JP2004157459A - Planographic printing plate original plate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a positive planographic printing plate original plate capable of direct plate making by scanning exposure based on digital signals and excellent in print durability and chemical resistance. <P>SOLUTION: A recording layer consisting of a lower layer comprising a water-insoluble and alkali-soluble polyurethane resin, and an upper layer comprising a water-insoluble and alkali-soluble resin and a development inhibitor and having solubility in an alkaline aqueous solution increased by exposure is disposed on a support, wherein an IR absorbent is comprised in at least one of the lower and upper layers of the recording layer. <P>COPYRIGHT: (C)2004,JPO

Description

【００１４】
式（Ｉ）中、Ｒ^１は二価の連結基を表す。そのような二価の連結基としては、脂肪族炭化水素、脂環式炭化水素、または、芳香族炭化水素が挙げられ、好ましくは、炭素数２〜１０のアルキレン基、炭素数６〜３０のアリーレン基が挙げられる。アリーレン基としては、２つ以上の環構造が、単結合またはメチレン基などの２価の有機連結基により結合されたものや、縮合多環構造を形成したものであってもよい。また、必要に応じて、Ｒ^１は式（Ｉ）におけるイソシアネート基と反応しない他の官能基、例えばエステル、ウレタン、アミド、ウレイド基等を有していてもよい。
さらに、Ｒ^１は置換基を有していてもよく、導入可能な置換基としては、ハロゲン原子（−Ｆ、−Ｃｌ、−Ｂｒ、−Ｉ）、アルキル基、アルコキシル基、アルキルエステル基、シアノ基など、該イソシアネート基に不活性な置換基が挙げられる。
また、本発明に用いられるジイソシアネート化合物としては、上記一般式（Ｉ）で表される範囲のもの以外にも、例えば、後述するジオール化合物からなるオリゴマーまたはポリマーなどの高分子化合物の両末端に、イソシアネート基を有する高分子量のジイソシアネート化合物などを用いることもできる。
【００１５】
式（ＩＩ）中、Ｒ^２は水素原子、アルキル基、アラルキル基、アリール基、アルコキシ基、アリーロキシ基を表す。ここで、Ｒ^２は置換基を有していてもよく、導入可能な置換基としては、シアノ基、ニトロ基、ハロゲン原子（−Ｆ、−Ｃｌ、−Ｂｒ、−Ｉ）、−ＣＯＮＨ_２、−ＣＯＯＲ^６、−ＯＲ^６、−ＮＨＣＯＮＨＲ^６、−ＮＨＣＯＯＲ^６、−ＮＨＣＯＲ^６、−ＯＣＯＮＨＲ^６、−ＣＯＮＨＲ^６（ここで、Ｒ^６は炭素数１〜１０のアルキル基、炭素数７〜１５のアラルキル基を示す。）などが挙げられる。
好ましいＲ^２としては水素原子、炭素数１〜８個の無置換のアルキル基、炭素数６〜１５個の無置換のアリール基が挙げられる。
【００１６】
式（ＩＩ）または（ＩＩＩ）中、Ｒ^３、Ｒ^４、Ｒ^５はそれぞれ同一でも相異していてもよく、単結合、または二価の連結基を表す。そのような二価の連結基としては、脂肪族炭化水素、または、芳香族炭化水素が挙げられる。ここで、Ｒ^３、Ｒ^４、Ｒ^５は置換基を有していてもよく、導入可能な置換基としては、アルキル基、アラルキル基、アリール基、アルコキシ基、ハロゲン原子（−Ｆ、−Ｃｌ、−Ｂｒ、−Ｉ）などが挙げられる。
好ましいＲ^３、Ｒ^４、Ｒ^５としては、炭素数１〜２０個の無置換のアルキレン基、炭素数６〜１５個の無置換のアリーレン基が挙げられ、更に好ましいものとしては炭素数１〜８個の無置換のアルキレン基が挙げられる。また、必要に応じて、Ｒ^３、Ｒ^４、Ｒ^５は上記式（Ｉ）におけるイソシアネート基と反応しない他の官能基、例えばエステル、ウレタン、アミド、ウレイド、エーテル基を有していてもよい。
また、上記Ｒ^２、Ｒ^３、Ｒ^４、Ｒ^５は、これらのうち２つあるいは３つが互いに結合して環構造を形成していてもよい。
【００１７】
式（ＩＩＩ）中、Ａｒは置換基を有していてもよい三価の芳香族炭化水素を表し、好ましくは炭素数６〜１５個のアリーレン基を示す。
【００１８】
上記一般式（Ｉ）で示されるジイソシアネート化合物の具体例としては以下に示すものが挙げられるが、本発明はこれらに限定されるものではない。
２，４−トリレンジイソシアネート、２，４−トリレンジイソシアネートの二量体、２，６−トリレンジイソシアネート、ｐ−キシリレンジイソシアネート、メタキシリレンジイソシアネート、４，４’−ジフェニルメタンジイソシアネート、１，５−ナフチレンジイソシアネート、３，３’−ジメチルビフェニル−４，４’−ジイソシアネート等の如き芳香族ジイソシアネート化合物；ヘキサメチレンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、リジンジイソシアネート、ダイマー酸ジイソシアネート等の如き脂肪族ジイソシアネート化合物；イソホロンジイソシアネート、４，４’−メチレンビス（シクロヘキシルイソシアネート）、メチルシクロヘキサン−２，４（又は２，６）ジイソシアネート、１，３−（イソシアネートメチル）シクロヘキサン等の如き脂環族ジイソシアネート化合物；１，３−ブチレングリコール１モルとトリレンジイソシアネート２モルとの付加体等の如きジオールとジイソシアネートとの反応物であるジイソシアネート化合物等が挙げられる。
中でも、４，４’−ジフェニルメタンジイソシアネート、キシリレンジイソシアネート、トリレンジイソシアネートのような芳香族環を有するものが耐刷性の観点より好ましい。
【００１９】
また、上記一般式（ＩＩ）又は（ＩＩＩ）で示されるカルボキシル基を有するジオール化合物の具体例としては以下に示すものが挙げられるが、本発明はこれらに限定されるものではない。
３，５−ジヒドロキシ安息香酸、２，２−ビス（ヒドロキシメチル）プロピオン酸、２，２−ビス（ヒドロキシエチル）プロピオン酸、２，２−ビス（３−ヒドロキシプロピルプロピオン酸、２，２−ビス（ヒドロキシメチル）酢酸、ビス−（４−ヒドロキシフェニル）酢酸、４，４−ビス−（４−ヒドロキシフェニル）ペンタン酸、酒石酸等が挙げられる。
中でも、２，２−ビス（ヒドロキシメチル）プロピオン酸、２，２−ビス（ヒドロキシエチル）プロピオン酸がイソシアネートとの反応性の観点より好ましい。
【００２０】
なお、本発明に係るポリウレタン樹脂は、上記一般式（Ｉ）で示されるジイソシアネート化合物、および、一般式（ＩＩ）又は（ＩＩＩ）で表されるカルボキシル基を有するジオール化合物を、それぞれ２種以上用いて形成されたものであってもよい。
また、一般式（ＩＩ）又は（ＩＩＩ）で示されるカルボキシル基を有するジオール化合物の他に、カルボキシル基を有さず、且つ、式（Ｉ）中のイソシアネート基と反応しない置換基を有していてもよいジオール化合物を、アルカリ現像性を低下させない程度に併用することもできる。
【００２１】
そのようなジオール化合物の具体例としては以下に示すものが挙げられる。
例えばエチレングリコール、プロピレングリコール、ネオペンチルグリコール、１，３−ブチレングリコール、１，６−ヘキサンジオール、２−ブテン−１，４−ジオール、２，２，４−トリメチル−１，３−ペンタンジオール、１，４−ビス−β−ヒドロキシエトキシシクロヘキサン、シクロヘキサンジメタノール、トリシクロデカンジメタノール、水添ビスフェノールＡ、水添ビスフェノールＦ、ビスフェノールＡのエチレンオキサイド付加体、ビスフェノールＡのプロピレンオキサイド付加体、ビスフェノールＦのエチレンオキサイド付加体、ビスフェノールＦのプロピレンオキサイド付加体、水添ビスフェノールＡのエチレンオキサイド付加体、水添ビスフェノールＡのプロピレンオキサイド付加体、ヒドロキノンジヒドロキシエチルエーテル、ｐ−キシリレングリコール、ジヒドロキシエチルスルホン、ビス−（２−ヒドロキシエチル）−２，４−トリレンジカルバメート、２，４−トリレン−ビス−（２−ヒドロキシエチルカルバミド）、ビス−（２−ヒドロキシエチル）ｍ−キシリレンカルバメート、ビス−（２−ヒドロキシエチルフタレート等が使用できる。
【００２２】
本発明に係るポリウレタン樹脂は上記ジイソシアネート化合物およびジオール化合物を非プロトン性溶媒中、それぞれの反応性に応じた活性を有する公知の触媒を添加し、加熱することにより合成することができる。
使用するジイソシアネートおよびジオール化合物のモル比は、好ましくは０．８：１〜１．２：１であり、ポリマー末端にイソシアネート基が残存した場合、アルコール類又はアミン類等で処理することにより、最終的にイソシアネート基が残存しない形で合成される。
また、本発明に係るポリウレタン樹脂は芳香族骨格を有するものが耐薬品性の観点より好ましい。
【００２３】
本発明に係るポリウレタン樹脂の分子量は、好ましくは重量平均で１，０００以上であり、更に好ましくは５，０００〜１０万の範囲である。これらのポリウレタン樹脂は単独で用いても２種以上を混合して用いてもよい。
【００２４】
本発明に係る下層成分中に含まれるこれらのポリウレタン樹脂の含有量は、全固形分中、約５０〜９９．５質量％、好ましくは約５５〜９５質量％である。
【００２５】
さらに、本発明に係る下層成分中には、前記ポリウレタン樹脂に加えて、本発明の効果を損なわない範囲で他の樹脂を併用することができる。下層自体は、特に非画像部領域において、アルカリ可溶性を発現することを要するため、この特性を損なわない樹脂を選択する必要がある。この観点から、併用可能な樹脂としては、水不溶性且つアルカリ可溶性樹脂が挙げられる。一般的な水不溶性且つアルカリ可溶性樹脂については以下に詳述するが、なかでも、例えば、ポリアミド樹脂、エポキシ樹脂、ポリアセタール樹脂、アクリル樹脂、メタクリル樹脂、ポリスチレン系樹脂、ノボラック型フェノール系樹脂等を好ましく挙げることができる。
また、混合する量としては、前記ポリウレタン樹脂に対して５０質量％以下であることが好ましい。
【００２６】
〔水不溶性且つアルカリ可溶性樹脂及び現像抑制剤を含有し、露光によりアルカリ性水溶液に対する溶解性が増大する上層〕
本発明に係る上層は、水不溶性且つアルカリ可溶性樹脂（以下、適宜、「アルカリ可溶性樹脂」と称する）と、現像抑制剤と、を含有し、露光によりアルカリ性水溶液に対する溶解性が増大することを特徴とする。以下、本発明に係る上層の各成分について説明する。
【００２７】
（水不溶性且つアルカリ可溶性樹脂）
本発明における上層に使用可能なアルカリ可溶性樹脂としては、アルカリ性現像液に接触すると溶解する特性を有するものであれば特に制限はないが、高分子中の主鎖および／または側鎖に酸性基を含有する単独重合体、これらの共重合体、またはこれらの混合物であることが好ましい。特に、ディスクリミネーション向上の観点からは、上層成分として後述の現像抑制剤と共にノボラック樹脂を用いることが好ましい。
このような酸性基を有するアルカリ可溶性樹脂としては、特に、（１）フェノール性水酸基、（２）スルホンアミド基、（３）活性イミド基のいずれかの官能基を分子内に有する高分子化合物が挙げられる。例えば、以下のものが例示されるが、本発明はこれらに限定されるものではない。
【００２８】
（１）フェノール性水酸基を有する高分子化合物としては、例えば、フェノールホルムアルデヒド樹脂、ｍ−クレゾールホルムアルデヒド樹脂、ｐ−クレゾールホルムアルデヒド樹脂、ｍ−／ｐ−混合クレゾールホルムアルデヒド樹脂、フェノール／クレゾール（ｍ−，ｐ−，又はｍ−／ｐ−混合のいずれでもよい）混合ホルムアルデヒド樹脂等のノボラック樹脂やピロガロールアセトン樹脂が挙げられる。フェノール性水酸基を有する高分子化合物としてはこの他に、側鎖にフェノール性水酸基を有する高分子化合物を用いることが好ましい。側鎖にフェノール性水酸基を有する高分子化合物としては、フェノール性水酸基と重合可能な不飽和結合とをそれぞれ１つ以上有する低分子化合物からなる重合性モノマーを単独重合、或いは該モノマーに他の重合性モノマーを共重合させて得られる高分子化合物が挙げられる。
【００２９】
フェノール性水酸基を有する重合性モノマーとしては、フェノール性水酸基を有するアクリルアミド、メタクリルアミド、アクリル酸エステル、メタクリル酸エステル、又はヒドキシスチレン等が挙げられる。具体的にはＮ−（２−ヒドキシフェニル）アクリルアミド、Ｎ−（３−ヒドキシフェニル）アクリルアミド、Ｎ−（４−ヒドキシフェニル）アクリルアミド、Ｎ−（２−ヒドキシフェニル）メタクリルアミド、Ｎ−（３−ヒドキシフェニル）メタクリルアミド、Ｎ−（４−ヒドキシフェニル）メタクリルアミド、ｏ−ヒドキシフェニルアクリレート、ｍ−ヒドキシフェニルアクリレート、ｐ−ヒドキシフェニルアクリレート、ｏ−ヒドキシフェニルメタクリレート、ｍ−ヒドキシフェニルメタクリレート、ｐ−ヒドキシフェニルメタクリレート、ｏ−ヒドロキシスチレン、ｍ−ヒドロキシスチレン、ｐ−ヒドロキシスチレン、２−（２−ヒドロキシフェニル）エチルアクリレート、２−（３−ヒドロキシフェニル）エチルアクリレート、２−（４−ヒドロキシフェニル）エチルアクリレート、２−（２−ヒドロキシフェニル）エチルメタクリレート、２−（３−ヒドロキシフェニル）エチルメタクリレート、２−（４−ヒドロキシフェニル）エチルメタクリレート等を好適に使用することができる。かかるフェノール性水酸基を有する樹脂は、２種類以上を組み合わせて使用してもよい。更に、米国特許４，１２３，２７９号明細書に記載されているように、ｔ−ブチルフェノールホルムアルデヒド樹脂、オクチルフェノールホルムアルデヒド樹脂のような、炭素数３〜８のアルキル基を置換基として有するフェノールとホルムアルデヒドとの共重合体を併用してもよい。
【００３０】
（２）スルホンアミド基を有するアルカリ可溶性樹脂としては、スルホンアミド基を有する重合性モノマーを単独重合、或いは該モノマーに他の重合性モノマーを共重合させて得られる高分子化合物が挙げられる。スルホンアミド基を有する重合性モノマーとしては、１分子中に、窒素原子上に少なくとも１つの水素原子が結合したスルホンアミド基−ＮＨ−ＳＯ_２−と、重合可能な不飽和結合をそれぞれ１つ以上有する低分子化合物からなる重合性モノマーが挙げられる。その中でも、アクリロイル基、アリル基、又はビニロキシ基と、置換或いはモノ置換アミノスルホニル基又は置換スルホニルイミノ基とを有する低分子化合物が好ましい。
【００３１】
（３）活性イミド基を有するアルカリ可溶性樹脂は、活性イミド基を分子内に有するものが好ましく、この高分子化合物としては、１分子中に活性イミド基と重合可能な不飽和結合をそれぞれ１つ以上有する低分子化合物からなる重合性モノマーを単独重合、或いは該モノマーに他の重合性モノマーを共重合させて得られる高分子化合物が挙げられる。
このような化合物としては、具体的には、Ｎ−（ｐ−トルエンスルホニル）メタクリルアミド、Ｎ−（ｐ−トルエンスルホニル）アクリルアミド等を好適に使用することができる。
【００３２】
本発明に係るアルカリ可溶性樹脂としては、前記フェノール性水酸基を有する重合性モノマー、スルホンアミド基を有する重合性モノマー、及び活性イミド基を有する重合性モノマーのうち２種類以上を重合させた高分子化合物であることが好ましい。上記重合性モノマーの共重合比、および重合性モノマーの組み合わせに制限はないが、特にフェノール性水酸基を有する重合性モノマーに、スルホンアミド基を有する重合性モノマー及び／又は活性イミド基を有する重合性モノマーを共重合させる場合には、これら成分の配合重合比は５０：５０から５：９５の範囲にあることが好ましく、４０：６０から１０：９０の範囲にあることが特に好ましい。
【００３３】
更に、本発明に係るアルカリ可溶性樹脂としては、上記フェノール性水酸基を有する重合性モノマー、スルホンアミド基を有する重合性モノマー、又は活性イミド基を有する重合性モノマーから選択される１種或いは２種類以上の重合性モノマーの他に、他の重合性モノマーを共重合させて得られる高分子化合物であることが好ましい。この場合の共重合比としては、アルカリ可溶性を付与するモノマーを１０モル％以上含むことが好ましく、２０モル％以上含むものがより好ましい。アルカリ可溶性を付与するモノマーの共重合成分が１０モル％より少ないと、アルカリ可溶性が不十分となりやすく、現像性が低下する傾向にある。
ここで使用可能な他の重合性モノマーとしては、下記（ｍ１）〜（ｍ１２）に挙げる化合物を例示することができるが、本発明はこれらに限定されるものではない。
【００３４】
（ｍ１）２−ヒドロキシエチルアクリレート又は２−ヒドロキシエチルメタクリレート等の脂肪族水酸基を有するアクリル酸エステル類、及びメタクリル酸エステル類。
（ｍ２）アクリル酸メチル、アクリル酸エチル、アクリル酸プロピル、アクリル酸ブチル、アクリル酸アミル、アクリル酸ヘキシル、アクリル酸オクチル、アクリル酸ベンジル、アクリル酸−２−クロロエチル、グリシジルアクリレート、等のアルキルアクリレート。
（ｍ３）メタクリル酸メチル、メタクリル酸エチル、メタクリル酸プロピル、メタクリル酸ブチル、メタクリル酸アミル、メタクリル酸ヘキシル、メタクリル酸シクロヘキシル、メタクリル酸ベンジル、メタクリル酸−２−クロロエチル、グリシジルメタクリレート等のアルキルメタクリレート。
（ｍ４）アクリルアミド、メタクリルアミド、Ｎ−メチロールアクリルアミド、Ｎ−エチルアクリルアミド、Ｎ−ヘキシルメタクリルアミド、Ｎ−シクロヘキシルアクリルアミド、Ｎ−ヒドロキシエチルアクリルアミド、Ｎ−フェニルアクリルアミド、Ｎ−ニトロフェニルアクリルアミド、Ｎ−エチル−Ｎ−フェニルアクリルアミド等のアクリルアミド若しくはメタクリルアミド。
【００３５】
（ｍ５）エチルビニルエーテル、２−クロロエチルビニルエーテル、ヒドロキシエチルビニルエーテル、プロピルビニルエーテル、ブチルビニルエーテル、オクチルビニルエーテル、フェニルビニルエーテル等のビニルエーテル類。
（ｍ６）ビニルアセテート、ビニルクロロアセテート、ビニルブチレート、安息香酸ビニル等のビニルエステル類。
（ｍ７）スチレン、α−メチルスチレン、メチルスチレン、クロロメチルスチレン等のスチレン類。
（ｍ８）メチルビニルケトン、エチルビニルケトン、プロピルビニルケトン、フェニルビニルケトン等のビニルケトン類。
（ｍ９）エチレン、プロピレン、イソブチレン、ブタジエン、イソプレン等のオレフィン類。
（ｍ１０）Ｎ−ビニルピロリドン、アクリロニトリル、メタクリロニトリル等。
（ｍ１１）マレイミド、Ｎ−アクリロイルアクリルアミド、Ｎ−アセチルメタクリルアミド、Ｎ−プロピオニルメタクリルアミド、Ｎ−（ｐ−クロロベンゾイル）メタクリルアミド等の不飽和イミド。
（ｍ１２）アクリル酸、メタクリル酸、無水マレイン酸、イタコン酸等の不飽和カルボン酸。
【００３６】
本発明に係るアルカリ可溶性樹脂が、前記フェノール性水酸基を有する重合性モノマー、スルホンアミド基を有する重合性モノマー、又は活性イミド基を有する重合性モノマーの単独重合体或いは共重合体の場合、重量平均分子量が２，０００以上、数平均分子量が５００以上のものが好ましい。更に好ましくは、重量平均分子量が５，０００〜３００，０００で、数平均分子量が８００〜２５０，０００であり、分散度（重量平均分子量／数平均分子量）が１．１〜１０のものである。
特に、本発明に係るアルカリ可溶性樹脂が、フェノールホルムアルデヒド樹脂、または、クレゾールアルデヒド樹脂等である場合には、重量平均分子量が５００〜２０，０００であり、数平均分子量が２００〜１０，０００のものが好ましい。
【００３７】
本発明に用いられるアルカリ可溶性樹脂としては、未露光部において強い水素結合性を生起し、露光部において一部の水素結合が容易に解除されるといった点から、フェノール性水酸基を有する樹脂が望ましく、フェノール性水酸基を有する樹脂の中でも特に好ましくはノボラック樹脂である。
また、本発明においては、アルカリ性水溶液に対し溶解速度の異なる２種類以上のアルカリ可溶性樹脂を混合して用いてもよく、その場合の混合比は自由である。なお、該フェノール性水酸基を有する樹脂と混合するのに好適なアルカリ可溶性樹脂としては、フェノール性水酸基を有する樹脂と相溶性が低いことから、アクリル樹脂であることが好ましく、更に好ましくはスルホアミド基を有するアクリル樹脂である。
【００３８】
本発明に係る上層の全固形分中に対するアルカリ可溶性樹脂の含有量は、併せて５０〜９８質量％の添加量で用いられる。アルカリ可溶性樹脂の添加量が５０質量％未満であると記録層の耐久性が悪化し、また、９８質量％を超えると感度、耐久性の両面で好ましくない。
【００３９】
〔現像抑制剤〕
本発明に係る上層には、そのインヒビション（溶解抑制能）を高める目的で、現像抑制剤を含有させる必要がある。
本発明に係る現像抑制剤としては、前記アルカリ可溶性樹脂と相互作用を形成し、未露光部においては該アルカリ可溶性樹脂の現像液に対する溶解性を実質的に低下させ、且つ、露光部においては該相互作用が弱まり、現像液に対して可溶となり得るものであれば特に限定はされないが、特に４級アンモニウム塩、ポリエチレングリコール系化合物等が好ましく用いられる。また後述する赤外線吸収剤、画像着色剤のなかにも現像抑制剤として機能する化合物があり、それらもまた好ましく挙げられる。
【００４０】
４級アンモニウム塩としては、特に限定されないが、テトラアルキルアンモニウム塩、トリアルキルアリールアンモニウム塩、ジアルキルジアリールアンモニウム塩、アルキルトリアリールアンモニウム塩、テトラアリールアンモニウム塩、環状アンモニウム塩、二環状アンモニウム塩が挙げられる。
具体的には、テトラブチルアンモニウムブロミド、テトラペンチルアンモニウムブロミド、テトラヘキシルアンモニウムブロミド、テトラオクチルアンモニウムブロミド、テトララウリルアンモニウムブロミド、テトラフェニルアンモニウムブロミド、テトラナフチルアンモニウムブロミド、テトラブチルアンモニウムクロリド、テトラブチルアンモニウムヨージド、テトラステアリルアンモニウムブロミド、ラウリルトリメチルアンモニウムブロミド、ステアリルトリメチルアンモニウムブロミド、ベヘニルトリメチルアンモニウムブロミド、ラウリルトリエチルアンモニウムブロミド、フェニルトリメチルアンモニウムブロミド、３−トリフルオロメチルフェニルトリメチルアンモニウムブロミド、ベンジルトリメチルアンモニウムブロミド、ジベンジルジメチルアンモニウムブロミド、ジステアリルジメチルアンモニウムブロミド、トリステアリルメチルアンモニウムブロミド、ベンジルトリエチルアンモニウムブロミド、ヒドロキシフェニルトリメチルアンモニウムブロミド、Ｎ−メチルピリジニウムブロミド等が挙げられる。特に特願２００１−２２６２９７号、特願２００１−３７００５９、特願２００１−３９８０４７明細書記載の４級アンモニウム塩が好ましい。
【００４１】
４級アンモニウム塩の添加量は上層全固形分に対して０．１〜５０質量％であることが好ましく、１〜３０質量％であることがより好ましい。０．１質量％未満では現像抑制効果が少なくなり好ましくない。また、５０質量％を超えて添加した場合は、前記アルカリ可溶性樹脂の製膜性に悪影響を与えることがある。
【００４２】
また、ポリエチレングリコール化合物としては、特に限定されないが、下記一般式（１）で表される構造のものが挙げられる。
Ｒ^１−｛−Ｏ−（Ｒ^３−Ｏ−）_ｍ−Ｒ^２｝_ｎ ・・・一般式（１）
上記一般式（１）中、Ｒ^１は多価アルコール残基又は多価フェノール残基を表し、Ｒ^２は水素原子、置換基を有していても良い炭素原子数１〜２５のアルキル基、アルケニル基、アルキニル基、アルキロイル基、アリール基又はアリーロイル基を表す。Ｒ^３は置換基を有しても良いアルキレン残基を表し、ｍは平均で１０以上、ｎは１以上４以下の整数を表す。
【００４３】
上記一般式（１）で表されるポリエチレングリコール化合物の例としては、ポリエチレングリコール類、ポリプロピレングリコール類、ポリエチレングリコールアルキルエーテル類、ポリプロピレングリコールアルキルエーテル類、ポリエチレングリコールアリールエーテル類、ポリプロピレングリコールアリールエーテル類、ポリエチレングリコールアルキルアリールエーテル類、ポリプロピレングリコールアルキルアリールエーテル類、ポリエチレングリコールグリセリンエステル、ポリプロピレングリコールグリセリンエステル類、ポリエチレンソルビトールエステル類、ポリプロピレングリコールソルビトールエステル類、ポリエチレングリコール脂肪酸エステル類、ポリプロピレングリコール脂肪酸エステル類、ポリエチレングリコール化エチレンジアミン類、ポリプロピレングリコール化エチレンジアミン類、ポリエチレングリコール化ジエチレントリアミン類、ポリプロピレングリコール化ジエチレントリアミン類が挙げられる。
【００４４】
さらにこれらの具体例としては、ポリエチレングリコール１０００、ポリエチレングリコール２０００、ポリエチレングリコール４０００、ポリエチレングリコール１００００、ポリエチレングリコール２００００、ポリエチレングリコール５０００、ポリエチレングリコール１０００００、ポリエチレングリコール２０００００、ポリエチレングリコール５０００００、ポリプロピレングリコール１５００、ポリプロピレングリコール３０００、ポリプロピレングリコール４０００、ポリエチレングリコールメチルエーテル、ポリエチレングリコールエチルエーテル、ポリエチレングリコールフェニルエーテル、ポリエチレングリコールジメチルエーテル、ポリエチレングリコールジエチルエーテル、ポリエチレングリコールジフェニルエーテル、ポリエチレングリコールラウリルエーテル、ポリエチレングリコールジラウリルエーテル、ポリエチレングリコールノニルエーテル、ポリエチレングリコールセチルエーテル、ポリエチレングリコールステアリルエーテル、ポリエチレングリコールジステアリルエーテル、ポリエチレングリコールベヘニルエーテル、ポリエチレングリコールジベヘニルエーテル、ポリプロピレングリコールメチルエーテル、ポリプロピレングリコールエチルエーテル、ポリプロピレングリコールフェニルエーテル、ポリプロピレングリコールジメチルエーテル、ポリプロピレングリコールジエチルエーテル、ポリプロピレングリコールジフェニルエーテル、ポリプロピレングリコールラウリルエーテル、ポリプロピレングリコールジラウリルエーテル、ポリプロピレングリコールノニルエーテル、ポリエチレングリコールアセチルエステル、ポリエチレングリコールジアセチルエステル、ポリエチレングリコール安息香酸エステル、ポリエチレングリコールラウリルエステル、ポリエチレングリコールジラウリルエステル、ポリエチレングリコールノニル酸エステル、ポリエチレングリコールセチル酸エステル、ポリエチレングリコールステアロイルエステル、ポリエチレングリコールジステアロイルエステル、ポリエチレングリコールベヘン酸エステル、ポリエチレングリコールジベヘン酸エステル、ポリプロピレングリコールアセチルエステル、ポリプロピレングリコールジアセチルエステル、ポリプロピレングリコール安息香酸エステル、ポリプロピレングリコールジ安息香酸エステル、ポリプロピレングリコールラウリル酸エステル、ポリプロピレングリコールジラウリル酸エステル、ポリプロピレングリコールノニル酸エステル、ポリエチレングリコールグリセリンエーテル、ポリプロピレングリコールグリセリンエーテル、ポリエチレングリコールソルビトールエーテル、ポリプロピレングリコールソルビトールエーテル、ポリエチレングリコール化エチレンジアミン、ポリプロピレングリコール化エチレンジアミン、ポリエチレングリコール化ジエチレントリアミン、ポリプロピレングリコール化ジエチレントリアミン、ポリエチレングリコール化ペンタメチレンヘキサミンが挙げられる。
【００４５】
ポリエチレングリコール系化合物の添加量は上層全固形分に対して０．１〜５０質量％であることが好ましく、１〜３０質量％であることがより好ましい。０．１質量％未満では現像抑制効果が少なく好ましくない。また５０質量％を超える量を添加した場合、前記アルカリ可溶性樹脂と相互作用できないポリエチレングリコール化合物が現像液の浸透を促進し、画像形成性へ悪影響を与えることがある。
【００４６】
また、このようなインヒビション（溶解抑制能）を高めるための施策を行った場合、感度の低下が生じるが、この場合、上層中にラクトン化合物を添加することが感度低下の抑制に有効である。このラクトン化合物は、露光部、即ち、インヒビションが解除された領域の記録層中に現像液が浸透する際、現像液とラクトン化合物が反応し、新たにカルボン酸化合物が発生して、露光部領域の記録層の溶解を促進させることにより感度が向上するものと考えられる。なお、未露光部では、このラクトン化合物はアルカリ可溶性樹脂中の極性基、例えば、ノボラック樹脂中の水酸基と相互作用を形成しており、また、環を有する嵩高な構造とあいまって膜中に安定に存在するため、未露光部表面においてはアルカリ現像液が接触しても、現像処理中におけるラクトン環の急激な開環反応が抑制されているため、当該領域の耐現像性が低下することはない。この相互作用は露光或いは加熱により、前記溶解抑制剤による抑制作用よりもさらに容易に解除されるため、露光部におけるラクトン化合物の開環反応は速やかに行われる。
このようなラクトン化合物としては、特に限定されないが、下記一般式（Ｌ−Ｉ）及び一般式（Ｌ−ＩＩ）で表される化合物が挙げられる。
【００４７】
【化２】

