JP2010526709A - 汎用航空の航空機用羽布 - Google Patents
汎用航空の航空機用羽布 Download PDFInfo
- Publication number
- JP2010526709A JP2010526709A JP2010507791A JP2010507791A JP2010526709A JP 2010526709 A JP2010526709 A JP 2010526709A JP 2010507791 A JP2010507791 A JP 2010507791A JP 2010507791 A JP2010507791 A JP 2010507791A JP 2010526709 A JP2010526709 A JP 2010526709A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- fabric
- dispersion
- adhesive
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【選択図】なし
Description
a.本発明の羽布を、羽布が構造体に接続される領域で、接着剤に接触させ、接着剤は熱活性化熱架橋接着物質を有し、熱活性化熱架橋接着物質は、0.5未満の好適なOH数の、カプセル化イソシアネートで作られた15%硬化剤を有する、高分子量ポリウレタンの水性アニオン分散体を基礎にし、そこでは構造体も接着剤で被覆あるいは塗装される、
b.接着剤の乾燥後、羽布は構造体にアイロン掛けされる、
c.羽布が構造体にアイロン掛けされた領域が適切な熱源(アイロン)により約95〜105℃、好ましくは100℃に加熱される、
d.接着剤が冷えたらすぐに、適切な熱源(たとえば、クオーツ放射体またはホットエアガン)により150℃ほどの表面温度で張る、ここで、
e.接着剤の活性化を防ぐために、へこんだ部品に加え、編み目や重なりがこの段階で約100℃の表面温度を超えないことを確認する必要がある、そうしないと、活性化により編み目や重なりがへこんだ部品から離れてしまう。
Claims (46)
- 汎用航空の航空機用羽布であって:
ポリエステル布またはポリエーテルエーテルケトン布を有し;
前記布は架橋された耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体で被覆されたことを特徴とする;
羽布。 - 前記被覆は、0.5未満の好適なOH数のアニオン脂肪族分散体を、好ましくは17〜18の好適なNCO値のヘキサメチル・ジイソシアネートを基礎にした、親水性の脂肪族ポリイソシアネートと架橋することにより製造されることを特徴とする;
請求項1の羽布。 - 汎用航空の航空機用羽布であって:
ポリエステル布またはポリエーテルエーテルケトン布を有し;
前記布は、架橋された耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体で前もって被覆された繊維あるいはフィラメント、またはリング糸、フィラメント糸もしくはより糸から編まれることを特徴とする;
羽布。 - 前記被覆は、0.5未満の好適なOH数のアニオン脂肪族分散体を、好ましくは17〜18の好適なNCO値のヘキサメチル・ジイソシアネートを基礎にした、親水性の脂肪族ポリイソシアネートと架橋することにより製造されることを特徴とする;
請求項3の羽布。 - 前記耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体は、顔料で着色されることを特徴とする;
請求項1ないし請求項4のいずれか1項の羽布。 - 前記布が作られる繊維あるいはフィラメント、またはリング糸、フィラメント糸あるいはより糸は、架橋され顔料で着色された耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体だけで被覆され、前記被覆は、0.5未満のOH数のアニオン脂肪族分散体を、17〜18の好適なNCO値のヘキサメチル・ジイソシアネートを基礎にした、親水性の脂肪族ポリイソシアネートと架橋することにより製造されることを特徴とする;
請求項1ないし請求項5のいずれか1項の汎用航空の航空機用羽布。 - 前記布は追加で接着剤で被覆され、接着剤は、好ましくは0.5未満のOH数の、好ましくはカプセル化イソシアネートで作られた15%硬化剤を含む、高分子量ポリウレタンの水性アニオン分散体を基礎にした熱活性化熱架橋接着物質から構成される;
請求項1ないし請求項6のいずれか1項の羽布。 - 前記アニオン脂肪族分散体は、好ましくはアルミニウム粒子で、着色された;
請求項1ないし請求項7のいずれか1項の羽布。 - 前記ポリエステル布の使用において、追加の疎水性物質を前記被覆に添加することを特徴とする;
