JP2007137472A

JP2007137472A - Packaging bag for use in microwave oven

Info

Publication number: JP2007137472A
Application number: JP2005333578A
Authority: JP
Inventors: Katsunobu Ito; 克伸伊藤; Atsuhiko Takeda; 淳彦武田; Kiyoshi Toda; 清志戸田; Yuichi Hirai; 裕一平井; Masanori Takahashi; 正憲高橋
Original assignee: Dai Nippon Printing Co Ltd
Current assignee: Dai Nippon Printing Co Ltd
Priority date: 2005-11-18
Filing date: 2005-11-18
Publication date: 2007-06-07

Abstract

<P>PROBLEM TO BE SOLVED: To provide a packaging bag for use in a microwave oven which is free from any peeling by the pressure or the impact applied during transportation and storage, capable of sealing and packaging a content of a solid, a liquid or a viscous body, having self-standing stability, free from any spill of the content, capable of sanitary and safely heat-cooking, easily taken out of the microwave oven, seal-processable with good productivity, and capable of discharging only steam outside the bag without preventing the liquid or the viscous object forming the content from blown off outside the bag even when the pressure in the bag is higher than required. <P>SOLUTION: In the packaging bag 1 for use in the microwave oven, a U-shaped seal part 9 connected to a peripheral edge seal part is provided on an upper portion of the packaging bag as a means for exhausting steam by the heating in the microwave oven. At least one steam passing port 17 is formed in a non-seal part 19 surrounded by the U-shaped seal part 9, and at least one seal part 16 for forming a passage to control the flow of steam is provided between the steam passing port 17 and an initial peeling end 20 of the U-shaped seal part 9. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、輸送や保管をするときに加わる圧力や衝撃によって剥離することなく、また、電子レンジで加熱するときに内容物を包装して袋を自立させた状態で、破裂を起こさず、自動的に内圧を低下させることができる電子レンジ用包装袋に関するものである。
さらに詳しくは、固体、液体、粘稠体の内容物を密封包装するために用いられ、内容物が袋外に吹き出すことなく、速やかに蒸気のみが排出され、衛生性に優れ、安全に加熱調理でき、生産性良くシール加工でき、店頭での陳列効果にも優れる電子レンジ用包装袋に関するものである。 The present invention does not peel off due to pressure or impact applied during transportation or storage, and does not cause rupture, with the contents wrapped and self-supporting when heated in a microwave oven. In particular, the present invention relates to a packaging bag for a microwave oven that can reduce the internal pressure.
More specifically, it is used for hermetically wrapping the contents of solids, liquids, and viscous bodies, and the steam is quickly discharged without the contents blowing out of the bag. This invention relates to a packaging bag for a microwave oven that can be sealed with high productivity and has an excellent display effect at a store.

近年、電子レンジの普及発展に伴い、また、調理の簡便化の要請から、調理済み加工食
品を、プラスチック製の包装袋等に包装し、密封して、保存性を持たせた形態で流通している。
しかし、こうした食品を電子レンジで加熱する場合において、包装袋が、密封したままであると、加熱により内容物から発生する水蒸気により袋内の内圧が上昇し、ついには破裂し、内容物が電子レンジ庫内に飛散してしまうことが多かった。
このような包装袋の破裂を防止した包装容器として、本出願人は、本件出願に先立ち、図５に示すように、天部シール部、または胴部シール部と連結してコの字状シール部を設け、コの字状シール部に囲まれた未シール部に蒸通口を備えるように構成された自立性のある電子レンジ用包装袋を開示している。（例えば、特許文献１参照）。
特許文献１の電子レンジ用包装袋は、図９に示すように、電子レンジの加熱する際、内圧の上昇によりコの字状シール部９の初期剥離端２０から剥離後退してコの字状シール部９に囲まれた未シール部に達し、未シール部に形成された蒸通口１７から蒸気が排出されるものである。
特開２００５−５９８７２号公報 In recent years, with the widespread development of microwave ovens and in response to the demand for simplified cooking, cooked processed foods are packaged in plastic packaging bags, etc., sealed, and distributed in a form that preserves them. ing.
However, when such foods are heated in a microwave oven, if the packaging bag remains sealed, the internal pressure in the bag increases due to the water vapor generated from the contents by heating, and eventually the contents are ruptured. It was often scattered in the range.
As a packaging container that prevents such a rupture of the packaging bag, the present applicant, prior to the filing of the present application, is connected to the top seal portion or the trunk seal portion as shown in FIG. A self-supporting packaging bag for a microwave oven is disclosed that is provided with a steaming port in an unsealed part surrounded by a U-shaped seal part. (For example, refer to Patent Document 1).
As shown in FIG. 9, the packaging bag for a microwave oven of Patent Document 1 peels back from the initial peeling end 20 of the U-shaped seal portion 9 due to an increase in internal pressure when the microwave oven is heated. The steam reaches the unsealed portion surrounded by the seal portion 9 and the steam is discharged from the steaming port 17 formed in the unsealed portion.
JP 2005-59872 A

しかしながら、従来の包装袋（特許文献１）では、電子レンジで加熱調理する内容物の種類や出力の高い電子レンジを使用することにより、内容物の入った包装袋を電子レンジで加熱する際、包装袋内の圧力が急激に上昇した結果、図１０に示すように、コの字状シール部９の初期剥離端２０から蒸通口１７の近傍まで剥離後退する場合があり、この場合、蒸気の排出される際に、内容物であるカレールーやソース等の液体や粘性体まで袋外に吹き出してしまうという欠点があった。 However, in the conventional packaging bag (Patent Document 1), by using a microwave oven with high output and the kind of contents to be cooked in a microwave oven, when heating a packaging bag containing the contents in a microwave oven, As a result of the rapid increase in the pressure in the packaging bag, as shown in FIG. 10, there is a case where the initial peeling end 20 of the U-shaped seal portion 9 is peeled and retracted from the vicinity of the steaming port 17. When the liquid is discharged, there is a drawback that the contents, such as a liquid such as carreru and sauce, and a viscous body are blown out of the bag.

本発明の目的は、輸送や保管をするときに加わる圧力や衝撃によって剥離することなく、また、内容物を包装し、包装袋を自立させた状態のまま、電子レンジで加熱しても破裂を起こさず、自動的に内圧を低下させることができる電子レンジ用包装袋であって、固体、液体、粘稠体の内容物を密封包装でき、自立安定性もあり、内容物をこぼすことなく、速やかに蒸気が排出され、衛生的で安全に加熱調理でき、電子レンジから取り出しやすく、生産性良くシール加工でき、店頭での陳列効果にも優れる電子レンジ用包装袋を提供することである。
なかんずく、本発明の目的は、袋内の圧力が必要以上に高くなっても、内容物であるカレールーやソース等の液体や粘体まで袋外に吹き出すことなく、蒸気のみを袋外に排出できる電子レンジ用包装袋を提供することである。 The purpose of the present invention is to prevent rupture even when heated in a microwave oven without detachment due to pressure or impact applied during transportation or storage, while packaging the contents and leaving the packaging bag self-supporting. It is a packaging bag for microwave ovens that can automatically reduce the internal pressure without causing it, it can seal and wrap the contents of solid, liquid, viscous material, has self-supporting stability, without spilling the contents, To provide a packaging bag for a microwave oven, in which steam is quickly discharged, can be cooked hygienically and safely, can be easily taken out from a microwave oven, can be sealed with good productivity, and has an excellent display effect at a store.
Among other things, the object of the present invention is to provide an electronic device that can discharge only vapor out of the bag without blowing out the liquid or sticky substance such as carreaux or sauce, even if the pressure in the bag is higher than necessary. It is to provide a packaging bag for a range.

そこで、上記課題を解決すべく、本発明に係る電子レンジ用包装袋では、電子レンジにより加熱するための袋であって、少なくとも片面がシーラント層から構成される積層フィルムを用いて、シーラント面同士を対向させて周縁部をシールして、密封した包装袋において、当該包装袋の上方に、電子レンジの加熱により蒸気抜きするための手段として、周縁シール部と連結してコの字状シール部を設け、当該コの字状シール部に囲まれた未シール部に蒸通口を少なくとも一つ備え、かつ、当該蒸通口と当該コの字状シール部の初期剥離端との間に、蒸気の流れを制御する通路を形成するためのシール部を少なくとも一つ備えていることを特徴とする電子レンジ用包装袋である。 Therefore, in order to solve the above-described problems, the microwave packaging bag according to the present invention is a bag for heating with a microwave oven, and uses a laminated film having at least one surface formed of a sealant layer, and sealant surfaces In the sealed packaging bag with the peripheral part sealed and facing, the U-shaped seal part connected to the peripheral seal part as means for venting steam by heating in the microwave oven above the packaging bag Provided with at least one steaming port in the unsealed part surrounded by the U-shaped seal part, and between the steaming port and the initial peeling end of the U-shaped seal part, A microwave oven packaging bag comprising at least one seal portion for forming a passage for controlling the flow of steam.

また、本発明の電子レンジ用包装袋は、更に上記構成において、前記の袋の中心部を中心とした円を描いたとき、袋の中心から前記のコの字状シール部の最下端内縁に接する円の半径が、胴部シール部内縁に接する円の半径よりも短くなるような位置に設けることを特徴とする電子レンジ用包装袋である。 Further, in the microwave oven packaging bag of the present invention, in the above configuration, when a circle centered on the center portion of the bag is drawn, the center of the bag extends from the bottom end inner edge of the U-shaped seal portion. It is a packaging bag for microwave ovens provided in the position where the radius of the circle which touches becomes shorter than the radius of the circle which touches the inner edge of a body part seal part.