【００４８】
一般式（Ｌ−Ｉ）及び一般式（Ｌ−ＩＩ）において、Ｘ^１、Ｘ^２、Ｘ^３及びＸ^４は、環を構成する２価の非金属原子又は非金属原子団であって、それぞれ同じでも異なっていてもよい。また、これらはそれぞれ独立に置換基を有していてもよい。さらに、一般式（Ｌ−Ｉ）におけるＸ^１、Ｘ^２及びＸ^３の少なくとも一つ、及び、一般式（Ｌ−ＩＩ）におけるＸ^１、Ｘ^２、Ｘ^３及びＸ^４の少なくとも一つは、電子吸引性置換基又は電子吸引性基で置換された置換基であることが好ましい。
【００４９】
好ましい非金属原子又は非金属原子団は、メチレン基、スルフィニル基、カルボニル基、チオカルボニル基、スルホニル基、硫黄原子、酸素原子及びセレニウム原子から選ばれる原子又は原子団であって、より好ましくは、メチレン基、カルボニル基及びスルホニル基から選ばれる原子団である。
【００５０】
また、本明細書において電子吸引性置換基とは、ハメットの置換基定数σｐが正の価を取る基を指す。ハメットの置換基定数に関しては、Ｊｏｕｒｎａｌ ｏｆ Ｍｅｄｉｃｉｎａｌ Ｃｈｅｍｉｓｔｒｙ，１９７３，Ｖｏｌ．１６，Ｎｏ．１１，１２０７−１２１６等を参考にすることができる。ハメットの置換基定数σｐが正の価を取る電子吸引性基としては、例えばハロゲン原子［フッ素原子（σｐ値：０．０６）、塩素原子（σｐ値：０．２３）、臭素原子（σｐ値：０．２３）、ヨウ素原子（σｐ値：０．１８）］、トリハロアルキル基［トリブロモメチル（σｐ値：０．２９）、トリクロロメチル（σｐ値：０．３３）、トリフルオロメチル（σｐ値：０．５４）］、シアノ基（σｐ値：０．６６）、ニトロ基（σｐ値：０．７８）、脂肪族・アリールもしくは複素環スルホニル基［例えば、メタンスルホニル（σｐ値：０．７２）］、脂肪族・アリールもしくは複素環アシル基［例えば、アセチル（σｐ値：０．５０）、ベンゾイル（σｐ値：０．４３）］、アルキニル基［例えば、Ｃ≡ＣＨ（σｐ値：０．２３）］、脂肪族・アリールもしくは複素環オキシカルボニル基［例えば、メトキシカルボニル（σｐ値：０．４５）、フェノキシカルボニル（σｐ値：０．４４）］、カルバモイル基（σｐ値：０．３６）、スルファモイル基（σｐ値：０．５７）、スルホキシド基、ヘテロ環基、オキソ基、ホスホリル基等が挙げられる。
【００５１】
また、好ましい電子吸引性基としては、アミド基、アゾ基、ニトロ基、炭素数１〜５のフルオロアルキル基、ニトリル基、炭素数１〜５のアルコキシカルボニル基、炭素数１〜５のアシル基、炭素数１〜９のアルキルスルホニル基、炭素数６〜９のアリールスルホニル基、炭素数１〜９のアルキルスルフィニル基、炭素数６〜９のアリールスルフィニル基、炭素数６〜９のアリールカルボニル基、チオカルボニル基、炭素数１〜９の含フッ素アルキル基、炭素数６〜９の含フッ素アリール基、炭素数３〜９の含フッ素アリル基、オキソ基及びハロゲン元素から選ばれる基が挙げられ、より好ましくは、ニトロ基、炭素数１〜５のフルオロアルキル基、ニトリル基、炭素数１〜５のアルコキシカルボニル基、炭素数１〜５のアシル基、炭素数６〜９のアリールスルホニル基、炭素数６〜９のアリールカルボニル基、オキソ基及びハロゲン元素から選ばれる基である。
以下に、一般式（Ｌ−Ｉ）及び一般式（Ｌ−ＩＩ）で表される化合物の具体例を示すが、本発明はこれらの化合物に限定されるものではない。
【００５２】
【化３】

