JP2006348009A - Pigment for cosmetic and cosmetic containing the pigment - Google Patents
Pigment for cosmetic and cosmetic containing the pigment Download PDFInfo
- Publication number
- JP2006348009A JP2006348009A JP2005203494A JP2005203494A JP2006348009A JP 2006348009 A JP2006348009 A JP 2006348009A JP 2005203494 A JP2005203494 A JP 2005203494A JP 2005203494 A JP2005203494 A JP 2005203494A JP 2006348009 A JP2006348009 A JP 2006348009A
- Authority
- JP
- Japan
- Prior art keywords
- cosmetic
- pigment
- general formula
- powder
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、例えばファンデーション、アイシャドウ、ほほ紅等のメイクアップ化粧料もしくはサンスクリーン化粧料に配合されて撥水撥油性を示す化粧料用顔料とその化粧料用顔料を含有してなる化粧料に関するものである。 The present invention relates to a cosmetic pigment containing water and oil repellency and blended in makeup cosmetics or sunscreen cosmetics such as foundations, eye shadows and cheeks, and cosmetics comprising the cosmetic pigments It is about.
従来、ファンデーション、アイシャドウ、ほほ紅等のメイクアップ化粧料もしくはサンスクリーン化粧料等に用いられる化粧料用顔料においては、撥水性がないと、皮膚の発汗作用、涙、雨等の水質によって化粧くずれを起こし易く、また撥油性がないと、皮膚の脂質等によって化粧くずれを起こし易い。 Conventionally, cosmetic pigments used in makeup cosmetics such as foundations, eye shadows, and cheeks, or sunscreen cosmetics, etc., have no water repellency, and make up according to the water quality such as skin sweating, tears, and rain. It is easy to cause breakage, and if it is not oil-repellent, it tends to cause makeup breakage due to skin lipids and the like.
そこで、例えば特許文献1〜3においては、顔料の表面をパーフルオロアルキルリン酸エステル化合物にて表面処理することによってその顔料に撥水撥油性を付与するようにしたものが提案されている。また、例えば特許文献4においては、顔料の表面をパーフルオロアルキルアルコキシシランにて表面処理することによってその顔料に撥水撥油性を付与するようにしたものが提案されている。 Therefore, for example, Patent Documents 1 to 3 propose a technique in which the surface of a pigment is surface treated with a perfluoroalkyl phosphate compound to impart water and oil repellency to the pigment. For example, Patent Document 4 proposes a method in which a surface of a pigment is surface-treated with perfluoroalkylalkoxysilane to impart water and oil repellency to the pigment.
ところが、このパーフルオロアルキルリン酸エステル化合物やパーフルオロアルキルアルコキシシランを用いたとしても、一般的に用いられている脂肪族系もしくはシリコン系の油分、いわゆるバインダーや界面活性剤のみでは良好な分散状態で感触が良好な満足できる化粧料が得られないことから、例えば特許文献5,6に開示されているように、パーフルオロポリエーテル、パーフルオロデカリン、パーフルオロオクタン等のフッ素系の油剤を使用することが行われている。 However, even when this perfluoroalkyl phosphate compound or perfluoroalkylalkoxysilane is used, it is a good dispersion state with only commonly used aliphatic or silicon oils, so-called binders and surfactants. Since satisfactory cosmetics with a good touch cannot be obtained, fluorine oils such as perfluoropolyether, perfluorodecalin and perfluorooctane are used as disclosed in Patent Documents 5 and 6, for example. To be done.
しかしながら、前述のパーフルオロポリエーテル、パーフルオロデカリン、パーフルオロオクタン等のフッ素系の油剤は非常に高価であるため、これを配合させるのは特定の化粧料のみに限られるという問題点がある。また、この油剤を用いて得られる化粧料、とりわけパウダーファンデーションは、非常に軽くサラッとした感触、言い方を変えれば粉っぽい感触であるという問題点もある。 However, fluorine oils such as perfluoropolyether, perfluorodecalin, and perfluorooctane described above are very expensive, and therefore, there is a problem that only a specific cosmetic is incorporated. In addition, cosmetics obtained by using this oil, particularly powder foundations, have a problem that they have a very light and smooth feel and, in other words, a powdery feel.
