JP2008081696A - 紫外線硬化型帯電防止性ハードコート樹脂組成物 - Google Patents
紫外線硬化型帯電防止性ハードコート樹脂組成物 Download PDFInfo
- Publication number
- JP2008081696A JP2008081696A JP2006266485A JP2006266485A JP2008081696A JP 2008081696 A JP2008081696 A JP 2008081696A JP 2006266485 A JP2006266485 A JP 2006266485A JP 2006266485 A JP2006266485 A JP 2006266485A JP 2008081696 A JP2008081696 A JP 2008081696A
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- hard coat
- meth
- ultraviolet curable
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】帯電防止性、透明性に優れ、高い硬度を有する紫外線硬化型樹脂組成物の提供。
【解決手段】分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートを反応させた多官能ウレタンアクリレート(A)とガリウムをドーピングした酸化亜鉛微粒子(B)とを含有することを特徴とする紫外線硬化型帯電防止性ハードコート樹脂組成物。
【選択図】なし
【解決手段】分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートを反応させた多官能ウレタンアクリレート(A)とガリウムをドーピングした酸化亜鉛微粒子(B)とを含有することを特徴とする紫外線硬化型帯電防止性ハードコート樹脂組成物。
【選択図】なし
Description
本発明は、プラスチック表面の耐擦傷性、帯電防止性を付与する紫外線硬化型ハードコート樹脂組成物に関する。更に詳しくはポリエステル、アクリル、トリアセチルセルロース、ポリカーボネート等のプラスチック表面に塗布するのに適した、透明で耐擦傷性、耐薬品性及び帯電防止性に優れた紫外線硬化型帯電防止性ハードコート樹脂組成物に関する。
現在、プラスチックは自動車業界、家電業界、電気電子業界を初めとして種々の産業界で大量に使われている。このようにプラスチックが大量に使われている理由は、その加工性、透明性に加えて軽量、安価、光学特性が優れているなどの理由による。しかしながら、ガラスなどに比べて柔らかく、表面に傷が付きやすいなどの欠点を有している。これらの欠点を改良するために、表面にハードコート剤をコーティングする事が一般的な手段として行われている。このハードコート剤には、シリコーン系塗料、アクリル系塗料、メラミン系塗料などの熱硬化型のハードコート剤が用いられている。この中でも特に、シリコーン系ハードコート剤は、ハードネスが高く、品質が優れているため多く用いられている。しかしながら、硬化時間が長く、高価であり、連続的に加工するフィルムに設けられるハードコート層には適しているとは言えない。
近年、感光性のアクリル系ハードコート剤が開発され、利用されるようになった(特許文献1参照)。感光性ハードコート剤は、紫外線などの放射線を照射することにより、直ちに硬化して硬い皮膜を形成するため、加工処理スピードが速く、またハードネス、耐擦傷性などに優れた性能を持ち、トータルコスト的に安価になるため、今やハードコート分野の主流になっている。特に、ポリエステルなどのフィルムの連続加工には適している。プラスチックのフィルムとしては、ポリエステルフィルム、アクリルフィルム、ポリカーボネートフィルム、塩化ビニルフィルム、トリアセチルセルロースフィルム、ポリエーテルスルホンフィルムなどがあるが、ポリエステルフィルムが種々の優れた特性から最も広く使用されている。このポリエステルフィルムは、ガラスの飛散防止フィルム、あるいは、自動車の遮光フィルム、ホワイトボード用表面フィルム、システムキッチン表面防汚フィルム、電子材料的には、CRTフラットテレビ、タッチパネル、液晶ディスプレイ、プラズマディスプレイなどの機能性フィルムとして広く用いられている。これらはいずれもその表面に傷が付かないようにするためにハードコートを塗工している。
また、プラスチックのフィルム以外ではポリカーボネートやアクリル等のシートや基板についてハードコートをされたものが、光ディスクやバックライト周辺の液晶関連部材にも使用されている。