また、本発明の電子レンジ用包装袋は、更に上記いずれかの構成において、前記のコの字状シール部の最下端が、突き出した形状の突端を形成することを特徴とする電子レンジ用包装袋である。 In addition, the microwave packaging bag of the present invention is characterized in that, in any of the above-described configurations, the lowermost end of the U-shaped seal part forms a protruding end with a protruding shape. It is a bag.

また、本発明の電子レンジ用包装袋は、更に上記いずれかの構成において、前記の蒸通口が、包装袋を構成する二枚の部材を貫通して形成されているか、または、包装袋を構成する二枚の部材の内、一方の面のみに形成されていることを特徴とする電子レンジ用包装袋である。 Moreover, the packaging bag for microwave ovens of the present invention may further include any one of the above-described configurations, wherein the steaming port is formed so as to penetrate through two members constituting the packaging bag, or It is a packaging bag for microwave ovens, which is formed only on one side of two members constituting.

また、本発明の電子レンジ用包装袋は、更に上記いずれかの構成において、胴部を構成する四角形からなる前面と後面の底部に、底面を逆Ｖ字状に折り畳んで挿入し、当該前面と当該後面と当該底面の周縁部をそれぞれヒートシールして周縁シール部を形成し、充填した内容物により前記の底部が前後に拡張して自立できる形態の自立性包装袋であることを特徴とする電子レンジ用包装袋である。 Further, the microwave oven packaging bag of the present invention, in any one of the above-mentioned configurations, is inserted into the front surface and the bottom surface of the quadrangle constituting the body portion by folding the bottom surface in an inverted V shape, It is a self-supporting packaging bag in which the peripheral portion of the rear surface and the bottom surface is heat sealed to form a peripheral seal portion, and the bottom portion expands back and forth by the filled contents and can stand on its own. It is a packaging bag for microwave ovens.

本発明の電子レンジ用包装袋においては、固体、液体、粘稠体の内容物を密封包装するために用いられ、内容物がこぼれることなく、安全に加熱調理でき、輸送や保管をするときに加わる圧力や衝撃によって剥離することなく、また、電子レンジで加熱するときに内容物を包装して袋を自立させた状態で破裂を起こさず、コの字状シールの最下部より速やかに蒸気が排出され、自動的に内圧を低下させることができ、自立安定性もあり、容易かつ安全に内容物を移し替えやすく、店頭での陳列効果にも優れ、生産性良くシール加工できるという利点を有する。
更に、内容物を包装袋に充填して密封した包装体を自立させた状態で電子レンジを加熱する際、包装袋の内圧が所定以上となると、袋外に蒸気のみを蒸通口である切込みまたは切欠を介して安全に排出可能であり、更に、蒸通口とコの字状シール部の初期剥離端との間に、蒸気の流れを制御する通路を形成するためのシール部を備えることによって、蒸通口から内容物であるカレールーやソース等の液体、粘体のを吹き出しを防止することができるものである。 In the packaging bag for microwave oven of the present invention, it is used for hermetically wrapping the contents of solids, liquids and viscous bodies, and can be cooked safely without spilling the contents. Steam does not rupture due to applied pressure or impact, and does not rupture when the contents are wrapped and the bag is self-supporting when heated in a microwave oven, and steam is quickly generated from the bottom of the U-shaped seal. It is discharged, can automatically reduce the internal pressure, has self-supporting stability, can easily and safely transfer contents, has an excellent display effect at stores, and has the advantage of being able to seal with good productivity .
Furthermore, when the microwave oven is heated in a state where the package body filled with the packaging bag and sealed is self-supported, when the internal pressure of the packaging bag exceeds a predetermined level, only steam is cut out from the bag as a steaming opening. Or it can be discharged safely through a notch, and further comprises a seal part for forming a passage for controlling the flow of steam between the steam opening and the initial peeling end of the U-shaped seal part. Therefore, it is possible to prevent the contents and liquids such as curry roux and sauce from being discharged from the steaming port.

以下、図面を参照しながら本発明について、実施の形態を詳述する。
図１は、本発明の電子レンジ用包装袋１の実施例を示す斜視図であり、図２は、本発明の電子レンジ用包装袋１を形成する包装材料の積層体１０の断面図であり、図３は、包装袋を形成する包装材料の別態様の積層体１０の断面図である。
図４は、本発明の電子レンジ用包装袋１におけるコの字状シール部９の形成位置の説明
図であり、図５は、蒸気の流れを制御する通路を形成するためのシール部１６の形状を示す図であり、図６は、コの字状シール部９で囲まれる未シール部１９内に形成する切欠１７または切込み１８の形状を示す図であり、図７は、図１のＸ−Ｘ線の断面図であり、図８は、図１の本発明の電子レンジ用包装袋１のコの字状シール部９の剥離開封を説明する模式図であり、図９、図１０は、従来の電子レンジ用包装袋のコの字状シール部９の剥離開封を説明する模式図である。 Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
FIG. 1 is a perspective view showing an embodiment of a microwave packaging bag 1 of the present invention, and FIG. 2 is a cross-sectional view of a laminate 10 of packaging materials forming the microwave packaging bag 1 of the present invention. FIG. 3 is a cross-sectional view of the laminate 10 of another embodiment of the packaging material forming the packaging bag.
FIG. 4 is an explanatory view of the formation position of the U-shaped seal portion 9 in the microwave packaging bag 1 of the present invention, and FIG. 5 shows the seal portion 16 for forming a passage for controlling the flow of steam. FIG. 6 is a diagram showing the shape of the notch 17 or the notch 18 formed in the unsealed portion 19 surrounded by the U-shaped seal portion 9, and FIG. FIG. 8 is a schematic view for explaining peeling and opening of the U-shaped seal portion 9 of the microwave packaging bag 1 of the present invention shown in FIG. 1, and FIG. 9 and FIG. FIG. 5 is a schematic diagram for explaining peeling and opening of a U-shaped seal portion 9 of a conventional microwave packaging bag.

図１は、本発明の電子レンジ用包装袋１の実施例を示す斜視図である。
本発明に係る電子レンジ用包装袋１は、少なくともその内層のシーラント層１３からなる積層体１０を使用し、その内層のシーラント層１３の面を対向させて、それを折り重ねるか、或いはその二枚を重ね合わせ、更にその周辺端部をヒートシールしてシール部を設けて袋体を構成し、更に、コの字状シール部９を胴部シール部６と連結して設け、コの字状シール部９に囲まれた未シール部１９に蒸通口１７を少なくとも一つ設け、蒸通口１７とコの字状シール部９の初期剥離端２０との間に、蒸気の流れを制御する通路を形成するためのシール部１６を少なくとも一つ備える包装袋１である。
なお、本発明にかかる電子レンジ用包装袋１の袋形態は、例えば、側面シール型、二方シール型、三方シール型、四方シール型、封筒貼りシール型、合掌貼りシール型（ピローシール型）、ひだ付シール型、平底シール型、ガセット型、スタンディングパウチ型、その他等のヒートシール形態によりヒートシールして、本発明にかかる種々の形態の包装用袋を製造することができる。
本発明にかかる電子レンジ用包装袋１の一実施例としては、図１に示すように、胴部を構成する四角形からなる前面２と後面３の底部に、底面４を逆Ｖ字状に折り畳んで挿入し、前面２と後面３と底面４の周縁部をそれぞれヒートシールして、胴部シール部５、および、底部シール部６を形成し、内容物を充填後、天部シール部７をヒートシールして密封され、充填した内容物により底面４が前後に拡張して自立できる形態の自立性包装袋である。
本発明にかかる電子レンジ用包装袋１は、自立性包装袋であると、包装袋を自立させたままの状態で、電子レンジで加熱でき、また、電子レンジからも取り出しやすく安全で、内容物が液体状のものであっても、消費者が内容物を取り出しやすいので好ましい袋形態である。
なお、本発明に係る電子レンジ用包装袋１が、自立性袋以外の扁平型包装袋の場合、自立補助手段３０として、外装用包装箱を使用し、これに包装袋を収納して、包装袋の自立を補助させて電子レンジ内での加熱調理を可能とすることができる。 FIG. 1 is a perspective view showing an embodiment of a packaging bag 1 for a microwave oven according to the present invention.
The packaging bag 1 for a microwave oven according to the present invention uses a laminate 10 composed of at least an inner sealant layer 13 and folds the inner sealant layer 13 so that the surfaces of the inner sealant layer 13 face each other. Overlap the sheets, heat seal the peripheral edge part to provide a seal part to constitute a bag body, and further provide a U-shaped seal part 9 connected to the trunk seal part 6, At least one steaming port 17 is provided in the unsealed part 19 surrounded by the ring-shaped seal part 9, and the flow of steam is controlled between the steaming port 17 and the initial peeling end 20 of the U-shaped seal part 9. The packaging bag 1 is provided with at least one seal portion 16 for forming a passage.
The form of the microwave packaging bag 1 according to the present invention includes, for example, a side seal type, a two-side seal type, a three-side seal type, a four-side seal type, an envelope-attached seal type, and a palm-attached seal type (pillow seal type). It is possible to manufacture various types of packaging bags according to the present invention by heat-sealing with a pleated seal type, flat bottom seal type, gusset type, standing pouch type, etc.
As an embodiment of the packaging bag 1 for a microwave oven according to the present invention, as shown in FIG. 1, the bottom surface 4 is folded in an inverted V shape on the bottoms of the front surface 2 and the rear surface 3 that form the body. Then, the peripheral portions of the front surface 2, the rear surface 3 and the bottom surface 4 are heat sealed to form the body seal portion 5 and the bottom seal portion 6, and after filling the contents, the top seal portion 7 is This is a self-supporting packaging bag that is sealed by heat sealing and can be self-supported by expanding the bottom surface 4 back and forth with the filled contents.
When the packaging bag 1 for a microwave oven according to the present invention is a self-supporting packaging bag, it can be heated in a microwave oven while the packaging bag is in a self-supporting state, and can be easily taken out from the microwave oven, and can be safely removed. Even if it is liquid, it is a preferable bag form because it is easy for consumers to take out the contents.
When the microwave packaging bag 1 according to the present invention is a flat packaging bag other than a self-supporting bag, an external packaging box is used as the self-supporting auxiliary means 30, and the packaging bag is stored in the packaging bag. The cooking of the inside of the microwave oven can be made possible by assisting the independence of the bag.