本発明は、このような問題点を解消するためになされたもので、一般的に用いられている油分および界面活性剤等を使用することができるとともに、肌への広がりが良くてしっとりとした感触を与えることができ、しかも撥水撥油性に優れた化粧料用顔料とその顔料を含有する化粧料を提供することを目的とするものである。 The present invention has been made to solve such problems, and can use commonly used oils and surfactants, and has a good spread to the skin and is moist. An object of the present invention is to provide a cosmetic pigment that can give a touch and is excellent in water and oil repellency and a cosmetic containing the pigment.
前記目的を達成するために、第1発明による化粧料用顔料は、
化粧料用の顔料粉体に、下記一般式(1)にて示されるパーフルオロアルキルアルコキシシランと、下記一般式(3)にて示されるポリエーテル基を有するアルコキシシランとを表面処理してなることを特徴とするものである。
A pigment powder for cosmetics is surface-treated with a perfluoroalkylalkoxysilane represented by the following general formula (1) and an alkoxysilane having a polyether group represented by the following general formula (3). It is characterized by this.
また、第2発明による化粧料用顔料は、
化粧料用の顔料粉体に、下記一般式(2)にて示されるパーフルオロアルキル基を有するリン酸エステルと、下記一般式(3)にて示されるポリエーテル基を有するアルコキシシランとを表面処理してなることを特徴とするものである。
A pigment powder for cosmetics is coated with a phosphoric acid ester having a perfluoroalkyl group represented by the following general formula (2) and an alkoxysilane having a polyether group represented by the following general formula (3). It is characterized by being processed.
次に、第3発明による化粧料は、
前記第1発明または第2発明の化粧料用顔料を含有してなることを特徴とするものである。
Next, the cosmetic according to the third invention is:
It contains the cosmetic pigment of the first invention or the second invention.
本発明の化粧料用顔料によれば、撥水撥油性を有するとともに、一般的に用いられている例えばワセリン、セレシン、マイクロクリスタリンワックス、カルナバロウ、キャンデリラロウ、高級脂肪酸、高級アルコール、スクワラン、流動パラフィン、エステル油、ジグリセライド、トリグリセライド、シリコン油等の油分と、一般的な界面活性剤等を用いることができる。また、ファンデーション、アイシャドウ、ほほ紅などのメイクアップ化粧料やサンスクリーン化粧料として配合した場合に、容易に分散、配合させることができ、化粧料として使用したときに肌への広がりが良くてしっとりとした感触を与えることができる。また、本発明の化粧料によれば、撥水撥油性を示して化粧くずれを防止する機能を有し、しかもしっとり感が付与されて使用感に優れた化粧料を得ることができる。 According to the cosmetic pigment of the present invention, it has water and oil repellency and is generally used, for example, petroleum jelly, ceresin, microcrystalline wax, carnauba wax, candelilla wax, higher fatty acid, higher alcohol, squalane, fluid Oils such as paraffin, ester oil, diglyceride, triglyceride, silicone oil, and general surfactants can be used. In addition, when formulated as makeup cosmetics such as foundations, eye shadows, and cheeks, and sunscreen cosmetics, they can be easily dispersed and blended, and when used as cosmetics, they spread well to the skin. Can give a moist feel. In addition, according to the cosmetic of the present invention, it is possible to obtain a cosmetic that exhibits water and oil repellency and has a function of preventing makeup slippage and has a moist feeling and excellent usability.
次に、本発明による化粧料用顔料およびその顔料を含有する化粧料の具体的な実施の形態について説明する。 Next, specific embodiments of a cosmetic pigment and a cosmetic containing the pigment according to the present invention will be described.
本発明に用いられる被覆剤は、下記一般式(1);
また、下記一般式(2);
また、下記一般式(3);
前記一般式(1)で示されるパーフルオロアルキルアルコキシシランもしくは前記一般式(2)で示されるパーフルオロアルキル基を有するリン酸エステルと前記一般式(3)で示されるポリエーテル基を有するアルコキシシランとを化粧料用顔料粉体の表面に被覆する方法としては、例えば次のような方法がある。 Perfluoroalkylalkoxysilane represented by the general formula (1) or a phosphoric ester having a perfluoroalkyl group represented by the general formula (2) and an alkoxysilane having a polyether group represented by the general formula (3) As a method for coating the surface of the pigment powder for cosmetics, for example, there are the following methods.