更に近年におけるハードコート剤をコーティングした基材については、耐擦傷性というハードコートとしての性能以外の機能性を求められてきている。例えば、フィルムを設けたCRT、LCD、PDPなどの表示体では、反射により表示体画面が見難くなり、目が疲れやすいと言う問題が生ずるため、用途によっては、表面反射防止能のあるハードコート処理が必要となっている。表面反射防止の方法としては、感光性樹脂中に無機フィラーや有機フィラーを分散させたものをフィルム上にコーティングし、表面に凹凸をつけて反射防止する方法(AG処理)、フィルム上に高屈折率層、低屈折率層の順に多層構造を設け、屈折率の差による光の干渉を利用し映り込み、反射を防止する方法(AR処理)、または上記2つの方法を合わせたAG/AR処理の方法などがある(特許文献2参照)。
また、帯電防止機能を付与したハードコートも開発されており、界面活性剤や導電性の金属酸化物を使用する方法がある(特許文献3参照)。
導電性の金属酸化物としては酸化錫、酸化インジウム、酸化ルテニウム、酸化亜鉛などが使用されているが、特許文献4には酸化亜鉛とガリウムの共沈体が、また、特許文献5にはアルミニウム又はガリウムを添加した酸化亜鉛がそれぞれ記載されている。
さらに特許文献6においては多官能ウレタンアクリレート及び導電性酸化亜鉛を含む紫外線硬化型ハードコート樹脂組成物について、特許文献7においては導電性酸化亜鉛の微粒子が高い透明性を確保すること、紫外線硬化型(メタ)アクリレート及びガリウムをドープした導電性酸化亜鉛を含む導電性樹脂組成物についてそれぞれ言及しているが、多官能ウレタンアクリレート及びガリウムをドープした導電性酸化亜鉛を含む組成物についての実施例はいずれも記載されていない。
機能性を付与したハードコートが求められる中で、特に電気電子材料分野においては、埃、ゴミ等の異物の付きにくい材料が求められている。発生する静電気を除去する目的で、帯電防止剤を添加する方法がある。帯電防止剤としては、カチオン、アニオン、ノニオン系の界面活性剤がしられているが、環境依存性が大きく帯電防止性がばらついたり、比較的効果の高い低分子量のものはブリードしたり、高分子量のものを多量に添加するとハードコート性能が低下してしまうといった問題がある。また、導電性ポリマーも知られているが、構造上、紫外線硬化型樹脂と混合すると性能が低下したり、着色が大きくなったりするといった問題がある。
このような問題がある中で金属酸化物の導電性微粒子をを使用する方法がハードコートへの帯電防止性能付与では主流になりつつある。これらの金属酸化物を使用するとハードコートの特性を保持したまま、永久的な帯電防止性を付与することが可能である。また、金属酸化物を細かくすることにより、曇りの少ない膜が得られる。しかしながら、導電性を有する金属酸化物は着色しているものが多く、導電性を保持するために金属酸化物を多量に添加すると塗膜が着色し、曇りはないが透過率が低下してしまうという欠点もある。透明に近い金属酸化物については、帯電防止性能が十分に得られないといった問題もある。
本発明は、上記の欠点を改善し、帯電防止性能が良好で環境依存性がなく、透明性が高く、高い硬度を有した紫外線硬化型帯電防止性ハードコート樹脂組成物を提供することを目的とする。
本発明者らは前記課題を解決するため、鋭意検討を行った結果、特定の化合物及び組成を有する感光性樹脂組成物が前記課題を解決することを見いだし、本発明に到達した。
即ち、本発明は、
(1)分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートを反応させた多官能ウレタンアクリレート(A)とガリウムをドーピングした酸化亜鉛微粒子(B)とを含有することを特徴とする紫外線硬化型帯電防止性ハードコート樹脂組成物、
(2)多官能ウレタンアクリレート(A)がジペンタエリスリトールペンタアクリレートとヘキサメチレンジイソシアネートとの反応物である前記(1)に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(3)樹脂組成物の固形分含量に対して、ガリウムをドーピングした酸化亜鉛微粒子(B)の含有量が95から10重量%の範囲にある前記(1)に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(4)光重合開始剤(C)を含有することを特徴とする前記(1)ないし(3)のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(5)希釈剤(D)を含有することを特徴とする前記(1)ないし(4)のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(6)前記(1)ないし(5)のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物の硬化層を有するフィルムまたは基材、