また、上記の自立補助手段３０としては、図１１に示すように、包装袋に形成される蒸通手段を外部に表出する形状からなるスリーブ状の厚紙等を用い、これに収納させた状態で、包装袋の自立補助するさせることができる。
前記のスリーブ状の自立補助手段３０は、正面板と背面板と折り襞状の折り返し部を有するガセット部を形成する底面板とを備え、かつ、前記の正面板と前記の底面板と前記の背面板とが折線を介して順設され、かつ、前記の正面板と前記の底面板とが、その上端部および側端部で一部を互いに連結して構成される。
包装袋に形成される蒸通口１７を外部に表出する形状から構成されることによって、冷凍効率を向上させ、蒸気抜きをする手段および内容物が吹き出すのを防止する手段を包装袋の上方に位置した状態で保持することができるので、内容物が液体であっても、加熱調理の際、包装袋から放出こぼれにくくできる点で好ましい。
なお、上記の自立補助手段３０として用いる外装用包装箱を構成する材料としては、紙、合成紙、紙とプラスチックからなる複合材料等を使用することができる。
図１１に示すように、本発明に係る電子レンジ用包装袋の自立を補助させる手段を用いて起立させる際、折り線を折り曲げ、起立した状態で保持することができる。
また、上記スリーブ状の外装用包装箱以外の自立補助手段３０としては、図示しないが、包装袋を収納箱の上面に開口用ミシン目を有し、側面にこの開口用ミシン目に接続する開口用ミシン目を備え、箱の底面にこの側面の開口用ミシン目に接続する折り線を備えた構成からなる外装用包装箱を使用できる。
上記の自立補助手段３０は、本発明に係る電子レンジ用包装袋を外装用包装箱に収納し、開口用ミシン目を切り離し、開口して、電子レンジ用包装袋の上方を外部に露出させた状態で、包装袋を収納した外装用包装箱の底部から角度をつけて、包装袋を斜めに起立させた状態で保持するものである。
上記の外装用包装箱を使用することによって、蒸通手段を高い位置に保持することができるので、包装袋の蒸通手段から、内容物が漏れるのを防止することができる。 Moreover, as said self-supporting auxiliary means 30, as shown in FIG. 11, the sleeve-shaped cardboard etc. which consist of the shape which exposes the steaming means formed in a packaging bag are used, and it is made to accommodate in this In this way, the packaging bag can be self-supporting.
The sleeve-like self-supporting auxiliary means 30 includes a front plate, a back plate, and a bottom plate that forms a gusset portion having a folded-back shape, and the front plate, the bottom plate, and the bottom plate A back plate is provided in order via a fold line, and the front plate and the bottom plate are configured by partially connecting each other at the upper end and the side end.
By constituting the steam outlet 17 formed in the packaging bag to the outside, it is possible to improve the refrigeration efficiency, and to provide means for venting the steam and preventing the contents from blowing out above the packaging bag. Since it can hold | maintain in the state located in this, even if the content is a liquid, it is preferable at the point which can be hard to discharge | emit from a packaging bag at the time of cooking.
In addition, as a material which comprises the packaging box for exteriors used as said independent support means 30, paper, a synthetic paper, the composite material which consists of paper and a plastics, etc. can be used.
As shown in FIG. 11, when the microwave packaging bag according to the present invention is erected using the means for assisting independence, the fold line can be folded and held in an erected state.
Further, as the self-supporting auxiliary means 30 other than the sleeve-shaped exterior packaging box, although not shown, the packaging bag has an opening perforation on the upper surface of the storage box, and an opening connected to the opening perforation on the side surface. An exterior packaging box having a configuration in which a perforation is provided and a fold line connected to the opening perforation on the side surface is provided on the bottom surface of the box can be used.
The self-supporting auxiliary means 30 stores the microwave packaging bag according to the present invention in the outer packaging box, cuts and opens the perforation for opening, and exposes the upper portion of the microwave packaging bag to the outside. In this state, the packaging bag is held at an angle from the bottom of the exterior packaging box that houses the packaging bag in an inclined state.
By using the outer packaging box, the steaming means can be held at a high position, so that the contents can be prevented from leaking from the steaming means of the packaging bag.

次に、図２は、本発明の電子レンジ用包装袋１を形成する包装材料の積層体１０の断面図である。
図２に示すように、本発明の電子レンジ用包装袋を形成する積層体１０は、基材層１１と、シーラント層１３とを接着層１２を介して順次に積層するものである。
なお、接着層１３は、必須の層ではなく、適宜必要に応じて設けられる層である。
また、図３に示すように、必要に応じて、基材層１１とシーラント層１３との層間に中間層１４、印刷層１５を設けてもよい。 Next, FIG. 2 is a cross-sectional view of a laminated body 10 of packaging materials forming the microwave packaging bag 1 of the present invention.
As shown in FIG. 2, the laminate 10 forming the microwave packaging bag of the present invention is a laminate in which a base material layer 11 and a sealant layer 13 are sequentially laminated via an adhesive layer 12.
Note that the adhesive layer 13 is not an essential layer, but is a layer provided as necessary.
In addition, as shown in FIG. 3, an intermediate layer 14 and a printing layer 15 may be provided between the base material layer 11 and the sealant layer 13 as necessary.

本発明にかかる電子レンジ用包装袋１において、図１に示すコの字状シール部９は、周縁にシール部を形成する際、胴部シール部５と一体でシール加工することができるので、生産性良くシール加工できるものである。
これに対し、前記のコの字状シール部９が、胴部シール部５と連結されず、独立して形成されていると、電子レンジの加熱により発生する蒸気の圧力が、前記の胴部シール部５や天部シール部７と独立して形成された独立シール部との間を通ってしまうため、効率的に独立シール部に圧力がかかりにくくなり、自動開封がスムーズに起らなくなるという理由で好ましくない。更に、内容物を充填する際または流通の過程において独立シール部と胴部シール部５や天部シール部７との間に内容物が入り込み、外観不良が生ずるため好ましくない。更に、独立シール部と胴部シール部５や天部シール部７の周縁シール部とを二工程でシール加工するため、シール加工の生産性に劣るので好ましくないものである。 In the microwave packaging bag 1 according to the present invention, the U-shaped seal portion 9 shown in FIG. 1 can be integrally sealed with the body seal portion 5 when the seal portion is formed on the periphery. It can be sealed with high productivity.
On the other hand, when the U-shaped seal portion 9 is not connected to the body seal portion 5 and is formed independently, the pressure of the steam generated by heating of the microwave oven is reduced. Since it passes between the seal part 5 and the independent seal part formed independently of the top seal part 7, it is difficult to apply pressure to the independent seal part efficiently, and automatic opening does not occur smoothly. It is not preferable for the reason. Furthermore, when the contents are filled or in the course of distribution, the contents enter between the independent seal portion and the body seal portion 5 or the top seal portion 7 to cause an appearance defect. Further, since the independent seal portion and the peripheral seal portion of the body seal portion 5 and the top seal portion 7 are sealed in two steps, the productivity of the seal processing is inferior, which is not preferable.

次に、本発明にかかる電子レンジ用包装袋１において、コの字状シール部９を形成する位置は、図４に示すように、包装袋の中心部を中心とした円を描いたとき、包装袋１の中心からコの字状シール部９の最下端に接する円の半径ｒ３が胴部シール部５の内縁に接する円の半径ｒ１や天部シール部７の内縁に接する円の半径ｒ２よりも短くなるような位置に設けることが必要である。
これに対し、半径ｒ３が、半径ｒ１や半径ｒ２よりも長いと、電子レンジの加熱による内圧の上昇で、包装袋の周縁シール部である胴部シール部５や天部シール部７に内圧がかかり、その結果、胴部シール部５や天部シール部７において剥離後退することとなり、包装袋の破袋により内容物が漏れる場合があるため好ましくない。 Next, in the microwave packaging bag 1 according to the present invention, the position where the U-shaped seal portion 9 is formed, as shown in FIG. 4, when a circle centered on the center of the packaging bag is drawn, The radius r3 of the circle that is in contact with the lowermost end of the U-shaped seal portion 9 from the center of the packaging bag 1 is the radius r1 of the circle that is in contact with the inner edge of the body seal portion 5 or the radius r2 of the circle that is in contact with the inner edge of the top seal portion 7. It is necessary to provide it at a position that is shorter than that.
On the other hand, if the radius r3 is longer than the radius r1 or the radius r2, the internal pressure rises due to heating of the microwave oven, so that the internal pressure is applied to the body seal portion 5 and the top seal portion 7 which are the peripheral seal portions of the packaging bag. As a result, the body seal part 5 and the top seal part 7 are peeled and retracted, and the contents may leak due to the broken bag of the packaging bag.

