JP2006182994A - ポリ乳酸樹脂組成物 - Google Patents
ポリ乳酸樹脂組成物 Download PDFInfo
- Publication number
- JP2006182994A JP2006182994A JP2004380707A JP2004380707A JP2006182994A JP 2006182994 A JP2006182994 A JP 2006182994A JP 2004380707 A JP2004380707 A JP 2004380707A JP 2004380707 A JP2004380707 A JP 2004380707A JP 2006182994 A JP2006182994 A JP 2006182994A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resin composition
- parts
- acid
- polylactic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 ポリ乳酸樹脂100重量部に対して、芳香族ポリカーボネート樹脂121〜200重量部、リン系難燃剤25〜55重量部、タルク10〜50重量部、フッ素系化合物0.01〜3重量部を配合してなる樹脂組成物であり、前記リン系難燃剤が芳香族縮合リン酸エステルである樹脂組成物、前記フッ素系化合物が、テトラフルオロエチレンである樹脂組成物。
【選択図】 なし
Description
繊維学会誌55(7)p.290−296(1999)
また、ポリ乳酸樹脂と芳香族ポリカーボネート樹脂の合計含量が、リン系難燃剤とタルクの合計含量に対する比を、2.5〜6とすることが好ましく、これらの条件を適用した場合には一層優れた効果の取得を期待することができる。
ポリテトラフルオロエチレンなどのフッ素系化合物の分子量は10万〜1000万の範囲のものが好ましく、とくに10万〜100万の範囲のものがより好ましい。フッ素系化合物の配合により本発明の樹脂組成物の押出成形性と難燃性にとくに効果がある。
D体の含有量が1.2%であり、PMMA換算の重量平均分子量が16万であるポリL乳酸樹脂、下記に示す芳香族ポリカーボネート樹脂、リン系難燃剤、タルク、フッ素化合物、エポキシ化合物を、それぞれ表1、表2に示した割合で混合し、30mm径の2軸押出機により、シリンダー温度235℃、回転数150rpmの条件で溶融混練を行い、樹脂組成物を得た。
B−2:芳香族ポリカーボネート樹脂(三菱瓦斯化学(株)製"S2000")
C−1:芳香族縮合リン酸エステル(大八化学工業(株)製"PX−200")
C−2:芳香族縮合リン酸エステル(旭電化(株)製"FP−700")
C−3:トリフェニルホスフェート(大八化学工業(株)製"TPP")
D−1:タルク(日本タルク(株)製"P−6"、平均粒径約4μm)
D−2:タルク(日本タルク(株)製"MS−P"、平均粒径約12μm)
E−1:テトラフルオロエチレン(三井・デュポンフロロケミカル(株)製"テフロン (登録商標)"6−J)
F−1:ビスフェノールAジグリシジルエーテル(ジャパンエポキシレジン製"エピコート"828)
○ : ほとんど変形が見られず、寸法安定性に優れる。
△ : 変形が見られる。
× : 大きく変形し、寸法安定性に問題がある。
これらの結果を表1、表2に併せて示す。
Claims (7)
- ポリ乳酸樹脂100重量部に対して、芳香族ポリカーボネート樹脂121〜200重量部、リン系難燃剤25〜55重量部、タルク10〜50重量部、フッ素系化合物0.01〜3重量部を配合してなる樹脂組成物。
- 前記リン系難燃剤が、芳香族縮合リン酸エステルである請求項1記載の樹脂組成物。
- 前記フッ素系化合物が、テトラフルオロエチレンである請求項1〜2のいずれか1項に記載の樹脂組成物。
- 前記ポリ乳酸樹脂100重量部に対して、さらにエポキシ化合物を0.01〜10重量部配合することを特徴とする請求項1〜3のいずれか1項に記載の樹脂組成物。
- 前記ポリ乳酸樹脂と前記芳香族ポリカーボネート樹脂の合計含量の、前記リン系難燃剤と前記タルクの合計含量に対する比が、2.5〜6であることを特徴とする請求項1〜4のいずれか1項に記載の樹脂組成物。
- 請求項1〜5のいずれか1項に記載の樹脂組成物からなる電子機器用筐体。
- 請求項1〜5のいずれか1項に記載の樹脂組成物からなるノートパソコン用筐体。