JP2009297993A - 超疎水性ナノ構造複合体で被覆された構造物及びその製法 - Google Patents
超疎水性ナノ構造複合体で被覆された構造物及びその製法 Download PDFInfo
- Publication number
- JP2009297993A JP2009297993A JP2008154121A JP2008154121A JP2009297993A JP 2009297993 A JP2009297993 A JP 2009297993A JP 2008154121 A JP2008154121 A JP 2008154121A JP 2008154121 A JP2008154121 A JP 2008154121A JP 2009297993 A JP2009297993 A JP 2009297993A
- Authority
- JP
- Japan
- Prior art keywords
- nanostructure
- solid substrate
- polymer
- silica
- superhydrophobic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 固体基材(X)の表面が、超疎水性ナノ構造複合体(Z1)で被覆されてなる構造物であって、該超疎水性ナノ構造複合体(Z1)がポリエチレンイミン骨格(a)を有するポリマー(A)とシリカ(B)とを含有するナノ構造体(y1)中の該シリカ(B)に疎水性基が結合してなる複合体であることを特徴とする超疎水性表面を有する構造物及びその製造方法。
【選択図】 図2
Description
本発明において使用する固体基材(X)としては、後述するポリエチレンイミン骨格(a)を有するポリマー(A)が吸着できるものであれば特に限定されず、例えば、ガラス、金属、金属酸化物などの無機材料系基材、樹脂(プラスチック)、セルロース、繊維、紙などの有機材料系基材等、更にはガラス、金属、金属酸化物表面をエッチング処理した基材、樹脂基材の表面をプラズマ処理、オゾン処理した基材などを使用できる。
本発明において、固体基材(X)上に形成するポリマー層には、ポリエチレンイミン骨格(a)を有するポリマー(A)を用いることを必須とする。該ポリエチレンイミン骨格(a)を有するポリマー(A)としては、線状、星状、櫛状構造の単独重合体であっても、他の繰り返し単位を有する共重合体であっても良い。共重合体の場合には、該ポリマー(A)中のポリエチレンイミン骨格(a)のモル比が20%以上であることが、安定なポリマー層を形成できる点から好ましく、該ポリエチレンイミン骨格(a)の繰り返し単位数が10以上である、ブロック共重合体であることがより好ましい。
本発明で得られる構造物の基材表面は、ポリマー(A)とシリカ(B)とを主構成成分とするナノ構造体(y1)、またはシリカ(B)を主構成成分とするナノ構造体(y2)で被覆されてなるものであることが大きな特徴である。シリカ(B)形成に必要なシリカソースとしては、例えば、アルコキシシラン類、水ガラス、ヘキサフルオロシリコンアンモニウム等を用いることができる。
本発明の構造物における基材表面は、前述のナノ構造体で被覆されている。このナノ構造体(y1)中には金属イオンを安定に取り込むことができ、従って、金属イオンを含有する超疎水性ナノ構造複合体で被覆された構造物を得ることができる。
上記した通り、本発明では金属イオンを構造物中のナノ構造体中に取り込むことができる。従って、これらの金属イオンのなかでも、還元反応により還元されやすい金属イオンは、金属ナノ粒子に変換させることで、該構造体(y1)中に金属ナノ粒子を含有させることができる。
本発明において、構造物を被覆するナノ構造体(y1)中のポリエチレンイミン骨格(a)はアミノ基、ヒドロキシ基、カルボン酸基、スルホン酸基、リン酸基を有する化合物と、水素結合及び/又は静電気引力により、物理的な結合構造を構成することができる。従って、これらの官能基を有する有機色素分子等を該ナノ構造体(y1)中に含有させることが可能である。
