JP2009249497A - 感圧接着シートおよびその製造方法 - Google Patents
感圧接着シートおよびその製造方法 Download PDFInfo
- Publication number
- JP2009249497A JP2009249497A JP2008099170A JP2008099170A JP2009249497A JP 2009249497 A JP2009249497 A JP 2009249497A JP 2008099170 A JP2008099170 A JP 2008099170A JP 2008099170 A JP2008099170 A JP 2008099170A JP 2009249497 A JP2009249497 A JP 2009249497A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- adhesive sheet
- emulsion
- polymerization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明に係る粘着シートは、アクリル系ポリマーエマルジョンと粘着付与樹脂エマルジョンを含む粘着剤組成物を用いて形成された粘着剤層を備え、1g当たりのトルエン放散量が20μg以下且つ総揮発性有機化合物量が150μg以下であって、官能試験において9割以上のパネラーが該粘着シートから放散した臭気物質の不快度が所定濃度のトルエンよりも低いと判定することを特徴とする。
【選択図】なし
Description
(a)80℃で30分間加熱したときのトルエン放散量が粘着シート1g当たり20μg以下である。
(b)80℃で30分間加熱したときの総揮発性有機化合物量が粘着シート1g当たり150μg以下である。
(c)温度23℃、相対湿度50%の条件下において粘着シート10cm2から24時間のあいだに放散した臭気物質を容積900cm3の空気中に含む測定ガスと、同容積の空気中に0.05gのトルエンを含む対照ガスと、の臭気不快度を比較する官能試験において、パネラーの9割以上が前記対照ガスよりも前記測定ガスのほうが不快度が低いと判定する。
ここで、前記エマルジョン重合は、以下の条件(A)および(B)をいずれも満たすように行われる。
(A)重合開始剤を有する反応容器に前記モノマー原料を供給して常温よりも高い重合温度に維持することにより該モノマー原料の重合反応を行い、次いでその反応液を前記重合温度から常温まで冷却する。
(B)前記モノマー原料を前記反応容器に供給し終えてから間隔をあけて(且つ、典型的には前記冷却を終える前に)、前記反応液に追加の重合開始剤を供給する。該追加の重合開始剤としては、先にモノマー原料の重合反応に使用された重合開始剤よりも半減期温度の低い重合開始剤および/またはレドックス系開始剤(例えば、過酸化水素とアスコルビン酸との組み合わせ)を好ましく採用することができる。
図3,図4は、基材レスの粘着シートの構成例である。図3に示す粘着シート13は、基材レスの粘着剤層2の両面が、少なくとも該粘着剤層側が剥離面となっている剥離ライナー3によってそれぞれ保護された構成を有する。図4に示す粘着シート14は、基材レスの粘着剤層2の一面が、両面が剥離面となっている剥離ライナー3により保護された構成を有し、これを巻回すると粘着剤層2の他面が剥離ライナー3に当接して該他面もまた剥離ライナー3で保護された構成とできるようになっている。このように、基材レス粘着シート13,14では、剥離ライナー3が粘着剤層2を保護するとともに該粘着剤層2を支持する支持体としての機能を果たしている。
図5,図6は、片面粘着タイプの基材付き粘着シートの構成例である。図5に示す粘着シート15は、基材1の片面に粘着剤層2が設けられ、その粘着剤層2の表面(接着面)が、少なくとも該粘着剤層側が剥離面となっている剥離ライナー3によって保護された構成を有する。図6に示す粘着シート16は、基材1の一面に粘着剤層2が設けられた構成を有する。その基材1の他面は剥離面となっており、粘着シート16を巻回すると該他面に粘着剤層2が当接して該粘着剤層の表面(接着面)が基材1の他面で保護された構成とできるようになっている。
