JP2010510376A - ポリマーブレンド組成物 - Google Patents
ポリマーブレンド組成物 Download PDFInfo
- Publication number
- JP2010510376A JP2010510376A JP2009538431A JP2009538431A JP2010510376A JP 2010510376 A JP2010510376 A JP 2010510376A JP 2009538431 A JP2009538431 A JP 2009538431A JP 2009538431 A JP2009538431 A JP 2009538431A JP 2010510376 A JP2010510376 A JP 2010510376A
- Authority
- JP
- Japan
- Prior art keywords
- polymer
- composition
- prepolymer
- polymer blend
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
混和性ポリマーブレンドおよび相溶性かつ非混和性ポリマーブレンドが開示される。前記混和性ポリマーブレンド類は単一のガラス転移温度を有している。前記相溶性ポリマーブレンド類は、2つのガラス転移温度を有している。
Description
1)例えば、転写染料をスクリーン印刷して、任意に単色または複数色を表面に有する、単層または多層の熱可塑性基板を製造する。
2)基板を成形して3次元形状にトリミングし、該基板の3次元形状に適合する表面を有する金型に該基板を取りつける方法などにより、前記基板を型構造に適合させる。
3)前記基板と前記金型との間隙に熱可塑性樹脂を射出して、(i)一体的に永久接着した3次元製品を製造、あるいは、(ii)印刷基板から前記射出樹脂に模様や美的効果を転写し、その後該印刷基板を取り除いて、美的効果を成形樹脂に付与する。
(実施例)
(調製方法)
(試験方法)
(結果)
Claims (52)
- (a)遊離アミン基類と遊離無水物基類、およびこれらの組み合わせからなる群から選択される成分を含み、さらに、二無水物とジアミンとから誘導される構造単位類を含むプレポリマーと、
(b)構造基類と末端基類、およびこれらの組み合わせからなる群から選択される反応性成分を含むポリマーと、
から誘導され、前記反応性成分は、前記遊離無水物基類および遊離アミン基類、あるいはこれらの組み合わせに対して反応性を有することを特徴とするポリマーブレンドを含み、前記ポリマーブレンドは非剥離性であることを特徴とする組成物。 - 前記二無水物はオキシジフタル酸無水物であり、前記ジアミンはジアミノジアリールスルホンであることを特徴とする請求項1に記載の組成物。
- 前記ポリマーは、ポリイミド類、ポリエーテルイミド類、ポリアミドイミド類、ポリアリールエーテルケトン類、ポリアリールケトン類、ポリエーテルケトン類、ポリエーテルエーテルケトン類、ポリアリールスルホン類、液晶ポリマー類、ポリアミド類、ポリエステル類、ポリスルフホン類、ポリフェニレンスルフィド類、ポリベンゾイミダゾール類、ポリフェニレン類、およびこれらの2つ以上の組み合わせなどからなる群から選択されることを特徴とする請求項1に記載の組成物。
- 前記ポリマーブレンドは2つのガラス転移温度を有しており、また前記組成物から成形される成形品は、280℃×240時間エイジング後で層間剥離を生じないことを特徴とする請求項1に記載の組成物。
- 前記2つのガラス転移温度は50℃以上であることを特徴とする請求項4に記載の組成物。
- 前記ポリマーは1つのガラス転移温度を有することを特徴とする請求項1に記載の組成物。
- 前記1つのガラス転移温度は100℃以上であることを特徴とする請求項6に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を1〜99質量%とし、前記ポリマーの量を1〜99質量%とすることを特徴とする請求項1に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を10〜90質量%とし、前記ポリマーの量を10〜90質量%とすることを特徴とする請求項8に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を20〜80質量%とし、前記ポリマーの量を20〜80質量%とすることを特徴とする請求項9に記載の組成物。
- 前記ポリマーブレンドは、ASTM D648に準拠した熱変形温度が100℃以上であることを特徴とする請求項1に記載の組成物。
- 前記ポリマーブレンドは、ASTM D638に準拠した引張強度が70MPaを超えることを特徴とする請求項1に記載の組成物。
- 前記ポリマーブレンドは、昇温速度5℃/分とした熱機械分析による測定で、30℃〜200℃における熱膨張係数が100ppm/℃以下であることを特徴とする請求項7に記載の組成物。
- 前記ポリマーブレンドは、連続使用温度が150℃以上であることを特徴とする請求項1に記載の組成物。
- 前記プレポリマーは本質的にベンジルプロトンを含まないことを特徴とする請求項1に記載の組成物。
