JP2008087158A - Decorative sheet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a decorative sheet used for the surface decoration of the interior trim, exterior trim, furniture and fittings of a building, the trim or the like of a vehicle, etc. and superior in decorative properties having damage resistance, antistaining properties, a tactile feeling, a matte feeling, a gloss feeling, etc., especially excellent in uneven feeling. <P>SOLUTION: The decorative sheet 1 is obtained by laminating at least a color layer 3, a protective layer 4 for covering the color layer 3 and the protruding layer 7 provided on the protective layer 4 and formed of a large number of protruding parts 6 on a base material 5 in this order. The occupying area within a height range of 20-50 μm of the protruding parts 6 with respect to the protective layer 4 is 50% or more. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

  The present invention relates to a decorative sheet used for interiors, exteriors, furniture, surface decorations of furniture, interiors of vehicles, etc., and in particular, design properties having scratch resistance, contamination resistance, touch, matte feeling, glossiness, etc. The present invention relates to a decorative sheet that is particularly excellent in unevenness.

As surface decorative boards for interiors, exteriors, furniture, joinery, and vehicle interiors of buildings, for example, those having a structure in which a decorative sheet printed with a wood grain pattern or the like is bonded with an adhesive are used.
The decorative sheet used for such a decorative sheet is required to have various characteristics such as excellent design as well as touch, matte, gloss and stain resistance.
Among these, it has been proposed to provide a raised portion on the surface of the decorative sheet, in particular, in order to obtain a tactile sensation, matte sensation, glossiness, and design.
As such a decorative sheet, for example, Patent Document 1 discloses a decorative sheet in which a polygonal or circular regular or regular raised portion is provided on the surface of the decorative sheet, and Patent Document 2 describes the unevenness of the raised portion. A decorative sheet, in which the surface area ratio of the difference and the convex portion is limited, Patent Document 3 discloses a decorative sheet provided with a concavo-convex portion made of an ionizing radiation curable resin ink on the surface.
However, this decorative sheet does not have sufficient scratch resistance, stain resistance, tactile sensation, matte feeling and glossiness as a sheet, and further improvement in design properties has been demanded.

JP 2003-94592 A Japanese Patent No. 3334365 JP 2004-249586

  An object of the present invention is to provide a decorative sheet having excellent design properties having scratch resistance, stain resistance, touch, matte feeling, glossiness, and the like, even though it has been made to solve the above problems.

As a result of intensive studies to achieve the above object, the present inventor has found that the above object can be achieved by making the embossed portion provided on the outermost surface of the decorative sheet an irregular pattern. The invention has been completed.
That is, in the present invention, at least a colored layer, a protective layer covering the colored layer, and a raised layer formed from a large number of raised portions provided on the protective layer are laminated in this order on the substrate. A decorative sheet, wherein an area occupied by a height of 20 to 50 μm of the raised portion with respect to the protective layer is 50% or more.

  ADVANTAGE OF THE INVENTION According to this invention, the decorative sheet which is excellent in the designability which has scratch resistance, stain resistance, a touch feeling, a mat | matte feeling, glossiness, etc., and was especially excellent in the unevenness | corrugation feeling can be obtained.

As shown in FIG. 1, the decorative sheet 1 of the present invention includes at least a colored layer 3, a protective layer 4 covering the colored layer 3, and a large number of raised portions provided on the protective layer 4. 6 is a decorative sheet 1 formed by laminating a buildup layer 7 formed in this order, and the occupied area in a range of 20 to 50 μm in height of the buildup portion 6 with respect to the protective layer 4 is 50% or more.
As shown in FIG. 1, the decorative sheet 1 of the present invention may have a colored solid layer 2 between the base material 5 and the colored layer 3.

