (an auxiliary portion (auxiliary line) that will be a crease in the future, a mold for folding) 108. The folded quay 108 can be processed against one or both sides of the fabric seal 10. The fabric seal 10 can be easily folded by the folding quay 108. The folding seal 108 can easily process the fabric seal 10 into a three-dimensional shape. In addition, since the fabric 100 generally has a relatively high flexibility, the fabric seal 10 without the folded quay 108 can be processed into a three-dimensional shape. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. The fold 108 may be formed substantially along the warp or weft of the fabric 100, or may intersect the warp or weft (eg, the intersection angle is about 5, 10, 15, 20, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, or 85 °). These can be selected and set according to the usage form, usage environment, characteristics of the adhesive material, and the like. Folding along the warp or weft can contribute to the ease of folding the fabric 100. Folding quay that intersects the warp or weft can contribute to suppression of bending fatigue of the fabric 100. As an auxiliary part (auxiliary line) that will be a crease in the future, it is possible to adopt a form other than the folding key. In one example, a partial film (linear film, area film) can be disposed on the fabric 100. In another example, the fabric 100 can have a tissue structure that assists in folding. In yet another example, the fabric 100 may have a form in which the thickness structure and / or flexibility is partially changed in one plane. Changes in the thickness structure and / or flexibility of the fabric 100 include the thickness of the fabric 100, the number of layers of the fabric 100, the material of the adhesive material 200, the thickness of the adhesive material 200, the number of layers of the adhesive material 200, and the front and / or back surfaces. It can have at least one change in the treatment material (such as a coating material).

  Further, in one example, the fabric seal 10 has an overall shape (a line-symmetric shape) that is symmetrical with respect to the folding key 108. That is, the shape of the first part on one side of the folded quay 108 and the shape of the second part on the other side have a mirror image relationship. In this example, the folding key 108 is an axis of symmetry. By folding the fabric seal 10 with the folding key 108 as a boundary, one overlaps the other. In this case, by bonding the back surfaces of the fabric 100 together, a state in which the back surface of the fabric 100 is hidden and only the surface of the fabric 100 is exposed is obtained. Furthermore, the adhesive material 200 can be disposed on one of the two exposed surfaces on both sides. By attaching this to an object 500 having substantial transparency and / or having an observation window, the object 500 is observed through the surface of the fabric 100 on one side and the fabric 100 on the other side. The surface of the object is directly observed without passing through the object 500. In this case, for example, the fabric seal 10 can be attached to a glass window of a store, and the surface of the fabric 100 can be observed from inside and outside the store. Alternatively, the fabric seal 10 may have a shape that hides the back surface of the fabric 100 by folding back two or more portions. Alternatively, the fabric seal 10 may have a shape that does not hide a portion of the back surface of the fabric 100 when folded. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 2I, the fabric seal 10 has a folding quay 108, a cut 110, and a stop blade 112. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. The fold 108 or crease 100 can be formed substantially along the warp or weft of the fabric 100, or can intersect the warp or weft (eg, the intersection angle is about 5, 10, 15, 20, 35). , 40, 45, 50, 55, 60, 65, 70, 75, 80, or 85 °). These can be selected and set according to the usage form, usage environment, characteristics of the adhesive material, and the like. The fabric seal 10 shown in FIG. 2I can be processed into a paper-like shape used for money or a skewer, for example.

  3A, 3B, and 3C are diagrams showing another example of the overall shape of the fabric seal 10. FIG. 3A-3C, a piece of fabric 100 may have a smaller size than separator (separator) 300. FIG. In one fabric seal 10, the fabric 100 can be a single piece or a plurality of pieces with respect to one separator 300.

  In FIG. 3A, the fabric seal 10 has a score line 106 provided in the fabric 100. A piece of fabric 100 can be spaced from the separator 300 along the score line 106. In FIG. 3A, the overall shape and overall size of the fabric 100 can be substantially the same as that of the separator 300. In this case, at least one of the color, pattern, character, design, and the like of the fabric 100 can be observed over the entire surface of the fabric seal 10. A score line 106 is formed substantially around a piece of fabric 100. The shape of the score line 106 may have a straight line and / or a curved line. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. The score line 106 can be formed along the warp or weft of the fabric 100, or so as to intersect the warp or weft (for example, the intersection angle is about 5, 10, 15, 20, 35, 40, 45, 50). , 55, 60, 65, 70, 75, 80, or 85 °). These can be selected and set according to the usage form, usage environment, characteristics of the adhesive material, and the like. In FIG. 3A, one piece of fabric 100 can be substantially spaced or adjacent to another piece. Alternatively, the score line 106 can have a substantial width. The manufacturing process of the fabric seal 10 shown in FIG. 3A includes, for example, a step of disposing the adhesive material 200 on one surface of the fabric 100, a step of disposing the separator 300 on one surface of the fabric 100 via the adhesive material 200, and a cut into the fabric 100. Providing a line 106; In the process of forming the score line 106, the fabric 100 and the adhesive material 200 can be simultaneously cut or punched into a predetermined shape. In one example, the shape of the cut line 106 can be set based on the result of image recognition of the pattern and characters of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The fabric seal 10 shown in FIG. 3B is a modification of the fabric seal 10 of FIG. 3A. In FIG. 3B, the score line 106 may have a shape along the contour of the pattern of the fabric 100. Alternatively, the cut line 106 may have a shape substantially along the outline of a predetermined symbol such as an animal or a flower. Alternatively, the score line 106 can have a shape that substantially follows the outline of the character. Alternatively, the score line may have a concave-convex shape such that the convex portion of one contour of the fabric 100 is incorporated into the concave portion of the contour of another piece of the fabric 100. The manufacturing process of the fabric seal 10 shown in FIG. 3B is substantially the same as that of FIG. 3A. In one example, the shape of the cut line 106 can be set based on the result of image recognition of the pattern and characters of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 3C, a piece of fabric 100 having a predetermined shape is disposed on the separator 300. A plurality of pieces of the fabric 100 having the same shape can be arranged on one separator 300. Alternatively, a plurality of pieces of fabric 100 having different shapes can be arranged on one separator 300. In the region where the piece of the fabric 100 is not disposed, one surface of the separator 300 is exposed. In FIG. 3C, the piece of fabric 100 may generally have a circular shape, a square shape, a diamond shape, or a star shape. Alternatively or additionally, the pieces of fabric 100 may be triangular, pentagonal, hexagonal, elliptical, or other shapes (eg, human / animal shapes, plant shapes, vehicle shapes, building shapes, Fruit / vegetable shape, confectionery shape, etc.). Alternatively, the fabric 100 may include a plurality of pieces 100A, 100B, and 100C having different fabric structures. Alternatively, the fabric seal 10 may have a configuration in which a piece of the fabric 100 and a piece 600 made of a material other than the fabric are arranged on one separator 300. Alternatively, the fabric seal 10 may have a configuration in which a piece including a piece of the fabric 100 and a piece 600 made of a material other than the fabric is disposed on the separator 300. For example, the fabric seal 10 may have a configuration in which a piece 600 of another material is arranged on the separator 300 and a piece of the fabric 100 is arranged on the piece 600 of other material. The other material piece 600 may have at least one of a color, a pattern, a character, a design, and the like. For example, the piece 600 of other material may have characters including information about the fabric 100 and / or information about how to use the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  An example of the process for manufacturing the fabric seal 10 shown in FIG. 3C is, for example, a step of placing the adhesive material 200 on one surface of the fabric 100, and heat treatment, light treatment, drying treatment, And / or a process of performing other treatments, a process of placing the separator 300 on one surface of the fabric 100 via the adhesive material 200, a process of providing the cut line 106 in the fabric 100, and removing the fabric 100 other than the predetermined piece from the separator 300. (Stripping) step. Alternatively, another example of the manufacturing process includes a step of placing the adhesive material 200 on one side of the separator 300, and optionally performing heat treatment, light treatment, drying treatment, and / or other processing on the adhesive material 200. A step of performing, a step of disposing the fabric 100 on one surface of the separator 300 via the adhesive material 200, a step of providing the cut line 106 on the fabric 100, and a step of removing (stripping) the fabric 100 other than the predetermined piece from the separator 300. Can have. Further alternatively, another example of the manufacturing process is a step of preparing a separator 300 in which an adhesive material 200 (layer of adhesive material 200) is arranged on one side, and the fabric 100 is provided on one side of the separator 300 via the adhesive material 200. A step of arranging, a step of providing a cut line in the fabric 100, and a step of removing (peeling) the fabric 100 other than the predetermined piece from the separator 300. In one example, the shape of the piece of the fabric 100 can be set based on the result of image recognition of the pattern and characters of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, various pressure-sensitive adhesive materials (adhesive substances) can be used as the pressure-sensitive adhesive material 200. For example, the adhesive material 200 can exhibit adhesiveness at room temperature. Or the adhesive material 200 does not express adhesiveness at normal temperature, but can express adhesiveness by a predetermined process. Examples of the adhesive material 200 include a water-soluble adhesive material and a solvent-based adhesive material. Examples include acrylic emulsion resin adhesives, natural rubber adhesives, synthetic rubber adhesives, acrylic resin adhesives, urethane resin adhesives, silicone resin adhesives, and polyvinyl ether resin adhesives. The pressure-sensitive adhesive material can contain a thermosetting resin or a thermoplastic resin. As the polymer compound as the adhesive material (adhesive substance), a natural system (such as cellulose), an addition system (such as vinyl alcohol), or a condensation system (such as urethane) can be used. The pressure-sensitive adhesive material (adhesive substance) can include a pressure-sensitive adhesive or a water-based adhesive (an adhesive dispersed in an aqueous medium, a wet glue). When the water-based adhesive / wet glue is used, the fabric 100 can have water permeability. Alternatively or additionally, an adhesive that is less irritating to the skin of the human body or organism can be selectively used. Alternatively, a re-peelable material can be selectively used as the adhesive material 200. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In the fabric seal 10, the structure of the fabric 100 is related to the permeability of the adhesive 200 to the fabric 100. The type and viscosity of the pressure-sensitive adhesive material 200 to be used can be determined based on the tissue structure of the fabric 100. By using an appropriate adhesive material 200, the adhesive material 200 can be prevented from oozing out onto the surface of the fabric. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Alternatively or additionally, as shown in FIGS. 4 and 5, an anchor process (anchor coating process, supplementary process, foundation process, barrier process) can be applied to one surface of the fabric 100. In FIG. 4, an anchor material (auxiliary material, base material, barrier material) 210 is disposed on one surface of the fabric 100. That is, the anchor material (auxiliary material, base material, barrier material) 210 is disposed between the fabric 100 and the adhesive material 200. As shown in FIG. 5, the anchor material 210 can be disposed on substantially the entire surface including the sparse and dense portions of the fabric 100. Alternatively, the anchor material can be arranged in a pattern and / or partially arranged according to a predetermined shape or pattern, such as a tissue structure of the fabric 100. The anchoring material 210 can be mainly arranged only in the sparse part of the fabric 100 and can be arranged substantially not in the dense part or in a relatively small amount. Or the film thickness of the anchor material 210 in a sparse part can be made comparatively large, and the film thickness of the anchor material 210 in a dense part can be made comparatively small. In one example, the anchor material (complementary material, base material, barrier material) 210 can have a stronger adhesive force (adhesive force) and / or higher hardness (high viscosity) than the adhesive material 200. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The anchor material 210 can function as a barrier layer for the adhesive material 200. The anchor material 210 can expand the selectivity in the type and viscosity of the adhesive material 200. Furthermore, the anchor material 210 can exhibit a function of complementing the flexibility of the fabric 100. By using an appropriate anchor material 210, the anchor material 210 can strengthen the fabric 100. That is, the anchor material 210 contributes to the solution of the problem regarding the liquid permeability on the tissue structure, which is one of the characteristics of the fabric 100, and the problem regarding the softness, which is another characteristic of the fabric 100. In addition, the anchor material 210 contributes to strengthening the bonding force between the fabric 100 and the adhesive material 200. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Alternatively or additionally, the anchor material 210 can function as a barrier layer (preventing penetration of an external material) against a predetermined material toward the adhesive material 200. In this case, for example, the predetermined substance may reduce the function of the adhesive material 200. The anchor material 210 may have a function of suppressing, preventing, and / or blocking a predetermined substance from the outside from passing through the fabric 100 and reaching the adhesive material 200. In one example, the arrival of moisture to the adhesive material 200 via the fabric 100 is suppressed, thereby suppressing the functional degradation of the adhesive material 200 (decrease in adhesive force, separation and / or peeling), and the adhesion of the adhesive material 200. The performance can be stably maintained. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The type, viscosity, and film thickness of the anchor material 210 to be used can be determined based on at least one of the tissue structure of the fabric 100 and the pressure-sensitive adhesive to be used. Examples include varnish, medium, and resin. By using an appropriate anchor material 210, it is possible to obtain an appropriate function as a seal while maintaining the texture of the fabric 100. By selectively using the anchor material 210 that is excellent in moisture barrier properties, it is possible to suppress the functional degradation of the adhesive material 200 due to moisture. For example, the anchor material 210 having good compatibility with the woven fabric 100, good compatibility with the adhesive material 200, and excellent moisture blocking property can be selected. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The anchor material 210 can also contribute to prevention of fraying of the cut end face (cut portion) in the fabric 100. That is, a part of the anchor material 210 is arranged in the tissue of the fabric 100, whereby the tissue structure of the fabric 100 is strengthened (substantially fixing the tissue). The anchor material 210 can be arranged only near the edge of the fabric 100. Also, the first part (for example, the vicinity of the edge) and the second part (for example, other part) of the fabric 100 can be different in at least one of the type, viscosity, and film thickness of the anchor material 210. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, a sheet-like member (a sheet material or a film material) can be used as the anchor material 210. In one example, the sheet material (film material) can have at least one of a porous structure, a network structure, an uneven structure, a protruding structure, an ultrathin structure, a permeation structure, a flexible structure, and the like. Such a structure can be advantageous for securing the bonding force between the fabric 100 and the adhesive material 200. As a sheet material (film material), a material (binder) that exhibits a function of promoting bonding between the fabric 100 and the adhesive material 200 by physical processing, chemical processing, optical processing, and / or thermal processing. Material, binder fiber) can be selected. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The anchor material 210 can be omitted by using an appropriate adhesive material 200. Further, the adhesive material 200 can strengthen the fabric 100. In this case, the adhesive material 200 contributes to the solution of the problem related to liquid permeability on the tissue structure of the fabric 100 and the problem related to flexibility. For example, the fabric seal 10 can be provided by attaching a separator 300 having a surface on which a film (adhesive film, adhesive layer) of the adhesive material 200 is formed in advance to one surface of the fabric 100. In at least most of the region on one side of the fabric seal 10 (fabric 100), the adhesive 200 can be substantially non-infiltrated or low infiltrated with respect to the inside of the yarn of the fabric 100. By additional processing such as heat treatment, light processing, and liquid processing, the intrusion state of the adhesive material 200 in the additional processing portion can be partially different from other portions. For example, at least 1, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95% or more on one side of the fabric 100 In this region, the adhesive material 200 can be substantially non-infiltrated with respect to the inside of the yarn of the fabric 100. In the cross section of the fabric 100 in the non-infiltrated portion, at least a part of the adhesive material 200 can be disposed in the gap of the tissue structure of the fabric 100 (can enter the gap). Depending on the structure of the woven fabric 100, the material, characteristics, entry rate and the like of the adhesive material 200 can be set. When the penetration rate is low (the distance to enter is short), it is possible to suppress the texture of the fabric 100 from being damaged. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  6A and 6B are diagrams each schematically showing an enlarged cross-sectional structure of the fabric seal 10. In one embodiment, the penetration rate of the adhesive 200 with respect to the material (yarn) of the fabric 100 can be controlled. The penetration rate of the adhesive material 200 into the material (yarn) of the fabric 100 (for example, the weight ratio of the adhesive material to the yarn) is, for example, about 1, 2, 3, 4, 5, 6, 7, 8, 9 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 110, 120, 130, 140, 150, 160, 170, 180, 190, 200%, or more. Alternatively, the penetration of the adhesive material 200 into the material (yarn) of the fabric 100 can be made substantially zero. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. In the fabric seal (woven fabric sheet) 10 having a high permeability, high rigidity and strength can be obtained. In the fabric seal (woven fabric sheet) 10 having a low penetration rate, deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 accompanying the penetration of the adhesive material 200 is suppressed. In an example of low penetration, the penetration rate is 0% or more and 150% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 100% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 80% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 50% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 20% or less by weight. The penetration rate can be set according to, for example, the usage pattern and usage environment of the fabric seal (fabric sheet) 10, the characteristics of the adhesive material, and the like. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the penetration rate of the adhesive 200 with respect to the fabric 100 is controlled. In FIG. 6A and FIG. 6B, the distance h1 into which the adhesive material 200 enters in the gap between the tissue structures of the fabric 100 is, for example, about 90, 80, 70, 60, 50, 40, 30, 20, It can be 10, 9, 8, 7, 6, 5, 4, 3, 2, 1% or less (entrance rate). Alternatively, the pressure-sensitive adhesive 200 can enter the gap between the texture structures of the fabric 100 to be substantially zero. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. In the fabric seal (fabric sheet) 10 having a high penetration rate, high rigidity and strength can be obtained. In the fabric seal (fabric sheet) 10 having a low penetration rate, deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 accompanying the entry of the adhesive material 200 is suppressed. In an example of low approach, the approach rate is 0% or more and 50% or less. Or in an example of low approach, an approach rate is 0% or more and 40% or less. Or in an example of low approach, an approach rate is 0% or more and 30% or less. Or in an example of low approach, an approach rate is 0% or more and 20% or less. Or in an example of low approach, an approach rate is 0% or more and 10% or less. Or in an example of low approach, an approach rate is 0% or more and 5% or less. The approach rate can be set according to, for example, the usage pattern and usage environment of the fabric seal (fabric sheet) 10 and the characteristics of the adhesive material. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the presence or absence of a gap (209) between the fabric 100 and the surface of the adhesive 200 or the proportion thereof is controlled. In FIG. 6A, the fabric 100 and the adhesive material 200 are in close contact with each other, and there is substantially no gap between the fabric 100 and the surface of the adhesive material 200. That is, substantially the entire surface of the yarn 100 of the fabric 100 facing the adhesive material 200 is in contact with the adhesive material 200. In other words, there is substantially no gap (space) surrounded by the warp yarn, the weft yarn, and the adhesive material 200. In such a low-gap fabric seal (fabric sheet) 10, high rigidity and strength can be obtained. In FIG. 6B, the fabric 100 and the adhesive material 200 are loosely in contact with each other, and there is a gap 209 between the fabric 100 and the surface of the adhesive material 200. In other words, at least a part of the surface of the yarn of the fabric 100 facing the adhesive material 200 is not in contact with the adhesive material 200. Alternatively, in the fabric seal (fabric sheet) 10 of FIG. 6B, there is a space (space) 209 surrounded by the warp yarn, the weft yarn and the adhesive material 200. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. In the fabric seal (woven fabric sheet) 10 having many voids 209, the deterioration of the properties (appearance characteristics, feel, flexibility, texture, etc.) inherent to the fabric 100 due to the influence of the adhesive material 200 is suppressed. The presence / absence of the gap 209 and the ratio thereof can be set according to, for example, the usage form and usage environment of the fabric seal (fabric sheet) 10 and the characteristics of the adhesive material. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the shape of the surface 201 of the adhesive 200 on the side facing the fabric 100 can be controlled. One surface of the fabric 100 includes a fine uneven structure. The shape of the surface of the pressure-sensitive adhesive 200 that is at least partially in contact with the fine concavo-convex structure of the fabric 100 is controlled. The shape of the surface 201 of the adhesive material 200 varies depending on the manufacturing process and conditions of the fabric seal (woven fabric sheet) 10. The production process and conditions of the fabric seal (fabric sheet) 10 can be selected so that a surface shape that gives the fabric 100 high rigidity and strength can be obtained. Further, the fabric seal (fabric sheet) 10 is provided so that a surface shape that suppresses deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 due to the influence of the adhesive material 200 is obtained. The manufacturing process and conditions can be selected. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. The manufacturing process and conditions can be set according to, for example, the usage form and usage environment of the fabric seal (fabric sheet) 10, the characteristics of the adhesive material, and the like. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  The adhesive material 200 can be a single layer or substantially multiple layers. In the adhesive material 200, specifications (materials and characteristics) and the like can be different between the surface in contact with the fabric 100 and the surface in contact with the separator 300. For example, as shown in FIG. 6C, in a multi-layer adhesive material 200, specifications (material, hardness, thickness, color, transparency, pattern, etc.) are defined between the layer 202 in contact with the fabric 100 and the layer 203 in contact with the separator 300. Can be different. The number of stacks can be 2, 3, 4, 5, 6, 7, 8, 9, 10, or more. Further, the adhesive material 200 may partially differ in material, characteristics, and the like in the plane. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  6D, the fabric seal (woven fabric sheet) 10 is in a state in which the adhesive material (or anchor material) can be directly observed from the front side (observation side) or directly from the front side. Can be set to a state in which substantially no observation is possible. That is, the observation state of the adhesive material on the front side of the fabric 100 can be controlled. The texture structure of the fabric 100 can have a plain weave texture or another texture. By controlling the observed state of the adhesive material from the front side, it is possible to control the observed state of colors, shadows, patterns, characters, and / or designs. The state of the adhesive material (the presence or absence of the adhesive material, the amount of the adhesive material, the surface area of the adhesive material, the thickness of the adhesive material, the distribution of the adhesive material) in the depression of the tissue structure of the woven fabric 100 can be controlled. In one example, when the adhesive material is present in the dent 125 of the tissue structure on the surface of the woven fabric 100 (the dent 125 at the boundary portion between adjacent threads in the surface layer of the woven fabric 100, the dent on the surface of the woven fabric 100), When the adhesive material can be directly observed at (boundary portion) 125, for example, a shadow based on the tissue structure of the fabric 100 can be suppressed by the adhesive material. In another example, when the adhesive material is not substantially present in the depression 125 (boundary portion 125 between adjacent yarns) on the surface of the fabric 100, or the adhesive material is substantially absent in the depression (boundary portion) 125. For example, a shadow based on the tissue structure of the fabric 100 can be effectively observed.