ポリマー(A)とシリカ(B)とを含有するナノ構造体(y1)は、基本的にはポリマー(A)がシリカ(B)でコートされた構造の複合ナノファイバーであり、それが基材表面での空間配列を変えながら、全体を覆った状態を構成し、様々なパターンまたはモルフォロジーを形成する。例えば、ナノファバーが固体基材上の全面に主として該ファイバーの長軸が垂直方向を向いて生えているような芝状(ナノ芝)または若干垂直方向よりも倒れている田んぼ状(ナノ田んぼ)、ナノファイバーが基材上全面で横倒れているような畳状(ナノ畳)、ナノファイバーが基材上の全面でネットワークを形成し、ネット状構造になっているスポンジ状(ナノスポンジ)など、多様多種の階層構造を構成することができる。
上記で得られるポリマー(A)とシリカ(B)とを含有するナノ構造体(y1)を、固体基材(X)ごと焼成することで、ポリマー(A)が除去された、シリカ(B)を主構成成分とするナノ構造体(y2)で被覆された固体基材(X)を得ることができる。このとき、焼成によりポリマー(A)は消失するが、シリカ(B)はその構造を維持したままである。従って、ナノ構造体(y1)の空間配置によってナノ構造体(y2)の形状も決定される。すなわち、例えば、ナノファバーが固体基材上の全面に主として該ファイバーの長軸が垂直方向を向いて生えているような芝状(ナノ芝)または若干垂直方向よりも倒れている田んぼ状(ナノ田んぼ)、ナノファイバーが基材上全面で横倒れているような畳状(ナノ畳)、ナノファイバーが基材上の全面でネットワークを形成しているスポンジ状(ナノスポンジ)など、多様多種の階層構造を構成している。
本発明では、超疎水性表面とするために疎水性基でナノ構造体(y1)又はナノ構造体(y2)の表面を修飾しなければならない。当該修飾は、疎水性基を有する化合物との接触で容易に行なうことができる。
本発明の構造物の製造方法は、基本的には、
ポリエチレンイミン骨格(a)を有するポリマー(A)の溶液、ポリエチレンイミン骨格(a)を有するポリマー(A)と金属イオンとの混合溶液、ポリエチレンイミン骨格(a)を有するポリマー(A)と有機色素分子等との混合溶液を固体基材(X)の表面に接触させた後、該基材(X)を取り出し、基材(X)の表面にポリエチレンイミン骨格(a)を有するポリマー(A)と、併用された金属イオンや有機色素分子等とからなるポリマー層が形成した基材を得る工程(1)と、
前記ポリマー層が形成した基材とシリカソース液(B’)と、を接触させて基材表面に吸着したポリマー層中のポリエチレンイミン骨格(a)が有する触媒機能により、シリカ(B)がその上に析出して、ナノ構造体(y1)を形成すると共にそれで基材を被覆する工程(2)と、
前記工程(2)で得られたナノ構造体(y1)に疎水性基を有するシランカップリング剤を含む溶液を接触させることで、疎水性基をナノ構造体表面に導入する工程(3)
から構成される。これらの工程を経て、ポリエチレンイミンが表面組成に含まれた超疎水性表面をする構造物を製造することができる。
単離乾燥したナノ構造体を両面テープにてサンプル支持台に固定し、それをキーエンス製表面観察装置VE−9800にて観察した。
接触角は自動接触角計Contact Angle System OCA (Dataphysics社製)により測定した。
<直鎖状のポリエチレンイミン(L−PEI)の合成>
市販のポリエチルオキサゾリン(数平均分子量50,000,平均重合度5,000,Aldrich社製)3gを、5モル/Lの塩酸15mLに溶解させた。その溶液をオイルバスにて90℃に加熱し、その温度で10時間攪拌した。反応液にアセトン50mLを加え、ポリマーを完全に沈殿させ、それを濾過し、メタノールで3回洗浄し、白色のポリエチレンイミンの粉末を得た。得られた粉末を1H−NMR(重水、日本電子株式会社製、AL300、300MHz)にて同定したところ、ポリエチルオキサゾリンの側鎖エチル基に由来したピーク1.2ppm(CH3)と2.3ppm(CH2)が完全に消失していることが確認された。即ち、ポリエチルオキサゾリンが完全に加水分解され、ポリエチレンイミンに変換されたことが示された。