The base material 5 used in the present invention is not particularly limited as long as it is usually used as a base material for a decorative sheet. Various papers, plastic films, plastic sheets, metal foils, metal sheets, metal plates, A woody board such as wood, a ceramic material, or the like can be appropriately selected according to the application. Each of these materials may be used alone, but may be a laminate of any combination such as a composite of paper or a composite of paper and a plastic film.
When using these substrates, particularly plastic films or plastic sheets, as a substrate, an oxidation method or a concavo-convex method may be applied to one or both sides as desired in order to improve the adhesion to the layer provided thereon. Physical or chemical surface treatment can be applied.
Examples of the oxidation method include corona discharge treatment, chromium oxidation treatment, flame treatment, hot air treatment, ozone / ultraviolet treatment method, and examples of the unevenness method include a sand blast method and a solvent treatment method. These surface treatments are appropriately selected depending on the type of substrate, but generally, a corona discharge treatment method is preferably used from the viewpoints of effects and operability.
In addition, the base material may be subjected to a treatment such as forming a primer layer, or a coating for adjusting the color or a pattern from a design viewpoint may be formed in advance.

As various papers used as the substrate 5, thin paper, kraft paper, titanium paper and the like can be used. These paper base materials are used to reinforce the interlaminar strength between the fibers of the paper base material or between the other layers and the paper base material, and to prevent the occurrence of scuffing, in addition to these paper base materials, acrylic resin, styrene butadiene rubber, A resin such as a melamine resin or a urethane resin may be added (resin impregnation after paper making or embedded during paper making). For example, inter-paper reinforced paper, resin-impregnated paper and the like.
In addition to these, various papers often used in the field of building materials such as linter paper, paperboard, base paper for gypsum board, or a vinyl wallpaper raw material in which a vinyl chloride resin layer is provided on the surface of the paper can be mentioned. Furthermore, coated paper, art paper, sulfate paper, glassine paper, parchment paper, paraffin paper, Japanese paper, or the like used in the office field or normal printing and packaging can also be used. Moreover, although distinguished from these papers, woven fabrics and non-woven fabrics of various fibers having an appearance and properties similar to paper can be used as the base material. Examples of various fibers include inorganic fibers such as glass fibers, asbestos fibers, potassium titanate fibers, alumina fibers, silica fibers, and carbon fibers, or synthetic resin fibers such as polyester fibers, acrylic fibers, and vinylon fibers.

  As a plastic film or a plastic sheet, what consists of various synthetic resins is mentioned. Synthetic resins include polyethylene resin, polypropylene resin, polymethylpentene resin, polyvinyl chloride resin, polyvinylidene chloride resin, polyvinyl alcohol resin, vinyl chloride-vinyl acetate copolymer resin, ethylene-vinyl acetate copolymer resin, ethylene-vinyl. Representative examples include alcohol copolymer resin, polyethylene terephthalate resin, polybutylene terephthalate resin, polyethylene naphthalate-isophthalate copolymer resin, polymethyl methacrylate resin, polyethyl methacrylate resin, polybutyl acrylate resin, nylon 6 or nylon 66 And polyamide resin, cellulose triacetate resin, cellophane, polystyrene resin, polycarbonate resin, polyarylate resin, polyimide resin, and the like.

  As metal foil, a metal sheet, or a metal plate, what consists of aluminum, iron, stainless steel, or copper, for example can be used, and what gave these metals by plating etc. can also be used. Examples of the various wood-based boards include wood fiberboards such as wood veneer, plywood, laminated wood, particle board, or MDF (medium density fiberboard). Examples of the ceramic material include ceramic building materials such as gypsum board, calcium silicate board, and wood cement board, ceramics, glass, firewood, and fired tile. In addition to these, composites of various materials, such as fiber reinforced plastic (FRP) plates, paper honeycombs with iron plates pasted on both sides, and two aluminum plates sandwiched with polyethylene resin can also be used as the base material. .

Although there is no restriction | limiting in particular about the thickness of the base material 5, When using the sheet | seat which uses a plastic as a raw material, thickness is about 20-150 micrometers normally, Preferably it is the range of 30-100 micrometers, and a paper base material is used. When used, the basis weight is usually about ²⁰ to 150 g / m ² , preferably 30 to 100 g / m ² .