- 前記組成物はさらに第2のポリマーを含むことを特徴とする請求項1に記載の組成物。
- 前記第2のポリマーは、ポリフェニレンスルホン、ポリエーテルイミド、ポリスルフホン、ポリカーボネート、ポリフェニレンエーテル、ポリメタクリル酸メチル、アクリロニトリルブタジエンスチレン、ポリスチレン、ポリ塩化ビニル、パーフルオロアルコキシアルカンポリマー、テトラフルオロエチレンとパーフルオロビニルエーテルとの共重合体、フッ素化エチレンプロピレンポリマ、ポリ(フェニレンスルフィド)、ポリ(エーテルケトン)、ポリ(エーテル−エーテルケトン)、エチレンクロロトリフルオロエチレンポリマー、ポリビニリデンフッ化物、ポリテトラフルオロエチレン、ポリエチレンテレフフタレート、ポリアセタール、ポリアミド、超高分子ポリエチレン、ポリプロピレン、ポリエチレン、高密度ポリエチレン、低密度ポリエチレン、ポリベンゾイミダゾール、ポリ(アミド−イミド)、ポリ(エーテルスルホン)、ポリ(アリールスルホン)、ポリフェニレン類、ポリベンゾオキサゾール類、ポリベンゾチアゾール類、およびこれらのブレンド類および共重合体類からなる群から選択されることを特徴とする請求項16に記載の組成物。
- 前記プレポリマーは、炭素原子数対(窒素原子数+酸素原子数+硫黄原子数)の比が2.8〜4.2であることを特徴とする請求項1に記載の組成物。
- (a)遊離アミン基類と遊離無水物基類、およびこれらの組み合わせからなる群から選択される成分を含み、さらに、第1の二無水物と第1のジアミンとから誘導される構造単位類を含むプレポリマーと、
(b)構造基類と末端基類、およびこれらの組み合わせからなる群から選択される反応性成分を含み、さらに、第2の二無水物と第2のジアミンとから誘導される構造単位類を含むポリマーと、
から誘導され、前記第1の二無水物が前記第2の二無水物と同じであるか、あるいは前記第1のジアミンが前記第2のジアミンと同じであることを特徴とするポリマーブレンドを含み、前記ポリマーブレンドは単一のガラス転移温度を有することを特徴とする組成物。 - 前記単一のガラス転移温度は100℃以上であることを特徴とする請求項19に記載の組成物。
- 前記第1の二無水物あるいは前記第2の二無水物は、オキシジフタル酸無水物類、ビスフェノール−A二無水物類およびこれらの組み合わせからなる群から選択されることを特徴とする請求項19に記載の組成物。
- 前記第1のジアミンまたは前記第2のジアミンは、ジアミノジアリールスルホン類、メタフェニレンジアミン類、パラフェニレンジアミン類、およびこれらの組み合わせからなる群から選択されることを特徴とする請求項19に記載の組成物。
- 前記プレポリマーは本質的にベンジルプロトンを含まないことを特徴とする請求項19に記載の組成物。
- 前記ポリマーブレンドは、ASTM D648に準拠した熱変形温度が100℃以上であることを特徴とする請求項19に記載の組成物。
- 前記ポリマーブレンドは、ASTM D638に準拠した引張強度が70MPaを超えることを特徴とする請求項19に記載の組成物。
- 前記ポリマーブレンドは、昇温速度5℃/分とした熱機械分析による測定で、30℃〜200℃における熱膨張係数が100ppm/℃以下であることを特徴とする請求項19に記載の組成物。
- 前記ポリマーブレンドは、連続使用温度が150℃以上であることを特徴とする請求項19に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を1〜99質量%とし、前記ポリマーの量を1〜99質量%とすることを特徴とする請求項19に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を10〜90質量%とし、前記ポリマーの量を10〜90質量%とすることを特徴とする請求項28に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を20〜80質量%とし、前記ポリマーの量を20〜80質量%とすることを特徴とする請求項28に記載の組成物。
- 前記プレポリマーは、炭素原子数対(窒素原子数+酸素原子数+硫黄原子数)の比が2.8〜4.2であることを特徴とする請求項19に記載の組成物。
- (a)遊離アミン基類と遊離無水物基類、およびこれらの組み合わせからなる群から選択される成分を含み、さらに、第1の二無水物と第1のジアミンとから誘導される構造単位類を含むプレポリマーと、
(b)構造基類と末端基類、およびこれらの組み合わせからなる群から選択される反応性成分を含み、さらに、第2の二無水物と第2のジアミンとから誘導される構造単位類を含むポリマーと、
から誘導され、前記第1の二無水物は前記第2の二無水物とは異なっており、また前記第1のジアミンは前記第2のジアミンとは異なっていることを特徴とするポリマーブレンドを含む組成物であって、前記ポリマーブレンドは2つ以上のガラス転移温度を有し、前記組成物から成形される成形品は、280℃×240時間エイジング後で本質的に層間剥離がないことを特徴とする組成物。 - 前記ガラス転移温度は50℃以上であることを特徴とする請求項32に記載の組成物。
- 前記第1の二無水物、あるいは第2の二無水物、あるいは前記第1および第の二無水物は共に、オキシジフタル酸無水物類、ビスフェノール−A二無水物類およびこれらの組み合わせからなる群から選択されることを特徴とする請求項32に記載の組成物。