  In FIG. 6D, when the tissue structure of the fabric 100 has gaps 126 (when the tissue structure is a substantially sparse structure), the adhesive material (or anchor material) is directly applied from the front side via the gaps 126. The adhesive material (or anchor material) can be made substantially unobservable in an observable state or directly through the gap 126 from the front side. In one example, when the adhesive material can be directly observed from the front side of the fabric 100 through the gap 126, by controlling the surface height of the adhesive material in the gap 126 (or the surface height of the anchor material), For example, the shading based on the tissue structure of the fabric 100 can be controlled. In one example, when the adhesive material (or anchor material) can be observed directly from the front side of the fabric 100 through the gap 126, the color and / or optical characteristics of the adhesive material (or anchor material) in the gap 126 are controlled. By doing so, for example, it is possible to control the observed state of the fabric 100, such as colors, shadows, patterns, characters, and / or designs. In addition, when the tissue structure of the fabric 100 has substantially no gap (when the tissue structure is a substantially dense structure), or directly from the front side of the fabric 100 having a sparse texture structure, through the gap 126. For example, even when the adhesive material (anchor material) cannot be substantially observed, by controlling the color and / or optical characteristics of the adhesive material (or anchor material), for example, the color, shadow, pattern, character of the fabric 100 And / or the state of observation such as symbols may be controllable.

  The adhesive material (or anchor material) can be substantially colorless or have a color. The hue, chromaticity, and / or saturation of the adhesive material (or anchor material) can be set according to the tissue structure, color, shading, pattern, character, and / or design of the fabric 100. In one example, the adhesive material (or anchor material) has a relatively light color, a relatively dark color, a color similar to the color of the fabric 100, and a color in a predetermined relationship with the color of the fabric 100. The entire surface can have a uniform color or at least partially have a color change on one surface. The adhesive material (or anchor material) can have light absorption and / or light reflectivity. For example, the adhesive material (or anchor material) can contain particles having light absorption and / or light reflectivity.

  In one embodiment, the yarn on the lower layer (hereinafter, the yarn closer to the surface in the fabric structure is appropriately referred to as the upper yarn, and the yarn far from the surface (opposite to the surface) is appropriately referred to as the lower yarn). The height of the adhesive material 200 (or anchor material) is controlled. In FIG. 6E, the ratio (lower layer approach rate) of the height (penetration height, entry height) h2 of the adhesive material 200 to the thickness (outer diameter) t2 of the lower layer or lowermost layer thread (123) is, for example, about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 20, 30, 40, 50, 60, 70, 80, 90, 100%, or more. Alternatively, the penetration height (entry height) h2 of the adhesive material 200 (or anchor material) with respect to the thickness t2 of the lowermost layer or the lowermost layer yarn (123) can be made substantially zero. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. High rigidity and strength can be obtained in the high penetration fabric seal (woven fabric sheet) 10. In the low-entry fabric seal (woven fabric sheet) 10, the deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 accompanying the entry of the adhesive material 200 (or anchor material) is suppressed. In an example of low approach, the lower layer approach rate is 0% or more and 100% or less. Or in an example of low approach, a lower layer approach rate is 0% or more and 80% or less. Or in an example of low approach, a lower layer approach rate is 0% or more and 60% or less. Or in an example of low approach, a lower layer approach rate is 0% or more and 40% or less. Or in an example of low approach, a lower layer approach rate is 0% or more and 20% or less. Or in an example of low approach, a lower layer approach rate is 0% or more and 10% or less. The lower layer approach rate can be set according to, for example, the usage pattern and usage environment of the fabric seal (fabric sheet) 10, the characteristics of the adhesive material, and the like. In the woven fabric 100 having a dense structure, the lower layer penetration rate is less than 100%, thereby avoiding and / or suppressing the directly observed state of the adhesive material 200 (or anchor material) from the front side (observation side). Is possible. In the woven fabric 100 having a sparse structure, the lower layer penetration rate is less than 50%, thereby avoiding and / or suppressing the directly observed state of the adhesive material 200 (or anchor material) from the front side (observation side). Is possible. The approach rate can be set according to, for example, the usage pattern and usage environment of the fabric seal (fabric sheet) 10 and the characteristics of the adhesive material. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the height of the adhesive material 200 relative to the upper yarn is controlled. In FIG. 6F, the ratio (upper layer penetration rate) of the height (penetration height, entry height) h3 of the adhesive material 200 to the thickness (outer diameter) t3 of the upper layer or uppermost layer thread (124) is, for example, about 100, 90, 80, 70, 60, 50, 40, 30, 20, 10, 9, 8, 7, 6, 5, 4, 3, 2, 1% or less. Alternatively, the penetration height (entry height) h3 of the pressure-sensitive adhesive 200 with respect to the thickness t3 of the upper layer or uppermost layer yarn (124) can be made substantially zero. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. High rigidity and strength can be obtained in the high penetration fabric seal (woven fabric sheet) 10. In the low-entry fabric seal (woven fabric sheet) 10, deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 accompanying the entry of the adhesive material 200 is suppressed. In an example of low approach, the approach rate is 50% or less. Or in an example of low approach, an approach rate is 40% or less. Or in an example of low approach, an approach rate is 30% or less. Or in an example of low approach, an approach rate is 0% or more and 20% or less. Or in an example of low approach, an approach rate is 0% or more and 10% or less. Or in an example of low approach, an approach rate is 0% or more and 5% or less. In the fabric 100 having a dense structure, the upper layer penetration rate is less than 50%, thereby avoiding and / or suppressing the directly observed state of the adhesive material 200 (or anchor material) from the front side (observation side). Is possible. In the woven fabric 100 having a sparse structure, when the upper layer penetration rate is less than 1%, the direct observation state of the adhesive material 200 (or anchor material) from the front side (observation side) can be suppressed. The approach rate can be set according to, for example, the usage pattern and usage environment of the fabric seal (fabric sheet) 10 and the characteristics of the adhesive material. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, as shown in FIG. 6G, the fabric 100 has the same or different characteristics between the upper portion 105 disposed on the front surface side and the lower portion 106 disposed on the back surface side (near the adhesive material 200). (Physical properties, chemical properties, optical properties, thermal properties, materials, etc.). In another embodiment, the fabric 100 includes an upper portion 105 disposed on the front surface side, a lower portion 106 disposed on the back surface side (near the adhesive material 200), and an intermediate portion 107 between the upper portion and the lower portion. At least a part can have the same or different characteristics (physical characteristics, chemical characteristics, optical characteristics, thermal characteristics, materials, etc.) with respect to other parts. In one example of the fabric 100, the lower part 106 or the intermediate part 107 has a different overall density of the tissue structure compared to the other parts. For example, the upper portion 105 can be entirely sparse and the lower portion 106 can be entirely dense. For example, the upper portion 105 can be entirely dense and the lower portion 106 can be entirely sparse. For example, the upper part 105 can be entirely sparse, the intermediate part 107 can be entirely dense, and the lower part 106 can be entirely sparse. For example, the upper part 105 can be made dense overall, the intermediate part 107 can be made sparse overall, and the lower part 106 can be made dense overall. The density of the tissue structure in each part can be set according to, for example, the usage pattern and usage environment of the fabric seal (woven fabric sheet) 10, the characteristics of the adhesive material 200, and the like. In another example of the fabric 100, both the upper portion 105 and the lower portion 106 can be sparse or dense. A laminated structure such as a double weave in the woven fabric 100 can be advantageous for securing the bonding force between the woven fabric 100 and the adhesive material 200 and / or securing the texture of the woven fabric 100. A large number of irregularities on the lower surface of the fabric 100 can be advantageous in increasing the contact area between the fabric 100 and the adhesive 200 and ensuring the bonding force. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one example of the fabric 100, the lower portion 106 or the intermediate portion 107 is different in overall flexibility or hardness compared to other portions. For example, the upper portion 105 is generally relatively flexible and the lower portion 106 is generally relatively rigid. For example, the upper portion 105 can be relatively rigid overall and the lower portion 106 can be relatively flexible overall. For example, the upper part 105 can be relatively flexible overall, the intermediate part 107 can be relatively rigid overall, and the lower part 106 can be relatively flexible overall. For example, the upper portion 105 can be relatively hard as a whole, the intermediate portion 107 can be relatively flexible as a whole, and the lower portion 106 can be relatively hard as a whole. The flexibility or hardness of the tissue structure in each part can be set according to, for example, the usage form and usage environment of the fabric seal (woven fabric sheet) 10, the characteristics of the adhesive material 200, and the like. The flexibility in the upper part 105 of the fabric 100 can be advantageous for ensuring the texture of the fabric 100. Hardness in the lower part 106 or the middle part 107 of the fabric 100 may be advantageous in increasing the contact area between the fabric 100 and the adhesive material 200 and ensuring the bonding force. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one example of the fabric 100, the lower surface 106 or the intermediate portion 107 has a different surface roughness (smoothness) of the yarn compared to other portions. For example, the overall smoothness of the yarn surface of the upper portion 105 can be relatively high and the smoothness of the yarn surface of the lower portion 106 can be relatively low overall (the surface is rough). For example, the overall smoothness of the yarn surface of the upper portion 105 can be relatively low, and the smoothness of the yarn surface of the lower portion 106 can be relatively high overall. For example, the smoothness of the yarn surface of the upper portion 105 is relatively high overall, the smoothness of the yarn surface of the intermediate portion 107 is relatively low overall, and the smoothness of the yarn surface of the lower portion 106 is relatively high overall. it can. For example, the smoothness of the yarn surface of the upper part 105 is relatively low overall, the smoothness of the yarn surface of the intermediate part 107 is relatively high overall, and the smoothness of the yarn surface of the lower part 106 is relatively low overall. Can be. The smoothness (roughness) of the yarn surface in each part can be set according to, for example, the usage form and usage environment of the fabric seal (fabric sheet) 10, the characteristics of the adhesive material 200, and the like. The smoothness of the yarn surface of the upper part 105 of the fabric 100 may be related to the texture of the fabric 100. The smoothness (surface roughness) of the yarn surface of the lower portion 106 or the intermediate portion 107 of the fabric 100 may be related to the contact area / bonding force between the fabric 100 and the adhesive material 200. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In the woven fabric 100, characteristics (physical characteristics, chemical characteristics, optical characteristics, thermal characteristics, materials, etc.) are present between the upper part 105 and the lower part 106 or between the upper part 105, the lower part 106 and the intermediate part 107. The difference can be advantageous for both ensuring the texture of the fabric 100 and ensuring the bonding force between the fabric 100 and the adhesive material 200. In addition, in FIG. 6G, although the case where it divides into two or three parts of the thickness direction of the textile fabric 100 and compared is shown typically, you may divide and compare in four or more parts. In addition, such characteristics are not limited to changes in the thickness direction of the fabric 100, and may have changes in the plane of the fabric 100. It is possible to obtain partial property changes in the fabric 100 by physical processing, chemical processing, optical processing, and / or thermal processing on the fabric 100. Alternatively, it is possible to obtain a partial change in the characteristics of the fabric 100 by partially changing the material (single material or a combination of materials). The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, as shown in FIGS. 6H and 6I, one surface of the separator 300 in contact with the adhesive material 200 may have a substantially uneven structure. In FIG. 6H, one surface 301 of the separator 300 has a plurality of protrusions 305. The shape, number (density), and / or rigidity of the protrusions 305 can be set according to, for example, the use form and use environment of the fabric seal (fabric sheet) 10, the tissue structure of the fabric 100, the characteristics of the adhesive material 200, and the like. It is. In FIG. 6I, a plurality of particles 306 are arranged on one surface 301 of the separator 300. Alternatively, the adhesive material 200 on the separator 300 includes a plurality of particles 306. The shape, number (density), and / or rigidity of the particles 306 can be set according to, for example, the use form and use environment of the fabric seal (fabric sheet) 10, the structure of the fabric 100, the characteristics of the adhesive material 200, and the like. is there. The fact that one surface of the separator 300 in contact with the adhesive material 200 has a substantially uneven structure can be advantageous in increasing the contact area between the fabric 100 and the adhesive material 200 and ensuring the bonding force. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  6J, FIG. 6K, and FIG. 6L are diagrams showing examples of arrangement of the adhesive material 200. FIG.

  In FIG. 6J, the adhesive material 200 can be disposed on the whole or a part of one surface of the fabric 100. The partial arrangement can be advantageous in exhibiting the texture and texture of the fabric 100. In partial arrangement | positioning, the adhesive material 200 can be arrange | positioned in the area | region except the edge part of the textile fabric 100, for example. Alternatively, the adhesive material 200 can be annularly disposed on the edge of the fabric 100. Or the adhesive material 200 can be divided | segmented into the several area | region which mutually separates in the one surface of the fabric 100, and can be arrange | positioned. For the purpose of giving the fabric seal 10 a three-dimensional shape, a partial arrangement of the adhesive material 200 can be used as appropriate. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 6K, the adhesive material 200 can be partially disposed at least near the center of the fabric 100. Alternatively, the adhesive material 200 can be partially disposed at least at the corners of the fabric 100. Or the adhesive material 200 can be partially arrange | positioned at the both ends of the horizontal direction on both sides of the center area | region in the one surface of the fabric 100. As shown in FIG. This form is suitable for attachment to a mask covering the mouth, for example. Or the adhesive material 200 can be arrange | positioned in the cloth | cross area | region in the one surface of the fabric 100. FIG. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 6L, the adhesive material 200 can be disposed on substantially the entire surface of the elongated fabric 100. In the long woven fabric 100, the ratio of length to width is about 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 30, 35, 40, 45, 50. , 100, 150, 200, 250, 300, 350, 400, 450, 500, 1000, 5000, or more. Or the adhesive material 200 can be partially arrange | positioned along the long side in the area | region of at least 1 long side in the elongate fabric 100. As shown in FIG. Or it can arrange | position partially along the short side in the area | region of at least 1 short side in the fabric 100. FIG. This form is preferably applied to, for example, sticky notes. Alternatively, the adhesive material 200 can include a plurality of materials 200X and 200Y that are disposed on one fabric 100 and have different characteristics. Alternatively, the adhesive material 200 is a portion 200X (or 200Y) in which characteristics (hardness, adhesiveness, etc.) are partially changed compared to other portions 200Y (or 200X) by a predetermined process such as light treatment, heat treatment, and liquid treatment. Can be included. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the separator (mounting board) 300 is made of a sheet-like member, and for example, paper, synthetic paper (which may belong to a film or paper), film, cloth, synthetic resin, or the like can be used. In addition, the separator 300 can have a release function. In the separator 300, a release agent such as silicon can be applied to the base material. In one example, a release agent treatment (silicon treatment or the like) is performed on at least one surface of the substrate. Alternatively, in the separator 300, the substrate itself can have releasability. In this case, examples of the separator 300 include a polyolefin film (polyethylene, polypropylene), a silicon resin film, and the like. In one example of the separator 300, a resin film (polyethylene or the like) is laminated on one side or both sides of a base material, and a release agent treatment (silicone treatment or the like) is performed on at least one side. In addition, the separator 300 can also have a printing layer on which patterns, characters, and the like are printed.

  In one example, the separator 300 (release paper, release material) can have a substantially at least three-layer structure (polyethylene laminate type) including a silicone layer, a polyethylene layer, and a paper layer (quality paper, kraft paper, etc.). ). In one example, the separator 300 can have a substantially at least two-layer structure including a silicone layer and a paper layer (craft paper, parchment paper, etc.) (glassine type). In one example, the separator 300 can have a substantially at least two-layer structure including a silicone layer and supercalendered paper (supercalendered type). In one example, the separator 300 can have a substantially at least three-layer structure (clay coat type) including a silicone layer, a clay binder layer, and a paper layer (quality paper, kraft paper, etc.). In one example, the separator 300 is substantially at least three layers including a silicone layer, a water-based resin layer (polyvinyl alcohol (PVA), starch, carboxymethyl cellulose (CMC), etc.), and a paper layer (quality paper, kraft paper, etc.). Can have a structure (aqueous resin type). In one example, the separator 300 includes a silicone layer and a plastic film layer (polyethylene terephthalate (PET), stretched polypropylene (OPP), unstretched polypropylene (CPP), polyethylene (PE), etc.) substantially at least a two-layer structure. (Film type).

  7A, 7B, 7C, and 7D are diagrams showing examples of the configuration of the separator 300. FIG.

  In FIG. 7A, one separator 300 can be disposed on the entire surface of one fabric 100. Alternatively, a plurality of separators 300 can be disposed on the entire surface of one fabric 100. That is, the separator 300 can have a substantially dividing slit 302. The number of divisions of the separator 300 for one woven fabric 100 is 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or Can be 20 or more. The slits 302 can be provided so as to divide the separator 300 substantially evenly. Alternatively, the slit 302 can be provided to divide the separator 300 substantially non-uniformly. For example, considering the ease of attaching the fabric seal 10 to the object, at least one of the number, position, and shape of the slits 302 can be set. The fabric 100 often has high flexibility. By optimizing the shape of the slit 302, it is possible to avoid problems during installation such as wrinkling of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. In FIG. 7A, the axis of the overall shape of the separator 300 can be formed substantially along the warp or weft of the fabric, and the slit 302 can be formed substantially along the warp or weft of the fabric. Alternatively, the separator 300 can be formed to intersect the warp or weft of the fabric, and the slit 302 can be formed to intersect the warp or weft of the fabric.