In the present invention, the colored solid layer 2 is also referred to as a concealing layer or a full surface solid layer provided as desired for the purpose of improving the design of the decorative sheet of the present invention. The colored solid layer 2 is formed when the color of the surface of the base material 5 is adjusted so that the base material 5 itself is colored or uneven in color, and gives the intended color to the surface of the base material 5 It is. Usually, it is formed with an opaque color, but it may be formed with a colored transparent color to make use of the pattern of the base. When utilizing that the base material 5 is white, or when the base material 5 itself is appropriately colored, it is not necessary to form the colored solid layer 2.
As the ink used for forming the colored solid layer 2, an ink in which a binder, a colorant such as a pigment or a dye, an extender pigment, a solvent, a stabilizer, a plasticizer, a catalyst, or a curing agent is appropriately mixed is used. The binder is not particularly limited, and examples thereof include polyurethane resins, vinyl chloride / vinyl acetate copolymer resins, vinyl chloride / vinyl acetate / acrylic copolymer resins, chlorinated polypropylene resins, acrylic resins, and polyesters. Arbitrary resins, polyamide resins, butyral resins, polystyrene resins, nitrocellulose resins, cellulose acetate resins and the like may be used alone or in combination of two or more.
Colorants include carbon black (black), iron black, titanium white, antimony white, yellow lead, titanium yellow, petal, cadmium red, ultramarine, cobalt blue and other inorganic pigments, quinacridone red, isoindolinone yellow, phthalocyanine Organic pigments or dyes such as blue, metallic pigments composed of scaly foil pieces such as aluminum and brass, pearlescent pigments composed of scaly foil pieces such as titanium dioxide-coated mica and basic lead carbonate, and the like are used.
The colored solid layer 2 is preferably a so-called solid printed layer having a thickness of about 1 to 20 μm.

In the present invention, the colored layer 3 gives decorativeness to the base material 5 and is formed by printing various patterns using ink and a printing machine. The colored layer 3 is preferably a pattern layer, It is preferable that the pattern layer is an abstract pattern. As patterns, there are stone patterns imitating the surface of rocks such as wood grain patterns, marble patterns (for example, travertine marble patterns), fabric patterns imitating cloth or cloth patterns, tiled patterns, brickwork patterns, etc. There are also patterns such as marquetry and patchwork that combine these. These patterns can be formed by multicolor printing with normal yellow, red, blue, and black process colors, and also by multicolor printing with special colors prepared by preparing individual color plates that make up the pattern. Is done.
The colored layer 3 may be provided on the front surface of the base material or may be provided partially as shown in FIG.
As the pattern ink used for the colored layer 3, the same ink as that used for the colored solid layer 2 can be used.
Although there is no restriction | limiting in particular about the thickness of the colored layer 3, Usually, about 1-20 micrometers, Preferably it is the range of 1-10 micrometers.

In the present invention, the protective layer 4 is not particularly limited as long as it is a material that protects the colored layer 3. For example, a known curable paint such as a thermosetting resin may be appropriately employed depending on the application. it can.
Examples of the thermosetting resin include polyester resin, urethane resin, epoxy resin, melamine resin, alkyd resin, phenol resin, and acrylic resin.
Although there is no restriction | limiting in particular about the thickness of the protective layer 4, Usually, about 1-20 micrometers, Preferably it is the range of 1-10 micrometers.

In the present invention, the raised layer 7 is formed from a large number of raised portions 6 provided on the protective layer 4, thereby enhancing the decorativeness or design of the decorative sheet.
In the present invention, by limiting the occupied area in the range of the height 20 to 50 μm of the raised portion 6 with respect to the protective layer 4 to 50% or more, in particular, in addition to touch, matte, gloss and design, A decorative sheet with excellent unevenness can be obtained, and the occupied area of the raised portion 6 in the range of 20 to 50 μm in height is preferably 50 to 99%.