なお、トルエン放散量としては、下記のトルエン放散量測定方法により得られた値を採用する。
粘着シートから所定のサイズ(面積:5cm2)を切り取って試料を作製し、該試料をバイアル瓶に入れて密栓する。その後、試料を入れたバイアル瓶を80℃で30分間加熱し、加熱状態のガス1.0mlをヘッドスペースオートサンプラーによりガスクロマトグラフ測定装置(GC測定装置)に注入してトルエンの量を測定し、試料(粘着シート)1g当たりのトルエンの含有量(放散量)[μg/g]を算出し、定量する。
なお、ここで粘着シート1g当たりのトルエン含有量を算出する基準となる粘着シートの質量は、基材付き粘着シートにおいては基材および該基材に支持された粘着剤層を含む全体の質量とし(但し剥離ライナーは含まない。)、基材レスの粘着シートにおいては粘着剤層自体の質量とする。
なお、TVOC量としては、下記のTVOC量測定方法により得られた値を採用する。
上記トルエン放散量測定方法と同様に作製した試料を入れたバイアル瓶を80℃で30分間加熱し、加熱状態のガス1.0mlをヘッドスペースオートサンプラーによりGC測定装置に注入する。得られたガスクロマトグラムに基づいて、粘着剤組成物の作製に使用した材料から予測される揮発物質(残存モノマー、粘着付与樹脂エマルジョンに含まれる溶剤等)については標準物質によりピークの帰属および定量を行い、その他の(帰属困難な)ピークについてはトルエン換算として定量することにより、試料(粘着シート)1g当たりのTVOC量[μg/g]を求める。
なお、ここで粘着シート1g当たりのTVOC量を算出する基準となる粘着シートの質量は、基材付き粘着シートにおいては基材および該基材に支持された粘着剤層を含む全体の質量とし(但し剥離ライナーは含まない。)、基材レスの粘着シートにおいては粘着剤層自体の質量とする。
・カラム:DB−FFAP 1.0μm(0.535mmφ×30m)
・キャリアガス:He 5.0mL/min
・カラムヘッド圧:23kPa(40℃)
・注入口:スプリット(スプリット比12:1、温度250℃)
・カラム温度:40℃(0min)−<+10℃/min>−250(9min)[40℃より、昇温速度10℃/minで250℃まで昇温させた後、250℃で9分間保持させるという意味]
・検出器:FID(温度250℃)
・試験環境:温度23±2℃、相対湿度50±5%に維持された室内にて行う。
・測定試料:粘着シートから所定のサイズ(面積:10cm2)を切り取ったものを測定試料とする。
・測定用容器:容積900cm3(0.9リットル)の新しいガラス瓶を蒸留水で洗浄し、次いでアセトンで洗浄し、80℃で12時間乾燥させた容器を使用する。
・測定ガス:上記試料の片面を上記測定用容器の内面に貼り付けて密栓し、上記試験環境下に24時間放置したもの(測定ガス容器)を少なくとも5個用意する。
・対照ガス:上記測定用容器に0.05gのトルエンを滴下して密栓し、上記試験環境下に24時間放置したもの(対照ガス容器)を、上記測定ガス容器と同数だけ用意する。
・パネラー:少なくとも10人のパネラーにより判定を行う。
・判定方法:各パネラーが測定ガス容器および対照ガス容器の蓋を短時間開けてにおいを嗅ぎ、測定ガスおよび対照ガスのうちどちらが不快度がより少ないと感じたかを記録する。なお、1個の容器につき評価するパネラーは2人までとする。すなわち、2回蓋を開けた容器はそれ以上評価に使用しない。
(サンプリング条件)
・捕集管:Waters社製「SEP−PAK DNPHSilica カートリッジ short type」
・流量:167mL/min
・採取量:10L
(測定機器等)
・小形チャンバー:ADTEC社製「20Lチャンバー」
・清浄空気供給装置:新菱エコビジネス社製「ADclean」