次に、本発明にかかる電子レンジ用包装袋１において、コの字状シール部９の形状は、図１に示すように、コの字状シール部の初期剥離端２０の形状としては、シール部の最下端を突き出した形状とすることが好ましい。
初期剥離端２０を上記のような形状にすれば、コの字状に限定されず、図示しないが、台形状や三角形状であってもよい。
このことによって、加熱による内圧が、突端に集中してかかりやすくなり、突端２０を起点にして確実かつスムーズにシール部の剥離後退が進むため、好ましいものである。
これに対して、コの字状シール部９の形状が、角がなく円形状や半円状であると、加熱により発生する内圧が分散されてしまい、シール部の剥離後退に圧力がより多く必要となるため、スムーズに剥離しにくく、コの字状シール部９以外の部分にもより大きな圧力がかかってしまうため好ましくない。
コの字状シール部９のシール幅としては、２ｍｍ〜５ｍｍ程度が、加熱による内圧でスムーズにシール剥離できるため好ましいものである。
これに対して、コの字状シール部９のシール幅が２ｍｍ未満であると、シール強度が不安定となるので好ましくなく、５ｍｍを超えると、加熱による内圧でスムーズにシール剥離しにくくなるので好ましくない。
また、本発明の電子レンジ用包装袋１において、周縁シール部、すなわち、胴部シール部５、底部シール部６および天部シール部７のシール幅としては、５ｍｍ〜２０ｍｍ程度であると、輸送や保管をするときに加わる圧力や衝撃によって破袋することがないため好ましいものである。 Next, in the packaging bag 1 for microwave ovens according to the present invention, the shape of the U-shaped seal portion 9 is, as shown in FIG. 1, as the shape of the initial peeling end 20 of the U-shaped seal portion. It is preferable to make it the shape which protruded the lowest end of the part.
If the initial peeling end 20 has a shape as described above, the shape is not limited to a U shape, and although not illustrated, a trapezoidal shape or a triangular shape may be used.
This is preferable because the internal pressure due to heating is likely to be concentrated on the tip, and the peeling and retreat of the seal portion proceeds reliably and smoothly starting from the tip 20.
On the other hand, if the U-shaped seal portion 9 is circular or semicircular with no corners, the internal pressure generated by heating is dispersed, resulting in more pressure in the separation and retraction of the seal portion. This is not preferable because it is difficult to peel off smoothly and a larger pressure is applied to portions other than the U-shaped seal portion 9.
The seal width of the U-shaped seal portion 9 is preferably about 2 mm to 5 mm because the seal can be smoothly peeled off by internal pressure due to heating.
On the other hand, if the seal width of the U-shaped seal portion 9 is less than 2 mm, the seal strength becomes unstable, which is not preferable. If it exceeds 5 mm, it becomes difficult to peel off the seal smoothly due to internal pressure due to heating. It is not preferable.
Further, in the microwave packaging bag 1 of the present invention, the peripheral seal portion, that is, the seal width of the body seal portion 5, the bottom seal portion 6 and the top seal portion 7 is about 5 mm to 20 mm. It is preferable because it is not broken by pressure or impact applied during storage.

また、本発明にかかる電子レンジ用包装袋１において、コの字状シール部９で囲まれる未シール部１９を形成することによって、未シール部１９内に形成する蒸通口１７、１８の形成する位置がずれても、シールが剥離後退する距離が一定であり、剥離が未シール部１９内に到達した時点で、未シール部１９内に形成する蒸通口１７、１８を一気に広く開口できるため、電子レンジで加熱する場合、確実かつ安定で速やかな蒸気抜きを行うことができるという利点を有する。
これに対して、コの字状シール部９で囲まれる未シール部１９を形成せず、ベタシールのみであると、蒸通口１７、１８の形成する位置がずれた場合にシール剥離後退の距離が変わってしまい、その結果、常に安定したシール剥離をしないため好ましくないものである。
なお、この蒸通口１７、１８は、コの字状シール部９と胴部シール部５に囲まれた内側にあるので流通段階では完全に密封性を保つことができ、衛生的である。 In addition, in the microwave packaging bag 1 according to the present invention, by forming the unsealed portion 19 surrounded by the U-shaped seal portion 9, formation of the steam ports 17 and 18 formed in the unsealed portion 19. Even if the position to be shifted is shifted, the distance at which the seal peels and retreats is constant, and when the peeling reaches the inside of the unsealed portion 19, the steam openings 17 and 18 formed in the unsealed portion 19 can be opened widely at once. Therefore, when heating in a microwave oven, there is an advantage that steam can be reliably, stably and promptly vented.
On the other hand, if the unsealed portion 19 surrounded by the U-shaped seal portion 9 is not formed and only the solid seal is formed, the distance of the seal peeling and retreating when the position where the steaming ports 17 and 18 are formed is shifted. As a result, it is not preferable because stable seal peeling is not always performed.
The steam openings 17 and 18 are inside surrounded by the U-shaped seal portion 9 and the body seal portion 5, so that the sealing performance can be completely maintained at the distribution stage, which is hygienic.

次に、本発明にかかる電子レンジ用包装袋１において、コの字状シール部９内の未シール部１９には、蒸通口として、切欠１７または切込み１８を形成することが必要である。
蒸通口を形成することによって、電子レンジの加熱による内圧の上昇で、コの字状シール部９の最下端から剥離後退し、未シール部１９に到達し、未シール部１９に形成された蒸通口を通って、袋内に充満した蒸気を袋外へ放散し、袋の内圧を低下でき、破裂を回避することができる。
更に、蒸通口１７、１８とコの字状シール部の初期剥離端２０との間にコの字状シール部９と一体形成されたシール部１６を少なくとも一つ備えることによって、電子レンジの加熱による内圧の上昇で、コの字状シール部９の初期剥離端２０から剥離後退し、未シール部１９に到達し、未シール部１９内のシール部１６により形成された曲がりくねった通路を通って蒸通口１７、１８から蒸気を袋外へ放散することができるので、蒸気の量が一定に保たれた状態で袋外へ放散されるされるため、穏やかに蒸気が放出されるため、内容物であるカレールーやソース等の液体や粘性体まで袋外に吹き出すことを回避することができる。
次に、コの字状シール部９で囲まれる未シール部１９内に形成する蒸通口の形状は、特に限定されず、例えば、図６に示すように、十字形、Ｉ字形、Ｕ字形等の切込み１８や、円形、三角形、四角形等の切欠１７を形成することができる。
上記の切欠１７または切込み１８の個数は、一個に限定されず、複数個であっても構わない。
また、蒸通口である切欠１７または切込み１８は、図７に示すように、対向させた胴部を構成する２枚の部材に貫通するように設けても、片面だけに設けてもよい。
切欠１７または切込み１８は、レーザー加工や打ち抜き等で形成することができる。 Next, in the microwave packaging bag 1 according to the present invention, the unsealed portion 19 in the U-shaped seal portion 9 needs to be formed with a notch 17 or a notch 18 as a steaming opening.
By forming the steaming opening, the internal pressure rises due to the heating of the microwave oven, and peels and retreats from the lowermost end of the U-shaped seal portion 9, reaches the unsealed portion 19, and is formed in the unsealed portion 19. The vapor filled in the bag is diffused to the outside of the bag through the steaming port, the internal pressure of the bag can be reduced, and rupture can be avoided.
Further, by providing at least one seal portion 16 integrally formed with the U-shaped seal portion 9 between the steam openings 17 and 18 and the initial peeling end 20 of the U-shaped seal portion, As the internal pressure increases due to heating, the U-shaped seal portion 9 peels back from the initial peeling end 20, reaches the unsealed portion 19, and passes through a tortuous path formed by the seal portion 16 in the unsealed portion 19. Since the steam can be dissipated out of the bag through the steaming ports 17 and 18, since the steam is dissipated out of the bag in a state where the amount of steam is kept constant, the steam is gently released, It is possible to avoid blowing out liquids and viscous bodies such as curry roux and sauce which are the contents out of the bag.
Next, the shape of the steaming opening formed in the unsealed portion 19 surrounded by the U-shaped seal portion 9 is not particularly limited. For example, as shown in FIG. 6, a cross shape, an I shape, a U shape A cut 18 such as a circle, a triangle, a quadrangle, or the like can be formed.
The number of the notches 17 or the notches 18 is not limited to one and may be plural.
Moreover, as shown in FIG. 7, the notch 17 or the notch 18 which is a steaming opening may be provided so that it may penetrate to the two members which comprise the opposing trunk | drum, or may be provided only on one side.
The notch 17 or the notch 18 can be formed by laser processing or punching.

また、本発明にかかる電子レンジ用包装袋１において、本発明における蒸通口である切欠１７の孔の直径は、４ｍｍφ〜８ｍｍφの範囲にあることが、電子レンジで加熱による内圧の上昇し、加熱調理によって電子レンジ用袋体内部の圧力が所定以上になると、電子レンジ用包装袋１の蒸通口から速やかに蒸気が抜けると共に、内容物が袋外に吹き出すのを防止することができるので好ましい。
これに対して、コの字状シール部９の孔の大きさが、孔の直径：４ｍｍφ未満であると、内容物が袋外から吹き出す場合があるので好ましくなく、孔の直径：８ｍｍφを超えると、加熱による内圧でスムーズに蒸気が抜けにくくなるので好ましくない。 In addition, in the microwave packaging bag 1 according to the present invention, the diameter of the hole of the notch 17 serving as a steaming opening in the present invention is in the range of 4 mmφ to 8 mmφ, and the internal pressure increases due to heating in the microwave oven, When the pressure inside the microwave oven bag body becomes equal to or higher than a predetermined temperature by cooking, the steam can be quickly removed from the steaming opening of the microwave oven packaging bag 1 and the contents can be prevented from being blown out of the bag. preferable.
On the other hand, if the size of the hole of the U-shaped seal portion 9 is less than the diameter of the hole: 4 mmφ, the contents may be blown out of the bag, which is not preferable, and the diameter of the hole exceeds 8 mmφ. Then, it is not preferable because the internal pressure due to heating makes it difficult for the steam to escape smoothly.