- 前記第1のジアミン、あるいは第のジアミン、あるいは前記第1および第のジアミンは共に、ジアミノジアリールスルホン類、メタフェニレンジアミン類、パラフェニレンジアミン類、およびこれらの組み合わせからなる群から選択されることを特徴とする請求項32に記載の組成物。
- 前記プレポリマーは本質的にベンジルプロトンを含まないことを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を1〜99質量%とし、前記ポリマーの量を1〜99質量%とすることを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を10〜90質量%とし、前記ポリマーの量を10〜90質量%とすることを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を20〜80質量%とし、前記ポリマーの量を20〜80質量%とすることを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドは、ASTM D648に準拠した熱変形温度が100℃以上であることを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドは、ASTM D638に準拠した引張強度が70MPaを超えることを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドは、昇温速度5℃/分とした熱機械分析による測定で、30℃〜200℃における熱膨張係数が100ppm/℃以下であることを特徴とする請求項32に記載の組成物。
- 前記ポリマーブレンドは、連続使用温度が150℃以上であることを特徴とする請求項32に記載の組成物。
- (a)遊離アミン基類と遊離無水物基類、およびこれらの組み合わせからなる群から選択される成分を含み、さらに、オキシジフタル酸無水物類とジアミノジアリールスルホン類とから誘導される構造単位類を含むプレポリマーと、
(b)構造基類と末端基類、およびこれらの組み合わせからなる群から選択される反応性成分を含み、さらに、ビスフェノール−A二無水物類とジアミノジアリールスルホン類とから誘導される構造単位類を含むポリマーと、
から誘導され、前記ポリマーブレンドは単一のガラス転移温度を有することを特徴とする組成物。 - (a)遊離アミン基類と遊離無水物基類、およびこれらの組み合わせからなる群から選択される成分を含み、さらに、オキシジフタル酸無水物類とジアミノジアリールスルホン類とから誘導される構造単位類を含むプレポリマーと、
(b)構造基類と末端基類、およびこれらの組み合わせからなる群から選択される反応性成分を含み、さらに、ビスフェノール−A二無水物類とジアミノジアリールスルホン類とから誘導される構造単位類を含むポリエーテルイミドポリマーと、
から誘導されるポリマーブレンドを含む組成物であって、前記ポリマーブレンドは2つ以上のガラス転移温度を有し、前記組成物から成形される成形品は、280℃×240時間エイジング後で本質的に層間剥離がないことを特徴とする組成物。 - (a)遊離アミン基類と遊離無水物基類、およびこれらの組み合わせからなる群から選択される成分を含み、さらに、オキシジフタル酸無水物類とジアミノジアリールスルホン類とから誘導される構造単位類を含むプレポリマーと、
(b)構造基類と末端基類、およびこれらの組み合わせからなる群から選択される反応性成分を含み、さらに、ビスフェノール−A二無水物とジアミノジアリールスルホンとから誘導される構造単位類を含むポリエーテルイミドポリマーと、さらに、酸化防止剤類と亜リン酸塩類、およびこれらの組み合わせからなる群から選択される安定剤と、
から誘導されるポリマーブレンドを含み、前記ポリマーブレンドは、ASTM D648に準拠した熱変形温度が200℃以上であり、ASTM D638に準拠した引張強度が90MPa以上であり、昇温速度5℃/分とした熱機械分析による測定で、30℃〜200℃における熱膨張係数が60ppm/℃以下であり、また、前記ポリマーブレンドの製造に当たって、前記プレポリマーと前記ポリマーの合計質量に対して、前記プレポリマーの量を50〜95質量%とし、前記ポリエーテルイミドポリマーの量を5〜50質量%とすることを特徴とする組成物。 - 請求項1から誘導される成形品を含む合成物。
- 請求項32から誘導される成形品を含む合成物。
- 請求項42から誘導される成形品を含む合成物。
- 請求項43から誘導される成形品を含む合成物。
- 請求項44から誘導される成形品を含む合成物。
- 前記成形品は、フィルム類、膜類、管類、複合材類、半導体処理具類、ワイヤーコーティング類およびジャケッティング類、流体取扱部品類、調理器具類、フードサービス用品類、医療器具類、トレー類、プレート類、ハンドル類、ヘルメット類、動物檻類、電気コネクタ類、電気設備筐体類、エンジン部品類、自動車エンジン部品類、ベアリング類、照明ソケット類およびリフレクタ類、電動機部品類、配電設備、通信設備、コンピュータ類、スナップ式コネクタ類に成形された器具および繊維類からなる群から選択されることを特徴とする請求項45に記載の合成物。