まず、混合撹拌機に被覆されるべき所定量の前記一般式(1)にて示されるパーフルオロアルキルアルコキシシランもしくは前記一般式(2)にて示されるパーフルオロアルキル基を有するリン酸エステルと前記一般式(3)で示されるポリエーテル基を有するアルコキシシランとを濃度がそれぞれ化粧料用顔料粉体の0.05〜30重量%となる量をはかり取り、混合液を作製し、この混合液を撹拌中の化粧料用顔料粉体に滴下して表面処理を行う。この後、約100℃にて6時間加熱して目的とする撥水撥油性化粧料用顔料粉体を得る。 First, a predetermined amount of perfluoroalkylalkoxysilane represented by the general formula (1) or a phosphoric acid ester having a perfluoroalkyl group represented by the general formula (2) to be coated on the mixing stirrer and the above Weigh out the amount of the alkoxysilane having a polyether group represented by the general formula (3) in an amount of 0.05 to 30% by weight of the cosmetic pigment powder to prepare a mixed solution. Is dropped on the pigment powder for cosmetics under stirring to perform surface treatment. Thereafter, the mixture is heated at about 100 ° C. for 6 hours to obtain a desired water / oil repellent cosmetic pigment powder.
また、その他に次のような方法もある。すなわち、表面に被覆されるべき所定量の前記一般式(1)にて示されるパーフルオロアルキルアルコキシシランもしくは前記一般式(2)にて示されるパーフルオロアルキル基を有するリン酸エステルと前記一般式(3)にて示されるポリエーテル基を有するアルコキシシランとを濃度がそれぞれ化粧料用顔料粉体の0.05〜30重量%となる量をはかり取り、適当な溶剤に溶解もしくは分散エマルジョン化しておき、この加熱撹拌中に化粧料用顔料粉体を加え、一定時間撹拌しておく。この後、加熱(必要な場合には減圧にて)して溶剤を除去した後、約100℃にて6時間加熱し、その後粉砕して目的とする撥水撥油性化粧料用顔料粉体を得る。ここで用いられる溶剤としては、イソプロピルアルコール、アセトン等の極性をもつ有機溶剤が適当である。 In addition, there are other methods as follows. That is, a predetermined amount of perfluoroalkylalkoxysilane represented by the general formula (1) or a phosphate ester having a perfluoroalkyl group represented by the general formula (2) to be coated on the surface and the general formula The alkoxysilane having a polyether group represented by (3) is weighed in an amount of 0.05 to 30% by weight of the cosmetic pigment powder, and dissolved or dispersed into an appropriate solvent to form an emulsion. The pigment powder for cosmetics is added during the heating and stirring, and the mixture is stirred for a certain time. Thereafter, the solvent is removed by heating (reduced pressure if necessary), and then heated at about 100 ° C. for 6 hours, and then pulverized to obtain the desired water / oil repellent cosmetic pigment powder. obtain. As the solvent used here, a polar organic solvent such as isopropyl alcohol and acetone is suitable.
ここで、前記一般式(1)にて示されるパーフルオロアルキルアルコキシシランもしくは前記一般式(2)にて示されるパーフルオロアルキル基を有するリン酸エステルの被覆量は被覆される原料粉体の粒子径によって異なり、十分な撥水撥油性を示すところで決定されるべきであるが、一般的にその被覆量が30重量%を超えると、前記一般式(1)にて示されるパーフルオロアルキルアルコキシシランもしくは前記一般式(2)にて示されるパーフルオロアルキル基を有するリン酸エステルそのものが析出するようになり、化粧料として配合したときに感触に悪い影響を及ぼす可能性があるため、30重量%以下にするのが良い。 Here, the coating amount of the perfluoroalkylalkoxysilane represented by the general formula (1) or the phosphoric ester having a perfluoroalkyl group represented by the general formula (2) is the particle of the raw material powder to be coated Depending on the diameter, it should be determined where sufficient water and oil repellency is exhibited. Generally, when the coating amount exceeds 30% by weight, the perfluoroalkylalkoxysilane represented by the general formula (1) is used. Alternatively, the phosphoric acid ester having a perfluoroalkyl group represented by the general formula (2) itself is precipitated, and when blended as a cosmetic, there is a possibility of adversely affecting the touch. The following should be used.