図５は、蒸気の流れを制御する通路を形成するためのシール部１６の形状を示す図である。
本発明にかかる電子レンジ用包装袋１において、蒸通口１７、１８とコの字状シール部９の初期剥離端２０との間に、蒸気の流れを制御する通路を形成するためのシール部１６を設けることが必要である。
図５に示すように、シール部１６は、蒸気の流れを制御する通路を形成できれば、図５（ａ）に示すように、コの字状シール部９や胴部シール部５と独立に形成しても構わないが、独立して形成されるより、図５（ｂ）に示すように、コの字状シール部９または胴部シール部５と一体で形成されている方が、内容物が蒸通口１７、１８を介して袋外に吹き出すのをより防止しやすくし、また、コの字状シール部９または胴部シール部５と一工程でシール加工可能であるため、シール加工の生産性に優れる点でもより好ましい。
更に、蒸気の流れを制御する通路を形成するためのシール部１６の形状は、図５（ｃ）に示すように、蒸通口１７、１８とコの字状シール部９の初期剥離端２０との間に、胴部シール部と平行に形成しても良い。
また、蒸気の流れを制御する通路を形成するためのシール部１６の形状は、特に限定されず、例えば、直線状の棒状シール、あるいは、曲線状の弓形シール、半円状、楕円状としてもよい。
また、シール部１６の張り出す方向は、特に限定されず、蒸通口１７、１８とコの字状シール部９の初期剥離端２０との間に形成されればよく、例えば、水平方向、上斜め方向、あるいは下斜め方向とするシール形状としてもよい。
更に、シール部１６とコの字状シール部９とのシール間の距離は、１．５ｍｍ〜１０ｍｍ程度であることによって、必要以上の圧がかっても、内容物が袋外に吹き出すのを留めると共に、蒸気のみ通路を通って袋外にスムーズに放出することができるので好ましい。
上記のシール間の距離が１．５ｍｍ未満であると、蒸気の通路が狭くなり、スムーズに内圧が袋外に排出できず、袋が膨らみ、消費者に恐怖感を与える場合があり、好ましくない。
上記のシール間の距離が１０ｍｍを超えると、必要以上に内圧がかかると、粒状固体、液体、あるいは粘体からなる内容物を、胴部シール部５から張り出したシール部１６の下方に留めておくことができず、また、必要以上にコの字シール部が剥離後退してしまい、蒸通口を通して、内容物が袋外に容易に吹き出してしまうので好ましくない。 FIG. 5 is a diagram showing the shape of the seal portion 16 for forming a passage for controlling the flow of steam.
In the microwave oven packaging bag 1 according to the present invention, a seal portion for forming a passage for controlling the flow of steam between the steam openings 17 and 18 and the initial peeling end 20 of the U-shaped seal portion 9. 16 is required.
As shown in FIG. 5, the seal portion 16 is formed independently of the U-shaped seal portion 9 and the trunk portion seal portion 5 as shown in FIG. 5 (a) if a passage for controlling the flow of steam can be formed. However, as shown in FIG. 5 (b), the contents formed integrally with the U-shaped seal portion 9 or the trunk portion seal portion 5 are better than the case where they are formed independently. Can be more easily prevented from being blown out of the bag through the steaming ports 17 and 18, and can be sealed with the U-shaped seal portion 9 or the trunk seal portion 5 in one step. It is more preferable also from the point which is excellent in productivity.
Further, as shown in FIG. 5C, the shape of the seal portion 16 for forming a passage for controlling the flow of steam is such that the steam inlets 17 and 18 and the initial peeling end 20 of the U-shaped seal portion 9 are formed. In between, it may be formed in parallel with the body seal part.
Further, the shape of the seal portion 16 for forming the passage for controlling the flow of the steam is not particularly limited. For example, the seal portion 16 may be a linear rod-shaped seal, a curved arc-shaped seal, a semicircular shape, or an elliptical shape. Good.
Further, the direction in which the seal portion 16 projects is not particularly limited, and may be formed between the steaming openings 17 and 18 and the initial peeling end 20 of the U-shaped seal portion 9, for example, in the horizontal direction, It is good also as a seal shape made into an upper diagonal direction or a lower diagonal direction.
Furthermore, the distance between the seals of the seal part 16 and the U-shaped seal part 9 is about 1.5 mm to 10 mm, so that the contents are not blown out of the bag even if pressure more than necessary is applied. At the same time, it is preferable because only steam can be smoothly discharged outside the bag through the passage.
If the distance between the above seals is less than 1.5 mm, the steam passage becomes narrow, the internal pressure cannot be smoothly discharged outside the bag, the bag swells, and may cause fear to the consumer. .
When the distance between the above seals exceeds 10 mm, when an internal pressure is applied more than necessary, the contents made up of granular solid, liquid, or viscous material are kept below the seal part 16 protruding from the body seal part 5. In addition, the U-shaped seal part peels and retracts more than necessary, and the contents easily blow out of the bag through the steaming port.

図８は、図１の本発明の電子レンジ用包装袋１のコの字状シール部９の剥離開封を説明する模式図である。
図８に示すように、蒸通口１７、１８からコの字状シール部９の未シール部初期到達点までの長さｇが、１０ｍｍ以上、２５ｍｍ以下であることによって、電子レンジの加熱条件が通常より内圧がかかり、コの字シール部の突端部２０から剥離後退しても、蒸通口から袋外にカレールーやソース等の液体、粘体からなる内容物が吹き出すことを防止すると共に、蒸気のみを蒸通口を介して安全に排出することができる。 FIG. 8 is a schematic view for explaining peeling and opening of the U-shaped seal portion 9 of the microwave packaging bag 1 of the present invention shown in FIG.
As shown in FIG. 8, when the length g from the steam inlets 17 and 18 to the initial arrival point of the unsealed portion of the U-shaped seal portion 9 is 10 mm or more and 25 mm or less, the heating condition of the microwave oven However, even if the internal pressure is applied more than usual, even when peeling and retreating from the protruding end 20 of the U-shaped seal part, it prevents liquids such as carrail and sauce from being out of the bag from the steaming port, and the contents consisting of viscous bodies are blown out, Only steam can be safely discharged through the vent.

また、本発明にかかる電子レンジ用包装袋１は、自立性の包装形態であるため、包装袋を自立させたままの状態で、電子レンジで加熱でき、また、電子レンジからも取り出しやすく安全で、内容物が液体状のものであっても、消費者が内容物を取り出しやすい。 Moreover, since the packaging bag 1 for microwave ovens concerning this invention is a self-supporting packaging form, it can be heated with a microwave oven in the state which left the packaging bag self-supporting, and it is easy to take out from a microwave oven, and is safe. Even if the contents are liquid, it is easy for consumers to take out the contents.

次に、本発明の電子レンジ用包装袋１を形成する積層体１０の構成材料について説明す
る。
まず、基材層１１としては、耐熱性を有し、一般に電子レンジで加熱または加熱調理される食品用包材として使用されているものならば、特に限定されない。
例えば、延伸ポリエチレンテレフタレートフィルム、シリカ蒸着延伸ポリエチレンテレフタレートフィルム、アルミナ蒸着延伸ポリエチレンテレフタレートフィルム、延伸ナイロンフィルム、シリカ蒸着延伸ナイロンフィルム、アルミナ蒸着延伸ナイロンフィルム、延伸ポリプロピレンフィルム、ポリビニルアルコールコート延伸ポリプロピレンフィルム、ナイロン６／メタキシリレンジアミンナイロン６共押共延伸フィルムまたはポリプロピレン／エチレンービニルアルコール共重合体共押共延伸フィルム等のいずれか、またはこれらの２以上のフィルムを積層した複合フィルムであってもよい。
これらの基材層は単層でも多層（積層）でもよく、融点、１５０℃ 以上の耐熱性を有し、厚みは１０μｍ〜５０μｍ、好ましくは１０μｍ〜３０μｍ程度が好ましい。 Next, the constituent material of the laminated body 10 which forms the packaging bag 1 for microwave ovens of this invention is demonstrated.
First, the base material layer 11 is not particularly limited as long as it has heat resistance and is generally used as a packaging material for food that is heated or cooked in a microwave oven.
For example, stretched polyethylene terephthalate film, silica-deposited stretched polyethylene terephthalate film, alumina-deposited stretched polyethylene terephthalate film, stretched nylon film, silica-deposited stretched nylon film, alumina-deposited stretched nylon film, stretched polypropylene film, polyvinyl alcohol-coated stretched polypropylene film, nylon 6 / Metaxylylenediamine nylon 6 co-extrusion co-stretched film or polypropylene / ethylene-vinyl alcohol copolymer co-extrusion co-stretched film or the like, or a composite film obtained by laminating two or more of these films may be used.
These substrate layers may be single layers or multilayers (laminates), have a melting point and heat resistance of 150 ° C. or higher, and have a thickness of about 10 μm to 50 μm, preferably about 10 μm to 30 μm.