請求項1ないし請求項8のいずれか1項の羽布。 - 前記布が、好ましくは請求項1のアニオン脂肪族ポリエステル−ポリウレタン分散体を含む着色被覆として少なくとも1層の、好ましくは2層の追加の被覆を含み、追加の着色顔料が前記分散体に添加されることを特徴とする;
請求項1ないし請求項9のいずれか1項の羽布。 - 好ましくは請求項1のアニオン脂肪族ポリエステル−ポリウレタンを有し、少なくとも1つの導電性顔料を含む追加被覆が塗布され、および/または、導電性材料を有する追加被覆が塗布されることを特徴とする;
請求項1ないし請求項10のいずれか1項の羽布。 - 好ましくは請求項1のアニオン脂肪族ポリエステル−ポリウレタンを有し、紫外線遮蔽体または紫外線吸収体と疎水性物質を含む表層被覆が塗布されることを特徴とする;
請求項1ないし請求項11のいずれか1項の羽布。 - 前記布はDIN53830T3による30〜350dtexの繊度を有することを特徴とする;
請求項1ないし請求項12のいずれか1項の羽布。 - DIN EN 12127による被覆なしのグラム重が30g/m2〜250g/m2の間の単位面積当たりの重量であることを特徴とする;
請求項1ないし請求項13のいずれか1項の羽布。 - 前記糸が備える単一フィラメントの数は、縦糸と横糸で好ましくは15と50の間、または80までであることを特徴とする;
請求項1ないし請求項14のいずれか1項の羽布。 - DIN EN 1049−2による糸の数は、縦糸で20〜50または15〜60で、横糸で15〜40または60までである;
請求項1ないし請求項15のいずれか1項の羽布。 - 前記縦糸あるいは縦糸と横糸が仕上げられていることを特徴とする;
請求項1ないし請求項16のいずれか1項の羽布。 - 前記縦糸および/または横糸の個々のフィラメントが互いに撚られフィラメントの束を形成することを特徴とする;
請求項1ないし請求項17のいずれか1項の羽布。 - 前記布の縮みは、縦方向と横方向とで約150℃の温度で約10%のとなることを特徴とする;
請求項1ないし請求項18のいずれか1項の羽布。 - 前記布が、乾燥チャネル中での被覆の乾燥中にフレームでの引っ張りにより好ましくは約10%の縦方向の縮みを呈する;
請求項1ないし請求項19のいずれか1項の羽布。 - 織り方は、平織りあるいはリップストップで織られることを特徴とする;
請求項1ないし請求項20のいずれか1項の羽布。 - 前記被覆は、水性ポリウレタン構成を基礎にした;
請求項1ないし請求項21のいずれか1項の羽布。 - 前記布が自己消火性被覆を含むことを特徴とする;
請求項1ないし請求項22のいずれか1項の羽布。 - 前記布あるいは繊維あるいはフィラメントあるいはリング糸、フィラメント糸もしくはより糸が、塗布される第1の被覆として、疎水性用被覆を有することを特徴とする;
請求項1ないし請求項23のいずれか1項の羽布。 - 全ての被覆、あるいは最後に塗布された被覆が、前記被覆の接着を硬化し改善するためにカレンダ加工されることを特徴とする;
請求項1ないし請求項24のいずれか1項の羽布。 - 前記布が、編む前にリング糸、フィラメント糸あるいはより糸に加工された繊維あるいはフィラメントを備えることを特徴とする;
請求項1ないし請求項25のいずれか1項の羽布。 - 汎用航空の航空機用羽布の製造方法であって、
プライマ被覆されたポリエステル布またはポリエーテルエーテルケトン布が製造され、そこでは:
a.架橋された耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体が、0.5未満の好適なOH数のアニオン脂肪族分散体を、好ましくは17〜18の好適なNCO値のヘキサメチル・ジイソシアネートを基礎にした、親水性の脂肪族ポリイソシアネートと架橋することにより製造され、その後にポリエステル布またはポリエーテルエーテルケトン布を前記分散体で被覆する、または
b.架橋された耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体で前もって被覆された、繊維あるいはフィラメントあるいはリング糸、フィラメント糸もしくはより糸がポリエステル布またはポリエーテルエーテルケトン布に加工され、前記被覆は、0.5未満の好適なOH数のアニオン脂肪族分散体を、好ましくは17〜18の好適なNCO値のヘキサメチル・ジイソシアネートを基礎にした、親水性の脂肪族ポリイソシアネートと架橋することにより製造される、
のいずれかである;
方法。 - 前記布が製造される前記繊維あるいはフィラメントあるいはリング糸、フィラメント糸もしくはより糸は架橋され顔料で着色された耐熱アニオン脂肪族ポリエステル−ポリウレタン分散体だけで被覆されることを特徴とする;