一方、前記一般式(3)にて示されるポリエーテル基を有するアルコキシシランの被覆量についても被覆される原料粉体の粒子径によって異なるが、一般的に0.05〜20重量%の被覆量で目的とする粉体が得られることになる。この被覆量が0.05重量%未満であると、化粧料として配合したときに、一般的に用いられる油分バインダーでは良好な分散が得られなかったり、化粧料に配合した際にしっとり感が得られなかったりする可能性がある。また、この被覆料が20重量%を超えると、前記一般式(1)にて示されるパーフルオロアルキルアルコキシシランもしくは前記一般式(2)にて示されるパーフルオロアルキル基を有するリン酸エステルの被覆によってもたらされる撥油性が十分に発現しなくなったり、被覆剤同士の反応によって感触が悪くなったりする可能性がある。 On the other hand, the coating amount of the alkoxysilane having a polyether group represented by the general formula (3) also varies depending on the particle diameter of the raw material powder to be coated, but is generally 0.05 to 20% by weight. Thus, the desired powder can be obtained. When this coating amount is less than 0.05% by weight, when blended as a cosmetic, good dispersion is not obtained with a commonly used oil binder, or a moist feeling is obtained when blended into a cosmetic. It may not be possible. Further, when this coating material exceeds 20% by weight, the coating of the perfluoroalkylalkoxysilane represented by the general formula (1) or the phosphoric acid ester having the perfluoroalkyl group represented by the general formula (2) There is a possibility that the oil repellency brought about by the resin may not be sufficiently developed, or the feeling may be deteriorated by the reaction between the coating agents.
本発明により表面被覆される化粧料用顔料としては、無機顔料、有機顔料および樹脂粉体顔料である。ここで、無機顔料としては、酸化チタン、ベンガラ、黄酸化鉄、黒色酸化鉄、群青、亜鉛華、酸化マグネシウム、酸化ジルコニウム、マイカ、セリサイト、タルク、シリカ、カオリン、炭酸カルシウム、水酸化クロム、ケイ酸マグネシウム、酸化アルミニウム、硫酸バリウム、チタン被覆雲母等が挙げられる。また、有機顔料としては、リソールルビンB、レーキレッドC、リソールレッド、ローダミンB、ヘリンドンピンクCN、パーマネントレッド、ベンジジンオレンジG、フタロシアニンブルー等が挙げられる。また、樹脂粉体顔料としては、ナイロンパウダー、アクリルパウダー、シリコンパウダー等が挙げられる。 Cosmetic pigments that are surface-coated according to the present invention include inorganic pigments, organic pigments, and resin powder pigments. Here, as the inorganic pigment, titanium oxide, bengara, yellow iron oxide, black iron oxide, ultramarine, zinc white, magnesium oxide, zirconium oxide, mica, sericite, talc, silica, kaolin, calcium carbonate, chromium hydroxide, Examples thereof include magnesium silicate, aluminum oxide, barium sulfate, and titanium-coated mica. Examples of organic pigments include Risol Rubin B, Lake Red C, Risol Red, Rhodamine B, Herringdon Pink CN, Permanent Red, Benzidine Orange G, and Phthalocyanine Blue. Examples of the resin powder pigment include nylon powder, acrylic powder, and silicon powder.
本発明の化粧料用顔料によれば、化粧料に配合される際に、パーフルオロポリエーテル、パーフルオロデカリン、パーフルオロオクタン等のフッ素系の分散配合剤を使用することなしに、分散油性成分として例えばワセリン、ラノリン、マイクロクリスタリンワックス、カルナバロウ、キャンデリアロウ、スクワラン、流動パラフィン、エステル油、ジグリセライド、トリグリセライド、シリコン油等の一般的な油性成分を用いて容易に化粧料を配合調整することができる。また、配合調整された化粧料においては、要求されるべき十分な撥水撥油性を示し、かつ肌への延展性がよくてしっとりとした感触を付与することができるという効果を奏する。 According to the cosmetic pigment of the present invention, when blended in a cosmetic, without using a fluorine-based dispersion compounding agent such as perfluoropolyether, perfluorodecalin, and perfluorooctane, the dispersed oil component For example, it is possible to easily blend and adjust cosmetics using general oil components such as petrolatum, lanolin, microcrystalline wax, carnauba wax, canderia wax, squalane, liquid paraffin, ester oil, diglyceride, triglyceride, silicone oil, etc. it can. In addition, the cosmetics that have been blended and adjusted exhibit sufficient water and oil repellency that should be required, and have the effect of being able to impart a moist feel with good spreadability to the skin.