【００５３】
【化４】

【００５４】
一般式（Ｌ−Ｉ）及び一般式（Ｌ−ＩＩ）で表される化合物の添加量は、上層全固形分に対して０．１〜５０質量％が好ましく、さらには、１〜３０質量％がより好ましい。０．１質量％未満では効果が少なく、５０質量％を超えて添加した場合、画像形成性が劣る。
本発明に用いられるラクトン化合物は、いずれか１種を用いても、２種以上を併用してもよい。また２種類以上の一般式（Ｌ−Ｉ）の化合物、又は２種類以上の一般式（Ｌ−ＩＩ）の化合物を用いる場合、合計添加量が上記範囲内であれば任意の比率で併用することができる。
【００５５】
そのほか、オニウム塩、ｏ−キノンジアジド化合物、芳香族スルホン化合物、芳香族スルホン酸エステル化合物等の、熱分解性であり、且つ、分解しない状態では、アルカリ可溶性樹脂の溶解性を実質的に低下させる物質を併用することが画像部の現像液へのインヒビションの向上を図る点で好ましい。
【００５６】
本発明において用いられるオニウム塩としては、ジアゾニウム塩、アンモニウム塩、ホスホニウム塩、ヨードニウム塩、スルホニウム塩、セレノニウム塩、アルソニウム塩等を挙げられ、特に好適なものとしては、例えば、Ｓ．Ｉ．Ｓｃｈｌｅｓｉｎｇｅｒ，Ｐｈｏｔｏｇｒ．Ｓｃｉ．Ｅｎｇ．，１８，３８７（１９７４）、Ｔ．Ｓ．Ｂａｌｅｔ ａｌ，Ｐｏｌｙｍｅｒ，２１，４２３（１９８０）、特開平５−１５８２３０号公報に記載のジアゾニウム塩、米国特許第４，０６９，０５５号、同４，０６９，０５６号、特開平３−１４０１４０号の明細書に記載のアンモニウム塩、Ｄ．Ｃ．Ｎｅｃｋｅｒ ｅｔ ａｌ，Ｍａｃｒｏｍｏｌｅｃｕｌｅｓ，１７，２４６８（１９８４）、Ｃ．Ｓ．Ｗｅｎ ｅｔ ａｌ，Ｔｅｈ，Ｐｒｏｃ．Ｃｏｎｆ．Ｒａｄ．Ｃｕｒｉｎｇ ＡＳＩＡ，ｐ４７８ Ｔｏｋｙｏ，Ｏｃｔ（１９８８）、米国特許第４，０６９，０５５号、同４，０６９，０５６号に記載のホスホニウム塩、
【００５７】
Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｍａｃｒｏｍｏｒｅｃｕｌｅｓ，１０（６），１３０７（１９７７）、Ｃｈｅｍ．＆Ｅｎｇ．Ｎｅｗｓ，Ｎｏｖ．２８，ｐ３１（１９８８）、欧州特許第１０４，１４３号、米国特許第５，０４１，３５８号、同第４，４９１，６２８号、特開平２−１５０８４８号、特開平２−２９６５１４号に記載のヨードニウム塩、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｐｏｌｙｍｅｒ Ｊ．１７，７３（１９８５）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏｅｔ ａｌ．Ｊ．Ｏｒｇ．Ｃｈｅｍ．，４３，３０５５（１９７８）、Ｗ．Ｒ．Ｗａｔｔ ｅｔ ａｌ，Ｊ．Ｐｏｌｙｍｅｒ Ｓｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，２２，１７８９（１９８４）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｐｏｌｙｍｅｒ Ｂｕｌｌ．，１４，２７９（１９８５）、
【００５８】
Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｍａｃｒｏｍｏｒｅｃｕｌｅｓ，１４（５），１１４１（１９８１）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｊ．Ｐｏｌｙｍｅｒ Ｓｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，１７，２８７７（１９７９）、欧州特許第３７０，６９３号、同２３３，５６７号、同２９７，４４３号、同２９７，４４２号、米国特許第４，９３３，３７７号、同３，９０２，１１４号、同４，４９１，６２８号、同４，７６０，０１３号、同４，７３４，４４４号、同２，８３３，８２７号、独国特許第２，９０４，６２６号、同３，６０４，５８０号、同３，６０４，５８１号に記載のスルホニウム塩、
【００５９】
Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｍａｃｒｏｍｏｒｅｃｕｌｅｓ，１０（６），１３０７（１９７７）、Ｊ．Ｖ．Ｃｒｉｖｅｌｌｏ ｅｔ ａｌ，Ｊ．Ｐｏｌｙｍｅｒ Ｓｃｉ．，Ｐｏｌｙｍｅｒ Ｃｈｅｍ．Ｅｄ．，１７，１０４７（１９７９）に記載のセレノニウム塩、Ｃ．Ｓ．Ｗｅｎ ｅｔ ａｌ，Ｔｅｈ，Ｐｒｏｃ．Ｃｏｎｆ．Ｒａｄ．Ｃｕｒｉｎｇ ＡＳＩＡ，ｐ４７８ Ｔｏｋｙｏ，Ｏｃｔ（１９８８）に記載のアルソニウム塩等があげられる。
このようなオニウム塩のなかでも、ジアゾニウム塩が特に好ましい。また、特に好適なジアゾニウム塩としては特開平５−１５８２３０号公報記載のものがあげられる。
【００６０】
オニウム塩の対イオンとしては、四フッ化ホウ酸、六フッ化リン酸、トリイソプロピルナフタレンスルホン酸、５−ニトロ−ｏ−トルエンスルホン酸、５−スルホサリチル酸、２，５−ジメチルベンゼンスルホン酸、２，４，６−トリメチルベンゼンスルホン酸、２−ニトロベンゼンスルホン酸、３−クロロベンゼンスルホン酸、３−ブロモベンゼンスルホン酸、２−フルオロカプリルナフタレンスルホン酸、ドデシルベンゼンスルホン酸、１−ナフトール−５−スルホン酸、２−メトキシ−４−ヒドロキシ−５−ベンゾイル−ベンゼンスルホン酸、及びパラトルエンスルホン酸等を挙げることができる。これらの中でも特に六フッ化リン酸、トリイソプロピルナフタレンスルホン酸や２，５−ジメチルベンゼンスルホン酸のごときアルキル芳香族スルホン酸が好適である。
【００６１】
好適なキノンジアジド類としてはｏ−キノンジアジド化合物を挙げることができる。本発明に用いられるｏ−キノンジアジド化合物は、少なくとも１個のｏ−キノンジアジド基を有する化合物で、熱分解によりアルカリ可溶性を増すものであり、種々の構造の化合物を用いることができる。つまり、ｏ−キノンジアジドは熱分解により現像抑制剤としてのインヒビションを失うことと、ｏ−キノンジアジド自身がアルカリ可溶性の物質に変化することの両方の効果により上層の溶解性を助ける。
そのようなｏ−キノンジアジド化合物としては、例えば、Ｊ．コーサー著「ライト−センシティブ・システムズ」（Ｊｏｈｎ Ｗｉｌｅｙ＆Ｓｏｎｓ．Ｉｎｃ．）第３３９〜３５２頁に記載の化合物が使用できるが、特に種々の芳香族ポリヒドロキシ化合物あるいは芳香族アミノ化合物と反応させたｏ−キノンジアジドのスルホン酸エステル又はスルホン酸アミドが好適である。また、特公昭４３−２８４０３号公報に記載されているようなベンゾキノン（１，２）−ジアジドスルホン酸クロライド又はナフトキノン−（１、２）−ジアジド−５−スルホン酸クロライドとピロガロール−アセトン樹脂とのエステル、米国特許第３，０４６，１２０号及び同第３，１８８，２１０号に記載されているベンゾキノン−（１，２−ジアジドスルホン酸クロライド又はナフトキノン−（１，２）−ジアジド−５スルホン酸クロライドとフェノール−ホルムアルデヒド樹脂とのエステルも好適に使用される。
【００６２】
さらにナフトキノン−（１，２）−ジアジド−４−スルホン酸クロライドとフェノールホルムアルデヒド樹脂あるいはクレゾール−ホルムアルデヒド樹脂とのエステル、ナフトキノン−（１，２）−ジアジド−４−スルホン酸クロライドとピロガロール−アセトン樹脂とのエステルも同様に好適に使用される。その他の有用なｏ−キノンジアジド化合物としては、数多くの特許に報告され知られている。例えば特開昭４７−５３０３号、特開昭４８−６３８０２号、特開昭４８−６３８０３号、特開昭４８−９６５７５号、特開昭４９−３８７０１号、特開昭４８−１３３５４号、特公昭４１−１１２２２号、特公昭４５−９６１０号、特公昭４９−１７４８１号、米国特許第２，７９７，２１３号、同第３，４５４，４００号、同第３，５４４，３２３号、同第３，５７３，９１７号、同第３，６７４，４９５号、同第３，７８５，８２５号、英国特許第１，２２７，６０２号、同第１，２５１，３４５号、同第１，２６７，００５号、同第１，３２９，８８８号、同第１，３３０，９３２号、ドイツ特許第８５４，８９０号などの各明細書中に記載されているものをあげることができる。
【００６３】
ｏ−キノンジアジド化合物の添加量は好ましくは上層全固形分に対し、１〜５０質量％、更に好ましくは５〜３０質量％、特に好ましくは１０〜３０質量％の範囲である。これらの化合物は単一で使用できるが、数種の混合物として使用してもよい。
また特開平１１−２８８０８９号記載の少なくとも一部がエステル化されたアルカリ可溶性樹脂を含んでも良い。
【００６４】
また、記録層表面のインヒビションの強化とともに表面のキズに対する抵抗力を強化する目的で、特開２０００−１８７３１８号に記載されているような、分子中に炭素数３〜２０のパーフルオロアルキル基を２又は３個有する（メタ）アクリレート単量体を重合成分とする重合体を併用すること好ましい。
添加量としては、上層全固形分に対し、０．１〜１０質量％が好ましく、より好ましくは０．５〜５質量％である。
【００６５】
〔赤外線吸収剤〕
本発明の平版印刷版原版には、記録層の下層および上層の少なくとも一方に、赤外線吸収剤を添加する必要がある。そのような赤外線吸収剤としては、赤外光を吸収し熱を発生する染料であれば特に制限はなく、赤外線吸収剤として知られる種々の染料を用いることができる。
【００６６】
本発明に係る赤外線吸収剤としては、市販の染料及び文献（例えば「染料便覧」有機合成化学協会編集、昭和４５年刊）に記載されている公知のものが利用できる。具体的には、アゾ染料、金属錯塩アゾ染料、ピラゾロンアゾ染料、アントラキノン染料、フタロシアニン染料、カルボニウム染料、キノンイミン染料、メチン染料、シアニン染料などの染料が挙げられる。本発明において、これらの染料のうち赤外光、もしくは近赤外光を吸収するものが、赤外光もしくは近赤外光を発光するレーザでの利用に適する点で特に好ましい。
【００６７】
そのような赤外光、もしくは近赤外光を吸収する染料としては例えば特開昭５８−１２５２４６号、特開昭５９−８４３５６号、特開昭５９−２０２８２９号、特開昭６０−７８７８７号等に記載されているシアニン染料、特開昭５８−１７３６９６号、特開昭５８−１８１６９０号、特開昭５８−１９４５９５号等に記載されているメチン染料、特開昭５８−１１２７９３号、特開昭５８−２２４７９３号、特開昭５９−４８１８７号、特開昭５９−７３９９６号、特開昭６０−５２９４０号、特開昭６０−６３７４４号等に記載されているナフトキノン染料、特開昭５８−１１２７９２号等に記載されているスクワリリウム色素、英国特許４３４，８７５号記載のシアニン染料等を挙げることができる。
【００６８】
また、染料として米国特許第５，１５６，９３８号記載の近赤外吸収増感剤も好適に用いられ、また、米国特許第３，８８１，９２４号記載の置換されたアリールベンゾ（チオ）ピリリウム塩、特開昭５７−１４２６４５号（米国特許第４，３２７，１６９号）記載のトリメチンチアピリリウム塩、特開昭５８−１８１０５１号、同５８−２２０１４３号、同５９−４１３６３号、同５９−８４２４８号、同５９−８４２４９号、同５９−１４６０６３号、同５９−１４６０６１号に記載されているピリリウム系化合物、特開昭５９−２１６１４６号記載のシアニン色素、米国特許第４，２８３，４７５号に記載のペンタメチンチオピリリウム塩等や特公平５−１３５１４号、同５−１９７０２号公報に開示されているピリリウム化合物等が、市販品としては、エポリン社製のＥｐｏｌｉｇｈｔ ＩＩＩ−１７８、Ｅｐｏｌｉｇｈｔ ＩＩＩ−１３０、Ｅｐｏｌｉｇｈｔ ＩＩＩ−１２５等が、特に好ましく用いられる。
また、染料として特に好ましい別の例として米国特許第４，７５６，９９３号明細書中に式（Ｉ）、（ＩＩ）として記載されている近赤外吸収染料を挙げることができる。
【００６９】
これらの赤外線吸収剤は、感度の観点から記録層の上層或いはその近傍に添加することが好ましい。特にシアニン色素の如き溶解抑制能を有するものを、前記アルカリ可溶性樹脂とともに添加すると、高感度化と同時に、未露光部に耐アルカリ溶解性を持たせることができる。また、これらの赤外線吸収剤は、下層に添加しても上下層双方に添加してもよい。下層に添加することでさらに高感度化することが可能である。上層と下層の双方に赤外線吸収剤を添加する場合には、互いに同じ化合物を用いてもよく、また異なる化合物を用いてもよい。
また、これらの赤外線吸収剤は記録層と同一の層に添加してもよいし、別の層を設けそこへ添加してもよい。別の層とする場合、記録層に隣接する層へ添加するのが望ましい。
さらに、赤外線吸収剤が溶解抑制能を有する化合物である場合には、前記アルカリ可溶性樹脂と同一の層に含まれることにより、該赤外線吸収剤が光熱変換機能のみならず、前記現像抑制剤としても機能するため好ましい。
【００７０】
赤外線吸収剤の添加量としては、上層に添加する場合、上層全固形分に対し０．０１〜５０質量％、好ましくは０．１〜３０質量％、特に好ましくは１．０〜３０質量％の割合で添加することができる。添加量が０．０１質量％未満であると感度が低くなり、また５０質量％を超えると上部記録層の均一性が失われ、上部記録層の耐久性が悪くなる。
【００７１】
また、下層に添加する場合、下層全固形分に対し０〜２０質量％、好ましくは０〜１０質量％、特に好ましくは０〜５質量％の割合で添加することができる。下層に赤外線吸収剤を添加する場合、溶解抑制能を有する赤外線吸収剤を用いると下層の溶解性が低下するが、一方、赤外線吸収剤が赤外線レーザ露光時に発熱し、熱による下層の溶解性向上が期待できるため、これらのバランスを考慮して添加する化合物及び添加量を選択すべきである。なお、支持体近傍の０．２〜０．３μｍの領域では露光時に発生した熱が支持体に拡散するなどして、熱による溶解性向上効果が得難く、赤外吸収染料添加による下層の溶解性低下が感度を低下させる要因となる場合がある。従って、先に示した添加量の範囲の中においても、下層の現像液（２５℃〜３０℃）に対する溶解速度が３０ｎｍ／ｓｅｃを下回る如き添加量は好ましくない。
【００７２】
〔その他の添加剤〕
前記記録層の下層および上層を形成するにあたっては、上記の必須成分の他、本発明の効果を損なわない限りにおいて、更に必要に応じて、種々の添加剤を添加することができる。以下に挙げる添加剤は下層のみに添加してもよいし、上層のみに添加してもよいし、両方の層に添加してもよい。
【００７３】
（現像促進剤）
本発明に係る記録層である上層および／または下層には、感度を向上させる目的で、酸無水物類、フェノール類、有機酸類を添加してもよい。
酸無水物類としては環状酸無水物が好ましく、具体的に環状酸無水物としては米国特許第４，１１５，１２８号明細書に記載されている無水フタル酸、テトラヒドロ無水フタル酸、ヘキサヒドロ無水フタル酸、３，６−エンドオキシ−テトラヒドロ無水フタル酸、テトラクロル無水フタル酸、無水マレイン酸、クロル無水マレイン酸、α−フェニル無水マレイン酸、無水コハク酸、無水ピロメリット酸などが使用できる。非環状の酸無水物としては無水酢酸などが挙げられる。
【００７４】
フェノール類としては、ビスフェノールＡ、２，２′−ビスヒドロキシスルホン、ｐ−ニトロフェノール、ｐ−エトキシフェノール、２，４，４’−トリヒドロキシベンゾフェノン、２，３，４−トリヒドロキシベンゾフェノン、４−ヒドロキシベンゾフェノン、４，４’，４”−トリヒドロキシトリフェニルメタン、４，４’，３”，４”−テトラヒドロキシ−３，５，３’，５’−テトラメチルトリフェニルメタンなどが挙げられる。
【００７５】
有機酸類としては、特開昭６０−８８９４２号、特開平２−９６７５５号公報などに記載されている、スルホン酸類、スルフィン酸類、アルキル硫酸類、ホスホン酸類、リン酸エステル類及びカルボン酸類などがあり、具体的には、ｐ−トルエンスルホン酸、ドデシルベンゼンスルホン酸、ｐ−トルエンスルフィン酸、エチル硫酸、フェニルホスホン酸、フェニルホスフィン酸、リン酸フェニル、リン酸ジフェニル、安息香酸、イソフタル酸、アジピン酸、ｐ−トルイル酸、３，４−ジメトキシ安息香酸、フタル酸、テレフタル酸、４−シクロヘキセン−１，２−ジカルボン酸、エルカ酸、ラウリン酸、ｎ−ウンデカン酸、アスコルビン酸などが挙げられる。
上記の酸無水物、フェノール類及び有機酸類の下層あるいは上層の全固形分に占める割合は、０．０５〜２０質量％が好ましく、より好ましくは０．１〜１５質量％、特に好ましくは０．１〜１０質量％である。
【００７６】
（界面活性剤）
本発明に係る記録層である上層および／または下層には、塗布性を良化するため、また、現像条件に対する処理の安定性を広げるため、特開昭６２−２５１７４０号公報や特開平３−２０８５１４号公報に記載されているような非イオン界面活性剤、特開昭５９−１２１０４４号公報、特開平４−１３１４９号公報に記載されているような両性界面活性剤、ＥＰ９５０５１７公報に記載されているようなシロキサン系化合物、特開昭６２−１７０９５０号公報、特開平１１−２８８０９３号公報、特願２００１−２４７３５１に記載されているようなフッ素含有のモノマー共重合体を添加することができる。
【００７７】
非イオン界面活性剤の具体例としては、ソルビタントリステアレート、ソルビタンモノパルミテート、ソルビタントリオレート、ステアリン酸モノグリセリド、ポリオキシエチレンノニルフェニルエーテル等が挙げられる。両性活性剤の具体例としては、アルキルジ（アミノエチル）グリシン、アルキルポリアミノエチルグリシン塩酸塩、２−アルキル−Ｎ−カルボキシエチル−Ｎ−ヒドロキシエチルイミダゾリニウムベタインやＮ−テトラデシル−Ｎ，Ｎ−ベタイン型（例えば、商品名「アモーゲンＫ」：第一工業（株）製）等が挙げられる。
【００７８】
シロキサン系化合物としては、ジメチルシロキサンとポリアルキレンオキシドのブロック共重合体が好ましく、具体例として、（株）チッソ社製、ＤＢＥ−２２４、ＤＢＥ−６２１、ＤＢＥ−７１２、ＤＢＰ−７３２、ＤＢＰ−５３４、独Ｔｅｇｏ社製、Ｔｅｇｏ Ｇｌｉｄｅ１００等のポリアルキレンオキシド変性シリコーンを挙げることが出来る。
上記非イオン界面活性剤及び両性界面活性剤の下層あるいは上層の全固形分に占める割合は、０．０１〜１５質量％が好ましく、より好ましくは０．１〜５質量％、さらに好ましくは０．０５〜２．０質量％である。
【００７９】
（焼出し剤／着色剤）
本発明に係る記録層である上層および／または下層には、露光による加熱後直ちに可視像を得るための焼き出し剤や、画像着色剤としての染料や顔料を加えることができる。
焼出し剤としては、露光による加熱によって酸を放出する化合物（光酸放出剤）と塩を形成し得る有機染料の組合せを代表として挙げることができる。具体的には、特開昭５０−３６２０９号、同５３−８１２８号の各公報に記載されているｏ−ナフトキノンジアジド−４−スルホン酸ハロゲニドと塩形成性有機染料の組合せや、特開昭５３−３６２２３号、同５４−７４７２８号、同６０−３６２６号、同６１−１４３７４８号、同６１−１５１６４４号及び同６３−５８４４０号の各公報に記載されているトリハロメチル化合物と塩形成性有機染料の組合せを挙げることができる。かかるトリハロメチル化合物としては、オキサゾール系化合物とトリアジン系化合物とがあり、どちらも経時安定性に優れ、明瞭な焼き出し画像を与える。
【００８０】
画像着色剤としては、前述の塩形成性有機染料以外に他の染料を用いることができる。塩形成性有機染料を含めて、好適な染料として油溶性染料と塩基性染料をあげることができる。具体的にはオイルイエロー＃１０１、オイルイエロー＃１０３、オイルピンク＃３１２、オイルグリーンＢＧ、オイルブルーＢＯＳ、オイルブルー＃６０３、オイルブラックＢＹ、オイルブラックＢＳ、オイルブラックＴ−５０５（以上オリエント化学工業（株）製）、ビクトリアピュアブルー、クリスタルバイオレットラクトン、クリスタルバイオレット（ＣＩ４２５５５）、メチルバイオレット（ＣＩ４２５３５）、エチルバイオレット、ローダミンＢ（ＣＩ１４５１７０Ｂ）、マラカイトグリーン（ＣＩ４２０００）、メチレンブルー（ＣＩ５２０１５）などを挙げることができる。また、特開昭６２−２９３２４７号公報に記載されている染料は特に好ましい。
これらの染料は、下層あるいは上層の全固形分に対し、０．０１〜１０質量％、好ましくは０．１〜３質量％の割合で添加することができる。
【００８１】
（可塑剤）
本発明に係る記録層である上層および／または下層には、塗膜の柔軟性等を付与するために可塑剤を添加しても良い。例えば、ブチルフタリル、ポリエチレングリコール、クエン酸トリブチル、フタル酸ジエチル、フタル酸ジブチル、フタル酸ジヘキシル、フタル酸ジオクチル、リン酸トリクレジル、リン酸トリブチル、リン酸トリオクチル、オレイン酸テトラヒドロフルフリル、アクリル酸又はメタクリル酸のオリゴマー及びポリマー等が用いられる。
これらの可塑剤は、下層あるいは上層の全固形分に対し、０．５〜１０質量％、好ましくは１．０〜５質量％の割合で添加することができる。
【００８２】
（ＷＡＸ剤）
本発明に係る上層には、キズに対する抵抗性を付与する目的で、表面の静摩擦係数を低下させる化合物を添加することもできる。具体的には、米国特許第６，１１７，９１３号明細書、或いは本願出願人が先に提案した特願２００１−２６１６２７号、特願２００２−０３２９０４号、特願２００２−１６５５８４号の各明細書に記載されているいるような、長鎖アルキルカルボン酸のエステルを有する化合物などを挙げることが出来る。添加量として好ましいのは、上層中に占める割合が０．１〜１０質量％、より好ましくは０．５〜５質量％である。
【００８３】
〔記録層の形成〕
本発明の平版印刷版原版における下層及び上層は、通常上記各成分を溶剤に溶かして、適当な支持体上に塗布することにより形成することができる。
ここで使用する溶剤としては、エチレンジクロライド、シクロヘキサノン、メチルエチルケトン、メタノール、エタノール、プロパノール、エチレングリコールモノメチルエーテル、１−メトキシ−２−プロパノール、２−メトキシエチルアセテート、１−メトキシ−２−プロピルアセテート、ジメトキシエタン、乳酸メチル、乳酸エチル、Ｎ，Ｎ−ジメチルアセトアミド、Ｎ，Ｎ−ジメチルホルムアミド、テトラメチルウレア、Ｎ−メチルピロリドン、ジメチルスルホキシド、スルホラン、γ−ブチロラクトン、トルエン等をあげることができるがこれに限定されるものではない。これらの溶剤は単独あるいは混合して使用される。
【００８４】
なお、該下層および上層は、原則的に２つの層を分離して形成することが好ましい。
２つの層を分離して形成する方法としては、例えば、下層に含まれる成分と、上層に含まれる成分との溶剤溶解性の差を利用する方法、または、上層を塗布した後、急速に溶剤を乾燥、除去させる方法等が挙げられる。
以下、これらの方法について詳述するが、２つの層を分離して塗布する方法はこれらに限定されるものではない。
【００８５】
下層に含まれる成分と上層に含まれる成分との溶剤溶解性の差を利用する方法としては、上層用塗布液を塗布する際に、下層に含まれる成分のいずれもが不溶な溶剤系を用いるものである。これにより、二層塗布を行っても、各層を明確に分離して塗膜にすることが可能になる。例えば、下層成分として、上層成分であるアルカリ可溶性樹脂を溶解するメチルエチルケトンや１−メトキシ−２−プロパノール等の溶剤に不溶な成分を選択し、該下層成分を溶解する溶剤系を用いて下層を塗布・乾燥し、その後、アルカリ可溶性樹脂を主体とする上層をメチルエチルケトンや１−メトキシ−２−プロパノール等で溶解し、塗布・乾燥することにより二層化が可能になる。
【００８６】
次に、２層目（上層）を塗布後に、極めて速く溶剤を乾燥させる方法としては、ウェブの走行方向に対してほぼ直角に設置したスリットノズルより高圧エアーを吹きつけることや、蒸気等の加熱媒体を内部に供給されたロール（加熱ロール）よりウェブの下面から伝導熱として熱エネルギーを与えること、あるいはそれらを組み合わせることにより達成できる。
【００８７】
また、新たな機能を付与するために、本発明の効果を充分に発揮する範囲において、積極的に上層および下層の部分相溶を行う場合もある。そのような方法としては、上記溶剤溶解性の差を利用する方法、２層目を塗布後に極めて速く溶剤を乾燥させる方法何れにおいても、その程度を調整する事によって可能となる。
【００８８】
支持体上に塗布される下層／上層用塗布液中の、溶剤を除いた前記成分（添加剤を含む全固形分）の濃度は、好ましくは１〜５０質量％である。
塗布する方法としては、種々の方法を用いることができるが、例えば、バーコーター塗布、回転塗布、スプレー塗布、カーテン塗布、ディップ塗布、エアーナイフ塗布、ブレード塗布、ロール塗布等を挙げることができる。
特に、上層塗布時に下層へのダメージを防ぐため、上層塗布方法は非接触式である事が望ましい。また接触型ではあるが溶剤系塗布に一般的に用いられる方法としてバーコーター塗布を用いる事も可能であるが、下層へのダメージを防止するために順転駆動で塗布する事が望ましい。
【００８９】
本発明の平版印刷版原版の支持体上に塗布される下層成分の乾燥後の塗布量は、０．５〜４．０ｇ／ｍ^２の範囲にあることが好ましく、更に好ましくは０．６〜２．５ｇ／ｍ^２の範囲である。０．５ｇ／ｍ^２未満であると耐刷性が低下する原因となり、４．０ｇ／ｍ^２を超えると画像再現性が劣化したり感度が低下したりするため好ましくない。
また、上層成分の乾燥後の塗布量は、０．０５〜１．０ｇ／ｍ^２の範囲にあることが好ましく、更に好ましくは０．０８〜０．７ｇ／ｍ^２の範囲である。０．０５ｇ／ｍ^２未満であると現像ラチチュード、耐傷性が低下する原因となり、１．０ｇ／ｍ^２を超えると感度が低下するため好ましくない。
下層および上層を合わせた乾燥後の塗布量としては、０．６〜４．０ｇ／ｍ^２の範囲にあることが好ましく、更に好ましくは０．７〜２．５ｇ／ｍ^２の範囲である。０．６ｇ／ｍ^２未満であると耐刷性が低下する原因となり、４．０ｇ／ｍ^２を超えると画像再現性が劣化したり感度が低下したりするため好ましくない。
【００９０】
〔支持体〕
本発明の平版印刷版原版に使用される支持体としては、必要な強度と耐久性を備えた寸度的に安定な板状物であれば特に制限はなく、例えば、紙、プラスチック（例えば、ポリエチレン、ポリプロピレン、ポリスチレン等）がラミネートされた紙、金属板（例えば、アルミニウム、亜鉛、銅等）、プラスチックフィルム（例えば、二酢酸セルロース、三酢酸セルロース、プロピオン酸セルロース、酪酸セルロース、酢酸酪酸セルロース、硝酸セルロース、ポリエチレンテレフタレート、ポリエチレン、ポリスチレン、ポリプロピレン、ポリカーボネート、ポリビニルアセタール等）、上記のごとき金属がラミネート、もしくは蒸着された紙、もしくはプラスチックフィルム等が挙げられる。
【００９１】
中でも、本発明においては、ポリエステルフィルム又はアルミニウム板が好ましく、その中でも寸度安定性がよく、比較的安価であるアルミニウム板は特に好ましい。好適なアルミニウム板は、純アルミニウム板及びアルミニウムを主成分とし、微量の異元素を含む合金板であり、更にアルミニウムがラミネートもしくは蒸着されたプラスチックフィルムでもよい。アルミニウム合金に含まれる異元素には、ケイ素、鉄、マンガン、銅、マグネシウム、クロム、亜鉛、ビスマス、ニッケル、チタンなどがある。合金中の異元素の含有量は高々１０質量％以下である。
【００９２】
本発明において特に好適なアルミニウムは、純アルミニウムであるが、完全に純粋なアルミニウムは精錬技術上製造が困難であるので、僅かに異元素を含有するものでもよい。
このように本発明に適用されるアルミニウム板は、その組成が特定されるものではなく、従来より公知公用の素材のアルミニウム板を適宜に利用することができる。本発明で用いられるアルミニウム板の厚みはおよそ０．１ｍｍ〜０．６ｍｍ程度、好ましくは０．１５ｍｍ〜０．４ｍｍ、特に好ましくは０．２ｍｍ〜０．３ｍｍである。
【００９３】
このようなアルミニウム板には、必要に応じて粗面化処理、陽極酸化処理などの表面処理を行なってもよい。以下、このような表面処理について簡単に説明する。
アルミニウム板を粗面化するに先立ち、所望により、表面の圧延油を除去するための例えば界面活性剤、有機溶剤又はアルカリ性水溶液などによる脱脂処理が行われる。アルミニウム板の表面の粗面化処理は、種々の方法により行われるが、例えば、機械的に粗面化する方法、電気化学的に表面を溶解粗面化する方法及び化学的に表面を選択溶解させる方法により行われる。機械的方法としては、ボール研磨法、ブラシ研磨法、ブラスト研磨法、バフ研磨法などの公知の方法を用いることができる。また、電気化学的な粗面化法としては塩酸又は硝酸電解液中で交流又は直流により行う方法がある。また、特開昭５４−６３９０２号公報に開示されているように両者を組み合わせた方法も利用することができる。
以上のように粗面化されたアルミニウム板は、必要に応じてアルカリエッチング処理及び中和処理された後、所望により表面の保水性や耐摩耗性を高めるために陽極酸化処理が施される。アルミニウム板の陽極酸化処理に用いられる電解質としては、多孔質酸化皮膜を形成する種々の電解質の使用が可能で、一般的には硫酸、リン酸、蓚酸、クロム酸あるいはそれらの混酸が用いられる。それらの電解質の濃度は電解質の種類によって適宜決められる。
【００９４】
陽極酸化の処理条件は用いる電解質により種々変わるので一概に特定し得ないが一般的には電解質の濃度が１〜８０質量％溶液、液温は５〜７０℃、電流密度５〜６０Ａ／ｄｍ^２、電圧１〜１００Ｖ、電解時間１０秒〜５分の範囲であれば適当である。陽極酸化皮膜の量は１．０ｇ／ｍ^２より少ないと耐刷性が不十分であったり、平版印刷版の非画像部に傷が付き易くなって、印刷時に傷の部分にインキが付着するいわゆる「傷汚れ」が生じ易くなる。
陽極酸化処理を施された後、アルミニウム表面は必要により親水化処理が施される。
【００９５】