請求項27の方法。 - 前記繊維あるいはフィラメントあるいはリング糸、フィラメント糸もしくはより糸は、追加で接着剤で被覆され、接着剤は、好ましくは0.5未満のOH数の、カプセル化イソシアネートで作られた好ましくは15%硬化剤を有する、高分子量ポリウレタンの水性アニオン分散体を基礎にした熱活性化熱架橋接着物質で構成されることを特徴とする;
請求項27または請求項28の方法。 - 好ましくはアルミニウム粒子で着色された、着色されたアニオン脂肪族分散体が用いられることを特徴とする;
請求項27ないし請求項29のいずれか1項の方法。 - 前記布の被覆において疎水性物質が追加で添加され、または前記プライマ被覆を前記布あるいは前記繊維あるいはフィラメントに塗布する前に疎水性の層が塗布されることを特徴とする;
請求項27ないし請求項30のいずれか1項の方法。 - 着色被覆として、少なくとも1層、好ましくは2層の追加被覆が前記布、または前記布を製造するのに用いられる繊維あるいはフィラメントに塗布されることを特徴とする;
請求項27ないし請求項31のいずれか1項の方法。 - 好ましくは請求項1のアニオン脂肪族ポリエステル−ポリウレタン分散体を有し、少なくとも1つの導電性顔料を有する追加被覆が塗布され、および/または導電性材料を有する追加被覆が塗布されることを特徴とする;
請求項27ないし請求項32のいずれか1項の方法。 - 好ましくは請求項1のアニオン脂肪族ポリエステル−ポリウレタン分散体を有し、紫外線遮蔽体および疎水性物質を有する表層被覆が塗布されることを特徴とする;
請求項27ないし請求項33のいずれか1項の方法。 - DIN53830T3による30〜350dtexの繊度の布を用いることをことを特徴とする;
請求項27ないし請求項34のいずれか1項の方法。 - 被覆なしのグラム重が用いられ、DIN EN 12127による30g/m2〜250g/m2の単位面積当たりの重量を有することを特徴とする;
請求項27ないし請求項35のいずれか1項の方法。 - 糸が構成される単一フィラメントの数は縦糸と横糸で15から50の間、または80までである糸が用いられることを特徴とする;
請求項27ないし請求項36のいずれか1項の方法。 - 150℃の温度での縮みが好ましくは縦方向でも横方向でも約10%である布を用いることを特徴とする;
請求項27ないし請求項37のいずれか1項の方法。 - 乾燥チャネルでの乾燥の間、フレームで引っ張ることで好ましくは約10%の横方向縮みが達成することを特徴とする;
請求項27ないし請求項38のいずれか1項の方法。 - 自己消火性被覆が追加で塗布されることを特徴とする;
請求項27ないし請求項39のいずれか1項の方法。 - 全ての被覆、あるいは最後に塗布された被覆は、被覆の接着が改善されるカレンダ加工により硬化されることを特徴とする;
請求項27ないし請求項40のいずれか1項の方法。 - 汎用航空の航空機、特に飛行機を被覆する方法であって;
a.請求項1ないし請求項26のいずれか1項の羽布を構造体に取り付ける領域で接着剤と接触させる工程であって、前記接着剤は好ましくは0.5未満のOH数の、カプセル化イソシアネートで作られた好ましくは15%硬化剤を有する高分子量ポリウレタンの水性アニオン分散体を基礎にした熱活性化熱架橋接着物質を有し、前記構造体も前記接着剤で被覆される、工程と、
b.前記接着剤の乾燥後、前記羽布を前記構造体上でアイロン掛けする工程と、
c.前記羽布が前記構造体上でアイロン掛けされた領域を適切な熱源により約95〜100℃に加熱する工程と、
d.前記接着剤が冷えると、全ての覆いの領域を適切な熱源により約150℃の表面温度で張る工程と、
e.前記接着剤を活性化することを防止するためであって、そうしないと編み目と重なりがへこんだ部品から離れてしまうので、前記へこんだ部品に加えて、前記編み目と重なりとをこの段階で100℃の表面温度を超えて加熱しないことを確かにする工程とを備えることを特徴とする;
方法。 - 航空機を覆うための請求項1ないし請求項26のいずれか1項の羽布の使用。
- 請求項1ないし請求項26のいずれか1項の羽布の使用であって、汎用航空の航空機、特に飛行機から静電気を放電するために、導電性被覆で覆われ、および/または、被覆は導電性材料を有し、前記布からの放電は導電性ロッドにより空気に対して効果的となる;
使用。 - 汎用航空の航空機を覆うためのキットであって、
請求項1ないし請求項26のいずれか1項の羽布と、前記羽布を被覆する接着剤とを有し、
前記接着剤は、0.5未満の好適なOH数の、カプセル化イソシアネートで作られた好適な15%硬化剤を有する高分子量ポリウレタンの水性アニオン分散体を基礎にした熱活性化熱架橋接着物質で作られ、前記ポリウレタン接着剤は40℃を超える熱を供給することで架橋される;
キット。 - 溝付きのベルトあるいは溝付きのテープおよび/または補強テープをさらに含む;
請求項45のキット。