  In FIG. 7B, separator 300 can include a relatively small size separator 300A that is removed (stripped) first, and a relatively large size separator 300B that is later removed (stripped). . The slit 302 may have a linear shape and / or a curved shape. Since the size of the separator 300A to be removed (peeled) first is relatively small, the position and posture of the fabric seal 10 with respect to the object can be easily controlled. In one example, the small size separator 300 </ b> A is disposed near the short side of the fabric seal 10. Alternatively, the small size separator 300 </ b> A is disposed near the center of the long side of the fabric seal 10. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 7C, a separator 300 </ b> C having a narrow pattern extending along the long axis direction at the center position in the width direction can be provided for the long fabric seal 10. In this case, the separator 300A or the separator 300C can be first removed (peeled) from the fabric seal 10 and the separator 300B can be removed from the fabric seal 10 later. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 7D, the overall shape axis of the separator 300 can be formed to substantially follow the warp or weft of the fabric, and the slit 302 can be formed to substantially intersect the warp or weft of the fabric. The slit 302 may have at least one of a straight line, a bent line, and a curved line. The crossing angle can be about 5, 10, 15, 20, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, or 85 °. The substantially parallel relationship between the fabric texture (warp, weft) and the overall shape of the separator 300 in the fabric seal 10 contributes to the excellent appearance of the fabric seal 10. The cross relationship between the fabric structure (warp and weft) and the slit 302 can contribute to the suppression of fatigue of the fabric 100.

  As described above, by disposing the adhesive material 200 on the fabric 100, the versatility of the fabric 100 is improved, and as a result, utilization of the fabric 100 can be promoted. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  FIG. 8A is a view showing a fabric seal (woven fabric sheet) 20 which is a modification of the embodiment shown in FIG. In the following drawings, elements substantially the same as those shown in FIGS. 1 to 7D are denoted by the same reference numerals, and description thereof is simplified or omitted.

  In FIG. 8A, a fabric seal (woven fabric sheet) 20 includes a fabric 100 and an adhesive material 200. In one embodiment, the adhesive material 200 is disposed on one side of the fabric 100. That is, in the present embodiment, the fabric sheet 20 has at least a two-layer structure including the fabric 100 and the adhesive material 200. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the adhesive material 200 can exhibit adhesiveness by being subjected to a predetermined treatment. For example, the adhesive material 200 exhibits adhesiveness when subjected to at least one of heat treatment, light treatment, liquid treatment, pressure application treatment, and the like. Examples of the adhesive material 200 include a water-soluble adhesive material, a solvent-based adhesive material, and hot melt. Examples include starch (emulsion, solvent), hot melt (UV curable, rubber, emulsion, urethane), acrylic emulsion resin adhesive, natural rubber adhesive, synthetic rubber adhesive, acrylic resin adhesive. Agents, urethane resin adhesives, silicone resin adhesives, and polyvinyl ether resin adhesives.

  In one embodiment, the pressure-sensitive adhesive material 200 is solid or semi-solid at room temperature and has low adhesiveness. By placing on the object 500 and performing a predetermined treatment, the adhesive material 200 exhibits adhesiveness, and the fabric 100 is attached to the object 500 via the adhesive material 200. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Thus, according to the above embodiment, it is possible to omit the separator 300 as compared with the embodiment of FIG. In addition, in FIG. 8A, the surface (fabric surface) of the fabric 100 can be arranged facing the object 500. In this case, the first surface 102 of the fabric 100 is observed from the side opposite to the object 500. Alternatively, the surface (fabric surface) of the fabric 100 can be disposed toward the object 500. In this case, the second surface 104 of the fabric 100 is observed through an object 500 having substantial transparency and / or having an observation window. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Alternatively, in the woven fabric sheet 20 having a two-layer structure, the adhesive material 200 can exhibit adhesiveness at room temperature. For example, as in the embodiment shown in FIG. 2G, when the fabric sheet 20 has a scroll shape, the separator can be omitted. In this case, in the scroll, the two-layer structure of the fabric 100 and the adhesive material 200 is repeated along the radial direction (thickness direction). The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  FIG. 8B is a view showing a fabric sheet 22 which is a modification of the embodiment shown in FIG. In the following drawings, elements substantially the same as those shown in FIGS. 1 to 8A are denoted by the same reference numerals, and the description thereof is simplified or omitted.

  In FIG. 8B, the fabric sheet 22 includes the fabric 100 and an attachment material 260. In one embodiment, the attachment material 260 is disposed on one side of the fabric 100. That is, in the present embodiment, the fabric sheet 22 has at least a two-layer structure including the fabric 100 and the attachment material 260. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the attachment material 260 can exhibit contractility by being subjected to a predetermined treatment (can contract (can shrink)). For example, the attachment material 260 exhibits contractility when subjected to at least one of heat treatment, light treatment, liquid treatment, pressure application treatment, and the like. Examples of the attachment material 260 include a stretched film and a heat shrink film. Examples thereof include various films such as a polystyrene film, a polyester film, a polylactic acid film, a polyvinyl chloride, a multilayer film of polyester and polystyrene. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In the example of FIG. 8B, the attachment material 260 has a substantially annular shape, and the fabric 100 is disposed on the inner surface side of the attachment material 260. Alternatively, the attachment material 260 can have a substantially non-annular shape (e.g., a belt shape) and / or at least a portion of the fabric 100 can be disposed on the outer surface side of the attachment material 260. The fabric 100 can extend over the entire circumferential direction of the attachment material 260 or can extend partially in the circumferential direction. Alternatively and / or additionally, the fabric 100 can have a fabric structure that is extensible and / or shrinkable. Alternatively and / or additionally, the fabric 100 may be functionally added with stretchability and / or shrinkage. In an example of the first stage of attachment, the attachment material 260 is disposed so as to surround the object 500. The fabric 100 (1) is firmly joined to the attachment material 260, (2) is not substantially joined to the attachment material 260, or (3) is weakly joined (for example, temporarily fixed) to the attachment material 260. be able to. In an example of the next stage, at least the attachment material 260 is contracted and attached to the object 500 by a predetermined process. The fabric 100 is also attached to the object 500. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  According to one embodiment, the use of an adhesive material between the object 500 and the fabric 100 can be avoided. In the present embodiment, the fabric 100 can be easily detached from the object 500. The removed fabric 100 is sorted or collected, for example. In addition, an adhesive between the object 500 and the fabric 100 can be used. In the example shown in FIG. 8C, the fabric 100 is observed through an attachment 260 having at least substantial transparency and / or having an observation window 262. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  FIG. 8D is a diagram showing a fabric sheet 24 which is a modification of the embodiment shown in FIG. In the following drawings, elements substantially the same as those shown in FIGS. 1 to 8C are denoted by the same reference numerals, and description thereof is simplified or omitted.

  In FIG. 8D, the fabric sheet 24 includes a fabric 100 and an attachment material 270. In one embodiment, the attachment material 270 is disposed on one side of the fabric 100. That is, in this embodiment, the fabric sheet 24 has at least a two-layer structure including the fabric 100 and the attachment material 270. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the attachment material 270 has stretchability (stretchability). An example of the attachment material 260 is an elastic member such as a stretch film. As an example, various films, such as a polyolefin-type film and a polyvinyl chloride, are mentioned.

  In the example of FIG. 8D, the attachment material 270 has a substantially annular shape, and the fabric 100 is disposed on the inner surface side of the attachment material 270. Alternatively, the attachment material 270 can have a substantially non-annular shape (eg, a band) and / or at least a portion of the fabric 100 can be disposed on the outer surface side of the attachment material 270. The fabric 100 can extend over the entire circumferential direction of the attachment material 270 or can extend partially in the circumferential direction. Alternatively and / or additionally, the fabric 100 can have a fabric structure that is extensible and / or shrinkable. Alternatively and / or additionally, the fabric 100 may be functionally added with stretchability and / or shrinkage. In an example of the stage of attachment, an attachment member 270 that is extended so as to surround the object 500 is disposed. The fabric 100 may be (1) firmly bonded to the mounting material 270, (2) not substantially bonded to the mounting material 270, or (3) weakly bonded to the mounting material 270 (eg, temporarily fixed). it can. In the attachment member 270 in the attached state, at least a part of the stretching force is released and / or the tension of the attachment member 270 is maintained. Accordingly, the attachment material 270 is attached to the object 500. The fabric 100 is also attached to the object 500. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Thus, according to the above embodiment, the use of the adhesive material between the object 500 and the fabric 100 can be avoided. In the above embodiment, the fabric 100 can be easily detached from the object 500. The removed fabric 100 is sorted or collected, for example. In addition, an adhesive between the object 500 and the fabric 100 can be used. In the example shown in FIG. 8C above, the fabric 100 is observed through at least the attachment 270 having substantial transparency and / or having an observation window 272. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 8E, the fabric sheet 26 is attached to the object 500 by in-mold molding. The fabric sheet 26 is temporarily placed in a molding die 280. In one example, at least a part of the components in the fabric 100 is melted by heat at the time of molding, and a molded product (object 500) to which the fabric 100 is attached is formed. In one example, at least a part of the material that has permeated or applied to the fabric 100 is melted by heat during molding, and a molded product to which the fabric 100 is attached is formed. In one example, at least a part of the attachment material disposed between the fabric 100 and the mold 280 is melted by heat at the time of molding, and a molded product to which the fabric 26 is attached is formed. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  FIG. 9A is a view showing a fabric seal (woven fabric sheet) 30 which is a modification of the embodiment shown in FIG. In the following drawings, elements substantially the same as those shown in FIGS. 1 to 8E are denoted by the same reference numerals, and the description thereof is simplified or omitted.

  9A, a fabric seal (woven fabric sheet) 30 includes a fabric 100, an adhesive material 200, and a separator 300. Further, the fabric sheet 30 includes a supplementary sheet 340. The adhesive material 200 includes a first adhesive material 200 </ b> A disposed between the fabric 100 and the auxiliary sheet 340, and a second adhesive material 200 </ b> B disposed between the auxiliary sheet 340 and the separator 300. In other words, the second adhesive material 200B is disposed on one surface of the auxiliary sheet 340, which is the surface opposite to the first adhesive material 200A. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the second adhesive material 200B is disposed on the separator 300, and the auxiliary sheet 340 is disposed on the second adhesive material 200B. Furthermore, the first adhesive material 200A is disposed on the auxiliary sheet 340, and the fabric 100 is disposed on the first adhesive material 200A. That is, in this embodiment, the fabric seal 30 has at least a five-layer structure. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 is made of, for example, a film, paper, synthetic paper (which may belong to film or paper), cloth, synthetic resin, or the like. These may be used alone or in combination. Typically, as the auxiliary sheet 340, polyester film (including matte PET and foamed PET), polypropylene film, polystyrene film, synthetic paper (YUPO (registered trademark), Povic (registered trademark), peach coat (registered trademark), and the like ), Vinyl chloride film, olefinic film, polyimide film, inkjet printing compatible film, thermal printing compatible film, thermal transfer printing compatible film, electrophotographic printing compatible film, thermal suncut film, hologram film, satin, fine paper (colorless, color) High quality paper), coated paper, art paper, cast coated paper, super cast paper, foil paper (including gold foil and silver foil), Japanese paper, water resistant paper, kraft paper, recycled paper, impregnated paper (polymer on paper) Resin impregnated), Kent paper (MS Kent paper) Thermal paper (general thermal paper, heat-resistant thermal paper, glossy thermal paper, two-color luminescent thermal paper, thermal paper for long-term storage, YUPO thermal paper (registered trademark)), printing paper, carbonless paper, matte coated paper, none Examples include dust paper, special paper (waterproof paper, fluorescent paper, etc.), inkjet printing compatible film, thermal printing compatible film, thermal transfer printing compatible film, and electrophotographic printing compatible film.

  Examples of the film material used for the auxiliary sheet 340 include an ionomer film (IO film), a polyethylene film (PE film), a polyvinyl chloride film (PVC film), a polyvinylidene chloride film (PVDC film), and a polyvinyl alcohol film (PVA film). ), Polypropylene film (PP film), polyester film, polycarbonate film (PC film), polystyrene film (PS film), polyacrylonitrile film (PAN film), ethylene vinyl acetate copolymer film (EVA film), ethylene-vinyl alcohol Polymer film (EVOH film), ethylene-methacrylic acid copolymer film (EMAA film), nylon film (NY film, Polyamide (PA) films), such as cellophane and the like. As a film material used for the auxiliary sheet 340, various metals and magnetic materials are also applicable. These may be used alone or in combination. The film material is not limited to the above example.

  As paper materials used for the supplementary sheet 340, Western paper (including high-quality paper, coated paper (including coated paper, art paper, lightweight coated paper, cast paper, cast coated paper, supercast paper, glossy, matte, etc.), Foil paper, craft paper, recycled paper, synthetic paper, impregnated paper, Kent paper, thermal paper, printing paper, carbonless paper, matte coated paper, dust-free paper, special paper, release paper, glassine paper, tracing paper, sulfuric acid paper, Including paraffin paper, acid paper, etc.), Japanese paper (including hemp paper, cereal paper, cocoon paper (crusted paper), sandpaper (Mutsu paper), etc.), paperboard (cardboard base paper, cardboard (white paperboard), chipball, (Including yellow balls) and synthetic paper. These may be used alone or in combination. The paper material is not limited to the above example.

  Examples of the cloth material used for the supplementary sheet 340 include denim, fleece, velvet, toweling, suede, corduroy, linen, satin, cotton satin, gauze, double gauze, gingham, cotton voile, cotton twill, organge, and willow ( Ryoru), twill weave, crepe, flannel, pile, velvet, flannel, bettin, velor, canvas, blanket, rasha, carako, stretch broad, exposure, sheeting, chiffon, shantung, georgette, new moss, broad, boil , Muslin, linen mask, waffle weave, calligraphy, yellow Hachijo, Shiose, upper cloth, cocoon, chirimen (shrinking), Nishijin, Hanae, Fuji silk, Honshu, meisen, cotton candy, yukata robe, Rinzu, Silk thread, core yarn, shirring, chambray, stretch Slabs, ripple, flat woven, and so forth twill (twill), or satin thereof. These may be used alone or in combination. The cloth and the material thereof are not limited to the above example.

  Synthetic resins used for the auxiliary sheet 340 include phenol resin (PF), epoxy resin (EP), melamine resin (MF), urea resin (urea resin, UF), unsaturated polyester resin (UP), alkyd resin, polyurethane. (PUR), thermosetting polyimide (PI) polyethylene (PE) (including high density polyethylene (HDPE), medium density polyethylene (MDPE), low density polyethylene (LDPE)), polypropylene (PP), polyvinyl chloride (PVC) ), Polyvinylidene chloride, polystyrene (PS), polyvinyl acetate (PVAc), Teflon (registered trademark) (polytetrafluoroethylene, PTFE), ABS resin (acrylonitrile butadiene styrene resin), AS resin, acrylic resin (PMMA), Polyamide (PA) (Nylon ), Polyacetal (POM), polycarbonate (PC), modified polyphenylene ether (m-PPE, modified PPE, PPO), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), glass fiber reinforced polyethylene terephthalate (GF-PET) , Cyclic polyolefin (COP), polyphenylene sulfide (PPS), polysulfone (PSF), polyethersulfone (PES), amorphous polyarylate (PAR), liquid crystal polymer (LCP), polyetheretherketone (PEEK), heat Examples thereof include plastic polyimide (PI) and polyamideimide (PAI). These may be used alone or in combination. The synthetic resin is not limited to the above example.

  The auxiliary sheet 340 may have a single layer structure or a multilayer structure. The substantial number of layers of the auxiliary sheet 340 is 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, Or it can be 20 or more. The auxiliary sheet 340 can also have a print layer on which a picture, a pattern, a character, or the like is printed.

  As shown in FIG. 9A, in one embodiment, it is possible to remove (peel) at least a portion of the separator 300 from one surface of the auxiliary sheet 340 while leaving the second adhesive material 200B on one surface of the auxiliary sheet 340. In the fabric seal 30 from which the separator 300 has been removed, at least a part of the second adhesive material 200B is exposed. The fabric seal 30 can be attached to the object 500 through the exposed second adhesive material 200B. For example, the fabric seal 30 from which the separator 300 is removed is attached to the object 500 by using the adhesive force of the second adhesive material 200B by bringing the second adhesive material 200B having adhesiveness into contact with the object 500. Can do. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the fabric 100 may have at least one of a color, a pattern, a character, a design, and the like. In the fabric 100 attached to the object 500, at least one of its color, pattern, character, design, etc. can be observed.

  In one example, the fabric seal 30 can be observed from the side opposite the object 500. In this case, the first surface 102 of the fabric 100 faces the observation side space. In another example, the fabric seal 30 may be observed through an object 500 that has substantial transparency and / or has an observation window. That is, the back surface (second surface 344) of the auxiliary sheet 340 is observed from the object 500 side. In this case, the second surface 344 of the auxiliary sheet 340 faces the observation side space through the object 500. When the auxiliary sheet 340 has a printing layer, a picture, a pattern, a character, or the like on the auxiliary sheet 340 can be observed through the object 500. In yet another example, both sides of the fabric seal 30 are observed. In other words, the first surface 102 of the fabric 100 is observed from the side opposite to the object 500, and the second surface 344 of the auxiliary sheet 340 passes through the object 500 having substantial transparency and / or having an observation window. Can be observed.

  In one embodiment, by attaching the fabric seal (woven fabric sheet) 30 to the object 500, the appearance characteristics and functional characteristics of the fabric seal 30 can be imparted to the object 500. For example, when the fabric 100 is a silk fabric, the silk fabric 100 contributes to the eye-catching appearance of the object 500 to which the fabric seal 30 (silk fabric seal 30) is attached. Alternatively, the silk fabric seal 30 contributes to the development of functions other than the appearance of the object 500 to which the silk fabric seal 30 is attached. The use of the silk fabric 100 is promoted by increasing the number of objects 500 to which the silk fabric seal 30 is attached.

  As a material used for the auxiliary sheet 340, a functional material having a predetermined function can be used. Functions include, for example, optical properties (antireflection properties, electromagnetic wave shielding properties, antistatic properties, light shielding properties, frequency selectivity, polarization properties, filter properties, light resistance, etc.), moisture permeability, water permeability, water absorption, peelability, Delamination, shape stability, punching, reinforcement, water resistance, fire resistance, heat resistance, non-permeability, shape following, shape retention, shape stability, ease of processing, static electricity removal, cushioning (Buffering), solvent resistance, insulation, shrinkage, extensibility, oil resistance, chemical resistance (alkali resistance, acid resistance, etc.), design, magnetism, conductivity, printability, photosensitivity, protection, Examples include rust prevention, releasability, decoration, stretchability, biodegradability, and antibacterial properties. For example, as an example of a functional film, an antireflection film, an alignment film, a polarizing film, a polarizing layer protective film, an optical compensation film (a retardation film, a viewing angle improving film, etc.), a luminance improving film, an electromagnetic wave shielding film, a light shielding film, Specific frequency selective blocking film, optical low-pass filter, weather-resistant film, conductive film, printed circuit board film, photosensitive film, protective film (including protective film, masking film, release film, rust-proof film), transfer film, polishing Examples include films, decorative films, biodegradable films, and antibacterial films. The functional material is not limited to the above example.

  The embodiment shown in FIGS. 2A to 2B, 2F to 2I, 3A to 5, 6A to 7D, and 8B to 8E is similarly applied to the fabric seal (woven fabric sheet) 30. Is possible.