本発明に使用される親水化処理としては、米国特許第２，７１４，０６６号、同第３，１８１，４６１号、第３，２８０，７３４号及び第３，９０２，７３４号に開示されているようなアルカリ金属シリケート（例えばケイ酸ナトリウム水溶液）法がある。この方法においては、支持体がケイ酸ナトリウム水溶液で浸漬処理されるか又は電解処理される。他に特公昭３６−２２０６３号公報に開示されているフッ化ジルコン酸カリウム及び米国特許第３，２７６，８６８号、同第４，１５３，４６１号、同第４，６８９，２７２号に開示されているようなポリビニルホスホン酸で処理する方法などが用いられる。
【００９６】
（下塗層）
本発明の平版印刷版原版は、支持体上に前記下層および上層の２層を積層して設けたものであるが、必要に応じて支持体と下層との間に下塗層を設けることができる。
下塗層成分としては種々の有機化合物が用いられ、例えば、カルボキシメチルセルロース、デキストリン、アラビアガム、２−アミノエチルホスホン酸などのアミノ基を有するホスホン酸類、置換基を有してもよいフェニルホスホン酸、ナフチルホスホン酸、アルキルホスホン酸、グリセロホスホン酸、メチレンジホスホン酸及びエチレンジホスホン酸などの有機ホスホン酸、置換基を有してもよいフェニルリン酸、ナフチルリン酸、アルキルリン酸及びグリセロリン酸などの有機リン酸、置換基を有してもよいフェニルホスフィン酸、ナフチルホスフィン酸、アルキルホスフィン酸及びグリセロホスフィン酸などの有機ホスフィン酸、グリシンやβ−アラニンなどのアミノ酸類、及びトリエタノールアミンの塩酸塩などのヒドロキシ基を有するアミンの塩酸塩等から選ばれるが、２種以上混合して用いてもよい。
【００９７】
この有機下塗層は次のような方法で設けることができる。即ち、水又はメタノール、エタノール、メチルエチルケトンなどの有機溶剤もしくはそれらの混合溶剤に上記の有機化合物を溶解させた溶液をアルミニウム板上に塗布、乾燥して設ける方法と、水又はメタノール、エタノール、メチルエチルケトンなどの有機溶剤もしくはそれらの混合溶剤に上記の有機化合物を溶解させた溶液に、アルミニウム板を浸漬して上記化合物を吸着させ、その後水などによって洗浄、乾燥して有機下塗層を設ける方法である。前者の方法では、上記の有機化合物の０．００５〜１０質量％の濃度の溶液を種々の方法で塗布できる。また後者の方法では、溶液の濃度は０．０１〜２０質量％、好ましくは０．０５〜５質量％であり、浸漬温度は２０〜９０℃、好ましくは２５〜５０℃であり、浸漬時間は０．１秒〜２０分、好ましくは２秒〜１分である。これに用いる溶液は、アンモニア、トリエチルアミン、水酸化カリウムなどの塩基性物質や、塩酸、リン酸などの酸性物質によりｐＨ１〜１２の範囲に調整することもできる。また、画像記録材料の調子再現性改良のために黄色染料を添加することもできる。
有機下塗層の被覆量は、２〜２００ｍｇ／ｍ^２が適当であり、好ましくは５〜１００ｍｇ／ｍ^２である。上記の被覆量が２ｍｇ／ｍ^２よりも少ないと十分な耐刷性能が得られない。また、２００ｍｇ／ｍ^２より大きくても同様である。
上記のようにして作製された平版印刷版原版は、画像様に露光され、その後、現像処理を施される。
【００９８】
（バックコート層）
本発明の平版印刷版原版の支持体裏面には、必要に応じてバックコート層が設けられる。かかるバックコート層としては、特開平５−４５８８５号公報記載の有機高分子化合物および特開平６−３５１７４号公報記載の有機または無機金属化合物を加水分解および重縮合させて得られる金属酸化物からなる被覆層が好ましく用いられる。これらの被覆層のうち、Ｓｉ（ＯＣＨ_３）_４、Ｓｉ（ＯＣ_２Ｈ_５）_４、Ｓｉ（ＯＣ_３Ｈ_７）_４、Ｓｉ（ＯＣ_４Ｈ_９）_４などのケイ素のアルコキシ化合物が安価で入手し易く、それから得られる金属酸化物の被覆層が耐現像液に優れており特に好ましい。
【００９９】
〔露光〕
本発明の平版印刷版原版の像露光に用いられる活性光線の光源としては、近赤外から赤外領域に発光波長を持つ光源が好ましく、固体レーザ、半導体レーザが特に好ましい。
【０１００】
〔現像処理〕
本発明の平版印刷版原版の現像処理に適用することのできる現像液は、ｐＨが９．０〜１４．０の範囲、好ましくは１２．０〜１３．５の範囲にある現像液である。現像液（以下、補充液も含めて現像液と呼ぶ）には、従来より知られているアルカリ水溶液が使用できる。例えば、ケイ酸ナトリウム、同カリウム、第３リン酸ナトリウム、同カリウム、同アンモニウム、第２リン酸ナトリウム、同カリウム、同アンモニウム、炭酸ナトリウム、同カリウム、同アンモニウム、炭酸水素ナトリウム、同カリウム、同アンモニウム、ほう酸ナトリウム、同カリウム、同アンモニウム、水酸化ナトリウム、同アンモニウム、同カリウムおよび同リチウムなどの無機アルカリ塩が挙げられる。また、モノメチルアミン、ジメチルアミン、トリメチルアミン、モノエチルアミン、ジエチルアミン、トリエチルアミン、モノイソプロピルアミン、ジイソプロピルアミン、トリイソプロピルアミン、ｎ−ブチルアミン、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、モノイソプロパノールアミン、ジイソプロパノールアミン、エチレンイミン、エチレンジアミン、ピリジンなどの有機アルカリ剤が挙げられる。これらのアルカリ水溶液は、１種単独で用いてもよいし、２種以上を併用してもよい。
【０１０１】
上記のアルカリ水溶液のうち、本発明による効果が発揮される現像液は、一つは、塩基としてケイ酸アルカリを含有した、又は塩基にケイ素化合物を混ぜてケイ酸アルカリとしたものを含有した、所謂「シリケート現像液」と呼ばれるｐＨ１２以上の水溶液であり、もう一つのより好ましい現像液は、ケイ酸アルカリを含有せず、非還元糖（緩衝作用を有する有機化合物）と塩基とを含有した所謂「ノンシリケート現像液」である。
【０１０２】
前者においては、アルカリ金属ケイ酸塩の水溶液はケイ酸塩の成分である酸化ケイ素ＳｉＯ_２とアルカリ金属酸化物Ｍ_２Ｏの比率（一般に〔ＳｉＯ_２〕／〔Ｍ_２Ｏ〕のモル比で表す）と濃度によって現像性の調節が可能であり、例えば、特開昭５４−６２００４号公報に開示されているような、ＳｉＯ_２／Ｎａ_２Ｏのモル比が１．０〜１．５（即ち〔ＳｉＯ_２〕／〔Ｎａ_２Ｏ〕が１．０〜１．５）であって、ＳｉＯ_２の含有量が１〜４質量％のケイ酸ナトリウムの水溶液や、特公昭５７−７４２７号公報に記載されているような、〔ＳｉＯ_２〕／〔Ｍ〕が０．５〜０．７５（即ち〔ＳｉＯ_２〕／〔Ｍ_２Ｏ〕が１．０〜１．５）であって、ＳｉＯ_２の濃度が１〜４質量％であり、かつ該現像液がその中に存在する全アルカリ金属のグラム原子を基準にして少なくとも２０％のカリウムを含有している、アルカリ金属ケイ酸塩の水溶液が好適に用いられる。
【０１０３】
また、ケイ酸アルカリを含有せず、非還元糖と塩基とを含有した所謂「ノンシリケート現像液」も、本発明の平版印刷版原版の現像に適用するのに好ましい。この現像液を用いて、平版印刷版原版の現像処理を行うと、記録層の表面を劣化させることがなく、かつ記録層の着肉性をより良好な状態に維持することができる。
【０１０４】
この現像液は、その主成分が、非還元糖から選ばれる少なくとも一つの化合物と、少なくとも一種の塩基からなり、液のｐＨが９．０〜１３．５の範囲であることが好ましい。かかる非還元糖とは、遊離のアルデヒド基やケトン基を持たず、還元性を示さない糖類であり、還元基同士の結合したトレハロース型少糖類、糖類の還元基と非糖類が結合した配糖体および糖類に水素添加して還元した糖アルコールに分類され、何れも好適に用いられる。トレハロース型少糖類には、サッカロースやトレハロースがあり、配糖体としては、アルキル配糖体、フェノール配糖体、カラシ油配糖体などが挙げられる。また糖アルコールとしてはＤ，Ｌ−アラビット、リビット、キシリット、Ｄ，Ｌ−ソルビット、Ｄ，Ｌ−マンニット、Ｄ，Ｌ−イジット、Ｄ，Ｌ−タリット、ズリシットおよびアロズルシットなどが挙げられる。更に二糖類の水素添加で得られるマルチトールおよびオリゴ糖の水素添加で得られる還元体（還元水あめ）が好適に用いられる。これらの中で特に好ましい非還元糖は糖アルコールとサッカロースであり、特にＤ−ソルビット、サッカロース、還元水あめが適度なｐＨ領域に緩衝作用があることと、低価格であることで好ましい。
【０１０５】
これらの非還元糖は、単独もしくは二種以上を組み合わせて使用でき、それらの現像液中に占める割合は０．１〜３０重量％が好ましく、更に好ましくは、１〜２０重量％である。
この範囲以下では十分な緩衝作用が得られず、またこの範囲以上の濃度では、高濃縮化し難く、また原価アップの問題が出てくる。尚、還元糖を塩基と組み合わせて使用した場合、経時的に褐色に変色し、ｐＨも徐々に下がり、よって現像性が低下するという問題点がある。
【０１０６】
非還元糖に組み合わせる塩基としては従来より知られているアルカリ剤が使用できる。例えば、水酸化ナトリウム、水酸化カリウム、水酸化リチウム、リン酸三ナトリウム、リン酸三カリウム、リン酸三アンモニウム、リン酸二ナトリウム、リン酸二カリウム、リン酸二アンモニウム、炭酸ナトリウム、炭酸カリウム、炭酸アンモニウム、炭酸水素ナトリウム、炭酸水素カリウム、炭酸水素アンモニウム、ホウ酸ナトリウム、ホウ酸カリウム、ホウ酸アンモニウムなどの無機アルカリ剤が挙げられる。また、モノメチルアミン、ジメチルアミン、トリメチルアミン、モノエチルアミン、ジエチルアミン、トリエチルアミン、モノイソプロピルアミン、ジイソプロピルアミン、トリイソプロピルアミン、ｎ−ブチルアミン、モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、モノイソプロパノールアミン、ジイソプロパノールアミン、エチレンイミン、エチレンジアミン、ピリジンなどの有機アルカリ剤も用いられる。
【０１０７】
これらのアルカリ剤は単独もしくは二種以上を組み合わせて用いられる。これらの中で好ましいのは水酸化ナトリウム、水酸化カリウムである、その理由は、非還元糖に対するこれらの量を調整することにより広いｐＨ領域でｐＨ調整が可能となるためである。また、リン酸三ナトリウム、リン酸三カリウム、炭酸ナトリウム、炭酸カリウムなどもそれ自身に緩衝作用があるので好ましい。
これらのアルカリ剤は現像液のｐＨを９．０〜１３．５の範囲になるように添加され、その添加量は所望のｐＨ、非還元糖の種類と添加量によって決められるが、より好ましいｐＨ範囲は１０．０〜１３．２である。
【０１０８】
現像液には更に、糖類以外の弱酸と強塩基からなるアルカリ性緩衝液が併用できる。かかる緩衝液として用いられる弱酸としては、解離定数（ｐＫａ）が１０．０〜１３．２のものが好ましい。
このような弱酸としては、Ｐｅｒｇａｍｏｎ Ｐｒｅｓｓ社発行のＩＯＮＩＳＡＴＩＯＮ ＣＯＮＳＴＡＮＴＳ ＯＦ ＯＲＧＡＮＩＣ ＡＣＩＤＳ ＩＮ ＡＱＵＥＯＵＳ ＳＯＬＵＴＩＯＮなどに記載されているものから選ばれ、例えば２，２，３，３−テトラフルオロプロパノール−１（ＰＫａ１２．７４）、トリフルオロエタノール（同１２．３７）、トリクロロエタノール（同１２．２４）などのアルコール類、ピリジン−２−アルデヒド（同１２．６８）、ピリジン−４−アルデヒド（同１２．０５）などのアルデヒド類、サリチル酸（同１３．０）、３−ヒドロキシ−２−ナフトエ酸（同１２．８４）、カテコール（同１２．６）、没食子酸（同１２．４）、スルホサリチル酸（同１１．７）、３，４−ジヒドロキシスルホン酸（同１２．２）、３，４−ジヒドロキシ安息香酸（同１１．９４）、１，２，４−トリヒドロキシベンゼン（同１１．８２）、ハイドロキノン（同１１．５６）、ピロガロール（同１１．３４）、ｏ−クレゾール（同１０．３３）、レゾルシノール（同１１．２７）、ｐ−クレゾール（同１０．２７）、ｍ−クレゾール（同１０．０９）などのフェノール性水酸基を有する化合物、２−ブタノンオキシム（同１２．４５）、アセトキシム（同１２．４２）、１，２−シクロヘプタンジオンジオキシム（同１２．３）、２−ヒドロキシベンズアルデヒドオキシム（同１２．１０）、ジメチルグリオキシム（同１１．９）、エタンジアミドジオキシム（同１１．３７）、アセトフェノンオキシム（同１１．３５）などのオキシム類、アデノシン（同１２．５６）、イノシン（同１２．５）、グアニン（同１２．３）、シトシン（同１２．２）、ヒポキサンチン（同１２．１）、キサンチン（同１１．９）などの核酸関連物質、他に、ジエチルアミノメチルホスホン酸（同１２．３２）、１−アミノ−３，３，３−トリフルオロ安息香酸（同１２．２９）、イソプロピリデンジホスホン酸（同１２．１０）、１，１−エチリデンジホスホン酸（同１１．５４）、１，１−エチリデンジホスホン酸１−ヒドロキシ（同１１．５２）、ベンズイミダゾール（同１２．８６）、チオベンズアミド（同１２．８）、ピコリンチオアミド（同１２．５５）、バルビツル酸（同１２．５）などの弱酸が挙げられる。
【０１０９】
これらの弱酸の中で好ましいのは、スルホサリチル酸、サリチル酸である。これらの弱酸に組み合わせる塩基としては、水酸化ナトリウム、同アンモニウム、同カリウムおよび同リチウムが好適に用いられる。これらのアルカリ剤は単独もしくは二種以上を組み合わせて用いられる。上記の各種アルカリ剤は濃度および組み合わせによりｐＨを好ましい範囲内に調整して使用される。
【０１１０】
現像液には、現像性の促進や現像カスの分散および印刷版画像部の親インキ性を高める目的で必要に応じて種々界面活性剤や有機溶剤を添加できる。好ましい界面活性剤としては、アニオン系、カチオン系、ノニオン系および両性界面活性剤が挙げられる。
【０１１１】
界面活性剤の好ましい例としては、ポリオキシエチレンアルキルエーテル類、ポリオキシエチレンアルキルフェニルエーテル類、ポリオキシエチレンポリスチリルフェニルエーテル類、ポリオキシエチレンポリオキシプロピレンアルキルエーテル類、グリセリン脂肪酸部分エステル類、ソルビタン脂肪酸部分エステル類、ペンタエリスリトール脂肪酸部分エステル類、プロピレングリコールモノ脂肪酸エステル類、しょ糖脂肪酸部分エステル類、ポリオキシエチレンソルビタン脂肪酸部分エステル類、ポリオキシエチレンソルビトール脂肪酸部分エステル類、ポリエチレングリコール脂肪酸エステル類、ポリグリセリン脂肪酸部分エステル類、ポリオキシエチレン化ひまし油類、ポリオキシエチレングリセリン脂肪酸部分エステル類、脂肪酸ジエタノールアミド類、Ｎ，Ｎ−ビス−２−ヒドロキシアルキルアミン類、ポリオキシエチレンアルキルアミン、トリエタノールアミン脂肪酸エステル、トリアルキルアミンオキシドなどの非イオン性界面活性剤、脂肪酸塩類、アビエチン酸塩類、ヒドロキシアルカンスルホン酸塩類、アルカンスルホン酸塩類、ジアルキルスルホ琥珀酸エステル塩類、直鎖アルキルベンゼンスルホン酸塩類、分岐鎖アルキルベンゼンスルホン酸塩類、アルキルナフタレンスルホン酸塩類、アルキルフェノキシポリオキシエチレンプロピルスルホン酸塩類、ポリオキシエチレンアルキルスルホフェニルエーテル塩類、Ｎ−メチル−Ｎ−オレイルタウリンナトリウム塩、Ｎ−アルキルスルホ琥珀酸モノアミド二ナトリウム塩、石油スルホン酸塩類、硫酸化牛脂油、脂肪酸アルキルエステルの硫酸エステル塩類、アルキル硫酸エステル塩類、ポリオキシエチレンアルキルエーテル硫酸エステル塩類、脂肪酸モノグリセリド硫酸エステル塩類、ポリオキシエチレンアルキルフェニルエーテル硫酸エステル塩類、ポリオキシエチレンスチリルフェニルエーテル硫酸エステル塩類、アルキルリン酸エステル塩類、ポリオキシエチレンアルキルエーテルリン酸エステル塩類、ポリオキシエチレンアルキルフェニルエーテルリン酸エステル塩類、スチレン／無水レイン酸共重合物の部分鹸化物類、オレフィン／無水マレイン酸共重合物の部分鹸化物類、ナフタレンスルホン酸塩ホルマリン縮合物類などのアニオン界面活性剤、アルキルアミン塩類、テトラブチルアンモニウムブロミド等の第四級アンモニウム塩類、ポリオキシエチレンアルキルアミン塩類、ポリエチレンポリアミン誘導体などのカチオン性界面活性剤、カルボキシベタイン類、アミノカルボン酸類、スルホべタイン類、アミノ硫酸エステル類、イミダゾリン類などの両性界面活性剤が挙げられる。以上挙げた界面活性剤の中でポリオキシエチレンとあるものは、ポリオキシメチレン、ポリオキシプロピレン、ポリオキシブチレンなどのポリオキシアルキレンに読み替えることもでき、それらの界面活性剤もまた包含される。
【０１１２】
更に好ましい界面活性剤は分子内にパーフルオロアルキル基を含有するフッ素系の界面活性剤である。かかるフッ素系界面活性剤としては、パーフルオロアルキルカルボン酸塩、パーフルオロアルキルスルホン酸塩、パーフルオロアルキルリン酸エステルなどのアニオン型、パーフルオロアルキルベタインなどの両性型、パーフルオロアルキルトリメチルアンモニウム塩などのカチオン型およびパーフルオロアルキルアミンオキサイド、パーフルオロアルキルエチレンオキシド付加物、パーフルオロアルキル基および親水性基含有オリゴマー、パーフルオロアルキル基および親油性基含有オリゴマー、パーフルオロアルキル基、親水性基および親油性基含有オリゴマー、パーフルオロアルキル基および親油性基含有ウレタンなどの非イオン型が挙げられる。上記の界面活性剤は、単独もしくは２種以上を組み合わせて使用することができ、現像液中に０．００１〜１０重量％、より好ましくは０．０１〜５重量％の範囲で添加される。
【０１１３】
現像液には、種々の現像安定化剤を用いることができる。それらの好ましい例として、特開平６−２８２０７９号公報記載の糖アルコールのポリエチレングリコール付加物、テトラブチルアンモニウムヒドロキシドなどのテトラアルキルアンモニウム塩、テトラブチルホスホニウムブロマイドなどのホスホニウム塩およびジフェニルヨードニウムクロライドなどのヨードニウム塩が好ましい例として挙げられる。更には、特開昭５０−５１３２４号公報記載のアニオン界面活性剤または両性界面活性剤、また特開昭５５−９５９４６号公報記載の水溶性カチオニックポリマー、特開昭５６−１４２５２８号公報に記載されている水溶性の両性高分子電解質を挙げることができる。
【０１１４】
更に、特開昭５９−８４２４１号公報のアルキレングリコールが付加された有機ホウ素化合物、特開昭６０−１１１２４６号公報記載のポリオキシエチレン・ポリオキシプロピレンブロック重合型の水溶性界面活性剤、特開昭６０−１２９７５０号公報のポリオキシエチレン・ポリオキシプロピレンを置換したアルキレンジアミン化合物、特開昭６１−２１５５５４号公報記載の重量平均分子量３００以上のポリエチレングリコール、特開昭６３−１７５８５８号公報のカチオン性基を有する含フッ素界面活性剤、特開平２−３９１５７号公報の酸またはアルコールに４モル以上のエチレンオキシドを付加して得られる水溶性エチレンオキシド付加化合物と、水溶性ポリアルキレン化合物などが挙げられる。
【０１１５】
現像液には更に必要により有機溶剤が加えられる。かかる有機溶剤としては、水に対する溶解度が約１０重量％以下のものが適しており、好ましくは５重量％以下のものから選ばれる。例えば、１−フェニルエタノール、２−フェニルエタノール、３−フェニル−１−プロパノール、４−フェニル−１−ブタノール、４−フェニル−２−ブタノール、２−フェニル−１−ブタノール、２−フェノキシエタノール、２−ベンジルオキシエタノール、ｏ−メトキシベンジルアルコール、ｍ−メトキシベンジルアルコール、ｐ−メトキシベンジルアルコール、ベンジルアルコール、シクロヘキサノール、２−メチルシクロヘキサノール、３−メチルシクロヘキサノールおよび４−メチルシクロヘキサノール、Ｎ−フェニルエタノールアミンおよびＮ−フェニルジエタノールアミンなどを挙げることができる。
有機溶剤の含有量は使用液の総重量に対して０．１〜５重量％である。その使用量は界面活性剤の使用量と密接な関係があり、有機溶剤の量が増すにつれ、界面活性剤の量は増加させることが好ましい。これは界面活性剤の量が少なく、有機溶剤の量を多く用いると有機溶剤が完全に溶解せず、従って、良好な現像性の確保が期待できなくなるからである。
【０１１６】
現像液には更に還元剤を加えることができる。これは印刷版の汚れを防止するものである。好ましい有機還元剤としては、チオサリチル酸、ハイドロキノン、メトール、メトキシキノン、レゾルシン、２−メチルレゾルシンなどのフェノール化合物、フェニレンジアミン、フェニルヒドラジンなどのアミン化合物が挙げられる。更に好ましい無機の還元剤としては、亜硫酸、亜硫酸水素酸、亜リン酸、亜リン酸水素酸、亜リン酸二水素酸、チオ硫酸および亜ジチオン酸などの無機酸のナトリウム塩、カリウム塩、アンモニウム塩などを挙げることができる。
これらの還元剤のうち汚れ防止効果が特に優れているのは亜硫酸塩である。これらの還元剤は使用時の現像液に対して好ましくは、０．０５〜５重量％の範囲で含有される。
【０１１７】
現像液には更に有機カルボン酸を加えることもできる。好ましい有機カルボン酸は炭素原子数６〜２０の脂肪族カルボン酸および芳香族カルボン酸である。脂肪族カルボン酸の具体的な例としては、カプロン酸、エナンチル酸、カプリル酸、ラウリン酸、ミリスチン酸、パルミチン酸およびステアリン酸などがあり、特に好ましいのは炭素数８〜１２のアルカン酸である。また炭素鎖中に二重結合を有する不飽和脂肪酸でも、枝分かれした炭素鎖のものでもよい。芳香族カルボン酸としてはベンゼン環、ナフタレン環、アントラセン環などにカルボキシル基が置換された化合物で、具体的には、ｏ−クロロ安息香酸、ｐ−クロロ安息香酸、ｏ−ヒドロキシ安息香酸、ｐ−ヒドロキシ安息香酸、ｏ−アミノ安息香酸、ｐ−アミノ安息香酸、２，４−ジヒドロシ安息香酸、２，５−ジヒドロキシ安息香酸、２，６−ジヒドロキシ安息香酸、２，３−ジヒドロキシ安息香酸、３，５−ジヒドロキシ安息香酸、没食子酸、１−ヒドロキシ−２−ナフトエ酸、３−ヒドロキシ−２−ナフトエ酸、２−ヒドロキシ−１−ナフトエ酸、１−ナフトエ酸、２−ナフトエ酸などがあるがヒドロキシナフトエ酸は特に有効である。
【０１１８】
上記脂肪族および芳香族カルボン酸は水溶性を高めるためにナトリウム塩やカリウム塩またはアンモニウム塩として用いるのが好ましい。本発明で用いる現像液の有機カルボン酸の含有量は格別な制限はないが、０．１重量％より低いと効果が十分でなく、また１０重量％以上ではそれ以上の効果の改善が計れないばかりか、別の添加剤を併用する時に溶解を妨げることがある。従って、好ましい添加量は使用時の現像液に対して０．１〜１０重量％であり、より好ましくは０．５〜４重量％である。
【０１１９】
現像液には、更に必要に応じて、防腐剤、着色剤、増粘剤、消泡剤および硬水軟化剤などを含有させることもできる。硬水軟化剤としては例えば、ポリリン酸およびそのナトリウム塩、カリウム塩およびアンモニウム塩、エチレンジアミンテトラ酢酸、ジエチレントリアミンペンタ酢酸、トリエチレンテトラミンヘキサ酢酸、ヒドロキシエチルエチレンジアミントリ酢酸、ニトリロトリ酢酸、１，２−ジアミノシクロヘキサンテトラ酢酸および１，３−ジアミノ−２−プロパノールテトラ酢酸などのアミノポリカルボン酸およびそれらのナトリウム塩、カリウム塩およびアンモニウム塩、アミノトリ（メチレンホスホン酸）、エチレンジアミンテトラ（メチレンホスホン酸）、ジエチレントリアミンペンタ（メチレンホスホン酸）、トリエチレンテトラミンヘキサ（メチレンホスホン酸）、ヒドロキシエチルエチレンジアミントリ（メチレンホスホン酸）および１−ヒドロキシタエン−１，１−ジホスホン酸やそれらのナトリウム塩、カリウム塩およびアンモニウム塩を挙げることができる。
【０１２０】
このような硬水軟化剤はそのキレート化と使用される硬水の硬度および硬水の量によって最適値が変化するが、一般的な使用量を示せば、使用時の現像液に０．０１〜５重量％、より好ましくは０．０１〜０．５重量％の範囲である。この範囲より少ない添加量では所期の目的が十分に達成されず、添加量がこの範囲より多い場合は、色抜けなど、画像部への悪影響がでてくる。現像液の残余の成分は水である。現像液は、使用時よりも水の含有量を少なくした濃縮液としておき、使用時に水で希釈するようにしておくことが運搬上有利である。この場合の濃縮度は、各成分が分離や析出を起こさない程度が適当である。
【０１２１】
本発明に用いられる現像液としてはまた、特開平６−２８２０７９号公報記載の現像液も使用できる。これは、ＳｉＯ_２／Ｍ_２Ｏ（Ｍはアルカリ金属を示す）のモル比が０．５〜２．０の珪酸アルカリ金属塩と、水酸基を４以上有する糖アルコールに５モル以上のエチレンオキシドを付加して得られる水溶性エチレンオキシド付加化合物を含有する現像液である。糖アルコールは糖のアルデヒド基およびケトン基を還元してそれぞれ第一、第二アルコール基としたものに相当する多価アルコールである。糖アルコールの貝体的な例としては、Ｄ，Ｌ−トレイット、エリトリット、Ｄ，Ｌ−アラビット、リビット、キシリット、Ｄ，Ｌ−ソルビット、Ｄ，Ｌ−マンニット、Ｄ，Ｌ−イジット、Ｄ，Ｌ−タリット、ズルシット、アロズルシットなどであり、更に糖アルコールを縮合したジ、トリ、テトラ、ペンタおよびヘキサグリセリンなども挙げられる。上記水溶性エチレンオキシド付加化合物は上記糖アルコール１モルに対し５モル以上のエチレンオキシドを付加することにより得られる。さらにエチレンオキシド付加化合物には必要に応じてプロピレンオキシドを溶解性が許容できる範囲でブロック共重合させてもよい。これらのエチレンオキシド付加化合物は単独もしくは二種以上を組み合わせて用いてもよい。
これらの水溶性エチレンオキシド付加化合物の添加量は現像液（使用液）に対して０．００１〜５重量％が適しており、より好ましくは０．００１〜２重量％である。
【０１２２】
この現像液にはさらに、現像性の促進や現像カスの分散および印刷版画像部の親インキ性を高める目的で必要に応じて、前述の種々の界面活性剤や有機溶剤を添加できる。
【０１２３】
かかる組成の現像液で現像処理された平版印刷版原版は水洗水、界面活性剤等を含有するリンス液、アラビアガムや澱粉誘導体等を主成分とするフィニッシャーや保護ガム液で後処理を施される。本発明の平版印刷版原版の後処理にはこれらの処理を種々組み合わせて用いることができる。
【０１２４】
近年、型版・印刷業界では製版作業の合理化および標準化のため、ＰＳ版用の自動現像機が広く用いられている。この自動現像機は、一般に現像部と後処理部からなり、ＰＳ版を搬送する装置と、各処理液槽およびスプレー装置からなり、露光済みのＰＳ版を水平に搬送しながら、ポンプで汲み上げた各処理液をスプレーノズルから吹き付けて現像および後処理するものである。また、最近は処理液が満たされた処理液槽中に液中ガイドロールなどによってＰＳ版を浸漬搬送させて現像処理する方法や、現像後一定量の少量の水洗水を版面に供給して水洗し、その廃水を現像液原液の希釈水としで再利用する方法も知られている。
【０１２５】
このような自動処理においては、各処理液に処理量や稼動時間等に応じてそれぞれの補充液を補充しながら処理することができる。また、実質的に未使用の処理液で処理するいわゆる使い捨て処理方式も適用できる。
【０１２６】
本発明の平版印刷版原版においては、画像露光し、現像し、水洗及び／又はリンス及び／又はガム引きして得られた平版印刷版に不必要な画像部（例えば原画フィルムのフィルムエッジ跡など）がある場合には、その不必要な画像部の消去が行なわれる。このような消去は、例えば特公平２−１３２９３号公報に記載されているような消去液を不必要画像部に塗布し、そのまま所定の時間放置したのちに水洗することにより行なう方法が好ましいが、特開平５９−１７４８４２号公報に記載されているようなオプティカルファイバーで導かれた活性光線を不必要画像部に照射したのち現像する方法も利用できる。
【０１２７】
以上のようにして本発明の平版印刷版原版より得られた平版印刷版は所望により不感脂化ガムを塗布したのち、印刷工程に供することができるが、より一層の高耐刷力の平版印刷版としたい場合にはバーニング処理が施される。平版印刷版をバーニングする場合には、バーニング前に特公昭６１−２５１８号、同５５−２８０６２号、特開昭６２−３１８５９号、同６１−１５９６５５号の各公報に記載されているような整面液で処理することが好ましい。
その方法としては、該整面液を浸み込ませたスポンジや脱脂綿にて、平版印刷版上に塗布するか、整面液を満たしたバット中に印刷版を浸漬して塗布する方法や、自動コーターによる塗布などが適用される。また、塗布した後でスキージ、あるいは、スキージローラーで、その塗布量を均一にすることは、より好ましい結果を与える。
【０１２８】
整面液の塗布量は一般に０．０３〜０．８ｇ／ｍ^２（乾燥質量）が適当である。整面液が塗布された平版印刷版は必要であれば乾燥された後、バーニングプロセッサー（たとえば富士写真フイルム（株）より販売されているバーニングプロセッサー：「ＢＰ−１３００」）などで高温に加熱される。この場合の加熱温度及び時間は、画像を形成している成分の種類にもよるが、１８０〜３００℃の範囲で１〜２０分の範囲が好ましい。
【０１２９】
バーニング処理された平版印刷版は、必要に応じて適宜、水洗、ガム引きなどの従来より行なわれている処理を施こすことができるが水溶性高分子化合物等を含有する整面液が使用された場合にはガム引きなどのいわゆる不感脂化処理を省略することができる。この様な処理によって得られた平版印刷版はオフセット印刷機等にかけられ、多数枚の印刷に用いられる。
【０１３０】
【実施例】
以下、本発明を実施例に従って説明するが、本発明の範囲はこれらの実施例に限定されない。
【０１３１】
［ポリウレタン樹脂の合成］
＜合成例１＞
５００ｍｌの３つ口フラスコに４，４’−ジフェニルメタンジイソシアネート１２５ｇと２，２−ビス（ヒドロキシメチル）プロピオン酸６７ｇをジオキサン２９０ｍｌに溶解した。Ｎ，Ｎ−ジエチルアニリンを１ｇを入れた後ジオキサン還流下６時間攪拌した。反応後、水４Ｌ、酢酸４０ｃｃの溶液に少しずつ加えポリマーを析出させた。この固体を真空乾燥させることにより１８５ｇのポリウレタン樹脂（１）を得た。酸含有量は２．４７ｍｅｑ／ｇであつた。ＧＰＣにて分子量を測定したところ重量平均（ポリスチレン標準）で２８，０００であった。
【０１３２】
＜合成例２〜１３＞
上記合成例１において、出発物質を下記１表のジイソシアネート化合物及びジオール化合物に代えた以外は、合成例１と同様にして、ポリウレタン樹脂（２）〜（１３）を合成した。
【０１３３】
【表１】