The material of the raised layer 7 is not particularly limited, and for example, the ink used for the colored solid layer 2 or the thermosetting resin, ionizing radiation, or ultraviolet curable resin composition mentioned in the protective layer 4 can be used.
The ionizing radiation or ultraviolet curable resin composition is one having an energy quantum capable of crosslinking and polymerizing molecules in an electromagnetic wave or a charged particle beam, that is, crosslinking by irradiating with an ultraviolet ray or an electron beam, It refers to a resin composition that cures. Specifically, it can be appropriately selected from polymerizable monomers and polymerizable oligomers or prepolymers conventionally used as ionizing radiation or ultraviolet curable resin compositions.

  Typically, a (meth) acrylate monomer having a radical polymerizable unsaturated group in the molecule is suitable as the polymerizable monomer, and among them, a polyfunctional (meth) acrylate is preferable. Here, “(meth) acrylate” means “acrylate or methacrylate”. The polyfunctional (meth) acrylate is not particularly limited as long as it is a (meth) acrylate having two or more ethylenically unsaturated bonds in the molecule. Specifically, ethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, 1,4-butanediol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, neopentyl glycol di (meth) ) Acrylate, polyethylene glycol di (meth) acrylate, hydroxypivalate neopentyl glycol di (meth) acrylate, dicyclopentanyl di (meth) acrylate, caprolactone modified dicyclopentenyl di (meth) acrylate, ethylene oxide modified diphosphate ( (Meth) acrylate, allylated cyclohexyl di (meth) acrylate, isocyanurate di (meth) acrylate, trimethylolpropane tri (meth) acrylate, ethylene oxide modified trimethylo Propane tri (meth) acrylate, dipentaerythritol tri (meth) acrylate, propionic acid modified dipentaerythritol tri (meth) acrylate, pentaerythritol tri (meth) acrylate, propylene oxide modified trimethylolpropane tri (meth) acrylate, tris ( Acryloxyethyl) isocyanurate, propionic acid modified dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, ethylene oxide modified dipentaerythritol hexa (meth) acrylate, caprolactone modified dipentaerythritol hexa (meth) acrylate, etc. Is mentioned. These polyfunctional (meth) acrylates may be used singly or in combination of two or more.

  In the present invention, a monofunctional (meth) acrylate can be used in combination with the polyfunctional (meth) acrylate as long as the object of the present invention is not impaired, for the purpose of lowering the viscosity. Examples of monofunctional (meth) acrylates include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, pentyl (meth) acrylate, hexyl (meth) acrylate, cyclohexyl ( Examples include meth) acrylate, 2-ethylhexyl (meth) acrylate, lauryl (meth) acrylate, stearyl (meth) acrylate, and isobornyl (meth) acrylate. These monofunctional (meth) acrylates may be used alone or in combination of two or more.

  Next, as the polymerizable oligomer, an oligomer having a radical polymerizable unsaturated group in the molecule, for example, epoxy (meth) acrylate, urethane (meth) acrylate, polyester (meth) acrylate, polyether (meth) acrylate The system etc. are mentioned. Here, the epoxy (meth) acrylate oligomer can be obtained, for example, by reacting (meth) acrylic acid with an oxirane ring of a relatively low molecular weight bisphenol type epoxy resin or novolak type epoxy resin and esterifying it. . Further, a carboxyl-modified epoxy (meth) acrylate oligomer obtained by partially modifying this epoxy (meth) acrylate oligomer with a dibasic carboxylic acid anhydride can also be used. The urethane (meth) acrylate oligomer can be obtained, for example, by esterifying, with (meth) acrylic acid, a polyurethane oligomer obtained by a reaction between polyether polyol or polyester polyol and polyisocyanate. Examples of polyester (meth) acrylate oligomers include esterification of hydroxyl groups of polyester oligomers having hydroxyl groups at both ends obtained by condensation of polyvalent carboxylic acids and polyhydric alcohols with (meth) acrylic acid, It can be obtained by esterifying the terminal hydroxyl group of an oligomer obtained by adding an alkylene oxide to a carboxylic acid with (meth) acrylic acid. The polyether (meth) acrylate oligomer can be obtained by esterifying the hydroxyl group of the polyether polyol with (meth) acrylic acid.