に関する。
(1)分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートを反応させた多官能ウレタンアクリレート(A)とガリウムをドーピングした酸化亜鉛微粒子(B)とを含有することを特徴とする紫外線硬化型帯電防止性ハードコート樹脂組成物、
(2)多官能ウレタンアクリレート(A)がジペンタエリスリトールペンタアクリレートとヘキサメチレンジイソシアネートとの反応物である前記(1)に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(3)樹脂組成物の固形分含量に対して、ガリウムをドーピングした酸化亜鉛微粒子(B)の含有量が95から10重量%の範囲にある前記(1)に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(4)光重合開始剤(C)を含有することを特徴とする前記(1)ないし(3)のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(5)希釈剤(D)を含有することを特徴とする前記(1)ないし(4)のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物、
(6)前記(1)ないし(5)のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物の硬化層を有するフィルムまたは基材、
に関する。
本発明により、優れた帯電防止性、耐擦傷性、透明性を有する紫外線硬化型帯電防止性ハードコートをもたらす樹脂組成物を提供することができる。
以下、本発明について詳細に説明する。
多官能ウレタンアクリレート(A)は、分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートとを反応させることにより得られる。
本発明において使用する分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとしては、例えばペンタエリスリトールトリ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールトリ(メタ)アクリレート、ジペンタエリスリトールジ(メタ)アクリレート等のペンタエリスリトール類、トリメチロールプロパンジ(メタ)アクリレート等のメチロール類、ビスフェノールAジエポキシアクリレート等のエポキシアクリレート類を挙げることができる。好ましい例としては、ペンタエリスリトールトリ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレートが挙げられる。これらの(メタ)アクリレートは単独で用いても2種以上混合してもよい。
ポリイソシアネートとしては、鎖状飽和炭化水素、環状飽和炭化水素、芳香族炭化水素で構成されるポリイソシアネートを用いることができる。このようなポリイソシアネートとしては、例えばテトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、2,2,4−トリメチルヘキサメチレンジイソシアネート等の鎖状飽和炭化水素イソシアネート、イソホロンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、メチレンビス(4−シクロヘキシルイソシアネート)、水添ジフェニルメタンジイソシアネート、水添キシレンジイソシアネート、水添トルエンジイソシアネート等の環状飽和炭化水素イソシアネート、2,4−トリレンジイソシアネート、1,3−キシリレンジイソシアネート、p−フェニレンジイソシアネート、3,3’−ジメチルー4,4’−ジイソシアネート、6−イソプロピルー1,3−フェニルジイソシアネート、1,5−ナフタレンジイソシアネート等の芳香族ポリイソシアネートを挙げることができる。好ましい例としては、イソホロンジイソシアネート、ヘキサメチレンジイソシアネートが挙げられる。これらポリイソシアネートは単独で用いても2種以上混合してもよい。
多官能ウレタンアクリレート(A)は、前記の活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートとを反応させることにより得られる。活性水素を有する紫外線硬化型多官能(メタ)アクリレート中の活性水素基1当量に対し、ポリイソシアネートは、イソシアネート基当量として通常0.1〜50の範囲であり、好ましくは、0.1〜10の範囲である。反応温度は、通常30〜150℃、好ましくは、50〜100℃の範囲である。反応の終点は残存イソシアネート量を過剰量のn−ブチルアミンで反応させ、1N塩酸にて逆滴定する方法により算出し、イソシアネートが0.5重量%以下となった時を終了とする。