【０１３４】
【表２】

【０１３５】
〔実施例１〕
［支持体の作製］
厚さ０．２４ｍｍのアルミニウム板（Ｓｉ：０．０６質量％、Ｆｅ：０．３０質量％、Ｃｕ：０．０１４質量％、Ｍｎ：０．００１質量％、Ｍｇ：０．００１質量％、Ｚｎ：０．００１質量％、Ｔｉ：０．０３質量％を含有し、残部はＡｌと不可避不純物のアルミニウム合金）に対し以下に示す表面処理を連続的に行った。
【０１３６】
６０Ｈｚの交流電圧を用いて連続的に電気化学的な粗面化処理を行った。このときの電解液は、硝酸１０ｇ／リットル水溶液（アルミニウムイオンを５ｇ／リットル、アンモニウムイオンを０．００７質量％含む。）、温度８０℃であった。水洗後、アルミニウム板をカセイソーダ濃度２６質量％、アルミニウムイオン濃度６．５質量％でスプレーによるエッチング処理を３２℃で行い、アルミニウム板を０．２０ｇ／ｍ^２溶解し、スプレーによる水洗を行った。その後、温度６０℃の硫酸濃度２５質量％水溶液（アルミニウムイオンを０．５質量％含む。）で、スプレーによるデスマット処理を行い、スプレーによる水洗を行った。
【０１３７】
二段給電電解処理法の陽極酸化装置を用いて陽極酸化処理を行った。電解部に供給した電解液としては、硫酸を用いた。その後、スプレーによる水洗を行った。最終的な酸化皮膜量は２．７ｇ／ｍ^２であった。
陽極酸化処理により得られたアルミニウム支持体を温度３０℃の３号ケイ酸ソーダの１質量％水溶液の処理槽中へ、１０秒間、浸せきすることでアルカリ金属ケイ酸塩処理（シリケート処理）を行った。その後、スプレーによる水洗を行った。
上記のようにして得られたアルカリ金属ケイ酸塩処理後のアルミニウム支持体上に、下記組成の下塗液を塗布し、８０℃で１５秒間乾燥し、塗膜を形成させた。乾燥後の塗膜の被覆量は１５ｍｇ／ｍ^２であった。
【０１３８】
＜下塗液組成＞
・下記化合物 ０．３ｇ
・メタノール １００ｇ
・水 １ｇ
【０１３９】
【化５】

【０１４０】
［記録層の形成］
上記により得られたウェブ状の支持体に、下記組成の下層用塗布液１を塗布量が０．８５ｇ／ｍ^２になるようバーコーターで塗布したのち、１６０℃で４４秒間乾燥し、直ちに１７〜２０℃の冷風で支持体の温度が３５℃になるまで冷却した。
その後、下記組成の上層用塗布液１を塗布量が０．２２ｇ／ｍ^２になるようバーコーター塗布したのち、１４８℃で２５分間乾燥し、更に２０〜２６℃の風で徐冷し、実施例１の平版印刷版原版を作製した。
【０１４１】

【０１４２】
【化６】

【０１４３】

【０１４４】
【化７】

【０１４５】
〔実施例２〜１３〕
実施例１における下層用塗布液１で用いたポリウレタン樹脂（１）を、前記合成例で得られたポリウレタン樹脂（２）〜（１３）に変更した以外は実施例１と同様にして実施例２〜１３の平版印刷版原版を作製した。
【０１４６】
〔比較例１〕
実施例１における下層用塗布液１で用いたポリウレタン樹脂（１）を、Ｎ−（４−アミノスルホニルフェニル）メタクリルアミド／アクリロニトリル／メタクリル酸メチル（３６／３４／３０：重量平均分子量５００００、酸価２．６５）に変更した以外は実施例１と同様にして比較例１の平版印刷版原版を作製した。
【０１４７】
〔平版印刷版原版の評価〕
（耐刷性の評価）
実施例１〜１３の平版印刷版原版及び比較例１の平版印刷版原版をＣｒｅｏ社製Ｔｒｅｎｄｓｅｔｔｅｒにて露光エネルギーを変えて、テストパターンを画像状に描き込みを行った。その後、富士写真フイルム（株）製現像液ＤＴ−２（希釈して、電導度４３ｍＳ／ｃｍとしたもの）を仕込んだ自動現像機ＬＰ−９４０Ｈ（富士写真フイルム（株）製）を用い、現像温度３０℃、現像時間１２秒で現像を行った。これを、小森コーポレーション（株）製印刷機リスロンを用いて連続して印刷した。この際、どれだけの枚数が充分なインキ濃度を保って印刷できるかを目視にて測定し、耐刷性を評価した。枚数が多いほど耐刷性に優れるものと評価する。結果を以下の表３に示す。
【０１４８】
（耐薬品性の評価）
実施例１〜１３の平版印刷版原版及び比較例１の平版印刷版原版を、上記耐刷性の評価と同様にして露光・現像および印刷を行った。この際、５，０００枚印刷する毎に、クリーナー（富士写真フイルム社製、マルチクリーナー）で版面を拭く工程を加え、耐薬品性を評価した。枚数が多いほど耐薬品性に優れるものと評価する。結果を以下の表３に示す。
【０１４９】
【表３】

【０１５０】
以上、表３から明らかなように、本発明に係るポリウレタン樹脂を下層の成分として用いた実施例１〜１３の平版印刷版原版は、耐刷性および耐薬品性に優れていることが確認された。特に、ポリマー内に芳香族骨格を有するポリウレタン樹脂については、他の実施例と比べても、耐刷性、耐薬品性共に一段と良好な結果が得られた。
一方、下層の成分として、本発明に係るポリウレタン樹脂を用いなかった比較例１の平版印刷版原版は、実施例のものと比べ、耐刷性、耐薬品性共に、著しく劣っていることが確認された。
【０１５１】
〔実施例１４〕
実施例１の支持体の作製において、陽極酸化処理を施した後、シリケート処理を行わなかった以外は、実施例１と同様の下塗り、記録層（下層・上層）を設け、実施例１４の平版印刷版原版を作製した。
【０１５２】
（耐刷性および耐薬品性の評価）
現像液として、６倍に希釈した富士写真フイルム（株）製シリケート現像液ＤＰ−４（２８℃）を用いた以外は、実施例１と同様の方法で耐刷性および耐薬品性の評価を行った。
結果は、耐刷性２０万枚、耐薬品性１８万枚であり、実施例１と同様の印刷枚数が得られた。このことにより、シリケート処理基板を用いた平版印刷版原版を非シリケート現像液で現像した実施例１〜１３と同様に、シリケートによる親水化処理を施さない基板を用いた平版印刷版原版をシリケート現像液で現像した実施例１４においても、本発明の効果である優れた耐刷性および耐薬品性が得られることが確認された。
【０１５３】
【発明の効果】
本発明によれば、デジタル信号に基づいた走査露光による直接製版が可能であり、且つ、耐刷性および耐薬品性に優れたポジ型平版印刷版原版を得ることができる。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a lithographic printing plate precursor that can be used as an offset printing master, and more particularly to a positive lithographic printing plate precursor for so-called direct plate making that can be directly made from a digital signal from a computer or the like.
[0002]
[Prior art]
In recent years, the development of lasers has been remarkable. In particular, solid-state lasers and semiconductor lasers having a light emitting region from the near infrared to the infrared can easily obtain high-power and small-sized lasers. In the field of lithographic printing, these lasers are very useful as an exposure light source for making a plate directly from digital data such as a computer.
[0003]
The positive type lithographic printing plate precursor for an infrared laser contains an alkali-soluble binder resin and an IR dye that absorbs light and generates heat as essential components. The IR dye or the like acts as a development inhibitor that substantially reduces the solubility of the binder resin in the developer by interaction with the binder resin in the unexposed area (image area), and in the exposed area (non-image area). The generated heat weakens the interaction between the IR dye and the binder resin and dissolves in an alkaline developer to form a lithographic printing plate.
[0004]
Since the image forming ability of such a positive lithographic printing plate precursor for infrared laser depends on the heat generated by infrared laser exposure on the surface of the recording layer, in the vicinity of the support, image formation is caused by diffusion of heat to the support, That is, the amount of heat used for solubilizing the recording layer is reduced, resulting in low sensitivity. Accordingly, there has been a problem that the effect of disappearing the development suppressing ability of the recording layer in the non-image area is not sufficiently obtained, and the difference between the image area and the non-image area becomes small and the highlight reproducibility is insufficient.
[0005]
In order to solve the above problem of highlight reproducibility, it is considered to use a recording layer made of a material capable of developing a non-image area more easily, i.e., having a better solubility in an alkaline aqueous solution. However, such a recording layer is chemically weak also in the image area, and is inferior in chemical resistance, such as being easily damaged by a developer, an ink washing solvent used during printing, a plate cleaner, and the like. In the unexposed area, the resin material is excellent in chemical resistance and durability of the film, and after the dissolution inhibiting action is released by exposure, the resin material having the characteristics of excellent developability is eagerly desired. It was.
[0006]
In order to solve the above problems, it comprises a lower layer excellent in alkali solubility containing a polyvinylphenol resin, and an upper layer that contains a water-insoluble and alkali-soluble resin and an infrared absorber and greatly increases the solubility in an alkaline aqueous solution upon exposure. A lithographic printing plate precursor provided with a recording layer is disclosed (for example, see Patent Document 1). This lithographic printing plate precursor was improved in sensitivity, but was insufficient in chemical resistance. Further, the adhesion between the support and the recording layer is insufficient, and there is a problem that the printing durability is poor.
Furthermore, various improved techniques have been proposed for the same purpose. For example, an image forming material obtained by laminating a lower layer containing a copolymer having a specific monomer and a photosensitive upper layer on a support (for example, Patent Document 2), and printing plate preparation using a lithographic printing plate precursor obtained by laminating a lower layer containing an alkali-soluble resin and an infrared-sensitive and alkali-resistant upper layer on a hydrophilic support. A method (for example, refer to Patent Document 3) has been proposed. Although the former is excellent in sensitivity and chemical resistance, there is a problem that the film strength of the resin used in the lower layer is insufficient and there is still room for improvement in printing durability. For the latter, the alkali-soluble resin used is chemical resistant. Since the recording layer elutes due to the solvent component contained in the plate cleaner, or the solvent component penetrates to the lower substrate interface, the adhesion between the recording layer and the substrate decreases, and the recording layer peels off. However, it is difficult to achieve both the printing durability depending on the film strength of the lower layer and the chemical resistance.
[0007]
[Patent Document 1]
JP-A-10-250255
[Patent Document 2]
JP 11-218914 A
[Patent Document 3]
Japanese Patent Laid-Open No. 11-194843
[0008]
[Problems to be solved by the invention]
An object of the present invention, which has been made in consideration of the drawbacks of the above-described conventional techniques, is a positive lithographic printing plate that can be directly made by scanning exposure based on a digital signal and that has excellent printing durability and chemical resistance. To provide the original version.
[0009]
[Means for Solving the Problems]
As a result of intensive studies, the present inventor has found that the above object can be achieved by providing a lower layer containing a polyurethane resin as a recording layer of a lithographic printing plate precursor, and has completed the present invention.
That is, the lithographic printing plate precursor of the present invention comprises a lower layer containing a water-insoluble and alkali-soluble polyurethane resin, a water-insoluble and alkali-soluble resin and a development inhibitor on a support, and is dissolved in an alkaline aqueous solution by exposure. And a recording layer composed of an upper layer with increased properties, and an infrared absorber is added to at least one of the lower layer and the upper layer of the recording layer.
[0010]
Although the action of the present invention is not clear, the water-insoluble and alkali-soluble polyurethane resin used in the lower layer of the lithographic printing plate precursor is excellent in film strength and contributes to improvement in printing durability even when formed alone. At the same time, for example, it is considered that it is less susceptible to damage by a plate cleaner or the like because it has excellent resistance to dissolution in an organic solvent or the like as compared with known acrylic alkali-soluble resins. Therefore, in the image area, that is, in the region where the upper image recording layer exists as an alkali-resistant development layer, high film strength and chemical resistance function effectively, and the upper layer is excellent in printing durability and chemical resistance. The removed non-image area is considered to dissolve and disperse quickly in an alkali developer due to the original alkali solubility.
[0011]
DETAILED DESCRIPTION OF THE INVENTION
The lithographic printing plate precursor of the present invention comprises a lower layer containing a water-insoluble and alkali-soluble polyurethane resin, a water-insoluble and alkali-soluble resin and a development inhibitor on a support, and is soluble in an alkaline aqueous solution upon exposure. A recording layer comprising an increasing upper layer is provided.
Hereinafter, each configuration of the lithographic printing plate precursor according to the invention will be described in detail sequentially.
[0012]
[Lower layer containing a water-insoluble and alkali-soluble polyurethane resin]
The lower layer according to the present invention is characterized by containing a water-insoluble and alkali-soluble polyurethane resin. The polyurethane resin used here is not particularly limited as long as it is insoluble in water and soluble in an alkaline aqueous solution, but among them, those having a carboxyl group in the polymer main chain are preferred, specifically, The basic skeleton is a reaction product of a diisocyanate compound represented by the following general formula (I) and at least one diol compound having a carboxyl group represented by the following general formula (II) or general formula (III). A polyurethane resin is mentioned.
[0013]
[Chemical 1]