  Furthermore, other polymerizable oligomers include polybutadiene (meth) acrylate oligomers with high hydrophobicity that have (meth) acrylate groups in the side chain of polybutadiene oligomers, and silicone (meth) acrylate oligomers that have polysiloxane bonds in the main chain. In a molecule such as an aminoplast resin (meth) acrylate oligomer modified with an aminoplast resin having many reactive groups in a small molecule, or a novolak epoxy resin, bisphenol epoxy resin, aliphatic vinyl ether, aromatic vinyl ether, etc. There are oligomers having a cationic polymerizable functional group.

  Moreover, various additives can be mix | blended with the said thermosetting resin and / or ionizing radiation, or an ultraviolet curable resin composition according to the desired physical property of the obtained cured resin layer. Examples of this additive include a weather resistance improver, an abrasion resistance improver, a polymerization inhibitor, a crosslinking agent, an infrared absorber, an antistatic agent, an adhesion improver, a leveling agent, a thixotropic agent, a coupling agent, A plasticizer, an antifoamer, a filler, a solvent, a coloring agent, etc. are mentioned.

The shape of the raised portion 6 in the present invention is not particularly limited, and may be a regular shape such as a regular arrangement of circles, squares, and hexagons, an irregular pattern, or an irregular pattern. It is preferable because it is excellent in touch, matte, gloss and design.
In addition, by synchronizing the pattern of the raised layer 7 with the colored layer 3, a real feeling of the grain can be obtained.

  Further, as the method of forming the raised layer 7, the raised portion 6 is formed by gravure printing using an irregular pattern plate shape, a lattice, a lattice 1/2 shift, and a turtle shell. The colored solid layer 2, the colored layer 3 and the protective layer 4 may be printed and laminated by a conventional method such as gravure or screen printing.

The decorative sheet 1 of the present invention can be attached to various substrates and used as a decorative board. The board | substrate used as a to-be-adhered body is not specifically limited, A plastic board, a metal board, woody board | plates, such as a timber, a ceramic material, etc. can be selected suitably according to a use. When these substrates, particularly plastic sheets, are used as substrates, a physical or chemical surface treatment such as an oxidation method or a concavo-convex method is applied to one or both sides as desired in order to improve adhesion to the decorative sheet. Can be applied.
Examples of the oxidation method include corona discharge treatment, chromium oxidation treatment, flame treatment, hot air treatment, ozone / ultraviolet treatment method, and examples of the unevenness method include a sand blast method and a solvent treatment method. These surface treatments are appropriately selected depending on the type of substrate, but generally, a corona discharge treatment method is preferably used from the viewpoints of effects and operability.

  As a plastic sheet, what consists of various synthetic resins is mentioned. Synthetic resins include polyethylene resin, polypropylene resin, polymethylpentene resin, polyvinyl chloride resin, polyvinylidene chloride resin, polyvinyl alcohol resin, vinyl chloride-vinyl acetate copolymer resin, ethylene-vinyl acetate copolymer resin, ethylene-vinyl. Representative examples include alcohol copolymer resin, polyethylene terephthalate resin, polybutylene terephthalate resin, polyethylene naphthalate-isophthalate copolymer resin, polymethyl methacrylate resin, polyethyl methacrylate resin, polybutyl acrylate resin, nylon 6 or nylon 66 And polyamide resin, cellulose triacetate resin, cellophane, polystyrene resin, polycarbonate resin, polyarylate resin, polyimide resin, and the like.