これら反応時間の短縮を目的として触媒を添加してもよい。この触媒としては、塩基性触媒及び酸性触媒のいずれかが用いられる。塩基性触媒としては、例えばピリジン、ピロール、トリエチルアミン、ジエチルアミン、ジブチルアミン、アンモニアなどのアミン類、トリブチルフォスフィン、トリフェニルフォスフィン等のフォスフィン類を挙げることができる。また、酸性触媒としては、例えばナフテン酸銅、ナフテン酸コバルト、ナフテン酸亜鉛、トリブトキシアルミニウム、トリチタニウムテトラブトキシド、ジルコニウムテトラブトキシド等の金属アルコキシド類、塩化アルミニウム等のルイス酸類、2−エチルヘキサンスズ、オクチルスズトリラウリレート、ジブチルスズジラウリレート、オクチルスズジアセテート等のスズ化合物である。これら触媒の添加量は、ポリイソシアネートを100重量部に対して、通常0.1〜1重量部である。また、必要に応じて、重合禁止剤を添加してもよい。重合禁止剤としては、メトキノン、メチルハイドロキノン、ハイドロキノン等が挙げられる。
本発明の樹脂組成物において、上記(A)成分の使用量は、本発明の樹脂組成物の固形分を100重量%とした場合、通常5〜90重量%であり、好ましくは20〜80重量%である。
本発明の樹脂組成物には必要に応じて(A)成分の他に、(メタ)アクリロイル基を有する紫外線硬化型多官能(メタ)アクリレートを使用することができる。例えばポリエチレングリコールジ(メタ)アクリレート、トリプロピレングリコールジ(メタ)アクリレート、ヒドロキシピバリン酸ネオペンチルグリコールのε−カプロラクトン付加物のジ(メタ)アクリレート(例えば、日本化薬(株)製、KAYARAD HX−220、HX−620など)、ビスフェノールAのEO付加物のジ(メタ)アクリレート、1,4−ブタンジオールジアクリレート、1,6−ヘキサンジオールジアクリレート、1,9−ノナンジオールジアクリレート、、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールプロパンポリエトキシトリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ジトリメチロールプロパンテトラ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、トリペンタエリスリトールオクタ(メタ)アクリレート等のポリエステルアクリレート類、ポリグリシジル化合物(ビスフェノールA型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、トリスフェノールメタン型エポキシ樹脂、ポリエチレングリコールジグリシジルエーテル、グリセリンポリグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテルなど)と(メタ)アクリル酸の反応物であるエポキシ(メタ)アクリレート類、(メタ)アクリレートモノマーとしては、例えばトリシクロデカン(メタ)アクリレート、ジシクロペンタジエンオキシエチル(メタ)アクリレート、ジシクロペンタニル(メタ)アクリレート、イソボニル(メタ)アクリレート、アダマンタン(メタ)アクリレート等の脂環式(メタ)アクリレート類、フェニルグリシジル(メタ)アクリレート、ベンジル(メタ)アクリレート等の芳香環を持つ(メタ)アクリレート類、テトラヒドロフルフリル(メタ)アクリレート、モルフォリン(メタ)アクリレート等の複素環(メタ)アクリレート類、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート等の水酸基を有する(メタ)アクリレート類、エチルカルビトール(メタ)アクリレートなどが挙げられる。これらは、単独または2種以上を混合して使用しても良い。
本発明において使用する、ガリウムをドーピングした酸化亜鉛微粒子(B)は特に限定はないが、有機溶剤に分散させた分散液が好ましい。分散液中の濃度も特に限定されない。ガリウムをドーピングした酸化亜鉛微粒子は導電性、透明性に優れている。ガリウムをドーピングした酸化亜鉛微粒子としては、例えば、ハクスイテック(株)製、パゼットGKシリーズ、パゼットCKシリーズ等が挙げられる。
本発明の樹脂組成物において、上記(B)成分の使用量は、本発明の樹脂組成物の固形分を100重量%とした場合、95〜10重量%であり、好ましくは80〜20重量%である。
上記(B)成分を樹脂中に混合、分散する際に、分散を安定化させるために分散剤を使用しても良い。これに使用しうる分散剤の例としては、カチオン系、アニオン系、ノニオン系あるいは両性界面活性剤等が挙げられる。その添加量は、使用する微粒子(B)100重量部に対して0.5〜30重量部、好ましくは1〜20重量部である。