  In one embodiment, the physical or chemical properties of the fabric seal (textile sheet) 30 may be supplemented by a supplementary sheet 340. In an example in which the relatively soft fabric 100 is used, the fabric seal (woven fabric sheet) 30 is relatively high even when the separator 300 is peeled off by integrating the fabric 100 with the auxiliary sheet 340 having relatively high rigidity. It can have rigidity. In another example in which an uneven surface is a target to be pasted, the auxiliary sheet 340 having a relatively high stretchability easily follows the surface shape of the fabric 100 and suppresses generation of wrinkles in the fabric seal (woven fabric sheet) 30. obtain. Alternatively, it is possible to improve the curved surface compatibility of the fabric seal (woven fabric sheet) 30 by the auxiliary sheet 340 having relatively high stretchability. In another example, the auxiliary sheet 340 may have a function of preventing moisture from entering from outside and releasing moisture from inside. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, as shown in FIG. 9B, the auxiliary sheet 340 includes a folding key (an auxiliary portion (auxiliary line) that will be a crease in the future, a mold for folding) 348. The folded 348 can be processed on one side or both sides of the auxiliary sheet 340. The fabric seal 30 can be easily folded by the folding key 348. The fabric seal 30 can be easily processed into a three-dimensional shape by the folded 348. By the folding 348 of the auxiliary sheet 340, the fabric 100 having a relatively high flexibility can be easily folded at a predetermined position, and the folded state can be easily maintained. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100. The folded 348 can be formed substantially along the warp or weft of the fabric 100, or so as to intersect the warp or weft (eg, the intersection angle is about 5, 10, 15, 20, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, or 85 °). These can be selected and set according to the usage form, usage environment, characteristics of the adhesive material, and the like. Folding along the warp or weft can contribute to the ease of folding the fabric 100. Folding quay that intersects the warp or weft can contribute to suppression of bending fatigue of the fabric 100. As an auxiliary part (auxiliary line) that will be a crease in the future, it is possible to adopt a form other than the folding key. In one example, a partial film (linear film, area film) can be disposed on the auxiliary sheet 340. In another example, the auxiliary sheet 340 may have a tissue structure that assists folding. In yet another example, the auxiliary sheet 340 may have a form in which the thickness structure and / or flexibility is partially changed within one surface. The change in the thickness structure and / or flexibility of the auxiliary sheet 340 may include at least one change in the thickness of the auxiliary sheet 340, the number of layers of the auxiliary sheet 340, and the front surface and / or the back surface treatment material (such as a coating material). it can. In addition, when forming the folding key 348 on the auxiliary sheet 340, the folding key or processing trace may remain on other members. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the predetermined function of the auxiliary sheet 340 can be expressed, controlled, strengthened, or promoted by the first adhesive material 200A and / or the second adhesive material 200B. For example, a predetermined function can be expressed, controlled, strengthened, or promoted by a combination of the auxiliary sheet 340 and the first adhesive material 200A. Alternatively, the predetermined function can be expressed, controlled, strengthened, or promoted by a combination of the auxiliary sheet 340 and the second adhesive material 200B. Alternatively, the predetermined function can be expressed, controlled, strengthened, or promoted by a combination of the auxiliary sheet 340, the first adhesive material 200A, and the second adhesive material 200B. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the first adhesive material 200A and the second adhesive material 200B can have the same specifications or different specifications. The specifications of the second adhesive material 200B include, for example, the surface specification (for example, material, outer shape, surface roughness, etc.) of the object (500), the specification of the auxiliary sheet 340, and / or the use of the fabric seal (woven fabric sheet) 30. It is selected according to the purpose. For example, the specifications of the second adhesive material 200B are set according to specifications required for the fabric seal (woven fabric sheet) 30 (e.g., returnable, retard, weak viscosity, etc.). The specification of the first adhesive material 200A is selected according to, for example, the specification of the fabric 100, the specification of the auxiliary sheet 340, and / or the purpose of use of the fabric seal (woven fabric sheet) 30. Even when the first adhesive material 200 </ b> A and the second adhesive material 200 </ b> B are different from each other, the auxiliary sheet 340 can avoid contact or mixing between the two. This is advantageous in maintaining the chemical stability of the first adhesive material 200A and the second adhesive material 200B, for example. In one example, the first adhesive material 200A is a hot-melt adhesive material (such as a thermoplastic resin), and the second adhesive material 200B is a water-soluble adhesive material. The type of combination of the first adhesive material 200A and the second adhesive material 200B can be variously changed. By arranging the auxiliary sheet 340 between the first adhesive material 200A and the second adhesive material 200B, the specification of the first adhesive material and / or the second adhesive material 200B can be easily optimized. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, each of the first adhesive material 200A and the second adhesive material 200B can be a single layer or a substantially multiple layer. In the first adhesive material 200 </ b> A, specifications (materials and characteristics) and the like can be different between the surface in contact with the fabric 100 and the surface in contact with the auxiliary sheet 340. In the second adhesive material 200 </ b> B, specifications (materials and characteristics) and the like can be different between the surface in contact with the auxiliary sheet 340 and the surface in contact with the separator 300. For example, as shown in FIG. 9C, in the multi-layer adhesive material 200A, specifications between the layer 204 in contact with the fabric 100 and the layer 205 in contact with the auxiliary sheet 340 (material, hardness, thickness, color, transparency, pattern, etc.) Can be different. Alternatively, the specifications (material, hardness, thickness, color, transparency, pattern, etc.) may differ between the layer 206 in contact with the fabric 100 and the layer 207 in contact with the auxiliary sheet 340 in the multi-layer adhesive material 200B. The number of stacks can be 2, 3, 4, 5, 6, 7, 8, 9, 10, or more. Further, the first adhesive material 200A and the second adhesive material 200B can be partially different in material, characteristics, etc. in the plane. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one example, the auxiliary sheet 340 can have excellent processability compared to the fabric 100 with respect to a blade for cutting or punching the fabric 100. In one example, the auxiliary sheet 340 can have a higher density than the fabric 100. In one example, the first pressure-sensitive adhesive material 200A can have stronger adhesiveness (stickiness, bondability) and / or higher hardness (high viscosity) than the second pressure-sensitive adhesive material 200B. In one example, a blade is inserted into the multilayer from above the fabric 100 during cutting or stamping. The blade first contacts the fabric 100. Subsequently, the blade contacts the auxiliary sheet 340 via the first adhesive material 200A, and further contacts the separator 300 via the second adhesive material 200B. Due to the presence of the auxiliary sheet 340 and the first adhesive material 200 </ b> A, the moving distance of the blade after contacting the fabric 100 can be increased. Alternatively, the auxiliary sheet 340 supports the fabric 100 from the back side, so that deformation (bending, etc.) and displacement (escape) of the fabric 100 during processing can be suppressed. The fact that the first pressure-sensitive adhesive material 200A has relatively strong adhesiveness (tackiness) and / or relatively high hardness (high viscosity) is advantageous in suppressing deformation and escape of the fabric 100 during processing. The long movement distance of the blade and the suppression of deformation and escape of the fabric 100 during processing are advantageous for improving the workability of the fabric 100. Such an improvement in workability can contribute to, for example, prevention of processing omission in which part of the yarn in the woven fabric 100 is not cut. This is particularly advantageous for processing fabric 100 having relatively thin threads. Due to the presence of the first adhesive material 200A, fraying of the yarn in the processed portion after cutting or punching is suppressed. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 and / or the first adhesive material 200A can function as a barrier layer for the second adhesive material 200B (a penetration preventing layer of the second adhesive material 200B). The auxiliary sheet 340 and / or the first adhesive material 200A can widen the selectivity in the type and viscosity of the second adhesive material 200B. Furthermore, the auxiliary sheet 340 and / or the first pressure-sensitive adhesive 200 </ b> A can exhibit a function of complementing the flexibility of the fabric 100. By using the appropriate auxiliary sheet 340 and / or the first adhesive material 200A, the auxiliary sheet 340 and / or the first adhesive material 200A can strengthen the fabric 100. The auxiliary sheet 340 and / or the first pressure-sensitive adhesive material 200 </ b> A is a solution to the problem related to liquid permeability on the tissue structure, which is one of the characteristics of the fabric 100, and the problem related to flexibility, which is another characteristic of the fabric 100. To contribute. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Alternatively or additionally, the auxiliary sheet 340 can function as a barrier layer (preventing penetration of an external substance) against a predetermined substance toward the second adhesive material 200B. In this case, for example, the predetermined substance may reduce the function of the second adhesive material 200B. The auxiliary sheet 340 can have a function of suppressing, preventing, and / or blocking a predetermined substance from the outside from passing through the fabric 100 and reaching the second adhesive material 200B. In one example, the function of the second adhesive material 200B (decrease in adhesive force, separation and / or peeling) is suppressed by suppressing the arrival of moisture through the fabric 100 to the second adhesive material 200B. 2 Adhesive performance of the adhesive material 200B can be stably maintained. By selectively using the auxiliary sheet 340 that is excellent in moisture blocking properties, it is possible to suppress the functional deterioration of the second adhesive material 200B due to moisture. Alternatively or additionally, the auxiliary sheet 340 can be treated to enhance moisture barrier properties. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one example, the auxiliary sheet 340 and the first adhesive material 200 </ b> A can be disposed on substantially the entire surface of the fabric 100. In another example, the auxiliary sheet 340 and the first pressure-sensitive adhesive material 200 </ b> A can be partially disposed on one surface of the fabric 100. For example, in the partial arrangement, the auxiliary sheet 340 and the first adhesive material 200 </ b> A can be arranged at a part including at least the processing position of the fabric 100. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 can have delamination properties. In this case, as shown in FIG. 9D, the auxiliary sheet 340 can be delaminated to relatively easily peel the fabric 100 from the object 500. This is advantageous for collecting the fabric 100 (seals and labels, etc.). In addition, the complementary sheet 340 can have at least one of a color, a pattern (pattern), a character, a design (design), and the like that can be observed when delamination is performed. In one example, the auxiliary sheet 340 can have a printed layer 341 including colors, patterns, characters, etc. that can be observed on the surface of the layer left on the object 500 when delaminated. Additionally or alternatively, the auxiliary sheet 340 can be observed on the surface of a layer peeled off from the object 500 (a layer separated from the object 500 by peeling) when delaminated. The printing layer 342 can be included. The print layers 341 and 342 may include at least one of information on the object 500, an identification code of the object 500, information on the fabric 100, an identification code of the fabric 100, and other information, for example. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the second adhesive material 200B may include a material (such as a water-soluble adhesive material) that can be easily peeled off mainly with water. In this case, as shown in FIG. 9E, the laminate of the fabric 100 and the auxiliary sheet 340 can be peeled off from the object 500 relatively easily. This is advantageous for collection of the fabric 100 (seals and labels, etc.), disposal of the fabric seal 30 and the like. In addition, the complementary sheet 340 may have at least one of a color, a pattern (pattern), a character, and a design (design) that can be observed when peeled. In one example, the auxiliary sheet 340 can have a printed layer 343 that includes colors, patterns, characters, etc. that are observable on the exposed surface when peeled. The print layer 343 can include, for example, at least one of information on the object 500, an identification code of the object 500, information on the fabric 100, an identification code of the fabric 100, and other information. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  9F and 9G are diagrams each schematically showing an enlarged cross-sectional structure of the fabric seal 30. FIG. In one embodiment, the penetration rate of the first adhesive material 200 </ b> A with respect to the material (yarn) of the fabric 100 can be controlled. The penetration rate of the first adhesive material 200A into the material (yarn) of the fabric 100 (for example, the weight ratio of the adhesive material to the yarn) is about 1, 2, 3, 4, 5, 6, 7, 8, 9 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 110, 120, 130, 140, 150, 160, 170, 180, 190, 200%, or more. Alternatively, the penetration of the first adhesive material 200A into the material (yarn) of the fabric 100 can be made substantially zero. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. In the fabric seal (woven fabric sheet) 30 having a high permeability, high rigidity and strength can be obtained. In the fabric seal (woven fabric sheet) 30 with a low penetration rate, deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 associated with the penetration of the first adhesive material 200A is suppressed. In an example of low penetration, the penetration rate is 0% or more and 150% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 100% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 80% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 50% or less by weight. Alternatively, in one example of low penetration, the penetration rate is 0% or more and 20% or less by weight. The penetration rate can be set according to, for example, the usage form and usage environment of the fabric seal (fabric sheet) 30, the characteristics of the adhesive material, and the like. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the penetration rate of the first adhesive material 200A with respect to the fabric 100 is controlled. 9F and 9G, the distance h1 that the first adhesive material 200A enters in the gap between the texture structures of the fabric 100 is about 90, 80, 70, 60, 50, 40, 30, 20, It can be 10, 9, 8, 7, 6, 5, 4, 3, 2, 1% or less (entrance rate). Alternatively, the entry of the first adhesive 200A into the gap of the tissue structure of the fabric 100 can be made substantially zero. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. In the fabric seal (woven fabric sheet) 30 having a high penetration rate, high rigidity and strength can be obtained. In the fabric seal (woven fabric sheet) 30 with a low penetration rate, the degradation of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 associated with the entry of the first adhesive material 200A is suppressed. In an example of low approach, the approach rate is 0% or more and 50% or less. Or in an example of low approach, an approach rate is 0% or more and 40% or less. Or in an example of low approach, an approach rate is 0% or more and 30% or less. Or in an example of low approach, an approach rate is 0% or more and 20% or less. Or in an example of low approach, an approach rate is 0% or more and 10% or less. Or in an example of low approach, an approach rate is 0% or more and 5% or less. The approach rate can be set according to, for example, the usage pattern and usage environment of the fabric seal (woven fabric sheet) 30, the characteristics of the adhesive material, and the like. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one Embodiment, the presence or absence of the space | gap (209) between the fabric 100 and the surface of the 1st adhesive material 200A or its ratio is controlled. In FIG. 9F, the fabric 100 and the first adhesive material 200A are in intimate contact, and there is substantially no gap between the fabric 100 and the surface of the first adhesive material 200A. That is, the entire surface facing the first adhesive material 200A of the surface of the yarn of the fabric 100 is in contact with the first adhesive material 200A. In other words, there is substantially no gap (space) surrounded by the warp, weft, and first adhesive material 200A. In such a low gap fabric seal (fabric sheet) 30, high rigidity and strength can be obtained. In FIG. 9G, the fabric 100 and the first adhesive material 200A are loosely in contact with each other, and there is a gap 209 between the fabric 100 and the surface of the first adhesive material 200A. In other words, at least a part of the surface of the yarn of the fabric 100 facing the first adhesive material 200A is not in contact with the first adhesive material 200A. Alternatively, in the fabric seal (woven fabric sheet) 30 in FIG. 9G, there is a space (space) 209 surrounded by the warp yarn, the weft yarn and the first adhesive material 200A. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. In the fabric seal (woven fabric sheet) 30 having a large number of voids 209, deterioration of the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 due to the influence of the adhesive material 200A is suppressed. The presence / absence of the gap 209 and the ratio thereof can be set according to, for example, the usage form and usage environment of the fabric seal (woven fabric sheet) 30, the characteristics of the adhesive material, and the like. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the surface shape of the first adhesive material 200A on the side facing the fabric 100 can be controlled. One surface of the fabric 100 includes a fine uneven structure. The shape of the surface of the first pressure-sensitive adhesive 200 </ b> A that is at least partially in contact with the fine concavo-convex structure of the fabric 100 is controlled. The surface shape of the first adhesive 200 </ b> A varies depending on the manufacturing process and conditions of the fabric seal (woven fabric sheet) 30. The manufacturing process and conditions of the fabric seal (fabric sheet) 30 can be selected so that a surface shape that gives the fabric 100 high rigidity and strength can be obtained. In addition, a fabric seal (fabric sheet) is provided so that a surface shape that suppresses deterioration of the inherent properties (appearance properties, feel, flexibility, texture, etc.) of the fabric 100 due to the influence of the first adhesive material 200A can be obtained. Thirty manufacturing processes and conditions can be selected. In these, as a target region, a portion (edge, edge, etc.) subjected to local processing (strengthening processing, etc.) can be removed. The manufacturing process and conditions can be set according to, for example, the usage form and usage environment of the fabric seal (woven fabric sheet) 30, the characteristics of the adhesive material, and the like. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  As shown in FIG. 9H, an example of the manufacturing process of the fabric seal 30 includes: (a) a step of placing the first adhesive material 200A on one surface of the fabric 100; A step of performing a treatment, a drying treatment, and / or other treatments, (b) a step of disposing the second adhesive material 200B on one surface of the separator 300, a heat treatment, an optical treatment, or the like on the second adhesive material 200B as necessary. A process of performing a drying process and / or other processes, (c) a process of disposing the auxiliary sheet 340 on one surface of the separator 300 via the second adhesive material 200B, and (d) a laminate including the separator 300 and the auxiliary sheet 340. A process of placing the fabric 100 on the first adhesive material 200A on top, and a process of performing predetermined processing (for example, cutting, edge processing, edge processing, etc.) on the laminate as necessary Including.

  As shown in FIG. 9I, an example of the manufacturing process of the fabric seal 30 includes (a) a step of placing the first adhesive material 200A on one surface of the fabric 100, and heat treatment and light for the first adhesive material 200A as necessary. A process of performing a treatment, a drying process, and / or other processes, (b) a process of arranging the second adhesive material 200B on one surface of the auxiliary sheet 340, and a heat treatment or an optical treatment for the second adhesive material 200B as necessary. A step of performing a drying process and / or other processes, (c) a step of placing the separator 300 on one surface of the auxiliary sheet 340 via the second adhesive material 200B, and (d) a lamination including the separator 300 and the auxiliary sheet 340 A step of placing the woven fabric 100 on the body via the first adhesive material 200A, and a step of performing predetermined processing (for example, cutting, edge processing, end processing, etc.) on the laminate as necessary. No.

  As shown in FIG. 9J, an example of the manufacturing process of the fabric seal 30 includes (a) a step of placing the first adhesive material 200A on one surface of the auxiliary sheet 340, and heat treatment for the first adhesive material 200A as necessary. A step of performing a light treatment, a drying treatment, and / or other treatments, (b) a step of placing the fabric 100 on one side of the auxiliary sheet 340 via the first adhesive material 200A, and (c) a second side of the separator 300. A step of disposing the adhesive material 200B, a step of subjecting the second adhesive material 200B to heat treatment, light treatment, drying treatment, and / or other treatment as needed, (d) a separator through the second adhesive material 200B A step of arranging a laminated body including the fabric 100 and the auxiliary sheet 340 on one surface of 300, and a step of performing predetermined processing (for example, cutting, edge processing, edge processing, etc.) on the laminated body as necessary. Including.

  As shown in FIG. 9K, an example of the manufacturing process of the fabric seal 30 includes (a) a step of placing the first adhesive material 200A on one surface of the auxiliary sheet 340, and heat treatment for the first adhesive material 200A as necessary. A step of performing a light treatment, a drying treatment, and / or other treatments; (b) a step of placing the second adhesive material 200B on one surface of the separator 300; and a heat treatment or a light treatment for the second adhesive material 200B as necessary. A step of performing a drying process, and / or other processes, (c) a step of disposing the auxiliary sheet 340 on one surface of the separator 300 through the second adhesive material 200B, and (d) a lamination including the auxiliary sheet 340 and the separator 300. A process of placing the fabric 100 on the body via the first adhesive material 200A, and a process for performing predetermined processing (for example, cutting, edge processing, edge processing, etc.) on the laminate as necessary. Including the.

  As shown in FIG. 9L, an example of the manufacturing process of the fabric seal 30 includes: (a) a step of placing the second adhesive material 200B on one surface of the separator 300; A process of performing a process, a drying process, and / or other processes, (b) a process of disposing the auxiliary sheet 340 on one surface of the separator 300 via the second adhesive material 200B, and (c) including the separator 300 and the auxiliary sheet 340. A step of disposing the first pressure-sensitive adhesive material 200A on one surface of the laminate, a step of performing heat treatment, light treatment, drying treatment, and / or other treatment on the first pressure-sensitive adhesive material 200A as needed, (d) a supplementary sheet 340 and the process which arranges textiles 100 on the layered product containing separator 300 via the 1st adhesive material 200A, and predetermined processing (for example, cutting, etc.) to a layered product as needed Part processing comprises performing such end treatment).