<ベンゼン環中心の星状ポリエチレンイミン(B−PEI)合成>
Jin,J.Mater.Chem.,13,672−675(2003)に示された方法に従い、前駆体ポリマーであるベンゼン環中心に6本のポリメチルオキサゾリンのアームが結合した星状ポリメチルオキサゾリンの合成を次の通り行った。
[超疎水性表面を有するガラス板構造物]
3×2cmのソーダライムガラス板を上記で得られた4%のL−PEIの水溶液(80℃液)に浸け、30秒間静置した。板を取り出し、室温にて5分間静置させた後、シリカソースの混合液(MS51*/蒸留水/IPA =0.5/3/3体積比)中に、室温で20分浸けた。板を液中から取り出し、エタノールで表面を洗浄し、室温にて乾燥させた。得られた板の表面をSEMで観察したところ、板表面全体はナノファイバーを基本ユニットとするナノ芝で被覆されていることが確認された(図1)。
*MS51:テトラメトキシシランの4量体(コルコート社製)。
[超疎水性表面を有するガラス板構造物]
実施例1の経路で得る図1で示されたガラス板を500℃で2時間焼成し、内部のポリマーを除去した後(図3)、実施例1の同様な方法で、デシルトリメトキシシラン(DTMS)溶液中一定時間浸漬した後、各時間帯での接触角を測定した。図4にそれらの結果を示した。実施例1での結果に比べて、実施例2でのナノ芝中のポリエチレンイミン骨格のポリマーが除去された後の超疎水性化はもっと容易に進行することが示唆された。
[水中で長期超疎水性を示す超疎水性表面を有するガラス板構造物]
実施例2の方法に示された疎水化処理段階で3時間浸漬してから得た構造物を、水道水中一定時間浸漬した後取り出し、接触角を測定した。表1に水道水中浸漬後の接触角を示した。接触角は1ヶ月後でも変化せず、超疎水性は保ったままであった。このことは、該構造物は水中でも長期に渡り水を弾く性質を有することを強く示唆する。即ち、該構造物は半永久性の超疎水性を有する。
[超疎水性表面を有するポリスチレン板構造物]
2×2cmのポスチレン板を濃硫酸液中に3時間浸けた後、水、メタノールで表面を洗浄し、室温で5分間乾燥した。その後、該ポリスチレン板を4%のB−PEIの水溶液(80℃)に浸け、30秒間静置した。板を取り出し、室温にて5分間静置させた後、シリカソースの混合液(MS51/水/IPA=0.5/3/3体積比)につけた後、室温で20分静置した。板を液中から取り出し、エタノールで表面を洗浄し、室温にて乾燥させた。得られた板の表面をSEMで観察した。図5は板表面を被覆したナノファイバーの構造写真である。板表面全体はナノファイバーを基本ユニットとするナノ芝で被覆されていることが確認された。
[超疎水性表面を有する銅板構造物]
1×1cmサイズの銅板を4%のL−PEIの水溶液(80℃液)に浸け、30秒間静置した。板を取り出し、室温にて5分間静置させた後、シリカソースの混合液(MS51/水/IPA=0.5/3/3)につけた後、室温で20分静置した。板を液中から取り出し、エタノールで表面を洗浄し、室温にて乾燥させた。得られた板の表面をSEMで観察した(図6)。銅板表面がナノファイバーを基本ユニットとするナノ構造体で覆われていることが確認された。これを実施例4で示した同様な方法で24時間疎水化処理した。得られた構造物の水接触角は178°であった。
[超疎水性表面中に金ナノ粒子を含む構造物]