本発明において使用しうる光重合開始剤(C)としては、例えばベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソブチルエーテルなどのベンゾイン類;アセトフェノン、2,2−ジエトキシ−2−フェニルアセトフェノン、1,1−ジクロロアセトフェノン、2−ヒドロキシ−2−メチル−フェニルプロパン−1−オン、ジエトキシアセトフェノン、1−ヒドロキシシクロヘキシルフェニルケトン、2−メチル−1−〔4−(メチルチオ)フェニル〕−2−モルホリノプロパン−1−オンなどのアセトフェノン類;2−エチルアントラキノン、2−t−ブチルアントラキノン、2−クロロアントラキノン、2−アミルアントラキノンなどのアントラキノン類;2,4−ジエチルチオキサントン、2−イソプロピルチオキサントン、2−クロロチオキサントンなどのチオキサントン類;アセトフェノンジメチルケタール、ベンジルジメチルケタールなどのケタール類;ベンゾフェノン、4−ベンゾイル−4’−メチルジフェニルサルファイド、4,4’−ビスメチルアミノベンゾフェノンなどのベンゾフェノン類;2,4,6−トリメチルベンゾイルジフェニルホスフィンオキサイド、ビス(2,4,6−トリメチルベンゾイル)−フェニルホスフィンオキサイドなどのホスフィンオキサイド類等が挙げられる。また、具体的には、市場より、チバ・スペシャリティケミカルズ社製イルガキュア184(1−ヒドロキシシクロヘキシルフェニルケトン)、イルガキュア907(2−メチル−1−(4−(メチルチオ)フェニル)−2−(4−モルフォリニル)−1−プロパノン)、BASF社製ルシリンTPO(2,4,6−トリメチルベンゾイルジフェニルフォスフィンオキサイド)等を容易に入手出来る。本発明においてはアセトフェノン類が好ましく用いられる。また、これらは、単独又は2種以上を混合して使用しても良い。
本発明の樹脂組成物において、上記(C)成分の使用量は、本発明の樹脂組成物の固形分を100重量%とした場合、0〜10重量%であり、好ましくは1〜7重量%である。
また、本発明の樹脂組成物は硬化促進剤と併用することもできる。併用しうる硬化促進剤としては、例えばトリエタノールアミン、ジエタノールアミン、N−メチルジエタノールアミン、2−メチルアミノエチルベンゾエート、ジメチルアミノアセトフェノン、p−ジメチルアミノ安息香酸イソアミノエステル、EPAなどのアミン類、2−メルカプトベンゾチアゾールなどの水素供与体が挙げられる。これらの硬化促進剤の使用量は、本発明の樹脂組成物の固形分を100重量%とした場合、0〜5重量%である。
本発明において使用しうる希釈剤(D)としては、例えばγ−ブチロラクトン、γ−バレロラクトン、γ−カプロラクトン、γ−ヘプタラクトン、α−アセチル−γ−ブチロラクトン、ε−カプロラクトン等のラクトン類;ジオキサン、1,2−ジメトキシメタン、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールジブチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、トリエチレングリコールジメチルエーテル、トリエチレングリコールジエチルエーテル、テトラエチレングリコールジメチルエーテル、テトラエチレングリコールジエチルエーテル等のエーテル類;エチレンカーボネート、プロピレンカーボネート等のカーボネート類;メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン、アセトフェノン等のケトン類;フェノール、クレゾール、キシレノール等のフェノール類;酢酸エチル、酢酸ブチル、乳酸エチル、エチルセロソルブアセテート、ブチルセロソルブアセテート、カルビトールアセテート、ブチルカルビトールアセテート、プロピレングリコールモノメチルエーテルアセテート等のエステル類;トルエン、キシレン、ジエチルベンゼン、シクロヘキサン等の炭化水素類;トリクロロエタン、テトラクロロエタン、モノクロロベンゼン等のハロゲン化炭化水素類等、石油エーテル、石油ナフサ等の石油系溶剤等の有機溶剤類、2H,3H−テトラフルオロプロパノール等のフッ素系アルコール類、パーフルオロブチルメチルエーテル、パーフルオロブチルエチルエーテル等のハイドロフルオロエーテル類;メチルアルコール、エチルアルコール、イソプロピルアルコール、n−プロピルアルコール等のアルコール類;ケトンとアルコールの両方の性能を兼ね備えたダイアセトンアルコールなどが挙げられる。本発明においてはエーテル類及びアルコール類、又は(B)成分が分散液の場合は使用されている有機溶剤と同一のものが好ましく用いられる。これらは、単独又は2種以上を混合して使用しても良い。