[0014]
In formula (I), R ¹ Represents a divalent linking group. Examples of such a divalent linking group include aliphatic hydrocarbons, alicyclic hydrocarbons, and aromatic hydrocarbons. Preferably, the alkylene group has 2 to 10 carbon atoms, and has 6 to 30 carbon atoms. An arylene group is mentioned. The arylene group may be a group in which two or more ring structures are linked by a single bond or a divalent organic linking group such as a methylene group, or a condensed polycyclic structure. If necessary, R ¹ May have other functional groups that do not react with the isocyanate group in the formula (I), such as ester, urethane, amide, ureido group and the like.
In addition, R ¹ May have a substituent, and examples of the substituent that can be introduced include a halogen atom (—F, —Cl, —Br, —I), an alkyl group, an alkoxyl group, an alkyl ester group, a cyano group, and the like. Examples of the inert group include an isocyanate group.
Moreover, as a diisocyanate compound used for this invention, in addition to the thing represented by the said general formula (I), at the both ends of high molecular compounds, such as an oligomer or a polymer which consists of a diol compound mentioned later, for example, A high molecular weight diisocyanate compound having an isocyanate group may also be used.
[0015]
In formula (II), R ² Represents a hydrogen atom, an alkyl group, an aralkyl group, an aryl group, an alkoxy group or an aryloxy group. Where R ² May have a substituent, and examples of the substituent that can be introduced include a cyano group, a nitro group, a halogen atom (—F, —Cl, —Br, —I), —CONH. ₂ , -COOR ⁶ , -OR ⁶ , -NHCONHR ⁶ , -NHCOOR ⁶ , -NHCOR ⁶ , -OCONHR ⁶ , -CONHR ⁶ (Where R ⁶ Represents an alkyl group having 1 to 10 carbon atoms and an aralkyl group having 7 to 15 carbon atoms. ) And the like.
Preferred R ² Examples thereof include a hydrogen atom, an unsubstituted alkyl group having 1 to 8 carbon atoms, and an unsubstituted aryl group having 6 to 15 carbon atoms.
[0016]
In formula (II) or (III), R ³ , R ⁴ , R ⁵ May be the same or different and each represents a single bond or a divalent linking group. Examples of such a divalent linking group include aliphatic hydrocarbons and aromatic hydrocarbons. Where R ³ , R ⁴ , R ⁵ May have a substituent, and examples of the substituent that can be introduced include an alkyl group, an aralkyl group, an aryl group, an alkoxy group, and a halogen atom (—F, —Cl, —Br, —I) and the like. .
Preferred R ³ , R ⁴ , R ⁵ Examples thereof include an unsubstituted alkylene group having 1 to 20 carbon atoms and an unsubstituted arylene group having 6 to 15 carbon atoms, and more preferable examples include an unsubstituted alkylene group having 1 to 8 carbon atoms. Can be mentioned. If necessary, R ³ , R ⁴ , R ⁵ May have other functional groups that do not react with the isocyanate group in the above formula (I), such as ester, urethane, amide, ureido, and ether groups.
In addition, the above R ² , R ³ , R ⁴ , R ⁵ In these, two or three of them may be bonded to each other to form a ring structure.
[0017]
In formula (III), Ar represents a trivalent aromatic hydrocarbon which may have a substituent, and preferably an arylene group having 6 to 15 carbon atoms.
[0018]
Specific examples of the diisocyanate compound represented by the general formula (I) include those shown below, but the present invention is not limited thereto.
2,4-tolylene diisocyanate, dimer of 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, p-xylylene diisocyanate, metaxylylene diisocyanate, 4,4'-diphenylmethane diisocyanate, 1,5 An aromatic diisocyanate compound such as naphthylene diisocyanate, 3,3′-dimethylbiphenyl-4,4′-diisocyanate; an aliphatic diisocyanate compound such as hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, dimer acid diisocyanate; Isophorone diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2,4 (or 2,6) diisocyanate, 1,3- (isocyanate) Nate methyl) cycloaliphatic diisocyanate compounds such as cyclohexane; and diisocyanate compounds which are a reaction product of diol and diisocyanate such as an adduct of 1 mol of 1,3-butylene glycol and 2 mol of tolylene diisocyanate.
Among these, those having an aromatic ring such as 4,4′-diphenylmethane diisocyanate, xylylene diisocyanate, and tolylene diisocyanate are preferable from the viewpoint of printing durability.
[0019]
Specific examples of the diol compound having a carboxyl group represented by the general formula (II) or (III) include those shown below, but the present invention is not limited thereto.
3,5-dihydroxybenzoic acid, 2,2-bis (hydroxymethyl) propionic acid, 2,2-bis (hydroxyethyl) propionic acid, 2,2-bis (3-hydroxypropylpropionic acid, 2,2-bis (Hydroxymethyl) acetic acid, bis- (4-hydroxyphenyl) acetic acid, 4,4-bis- (4-hydroxyphenyl) pentanoic acid, tartaric acid and the like.
Among these, 2,2-bis (hydroxymethyl) propionic acid and 2,2-bis (hydroxyethyl) propionic acid are preferable from the viewpoint of reactivity with isocyanate.
[0020]
The polyurethane resin according to the present invention uses two or more diisocyanate compounds represented by the above general formula (I) and two or more diol compounds each having a carboxyl group represented by the general formula (II) or (III). May be formed.
In addition to the diol compound having a carboxyl group represented by the general formula (II) or (III), the diol compound does not have a carboxyl group and has a substituent that does not react with the isocyanate group in the formula (I). The diol compound that may be used may be used in combination so as not to lower the alkali developability.
[0021]
Specific examples of such a diol compound include those shown below.
For example, ethylene glycol, propylene glycol, neopentyl glycol, 1,3-butylene glycol, 1,6-hexanediol, 2-butene-1,4-diol, 2,2,4-trimethyl-1,3-pentanediol, 1,4-bis-β-hydroxyethoxycyclohexane, cyclohexanedimethanol, tricyclodecane dimethanol, hydrogenated bisphenol A, hydrogenated bisphenol F, ethylene oxide adduct of bisphenol A, propylene oxide adduct of bisphenol A, bisphenol F Ethylene oxide adduct, bisphenol F propylene oxide adduct, hydrogenated bisphenol A ethylene oxide adduct, hydrogenated bisphenol A propylene oxide adduct, hydroquinone dihydroxyethyl Ether, p-xylylene glycol, dihydroxyethyl sulfone, bis- (2-hydroxyethyl) -2,4-tolylene dicarbamate, 2,4-tolylene-bis- (2-hydroxyethylcarbamide), bis- (2- Hydroxyethyl) m-xylylene carbamate, bis- (2-hydroxyethyl phthalate) and the like can be used.
[0022]
The polyurethane resin according to the present invention can be synthesized by adding the above-mentioned diisocyanate compound and diol compound to an aprotic solvent by adding a known catalyst having an activity corresponding to the reactivity and heating.
The molar ratio of the diisocyanate and the diol compound to be used is preferably 0.8: 1 to 1.2: 1. When an isocyanate group remains at the end of the polymer, it is finally treated by treatment with alcohols or amines. Thus, it is synthesized in a form in which no isocyanate group remains.
In addition, the polyurethane resin according to the present invention preferably has an aromatic skeleton from the viewpoint of chemical resistance.
[0023]
The molecular weight of the polyurethane resin according to the present invention is preferably 1,000 or more in weight average, and more preferably in the range of 5,000 to 100,000. These polyurethane resins may be used alone or in combination of two or more.
[0024]
The content of these polyurethane resins contained in the lower layer component according to the present invention is about 50 to 99.5% by mass, preferably about 55 to 95% by mass in the total solid content.
[0025]
Further, in the lower layer component according to the present invention, in addition to the polyurethane resin, other resins can be used in combination as long as the effects of the present invention are not impaired. Since the lower layer itself needs to express alkali solubility, particularly in the non-image area, it is necessary to select a resin that does not impair this property. From this viewpoint, examples of resins that can be used in combination include water-insoluble and alkali-soluble resins. General water-insoluble and alkali-soluble resins will be described in detail below. Among them, for example, polyamide resins, epoxy resins, polyacetal resins, acrylic resins, methacrylic resins, polystyrene resins, novolac type phenol resins are preferable. Can be mentioned.
Moreover, it is preferable that it is 50 mass% or less with respect to the said polyurethane resin as a quantity to mix.
[0026]
[Upper layer that contains a water-insoluble and alkali-soluble resin and a development inhibitor and increases the solubility in an alkaline aqueous solution upon exposure]
The upper layer according to the present invention contains a water-insoluble and alkali-soluble resin (hereinafter, appropriately referred to as “alkali-soluble resin”) and a development inhibitor, and the solubility in an alkaline aqueous solution is increased by exposure. And Hereinafter, each component of the upper layer according to the present invention will be described.
[0027]
(Water-insoluble and alkali-soluble resin)
The alkali-soluble resin that can be used in the upper layer in the present invention is not particularly limited as long as it has a property of dissolving when contacted with an alkaline developer, but an acidic group is present in the main chain and / or side chain in the polymer. It is preferably a homopolymer to be contained, a copolymer thereof, or a mixture thereof. In particular, from the viewpoint of improving discrimination, it is preferable to use a novolac resin together with a development inhibitor described later as an upper layer component.
As such an alkali-soluble resin having an acidic group, in particular, a polymer compound having a functional group in any one of (1) a phenolic hydroxyl group, (2) a sulfonamide group, and (3) an active imide group. Can be mentioned. For example, although the following are illustrated, this invention is not limited to these.
[0028]
(1) Examples of the polymer compound having a phenolic hydroxyl group include phenol formaldehyde resin, m-cresol formaldehyde resin, p-cresol formaldehyde resin, m- / p-mixed cresol formaldehyde resin, phenol / cresol (m-, p Any of-or m- / p-mixing) may be used. Examples thereof include novolak resins such as mixed formaldehyde resins and pyrogallol acetone resins. In addition to this, a polymer compound having a phenolic hydroxyl group in the side chain is preferably used as the polymer compound having a phenolic hydroxyl group. As a polymer compound having a phenolic hydroxyl group in the side chain, a polymerizable monomer comprising a low molecular compound having at least one phenolic hydroxyl group and at least one polymerizable unsaturated bond is homopolymerized, or other polymerization is performed on the monomer. And a high molecular compound obtained by copolymerizing a functional monomer.
[0029]
Examples of the polymerizable monomer having a phenolic hydroxyl group include acrylamide, methacrylamide, acrylic acid ester, methacrylic acid ester, and hydroxystyrene having a phenolic hydroxyl group. Specifically, N- (2-hydroxyphenyl) acrylamide, N- (3-hydroxyphenyl) acrylamide, N- (4-hydroxyphenyl) acrylamide, N- (2-hydroxyphenyl) methacrylamide, N -(3-Hydroxyphenyl) methacrylamide, N- (4-Hydroxyphenyl) methacrylamide, o-Hydroxyphenyl acrylate, m-Hydroxyphenyl acrylate, p-Hydroxyphenyl acrylate, o-Hydroxyphenyl methacrylate , M-hydroxyphenyl methacrylate, p-hydroxyphenyl methacrylate, o-hydroxystyrene, m-hydroxystyrene, p-hydroxystyrene, 2- (2-hydroxyphenyl) ethyl acrylate, 2- (3-hydroxyphenyl) ethyl Acrylate, 2- 4-hydroxyphenyl) ethyl acrylate, 2- (2-hydroxyphenyl) ethyl methacrylate, 2- (3-hydroxyphenyl) ethyl methacrylate can be suitably used 2- (4-hydroxyphenyl) ethyl methacrylate. Such resins having a phenolic hydroxyl group may be used in combination of two or more. Furthermore, as described in U.S. Pat. No. 4,123,279, phenol and formaldehyde having an alkyl group having 3 to 8 carbon atoms as a substituent, such as t-butylphenol formaldehyde resin and octylphenol formaldehyde resin, These copolymers may be used in combination.
[0030]
(2) Examples of the alkali-soluble resin having a sulfonamide group include polymer compounds obtained by homopolymerizing a polymerizable monomer having a sulfonamide group or copolymerizing the monomer with another polymerizable monomer. Examples of the polymerizable monomer having a sulfonamide group include a sulfonamide group —NH—SO in which at least one hydrogen atom is bonded to a nitrogen atom in one molecule. ₂ -And a polymerizable monomer composed of a low molecular compound each having one or more polymerizable unsaturated bonds. Among them, a low molecular compound having an acryloyl group, an allyl group, or a vinyloxy group, and a substituted or monosubstituted aminosulfonyl group or a substituted sulfonylimino group is preferable.
[0031]
(3) The alkali-soluble resin having an active imide group is preferably one having an active imide group in the molecule, and the polymer compound has one unsaturated bond polymerizable with the active imide group in each molecule. Examples thereof include a polymer compound obtained by homopolymerizing a polymerizable monomer comprising the above-described low molecular weight compound, or copolymerizing the monomer with another polymerizable monomer.
As such a compound, specifically, N- (p-toluenesulfonyl) methacrylamide, N- (p-toluenesulfonyl) acrylamide and the like can be preferably used.
[0032]
The alkali-soluble resin according to the present invention includes a polymer compound obtained by polymerizing two or more of the polymerizable monomer having a phenolic hydroxyl group, the polymerizable monomer having a sulfonamide group, and the polymerizable monomer having an active imide group. It is preferable that Although there is no restriction | limiting in the copolymerization ratio of the said polymerizable monomer, and the combination of a polymerizable monomer, Especially the polymerizable monomer which has a sulfonamide group in the polymerizable monomer which has a phenolic hydroxyl group, and / or the polymerizable property which has an active imide group When the monomers are copolymerized, the compounding polymerization ratio of these components is preferably in the range of 50:50 to 5:95, and particularly preferably in the range of 40:60 to 10:90.
[0033]
Furthermore, as the alkali-soluble resin according to the present invention, one or more kinds selected from the polymerizable monomer having a phenolic hydroxyl group, the polymerizable monomer having a sulfonamide group, or the polymerizable monomer having an active imide group are used. In addition to the polymerizable monomer, a polymer compound obtained by copolymerizing another polymerizable monomer is preferable. As a copolymerization ratio in this case, it is preferable that the monomer which provides alkali solubility is contained 10 mol% or more, and what contains 20 mol% or more is more preferable. If the copolymerization component of the monomer imparting alkali solubility is less than 10 mol%, alkali solubility tends to be insufficient, and developability tends to be lowered.
Examples of other polymerizable monomers that can be used here include the compounds listed in the following (m1) to (m12), but the present invention is not limited thereto.
[0034]
(M1) Acrylic acid esters and methacrylic acid esters having an aliphatic hydroxyl group such as 2-hydroxyethyl acrylate or 2-hydroxyethyl methacrylate.
(M2) Alkyl acrylates such as methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, amyl acrylate, hexyl acrylate, octyl acrylate, benzyl acrylate, 2-chloroethyl acrylate, and glycidyl acrylate.
(M3) Alkyl methacrylates such as methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, amyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, 2-chloroethyl methacrylate and glycidyl methacrylate.
(M4) Acrylamide, methacrylamide, N-methylol acrylamide, N-ethyl acrylamide, N-hexyl methacrylamide, N-cyclohexyl acrylamide, N-hydroxyethyl acrylamide, N-phenyl acrylamide, N-nitrophenyl acrylamide, N-ethyl- Acrylamide or methacrylamide such as N-phenylacrylamide.
[0035]
(M5) Vinyl ethers such as ethyl vinyl ether, 2-chloroethyl vinyl ether, hydroxyethyl vinyl ether, propyl vinyl ether, butyl vinyl ether, octyl vinyl ether, and phenyl vinyl ether.
(M6) Vinyl esters such as vinyl acetate, vinyl chloroacetate, vinyl butyrate and vinyl benzoate.
(M7) Styrenes such as styrene, α-methylstyrene, methylstyrene, chloromethylstyrene.
(M8) Vinyl ketones such as methyl vinyl ketone, ethyl vinyl ketone, propyl vinyl ketone, and phenyl vinyl ketone.
(M9) Olefins such as ethylene, propylene, isobutylene, butadiene and isoprene.
(M10) N-vinylpyrrolidone, acrylonitrile, methacrylonitrile and the like.
(M11) Unsaturated imides such as maleimide, N-acryloylacrylamide, N-acetylmethacrylamide, N-propionylmethacrylamide, N- (p-chlorobenzoyl) methacrylamide.
(M12) Unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic anhydride and itaconic acid.
[0036]
When the alkali-soluble resin according to the present invention is a homopolymer or copolymer of a polymerizable monomer having a phenolic hydroxyl group, a polymerizable monomer having a sulfonamide group, or a polymerizable monomer having an active imide group, Those having a molecular weight of 2,000 or more and a number average molecular weight of 500 or more are preferred. More preferably, the weight average molecular weight is 5,000 to 300,000, the number average molecular weight is 800 to 250,000, and the dispersity (weight average molecular weight / number average molecular weight) is 1.1 to 10. .
In particular, when the alkali-soluble resin according to the present invention is a phenol formaldehyde resin or a cresol aldehyde resin, the weight average molecular weight is 500 to 20,000, and the number average molecular weight is 200 to 10,000. Is preferred.
[0037]
As the alkali-soluble resin used in the present invention, a resin having a phenolic hydroxyl group is desirable because it causes strong hydrogen bonding in the unexposed area and some hydrogen bonds are easily released in the exposed area. Among the resins having a phenolic hydroxyl group, a novolak resin is particularly preferable.
In the present invention, two or more kinds of alkali-soluble resins having different dissolution rates in an alkaline aqueous solution may be mixed and used, and the mixing ratio in that case is arbitrary. The alkali-soluble resin suitable for mixing with the resin having a phenolic hydroxyl group is preferably an acrylic resin because of its low compatibility with a resin having a phenolic hydroxyl group, and more preferably a sulfoamide group. It is an acrylic resin.
[0038]
Content of alkali-soluble resin with respect to the total solid content of the upper layer which concerns on this invention is used by the addition amount of 50-98 mass% collectively. When the addition amount of the alkali-soluble resin is less than 50% by mass, the durability of the recording layer is deteriorated, and when it exceeds 98% by mass, both the sensitivity and the durability are not preferable.
[0039]
(Development inhibitor)
The upper layer according to the present invention needs to contain a development inhibitor for the purpose of enhancing its inhibition (dissolution inhibiting ability).
The development inhibitor according to the present invention forms an interaction with the alkali-soluble resin, substantially lowers the solubility of the alkali-soluble resin in a developing solution in an unexposed area, and There is no particular limitation as long as the interaction is weakened and can be soluble in the developer, but quaternary ammonium salts, polyethylene glycol compounds, and the like are particularly preferably used. Among infrared absorbers and image colorants described later, there are compounds that function as a development inhibitor, and these are also preferred.
[0040]
Although it does not specifically limit as a quaternary ammonium salt, A tetraalkyl ammonium salt, a trialkyl aryl ammonium salt, a dialkyl diaryl ammonium salt, an alkyl triaryl ammonium salt, a tetraaryl ammonium salt, a cyclic ammonium salt, and a bicyclic ammonium salt are mentioned. .
Specifically, tetrabutylammonium bromide, tetrapentylammonium bromide, tetrahexylammonium bromide, tetraoctylammonium bromide, tetralaurylammonium bromide, tetraphenylammonium bromide, tetranaphthylammonium bromide, tetrabutylammonium chloride, tetrabutylammonium iodide , Tetrastearyl ammonium bromide, lauryl trimethyl ammonium bromide, stearyl trimethyl ammonium bromide, behenyl trimethyl ammonium bromide, lauryl triethyl ammonium bromide, phenyl trimethyl ammonium bromide, 3-trifluoromethylphenyl trimethyl ammonium bromide, benzyl trimethyl ammonium bromide De, dibenzyl dimethyl ammonium bromide, distearyl dimethyl ammonium bromide, tristearyl methyl ammonium bromide, benzyl triethyl ammonium bromide, hydroxyphenyl trimethyl ammonium bromide, N- methyl pyridinium bromide, and the like. In particular, quaternary ammonium salts described in Japanese Patent Application Nos. 2001-226297, 2001-370059, and 2001-398047 are preferable.
[0041]
The addition amount of the quaternary ammonium salt is preferably 0.1 to 50% by mass, and more preferably 1 to 30% by mass with respect to the total solid content of the upper layer. If it is less than 0.1% by mass, the effect of suppressing development is reduced, which is not preferable. Moreover, when adding exceeding 50 mass%, the film forming property of the said alkali-soluble resin may be adversely affected.
[0042]
Moreover, it does not specifically limit as a polyethyleneglycol compound, However, The thing of the structure represented by following General formula (1) is mentioned.
R ¹ -{-O- (R ³ -O-) _m -R ² } _n ... General formula (1)
In the general formula (1), R ¹ Represents a polyhydric alcohol residue or a polyhydric phenol residue, R ² Represents a hydrogen atom, an alkyl group having 1 to 25 carbon atoms which may have a substituent, an alkenyl group, an alkynyl group, an alkylyl group, an aryl group or an aryloyl group. R ³ Represents an alkylene residue which may have a substituent, m represents an average of 10 or more, and n represents an integer of 1 to 4.
[0043]
Examples of the polyethylene glycol compound represented by the general formula (1) include polyethylene glycols, polypropylene glycols, polyethylene glycol alkyl ethers, polypropylene glycol alkyl ethers, polyethylene glycol aryl ethers, polypropylene glycol aryl ethers, Polyethylene glycol alkyl aryl ethers, polypropylene glycol alkyl aryl ethers, polyethylene glycol glycerol esters, polypropylene glycol glycerol esters, polyethylene sorbitol esters, polypropylene glycol sorbitol esters, polyethylene glycol fatty acid esters, polypropylene glycol fatty acid esters, polyethylene glycol Lumpur ethylenediamines, polypropylene glycolated ethylenediamines, polyethylene glycolated diethylenetriamine, and polypropylene glycol diethylenetriamines.
[0044]
Further specific examples include polyethylene glycol 1000, polyethylene glycol 2000, polyethylene glycol 4000, polyethylene glycol 10000, polyethylene glycol 20000, polyethylene glycol 5000, polyethylene glycol 100000, polyethylene glycol 200000, polyethylene glycol 500000, polypropylene glycol 1500, polypropylene glycol. 3000, polypropylene glycol 4000, polyethylene glycol methyl ether, polyethylene glycol ethyl ether, polyethylene glycol phenyl ether, polyethylene glycol dimethyl ether, polyethylene glycol diethyl ether, polyethylene glycol diphenyl ether Ter, polyethylene glycol lauryl ether, polyethylene glycol dilauryl ether, polyethylene glycol nonyl ether, polyethylene glycol cetyl ether, polyethylene glycol stearyl ether, polyethylene glycol distearyl ether, polyethylene glycol behenyl ether, polyethylene glycol dibehenyl ether, polypropylene glycol methyl ether, Polypropylene glycol ethyl ether, polypropylene glycol phenyl ether, polypropylene glycol dimethyl ether, polypropylene glycol diethyl ether, polypropylene glycol diphenyl ether, polypropylene glycol lauryl ether, polypropylene glycol dilauryl ether , Polypropylene glycol nonyl ether, polyethylene glycol acetyl ester, polyethylene glycol diacetyl ester, polyethylene glycol benzoic acid ester, polyethylene glycol lauryl ester, polyethylene glycol dilauryl ester, polyethylene glycol nonyl acid ester, polyethylene glycol cetyl acid ester, polyethylene glycol stearoyl ester, Polyethylene glycol distearoyl ester, polyethylene glycol behenate ester, polyethylene glycol dibehenate ester, polypropylene glycol acetyl ester, polypropylene glycol diacetyl ester, polypropylene glycol benzoate ester, polypropylene glycol dibenzoate ester Polypropylene glycol laurate, polypropylene glycol dilaurate, polypropylene glycol nonyl ester, polyethylene glycol glycerol ether, polypropylene glycol glycerol ether, polyethylene glycol sorbitol ether, polypropylene glycol sorbitol ether, polyethylene glycolated ethylenediamine, polypropylene glycolated ethylenediamine Polyethylene glycolated diethylenetriamine, polypropylene glycolated diethylenetriamine, and polyethylene glycolated pentamethylenehexamine.
[0045]
The addition amount of the polyethylene glycol compound is preferably 0.1 to 50% by mass, and more preferably 1 to 30% by mass with respect to the total solid content of the upper layer. If it is less than 0.1% by mass, the effect of suppressing development is small, which is not preferable. When an amount exceeding 50% by mass is added, the polyethylene glycol compound that cannot interact with the alkali-soluble resin accelerates the penetration of the developer and may adversely affect image forming properties.
[0046]
In addition, when such measures are taken to increase the inhibition (dissolution suppression ability), the sensitivity decreases. In this case, it is effective to add a lactone compound to the upper layer to suppress the sensitivity decrease. is there. The lactone compound reacts with the lactone compound when the developer penetrates into the exposed area, that is, the recording layer in the area where the inhibition is released. It is considered that the sensitivity is improved by promoting the dissolution of the recording layer in the partial area. In the unexposed area, this lactone compound forms an interaction with a polar group in the alkali-soluble resin, for example, a hydroxyl group in the novolak resin, and is stable in the film together with a bulky structure having a ring. Therefore, even when an alkaline developer is contacted with the surface of the unexposed area, the rapid opening of the lactone ring during the development process is suppressed, so that the development resistance of the region is reduced. Absent. This interaction is released more easily by the exposure or heating than the inhibitory action by the dissolution inhibitor, so that the ring-opening reaction of the lactone compound in the exposed part is performed rapidly.
Such a lactone compound is not particularly limited, and examples thereof include compounds represented by the following general formula (LI) and general formula (L-II).
[0047]
[Chemical 2]