  As shown in FIG. 9M, an example of the manufacturing process of the fabric seal 30 is as follows: (a) a step of arranging the first adhesive material 200A on one surface of the auxiliary sheet 340 and arranging the second adhesive material 200B on the other surface. , A step of performing heat treatment, light treatment, drying treatment, and / or other treatment on the first pressure-sensitive adhesive material 200A and the second pressure-sensitive adhesive material 200B as required, (b) a complementary sheet via the second pressure-sensitive adhesive material 200B A step of disposing the separator 300 on one side of 340, (c) a step of disposing the fabric 100 on the laminate including the auxiliary sheet 340 and the separator 300 via the first adhesive material 200A, and if necessary, the laminate It includes a step of performing predetermined processing (for example, cutting, edge processing, edge processing, etc.).

  As shown in FIG. 9N, FIG. 9O, FIG. 9P, FIG. 9Q, and FIG. 9R, in at least one step of the manufacturing process of the fabric seal 30, a temporary separator ( Cover sheet, protective sheet) 1300A, 1300B, 1300C can be used at least temporarily. Temporary separators 1300A, 1300B, and 1300C are used, for example, in a semi-finished product stage. In one example, temporary separators 1300A, 1300B, and 1300C are attached to a predetermined base material (for example, auxiliary sheet 340, separator 300) on which adhesive materials (for example, first adhesive material 200A and second adhesive material 200B) are arranged. In addition, the adhesive material (200A, 200B) can be left and peeled off from the base material (340, 300). In one example, adhesive materials (for example, the first adhesive material 200A and the second adhesive material 200B) are disposed on the temporary separators 1300A, 1300B, and 1300C, and the temporary separator 1300A is interposed via the adhesive materials (200A and 200B). , 1300B, 1300C are attached to a predetermined substrate (for example, the fabric 100, the auxiliary sheet 340, the separator 300). Further, in one example, a predetermined base material on which the adhesive materials (200A, 200B) are arranged while peeling the temporary separators 1300A, 1300B, 1300C from the adhesive materials (for example, the first adhesive material 200A, the second adhesive material 200B). (For example, the fabric 100, the auxiliary sheet 340, the separator 300) and another base material (for example, the fabric 100, the auxiliary sheet 340, the separator 300) are bonded together. In one example, adhesive materials (for example, the first adhesive material 200A and the second adhesive material 200B) are disposed on the temporary separators 1300A, 1300B, and 1300C, and the temporary separator 1300A is interposed via the adhesive materials (200A and 200B). , 1300B, 1300C are attached to the other temporary separators 1300A, 1300B, 1300C.

  The manufacturing process of the fabric seal 30 is not limited to the above example. The treatment for a roll-shaped (roll-shaped) base material can be applied as appropriate. The substrate or semi-finished product can be provided in the form of a sheet or a roll. The use of a scroll is advantageous for improving the production capacity. For example, a scroll made only of a predetermined base material is provided. For example, a scroll is provided in which a plurality of layers including at least one substrate are repeated in the radial direction. For example, at the time of bonding a predetermined base material and another base material, at least one base material can be used as a scroll. An example of the manufacturing process of the roll-shaped fabric seal 30 further includes a step of unwinding the base material, a step of winding up the treated base material, and the like. In the scroll in one example, the lamination of the fabric 100, the first adhesive material 200A (or the second adhesive material 200B), and the auxiliary sheet 340 is repeated along the radial direction. By providing the fabric seal (woven fabric sheet) 30 in the form of a scroll, the separator 300 can be omitted. In an example of this case, in the scroll, the lamination of the fabric 100, the first adhesive material 200A, the auxiliary sheet 340, and the second adhesive material 200B is repeated along the radial direction. The removal of the separator 300 is advantageous for cost reduction and scroll size reduction. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the heat treatment temperature for the first pressure-sensitive adhesive material 200A and the second pressure-sensitive adhesive material 200B is appropriately set according to the pressure-sensitive adhesive material used, the type of base material, and the like. In the manufacturing process, the heat treatment temperature can be substantially the same or different from each other between the first adhesive material 200A and the second adhesive material 200B. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In the process of disposing another base material on one base material via an adhesive material, the adhesive material can be softened by heat treatment, or at least a part can be melted by heat treatment. With proper temperature control, a high quality fabric seal can be obtained. In this case, the heat treatment temperature can be set according to, for example, the use form and use environment of the fabric seal (woven fabric sheet), the fabric structure, the properties of the adhesive (softening temperature, melting temperature), and the like.

  In one embodiment, as shown in FIGS. 9S and 9T, one surface of the auxiliary sheet 340 in contact with the first adhesive material 200A can have a substantially uneven structure. In FIG. 9S, one surface 349 of the auxiliary sheet 340 has a plurality of protrusions 345. The shape, number (density), and / or rigidity of the protrusions 345 can be set according to, for example, the use form and use environment of the fabric seal (woven fabric sheet), the structure of the fabric 100, the characteristics of the adhesive material, and the like. . In FIG. 9T, a plurality of particles 346 are arranged on one surface 349 of the auxiliary sheet 340. Alternatively, the first adhesive material 200 </ b> A on the auxiliary sheet 340 includes a plurality of particles 346. The shape, number (density), and / or rigidity of the particles 346 can be set according to, for example, the use form and use environment of the fabric seal (fabric sheet) 10, the structure of the fabric 100, the characteristics of the adhesive material, and the like. . The fact that one surface of the auxiliary sheet 340 in contact with the first pressure-sensitive adhesive material 200A has a substantially uneven structure can be advantageous for increasing the contact area between the fabric 100 and the first pressure-sensitive adhesive material 200A / securing the bonding force. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  FIG. 10A, FIG. 10B, and FIG. 10C are diagrams showing a fabric seal (fabric sheet) 40, which is a modification of the form shown in FIG. 9A. In the following drawings, elements substantially the same as those shown in FIGS. 1 to 9T are denoted by the same reference numerals, and the description thereof is simplified or omitted.

  10A and 10B, a fabric seal (fabric sheet) 40 includes a fabric 100, an adhesive material 200, and a separator 300, similarly to the fabric seal 30 of FIG. 9A. Further, the fabric sheet 40 includes a supplementary sheet 340. The adhesive material 200 includes a first adhesive material 200 </ b> A disposed between the fabric 100 and the auxiliary sheet 340, and a second adhesive material 200 </ b> B disposed between the auxiliary sheet 340 and the separator 300. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the second adhesive material 200B is disposed on the separator 300 and the auxiliary sheet 340 is disposed on the second adhesive material 200B, similarly to the fabric seal 30 of FIG. 9A. Furthermore, the first adhesive material 200A is disposed on the auxiliary sheet 340, and the fabric 100 is disposed on the first adhesive material 200A. That is, in this embodiment, the fabric seal 30 has at least a five-layer structure. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 can be peeled from the separator 300. At this time, the fabric 100 is disposed on one surface of the auxiliary sheet 340 via the first adhesive material 200 </ b> A, and the second adhesive material 200 </ b> B is disposed on the other surface of the auxiliary sheet 340. As shown in FIG. 10C, the auxiliary sheet 340 on which the fabric 100 is mounted can be disposed on the object 500. Furthermore, the fabric 100 can be peeled from the auxiliary sheet 340 on the object 500. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the separator (mounting paper) 300 is made of a sheet-like member and has a releasing function with respect to the auxiliary sheet 340, as in the embodiment of FIG. The auxiliary sheet 340 has a mold release function with respect to the fabric 100. That is, in the auxiliary sheet 340, a release agent such as silicon can be applied to the base material. In one example, a release agent treatment (silicon treatment or the like) is performed on at least one surface of the substrate. Alternatively, in the auxiliary sheet 340, the base material itself can have releasability. In this case, a polyolefin film (polyethylene, polypropylene), a silicon resin film, etc. are mentioned as an example. In one example of the separator 300, a resin film (polyethylene or the like) is laminated on one side or both sides of a base material, and a release agent treatment (silicone treatment or the like) is performed on at least one side. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 may have a printed layer on which colors, patterns, characters, and the like are printed. For example, a character can be printed in the area | region where the fabric 100 is arrange | positioned in the supplementary sheet 340. FIG. In this case, the characters on the auxiliary sheet 340 can be observed by peeling the fabric 100 from the auxiliary sheet 340 disposed on the object 500.

  FIG. 10D is a diagram showing a fabric seal (fabric sheet) 25 which is a modification of the embodiment shown in FIG. 1. In the following drawings, elements substantially the same as those shown in FIGS. 1 to 10C are denoted by the same reference numerals, and the description thereof is simplified or omitted.

  In FIG. 10D, the fabric seal (woven fabric sheet) 25 includes a fabric 100 and an adhesive material 200. Furthermore, the fabric sheet 25 includes a supplementary sheet 340. The adhesive material 200 is disposed on the first adhesive material 200A disposed between the fabric 100 and the auxiliary sheet 340, and on the one surface of the auxiliary sheet 340, which is the surface opposite to the first adhesive material 200A. 2 adhesive material 200B. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the 2nd adhesive material 200B can express adhesiveness by performing predetermined processing. For example, the second adhesive material 200 </ b> B exhibits adhesiveness by being subjected to at least one of heat treatment, light treatment, liquid treatment, pressure application treatment, and the like. Examples of the second adhesive material 200B include a water-soluble adhesive material, a solvent-based adhesive material, and hot melt. Examples include starch (emulsion, solvent), hot melt (UV curable, rubber, emulsion, urethane), acrylic emulsion resin adhesive, natural rubber adhesive, synthetic rubber adhesive, acrylic resin adhesive. Agents, urethane resin adhesives, silicone resin adhesives, and polyvinyl ether resin adhesives.

  In one embodiment, the 2nd adhesive material 200B is solid or semi-solid at normal temperature, and its adhesiveness is low. By placing on the object 500 and applying a predetermined treatment, the adhesiveness of the second adhesive material 200B is expressed, and the fabric 100 is attached to the object 500 via the second adhesive material 200B. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In FIG. 10D, the surface of the woven fabric 100 (the fabric surface) can be disposed facing away from the object 500. In this case, the first surface 102 of the fabric 100 is observed from the side opposite to the object 500. In addition, the second surface 344 of the auxiliary sheet 340 can be observed through the object 500 having substantial transparency and / or having an observation window. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Alternatively, in the woven fabric sheet 25 having a four-layer structure, the second pressure-sensitive adhesive material 200B can exhibit adhesiveness at room temperature. For example, as in the embodiment shown in FIG. 2G, when the fabric sheet 25 has a scroll shape, a separator can be omitted. In this case, in the scroll, the lamination of the fabric 100, the first adhesive material 200A, the auxiliary sheet 340, and the second adhesive material 200B is repeated along the radial direction. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  FIG. 10E is a diagram showing a fabric seal (fabric sheet, fabric glue label) 27, which is a modification of the embodiment shown in FIG. In the following drawings, elements that are substantially the same as those shown in FIGS. 1 to 10D are given the same reference numerals, and descriptions thereof are simplified or omitted.

  In FIG. 10E, a fabric seal (woven fabric sheet, fabric glue label) 27 includes a fabric 100 and an adhesive material 200. Further, the fabric sheet 27 includes a supplementary sheet 340. The adhesive material 200 includes a first adhesive material 200 </ b> A disposed between the fabric 100 and the auxiliary sheet 340. By applying a bonding material (adhesive, adhesive) 215 on one surface of the auxiliary sheet 340 and / or the surface of the object 500 and arranging the fabric seal 27 on the object 500, the fabric 100 is attached to the object 500. It is done. The fabric seal 27 shown in FIG. 10E can be used as a so-called glue label. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the fabric 100 may have at least one of a color, a pattern, a character, a design, and the like. In the fabric 100 attached to the object 500, at least one of its color, pattern, character, design, etc. can be observed.

  In one example, the fabric seal 27 can be observed from the side opposite the object 500. In this case, the first surface 102 of the fabric 100 faces the observation side space. In another example, the fabric seal 27 can be observed through an object 500 that has substantial transparency and / or has an observation window. That is, the back surface (second surface 344) of the auxiliary sheet 340 is observed from the object 500 side. In this case, the second surface 344 of the auxiliary sheet 340 faces the observation side space through the object 500. When the auxiliary sheet 340 has a printing layer, a picture, a pattern, a character, or the like on the auxiliary sheet 340 can be observed through the object 500. In yet another example, both sides of the fabric seal 27 are observed. In other words, the first surface 102 of the fabric 100 is observed from the side opposite to the object 500, and the second surface 344 of the auxiliary sheet 340 passes through the object 500 having substantial transparency and / or having an observation window. Can be observed. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the physical or chemical properties of the fabric seal (fabric sheet) 27 can be supplemented by a supplementary sheet 340. The presence of the auxiliary sheet 340 avoids (1) contact between the fabric 100 and the bonding material 215 and (2) penetration / entry of the bonding material 215 into the fabric 100. As a result, leakage of the bonding material 215 to the surface of the fabric 100, alteration of the fabric 100, loss of texture of the fabric 100, and the like are avoided. The fabric seal 27 having the auxiliary sheet 340 has a high degree of freedom as a glue label. Various materials can be used as the bonding material 215. Even when the liquid absorbency of the fabric 100 is relatively high, the restriction on the type of the bonding material 215 can be relatively low. Further, in an example in which the relatively soft fabric 100 is used, the fabric seal (fabric sheet) 27 may have a relatively high rigidity by being integrated with the auxiliary sheet 340 having a relatively high stiffness. it can. In another example in which an uneven surface is used as an object to be pasted, the auxiliary sheet 340 having a relatively high stretchability easily follows the surface shape of the fabric 100 and suppresses generation of wrinkles in the fabric seal (fabric sheet) 27. obtain. Alternatively, it is possible to improve the curved surface compatibility of the fabric seal (fabric sheet) 27 by the auxiliary sheet 340 having relatively high stretchability. In another example, the auxiliary sheet 340 may have a function of preventing moisture from entering from outside and releasing moisture from inside. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the predetermined function of the auxiliary sheet 340 can be expressed, controlled, strengthened, or promoted by the first adhesive material 200 </ b> A and / or the bonding material (adhesive, adhesive material) 215. For example, a predetermined function can be expressed, controlled, strengthened, or promoted by a combination of the auxiliary sheet 340 and the first adhesive material 200A. Alternatively, a predetermined function can be expressed, controlled, strengthened, or promoted by a combination of the auxiliary sheet 340 and the bonding material (adhesive, adhesive material) 215. Alternatively, a predetermined function can be expressed, controlled, strengthened, or promoted by a combination of the auxiliary sheet 340, the first adhesive material 200A, and the bonding material (adhesive, adhesive material) 215. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the first adhesive 200A may be a single layer or a substantially multiple layer. In the first adhesive material 200 </ b> A, specifications (materials and characteristics) and the like can be different between the surface in contact with the fabric 100 and the surface in contact with the auxiliary sheet 340. For example, in the multi-layer adhesive material 200A, the specifications (material, hardness, thickness, color, transparency, pattern, etc.) can be different between the layer in contact with the fabric 100 and the layer in contact with the auxiliary sheet 340. The number of stacks can be 2, 3, 4, 5, 6, 7, 8, 9, 10, or more. In addition, the first adhesive material 200A can partially differ in material, characteristics, and the like in the plane. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one example, the auxiliary sheet 340 can have excellent processability compared to the fabric 100 with respect to a blade for cutting or punching the fabric 100. In one example, the auxiliary sheet 340 can have a higher density than the fabric 100. In one example, a blade is inserted into the fabric 100 during cutting or stamping. Due to the presence of the auxiliary sheet 340, the moving distance of the blade after contacting the fabric 100 can be increased. Alternatively, the auxiliary sheet 340 supports the fabric 100 from the back side, so that deformation (bending, etc.) and displacement (escape) of the fabric 100 during processing can be suppressed. The fact that the first pressure-sensitive adhesive material 200A has relatively strong adhesiveness (tackiness) and / or relatively high hardness (high viscosity) is advantageous in suppressing deformation and escape of the fabric 100 during processing. The long movement distance of the blade and the suppression of deformation and escape of the fabric 100 during processing are advantageous for improving the workability of the fabric 100. Such an improvement in workability can contribute to, for example, prevention of processing omission in which part of the yarn in the woven fabric 100 is not cut. This is particularly advantageous for processing fabric 100 having relatively thin threads. Due to the presence of the first adhesive material 200A, fraying of the yarn in the processed portion after cutting or punching is suppressed. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 and / or the first adhesive material 200A can function as a barrier layer for the bonding material 215 (a penetration preventing layer for the bonding material 215). The auxiliary sheet 340 and / or the first adhesive material 200 </ b> A can widen the selectivity in the type and viscosity of the bonding material 215. Furthermore, the auxiliary sheet 340 and / or the first pressure-sensitive adhesive 200 </ b> A can exhibit a function of complementing the flexibility of the fabric 100. By using the appropriate auxiliary sheet 340 and / or the first adhesive material 200A, the auxiliary sheet 340 and / or the first adhesive material 200A can strengthen the fabric 100. The auxiliary sheet 340 and / or the first pressure-sensitive adhesive material 200 </ b> A is a solution to the problem related to liquid permeability on the tissue structure, which is one of the characteristics of the fabric 100, and the problem related to flexibility, which is another characteristic of the fabric 100. To contribute. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Alternatively or additionally, the auxiliary sheet 340 can function as a barrier layer (preventing penetration of an external substance) against a predetermined substance toward the bonding material 215. In this case, for example, the predetermined substance may reduce the function of the bonding material 215. The auxiliary sheet 340 can have a function of suppressing, preventing, and / or blocking a predetermined substance from the outside from passing through the fabric 100 and reaching the bonding material 215. In one example, by suppressing the arrival of moisture to the bonding material 215 via the woven fabric 100, the function of the bonding material 215 (decrease in bonding force, separation and / or peeling) is suppressed, and the performance of the bonding material 215 is achieved. Can be stably maintained. By selectively using the auxiliary sheet 340 that is excellent in moisture blocking properties, it is possible to suppress the functional degradation of the bonding material 215 due to moisture. Alternatively or additionally, the auxiliary sheet 340 can be treated to enhance moisture barrier properties. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one example, the auxiliary sheet 340 and the first adhesive material 200 </ b> A can be disposed on substantially the entire surface of the fabric 100. In another example, the auxiliary sheet 340 and the first pressure-sensitive adhesive material 200 </ b> A can be partially disposed on one surface of the fabric 100. For example, in the partial arrangement, the auxiliary sheet 340 and the first adhesive material 200A can be arranged in a portion where the bonding material 215 is to be applied. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the auxiliary sheet 340 can have delamination properties. In this case, as in the case shown in FIG. 9D, it is possible to peel the fabric 100 from the object 500 relatively easily by delaminating the auxiliary sheet 340. This is advantageous for collecting the fabric 100 (seals and labels, etc.). In addition, the complementary sheet 340 can have at least one of a color, a pattern (pattern), a character, a design (design), and the like that can be observed when delamination is performed. In one example, the auxiliary sheet 340 can have a printed layer that includes colors, patterns, characters, etc. that are observable on the surface of the layer left on the object 500 when delaminated. Additionally or alternatively, the auxiliary sheet 340 can have a printed layer that includes colors, patterns, characters, etc. that are observable on the surface of the layer being peeled from the object 500 when delaminated. The print layer can include, for example, at least one of information on the object 500, an identification code of the object 500, information on the fabric 100, an identification code of the fabric 100, and other information. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  In one embodiment, the bonding material 215 can include a material (such as a water-soluble adhesive) that can be easily peeled off mainly with water. In this case, the laminated body of the fabric 100 and the auxiliary sheet 340 can be peeled off from the object 500 relatively easily as in the case shown in FIG. 9E. This is advantageous for collection of the fabric 100 (seals and labels, etc.), disposal of the fabric seal 30 and the like. In addition, the complementary sheet 340 may have at least one of a color, a pattern (pattern), a character, and a design (design) that can be observed when peeled. In one example, the auxiliary sheet 340 can have a printed layer that includes colors, patterns, characters, and the like that are observable on the exposed surface when peeled. The print layer can include, for example, at least one of information on the object 500, an identification code of the object 500, information on the fabric 100, an identification code of the fabric 100, and other information. The same can be done when a cloth other than the woven fabric or Japanese paper is used instead of the woven fabric 100.