本発明の樹脂組成物において、上記(D)成分の使用量は、本発明の樹脂組成物全体量に対し、0〜80重量%の範囲であり、好ましくは20〜80重量%である。
更に、本発明の樹脂組成物には、必要に応じてレベリング剤、消泡剤、紫外線吸収剤、光安定化剤、酸化防止剤、重合禁止剤などを本発明の感光性樹脂組成物に添加し、それぞれ目的とする機能性を付与することも可能である。レベリング剤としてはフッ素系化合物、シリコーン系化合物、アクリル系化合物等が、紫外線吸収剤としては、ベンゾトリアゾール系化合物、ベンゾフェノン系化合物、トリアジン系化合物等、光安定化剤としてはヒンダードアミン系化合物、ベンゾエート系化合物等、酸化防止剤としてはフェノール系化合物等、重合禁止剤としては、メトキノン、メチルハイドロキノン、ハイドロキノン等が挙げられる。
本発明の樹脂組成物は、上記(A)成分、(B)成分、並びに必要に応じて(C)成分、(D)成分及びその他の成分を任意の順序で混合することにより得ることができる。
こうして得られた本発明の樹脂組成物は、経時的に安定である。
本発明の帯電防止性ハードコートは、上記の紫外線硬化型帯電防止性ハードコート樹脂組成物を基材上に、該樹脂組成物の乾燥後の膜厚が通常0.1〜50μm、好ましくは1〜20μmになるように塗布し、乾燥後紫外線を照射して硬化膜を形成させることにより得ることができる。
基材にフィルムを使用する場合、基材フィルムとしては、例えば、ポリエステル、ポリプロピレン、ポリエチレン、ポリアクリレート、ポリカーボネート、トリアセチルセルロース、ポリエーテルスルホン、シクロオレフィン系ポリマーなどが挙げられる。フィルムはある程度厚いシート状のものであっても良い。使用するフィルムは、柄や易接着層を設けたもの、コロナ処理等の表面処理をしたものであっても良い。
上記の樹脂組成物の塗布方法としては、例えば、バーコーター塗工、メイヤーバー塗工、エアナイフ塗工、グラビア塗工、リバースグラビア塗工、マイクログラビア塗工、マイクロリバースグラビアコーター塗工、ダイコーター塗工、ディップ塗工、スピンコート塗工、スプレー塗工などが挙げられる。
硬化のために紫外線を照射するが、電子線などを使用することもできる。紫外線により硬化させる場合、光源としては、キセノンランプ、高圧水銀灯、メタルハライドランプなどを有する紫外線照射装置が使用され、必要に応じて光量、光源の配置などが調整される。高圧水銀灯を使用する場合、80〜120W/cm2のエネルギーを有するランプ1灯に対して搬送速度5〜60m/分で硬化させるのが好ましい。一方、電子線により硬化させる場合は、光重合開始剤(C)は添加しなくても良く、100〜500eVのエネルギーを有する電子線加速装置を使用するのが好ましい。
以下、本発明を実施例により更に詳細に説明するが、本発明はこれら実施例によって限定されるものではない。また、実施例中、特に断りがない限り、部は重量部を示す。
合成例
乾燥容器中にジペンタエリスリトールペンタアクリレート939.7部、ジブチルスズジラウリレート0.47部、メトキノン0.3部を入れ、80℃まで加熱攪拌した。これにヘキサメチレンジイソシアネート60.3部を1時間かけて滴下し、2時間攪拌後のイソシアネートの割合は0.1%以下であり、反応がほぼ定量的に終了したことを示した。
乾燥容器中にジペンタエリスリトールペンタアクリレート939.7部、ジブチルスズジラウリレート0.47部、メトキノン0.3部を入れ、80℃まで加熱攪拌した。これにヘキサメチレンジイソシアネート60.3部を1時間かけて滴下し、2時間攪拌後のイソシアネートの割合は0.1%以下であり、反応がほぼ定量的に終了したことを示した。
実施例1及び比較例1〜3
表1に示す材料を配合した樹脂組成物を易接着処理済みPETフィルム(125μm)上にバーコーターにて塗布し、約80〜100℃で乾燥後、紫外線照射器により硬化させて膜厚3〜5μmの帯電防止性ハードコートフィルムを得た。尚、表1において単位は「部」を表す。
表1に示す材料を配合した樹脂組成物を易接着処理済みPETフィルム(125μm)上にバーコーターにて塗布し、約80〜100℃で乾燥後、紫外線照射器により硬化させて膜厚3〜5μmの帯電防止性ハードコートフィルムを得た。尚、表1において単位は「部」を表す。
表1
実施例1 比較例1 比較例2 比較例3
合成例の化合物 13.80 6.90
DPHA 13.80 19.00 6.90
Irg.184 0.60 0.60 0.50 0.60
Irg.907 0.60 0.60 0.50 0.60
導電性酸化亜鉛分散液 75.00
酸化亜鉛分散液 60.00
アンチモン酸亜鉛分散液 75.00
IPA 10.00 10.00
PGM 20.00 10.00
合 計 100.00 100.00 100.00 100.00