・シール材、シールボックス:なし
・温湿度制御装置:ADTEC社製「ADPAC−SYSTEM III 温湿度ユニット」
・空気捕集装置:ジーエルサイエンス社製「SP208−1000DUAL サンプリングポンプ」
(分析条件)
・高速液体クロマトグラフ:Waters社製「TM996PAD」
・検出器:UV Detector
・カラム:Waters社製「Puresil C18(4.6×150mm)」
・移動相:アセトニトリル水溶液(アセトニトリル:水=50:50)
・注入量:20μL
・検出波長:360nm
CH2=C(R1)COOR2 ・・・(1);
で表される化合物から選択される一種または二種以上であり得る。ここで、上記式(1)中のR1は水素原子またはメチル基である。また、該式(1)中のR2は炭素数1〜20のアルキル基である。上記R2の具体例としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、s−ブチル基、t−ブチル基、ペンチル基、イソアミル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、イソオクチル基、2−エチルヘキシル基、ノニル基、イソノニル基、デシル基、イソデシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等が挙げられる。これらのうち炭素数が2〜14(以下、このような炭素数の範囲を「C2−14」と表すことがある。)のアルキル基が好ましく、C2−10のアルキル基(例えばブチル基、2−エチルヘキシル基等)がより好ましい。
かかる官能基含有モノマーを含む組成のモノマー原料では、アルキル(メタ)アクリレート100質量部に対する官能基含有モノマー(二種以上を含む場合にはそれらの合計)の含有割合を例えば凡そ12質量部以下(典型的には凡そ0.5〜12質量部)とすることができる。この割合がアルキル(メタ)アクリレート100質量部に対して凡そ8質量部以下(典型的には凡そ1〜8質量部)であってもよい。
重合開始剤の使用量は、通常と同程度の使用量であればよく、例えばモノマー原料100質量部に対して凡そ0.005〜1質量部程度の範囲から選択することができる。
乳化剤の使用量は、アクリル系ポリマーをエマルジョンの形態に調製することが可能な使用量であれば特に制限されず、例えば、アクリル系ポリマーまたはモノマー原料に対して凡そ0.2〜10質量%(好ましくは凡そ0.5〜5質量%)程度の範囲から選択することができる。
粘着シートを構成する基材(典型的にはシート状基材)としては、例えば、ポリオレフィン(ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体等)製フィルム、ポリエステル(ポリエチレンテレフタレート等)製フィルム、塩化ビニル系樹脂製フィルム、酢酸ビニル系樹脂製フィルム、ポリイミド系樹脂製フィルム、ポリアミド系樹脂製フィルム、フッ素系樹脂製フィルム、その他セロハン類等のプラスチックフィルム類;和紙、クラフト紙、グラシン紙、上質紙、合成紙、トップコート紙等の紙類;綿繊維、スフ、マニラ麻、パルプ、レーヨン、アセテート繊維、ポリエステル繊維、ポリビニルアルコール繊維、ポリアミド繊維、ポリオレフィン繊維等の天然繊維、半合成繊維または合成繊維の繊維状物質等からなる単独または混紡等の織布や不織布等の布類;天然ゴム、ブチルゴム等からなるゴムシート類;発泡ポリウレタン、発泡ポリクロロプレンゴム等の発泡体からなる発泡体シート類;アルミニウム箔、銅箔等の金属箔;およびこれらの複合体等が挙げられる。前記プラスチックフィルム類は、無延伸タイプであってもよく、延伸タイプ(1軸延伸タイプまたは2軸延伸タイプ)であってもよい。基材は、単層の形態を有していてもよく、積層された形態を有していてもよい。また、基材には、必要に応じて、滑剤、可塑剤、充填剤、顔料や染料等の着色剤、帯電防止剤、老化防止剤、紫外線吸収剤、酸化防止剤等の各種添加剤が配合されていてもよい。基材の表面(特に、粘着剤層が設けられる側の表面)には、例えば、コロナ放電処理、プラズマ処理等の物理的処理、下塗り処理、背面処理等の化学的処理等の適宜な公知または慣用の表面処理が施されていてもよい。基材の厚さは目的に応じて適宜選択できるが、一般には凡そ10μm〜500μm(好ましくは凡そ10μm〜200μm)程度である。