  Here, as described above, a composite material (composite silk thread) in which a natural fiber silk thread and another material are combined can be used as a material used for the woven fabric. The composite material is formed, for example, by mixing and reeling a kite string and other fibers. Alternatively, the composite material is formed by mixing and spinning different types of short fibers. Alternatively, the composite material is generated by twisting different types of yarn (intertwisted yarn). Alternatively, the composite material is formed by weaving different types of yarns in combination. Alternatively, the composite material is formed by weaving a twisted yarn.

  Further, as described above, the silk thread or the woven fabric can be modified by applying a predetermined treatment. For example, by providing auxiliary materials (modifiers, processing agents, reinforcing materials) to silk and / or fabrics, and performing heat treatment and / or light treatment as necessary, the fabrics are improved in strength, liquid repellency and antifouling. Functions such as sexuality, elasticity, and unique texture can be added.

  Examples of the auxiliary material (modifier, processing agent, reinforcing material) to be given to the fabric 100 include, for example, UV curable resin, silicon resin, cellulose resin, Alkit resin, acrylic resin, polyurethane resin, polyester resin, gum arabic, glue ( Nika), varnish, and pine resin (Matsuyani). The said processing agent is an example and this invention is not limited to this.

  In the woven fabric 100 having the auxiliary material, the auxiliary material is arranged in at least a part of the gap portion of the tissue, the auxiliary material is arranged inside the yarn, covers at least a part of the tissue, and / or at least a part of the tissue. Enclose. For example, the auxiliary material can contribute to the reinforcement of the fabric 100 as a binder (binder) of the tissue structure in the fabric 100.

  FIG. 11 is a diagram illustrating an arrangement example of the auxiliary material (or a reinforcing portion 172 described later). As shown in FIG. 11, the auxiliary material 220 can be disposed on substantially the entire surface of the fabric 100. Alternatively, the auxiliary material 220 can be partially disposed on the fabric 100. In an example of the partial arrangement, the auxiliary material 220 is arranged along the edge of the fabric 100 (full circumference, partial circumference). Alternatively and / or additionally, the auxiliary material 220 is arranged in a straight line, a curved line, and / or a dotted line on the edge and other parts of the fabric 100. Alternatively and / or additionally, the auxiliary material 220 is disposed at the corner of the fabric 100. Alternatively and / or additionally, the auxiliary material 220 is disposed near the edge of the fabric 100 and the slit 302. Alternatively and / or additionally, the auxiliary material 220 is disposed near the edge (outer edge) of the fabric 100 and near the window 304 (near the inner edge). When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100. The placement region of the auxiliary material 220 may have a shape having an axis substantially along the warp or weft of the fabric 100. Alternatively, the placement region of the supplement 220 can have a shape having an axis that intersects the warp or weft.

  The auxiliary material 220 can be disposed substantially uniformly throughout the fabric 100. Alternatively, the auxiliary material 220 can be disposed on the fabric 100 substantially non-uniformly. By arranging the auxiliary material at least at the cut portion (edge or slit portion) of the fabric 100, fraying or tissue collapse of the cut portion of the fabric 100 can be suppressed. The fabric 100 having a partial and / or non-uniform auxiliary material arrangement differs in at least one of the structure, composition, strength, filling rate, density, hardness, and the like in one part from the other part. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  The placement of the auxiliary material 220 is, for example, at the time of creating the fabric 100, after creating the fabric 100, before placing the adhesive material 200, after placing the adhesive material 200, after placing the adhesive material 200, before placing the separator 300, and before separating the separator 300. It is possible to carry out the process after the placement of the separator 300, the placement of the separator 300, the cutting process of the fabric 100, the cutting process of the fabric 100, the cutting process of the fabric 100, and / or the auxiliary process such as the slit process. The auxiliary material 220 can be provided as a liquid material, a gel material, a solid material, a capsule material, and / or a sheet material. For example, the material can be soaked into silk thread. Further, the material can be disposed on the fabric 100, the adhesive material 200, and / or the separator 300. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  The process for expressing the function of the auxiliary material 220 can be performed separately from other processes. Or at least one part of the process for expressing the function of the auxiliary material 220 can be performed simultaneously with another process. For example, the function of the auxiliary material 220 can be expressed using processing energy at the time of cutting. Alternatively, the function of the auxiliary material 220 can be expressed using heat treatment and / or light treatment in another treatment. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  Silk yarn has a relatively high heat resistance. For example, the function of the auxiliary material 220 can be expressed by heat treatment. In this case, the heat treatment temperature can be, for example, 100, 110, 120, 130, 140, 150, 160, 170, 180, 190, 200, 210, 220, 230 ° C. or higher.

  Alternatively and / or additionally, at least part of the material (yarn) of the fabric 100 can function as the auxiliary material 220. For example, due to the pressing force, thermal energy, light energy, chemical reaction caused by the treatment liquid, and / or chemical reaction caused by the treatment gas, the properties of the material and / or tissue structure of the fabric 100 (structure, strength, density, hardness, etc.) At least partially change. Since at least a part of the material (yarn) of the fabric 100 functions as the auxiliary material 220, the strength, liquid repellency / antifouling properties, elasticity, and unique texture of the fabric 100 are at least partially on one surface of the fabric 100. Such functions can be expressed. For example, fraying or tissue collapse in the fabric 100 can be suppressed by curing the material and / or the tissue structure of the fabric 100. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  The material that functions as the auxiliary material 220 can be a natural fiber silk thread and / or another fiber thread. For example, synthetic fibers such as nylon, polyester, and acrylic can be cured using energy during cutting (for example, laser processing, cutting using a heated blade, partial heat application, and the like). When the woven fabric 100 contains a composite material, fibers other than silk can be cured by heat and / or light treatment to strengthen the tissue structure. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided.

  FIG. 12 is a diagram illustrating an example of a process for applying a UV curable resin to the fabric 100. In the process shown in FIG. 12, the punching of the fabric 100 and the placement of the UV curable resin 700 can be performed substantially simultaneously. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  In FIG. 12, first, the UV curable resin 700 (auxiliary material 220) is arranged on the blade mold 800 in the processing apparatus. That is, the resin 700 is held on the surface of the blade mold 800. Next, the blade mold 800 is driven into the fabric 100 that is a base material. In this punching process, the blade mold 800 contacts the fabric 100, and at least a part of the resin 700 moves from the blade mold 800 to the fabric 100. In the woven fabric 100, the resin 700 penetrates into the tissue. Next, the resin 700 can be cured by irradiating the fabric 100 with UV light. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  By the curing process, the fabric seal 50 in which the strength of the fabric 100 is improved is provided. In the fabric seal 50, the structure of at least the cut portion of the fabric 100 is substantially fixed by the hardening of the resin 700. Moreover, fraying of the cut part in the fabric 100 can be prevented by strengthening the tissue structure of the fabric 100. In the example of FIG. 12, the punching of the fabric 100 and the placement of the UV curable resin 700 are performed substantially simultaneously, which is advantageous in improving the processing capability. Alternatively or additionally, other processing agents can be applied to the fabric 100, similar to UV curable resins. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  FIG. 13 is a diagram illustrating another example of a process for applying a UV curable resin to the fabric 100.

  In FIG. 13, first, a UV curable resin 700 (auxiliary material 220) is disposed on the fabric 100. In this example, the UV curable resin 700 is annularly arranged on one surface of the fabric 100. In FIG. 13, the arrangement shape of the resin 700 is an annular shape. Alternatively, the arrangement shape of the resin 700 can be another annular shape or a non-annular shape. At least a part of the resin 700 on the fabric 100 can penetrate into the fabric 100. Next, the blade mold 800 is driven into the fabric 100 that is a base material. In this punching process, the resin 700 comes into contact with the fabric 100, and the resin 700 can further penetrate into the fabric 100. In this example, the edge of the annular resin 700 may have a substantially similar shape to the edge of the blade mold 800. The inner edge of the resin 700 has a smaller shape than the edge of the blade mold 800. The outer edge of the resin 700 has a larger shape than the edge of the blade mold 800. At the time of punching, the edge of the blade mold 800 can be positioned between the inner edge and the outer edge of the resin 700. Such a positional relationship is effective in infiltrating the resin 700 into the fabric 100 using the movement of the blade mold 800. Finally, the resin 700 can be cured by irradiating the fabric 100 with UV light. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided.

  By the curing process, a fabric seal 60 is provided in which the strength of the fabric 100 is improved particularly in the vicinity of the edge. Moreover, fraying of the cut part in the fabric 100 can be prevented by strengthening the tissue structure of the fabric 100. Alternatively or additionally, other processing agents can be applied to the fabric 100, similar to UV curable resins. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided.

  FIG. 14 is a diagram illustrating another example of a process for partially processing the silk fabric 100 when the fabric 100 is a silk fabric.

  In FIG. 14, first, silk fabric 100 is impregnated with sericin as necessary. The silk thread mainly contains fibroin and sericin. In the silk thread, sericin having adhesive strength (adhesive strength) covers fibroin. By supplying sericin, the sericin concentration in the silk fabric 100 is increased. Next, the member 810 having a predetermined protrusion (convex shape) is pressed against the silk fabric 100. At this time, the member 810 can be heated. The heating temperature is determined based on the melting temperature or softening temperature of sericin. In the portion 114 heated and pressed by the protrusion of the member 810, at least a part of sericin in the silk fabric 100 is melted and then solidified, whereby the silk threads are joined. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided.

  This treatment provides a silk fabric seal 62 in which the silk fabric 100 is partially reinforced. By strengthening the portion along the cutting line (cutting line), the strength of the silk fabric 100 is improved particularly in the vicinity of the edge. By strengthening the tissue structure of the silk fabric 100, fraying (for example, fraying of a cut part) in the silk fabric 100 can be prevented. By adjusting the pressing position, portions other than the cut portion in the silk fabric 100 can be strengthened. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided.

  FIG. 15 is a diagram illustrating another example of a process for partial processing of the fabric 100.

  In FIG. 15, first, a thermoplastic resin is infiltrated into the fabric 100. Next, a member 810 having a predetermined protrusion (convex shape) is pressed against the fabric 100. At this time, the member 810 can be heated. The heating temperature is determined based on the melting temperature or softening temperature of the thermoplastic resin. In the portion 115 heated and pressed by the protrusion of the member 810, at least a part of the thermoplastic resin in the fabric 100 is melted and then solidified, whereby the yarns are joined. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  This process provides a fabric seal 64 in which the fabric 100 is partially reinforced. By strengthening the portion along the cutting line (cutting line), the strength of the fabric 100 can be improved particularly in the vicinity of the edge. By strengthening the tissue structure of the fabric 100, fraying (for example, fraying of the cut portion) in the fabric 100 can be prevented. By adjusting the pressing position, the portion other than the cut portion in the fabric 100 can be strengthened. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  FIG. 16A is a diagram illustrating another example of a process for partial processing of the fabric 100.

  In FIG. 16A, the adhesive material 200 contains a thermoplastic resin. A member 810 having a predetermined planar protrusion (convex shape) is pressed against the fabric 100. At this time, the member 810 can be heated. The heating temperature is determined based on the melting temperature or softening temperature of the thermoplastic resin. In the portion heated and pressed by the protrusion of the member 810, a part of the thermoplastic resin in the adhesive material 200 is melted and penetrates into the portion 116 of the fabric 100. By applying pressure, the particles of the adhesive material enter between the yarns of the woven fabric, and the distance between the yarns becomes shorter (dense). In the portion 116 of the fabric 100, at least a part of the thermoplastic resin is solidified and then solidified. That is, the adhesive material particles entering between the yarns of the dense fabric are once melted and then solidified at that position because there is no heat source. As a result, the yarns are joined and fraying is prevented. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  This process provides a fabric seal 66 in which the fabric 100 is partially reinforced. By strengthening the portion along the cutting line (cutting line), the strength of the fabric 100 can be improved particularly in the vicinity of the edge. The part 116 is a high penetration part into which the adhesive material (thermoplastic resin) has penetrated more than the other part, and is a high density part where the density of the base material is higher than the other part. By strengthening the tissue structure of the fabric 100, fraying (for example, fraying of the cut portion) in the fabric 100 can be prevented. By adjusting the pressing position, the portion other than the cut portion in the fabric 100 can be strengthened. In the example of FIG. 16A, since the thermoplastic resin does not permeate other than the portion 116, as a whole, a decrease in the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 due to the permeation of the resin is suppressed. Is done. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided.

  FIG. 16B is a modification of the process of FIG. 16A and is a diagram illustrating an example in which a fabric seal (fabric sheet) includes a supplementary sheet (340).

  In FIG. 16B, the first adhesive material 200A includes a thermoplastic resin, and the second adhesive material 200B mainly includes a water-soluble adhesive material. In the process of heating and pressing the fabric 100 by the protrusions of the member 810, a part of the thermoplastic resin in the first adhesive material 200A melts and penetrates into the portion 116 of the fabric 100, while the second adhesive material 200B includes The water-soluble adhesive material does not substantially react. Similar to the process of FIG. 16A, the process of FIG. 16B proceeds to provide a fabric seal 68 in which the fabric 100 is partially reinforced. The part 116 is a high penetration part into which the adhesive material (thermoplastic resin) has penetrated more than the other part, and is a high density part where the density of the base material is higher than the other part. By strengthening the portion along the cutting line (cutting line), the strength of the fabric 100 can be improved particularly in the vicinity of the edge. By strengthening the tissue structure of the fabric 100, fraying (for example, fraying of the cut portion) in the fabric 100 can be prevented. By adjusting the pressing position, the portion other than the cut portion in the fabric 100 can be strengthened. In the example of FIG. 16B, since the thermoplastic resin does not permeate other than the portion 116, as a whole, a decrease in the inherent properties (appearance characteristics, feel, flexibility, texture, etc.) of the fabric 100 due to the permeation of the resin is suppressed. Is done. The same can be done when the fabric seal (woven fabric sheet) does not include the separator (300) or when the fabric seal (woven fabric sheet) does not include the separator (300) and the second adhesive (200B).

  FIG. 16C shows a variation of the process of FIG. 16B.

  In FIG. 16C, a sheet 815 is sandwiched between the member 810 and the fabric 100 during the heating / pressing process. Examples of the sheet 815 include a heat-resistant thin film sheet such as a film and glassine paper. One surface of the sheet 815 is treated to prevent adhesion with the molten resin. For example, a release material is disposed on at least one surface of the sheet 815. When the sheet 815 is sandwiched between the member 810 and the fabric 100 during the heating / pressing process, the adhesion between the member 810 and the fabric 100 is prevented. The same can be done when the fabric seal (woven fabric sheet) does not include the separator (300) or when the fabric seal (woven fabric sheet) does not include the separator (300) and the second adhesive (200B). The arrangement of sheet 815 is equally applicable to the processes of FIGS. 14, 15 and 16A.

  FIG. 17A, FIG. 17B, FIG. 17C, FIG. 17D, FIG. 17E, and FIG. 17F are diagrams showing examples of forms in which the cut portion of the fabric 100 is reinforced by the method shown in FIG. FIG. 17A and FIG. 17D are an example of a form without a supplementary sheet, FIG. 17B and FIG. 17E are an example of a form with a supplementary sheet 340, and FIGS. 17C and 17F are fabric seals (woven fabric sheets). Is a case where the auxiliary sheet (340) is provided and the separator (300) and the second adhesive material (200B) are not provided. In FIG. 17A, FIG. 17B, and FIG. 17C, the fabric seal (fabric sheet) has a step at the cut end (edge, edge portion) of the fabric 100. That is, the thickness of the woven fabric 100 of the reinforced portion (reinforced portion) 172 is smaller than the other portions. This shows a trace of the pressing process (compression process). The reinforced portion 172 has a high yarn density due to the press bonding process. The reinforced portion 172 has a high-density portion where the density of the base material is higher than that of other portions. When observed in a planar manner, the reflectance and / or color of the reinforcing portion 172 may differ from other portions. By adjusting the reinforcing material, the observed state of the reinforcing portion 172 can be adjusted. The same can be done when the fabric seal (woven fabric sheet) does not include the separator (300). Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  In FIG. 17D, FIG. 17E, and FIG. 17F, the fabric seal (fabric sheet) has a step at another portion 174 in addition to the cut end portion (edge, edge portion, reinforcing portion) 172 of the fabric 100. In a portion other than the edge of the fabric 100, the thickness of the fabric 100 of the reinforced portion (reinforced portion) 174 is smaller than that of the other portions. The reinforced portion 174 has a high yarn density due to the press bonding process. A pattern (pattern), a character, a design (design), and the like can be drawn on one surface of the fabric 100 using the difference in appearance. By adding a color material and / or a reflective material to the reinforcing material, the colors of the reinforcing portions 172 and 174 can be changed. The same can be done when the fabric seal (woven fabric sheet) does not include the separator (300). Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  At the cut end portion of the fabric 100, the width of the reinforcing portion 172 is 0.1, 0.2, 0.4, 0.6, 0.8, 1.0, 1.5, 2.0, 2.5. , 3.0, 3.5, 4.0, 4.5, 5.0 mm, or more.

  As shown in FIG. 11, the reinforcing portion 172 can be formed on substantially the entire surface of the fabric 100. Alternatively, the reinforcing portion 172 can be partially formed on the fabric 100. In an example of partial formation, the reinforcement part 172 is formed along the edge of the fabric 100 (full circumference, partial circumference). Alternatively and / or additionally, the reinforcement 172 may be formed in a straight line, a curved line, and / or a dot on the edge and other parts of the fabric 100. Alternatively and / or additionally, the reinforcement 172 is formed at the corner of the fabric 100. Alternatively and / or additionally, the reinforcement 172 is formed near the edge of the fabric 100 and the slit 302. Alternatively and / or additionally, the reinforcement 172 is formed near the edge (outer edge) of the fabric 100 and near the window 304 (near the inner edge). The same can be done when the fabric seal (woven fabric sheet) does not include the separator (300). Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100. The region where the reinforcement 172 is formed may have a shape having an axis substantially along the warp or weft of the fabric 100. Alternatively, the region where the reinforcement 172 is formed can have a shape having an axis that intersects the warp or weft.