実施例1 比較例1 比較例2 比較例3
合成例の化合物 13.80 6.90
DPHA 13.80 19.00 6.90
Irg.184 0.60 0.60 0.50 0.60
Irg.907 0.60 0.60 0.50 0.60
導電性酸化亜鉛分散液 75.00
酸化亜鉛分散液 60.00
アンチモン酸亜鉛分散液 75.00
IPA 10.00 10.00
PGM 20.00 10.00
合 計 100.00 100.00 100.00 100.00
(注)
合成例からの化合物:((A)成分)
DPHA:日本化薬(株)製、ジペンタエリスリトールペンタアクリレートとヘキサアクリレートの混合物((A)成分比較例)
Irg.184:チバ・スペシャルティ・ケミカルズ(株)製、1−ヒドロキシシクロヘキシルフェニルケトン((C)成分)
Irg.907:チバ・スペシャルティ・ケミカルズ(株)製、2−メチル−〔4−(メチルチオ)フェニル〕−2−モルホリノ−1−プロパノン((C)成分)
導電性酸化亜鉛分散液:ハクスイテック(株)製ガリウムドープ酸化亜鉛パゼットGK−40、固形分20%、PGM分散品((B)成分)
酸化亜鉛分散液:テイカ(株)製711Z、固形分50%、酸化亜鉛IPA分散液、((B)成分比較例)
アンチモン酸亜鉛分散液:日産化学工業(株)製、固形分20%IPAゾル((B)成分比較例)
IPA:イソプロピルアルコール((D)成分)
PGM:プロピレングリコールモノメチルエーテル((D)成分)
合成例からの化合物:((A)成分)
DPHA:日本化薬(株)製、ジペンタエリスリトールペンタアクリレートとヘキサアクリレートの混合物((A)成分比較例)
Irg.184:チバ・スペシャルティ・ケミカルズ(株)製、1−ヒドロキシシクロヘキシルフェニルケトン((C)成分)
Irg.907:チバ・スペシャルティ・ケミカルズ(株)製、2−メチル−〔4−(メチルチオ)フェニル〕−2−モルホリノ−1−プロパノン((C)成分)
導電性酸化亜鉛分散液:ハクスイテック(株)製ガリウムドープ酸化亜鉛パゼットGK−40、固形分20%、PGM分散品((B)成分)
酸化亜鉛分散液:テイカ(株)製711Z、固形分50%、酸化亜鉛IPA分散液、((B)成分比較例)
アンチモン酸亜鉛分散液:日産化学工業(株)製、固形分20%IPAゾル((B)成分比較例)
IPA:イソプロピルアルコール((D)成分)
PGM:プロピレングリコールモノメチルエーテル((D)成分)
実施例1、比較例1〜3で得られた帯電防止性ハードコートフィルムにつき、下記項目を評価しその結果を表2に示した。
(鉛筆硬度)
JIS K 5400に従い、鉛筆引っかき試験機を用いて、上記組成の塗工フィルムの鉛筆硬度を測定した。詳しくは、測定する硬化皮膜を有するポリエステルフィルム上に、鉛筆を45度の角度で、上から1kgの荷重を掛け5mm程度引っかき、5回中、4回以上傷の付かなかった鉛筆の硬さで表した。
JIS K 5400に従い、鉛筆引っかき試験機を用いて、上記組成の塗工フィルムの鉛筆硬度を測定した。詳しくは、測定する硬化皮膜を有するポリエステルフィルム上に、鉛筆を45度の角度で、上から1kgの荷重を掛け5mm程度引っかき、5回中、4回以上傷の付かなかった鉛筆の硬さで表した。
(全光線透過率)
ヘイズメーター東京電色(株)製、TC−H3DPKを使用し測定した。
ヘイズメーター東京電色(株)製、TC−H3DPKを使用し測定した。
(ヘイズ)
ヘイズメーター東京電色(株)製、TC−H3DPKを使用し測定した。
ヘイズメーター東京電色(株)製、TC−H3DPKを使用し測定した。
(表面抵抗率)
抵抗率計 三菱化学(株)製、HIRESTA IPを使用し測定した。
抵抗率計 三菱化学(株)製、HIRESTA IPを使用し測定した。
表2
鉛筆硬度 全光線透過率 ヘイズ 表面抵抗率
(%) (%) (Ω/□)
実施例1 2H 90.1 0.9 6.9E+09
比較例1 2H 90.1 0.9 OVER
比較例2 H 90.0 0.7 OVER
比較例3 H 86.1 1.1 2.0E+10
鉛筆硬度 全光線透過率 ヘイズ 表面抵抗率
(%) (%) (Ω/□)
実施例1 2H 90.1 0.9 6.9E+09
比較例1 2H 90.1 0.9 OVER
比較例2 H 90.0 0.7 OVER
比較例3 H 86.1 1.1 2.0E+10
実施例1の帯電防止性ハードコートフィルムは、鉛筆硬度、全光線透過率、ヘイズ、表面抵抗率について良好な結果を示した。比較例1は(A)成分を水酸基を持つ多官能アクリレートに変更したが、表面抵抗率が悪い結果となった。また、比較例2は(B)成分を酸化亜鉛とした場合であるが、電導性が悪く、表面抵抗率が出ない結果となった。(B)成分をアンチモン酸亜鉛とした比較例3では、透過率、ヘイズが悪い結果となった。これらのことから、本発明の組成物は多官能ウレタンアクリレートとガリウムをドープした酸化亜鉛との組み合わせにより、優れた帯電防止性、耐擦傷性、透明性を有する紫外線硬化型帯電防止性ハードコートをもたらすことが明らかである。