[0048]
In general formula (LI) and general formula (L-II), X ¹ , X ² , X ³ And X ⁴ Are divalent non-metallic atoms or non-metallic atomic groups constituting the ring, which may be the same or different. Moreover, these may each independently have a substituent. Furthermore, X in the general formula (LI) ¹ , X ² And X ³ And at least one of X in general formula (L-II) ¹ , X ² , X ³ And X ⁴ At least one of is preferably an electron-withdrawing substituent or a substituent substituted with an electron-withdrawing group.
[0049]
A preferred nonmetallic atom or nonmetallic atomic group is an atom or atomic group selected from a methylene group, a sulfinyl group, a carbonyl group, a thiocarbonyl group, a sulfonyl group, a sulfur atom, an oxygen atom, and a selenium atom, and more preferably, It is an atomic group selected from a methylene group, a carbonyl group and a sulfonyl group.
[0050]
In this specification, the electron-withdrawing substituent refers to a group in which Hammett's substituent constant σp takes a positive value. For Hammett's substituent constants, see Journal of Medicinal Chemistry, 1973, Vol. 16, no. 11, 1207-1216 etc. can be referred to. Examples of electron-withdrawing groups in which Hammett's substituent constant σp takes a positive valence include halogen atoms [fluorine atoms (σp value: 0.06), chlorine atoms (σp value: 0.23), bromine atoms (σp value). : 0.23), iodine atom (σp value: 0.18)], trihaloalkyl group [tribromomethyl (σp value: 0.29), trichloromethyl (σp value: 0.33), trifluoromethyl (σp Value: 0.54)], cyano group (σp value: 0.66), nitro group (σp value: 0.78), aliphatic / aryl or heterocyclic sulfonyl group [for example, methanesulfonyl (σp value: 0. 72)], aliphatic / aryl or heterocyclic acyl groups [for example, acetyl (σp value: 0.50), benzoyl (σp value: 0.43)], alkynyl groups [for example, C≡CH (σp value: 0) .23)], Aliphatic Ali Or a heterocyclic oxycarbonyl group [for example, methoxycarbonyl (σp value: 0.45), phenoxycarbonyl (σp value: 0.44)], carbamoyl group (σp value: 0.36), sulfamoyl group (σp value: 0.57), sulfoxide groups, heterocyclic groups, oxo groups, phosphoryl groups and the like.
[0051]
Preferred electron withdrawing groups include amide groups, azo groups, nitro groups, fluoroalkyl groups having 1 to 5 carbon atoms, nitrile groups, alkoxycarbonyl groups having 1 to 5 carbon atoms, and acyl groups having 1 to 5 carbon atoms. , An alkylsulfonyl group having 1 to 9 carbon atoms, an arylsulfonyl group having 6 to 9 carbon atoms, an alkylsulfinyl group having 1 to 9 carbon atoms, an arylsulfinyl group having 6 to 9 carbon atoms, and an arylcarbonyl group having 6 to 9 carbon atoms , A thiocarbonyl group, a fluorine-containing alkyl group having 1 to 9 carbon atoms, a fluorine-containing aryl group having 6 to 9 carbon atoms, a fluorine-containing allyl group having 3 to 9 carbon atoms, an oxo group, and a group selected from a halogen element. More preferably, a nitro group, a fluoroalkyl group having 1 to 5 carbon atoms, a nitrile group, an alkoxycarbonyl group having 1 to 5 carbon atoms, an acyl group having 1 to 5 carbon atoms, a carbon number 6 9 arylsulfonyl group, an arylcarbonyl group having 6 to 9 carbon atoms, an oxo group, and a halogen element.
Specific examples of the compounds represented by formulas (LI) and (L-II) are shown below, but the present invention is not limited to these compounds.
[0052]
[Chemical 3]

[0053]
[Formula 4]