また、フッ素系ポリマー(例えば、ポリテトラフルオロエチレン、ポリクロロトリフルオロエチレン、ポリフッ化ビニル、ポリフッ化ビニリデン、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体、クロロフルオロエチレン−フッ化ビニリデン共重合体等)または低極性ポリマー(例えば、ポリエチレン、ポリプロピレン等のオレフィン系樹脂等)からなる低接着性の基材を、該基材の表面に剥離処理を施すことなく剥離ライナーとして用いてもよい。あるいは、かかる低接着性基材の表面に剥離処理を施したものを剥離ライナーとして用いてもよい。剥離ライナーを構成する基材や剥離処理層の厚みは特に制限されず、目的等に応じて適宜選択することができる。剥離ライナーの総厚み(基材表面に剥離処理層を有する構成の剥離ライナーでは、基材および剥離処理層を含む全体の厚さ)は、例えば凡そ15μm以上(典型的には凡そ15μm〜500μm)であることが好ましく、凡そ25μm〜500μmであることがより好ましい。
これら好適な態様に係る粘着シートが形成されるように、アクリル系ポリマーエマルジョンの重合態様(例えば、追加開始剤の種類や添加タイミング)の設定および使用する粘着付与樹脂エマルジョンの選択を行うことが好ましい。
冷却管、窒素導入管、温度計および攪拌機を備えた反応容器に、2,2’−アゾビス[N−(2−カルボキシエチル)−2−メチルプロピオンアミジン]ハイドレート(重合開始剤)(和光純薬工業株式会社から入手可能な商品名「VA−057」を使用した。)0.1部およびイオン交換水35部を投入し、窒素ガスを導入しながら1時間攪拌して60℃に昇温した。該重合温度(ここでは60℃)を維持しつつ、ここにブチルアクリレート90部、2−エチルヘキシルアクリレート10部、アクリル酸4部、ドデカンチオール(連鎖移動剤)0.05部およびポリオキシエチレンラウリル硫酸ナトリウム(乳化剤)2部をイオン交換水40部に添加して乳化したもの(すなわち、モノマー原料のエマルジョン)を4時間かけて徐々に滴下して乳化重合反応を進行させた。モノマー原料エマルジョンの滴下終了後、さらに2時間同温度(ここでは60℃)に保持して熟成した。熟成終了後、アスコルビン酸0.1部および35%過酸化水素水0.1部(追加の重合開始剤)を添加して、系を常温まで冷却した。このようにしてアクリル系ポリマーを含む反応混合物を得た。
上記反応混合物に10%アンモニウム水を添加して液性をpH7に調整し、次いでオキサゾリン系架橋剤(日本触媒化学工業株式会社から入手可能な商品名「エポクロス(商標)WS−700」、オキサゾリン基含有ポリマーの水溶液)を固形分基準で0.7部添加して、例1に係るアクリル系ポリマーの水分散液(エマルジョン)を得た。
本例では、例1に係るアクリル系ポリマーエマルジョンに添加する粘着付与樹脂エマルジョンとして商品名「タマノルE−200−NT」(荒川化学株式会社製、軟化点150℃のロジンフェノール系樹脂の水性エマルジョン)を、該エマルジョンに含まれるアクリル系ポリマー100部当たり30部(固形分基準)の割合で使用した。その他の点については例1と同様にして、例2に係る両面粘着シートを作製した。なお、商品名「タマノルE−200−NT」は、脂環式炭化水素系有機溶剤(すなわち、非芳香族炭化水素系有機溶剤)を用いて製造された粘着付与樹脂エマルジョンである。