実施例2及び比較例4
次に、透明性、帯電防止性をより明確に確認するため、(B)成分の添加量をアップして比較を行った。
表3に示す材料を配合した樹脂組成物を日本化薬製ハードコート処理済みPETフィルム(125μm)上にバーコーターにて塗布し、約80〜100℃で乾燥後、紫外線照射器により硬化させて、膜厚0.1μmの帯電防止性ハードコートフィルムを得た。尚、表1において単位は「部」を表す。
次に、透明性、帯電防止性をより明確に確認するため、(B)成分の添加量をアップして比較を行った。
表3に示す材料を配合した樹脂組成物を日本化薬製ハードコート処理済みPETフィルム(125μm)上にバーコーターにて塗布し、約80〜100℃で乾燥後、紫外線照射器により硬化させて、膜厚0.1μmの帯電防止性ハードコートフィルムを得た。尚、表1において単位は「部」を表す。
表3
実施例2 比較例4
合成例からの化合物 2.00 2.00
Irg.184 0.25 0.25
Irg.907 0.25 0.25
導電性酸化亜鉛分散液 37.50
導電性酸化亜鉛分散液(2) 25.00
PGM 30.00 30.00
IPA 30.00 42.50
合 計 100.00 100.00
実施例2 比較例4
合成例からの化合物 2.00 2.00
Irg.184 0.25 0.25
Irg.907 0.25 0.25
導電性酸化亜鉛分散液 37.50
導電性酸化亜鉛分散液(2) 25.00
PGM 30.00 30.00
IPA 30.00 42.50
合 計 100.00 100.00
(注)
導電性酸化亜鉛分散液(2):ハクスイテック(株)製アルミドープ酸化亜鉛パゼットCK−4、固形分30%、PGM分散品((B)成分比較例)
導電性酸化亜鉛分散液(2):ハクスイテック(株)製アルミドープ酸化亜鉛パゼットCK−4、固形分30%、PGM分散品((B)成分比較例)
表4
鉛筆硬度 全光線透過率 ヘイズ 表面抵抗率
(%) (%) (Ω/□)
実施例2 2H 90.3 0.8 1.4E+10
比較例4 2H 90.6 4.1 6.9E+10
鉛筆硬度 全光線透過率 ヘイズ 表面抵抗率
(%) (%) (Ω/□)
実施例2 2H 90.3 0.8 1.4E+10
比較例4 2H 90.6 4.1 6.9E+10
実施例2の帯電防止性ハードコートフィルムは、鉛筆硬度、全光線透過率、ヘイズ、表面抵抗率について非常に良好な結果を示した。比較例4は(B)成分をアルミドープの酸化亜鉛に変更したが、電導性が悪く、表面抵抗率が高くなった。また、ヘイズが劣り、得られた膜が曇ってしまう結果となった。
本発明の樹脂組成物で得られた帯電防止性ハードコートフィルムは、帯電防止性に優れ、透明性が高く、硬度も良好であり、特にプラスチック光学部品、光ディスク、タッチパネル、フラットパネルディスプレイ、携帯電話、フィルム液晶素子など、埃を嫌い、硬度、透明性を必要とする分野に好適なハードコートフィルムである。
Claims (6)
- 分子中に少なくとも2個以上の(メタ)アクリロイル基と活性水素を有する紫外線硬化型多官能(メタ)アクリレートとポリイソシアネートを反応させた多官能ウレタンアクリレート(A)とガリウムをドーピングした酸化亜鉛微粒子(B)とを含有することを特徴とする紫外線硬化型帯電防止性ハードコート樹脂組成物。
- 多官能ウレタンアクリレート(A)がジペンタエリスリトールペンタアクリレートとヘキサメチレンジイソシアネートとの反応物である請求項1に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物。
- 樹脂組成物の固形分含量に対して、ガリウムをドーピングした酸化亜鉛微粒子(B)の含有量が95から10重量%の範囲にある請求項1に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物。
- 光重合開始剤(C)を含有することを特徴とする請求項1ないし請求項3のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物。
- 希釈剤(D)を含有することを特徴とする請求項1ないし請求項4のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物。
- 請求項1ないし請求項5のいずれか一項に記載の紫外線硬化型帯電防止性ハードコート樹脂組成物の硬化層を有するフィルムまたは基材。