本発明におけるシーラント層１３を構成する樹脂は、熱接着性樹脂層で、一般に電子レンジで加熱または加熱調理される食品用包材として使用されるものであれば、特に限定されない。
例えば、低密度ポリエチレン、直鎖状低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、ポリプロピレン、プロピレン−エチレン共重合体、エチレン−酢酸ビニル共重合体、エチレンーアクリル酸共重合体、エチレン−メタクリル酸共重合体、エチレン−メチルアクリレート共重合体、エチレン−エチルアクリレート共重合体、エチレン−メチルメタクリレート共重合体またはアイオノマー等樹脂を使用できる。
シーラント層はこれらの樹脂を押出ラミネート法により形成しても良いし、予め、Ｔダイ法またはインフレーション法等により製膜したフィルムとして、耐熱性基材層とドライラミネートあるいは押出ラミネート法等により積層しても良い。
シーラント層の厚さは、２０μｍ〜１００μｍ程度が好ましく、４０μｍ〜７０μｍが
より好ましい。
前記のシーラント層１５間のシール強度は、９０℃以上の温度で５Ｎ／１５ｍｍ巾〜２５Ｎ／１５ｍｍ巾であることが好ましく、１０Ｎ／１５ｍｍ巾〜１５Ｎ／１５ｍｍ巾であることがより好ましい。
前記のシール強度が９０℃ 以上の温度で２５Ｎ／１５ｍｍ巾を超えると、シール後退がスムースに起きず、自動開封が速やかで確実に達成されない恐れがあり、破袋する場合もあるので好ましくない。
シール後退の状態は特に規定されないが凝集破壊が好ましい。
また、コの字状シール部９と周縁シール部、すなわち胴部シール部５、底部シール部６および天部シール部７とのシール強度に差をつけてもよいが、本発明において、その必然性はなく、同等の強度を有していても、以上に説明した形状により自動開放は達成される。
また、常温で、２３Ｎ／１５ｍｍ以上のシール強度を有していることが、輸送や保管をするときに加わる圧力や衝撃によって剥離することなく使用できるため好ましい。
前記のシーラント層１３において、とりわけ、低温時（０℃）および常温時（２５℃）において十分なシール強度があり、電子レンジ加熱時（９０℃以上）にシール強度が低く、速やかに剥離する性質を有する熱接着性樹脂層として、プロピレン−エチレンブロック共重合体樹脂を主成分とする樹脂組成物からなるものを使用することが好ましい。 The resin constituting the sealant layer 13 in the present invention is not particularly limited as long as it is a heat-adhesive resin layer and is generally used as a food packaging material heated or cooked in a microwave oven.
For example, low density polyethylene, linear low density polyethylene, medium density polyethylene, high density polyethylene, polypropylene, propylene-ethylene copolymer, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-methacrylic acid A resin such as a copolymer, an ethylene-methyl acrylate copolymer, an ethylene-ethyl acrylate copolymer, an ethylene-methyl methacrylate copolymer, or an ionomer can be used.
The sealant layer may be formed by extrusion lamination of these resins, or laminated in advance by a heat resistant substrate layer and dry lamination or extrusion lamination as a film formed by T-die method or inflation method. May be.
The thickness of the sealant layer is preferably about 20 μm to 100 μm, and more preferably 40 μm to 70 μm.
The seal strength between the sealant layers 15 is preferably 5 N / 15 mm width to 25 N / 15 mm width at a temperature of 90 ° C. or more, and more preferably 10 N / 15 mm width to 15 N / 15 mm width.
If the seal strength exceeds 25 N / 15 mm width at a temperature of 90 ° C. or higher, the seal retraction does not occur smoothly, automatic opening may not be achieved quickly and reliably, and the bag may be broken.
The state of seal retraction is not particularly defined, but cohesive failure is preferred.
Further, the seal strength between the U-shaped seal portion 9 and the peripheral seal portion, that is, the body seal portion 5, the bottom seal portion 6 and the top seal portion 7 may be different. However, even if they have the same strength, automatic opening is achieved by the shape described above.
Moreover, it is preferable that it has a seal strength of 23 N / 15 mm or more at normal temperature because it can be used without being peeled off by pressure or impact applied during transportation or storage.
The sealant layer 13 has a sufficient sealing strength especially at low temperatures (0 ° C.) and normal temperatures (25 ° C.), and has low sealing strength when heated in a microwave oven (90 ° C. or higher), and can be peeled off quickly. It is preferable to use a heat-adhesive resin layer comprising a resin composition containing a propylene-ethylene block copolymer resin as a main component.

次に、基材層１１とシーラント層１３との積層は共押出ラミネート法、ドライラミネート法等の方法であれば特に限定されない。
接着層１２は、ラミネートによる接着剤、あるいは、接着樹脂層である。
上記において、ラミネート用接着剤としては、例えば、１液、あるいは２液型の硬化ないし非硬化タイプのビニル系、（メタ）アクリル系、ポリアミド系、ポリエステル系、ポリエーテル系、ポリウレタン系、エポキシ系、ゴム系、その他等の溶剤型、水性型、あるいは、エマルジョン型等のラミネート用接着剤を使用することができる。
上記のラミネート用接着剤のコーティング方法としては、例えば、ダイレクトグラビアロールコート法、グラビアロールコート法、キスコート法、リバースロールコート法、フォンテン法、トランスファーロールコート法、その他の方法で塗布することができる。
その塗布量としては、０．１ｇ／ｍ²〜１０ｇ／ｍ²（乾燥状態）位が好ましく、１ｇ／ｍ²〜５ｇ／ｍ²（乾燥状態）位がより好ましい。
上記において、接着樹脂層としては、熱可塑性樹脂層からなる樹脂層が使用され、各層間を接着するために使用することができる。 Next, lamination | stacking with the base material layer 11 and the sealant layer 13 will not be specifically limited if it is methods, such as a coextrusion laminating method and a dry laminating method.
The adhesive layer 12 is an adhesive by lamination or an adhesive resin layer.
In the above, as the laminating adhesive, for example, one-part or two-part curable or non-cured vinyl type, (meth) acrylic type, polyamide type, polyester type, polyether type, polyurethane type, epoxy type, etc. It is possible to use adhesives for laminating such as rubber type, other solvent type, aqueous type, or emulsion type.
As a coating method of the adhesive for laminating, for example, direct gravure roll coating method, gravure roll coating method, kiss coating method, reverse roll coating method, fountain method, transfer roll coating method, and other methods can be used. .
As the coating ^{amount, 0.1g / m 2 ~10g / m} 2 ( dry state) position are ^{preferred, 1g / m 2 ~5g / m} 2 ( dry state) position is more preferred.
In the above, a resin layer made of a thermoplastic resin layer is used as the adhesive resin layer, and can be used for bonding the respective layers.

具体的には、接着層１２の材料としては、低密度ポリエチレン樹脂、中密度ポリエチレン樹脂、高密度ポリエチレン樹脂、直鎖状低密度ポリエチレン樹脂、メタロセン触媒を利用して重合したエチレン・αオレフィンとの共重合体樹脂、エチレン・ポリプロピレン共重合体樹脂、エチレン・酢酸ビニル共重合体樹脂、エチレン・アクリル酸共重合体樹脂、エチレン・アクリル酸エチル共重合体樹脂、エチレン・メタクリル酸共重合体樹脂、エチレン・メタクリル酸メチル共重合体樹脂、エチレン・マレイン酸共重合体樹脂、アイオノマー樹脂、ポリオレフィン樹脂に不飽和カルボン酸、不飽和カルボン酸、不飽和カルボン酸無水物、エステル単量体をグラフト重合、または、共重合した樹脂、無水マレイン酸をポリオレフィン樹脂にグラフト変性した樹脂等を使用することができる。
これらの材料は、一種ないしそれ以上を組み合わせて使用することができる。
その樹脂層の厚みとしては、１０〜３０μｍ位が好ましい。 Specifically, the material of the adhesive layer 12 includes a low density polyethylene resin, a medium density polyethylene resin, a high density polyethylene resin, a linear low density polyethylene resin, and ethylene / α-olefin polymerized using a metallocene catalyst. Copolymer resin, ethylene / polypropylene copolymer resin, ethylene / vinyl acetate copolymer resin, ethylene / acrylic acid copolymer resin, ethylene / ethyl acrylate copolymer resin, ethylene / methacrylic acid copolymer resin, Graft polymerization of unsaturated carboxylic acid, unsaturated carboxylic acid, unsaturated carboxylic acid anhydride, ester monomer to ethylene / methyl methacrylate copolymer resin, ethylene / maleic acid copolymer resin, ionomer resin, polyolefin resin, Or graft copolymerized resin, maleic anhydride to polyolefin resin It can be used sexual resin or the like.
These materials can be used alone or in combination.
The thickness of the resin layer is preferably about 10 to 30 μm.

さらに、本発明においては、基材層１１とシーラント層１３の間に中間層１４を設けてもよく、中間層１４は、通常、基材層１１とシーラント層１３だけでは包装袋１としての機能を十分に果たすことができない場合等に設けられる。
前記の機能としては、気体遮断性、機械的強靱性、耐屈曲性、耐突き刺し性、耐衝撃性、耐磨耗性、耐寒性、耐熱性、耐薬品性等であり、包装袋１として要求されるこれらの機能を中間層１４として設けることで達成するものである。 Furthermore, in this invention, you may provide the intermediate | middle layer 14 between the base material layer 11 and the sealant layer 13, and the intermediate | middle layer 14 is the function as the packaging bag 1 only by the base material layer 11 and the sealant layer 13 normally. It is provided when it is not possible to sufficiently fulfill the above.
The above functions include gas barrier properties, mechanical toughness, bending resistance, puncture resistance, impact resistance, wear resistance, cold resistance, heat resistance, chemical resistance, etc., which are required as a packaging bag 1 These functions are achieved by providing the intermediate layer 14 as an intermediate layer 14.