本例では、モノマー原料のエマルジョンとして、ブチルアクリレート40部、2−エチルヘキシルアクリレート60部、メチルアクリレート3部、アクリル酸3部、3−メタクリロイルオキシプロピルトリメトキシシラン(信越化学工業株式会社から入手可能な商品名「KBM−503」を使用した。)0.06部、ドデカンチオール(連鎖移動剤)0.05部およびポリオキシエチレンラウリル硫酸ナトリウム2部をイオン交換水40部に添加して乳化したものを使用した。また、オキサゾリン系架橋剤は使用しなかった。その他の点については例1と同様にして、例3に係るアクリル系ポリマーエマルジョンを得た。
このアクリル系ポリマーエマルジョンに対し、該エマルジョンに含まれるアクリル系ポリマー100部当たり30部(固形分基準)の割合で商品名「SK−253NS」を添加して例3に係る粘着剤組成物を調製し、該粘着剤組成物を用いて例1と同様に両面粘着シートを作製した。
本例では、アクリル系ポリマーエマルジョンに粘着付与樹脂エマルジョンを添加しない点を除いては例1と同様にして粘着剤組成物を調製した。この粘着剤組成物を用いて例1と同様に両面粘着シート(すなわち、粘着付与樹脂を含まない粘着剤層を備える粘着シート)を作製した。
本例では、モノマー原料のエマルジョンとして、ブチルアクリレート80部、2−エチルヘキシルアクリレート20部、メチルアクリレート3部、アクリル酸2部、ドデカンチオール(連鎖移動剤)0.05部およびポリオキシエチレンラウリル硫酸ナトリウム2部をイオン交換水40部に添加して乳化したものを使用した。冷却管、窒素導入管、温度計および攪拌機を備えた反応容器に、2,2’−アゾビス[2−(2−イミダゾリン−2−イル)]プロパン(重合開始剤)(和光純薬工業株式会社から入手可能な商品名「VA−061」を使用した。)0.1部およびイオン交換水35部を投入し、窒素ガスを導入しながら1時間攪拌して60℃に昇温した。該重合温度(ここでは60℃)を維持しつつ、上記モノマー原料のエマルジョンを4時間かけて徐々に滴下して乳化重合反応を進行させた。モノマー原料エマルジョンの滴下終了後、さらに2時間同温度(ここでは60℃)に保持して熟成した。熟成終了後、追加の重合開始剤を添加することなく系を常温まで冷却した。このようにしてアクリル系ポリマーを含む反応混合物を得た。該混合物を用いた点以外は例1と同様にして(すなわち、オキサゾリン系架橋剤および粘着付与樹脂としての商品名「SK−253NS」を添加して)、例5に係る両面粘着シートを作製した。
本例では、例1に係るアクリル系ポリマーエマルジョンに添加する粘着付与樹脂エマルジョンとして商品名「タマノルE−200」(荒川化学株式会社製、軟化点150℃のロジンフェノール系樹脂のエマルジョン)を、該エマルジョンに含まれるアクリル系ポリマー100部当たり30部(固形分基準)の割合で使用した。その他の点については例1と同様にして、例6に係る両面粘着シートを作製した。なお、商品名「タマノルE−200」は、芳香族炭化水素系有機溶剤を用いて製造された粘着付与樹脂エマルジョンである。
また、例1〜6に係る両面粘着シートにつき、上述した方法により、臭気不快度試験を行った。パネラーの人数は10人とし、一種類の試料につき5個の測定ガス容器および同数の対照ガス容器を用意した。なお、例1〜6に係る両面粘着シート10cm2には約1.6gの粘着剤が含まれる。
さらに、例1〜6に係る両面粘着シートの接着性および端末剥がれ防止性を以下の方法により評価した。得られた結果を、各例に係る粘着シートの製造に使用した粘着剤組成物の概略構成(追加開始剤使用の有無、使用した粘着付与樹脂エマルジョンの商品名)とともに表1に示す。表中の「におい低減効果」の欄には、対照ガスよりも測定ガスのほうが臭気不快度が低いと判定したパネラーの人数を示している。
両面粘着シートの一面を覆う剥離ライナーを剥がして粘着剤層を露出させ、これを厚さ25μmのPETフィルムに貼り付けて裏打ちした。この裏打ちされた粘着シートを幅20mm、長さ100mmのサイズにカットして試験片を作製した。上記試験片の他面から剥離ライナーを剥がし、該試験片を被着体としてのSUS304ステンレス板に、2kgのローラを1往復させる方法で圧着した。これを23℃に30分間放置した後、JIS Z0237に準じ、温度23℃、相対湿度50%の測定環境下、引張試験機を使用して引張速度300mm/分、剥離角度180°の条件で剥離強度(N/20mm幅)を測定した。