なお、化粧料に配合される前記化粧料用顔料の配合量としては、化粧料の総量に対して0.1〜100重量%が好ましく、より好ましくは1〜80重量%である。また、前記化粧料の剤型としては、二層状、油中水型エマルション、水中油型エマルション、ジェル状、スプレー、ムース状、油性、固形状等、従来公知の剤型を使用することができる。特に、サンスクリーン剤の用途には、二層状、油中水型エマルション、ジェル状が好ましく、またファンデーションの用途には、固形状、固形エマルション状、ジェル状、油中水型エマルション、水中油型エマルション、油状、ムース状等が好ましい。 In addition, as a compounding quantity of the said pigment for cosmetics mix | blended with cosmetics, 0.1 to 100 weight% is preferable with respect to the total amount of cosmetics, More preferably, it is 1 to 80 weight%. As the cosmetic dosage form, conventionally known dosage forms such as bilayer, water-in-oil emulsion, oil-in-water emulsion, gel, spray, mousse, oily, solid, etc. can be used. . In particular, for use as a sunscreen agent, a two-layered, water-in-oil emulsion or gel is preferred, and for a foundation as a solid, solid emulsion, gel, water-in-oil emulsion, oil-in-water type. Emulsions, oils, mousses and the like are preferred.
次に、本発明による化粧料用顔料およびその顔料を含有する化粧料の具体的な実施例について以下に説明する。なお、本発明は、以下に述べる実施例に限定されるものではない。 Next, specific examples of the cosmetic pigment and the cosmetic containing the pigment according to the present invention will be described below. In addition, this invention is not limited to the Example described below.
(製造実施例1)
化粧料用酸化チタン1kgに対して5重量%のデグサ社製DYNASYLAN F8261(トリデカフルオロオクチルトリエトキシシラン)と1重量%のデグサ社製DYNASYLAN4140のイソプロピルアルコール混合溶液を作製し、撹拌槽で撹拌されている酸化チタンと混合し、イソプロピルアルコールを加熱除去して撹拌槽から粉体を取り出した。この後、100℃にて6時間加熱処理を行い、粉砕して表面被覆した酸化チタンを得た。これと同様な方法で、顔料として酸化チタンに代えてセリサイト、タルク、マイカ、黄酸化鉄、ベンガラ、黒色酸化鉄を用いて計7種類の化粧料用顔料を得た。
(Production Example 1)
A isopropyl alcohol mixed solution of 5% by weight of DYNASYLAN F8261 (tridecafluorooctyltriethoxysilane) manufactured by Degussa and 1% by weight of DYNASYLAN 4140 manufactured by Degussa is prepared with respect to 1 kg of titanium oxide for cosmetics and stirred in a stirring tank. The mixture was mixed with titanium oxide, and isopropyl alcohol was removed by heating to take out the powder from the stirring tank. Thereafter, heat treatment was performed at 100 ° C. for 6 hours, and crushed and surface-coated titanium oxide was obtained. In the same manner, seven types of cosmetic pigments were obtained using sericite, talc, mica, yellow iron oxide, red iron oxide, and black iron oxide in place of titanium oxide.
(製造実施例2)
化粧料用酸化チタン1kgに対して5重量%の炭素数が13のパーフルオロアルキルリン酸エステルアンモニウム塩と1重量%のデグサ社製DYNASYLAN4140のイソプロピルアルコール混合エマルション溶液を作製し、撹拌槽で撹拌されている酸化チタンと混合し、イソプロピルアルコールを加熱除去して撹拌槽から粉体を取り出した。この後、100℃にて6時間加熱処理を行い、粉砕して表面被覆した酸化チタンを得た。これと同様な方法で、顔料として酸化チタンに代えてセリサイト、タルク、マイカ、黄酸化鉄、ベンガラ、黒色酸化鉄を用いて計7種類の化粧料用顔料を得た。
(Production Example 2)
A perfluoroalkyl phosphate ammonium salt having a carbon number of 5% by weight and 1% by weight of DYNASYLAN 4140 made by Degussa Co., Ltd. is prepared in a stirring tank and stirred in a stirring tank. The mixture was mixed with titanium oxide, and isopropyl alcohol was removed by heating to take out the powder from the stirring tank. Thereafter, heat treatment was performed at 100 ° C. for 6 hours, and crushed and surface-coated titanium oxide was obtained. In the same manner, seven types of cosmetic pigments were obtained using sericite, talc, mica, yellow iron oxide, red iron oxide, and black iron oxide in place of titanium oxide.