前記の中間層１４として用いられる基材としては、例えば、ポリエチレンテレフタレート、ポリアミド、ポリエチレン、ポリプロピレン等のポリオレフィン、ポリ塩化ビニル、ポリカーボネート、ポリビニルアルコール、エチレン−プロピレン共重合体、エチレン−酢酸ビニル共重合体ケン化物等のフィルムあるいはこれらにポリ塩化ビニリデンを塗工したフィルムないしは酸化珪素、酸化アルミニウム等の無機物の蒸着を施したフィルムあるいはポリ塩化ビニリデン等のフィルム等を用いることができる。
また、これら基材の一種ないしそれ以上を組み合わせて使用することができる。
尚、上記基材の厚さとしては、包装体として要求される機能を満たすことができればよいのであって、必要に応じて適宜に選ぶことができる。
なお、上記の積層を行う場合、必要ならば、例えば、コロナ処理、オゾン処理、フレーム処理、その他等の前処理を施し、積層することができる。 Examples of the base material used as the intermediate layer 14 include polyolefins such as polyethylene terephthalate, polyamide, polyethylene, and polypropylene, polyvinyl chloride, polycarbonate, polyvinyl alcohol, ethylene-propylene copolymer, and ethylene-vinyl acetate copolymer. A film such as a saponified product, a film obtained by coating polyvinylidene chloride on these films, a film obtained by depositing an inorganic substance such as silicon oxide or aluminum oxide, or a film such as polyvinylidene chloride can be used.
One or more of these substrates can be used in combination.
It should be noted that the thickness of the base material only needs to satisfy the function required for the package, and can be appropriately selected as necessary.
In addition, when performing said lamination | stacking, if necessary, it can laminate | stack by performing pretreatments, such as a corona treatment, an ozone treatment, a flame | frame treatment, etc., for example.

上記の表面前処理は、各種の樹脂のフィルムないしシートと各層を積層する際、密着性等を改良するための方法として実施するものであるが、上記の密着性を改良する方法として、例えば、各種の樹脂のフィルムないしシートの表面に、予め、プライマーコート剤層、アンダーコート剤層、アンカーコート剤層等を任意に形成して、表面処理層とすることもできる。 The above-mentioned surface pretreatment is carried out as a method for improving the adhesion and the like when laminating each resin film or sheet and each layer. As a method for improving the above adhesion, for example, A primer coat agent layer, an undercoat agent layer, an anchor coat agent layer, and the like can be arbitrarily formed in advance on the surface of various resin films or sheets to form a surface treatment layer.

さらに、本発明においては、電子レンジ用包装袋１の胴部シール部５の縁にノッチ２２を形成しておくことが好ましい。
この場合、ノッチ２２を介して横方向に引き裂き容易な引き裂き方向性のある延伸フィルムを使用することが好ましい。 Furthermore, in this invention, it is preferable to form the notch 22 in the edge of the trunk | drum seal | sticker part 5 of the packaging bag 1 for microwave ovens.
In this case, it is preferable to use a stretched film having a tearing directionality that is easy to tear laterally through the notch 22.

上記において、ヒートシールの方法としては、例えば、バーシール、回転ロールシール、ベルトシール、インパルスシール、高周波シール、超音波シール等の方法で行うことができる。 In the above, as a heat sealing method, for example, a bar seal, a rotary roll seal, a belt seal, an impulse seal, a high frequency seal, an ultrasonic seal, or the like can be used.

なお、本発明の電子レンジ用包装袋１には、図示しないが、コの字状シール部の下側の胴部シール部５に、広幅のシール部を形成して、保持手段２１とすることができる。
このことによって、電子レンジで加熱後に包装袋を取出す際、コの字状シール部９内の切欠１７または切込み１８から放出される蒸気で消費者が火傷することなく、また、広幅シール部は、内容物に接する袋のフィルムの表面部分と比べて熱くならないため、安全かつ確実に取り出すことができる。
なお、広幅シール部のシール幅としては、１０ｍｍ〜２０ｍｍ程度が、消費者が電子レンジで加熱後に包装袋を取出す際、安全かつ確実に取り出すことができるため好ましいものである。 Although not shown in the drawings, the microwave packaging bag 1 of the present invention forms a wide seal portion on the lower body seal portion 5 on the lower side of the U-shaped seal portion to form the holding means 21. Can do.
By this, when taking out the packaging bag after heating in the microwave oven, the consumer is not burned by the steam released from the notch 17 or the notch 18 in the U-shaped seal part 9, and the wide seal part is Since it does not become hot compared with the surface portion of the bag film in contact with the contents, it can be removed safely and reliably.
In addition, as a seal width of the wide seal portion, about 10 mm to 20 mm is preferable because it can be taken out safely and reliably when the consumer takes out the packaging bag after heating with a microwave oven.

また、図示はしないが、包装袋１の中には、固体状の内容物以外に液状の内容物を充填することが可能であり、例えば、冷凍しゅうまい等の固形食品、カレー、スープ、醤油、ソース、出し汁、香辛料、料理用酒類、果汁類、水等の各種の流動性食品、飲食品を充填包装し得るものであり、食品を食べるに際して袋を自立させた状態のまま、電子レンジで所定時間、加熱調理することができ、内容物であるカレールーやソース等の液体、粘体を吹き出すことを防止すると共に、加熱により発生する蒸気のみを速やかに排出し、自動的に内圧を低下させることができ、自立性に優れ、電子レンジから保持手段によりやけどすることなく安全に取り出すことができ、容易かつ安全に内容物を移し替えやすく、店頭での陳列効果にも優れ、生産性良くシール加工できるものである。 Although not shown, the packaging bag 1 can be filled with liquid contents in addition to the solid contents. For example, solid foods such as frozen sushi, curry, soup, soy sauce, Various fluid foods such as sauces, soup stocks, spices, cooking liquors, fruit juices, water, etc., can be filled and packaged, and prescribed in a microwave oven with the bags left free when eating foods It can be cooked for a long time, and it prevents liquids and mucilages such as curry roux and sauce that are the contents from being blown out, and quickly discharges only the steam generated by heating, automatically reducing the internal pressure It is easy to stand, can be safely removed from the microwave oven without being burned by holding means, the contents can be easily and safely transferred, the display effect at the store is excellent, and the productivity is good It is those that can seal processing.

以下に実施例および比較例をあげて本発明を更に説明する。
基材層として、厚さ１２μｍのポリエチレンテレフタレートフィルムを使用し、中間層として、１５μｍの延伸ナイロンフィルムを使用し、シーラント層１３として、６０μｍの無延伸ポリプロピレンフィルムを使用し、層間をウレタン系接着剤でドライラミネートして、順次積層し、層構成、ポリエチレンテレフタレートフィルム（１２μｍ）／延伸ナイロンフィルム（１５μｍ）／無延伸ポリプロピレンフィルム（６０μｍ）からなる積層フィルム１０を作製した。
上記で得られた積層フィルム１０を用いて、胴部が前面２と後面３の２枚の壁面フィルムの両側端縁部を胴部シール部５でヒートシールして形成し、蒸通口１７とコの字状シール部９の初期剥離端２０との間に、蒸気の流れを制御する通路を形成するためのシール部１６をコの字状シール部９と一体で形成し、更に、コの字状シール部９に囲まれた未シール部１９に切欠１７を一つ設けた後、底面４のフィルムを内側に折り返してなるガセット形式で形成され、底部シール部６が舟底形のシールパターンでヒートシールされ、図４に示すような本発明にかかる形態の自立性電子レンジ用包装袋１を製造した。（外寸法、高さｂ：１５０ｍｍ、巾ａ：１４５ｍｍ、ｃ：１５ｍｍ、ｄ：３０ｍｍ、切欠の直径：４ｍｍφ、コの字状シール部のシール幅：３ｍｍ、周縁シール部のシール幅：１０ｍｍ）
上記で得られた包装袋１を用いて、内容物を充填し、天部シール部７をシールして密封後、１２１℃で３０分レトルト処理した。
上記で得られたレトルト処理後の包装体を自立させた状態で入れ、１６００Ｗの家庭用電子レンジで加熱した。
その結果、本発明に係る電子レンジ用包装袋１は、電子レンジ内の回転したトレーの上で転倒することなく、周縁シール部が破袋して内容物が吹きこぼれることなく、電子レンジ用包装袋１の蒸通口１７から速やかに蒸気のみが抜け、包装袋の蒸通口から内容物の液垂れもなく、内容物の液の吹き出しもなく、消費者が恐怖感を感じることなく、安全に加熱調理することができ、包装体の外観、衛生性にも優れる包装袋であった。 The present invention will be further described below with reference to examples and comparative examples.
A polyethylene terephthalate film having a thickness of 12 μm is used as the base material layer, a 15 μm stretched nylon film is used as the intermediate layer, a 60 μm unstretched polypropylene film is used as the sealant layer 13, and a urethane adhesive is used between the layers. Were laminated in order, and a laminated film 10 consisting of a layer structure, a polyethylene terephthalate film (12 μm) / stretched nylon film (15 μm) / unstretched polypropylene film (60 μm) was produced.
Using the laminated film 10 obtained above, the body portion is formed by heat-sealing both side edge portions of the two wall-surface films of the front surface 2 and the rear surface 3 with the body seal portion 5, A seal portion 16 for forming a passage for controlling the flow of steam is formed integrally with the U-shaped seal portion 9 between the initial peeling end 20 of the U-shaped seal portion 9 and further, After forming one notch 17 in the unsealed portion 19 surrounded by the letter-shaped seal portion 9, the bottom seal portion 6 is formed in a gusset form by folding the film of the bottom surface 4 inward, and the bottom seal portion 6 is a boat bottom-shaped seal pattern The self-supporting microwave packaging bag 1 according to the present invention as shown in FIG. 4 was manufactured. (Outer dimensions, height b: 150 mm, width a: 145 mm, c: 15 mm, d: 30 mm, notch diameter: 4 mmφ, U-shaped seal part seal width: 3 mm, peripheral seal part seal width: 10 mm)
Using the packaging bag 1 obtained above, the contents were filled, the top seal portion 7 was sealed and sealed, and then retorted at 121 ° C. for 30 minutes.
The retort-treated package obtained above was placed in a self-supporting state and heated in a 1600 W household microwave oven.
As a result, the microwave packaging bag 1 according to the present invention does not fall on the rotated tray in the microwave oven, and the peripheral seal portion breaks and the contents are not blown out. Only the steam quickly escapes from the steaming port 17 of the bag 1, there is no dripping of the contents from the steaming port of the packaging bag, no liquid is blown out of the contents, and the consumer does not feel a sense of fear. It was a packaging bag that can be cooked with heat and has excellent appearance and hygiene.