実施例1で得たナノ芝被覆ガラス板を2mLのNaAuCl4・2H2Oの水溶液(1%)中に浸けて、80℃で1時間加熱した。ガラス管を取り出し、蒸留水、エタノール順に洗浄した後、室温で乾燥した。これで得たガラス板には薄いワインレッド色が現れた。このワインレッド色はガラス板内壁を被覆するナノ芝中に金ナノ粒子の存在を示すプラズモン吸収に由来する。反射スペクトル(日立製作所株式会社製、UV−3500)からも520nmをピークトップとする金ナノ粒子由来のプラズモン吸収が観測された。掻き落としたナノファイバーのTEM観察から、2〜3nm大きさの金ナノ粒子が確認された。上記金ナノ粒子が含まれたガラス板を実施例4で示した同様な方法で24時間疎水化処理した。得られた構造物の水接触角は179°であった。
[ガラス管内壁が超疎水性表面からなる管状構造物]
上記合成例1で得たポリマーL−PEIを蒸留水中に加え、90℃まで加熱し、4%の水溶液を調製した。ソーダライム材質のガラスピペット(内径6mm、長さ5cm)とシリンジをゴム管で連結し、該ガラス管中に一定目安のところまで前記加温したポリマー水溶液を吸い取ってから、30秒間静置した後、該ポリマー水溶液をシリンジの押し力で排出した。この操作でガラス管内壁にL−PEIポリマー層が形成された。該ガラス管を室温にて5分間静置したのち、ガラス管を20mLのMS51/水(体積比1/1)のシリカソース液中に30分間浸けた。ガラス管を取り出し、ガラス管内壁をエタノールで洗浄した後、それを室温で乾燥した。この作業後、ガラス管に薄青色の反射色が見えた。
[棉性糸表面が超疎水性表面からなる構造物]
50mgの凧糸を2%のL−PEIの水溶液(80℃液)に浸け、30秒間静置した。糸を取り出し、室温にて60分間静置させた後、シリカソースの混合液(MS51/水/IPA=0.5/3/3)中に室温下20分浸漬した。糸を液中から取り出し、エタノールで表面洗浄、室温乾燥を経て、シリカで表面被覆された糸の構造物を得た。得られた糸の表面をSEMで観察した(図10)。シリカ被覆前と後の表面比較から、糸の表面がナノファイバーを基本ユニットとするナノ構造体で覆われていることが確認された。これを実施例4で示した同様な方法で24時間疎水化処理した。
[濾紙表面が超疎水性表面からなる構造物]
2×2cm大きさの濾紙を2%のL−PEIの水溶液(80℃液)に浸け、30秒間静置した。濾紙を取り出し、室温にて60分間静置させた後、シリカソースの混合液(MS51/水/IPA=0.5/3/3)中に室温下20分浸漬した。濾紙を液中から取り出し、エタノールで表面洗浄、室温乾燥を経て、シリカで表面被覆された濾紙の構造物を得た。得られた濾紙の表面をSEMで観察した(図11)。シリカ被覆前後の表面比較から、濾紙の表面がナノファイバーを基本ユニットとするナノ構造体で覆われていることが確認された。これを実施例4で示した同様な方法で24時間疎水化処理した。
Claims (11)
- 固体基材(X)の表面が、超疎水性ナノ構造複合体(Z1)で被覆されてなる構造物であって、
該超疎水性ナノ構造複合体(Z1)がポリエチレンイミン骨格(a)を有するポリマー(A)とシリカ(B)とを含有するナノ構造体(y1)中の該シリカ(B)に疎水性基が結合してなる複合体であることを特徴とする超疎水性表面を有する構造物。 - 前記ナノ構造体(y1)が、太さが10〜200nmの範囲で、且つ長さが50nm〜2μmの範囲にあるナノファイバーを基本ユニットとし、該ナノファイバーの長軸が固体基材(X)の表面に対して略垂直の方向を向いているものである請求項1記載の構造物。
- 前記ナノ構造体(y1)が、太さが10〜200nmの範囲にあるナノファイバーを基本ユニットとし、該ナノファイバーが固体基板(X)上でネット状構造を形成しているものである請求項1記載の構造物。
- 前記ナノ構造体(y1)中に、金属イオン又は金属ナノ粒子を含むものである請求項1〜3の何れか一項記載の構造物。
- 固体基材(X)の表面が、超疎水性ナノ構造複合体(Z2)で被覆されてなる構造物であって、