(製造比較例1)
化粧料用顔料1kgに対してデグサ社製DYNASYLAN F8261(トリデカフルオロオクチルトリエトキシシラン)を5重量%だけ用いて前記製造実施例1と同様にして表面被覆を行い、撥水撥油性を示す酸化チタン、セリサイト、タルク、マイカ、黄酸化鉄、ベンガラ、黒色酸化鉄の計7種類の化粧料用顔料を得た。
(Production Comparative Example 1)
Surface coating was carried out in the same manner as in Production Example 1 using 5% by weight of DYNASYLAN F8261 (Tridecafluorooctyltriethoxysilane) manufactured by Degussa Co. per 1 kg of cosmetic pigment, and an oxidation exhibiting water and oil repellency. Seven types of cosmetic pigments were obtained: titanium, sericite, talc, mica, yellow iron oxide, bengara, and black iron oxide.
これら製造実施例1,2および製造比較例1の各表面被覆顔料について、撥水度、撥油度を測定した。この測定結果が表1に示されている。ここで、撥水度については水による接触角を、撥油度についてはパラフィンによる接触角を測定した。なお、この接触角の測定にはエルマー社製ゴニオメータ式接触角測定装置を用いた。 For each of the surface-coated pigments of Production Examples 1 and 2 and Production Comparative Example 1, the water repellency and oil repellency were measured. The measurement results are shown in Table 1. Here, the contact angle with water was measured for the water repellency, and the contact angle with paraffin was measured for the oil repellency. The contact angle was measured using a goniometer type contact angle measuring device manufactured by Elmer.
(実施例1)
製造実施例1で調製された顔料を用い、以下の配合にてパウダーファンデーションを調製した。
表面被覆セリサイト 35.0
表面被覆タルク 25.0
表面被覆マイカ 20.0
表面被覆酸化チタン 10.0
表面被覆黄酸化鉄 4.0
表面被覆ベンガラ 1.2
表面被覆黒色酸化鉄 0.8
ナイロンパウダー 4.0
100.0
Example 1
Using the pigment prepared in Production Example 1, a powder foundation was prepared with the following composition.
Surface coated sericite 35.0
Surface coated talc 25.0
Surface coating mica 20.0
Surface coated titanium oxide 10.0
Surface coated yellow iron oxide 4.0
Surface coating Bengala 1.2
Surface coating black iron oxide 0.8
Nylon powder 4.0
100.0
前記パウダーファンデーションをパウダーベースとして88%含み、バインダーベースを12%として、これらをヘンシェルミキサーにて混合した。このときバインダーベースの配合は次のとおりである。
ジメチルポリシロキサン(6CS) 30.0
ジメチルポリシロキサン(10000CS) 25.0
精製ラノリン 9.0
エステル油 36.0
100.0
The powder foundation was mixed with a Henschel mixer containing 88% as a powder base and 12% as a binder base. At this time, the binder base was blended as follows.
Dimethylpolysiloxane (6CS) 30.0
Dimethylpolysiloxane (10000CS) 25.0
Purified lanolin 9.0
Ester oil 36.0
100.0
(実施例2)
製造実施例2で調製された顔料を用い、以下の配合にてW/Oリキッドファンデーションを調製した。
表面被覆タルク 3.0
表面被覆セリサイト 2.0
表面被覆酸化チタン 15.0
表面被覆ベンガラ 0.2
表面被覆黄酸化鉄 2.5
表面被覆黒色酸化鉄 0.8
メチルポリシロキサン(6CS) 7.4
ジメチルシクロヘキサン−メチル(ポリオキシエチレン)
ジメチルシロキサン共重合体 1.8
メチルポリシロキサン(100CS) 8.0
メチルポリシロキサン(10000CS) 4.0
メチルフェニルポリシロキサン 10.0
エタノール 10.0
1,3−ブチレングリコール 2.0
精製水 33.3
100.0
(Example 2)
Using the pigment prepared in Production Example 2, a W / O liquid foundation was prepared with the following composition.