  The reinforcing part 172 can be formed substantially uniformly over the entire fabric 100. Alternatively, the reinforcing portion 172 can be formed on the fabric 100 substantially non-uniformly. By forming the reinforced portion 172 at least at the cut portion (edge or slit portion) of the fabric 100, fraying or disruption of the cut portion of the fabric 100 can be suppressed. The fabric 100 having the formation of the partial reinforcing portion 172 and / or the formation of the non-uniform reinforcing portion 172 and the reinforcing portion 172 has at least one of the structure, composition, strength, filling rate, density, hardness, etc. in a certain part. Different from that of the department. The same can be done when the fabric seal (woven fabric sheet) does not include the separator (300). Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  FIG. 17G is a diagram illustrating another example of a form in which the cut portion of the fabric 100 is reinforced. In FIG. 17G, the fabric seal 70 includes a resin 720 (auxiliary material 220) partially disposed at a cut end (edge, edge portion) of the fabric 100. The partial arrangement of the resin 720 can be performed after the cutting of the fabric 100 or before the cutting, for example. The resin 720 can be disposed along the edge of the cut fabric 100. The resin 720 can be disposed over the entire circumference of the edge of the cut fabric 100. Alternatively, the resin 720 can be disposed on a part of the periphery of the edge of the cut fabric 10. The resin 720 can be provided in a raised state on the surface of the fabric 100 (for example, the surface of the edge), and can be provided so as to be substantially flush with the surface of the fabric 100. It can be provided so as not to protrude, or can be provided mainly on the side surface of the fabric 100. In FIG. 17G, the fabric seal 70 has at least a three-layer structure. Alternatively, the reinforcing resin can be partially disposed on a fabric seal having a four-layer structure or more. Alternatively, materials other than resins can be used to reinforce the cuts of the fabric 100. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  FIG. 17H is a diagram illustrating another example of a form in which the cut portion of the fabric 100 is reinforced. In FIG. 17H, the fabric seal 80 includes a protective sheet 740 (auxiliary material 220) that covers the surface of the fabric 100. The protective sheet 740 can be partially disposed at the cut end (edge, edge portion) of the fabric 100. Alternatively, the protective sheet 740 can be disposed so as to cover (laminate) the entire surface of the fabric 100. As the protective sheet 740, a colorless and substantially transparent sheet, a colored and substantially transparent sheet, a substantially translucent sheet, or a sheet that is not substantially transparent can be used. Various materials can be used as the protective sheet 740. In the example of FIG. 17H, the fabric seal 80 has at least a three-layer structure. Alternatively, a protective sheet can be placed against a fabric seal having a four or more layer structure. When the fabric seal (fabric sheet) is provided with the auxiliary sheet (340), when the fabric seal (woven fabric sheet) is not provided with the separator (300), or when the fabric seal (woven fabric sheet) is provided with the auxiliary sheet (340) and the separator (300) and the second adhesive material (200B) can be similarly provided. Moreover, it can do similarly when using cloth and Japanese paper other than a textile instead of the textile 100.

  FIG. 18 is a diagram illustrating an example of a surface of a fabric seal (woven fabric sheet). As described above, the fabric 100 may have a design including at least one of a color, a pattern (pattern), a character, and a design (design). The design of the woven fabric 10 (first design 150) can be expressed based on a woven fabric texture (a dyed woven fabric texture, a weave pattern, a woven pattern, etc.) (hereinafter referred to as a first design process as appropriate). For example, a pattern or a character can be expressed based on only a woven fabric structure or a combination of a woven fabric fabric and a colored yarn arrangement of warp and weft. Additionally and / or alternatively, the fabric 100 design (second design 160) may be post-dyed or printed (such as printing), resin potting, foiling, embroidery, hand drawing, airbrushing, lacquering, prints, or other decorations. Etc. (hereinafter referred to as second design process as appropriate). A hot stamping method or a cold transfer method (a method using a flexographic printing machine, a method using an offset printing machine, etc.) can be applied to the foiling. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable.

  At least one of the contents (first contents) of the first design 150 by the first design process and the contents (second contents) of the second design 160 by the second design process is an object to which a fabric seal (woven sheet) is attached. Or to the application of a fabric seal (textile sheet). For example, at least one of the contents of the first design 150 and the contents of the second design 160 may include a name / brand of the object, a symbol image of the object, or a description / advertisement advertisement of the object. In the case where the mounting surface of the object has a curved surface, a bent surface, and / or a step, the mounting portion has light transmittance, the application has a three-dimensional shape, and / or the application state has a drape, etc. 100 optical characteristics can be exhibited more effectively. By affixing the fabric 100 to the object via the adhesive material, the fabric 100 can be at least partially adhered to the object following the attachment surface having a curved surface, a bent surface, and / or a step. The close contact portion of the fabric 100 may have a three-dimensional shape along the surface of the object. The state of light from the fabric 100 is different for each part, and a characteristic appearance is exhibited. Alternatively, in the fabric 100 provided with the non-arrangement region of the adhesive (adhesive material), the non-contact portion of the fabric 100 exhibits a texture. According to the shape of the attachment surface of the object, at least one of the first design 150 and the second design 160 of the fabric 100 can be determined. At least one of the first design 150 and the second design 160 of the fabric 100 can be determined in accordance with the arrangement pattern of the adhesive (adhesive). Alternatively, in the fabric 100 attached to a light-transmitting object via a light-transmitting adhesive material, a unique appearance can be exhibited based on the light transmittance and color developability of the fabric 100.

  In addition, the combination of the first design process and the second design process can effectively exhibit the appearance characteristics and functional characteristics of the fabric seal (fabric sheet). Even in this case, the attachment surface has a curved surface, a bent surface, and / or a step, the attachment portion has light transmittance, the application object has a three-dimensional shape, and / or the application state has a drape, etc. 100 optical characteristics can be exhibited more effectively. In one example, the content of the first design 150 and the content of the second design 160 can be related to each other. For example, one of the contents of the first design 150 and the contents of the second design 160 may include information on a company name and a company logo, and the other may include information on an object (product). Alternatively, one of the first content and the second content can include main information related to the object, and the other can include auxiliary information related to the object. The appearance characteristics of the first design and the second design change according to the observation angle and the incident state of light on the fabric 100, and the state of the change can be different between the first design and the second design. In one example, characters and designs are printed on the silk fabric 100 of crepe. The surface of the crimped dough has fine wrinkles (unevenness). The light reflection differs between the printed area and the non-printed area, which contributes to excellent appearance. Shibo also contributes to the richness and texture of the silk fabric 100.

  Textile printing / printing on the fabric 100 can include a direct printing method and a transfer method. Printing / printing on the fabric 100 includes letterpress printing (letterpress printing, flexographic printing, seal printing, etc.), intaglio printing (gravure printing, etc.), lithographic printing (offset printing (sheet-fed printing, rotary printing, dry type), etc.), stencil printing Examples thereof include printing (screen printing, etc.), laser method (laser printer, etc.), and ink jet method (continuous method, on-demand method (piezo method, thermal ink method, etc.)). Examples of the ink for textile printing / printing include an oxidation polymerization type, an evaporation type, a penetration type, and a photopolymerization type. Ink for an inkjet printer can include at least one of pigment ink, dye ink, sublimation ink, universal ink, solvent ink, sublimation fluorescent ink, and UV curable ink. The pigment ink is generally an ink in which a pigment is dissolved in a solvent, and printing is performed by attaching a pigment coloring matter to a printing surface. A dye ink is generally an ink in which a dye is dissolved in a solvent, and can produce more colors than a pigment ink. Printing is performed by the dye ink penetrating the printing surface. In sublimation, the ink changes from a gas to a solid, and the ink components are fixed to the object.

  In textile printing / printing on the fabric 100, a combination of a printing method and an ink is appropriately selected. In one example, a combination of pigment printing direct printing and pigment printing ink (resin ink) may be selected. The resin ink is advantageous in favorably maintaining the appearance characteristics of the fabric 100 and / or balancing the color characteristics and appearance characteristics of the printed portion and the non-printed portion. In an appropriate combination, a unique appearance in which the first design 150 and the second design 160 are harmonized can be exhibited. For example, the woven pattern of the first design 150 is also expressed in the second design 160, and the light effect in which the first design 150 and the second design 160 are combined can be exhibited. In other examples, a combination of acid direct printing and acid dye ink may be selected. In yet another example, a combination of sublimation transfer / direct printing scheme and sublimation dye ink may be selected. In yet another example, a combination of reactive direct printing and reactive dye ink may be selected. Alternatively, combinations other than the above examples may be selected as appropriate.

  FIG. 19 is a diagram illustrating another example of the surface of the fabric seal (woven fabric sheet). In FIG. 19, a design including at least one of a color, a pattern (pattern), a character, and a design (design) in the fabric 100 includes at least a part of the reinforcing portion 172. As described above, the reinforcing portion 172 may have a high yarn density by a predetermined process and may have different light reflection from other portions. A pattern (pattern), a character, a design (design), and the like can be drawn on one surface of the fabric 100 using the difference in appearance. By adding a color material and / or a reflective material to the reinforcing material, the color of the reinforcing portion 172 can be changed. For example, the reinforcing part 172 can be expressed as a pattern indicating the frame of the fabric 100. For example, the reinforcing unit 172 can be expressed as a pattern indicating a pattern. For example, the strengthening unit 172 can be expressed as a character. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Further, the present invention can also be applied to the case where the fabric seal (woven fabric sheet) does not include the separator (300), or the fabric seal (woven fabric sheet) includes the auxiliary sheet and does not include the separator (300) and the second adhesive material. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

  FIG. 20 is a diagram illustrating another example of the surface of the fabric seal (woven fabric sheet). In FIG. 20, the formation region of the reinforced portion 172 is based on post-weaving processing including at least one of post-dyeing, textile printing, printing, resin potting, foiling, embroidery, hand drawing, airbrush, lacquering, prints, and decoration. Includes the design to be expressed. The addition of a design to the reinforcing part 172 that looks different from other parts can contribute to matching with other designs and improving balance. For example, at least a part of the frame line can be drawn in the formation region of the reinforcing portion 172. For example, a color can be added to the formation region of the reinforcing portion 172. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Further, the present invention can also be applied to the case where the fabric seal (woven fabric sheet) does not include the separator (300), or the fabric seal (woven fabric sheet) includes the auxiliary sheet and does not include the separator (300) and the second adhesive material. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

  As described above, when the woven fabric 100 is a silk woven fabric, the silk thread or the silk woven fabric has gloss, color, dyeability, stretchability, hygroscopicity / moisture permeability, low chargeability, wrinkle resistance, and flame retardancy. It can have functions such as UV-cutting property, antibacterial property, oxidation resistance, substance absorbability (gas absorbability, etc.), metal adsorbability and the like. Further, various functions can be obtained by combining the natural fiber silk thread with other materials. The gloss of silk is generally based on the prism light effect due to the cross section of the silk thread having a substantially triangular shape as a whole, a complicated fine fiber structure (layered structure, fibril structure), and the like. Silk is a protein fiber and includes a crystalline part and an amorphous part. Silk also contains various active groups suitable for dyeing. Silk also has a relatively low refractive index. Reflected light from the inside of the silk fiber can pass through the surface and emit a fresh color. Silk fabric includes a large number of air chambers and has a relatively high air content. Silk fabrics can be relatively maintained in thickness (high compression elasticity). Silk fabric is relatively difficult to transmit heat. Silk fabric is relatively easy to deform. Silk has higher water absorption than cotton. Silk has the same moisture release properties as silk. Silk fabric is relatively difficult to wrinkle, and even if wrinkled, it is difficult to remain. The difficulty of remaining wrinkles is advantageous for sealing and decorative use, such as being suitable for repeated use. Silk does not burn to relatively high temperatures, and toxic gases are less likely to be generated when burned. Silk is difficult to melt. The ultraviolet absorption spectrum of silk fibroin shows a high absorption rate at a specific wavelength. The silk fabric has a function of absorbing at least a part of ultraviolet rays.

  Various application products that promote the use of silk fabrics can be made by using the above-described techniques or combining a plurality of techniques as required.

(Thousand company bills / exchange bills)
In one example, as shown in FIG. 21, a fabric seal 1001 is provided as a thousand company bill / exchange bill. The appearance characteristics of the woven fabric 100 contribute to a unique texture. Both the case where the fabric seal (woven fabric sheet) 1001 does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. The fabric 100 is a silk fabric, for example. The fabric 100 can be a fabric other than a silk fabric. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Label for alcoholic beverage containers)
In one example, as shown in FIG. 22, fabric seals (woven fabric sheets) 1002, 1003, and 1004 are attached to containers of alcoholic beverages (Japanese sake, plum wine, shochu, whiskey, brandy, wine, beer, cocktail, etc.). Appearance characteristics and UV-cutting properties of the fabric 100 can be imparted to the alcohol beverage container. Any of the cases where the fabric seals (woven fabric sheets) 1002, 1003, and 1004 are not provided with the auxiliary sheet and the case where the auxiliary sheet is provided are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Label for container)
In one example, a fabric seal (fabric sheet) is attached to a food / food container. For example, as shown in FIG. 23, fabric seals (woven fabric sheets) 1005, 1006, and 1007 are attached to sake barrels, miso (pickled rice cakes), and wooden boxes (for example, high-quality food wooden boxes). Examples of food containers to which a fabric seal (woven fabric sheet) is attached include containers for pickles, rice, rice cakes, Japanese sweets, processed fish products, tea, honey, fruits and the like. Examples of the seasoning container to which the fabric seal (woven fabric sheet) is attached include containers for soy sauce, sauce, vinegar, miso, salt, sugar, pepper, nanami and the like. Examples of the beverage container to which the fabric seal (woven fabric sheet) is attached include fruit juice, carbonated beverage, and vegetable juice. Such containers can be given the appearance characteristics of the fabric 100 and other functions. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Seal for human body decoration)
In one example, a decorative fabric seal (woven fabric sheet) is attached to the human body. In this example, for example, an adhesive material (attachment material) that is less irritating to human skin is employed. The appearance of the fabric can be used to decorate the human body. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Quasi-drug seal)
In one example, a fabric seal (woven fabric sheet) as a quasi-drug is attached to the human body. In this example, for example, a metal material containing at least one of titanium, magnesium, and aluminum is mixed into the adhesive material (attachment material). Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Fragrance seal)
In one example, a fabric seal (woven fabric sheet) containing a fragrance is attached to the human body. In this example, a fragrance | flavor is mixed in an adhesive material (attachment material), for example. The fragrance is released from the adhesive material when the adhesive material is exposed. Such a seal is manufactured, for example, by mixing a fragrance encapsulated material in an adhesive material and applying it to a fabric. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Insect repellent seal)
In one example, a fabric seal (woven fabric sheet) for repelling insects is attached to a human body. This example is an application of the above fragrance seal. As the fragrance, a material having an effect on insect repellent is used. An insect repellent effect can be obtained by applying a seal to the skin or clothing. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Textile tape)
In one example, a fabric seal (fabric sheet) manufactured in a tape form is provided. In this example, for example, a tape having a textile appearance is provided. In addition, because of the wrinkle resistance of the woven fabric, the appearance is hardly impaired even if it is re-applied. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Decoration letter paper)
In one example, a letter paper with a fabric attached is provided. That is, in this example, the woven fabric and the letter paper are combined. The appearance of the fabric can be imparted to the letter paper. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Photocatalyst seal)
In one example, a fabric seal (fabric sheet) having a photocatalytic function is provided. In this example, for example, a photocatalytic function is imparted to a woven fabric or an adhesive material. The photocatalyst can exert a deodorizing effect on the space in the vicinity of the seal. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Ship)
In one example, a fabric seal (fabric sheet) having a ship function is provided. In this example, for example, a material having a function of a warm ship or a cold ship is mixed in the attachment agent (adhesive material). A ship having the appearance of a fabric is provided. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Cooling agent)
In one example, a fabric seal (fabric sheet) having a cooling function is provided. In this example, for example, an adhesive material having a cooling function is applied. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Broken seal)
In one example, a fabric seal (woven fabric sheet) subjected to a predetermined processing (broken processing) is provided. In this example, for example, a worn-out appearance is given to the fabric. Unique appearance is demonstrated. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Seal for inkjet printer)
In one example, a seal that can be printed with commercial and home inkjet printers is provided. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Laser printer compatible sticker)
In one example, a seal printable with commercial and home laser printers is provided. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Hot melt for inkjet printer)
In one example, a fabric sheet is provided as a hot melt for an inkjet printer. In this example, for example, the sheet can be adhered to an object using an iron for commercial and household inkjet printers. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Hot melt for laser printer)
In one example, a fabric sheet is provided as a hot melt for a laser printer. In this example, for example, the sheet can be bonded to an object using an iron for commercial and household laser printers. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Dry decal)
In one example, a fabric seal (fabric sheet) is provided as a dry decal. In this example, for example, after the seal is disposed at a predetermined position of the object, the seal adheres to the object by rubbing the surface of the seal. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Food freshness preservation seal)
In one example, a fabric seal (fabric sheet) is provided as a food freshness-keeping seal. In this example, a fabric seal is affixed, for example, to the inside of a refrigerator. The decorativeness of the fabric is given in the refrigerator. In addition, when the woven fabric is a silk woven fabric, the reduction of food freshness is suppressed by the gas absorption of silk. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(wallpaper)
In one example, a fabric seal is used for interiors such as walls. In this example, for example, the appearance of a fabric is given to a wall or the like. Further, when the woven fabric is a silk woven fabric, the release of environmental hormones and the like is suppressed by the gas absorption of silk. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Cryptographic stickers, information stickers)
In one example, a fabric seal (woven fabric sheet) is provided as an encryption seal or an information seal. In this example, for example, a woven cord or a color cord includes predetermined information. In this example, for example, a dyed fabric structure is preferably used. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable.

(Antimicrobial sheet)
In one example, a fabric seal (fabric sheet) is provided as a fungicidal sheet. In this example, a woven sheet is used for masks, gauze, bandages, adhesive bandages, and the like. These articles are given the appearance of silk fabric. Moreover, when the fabric is a silk fabric, the antibacterial properties of silk are imparted. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable.

(Reflective seal, security seal)
In one example, a fabric seal (fabric sheet) is provided as a reflective seal or a security seal. In this example, a fabric seal is affixed to, for example, a bicycle or a sign. When the woven fabric is a silk fabric, the gloss and appearance of the silk fabric are imparted to the object. In addition, a silk fabric in which reflective yarns are used in combination can be used. Alternatively, the gloss layer can be coated on the surface of the silk fabric. Alternatively, in one piece of seal, an area where the silk fabric is arranged and an area where the reflective printing is performed are provided. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable.

(Hybrid fiber fabric seal)
In one example, a hybrid type fabric seal that combines fibers of different materials is provided. In this example, for example, in one piece of seal, a combination of a plurality of materials such as natural fibers and chemical fibers can be used. The fabric is, for example, a silk fiber and acetate fabric. As the woven fabric, a woven fabric having fibers other than silk fibers can be used. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable.

(Hybrid laminated seal)
In one example, a hybrid type laminated fabric seal combined with other materials is provided. In this example, for example, in one piece of seal, an area of another material and an area of a fabric are provided. Examples of other materials include paper, Japanese paper, resin, and metal. The fabric is, for example, a silk fabric. As the woven fabric, a woven fabric other than the silk woven fabric can be used. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable.

(Seal for greeting card design)
In one example, a fabric seal (fabric sheet) is provided as a greeting card design seal. In this example, a fabric seal is affixed to a postcard such as a New Year's card. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Point seal)
In one example, a fabric seal is used as a point seal provided by a store or the like. Both the case where the fabric seal (woven fabric sheet) does not include the auxiliary sheet and the case where the auxiliary fabric sheet includes the auxiliary sheet are applicable. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

(Adhesive bandage)
In one example, a fabric seal as a bandage is provided. In this example, the fabric seal can include an auxiliary sheet having a function of preventing moisture from entering from the outside and releasing moisture from the inside. The fabric is, for example, a silk fabric. As the woven fabric, a woven fabric other than the silk woven fabric can be used. Moreover, it is applicable also when using cloth and Japanese paper other than a textile instead of a textile.

  As mentioned above, although embodiment of this invention was described, this invention is not limited to said embodiment. The numerical value used in the above description is an example, and the present invention is not limited to this. Additions, omissions, substitutions, and other modifications can be made without departing from the spirit of the present invention.

  In one embodiment, a fabric seal (woven fabric sheet) is attached to the one surface of the fabric through the adhesive material, an adhesive material disposed on one surface of the fabric, and at least one of the adhesive materials. And a separator (mounting sheet, sheet) that can be peeled off from the one surface of the woven fabric while leaving a portion on the one surface of the woven fabric. In this embodiment, the adhesive material can have a function of reinforcing the fabric. In the present embodiment, the fabric seal may include an auxiliary material that is disposed between the adhesive material and the fabric and reinforces the fabric.

  In one embodiment, the fabric seal (woven fabric sheet) is a fabric and an adhesive material disposed on one surface of the fabric, and the fabric can be attached to another object by performing a predetermined treatment. The pressure-sensitive adhesive material exhibiting adhesiveness.