該超疎水性ナノ構造複合体(Z2)がシリカ(B)を主構成成分とするナノ構造体(y2)中の該シリカ(B)に疎水性基が結合してなる複合体であることを特徴とする超疎水性表面を有する構造物。 - 前記ナノ構造体(y2)が、太さが10〜200nmの範囲で、且つ長さが50nm〜2μmの範囲にあるナノファイバーを基本ユニットとし、該ナノファイバーの長軸が固体基材(X)の表面に対して略垂直の方向を向いているものである請求項5記載の構造物。
- 前記ナノ構造体(y2)が、太さが10〜200nmの範囲にあるナノファイバーを基本ユニットとし、該ナノファイバーが固体基板(X)上でネット状構造を形成しているものである請求項5記載の構造物。
- ポリエチレンイミン骨格(a)を有するポリマー(A)を含有する溶液中に固体基材(X)を浸漬させた後取り出し、該固体基材(X)の表面にポリマー層を形成させる工程(1)と、
前記で得られたポリマー層を有する固体基材(X)と、シリカソース液(B’)とを接触して、固体基材(X)表面のポリマー層中にシリカ(B)を析出させ、ナノ構造体(y1)を形成させる工程(2)と、
前記工程(2)で得た固体基材上のナノ構造体(y1)の表面を、疎水性基を有するシランカップリング剤で処理する工程(3)と、
を有することを特徴とする超疎水性ナノ構造複合体で被覆された構造物の製造方法。 - ポリエチレンイミン骨格(a)を有するポリマー(A)を含有する溶液中に固体基材(X)を浸漬させた後取り出し、該固体基材(X)の表面にポリマー層を形成させる工程(1)と、
前記で得られたポリマー層を有する固体基材(X)と、シリカソース液(B’)とを接触して、固体基材(X)表面のポリマー層中にシリカ(B)を析出させ、ナノ構造体(y1)を形成させる工程(2)と、
前記で得られたナノ構造体(y1)で被覆された固体基材(X)を、更に金、銀及び白金からなる群から選ばれる貴金属のイオン水溶液中に浸漬させることにより、該貴金属イオンをナノ構造体(y1)中に浸透させ、該ナノ構造体(y1)中のポリエチレンイミン骨格(a)による自発還元作用により、当該貴金属の金属ナノ粒子を形成する工程(3)と、
前記工程(3)で得た固体基材(X)上のナノ構造体(y1)の表面を、疎水性基を有するシランカップリング剤で処理する工程(4)、
を有することを特徴とする、金属ナノ粒子を含有する超疎水性ナノ構造複合体で被覆された構造物の製造方法。 - ポリエチレンイミン骨格(a)を有するポリマー(A)と金属イオンとを含有する溶液中に固体基材(X)を浸漬させた後取り出し、該固体基材(X)の表面に金属イオンを含有するポリマー層を形成させる工程(1)と、
前記で得られたポリマー層を有する固体基材(X)と、シリカソース液(B’)とを接触して、固体基材(X)表面のポリマー層中にシリカ(B)を析出させ、金属イオンを含むナノ構造体(y1)を形成させる工程(2)と、
前記工程(2)で得た固体基材(X)上のナノ構造体(y1)の表面を、疎水性基を有するシランカップリング剤で処理する工程(3)と、
を有することを特徴とする、金属イオンを含有する超疎水性ナノ構造複合体で被覆された構造物の製造方法。 - ポリエチレンイミン骨格(a)を有するポリマー(A)を含有する溶液中に固体基材(X)を浸漬させた後取り出し、該固体基材(X)の表面にポリマー層を形成させる工程(1)と、
前記で得られたポリマー層を有する固体基材(X)と、シリカソース液(B’)とを接触して、固体基材(X)表面のポリマー層中にシリカ(B)を析出させ、ナノ構造体(y1)を形成させる工程(2)と、
前記(2)で得たナノ構造体(y1)で被覆された固体基材(X)を焼成し、ナノ構造体(y1)中のポリエチレンイミン骨格(a)を有するポリマー(A)を除去してナノ構造体(y2)とする工程(3)と、
前記工程(3)で得た固体基材上のナノ構造体(y2)の表面を、疎水性基を有するシランカップリング剤で処理する工程(4)と、
を有することを特徴とする超疎水性ナノ構造複合体で被覆された構造物の製造方法。