Surface coated talc 3.0
Surface coated sericite 2.0
Surface coated titanium oxide 15.0
Surface coating Bengala 0.2
Surface coated yellow iron oxide 2.5
Surface coating black iron oxide 0.8
Methyl polysiloxane (6CS) 7.4
Dimethylcyclohexane-methyl (polyoxyethylene)
Dimethylsiloxane copolymer 1.8
Methyl polysiloxane (100CS) 8.0
Methyl polysiloxane (10000CS) 4.0
Methylphenyl polysiloxane 10.0
Ethanol 10.0
1,3-butylene glycol 2.0
Purified water 33.3
100.0
(比較例1)
実施例1と同様の配合にて、表面被覆顔料として製造比較例1で調製された顔料を用いてパウダーファンデーションを調製した。
(Comparative Example 1)
A powder foundation was prepared using the pigment prepared in Production Comparative Example 1 as a surface coating pigment with the same formulation as in Example 1.
(比較例2)
実施例2と同様の配合にて、表面被覆顔料として製造比較例1で調製された顔料を用いてW/Oリキッドファンデーションを調製した。
(Comparative Example 2)
A W / O liquid foundation was prepared using the pigment prepared in Production Comparative Example 1 as a surface coating pigment with the same formulation as in Example 2.
これら実施例1,2および比較例1,2の各化粧料について、分散状態、分散安定性、撥水性、撥油性の結果をまとめた。この結果が表2に示されている。 The results of dispersion state, dispersion stability, water repellency, and oil repellency were summarized for each of the cosmetics of Examples 1 and 2 and Comparative Examples 1 and 2. The results are shown in Table 2.
前述の表1に示される結果より、製造実施例1,2で調製された表面被覆顔料によれば、満足できる撥水撥油性が得られている。また、表2に示される結果より、実施例1のパウダーファンデーションによれば、分散状態も良く、良好な撥水撥油性を示し、ケーキングを起こすこともなく状態が安定している。また、肌への延展性も良好でしっとりとしていて粉っぽい感触とはならなかった。これに対して、比較例1のパウダーファンデーションでは、良好な撥水撥油性を示すものの、ケーキングを起こしており、良好なパウダーファンデーションとは言えない。 From the results shown in Table 1, the surface-coated pigments prepared in Production Examples 1 and 2 have satisfactory water and oil repellency. Moreover, from the results shown in Table 2, according to the powder foundation of Example 1, the dispersion state is good, the water and oil repellency is good, and the state is stable without causing caking. Moreover, the extensibility to skin was also good and it was moist and did not become a powdery touch. On the other hand, the powder foundation of Comparative Example 1 shows good water and oil repellency, but causes caking and cannot be said to be a good powder foundation.
一方、実施例2のW/Oリキッドファンデーションでは、W/Oエマルジョンの安定性、分散状態も良く、肌に塗った際に良好な撥水撥油性を示し、またしっとりとした感触を与えている。これに対して、比較例2では、W/Oエマルジョンが非常に不安定ですぐに分離を起こしてしまい、安定なW/Oリキッドファンデーションを得ることができなかった。 On the other hand, in the W / O liquid foundation of Example 2, the stability and dispersion state of the W / O emulsion are good, exhibit good water and oil repellency when applied to the skin, and give a moist feel. . On the other hand, in Comparative Example 2, the W / O emulsion was very unstable and immediately separated, and a stable W / O liquid foundation could not be obtained.
以上のように、本製造実施例の化粧料用顔料およびその化粧料用顔料を配合した本実施例の化粧料によれば、撥水撥油性に優れるとともに、化粧料への配合時にパーフルオロポリエーテル、パーフルオロデカリン、パーフルオロオクタン等のフッ素化合物系のバインダーを配合することなしに、一般に用いられている分散配合剤(例えばワセリン、ラノリン、マイクロクリスタリンワックス、カルナバロウ、キャンデリアロウ、スクワラン、流動パラフィン、エステル油、ジグリセライド、トリグリセライド、シリコン油等)にて容易に分散配合できるという優れた効果を有していると言える。 As described above, according to the cosmetic pigment of this production example and the cosmetic of this example containing the cosmetic pigment, the water- and oil-repellency is excellent, and the perfluoropoly Commonly used dispersion compounding agents (eg petrolatum, lanolin, microcrystalline wax, carnauba wax, canderia wax, squalane, fluidization, without blending fluorine compound binders such as ether, perfluorodecalin, perfluorooctane, etc. Paraffin, ester oil, diglyceride, triglyceride, silicone oil, etc.) can be said to have an excellent effect of being easily dispersible and compounded.
Claims (3)