〔比較例１〕
実施例１において、蒸通口１７とコの字状シール部９の初期剥離端２０との間に、蒸気の流れを制御する通路を形成するためのシール部１６を形成しない以外は、実施例１と同様の包装材料を用いて、同様の製造方法で比較例１の電子レンジ用包装袋を作製した。 [Comparative Example 1]
In Example 1, except that the seal part 16 for forming a passage for controlling the flow of the steam is not formed between the steaming port 17 and the initial peeling end 20 of the U-shaped seal part 9. Using the same packaging material as in No. 1, a packaging bag for microwave oven of Comparative Example 1 was produced by the same manufacturing method.

実施例１及び比較例１で得られた包装袋にトマトカレーソース、２０５ｇを充填後、天部シール部７をシールして密封し、１２１℃で３０分レトルト殺菌したものを、１５袋作製した。
上記で得られたレトルト殺菌処理したトマトカレーの包装体を出力１６００Ｗの電子レンジで２分加熱し、包装袋の蒸通口１７からの内容物の液垂れ、および包装袋の蒸通口１７付近の汚れの状態を観察した。結果を表１に示す。 After filling the packaging bags obtained in Example 1 and Comparative Example 1 with 205 g of tomato curry sauce, the top seal part 7 was sealed and sealed, and 15 bags were produced by retort sterilization at 121 ° C. for 30 minutes. .
The package of tomato curry treated with retort sterilization obtained above is heated in a microwave oven with an output of 1600 W for 2 minutes, the content dripping from the steaming port 17 of the packaging bag, and the vicinity of the steaming port 17 of the packaging bag The state of soiling was observed. The results are shown in Table 1.

その結果、蒸通口１７とコの字状シール部９の初期剥離端２０との間に、蒸気の流れを制御する通路を形成するためのシール部１６を設けた実施例１の包装袋１では、電子レンジで加熱による内圧の上昇し、加熱調理によって調理用袋体内部の圧力が所定以上となると、電子レンジ用包装袋１の蒸通口１７から内容物が吹き出すことを妨げると共に蒸気のみが蒸通口１７から抜けるため、包装袋の蒸通口付近から内容物の液垂れもなく、内容物の液の汚れもなく、内容物を安全に調理され、衛生的に内容物を取り出すことが確認できた。
これに対して、比較例１の包装袋では、包装袋の蒸通口１７から内容物の液垂れが発生したり、蒸通口付近に内容物の汚れの付着がみられるものがあった。 As a result, the packaging bag 1 according to the first embodiment in which the seal portion 16 for forming a passage for controlling the flow of the steam is provided between the steam opening 17 and the initial peeling end 20 of the U-shaped seal portion 9. Then, when the internal pressure rises due to heating in the microwave oven and the pressure inside the cooking bag becomes higher than a predetermined value due to cooking, the contents are prevented from blowing out from the steaming opening 17 of the microwave packaging bag 1 and only steam is used. Is removed from the steaming port 17, so that the contents do not drip from the steaming port of the packaging bag, the contents are not contaminated, the contents are cooked safely, and the contents are taken out hygienically. Was confirmed.
On the other hand, in the packaging bag of Comparative Example 1, there was a case in which the liquid dripping of the contents occurred from the steaming port 17 of the packaging bag or the contents were adhered to the vicinity of the steaming port.

本発明の電子レンジ用包装袋の用途は、飲食品を充填包装し、電子レンジで所定時間加熱調理するために使用するものであり、例えば、固体状の内容物以外に液体を含む内容物を調理することが可能であり、例えば、冷凍しゅうまい等の固形食品以外に、カレー、スープ、醤油、ソース、出し汁、香辛料、料理用酒類、果汁類、水等の各種の流動性食品、飲食品を充填包装し電子レンジで加熱調理し得るものであり、特に制限は無い。 The microwave oven packaging bag of the present invention is used for filling and packaging foods and beverages and cooking for a predetermined time in a microwave oven. For example, contents containing liquid other than solid contents are used. For example, in addition to solid foods such as frozen cucumbers, various fluid foods such as curry, soup, soy sauce, sauce, soup stock, spices, liquor for cooking, fruit juices, water, etc. There is no particular limitation as it can be filled and packaged and cooked in a microwave oven.

本発明の電子レンジ用包装袋１の実施例を示す斜視図である。It is a perspective view which shows the Example of the packaging bag 1 for microwave ovens of this invention. 本発明の電子レンジ用包装袋１を形成する包装材料の積層体１０の断面図である。It is sectional drawing of the laminated body 10 of the packaging material which forms the packaging bag 1 for microwave ovens of this invention. 包装袋を形成する包装材料の別態様の積層体の断面図である。It is sectional drawing of the laminated body of another aspect of the packaging material which forms a packaging bag. 本発明の電子レンジ用包装袋１におけるコの字状シール部９の形成位置の説明図である。It is explanatory drawing of the formation position of the U-shaped seal part 9 in the packaging bag 1 for microwave ovens of this invention. 蒸気の流れを制御する通路を形成するためのシール部１６の形状を示す図である。It is a figure which shows the shape of the seal part 16 for forming the channel | path which controls the flow of a vapor | steam. コの字状シール部９で囲まれる未シール部１９内に形成する切欠１７または切込み１８の形状を示す図である。It is a figure which shows the shape of the notch 17 or notch 18 formed in the unsealed part 19 enclosed by the U-shaped seal part 9. FIG. 図１のＸ−Ｘ線の断面図である。It is sectional drawing of the XX line of FIG. 図１の本発明の電子レンジ用包装袋１のコの字状シール部９の剥離開封を説明する模式図である。It is a schematic diagram explaining peeling opening of the U-shaped seal part 9 of the packaging bag 1 for microwave ovens of this invention of FIG. 従来の電子レンジ用包装袋のコの字状シール部９の剥離開封を説明する模式図である。It is a schematic diagram explaining peeling opening of the U-shaped seal part 9 of the conventional packaging bag for microwave ovens. 従来の電子レンジ用包装袋のコの字状シール部９の剥離開封を説明する模式図である。It is a schematic diagram explaining peeling opening of the U-shaped seal part 9 of the conventional packaging bag for microwave ovens. 電子レンジ用包装袋の外装箱に収納した状態で起立させるための説明図である。It is explanatory drawing for standing up in the state accommodated in the exterior box of the packaging bag for microwave ovens.

Explanation of symbols

１本発明の電子レンジ用包装袋
２前面
３後面
４底面
５胴部シール部
６底部シール部
７天部シール部
８底面フィルム切り欠き部
９コの字状シール部
１０積層体
１１基材層
１２接着層
１３シーラント層
１４中間層
１５印刷層
１６蒸気の流れを制御する通路を形成するためのシール部
１７蒸通口（切欠）
１８蒸通口（切込み）
１９未シール部
２０初期剥離端
２１未シール部初期到達点
２２ノッチ
２３内容物
２４剥離部
３０自立補助手段
DESCRIPTION OF SYMBOLS 1 Microwave packaging bag 2 Front surface 3 Rear surface 4 Bottom surface 5 Body seal portion 6 Bottom seal portion 7 Top seal portion 8 Bottom film cutout portion 9 U-shaped seal portion 10 Laminate 11 Base material layer 12 Adhesive layer 13 Sealant layer 14 Intermediate layer 15 Print layer 16 Sealing portion 17 for forming a passage for controlling the flow of steam
18 Steaming mouth (cutting)
19 Unsealed part 20 Initial peeling end 21 Unsealed part initial arrival point 22 Notch 23 Contents 24 Peeling part 30 Self-supporting means

Claims

In a bag for heating by a microwave oven, using a laminated film composed of at least one side of a sealant layer, sealing the peripheral part with the sealant surfaces facing each other, and in a sealed packaging bag,
An unsealed portion surrounded by the U-shaped seal portion is provided above the packaging bag as a means for venting steam by heating in a microwave oven in connection with the peripheral seal portion. Equipped with at least one vent
An electronic device comprising at least one seal portion for forming a passage for controlling the flow of steam between the steam opening and the initial peeling end of the U-shaped seal portion. Packaging bag for range.

When a circle centered on the center of the bag is drawn, the radius of the circle in contact with the innermost edge of the U-shaped seal portion from the center of the bag is larger than the radius of the circle in contact with the inner edge of the trunk seal portion. The microwave oven packaging bag according to claim 1, wherein the packaging bag is provided at a position that shortens the length.

The packaging bag for a microwave oven according to any one of claims 1 to 2, wherein a lowermost end of the U-shaped seal portion forms a protruding end having a protruding shape.

The above-mentioned steaming opening is formed through two members constituting the packaging bag, or formed on only one surface of the two members constituting the packaging bag. The packaging bag for microwave ovens in any one of Claims 1-3 characterized by the above-mentioned.

The packaging bag is inserted into the bottom part of the front surface and the rear surface made of a quadrangle that constitutes the body part by folding the bottom surface in an inverted V shape, and heat-sealing the front surface, the rear surface, and the periphery of the bottom surface, respectively. The electronic device according to any one of claims 1 to 4, wherein the electronic device according to any one of claims 1 to 4, wherein the electronic device is a self-supporting packaging bag in which a peripheral seal portion is formed and the bottom portion expands back and forth by the filled contents and can stand on its own. Packaging bag for range.