両面粘着シートの一面を覆う剥離ライナーを剥がして粘着剤層を露出させ、これを厚さ0.5mm、幅10mm、長さ90mmのアルミニウム板に貼り合わせて試験片を作製した。その試験片の長手方向をφ50mmの丸棒に沿わせて弧状に曲げた後、該試験片の他面から剥離ライナーを剥がし、ラミネータを用いてポリプロピレン板に圧着した。これを23℃の環境下に24時間放置し、次いで70℃で2時間加温した後に、ポリプロピレン板表面から浮きあがった試験片端部の高さ(mm)を測定した。
一方、粘着付与樹脂エマルジョンを配合しない例4に係る粘着剤組成物を用いて得られた粘着シートは粘着性能の低いものであった。また、追加開始剤の添加を省略したアクリル系ポリマーエマルジョンを用いてなる例5に係る粘着剤組成物から形成された粘着シートは臭気不快度が高く、TVOC量も多かった。また、芳香族系炭化水素系有機溶剤を用いて製造された粘着付与樹脂エマルジョンを配合した例6に係る粘着剤組成物を用いた粘着シートはトルエン放散量が明らかに多く、臭気不快度も高めであった。
2:粘着剤層
3:剥離ライナー
11,12,13,14,15,16:粘着シート
Claims (8)
- アクリル系ポリマーの水性エマルジョンと粘着付与樹脂の水性エマルジョンとを含む感圧接着剤組成物を用いて形成された感圧接着剤層を有する感圧接着シートであって、
以下の条件:
80℃で30分間加熱したときのトルエン放散量が感圧接着シート1g当たり20μg以下である;
80℃で30分間加熱したときの総揮発性有機化合物量が感圧接着シート1g当たり150μg以下である;および、
温度23℃、相対湿度50%の条件下において感圧接着シート10cm2から24時間のあいだに放散した臭気物質を容積900cm3の空気中に含む測定ガスと、同容積の空気中に0.05gのトルエンを含む対照ガスと、の臭気不快度を比較する官能試験において、パネラーの9割以上が前記対照ガスよりも前記測定ガスのほうが不快度が低いと判定する;
をいずれも満たすことを特徴とする、感圧接着シート。 - 前記粘着付与樹脂エマルジョンは軟化点120℃以上の粘着付与樹脂の水性エマルジョンであり、該粘着付与樹脂エマルジョンは芳香族炭化水素系溶剤を実質的に使用することなく調製されたエマルジョンである、請求項1に記載の感圧接着シート。
- 前記粘着付与樹脂エマルジョンは、有機溶剤を実質的に使用することなく調製されたエマルジョンである、請求項1または2に記載の感圧接着シート。
- 請求項1から3のいずれかに記載の感圧接着シートを製造する方法であって:
アルキル(メタ)アクリレートを主モノマーとするモノマー原料をエマルジョン重合に付して前記アクリル系ポリマーの水性エマルジョンを得ること;
該アクリル系ポリマーエマルジョンと前記粘着付与樹脂の水性エマルジョンとを混合して前記感圧接着剤組成物を調製すること;および、
その感圧接着剤組成物を乾燥させて前記感圧接着剤層を形成すること;
を包含し、
ここで、前記エマルジョン重合は、以下の条件:
重合開始剤を有する反応容器に前記モノマー原料を供給して常温よりも高い重合温度に維持することにより該モノマー原料の重合反応を行い、次いでその反応液を前記重合温度から常温まで冷却する;および、
前記モノマー原料を前記反応容器に供給し終えてから間隔をあけて、前記反応液に追加の重合開始剤を供給する;
をいずれも満たすように行われる、感圧接着シート製造方法。 - 前記追加の重合開始剤は、先にモノマー原料の重合反応に使用された重合開始剤よりも半減期温度の低い重合開始剤である、請求項4に記載の方法。
- 前記追加の重合開始剤はレドックス系開始剤である、請求項4に記載の方法。
- 前記レドックス系開始剤が過酸化水素とアスコルビン酸との組み合わせである、請求項6に記載の方法。
- 前記感圧接着剤組成物の乾燥を110℃以下の温度で行う、請求項4から7のいずれかに記載の方法。