  In one embodiment, the fabric seal (woven fabric sheet) has a fabric, a first adhesive material disposed on one surface of the fabric, and a first surface attached to the one surface of the fabric via the adhesive material. A separator (sheet) capable of peeling off the first surface from the one surface of the fabric while leaving at least a part of the adhesive material on the one surface of the fabric, and a second disposed on the second surface of the separator 2 adhesive materials.

10, 20, 22, 24, 25, 26, 27, 30, 40, 50, 60, 70, 80: Fabric seal (woven fabric sheet, adhesive sheet, seal), 100: Fabric (base material), 150: No. 1 design, 160: 2nd design, 200: adhesive material, 200A: 1st adhesive material, 200B: 2nd adhesive material, 210: anchor material, 260, 270: mounting material, 300: separator, 340: supplementary sheet, 500 :Object.

Claims (82)

Weaving,
Adhesive material,
Fabric seal with Weaving,
Means for attaching the fabric to another object;
Fabric sheet with Preparing a fabric;
Providing the fabric with means for attaching the fabric to another object;
A method for producing a fabric seal or fabric sheet comprising: Weaving,
An adhesive material,
The total number of substantial layers is 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, or That is the fabric seal.   The fabric seal according to claim 4, wherein the fabric has at least one of a color, a pattern, a character, and a design.   The fabric seal according to claim 4 or 5, wherein at least one of the first surface of the fabric disposed on the space side and the second surface of the fabric disposed on the object side is observed.   The fabric seal according to any one of claims 4 to 6, wherein the fabric includes at least one of silk fabric, wool fabric, cotton fabric, hemp fabric, and chemical fiber fabric.   The fabric seal according to any one of claims 4 to 7, wherein the fabric includes at least one of a pre-dyed fabric and a post-dyed fabric. Stationery, auxiliary equipment, containers, portable equipment, portable equipment accessories, electrical products, electrical equipment accessories, recording media, mechanical equipment, clothing, clothing accessories, decorative goods, cosmetics, cosmetic accessories, kitchenware, medical products , Articles related to shrines and temples, daily necessities, vehicles, stage sets, stage equipment, stadium structures, stadium decorations, dojo structures, dojo decorations, baskets, table decorations, transportation network components, Buildings, public facilities, vending machines, cash handling equipment, signs, walls, floors, ceilings, windows, shelves, furniture, tables, chairs, bedding, books, newspapers, magazines, brochures, calendars, business cards, business cards, name tags, paper Attached to at least one of wrapping paper, ticket, menu table, card, plant, flower, human body, organism, construction site partition, guide plate, or souvenir goods seal, wrapping seal, decoration seal, shop It is used as an external seal, a bonding tape, a sticky note, a label, a puzzle, a pennant, a flame retardant sheet, a fireproof sheet, a quasi-drug, an article related to a shrine, a thousand company bill, a decoration material, and the like. The fabric seal according to any one of the above.   The fabric has strength, abrasion resistance, weather resistance, moisture permeability, waterproofness, water resistance, chemical resistance, washability, appearance, wrinkle resistance, thermal properties, heat retention, cold retention, flexibility, flame retardancy And a fabric seal according to any one of claims 4 to 9, having at least a portion that has been treated for at least one of its bondability.   11. The fabric according to any one of claims 4 to 10, wherein the fabric has a shape having an axis substantially along the warp or weft, or a shape having an axis substantially intersecting the warp or weft. A fabric seal as described in 1.   The fabric seal according to any one of claims 4 to 11, wherein the fabric seal has at least one of a sheet shape, a scroll shape, and a three-dimensional shape.   The fabric seal according to any one of claims 4 to 12, wherein the fabric has at least one of a letter, a design, and a pattern having an axis substantially along the warp or weft. The fabric is
A first design expressed based on the fabric structure;
A second design expressed based on post-weaving processing, including at least one of post-dyeing, textile printing, printing, resin potting, foiling, embroidery, hand drawing, airbrushing, lacquering, prints, and decorating;
14. A fabric seal according to any one of claims 4 to 13, comprising at least one of the following.   The observed state of the adhesive material on the front side of the fabric is controlled, or the observed state of the adhesive material is controlled through a gap in the tissue structure of the fabric. The fabric seal according to any one of the above.   The state of the adhesive material such as presence / absence, amount, surface area, thickness, distribution, etc. of the adhesive material in a dent of the tissue structure of the woven fabric is controlled according to any one of claims 4 to 15. Textile seal. The surface height of the adhesive material is controlled in the dent on the surface of the fabric, or
The fabric seal according to any one of claims 4 to 16, wherein a surface height of the pressure-sensitive adhesive material in a gap between the texture structures of the fabric is controlled. The pressure-sensitive adhesive material has at least one of color and optical properties controlled, or
The hue, chromaticity, and / or saturation of the adhesive material is set according to the texture structure, color, shadow, pattern, character, or pattern of the fabric.
The fabric seal according to any one of claims 4 to 17.   The adhesive material is substantially transparent, lighter than the entire fabric, darker than the entire fabric, a color similar to the color of the fabric, and a color having a predetermined relationship with the color of the fabric. The fabric according to any one of claims 4 to 18, wherein the fabric has at least one of a uniform color over the entire surface, at least a partial color change on one surface, light absorption and light reflectivity. sticker.   The ratio of the height of the pressure-sensitive adhesive material to the thickness of the lower layer or the lowermost layer of the fabric is about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 20, 30, 40, 20. A fabric seal according to any one of claims 4 to 19, which is 50, 60, 70, 80, 90, 100% or more.   The ratio of the height of the adhesive material to the thickness of the upper layer or the uppermost layer of the fabric is about 100, 90, 80, 70, 60, 50, 40, 30, 20, 10, 9, 8, 7, 21. A fabric seal according to any one of claims 4 to 20, which is 6, 5, 4, 3, 2, 1% or less.   A substantial proportion of the adhesive material penetrating into the fabric is about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 20, by weight ratio to the fabric. 30 to 40, 50, 60, 70, 80, 90, 100, 110, 120, 130, 140, 150, 160, 170, 180, 190, 200%, or more. The woven fabric seal according to any one of the above.   The substantial distance that the adhesive material has entered the gap between the fabric structure is about 90, 80, 70, 60, 50, 40, 30, 20, 10, 9, 8 with respect to the thickness of the fabric. 23. A fabric seal according to any one of claims 4 to 22, wherein the fabric seal is 7, 6, 5, 4, 3, 2, 1% or less.   24. The fabric seal according to any one of claims 4 to 23, wherein the presence or absence of a space surrounded by the warp and weft of the fabric and the adhesive material is controlled.   25. The fabric seal according to any one of claims 4 to 24, wherein the pressure-sensitive adhesive material has a single layer or has a plurality of layers at least partially different from each other.   The fabric seal according to any one of claims 4 to 25, wherein the pressure-sensitive adhesive material is disposed on the whole or a part of one surface of the fabric.   27. The fabric seal according to any one of claims 4 to 26, wherein the fabric has the same or different characteristics between an upper portion disposed on the front surface side and a lower portion disposed on the back surface side.   The fabric has an upper or lower part disposed on the front side, a lower part disposed on the back side, and an intermediate part between the upper part and the lower part, at least part of which has the same or different characteristics with respect to other parts. 28. A fabric seal according to any one of claims 4 to 27.   29. The fabric seal according to any one of claims 4 to 28, wherein the fabric has at least one of a plain weave, a twill weave, a satin weave, and other structures.   30. A fabric seal according to any one of claims 4 to 29, wherein the fabric comprises a partial reinforcing structure.   The fabric seal according to any one of claims 4 to 30, wherein the fabric has a pattern based on a combination of a fabric structure and a color yarn arrangement.   32. The fabric seal according to any one of claims 4 to 31, wherein the fabric includes a lap tissue.   The woven fabric includes bag weaving, air-woven weaving, weaving weaving, mesh weaving, Toriko weaving, picket, fold weaving, Bedford cord weaving, crepon, diagonal cord weaving, crest cord weaving, double knot weaving, pile weaving, tangle Organization, spelling, freshly nishiki, yokonishiki, lion, shujin, shaun, futsu, tangle weave, velvet, sushi weave, woven weave, cocoon, lion, gold and silver rind, handu, lion, call, meisen, 33. The fabric seal according to any one of claims 4 to 32, comprising at least one of Oshima, Tsunishiki, Hakata woven, and crepe.   The textile seal according to any one of claims 4 to 33, further comprising a separator that covers the adhesive material. A separator,
35. Any of claims 4 to 34, wherein the separator has a shape having an axis substantially along the warp or weft of the fabric, or a shape having an axis substantially intersecting the warp or weft. A fabric seal according to claim 1. A separator,
The separator has a slit for substantial division,
36. Any of claims 4 to 35, wherein the slit is formed substantially along the warp or weft of the fabric or substantially intersecting the warp or weft of the fabric. A fabric seal according to claim 1. A separator,
37. A fabric seal according to any one of claims 4 to 36, wherein the fabric has a single piece or multiple pieces for one separator. A separator,
38. A fabric seal according to any one of claims 4 to 37, wherein the fabric has a score line. A separator,
The fabric seal according to any one of claims 4 to 38, wherein one surface of the separator in contact with the adhesive material has a substantially uneven structure.   40. A fabric according to any one of claims 4 to 39, wherein at least a majority of the area on one side of the fabric is substantially non-infiltrated by the adhesive with respect to the interior of the yarn of the fabric. sticker.   41. The fabric seal according to any one of claims 4 to 40, wherein the fabric has a portion with a smaller thickness than other portions.   The woven fabric seal according to any one of claims 4 to 41, wherein the woven fabric has a higher density of the base material than other portions and has a high-density portion formed at least partially.   43. The fabric seal according to any one of claims 4 to 42, wherein the fabric has a high penetration portion into which the adhesive material has penetrated more than other portions.   44. The fabric seal according to any one of claims 4 to 43, wherein at least a region of at least one surface of the fabric is anchored.   45. The fabric seal according to any one of claims 4 to 44, further comprising an anchor material disposed on at least one surface of the fabric. An anchor material disposed on at least one surface of the fabric;
46. The fabric seal according to any one of claims 4 to 45, wherein the anchor material is disposed in whole or in part on one surface of the fabric. An anchor material disposed on at least one surface of the fabric;
The anchor material is at least one of a function of ensuring the bonding between the fabric and the adhesive material, a function as a barrier layer for the adhesive material, a function of reinforcing the texture of the fabric, and a function of preventing fraying of the fabric. 47. A fabric seal according to any one of claims 4 to 46, having: An anchor material disposed on at least one surface of the fabric;
48. The fabric seal according to any one of claims 4 to 47, wherein the anchor material has a sheet-like member including a sheet material and a film material. An anchor material disposed on at least one surface of the fabric;
The fabric according to any one of claims 4 to 48, wherein the anchor material has at least one of a porous structure, a network structure, an uneven structure, a protruding structure, an ultrathin structure, a permeation structure, and a flexible structure. sticker. An anchor material disposed on at least one surface of the fabric;
The said anchor material is a textile seal as described in any one of Claims 4 to 49 containing the material which expresses the function which accelerates | stimulates joining between the said textile fabric and the said adhesive material.   51. The fabric seal according to any one of claims 4 to 50, wherein the fabric has a reinforcing portion that partially reinforces the texture structure of the fabric in one plane. The woven fabric has a reinforced portion that partially reinforces the tissue structure of the woven fabric in one plane.
52. The fabric seal according to any one of claims 4 to 51, wherein the reinforcement has a region shaped with an axis substantially along the warp or weft of the fabric. The woven fabric has a reinforced portion that partially reinforces the tissue structure of the woven fabric in one plane.
53. The fabric seal according to any one of claims 4 to 52, wherein at least one of a character, a pattern, and a pattern in the fabric includes at least a part of the reinforcing portion. The woven fabric has a reinforced portion that partially reinforces the tissue structure of the woven fabric in one plane.
At least one of a character, a pattern, and a pattern in the fabric includes at least a part of the reinforcing portion,
The formation region of the reinforced portion is a design expressed based on post-weaving processing, including at least one of post-dyeing, textile printing, printing, resin potting, foiling, embroidery, hand drawing, airbrush, lacquering, prints, and decoration. 54. A fabric seal according to any one of claims 4 to 53, comprising:   The fabric seal according to any one of claims 4 to 54, wherein a shape of a surface of the pressure-sensitive adhesive material in contact with the fabric is controlled. A separator, and a supplementary sheet disposed between the fabric and the separator,
The said adhesive material contains the 1st adhesive material distribute | arranged between the said base material and the said auxiliary sheet | seat, and the 2nd adhesive material distribute | arranged between the said auxiliary sheet | seat and the said separator. 56. A fabric seal according to any one of claims 55. A separator, and a supplementary sheet disposed between the fabric and the separator,
The fabric includes a permeable material, a liquid-absorbing material, or a porous material,
The pressure-sensitive adhesive material includes a first pressure-sensitive adhesive material disposed between the woven fabric and the auxiliary sheet, and a second pressure-sensitive adhesive material disposed between the auxiliary sheet and the separator,
57. The fabric seal according to any one of claims 4 to 56, wherein the specifications of the first adhesive material and the specifications of the second adhesive material are different from each other. A separator, and a supplementary sheet disposed between the fabric and the separator,
The pressure-sensitive adhesive material includes a first pressure-sensitive adhesive material disposed between the woven fabric and the auxiliary sheet, and a second pressure-sensitive adhesive material disposed between the auxiliary sheet and the separator,
The fabric and the first adhesive material are in intimate contact, or
58. The fabric seal according to any one of claims 4 to 57, wherein the fabric and the first adhesive material are loosely in contact with each other. A separator, and a supplementary sheet disposed between the fabric and the separator,
The pressure-sensitive adhesive material includes a first pressure-sensitive adhesive material disposed between the woven fabric and the auxiliary sheet, and a second pressure-sensitive adhesive material disposed between the auxiliary sheet and the separator,
59. The fabric seal according to any one of claims 4 to 58, wherein a shape of a surface of the first adhesive material that is at least partially in contact with the fabric is controlled. A separator, and a supplementary sheet disposed between the fabric and the separator,
The pressure-sensitive adhesive material includes a first pressure-sensitive adhesive material disposed between the woven fabric and the auxiliary sheet, and a second pressure-sensitive adhesive material disposed between the auxiliary sheet and the separator,
The fabric seal according to any one of claims 4 to 59, wherein one surface of the auxiliary sheet in contact with the first adhesive material has a substantially uneven structure. A separator, and a supplementary sheet disposed between the fabric and the separator,
61. The fabric seal according to any one of claims 4 to 60, wherein the auxiliary sheet comprises a film, paper, synthetic paper, cloth, or synthetic resin. A separator, and a supplementary sheet disposed between the fabric and the separator,
The auxiliary sheet has antireflection properties, electromagnetic wave shielding properties, antistatic properties, light shielding properties, frequency selectivity, polarization properties, filter properties, light resistance, moisture permeability, water permeability, water absorption, releasability, delamination property, shape Stability, punching, reinforcement, water resistance, fire resistance, heat resistance, non-permeability, shape following, shape retention, shape stability, ease of processing, static electricity removal, buffering, solvent resistance, Insulation, shrinkage, extensibility, oil resistance, chemical resistance, design, magnetism, conductivity, printability, photosensitivity, protection, rust prevention, mold release, decoration, stretchability, biodegradability 62. The fabric seal according to any one of claims 4 to 61, having at least one of: and antibacterial. A separator, and a supplementary sheet disposed between the fabric and the separator,
The auxiliary sheet has a printed layer,
The printed layer can be observed when the auxiliary sheet is peeled from the object, or can be observed on the surface of the layer left on the object when the auxiliary sheet is delaminated, or 63. The fabric seal according to any one of claims 4 to 62, wherein when the auxiliary sheet is delaminated, it can be observed on the surface of a layer away from the object.   64. The fabric seal according to any one of claims 4 to 63, further comprising at least one of a fold key, a score, and a stop blade.   65. The fabric seal according to any one of claims 4 to 64, wherein the adhesive material does not substantially exhibit adhesiveness at room temperature and develops adhesiveness by a predetermined treatment.   68. A substrate including at least one of a nonwoven fabric, felt, knitting, and lace, or a substrate other than a fabric such as Japanese paper is used instead of the fabric in the fabric seal according to any one of claims 4 to 65. , Adhesive sheet. A substrate;
A supplementary sheet,
A separator;
A first adhesive material disposed between the base material and the auxiliary sheet;
A second adhesive material disposed between the auxiliary sheet and the separator;
With a seal. A substrate;
A supplementary sheet,
A first adhesive material disposed between the base material and the auxiliary sheet;
A second adhesive material disposed on one surface of the auxiliary sheet, which is the surface opposite to the first adhesive material;
Adhesive sheet with The substrate includes a permeable material, a liquid-absorbing material, or a porous material,
69. The adhesive sheet according to claim 68, wherein the specifications of the first adhesive material and the specifications of the second adhesive material are different from each other.   The adhesive sheet according to any one of claims 68 to 69, wherein the base material and the first adhesive material are in close contact with each other.   The adhesive sheet according to any one of claims 68 to 70, wherein the base material and the first pressure-sensitive adhesive material are loosely in contact with each other. One surface of the substrate includes a fine relief structure,
72. The adhesive sheet according to any one of claims 68 to 71, wherein a shape of a surface of the first pressure-sensitive adhesive material at least part of which is in contact with the fine concavo-convex structure is controlled.   The adhesive sheet according to any one of claims 68 to 72, wherein the substrate has a portion having a smaller thickness than other portions.   The adhesive sheet according to any one of claims 68 to 73, wherein the base material has a density of the base material that is higher than that of other parts, and has a high-density portion formed at least partially. .   The said base material is an adhesive sheet as described in any one of Claims 68-74 which has the high osmosis | permeation part which the said 1st adhesive material osmose | permeated more compared with the other part.   76. The adhesive sheet according to any one of claims 68 to 75, wherein the substrate includes a cloth including at least one of a woven fabric, a nonwoven fabric, a felt, a knitted fabric, and a lace, or Japanese paper.   77. The adhesive sheet according to any one of claims 68 to 76, wherein the auxiliary sheet includes at least one of a film, paper, synthetic paper, cloth, and synthetic resin.   The auxiliary sheet has antireflection properties, electromagnetic wave shielding properties, antistatic properties, light shielding properties, frequency selectivity, polarization properties, filter properties, light resistance, moisture permeability, water permeability, water absorption, releasability, delamination property, shape Stability, punching, reinforcement, water resistance, fire resistance, heat resistance, non-permeability, shape following, shape retention, shape stability, ease of processing, static electricity removal, buffering, solvent resistance, Insulation, shrinkage, extensibility, oil resistance, chemical resistance, design, magnetism, conductivity, printability, photosensitivity, protection, rust prevention, mold release, decoration, stretchability, biodegradability 78. The adhesive sheet according to any one of claims 68 to 77, which has at least one of antibacterial properties.   79. The adhesive sheet according to any one of claims 68 to 78, further comprising a separator disposed in contact with the second adhesive material. Preparing a substrate;
Preparing a separator;
Bonding the base material and the separator through an adhesive material;
Providing the substrate with a predetermined function;
The manufacturing method of the adhesive sheet or seal | sticker containing this. Preparing a substrate;
Preparing a separator;
Preparing a supplementary sheet disposed between the substrate and the separator;
Bonding the base material and the auxiliary sheet through a first adhesive material;
Bonding the auxiliary sheet and the separator via a second adhesive material;
Providing the substrate with a predetermined function;
The manufacturing method of the adhesive sheet or seal | sticker containing this.   The predetermined function is strength, abrasion resistance, weather resistance, moisture permeability, waterproofness, water resistance, chemical resistance, washability, appearance, wrinkle resistance, thermal characteristics, heat retention, cold insulation, flexibility, or The method includes at least one of a function of improving flame retardancy, a function of enhancing bondability between the base material and the adhesive material, a barrier function with respect to the adhesive material, and a fraying prevention function of the base material. The manufacturing method of the adhesive sheet or seal | sticker of 80 or 81.