As a metal plate, what consists of aluminum, iron, stainless steel, or copper, for example can be used, and what gave these metals by plating etc. can also be used.
Examples of wood-based boards include veneer of various materials such as cedar, firewood, firewood, pine, lawan, teak and melapie, and wood materials such as wood veneer, wood plywood, particle board and medium density fiberboard (MDF). . These can be used alone or in a stacked manner. The wooden board includes not only a wooden board but also a plastic board containing paper powder and reinforced paper having strength.
Examples of the ceramic material include ceramic building materials such as a gypsum plate, a calcium silicate plate, and a wood piece cement plate, ceramics, glass, firewood, fired tiles, plates made mainly of volcanic ash, and the like.
In addition to these, composites of various materials, such as fiber reinforced plastic (FRP) plates, paper honeycombs with iron plates pasted on both sides, and two aluminum plates sandwiched with polyethylene resin can also be used as the base material. .

Further, the substrate may be subjected to a treatment such as forming a primer layer, or a coating for adjusting the color or a pattern from a design viewpoint may be formed in advance. As a substrate to be an adherend, plate materials such as flat plates and curved plates of various materials, or three-dimensional shaped articles (molded products) in which the above materials are used alone or in combination are targeted.
A backing material such as Japanese paper, Western paper, synthetic paper, non-woven fabric, woven fabric, cold paper, impregnated paper, synthetic resin sheet, or the like may be attached to the decorative sheet. By sticking the backing material, it acts to reinforce the decorative sheet itself, prevent cracking and tearing of the decorative sheet, prevent bleeding of the adhesive to the decorative sheet surface, and prevent the occurrence of defective products, Handling becomes easy and productivity can be improved.
Thus, a substrate on which a decorative sheet is placed every leaf or continuously via an adhesive is attached to a cold press, a hot press, a roll press, a laminator, a lapping, an edge pasting machine, a vacuum press, etc. The decorative sheet is bonded to the substrate surface by pressing with an apparatus to obtain a decorative plate.

The adhesive is applied using an application device such as a spray, spreader, or bar coater. As the adhesive, vinyl acetate resin-based, urea resin-based, melamine resin-based, phenol resin-based, isocyanate-based adhesives, etc., are used alone or as a mixed adhesive obtained by arbitrarily mixing them. As needed, talc, calcium carbonate, clay, titanium white and other inorganic powders, wheat flour, wood flour, plastic powder, coloring agents, insect repellents, fungicides and the like can be added and mixed in the adhesive. . In general, the adhesive is applied to the substrate surface with a solid content of 35 to 80% by mass and an application amount of 50 to 300 g / m ² .
Adhesion of the decorative sheet on the substrate is usually performed by forming an adhesive layer on the back surface of the decorative sheet of the present invention and adhering the substrate or applying an adhesive on the substrate and adhering the decorative sheet. Etc.

  The decorative board manufactured as described above can be arbitrarily cut and subjected to optional decoration such as grooving and chamfering on the surface and the end of the cut using a cutting machine such as a router or a cutter. And various uses, for example, interior or exterior materials of buildings such as walls, ceilings, floors, window frames, doors, handrails, skirting boards, surrounding edges, surface decorative panels of fittings such as malls, kitchens, furniture, or light electrical appliances, It can be used for surface decorative boards of cabinets such as OA equipment, interiors and exteriors of vehicles.

EXAMPLES Next, although an Example demonstrates this invention further in detail, it is not limited at all by these.
In the examples and comparative examples, the occupied area of the conduit portion and the upper portion, the touch feeling, the matte feeling, the glossiness, and the design (the unevenness feeling, the fine feeling of rise and the wood grain design feeling (random feeling)) are as follows. Measured.
(1) Measuring method of occupied area of conduit part and top part Olympus Optical Co., Ltd. non-contact surface roughness meter “three-dimensional measuring microscope” STM6ZP (trade name), magnification 50 times, measuring pitch 0.1010 mm, The driving speed was measured under high speed conditions.
(2) Contamination resistance It evaluated based on the JAS special plywood contamination A test.
○: No contamination remains △: Some contamination remains ×: Remarkably contamination remains (3) Marling resistance Steel wool manufactured by Bonstar Sales Co., Ltd. is attached to the end of the weight (300 g / cm ² ), and the sample surface is attached. The appearance after 50 reciprocations was evaluated.
○: No change in appearance Δ: Surface changes in gloss ×: The coating film is scratched (4) Feeling of unevenness The feeling of contact with human hands was evaluated according to the following criteria.
○: Very uneven feeling Δ: Some uneven feeling ×: Almost no uneven feeling

Examples 1-3
As the base material 5, a reinforced paper between building materials with a weight of 30 g / m ² of rice is used, and acrylic resin and nitrified cotton are used as binders on one side, and ink containing titanium white, petal, and chrome lead as colorants is used. A (solid entire surface) layer having a coating amount of 5 g / m ² was applied by gravure printing to obtain a colored solid layer 2. A woodgrain colored layer 3 was formed by gravure printing using an ink containing nitrified cotton as a binder and a colorant mainly composed of a dial.
Next, on these ink layers, urethane resin (“UC” manufactured by Dainippon Ink & Chemicals, Inc.) composed of acrylic polyol and isocyanate is 55% by mass and silica particles having an average particle diameter of about 2 μm are 22.5% by mass. %, A thermosetting resin composition obtained by dissolving or dispersing in ethyl acetate (solvent) was applied by gravure printing at a coating amount of 5 g / m ² to obtain a protective layer 4.
After that, gravure printing was performed using an ink for raising the main component of acrylic resin (manufactured by Dainichi Seika Kogyo Co., Ltd., trade name: KKB Cure U Semi Matte Medium) so as to have the occupied area shown in Table 1. The convex part was formed, and the raised layer 7 consisting of many raised parts 6 was formed, and the decorative sheet 1 was manufactured.
Table 1 shows the results of measuring the occupied area of the raised portion 6 on the protective layer 4 of the decorative sheet 1 obtained. Table 2 shows the results of the evaluations (2) to (4).

Comparative Examples 1-3
In Examples 1 to 3, decorative sheets were produced in the same manner except that the occupied areas shown in Table 1 were obtained.
Table 1 shows the results of measuring the occupied area of the raised portion 6 on the protective layer 4 of the decorative sheet 1 obtained. Table 2 shows the results of the evaluations (2) to (4).

ADVANTAGE OF THE INVENTION According to this invention, the decorative sheet which is excellent in the designability which has scratch resistance, stain resistance, a touch feeling, a mat | matte feeling, glossiness, etc., and was especially excellent in the unevenness | corrugation feeling can be obtained.
In particular, when it is used for a wood grain pattern, it is possible to realistically express the unevenness of the raised portion, and it is possible to obtain the same texture as a material using actual wood. Moreover, it is suitable for the interior of a building, exterior, furniture, surface makeup of joinery, interior of a vehicle, and the like.

It is a schematic diagram which shows the cross section of the decorative sheet of this invention.

Explanation of symbols

1. Cosmetic sheet 2. Colored solid layer 3. Colored layer Protective layer 5. Base material 6. Upper part 7. Top layer

Claims (5)

  A decorative sheet in which at least a colored layer, a protective layer covering the colored layer, and a raised layer formed from a large number of raised portions provided on the protective layer are laminated in this order on a substrate. A decorative sheet having an occupied area in a range of 20 to 50 μm in height of the raised portion with respect to the protective layer is 50% or more.   The decorative sheet according to claim 1, wherein the colored layer is a pattern layer.   The decorative sheet according to claim 2, wherein the pattern layer is a wood grain pattern, and a space between the upper portions is synchronized with a conduit part of the wood grain pattern.   The decorative sheet according to claim 2 or 3, wherein the pattern layer is an abstract pattern.   The decorative sheet according to any one of claims 1 to 4, further comprising a colored solid layer between the substrate and the colored layer.

Images