[0054]
The addition amount of the compounds represented by the general formula (LI) and the general formula (L-II) is preferably 0.1 to 50% by mass, more preferably 1 to 30% by mass with respect to the total solid content of the upper layer. Is more preferable. If it is less than 0.1% by mass, the effect is small, and if it is added in excess of 50% by mass, the image formability is inferior.
Any one lactone compound may be used in the present invention, or two or more lactone compounds may be used in combination. When two or more types of compounds of general formula (LI) or two or more types of compounds of general formula (L-II) are used, they should be used in any ratio as long as the total addition amount is within the above range. Can do.
[0055]
In addition, substances that are thermally decomposable, such as onium salts, o-quinonediazide compounds, aromatic sulfone compounds, aromatic sulfonic acid ester compounds, and that substantially reduce the solubility of alkali-soluble resins when not decomposed. Is preferably used from the viewpoint of improving the inhibition of the image portion in the developer.
[0056]
Examples of the onium salts used in the present invention include diazonium salts, ammonium salts, phosphonium salts, iodonium salts, sulfonium salts, selenonium salts, arsonium salts, and the like. I. Schlesinger, Photogr. Sci. Eng. , 18, 387 (1974), T.A. S. Balet al, Polymer, 21, 423 (1980), diazonium salts described in JP-A-5-158230, U.S. Pat. Nos. 4,069,055, 4,069,056, and JP-A-3-140140. Ammonium salts described in the specification, D.I. C. Necker et al, Macromolecules, 17, 2468 (1984), C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988), U.S. Pat. Nos. 4,069,055 and 4,069,056,
[0057]
J. et al. V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), Chem. & Eng. News, Nov. 28, p31 (1988), European Patent No. 104,143, US Pat. Nos. 5,041,358, 4,491,628, JP-A-2-150848 and JP-A-2-296514. Iodonium salts, J.M. V. Crivello et al, Polymer J. et al. 17, 73 (1985), J. Am. V. Crivello et al. J. et al. Org. Chem. 43, 3055 (1978); R. Watt et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 22, 1789 (1984), J. Am. V. Crivello et al, Polymer Bull. , 14, 279 (1985),
[0058]
J. et al. V. Crivello et al, Macromolecules, 14 (5), 1141 (1981), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. 17, 2877 (1979), European Patents 370,693, 233,567, 297,443, 297,442, U.S. Pat. Nos. 4,933,377, 3,902,114 No. 4,491,628, No. 4,760,013, No. 4,734,444, No. 2,833,827, German Patent No. 2,904,626, No. 3,604 Sulfonium salts described in No. 580 and No. 3,604,581,
[0059]
J. et al. V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 17, 1047 (1979), a selenonium salt described in C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988).
Of these onium salts, a diazonium salt is particularly preferable. Particularly suitable diazonium salts include those described in JP-A-5-158230.
[0060]
The counter ion of the onium salt includes tetrafluoroboric acid, hexafluorophosphoric acid, triisopropylnaphthalenesulfonic acid, 5-nitro-o-toluenesulfonic acid, 5-sulfosalicylic acid, 2,5-dimethylbenzenesulfonic acid, 2,4,6-trimethylbenzenesulfonic acid, 2-nitrobenzenesulfonic acid, 3-chlorobenzenesulfonic acid, 3-bromobenzenesulfonic acid, 2-fluorocaprylnaphthalenesulfonic acid, dodecylbenzenesulfonic acid, 1-naphthol-5-sulfone Examples include acid, 2-methoxy-4-hydroxy-5-benzoyl-benzenesulfonic acid, and paratoluenesulfonic acid. Of these, particularly preferred are alkyl aromatic sulfonic acids such as hexafluorophosphoric acid, triisopropylnaphthalenesulfonic acid and 2,5-dimethylbenzenesulfonic acid.
[0061]
Suitable quinonediazides include o-quinonediazide compounds. The o-quinonediazide compound used in the present invention is a compound having at least one o-quinonediazide group, which increases alkali solubility by thermal decomposition, and compounds having various structures can be used. That is, o-quinonediazide assists the solubility of the upper layer by both the effect of losing the inhibition as a development inhibitor due to thermal decomposition and the change of o-quinonediazide itself into an alkali-soluble substance.
Examples of such o-quinonediazide compounds include J. Org. The compounds described in pages 339 to 352 of “Light-sensitive systems” by John Coley (John Wiley & Sons. Inc.) can be used, and in particular, o-quinonediazide reacted with various aromatic polyhydroxy compounds or aromatic amino compounds. The sulfonic acid esters or sulfonic acid amides are preferred. Further, benzoquinone (1,2) -diazide sulfonic acid chloride or naphthoquinone- (1,2) -diazide-5-sulfonic acid chloride and pyrogallol-acetone resin as described in JP-B-43-28403 Esters of benzoquinone- (1,2-diazide sulfonic acid chloride or naphthoquinone- (1,2) -diazide-5 described in US Pat. Nos. 3,046,120 and 3,188,210 Esters of sulfonic acid chloride and phenol-formaldehyde resin are also preferably used.
[0062]
Further, an ester of naphthoquinone- (1,2) -diazido-4-sulfonic acid chloride and phenol formaldehyde resin or cresol-formaldehyde resin, naphthoquinone- (1,2) -diazido-4-sulfonic acid chloride and pyrogallol-acetone resin Similarly, the esters are also preferably used. Other useful o-quinonediazide compounds are reported and known in numerous patents. For example, JP-A-47-5303, JP-A-48-63802, JP-A-48-63803, JP-A-48-96575, JP-A-49-38701, JP-A-48-13354, Japanese Patent Publication Nos. 41-11222, 45-9610, 49-17474, U.S. Pat. Nos. 2,797,213, 3,454,400, 3,544,323, 3,573,917, 3,674,495, 3,785,825, British Patents 1,227,602, 1,251,345, 1,267, No. 005, No. 1,329,888, No. 1,330,932, German Patent No. 854,890, and the like.
[0063]
The addition amount of the o-quinonediazide compound is preferably in the range of 1 to 50% by mass, more preferably 5 to 30% by mass, and particularly preferably 10 to 30% by mass with respect to the total solid content of the upper layer. These compounds can be used alone, but may be used as a mixture of several kinds.
Moreover, you may include the alkali-soluble resin by which at least one part of Unexamined-Japanese-Patent No. 11-288089 was esterified.
[0064]
Further, for the purpose of enhancing the inhibition of the scratch on the surface as well as the inhibition of the recording layer surface, the perfluoroalkyl having 3 to 20 carbon atoms in the molecule as described in JP-A-2000-187318. It is preferable to use a polymer having a (meth) acrylate monomer having 2 or 3 groups as a polymerization component.
As addition amount, 0.1-10 mass% is preferable with respect to upper layer total solid, More preferably, it is 0.5-5 mass%.
[0065]
[Infrared absorber]
In the lithographic printing plate precursor according to the invention, it is necessary to add an infrared absorber to at least one of the lower layer and the upper layer of the recording layer. Such an infrared absorber is not particularly limited as long as it is a dye that absorbs infrared light and generates heat, and various dyes known as infrared absorbers can be used.
[0066]
As the infrared absorber according to the present invention, commercially available dyes and known ones described in literature (for example, “Dye Handbook” edited by the Society of Synthetic Organic Chemistry, published in 1970) can be used. Specific examples include azo dyes, metal complex azo dyes, pyrazolone azo dyes, anthraquinone dyes, phthalocyanine dyes, carbonium dyes, quinoneimine dyes, methine dyes, and cyanine dyes. In the present invention, among these dyes, those that absorb infrared light or near infrared light are particularly preferred because they are suitable for use in lasers that emit infrared light or near infrared light.
[0067]
Examples of dyes that absorb such infrared light or near infrared light include, for example, JP-A-58-125246, JP-A-59-84356, JP-A-59-202829, and JP-A-60-78787. Methine dyes described in JP-A-58-173696, JP-A-58-181690, JP-A-58-194595, etc., JP-A-58-112793, Naphthoquinone dyes described in JP-A-58-224793, JP-A-59-48187, JP-A-59-73996, JP-A-60-52940, JP-A-60-63744, etc. Examples thereof include squarylium dyes described in 58-112792 and cyanine dyes described in British Patent 434,875.
[0068]
Further, near-infrared absorption sensitizers described in US Pat. No. 5,156,938 are also preferably used as dyes, and substituted arylbenzo (thio) pyrylium described in US Pat. No. 3,881,924. Salts, trimethine thiapyrylium salts described in JP-A-57-142645 (US Pat. No. 4,327,169), JP-A-58-181051, 58-220143, 59-41363, 59 -84248, 59-84249, 59-146063, 59-146061, pyrylium compounds described in JP-A-59-216146, cyanine dyes, U.S. Pat. No. 4,283,475 The pentamethine thiopyrylium salt described in No. 5 and the pyrylium compound disclosed in Japanese Patent Publication Nos. 5-13514 and 5-19702 Commercially available products, Eporin Co. Epolight III-178, Epolight III-130, Epolight III-125 and the like are particularly preferably used.
Another particularly preferable example of the dye is a near-infrared absorbing dye described as formulas (I) and (II) in US Pat. No. 4,756,993.
[0069]
These infrared absorbers are preferably added to the upper layer of the recording layer or in the vicinity thereof from the viewpoint of sensitivity. In particular, when a substance having a dissolution inhibiting ability such as a cyanine dye is added together with the alkali-soluble resin, at the same time as increasing the sensitivity, the unexposed area can be made resistant to alkali. These infrared absorbers may be added to the lower layer or both the upper and lower layers. By adding it to the lower layer, it is possible to further increase the sensitivity. When an infrared absorber is added to both the upper layer and the lower layer, the same compound may be used, or different compounds may be used.
These infrared absorbers may be added to the same layer as the recording layer, or another layer may be provided and added thereto. In the case of a separate layer, it is desirable to add it to a layer adjacent to the recording layer.
Furthermore, when the infrared absorber is a compound having dissolution inhibiting ability, the infrared absorber can be used not only as a photothermal conversion function but also as the development inhibitor by being contained in the same layer as the alkali-soluble resin. It is preferable because it functions.
[0070]
As addition amount of an infrared absorber, when adding to an upper layer, it is 0.01-50 mass% with respect to upper layer total solid, Preferably it is 0.1-30 mass%, Most preferably, it is 1.0-30 mass%. It can be added in proportions. If the addition amount is less than 0.01% by mass, the sensitivity is lowered, and if it exceeds 50% by mass, the uniformity of the upper recording layer is lost and the durability of the upper recording layer is deteriorated.
[0071]
Moreover, when adding to a lower layer, it is 0-20 mass% with respect to a lower layer total solid, Preferably it is 0-10 mass%, Most preferably, it can add in the ratio of 0-5 mass%. When an infrared absorber is added to the lower layer, the solubility of the lower layer decreases if an infrared absorber having dissolution inhibiting ability is used. On the other hand, the infrared absorber generates heat during infrared laser exposure and improves the solubility of the lower layer due to heat. In view of these balances, the compound to be added and the amount to be added should be selected. In the region of 0.2 to 0.3 μm in the vicinity of the support, it is difficult to obtain the effect of improving the solubility due to heat, for example, the heat generated during exposure diffuses to the support. In some cases, the decrease in sensitivity may cause a decrease in sensitivity. Therefore, even within the range of the addition amount shown above, such an addition amount that the dissolution rate in the lower layer developer (25 ° C. to 30 ° C.) is lower than 30 nm / sec is not preferable.
[0072]
[Other additives]
In forming the lower layer and the upper layer of the recording layer, various additives can be added as necessary, in addition to the above essential components, as long as the effects of the present invention are not impaired. The additives listed below may be added only to the lower layer, may be added only to the upper layer, or may be added to both layers.
[0073]
(Development accelerator)
For the purpose of improving sensitivity, acid anhydrides, phenols, and organic acids may be added to the upper layer and / or the lower layer, which are recording layers according to the present invention.
As the acid anhydrides, cyclic acid anhydrides are preferable. Specific examples of the cyclic acid anhydrides include phthalic anhydride, tetrahydrophthalic anhydride, and hexahydrophthalic anhydride described in US Pat. No. 4,115,128. Acid, 3,6-endooxy-tetrahydrophthalic anhydride, tetrachlorophthalic anhydride, maleic anhydride, chloromaleic anhydride, α-phenylmaleic anhydride, succinic anhydride, pyromellitic anhydride and the like can be used. Examples of the non-cyclic acid anhydride include acetic anhydride.
[0074]
Examples of phenols include bisphenol A, 2,2′-bishydroxysulfone, p-nitrophenol, p-ethoxyphenol, 2,4,4′-trihydroxybenzophenone, 2,3,4-trihydroxybenzophenone, 4- Examples include hydroxybenzophenone, 4,4 ′, 4 ″ -trihydroxytriphenylmethane, 4,4 ′, 3 ″, 4 ″ -tetrahydroxy-3,5,3 ′, 5′-tetramethyltriphenylmethane. .
[0075]
Examples of organic acids include sulfonic acids, sulfinic acids, alkyl sulfates, phosphonic acids, phosphate esters, and carboxylic acids described in JP-A-60-88942 and JP-A-2-96755. Specifically, p-toluenesulfonic acid, dodecylbenzenesulfonic acid, p-toluenesulfinic acid, ethyl sulfate, phenylphosphonic acid, phenylphosphinic acid, phenyl phosphate, diphenyl phosphate, benzoic acid, isophthalic acid, adipic acid , P-toluic acid, 3,4-dimethoxybenzoic acid, phthalic acid, terephthalic acid, 4-cyclohexene-1,2-dicarboxylic acid, erucic acid, lauric acid, n-undecanoic acid, ascorbic acid and the like.
The proportion of the acid anhydride, phenols, and organic acids in the total solid content of the lower layer or upper layer is preferably 0.05 to 20% by mass, more preferably 0.1 to 15% by mass, and particularly preferably 0.8. 1 to 10% by mass.
[0076]
(Surfactant)
In order to improve the coating properties and to improve the stability of the processing with respect to the developing conditions, the upper layer and / or the lower layer, which are the recording layers according to the present invention, are disclosed in Japanese Patent Application Laid-Open Nos. 62-251740 and 3- Nonionic surfactants as described in Japanese Patent No. 208514, amphoteric surfactants as described in Japanese Patent Application Laid-Open Nos. 59-121044 and 4-13149, and described in EP950517 Such siloxane compounds, fluorine-containing monomer copolymers as described in JP-A-62-170950, JP-A-11-288093, and Japanese Patent Application No. 2001-247351 can be added.
[0077]
Specific examples of the nonionic surfactant include sorbitan tristearate, sorbitan monopalmitate, sorbitan trioleate, stearic acid monoglyceride, polyoxyethylene nonylphenyl ether and the like. Specific examples of amphoteric activators include alkyldi (aminoethyl) glycine, alkylpolyaminoethylglycine hydrochloride, 2-alkyl-N-carboxyethyl-N-hydroxyethylimidazolinium betaine and N-tetradecyl-N, N-betaine. Type (for example, trade name “Amorgen K” manufactured by Daiichi Kogyo Co., Ltd.).
[0078]
As the siloxane compound, a block copolymer of dimethylsiloxane and polyalkylene oxide is preferable. Specific examples include DBE-224, DBE-621, DBE-712, DBP-732, DBP-534, manufactured by Chisso Corporation. And polyalkylene oxide-modified silicones such as Tego Glide 100 manufactured by Tego, Germany.
The proportion of the nonionic surfactant and amphoteric surfactant in the total solid content of the lower layer or upper layer is preferably 0.01 to 15% by mass, more preferably 0.1 to 5% by mass, and still more preferably 0.8. It is 05-2.0 mass%.
[0079]
(Bake-out agent / colorant)
To the upper layer and / or the lower layer, which is the recording layer according to the present invention, a print-out agent for obtaining a visible image immediately after heating by exposure, or a dye or pigment as an image colorant can be added.
A representative example of the printing-out agent is a combination of a compound that releases an acid by heating by exposure (photoacid releasing agent) and an organic dye that can form a salt. Specifically, combinations of o-naphthoquinonediazide-4-sulfonic acid halides and salt-forming organic dyes described in JP-A-50-36209 and JP-A-53-8128, 36223, 54-74728, 60-3626, 61-143748, 61-151644, and 63-58440, and trihalomethyl compounds and salt-forming organic dyes Can be mentioned. Such trihalomethyl compounds include oxazole-based compounds and triazine-based compounds, both of which have excellent temporal stability and give clear printout images.
[0080]
As the image colorant, other dyes can be used in addition to the aforementioned salt-forming organic dyes. Examples of suitable dyes including salt-forming organic dyes include oil-soluble dyes and basic dyes. Specifically, Oil Yellow # 101, Oil Yellow # 103, Oil Pink # 312, Oil Green BG, Oil Blue BOS, Oil Blue # 603, Oil Black BY, Oil Black BS, Oil Black T-505 (above Orient Chemical Industry) Co., Ltd.), Victoria Pure Blue, Crystal Violet Lactone, Crystal Violet (CI42555), Methyl Violet (CI42535), Ethyl Violet, Rhodamine B (CI145170B), Malachite Green (CI42000), Methylene Blue (CI522015), and the like. it can. The dyes described in JP-A-62-293247 are particularly preferred.
These dyes can be added in a proportion of 0.01 to 10% by mass, preferably 0.1 to 3% by mass, based on the total solid content of the lower layer or upper layer.
[0081]
(Plasticizer)
A plasticizer may be added to the upper layer and / or the lower layer, which is the recording layer according to the present invention, in order to impart flexibility and the like of the coating film. For example, butylphthalyl, polyethylene glycol, tributyl citrate, diethyl phthalate, dibutyl phthalate, dihexyl phthalate, dioctyl phthalate, tricresyl phosphate, tributyl phosphate, trioctyl phosphate, tetrahydrofurfuryl oleate, acrylic acid or methacrylic acid These oligomers and polymers are used.
These plasticizers can be added at a ratio of 0.5 to 10% by mass, preferably 1.0 to 5% by mass, based on the total solid content of the lower layer or the upper layer.
[0082]
(WAX agent)
In the upper layer according to the present invention, for the purpose of imparting resistance to scratches, a compound that reduces the static friction coefficient of the surface can be added. Specifically, US Pat. No. 6,117,913 or Japanese Patent Application Nos. 2001-261627, 2002-032904, and 2002-165854 previously proposed by the applicant of the present application. And compounds having an ester of a long-chain alkyl carboxylic acid as described in the above. The addition amount is preferably 0.1 to 10% by mass, more preferably 0.5 to 5% by mass in the upper layer.
[0083]
[Formation of recording layer]
The lower layer and the upper layer in the lithographic printing plate precursor according to the invention can be usually formed by dissolving the above-described components in a solvent and coating the solution on a suitable support.
Solvents used here include ethylene dichloride, cyclohexanone, methyl ethyl ketone, methanol, ethanol, propanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, 2-methoxyethyl acetate, 1-methoxy-2-propyl acetate, dimethoxy Examples include ethane, methyl lactate, ethyl lactate, N, N-dimethylacetamide, N, N-dimethylformamide, tetramethylurea, N-methylpyrrolidone, dimethyl sulfoxide, sulfolane, γ-butyrolactone, and toluene. It is not limited. These solvents are used alone or in combination.
[0084]
In principle, the lower layer and the upper layer are preferably formed by separating two layers.
As a method for forming the two layers separately, for example, a method using a difference in solvent solubility between a component contained in the lower layer and a component contained in the upper layer, or after applying the upper layer, a solvent is rapidly used. For example, a method of drying and removing.
Hereinafter, although these methods are explained in full detail, the method of apply | coating two layers separately is not limited to these.
[0085]
As a method of utilizing the difference in solvent solubility between the component contained in the lower layer and the component contained in the upper layer, a solvent system in which any of the components contained in the lower layer is insoluble is used when the upper layer coating solution is applied. Is. Thereby, even if it carries out 2 layer application | coating, it becomes possible to isolate | separate each layer clearly and to make a coating film. For example, as the lower layer component, a component insoluble in a solvent such as methyl ethyl ketone or 1-methoxy-2-propanol that dissolves the alkali-soluble resin that is the upper layer component is selected, and the lower layer is applied using a solvent system that dissolves the lower layer component. -It is possible to form two layers by drying and then dissolving the upper layer mainly composed of alkali-soluble resin with methyl ethyl ketone, 1-methoxy-2-propanol, etc., and applying and drying.
[0086]
Next, after applying the second layer (upper layer), as a method of drying the solvent very quickly, high-pressure air is blown from a slit nozzle installed substantially perpendicular to the web traveling direction, or heating such as steam is performed. This can be achieved by applying thermal energy as conduction heat from the lower surface of the web from a roll (heating roll) supplied inside the medium, or by combining them.
[0087]
In addition, in order to impart a new function, the upper layer and the lower layer may be partly compatible in a range where the effects of the present invention are sufficiently exhibited. Such a method can be achieved by adjusting the degree of any of the above methods using the difference in solvent solubility and the method of drying the solvent very quickly after coating the second layer.
[0088]
The concentration of the above-described components (total solid content including additives) in the lower layer / upper layer coating solution to be coated on the support is preferably 1 to 50% by mass.
Various methods can be used as the coating method, and examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.
In particular, in order to prevent damage to the lower layer when the upper layer is applied, the upper layer application method is preferably a non-contact type. Further, although it is a contact type, it is possible to use bar coater coating as a method generally used for solvent-based coating, but it is desirable to perform coating by forward rotation in order to prevent damage to the lower layer.
[0089]
The coating amount after drying of the lower layer component coated on the support of the planographic printing plate precursor of the present invention is 0.5 to 4.0 g / m. ² Preferably, it is in the range of 0.6 to 2.5 g / m. ² Range. 0.5g / m ² If it is less than the range, printing durability will be reduced, and 4.0 g / m. ² Exceeding this is not preferable because the image reproducibility deteriorates and the sensitivity decreases.
The coating amount after drying the upper layer component is 0.05 to 1.0 g / m. ² Is preferably in the range of 0.08 to 0.7 g / m. ² Range. 0.05g / m ² If it is less than 1.0 g / m, the development latitude and scratch resistance will be reduced. ² Exceeding this is not preferable because the sensitivity decreases.
The coating amount after drying of the lower layer and the upper layer is 0.6 to 4.0 g / m. ² Is preferably in the range of 0.7 to 2.5 g / m. ² Range. 0.6 g / m ² If it is less than the range, printing durability will be reduced, and 4.0 g / m. ² Exceeding this is not preferable because the image reproducibility deteriorates and the sensitivity decreases.
[0090]
[Support]
The support used in the lithographic printing plate precursor according to the present invention is not particularly limited as long as it is a dimensionally stable plate having the required strength and durability. For example, paper, plastic (for example, Paper laminated with polyethylene, polypropylene, polystyrene, etc., metal plate (eg, aluminum, zinc, copper, etc.), plastic film (eg, cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, Cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), paper laminated with metal as described above, vapor-deposited paper, or plastic film.
[0091]
Among them, in the present invention, a polyester film or an aluminum plate is preferable, and among them, an aluminum plate that has good dimensional stability and is relatively inexpensive is particularly preferable. A suitable aluminum plate is a pure aluminum plate or an alloy plate containing aluminum as a main component and containing a trace amount of foreign elements, and may be a plastic film on which aluminum is laminated or vapor-deposited. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is at most 10% by mass.
[0092]
Particularly suitable aluminum in the present invention is pure aluminum, but completely pure aluminum is difficult to produce in the refining technique, and may contain slightly different elements.
Thus, the composition of the aluminum plate applied to the present invention is not specified, and an aluminum plate made of a publicly known material can be appropriately used. The thickness of the aluminum plate used in the present invention is about 0.1 mm to 0.6 mm, preferably 0.15 mm to 0.4 mm, and particularly preferably 0.2 mm to 0.3 mm.
[0093]
Such an aluminum plate may be subjected to surface treatment such as roughening treatment or anodizing treatment, if necessary. Hereinafter, such a surface treatment will be briefly described.
Prior to roughening the aluminum plate, a degreasing treatment with, for example, a surfactant, an organic solvent, or an alkaline aqueous solution for removing rolling oil on the surface is performed as desired. The surface roughening treatment of the aluminum plate is performed by various methods. For example, a method of mechanically roughening, a method of electrochemically dissolving and roughening a surface, and a method of selectively dissolving a surface chemically. This is done by the method of As the mechanical method, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used. Further, as an electrochemical surface roughening method, there is a method of performing alternating current or direct current in hydrochloric acid or nitric acid electrolyte. Further, as disclosed in JP-A-54-63902, a method in which both are combined can also be used.
The aluminum plate roughened as described above is subjected to an alkali etching treatment and neutralization treatment as necessary, and then subjected to an anodizing treatment if desired in order to enhance the water retention and wear resistance of the surface. As the electrolyte used for the anodizing treatment of the aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, phosphoric acid, oxalic acid, chromic acid, or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.
[0094]
The anodizing treatment conditions vary depending on the electrolyte used and cannot be specified in general, but in general, the electrolyte concentration is 1 to 80% by mass solution, the liquid temperature is 5 to 70 ° C., and the current density is 5 to 60 A / dm. ² A voltage of 1 to 100 V and an electrolysis time of 10 seconds to 5 minutes are suitable. The amount of anodized film is 1.0 g / m ² If it is less, the printing durability is insufficient, or the non-image part of the lithographic printing plate is easily scratched, and so-called “scratch stains” in which ink adheres to the scratched part during printing tend to occur.
After the anodizing treatment, the aluminum surface is subjected to a hydrophilic treatment if necessary.
[0095]
The hydrophilization treatment used in the present invention is disclosed in US Pat. Nos. 2,714,066, 3,181,461, 3,280,734 and 3,902,734. There are alkali metal silicate (such as aqueous sodium silicate) methods. In this method, the support is immersed in an aqueous sodium silicate solution or electrolytically treated. In addition, it is disclosed in potassium fluoride zirconate disclosed in Japanese Patent Publication No. 36-22063 and US Pat. Nos. 3,276,868, 4,153,461, and 4,689,272. A method of treating with polyvinylphosphonic acid is used.
[0096]
(Undercoat layer)
The lithographic printing plate precursor according to the invention is provided by laminating the lower layer and the upper layer on a support, and if necessary, an undercoat layer may be provided between the support and the lower layer. it can.
Various organic compounds are used as the primer layer component. For example, phosphonic acids having an amino group such as carboxymethylcellulose, dextrin, gum arabic, 2-aminoethylphosphonic acid, and phenylphosphonic acid which may have a substituent Organic phosphonic acids such as naphthyl phosphonic acid, alkyl phosphonic acid, glycero phosphonic acid, methylene diphosphonic acid and ethylene diphosphonic acid, phenyl phosphoric acid, naphthyl phosphoric acid, alkyl phosphoric acid and glycerophosphoric acid which may have a substituent Organic phosphoric acid, optionally substituted phenylphosphinic acid, naphthylphosphinic acid, alkylphosphinic acid, glycerophosphinic acid and other organic phosphinic acids, glycine and β-alanine amino acids, and triethanolamine hydrochloric acid Has a hydroxy group such as salt -Alanine, and hydrochlorides of amines that may be used in combination of two or more.
[0097]
This organic undercoat layer can be provided by the following method. That is, a method in which water or an organic solvent such as methanol, ethanol, methyl ethyl ketone, or a mixed solvent thereof is dissolved and applied on an aluminum plate and dried, and water, methanol, ethanol, methyl ethyl ketone, etc. In this method, an aluminum plate is immersed in a solution obtained by dissolving the organic compound in an organic solvent or a mixed solvent thereof to adsorb the compound, and then washed with water and dried to provide an organic undercoat layer. . In the former method, a solution having a concentration of 0.005 to 10% by mass of the organic compound can be applied by various methods. In the latter method, the concentration of the solution is 0.01 to 20% by mass, preferably 0.05 to 5% by mass, the immersion temperature is 20 to 90 ° C., preferably 25 to 50 ° C., and the immersion time is 0.1 second to 20 minutes, preferably 2 seconds to 1 minute. The solution used for this can be adjusted to a pH range of 1 to 12 with basic substances such as ammonia, triethylamine, potassium hydroxide, and acidic substances such as hydrochloric acid and phosphoric acid. A yellow dye can also be added to improve the tone reproducibility of the image recording material.
The coverage of the organic undercoat layer is 2 to 200 mg / m ² Is suitable, preferably 5 to 100 mg / m ² It is. The above coating amount is 2 mg / m ² If it is less, sufficient printing durability cannot be obtained. 200 mg / m ² It is the same even if it is larger.
The lithographic printing plate precursor produced as described above is imagewise exposed and then developed.
[0098]
(Back coat layer)
A back coat layer is provided on the back surface of the support of the lithographic printing plate precursor according to the invention, if necessary. Such a back coat layer comprises a metal oxide obtained by hydrolysis and polycondensation of an organic polymer compound described in JP-A-5-45885 and an organic or inorganic metal compound described in JP-A-6-35174. A coating layer is preferably used. Of these coating layers, Si (OCH ₃ ) ₄ , Si (OC ₂ H ₅ ) ₄ , Si (OC ₃ H ₇ ) ₄ , Si (OC ₄ H ₉ ) ₄ A silicon alkoxy compound such as the above is inexpensive and readily available, and a metal oxide coating layer obtained therefrom is particularly preferable because of its excellent developer resistance.
[0099]
〔exposure〕
The actinic ray light source used for image exposure of the lithographic printing plate precursor according to the present invention is preferably a light source having an emission wavelength in the near infrared to infrared region, and a solid laser or a semiconductor laser is particularly preferred.
[0100]
[Development processing]
The developer that can be applied to the development processing of the lithographic printing plate precursor according to the invention is a developer having a pH in the range of 9.0 to 14.0, preferably in the range of 12.0 to 13.5. A conventionally known alkaline aqueous solution can be used as the developer (hereinafter referred to as developer including the replenisher). For example, sodium silicate, potassium, tribasic sodium phosphate, potassium, ammonium, dibasic sodium phosphate, potassium, ammonium, sodium carbonate, potassium, ammonium, sodium bicarbonate, potassium, Examples thereof include inorganic alkali salts such as ammonium, sodium borate, potassium, ammonium, sodium hydroxide, ammonium, potassium and lithium. Moreover, monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropylamine, diisopropylamine, triisopropylamine, n-butylamine, monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, Organic alkali agents such as ethyleneimine, ethylenediamine, and pyridine are listed. These alkaline aqueous solutions may be used individually by 1 type, and may use 2 or more types together.
[0101]
Among the above alkaline aqueous solutions, one of the developers exhibiting the effect of the present invention contains one containing an alkali silicate as a base, or an alkali silicate mixed with a silicon compound in a base, The so-called “silicate developer” is an aqueous solution having a pH of 12 or more, and another more preferable developer does not contain an alkali silicate and contains a non-reducing sugar (an organic compound having a buffering action) and a base. “Non-silicate developer”.
[0102]
In the former, the aqueous solution of alkali metal silicate is silicon oxide SiO which is a component of silicate. ₂ And alkali metal oxide M ₂ O ratio (generally [SiO ₂ ] / [M ₂ The development property can be adjusted by adjusting the concentration and the concentration of O], for example, as disclosed in JP-A-54-62004. ₂ / Na ₂ The molar ratio of O is 1.0 to 1.5 (ie [SiO ₂ ] / [Na ₂ O] is 1.0 to 1.5), and SiO ₂ An aqueous solution of sodium silicate having a content of 1 to 4% by mass, or as described in JP-B-57-7427, [SiO 2 ₂ ] / [M] is 0.5 to 0.75 (ie, [SiO ₂ ] / [M ₂ O] is 1.0 to 1.5), and SiO ₂ An aqueous solution of an alkali metal silicate, wherein the concentration is from 1 to 4% by weight and the developer contains at least 20% potassium, based on gram atoms of all alkali metals present therein. Preferably used.
[0103]
A so-called “non-silicate developer” that does not contain an alkali silicate and contains a non-reducing sugar and a base is also preferable for application to the development of the lithographic printing plate precursor according to the invention. When the development processing of the lithographic printing plate precursor is performed using this developer, the surface of the recording layer is not deteriorated and the thickness of the recording layer can be maintained in a better state.
[0104]
The main component of the developer is preferably composed of at least one compound selected from non-reducing sugars and at least one base, and the pH of the solution is in the range of 9.0 to 13.5. Such non-reducing sugars are saccharides that do not have a free aldehyde group or ketone group and do not exhibit reducing properties, and are trehalose-type oligosaccharides in which reducing groups are bonded to each other, and glycosides in which a reducing group of saccharides and non-saccharides are bonded. It is classified into sugar alcohols reduced by hydrogenating the body and saccharides, and any of them is preferably used. Trehalose type oligosaccharides include saccharose and trehalose. Examples of glycosides include alkyl glycosides, phenol glycosides, mustard oil glycosides, and the like. Examples of the sugar alcohol include D, L-arabit, rebit, xylit, D, L-sorbit, D, L-mannit, D, L-exit, D, L-talit, zulsiit and allozulcit. Furthermore, maltitol obtained by hydrogenation of a disaccharide and a reduced form (reduced water candy) obtained by hydrogenation of an oligosaccharide are preferably used. Among these, sugar alcohol and saccharose are particularly preferred non-reducing sugars, and D-sorbite, saccharose, and reduced syrup are particularly preferred because they have a buffering action in an appropriate pH region and are inexpensive.
[0105]
These non-reducing sugars can be used alone or in combination of two or more thereof, and the proportion of the non-reducing sugar in the developer is preferably 0.1 to 30% by weight, more preferably 1 to 20% by weight.
Below this range, a sufficient buffering effect cannot be obtained, and when the concentration is above this range, it is difficult to achieve high concentration, and the problem of increased costs arises. In addition, when reducing sugar is used in combination with a base, there is a problem that the color changes to brown over time, the pH gradually decreases, and thus developability decreases.
[0106]
A conventionally known alkaline agent can be used as the base to be combined with the non-reducing sugar. For example, sodium hydroxide, potassium hydroxide, lithium hydroxide, trisodium phosphate, tripotassium phosphate, triammonium phosphate, disodium phosphate, dipotassium phosphate, diammonium phosphate, sodium carbonate, potassium carbonate, Examples include inorganic alkali agents such as ammonium carbonate, sodium hydrogen carbonate, potassium hydrogen carbonate, ammonium hydrogen carbonate, sodium borate, potassium borate, and ammonium borate. Moreover, monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropylamine, diisopropylamine, triisopropylamine, n-butylamine, monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, Organic alkali agents such as ethyleneimine, ethylenediamine, and pyridine are also used.
[0107]
These alkali agents are used alone or in combination of two or more. Among these, sodium hydroxide and potassium hydroxide are preferable because the pH can be adjusted in a wide pH range by adjusting these amounts relative to the non-reducing sugar. Further, trisodium phosphate, tripotassium phosphate, sodium carbonate, potassium carbonate and the like are preferable because they have a buffering action.
These alkali agents are added so that the pH of the developer is in the range of 9.0 to 13.5, and the addition amount is determined by the desired pH, the type and addition amount of the non-reducing sugar, and more preferable pH. The range is 10.0 to 13.2.
[0108]
Further, an alkaline buffer composed of a weak acid other than sugars and a strong base can be used in combination with the developer. As the weak acid used as such a buffer, one having a dissociation constant (pKa) of 10.0 to 13.2 is preferable.
Such a weak acid is selected from those described in IONATION CONSTANTS OF ORGANIC ACIDS IN AQUEOUS SOLUTION published by Pergamon Press, for example, 2,2,3,3-tetrafluoropropanol-1 (PKa12.74) , Alcohols such as trifluoroethanol (12.37) and trichloroethanol (12.24), aldehydes such as pyridine-2-aldehyde (12.68) and pyridine-4-aldehyde (12.05) , Salicylic acid (13.0), 3-hydroxy-2-naphthoic acid (12.84), catechol (12.6), gallic acid (12.4), sulfosalicylic acid (11.7) 3,4-dihydroxysulfonic acid (12) 2), 3,4-dihydroxybenzoic acid (11.94), 1,2,4-trihydroxybenzene (11.82), hydroquinone (11.56), pyrogallol (11.34), o -Compounds having phenolic hydroxyl groups such as cresol (10.33), resorcinol (11.27), p-cresol (10.27), m-cresol (10.09), 2-butanone oxime ( 12.45), acetoxime (12.42), 1,2-cycloheptanedione dioxime (12.3), 2-hydroxybenzaldehyde oxime (12.10), dimethylglyoxime (11.9) ), Ethanediamide dioxime (11.37), oximes such as acetophenone oxime (11.35), adenosine (12.5 6) Nucleic acid-related substances such as inosine (12.5), guanine (12.3), cytosine (12.2), hypoxanthine (12.1), xanthine (11.9), etc. Diethylaminomethylphosphonic acid (12.32), 1-amino-3,3,3-trifluorobenzoic acid (12.29), isopropylidenediphosphonic acid (12.10), 1,1-ethylidene Diphosphonic acid (11.54), 1,1-ethylidene diphosphonic acid 1-hydroxy (11.52), benzimidazole (12.86), thiobenzamide (12.8), picoline thioamide (same as above) Weak acids such as 12.55) and barbituric acid (12.5).
[0109]
Of these weak acids, sulfosalicylic acid and salicylic acid are preferred. As the base to be combined with these weak acids, sodium hydroxide, ammonium, potassium and lithium are preferably used. These alkali agents are used alone or in combination of two or more. The above various alkali agents are used by adjusting the pH within a preferable range depending on the concentration and combination.
[0110]
Various surfactants and organic solvents can be added to the developer as needed for the purpose of promoting developability, dispersing development residue, and improving the ink affinity of the printing plate image area. Preferred surfactants include anionic, cationic, nonionic and amphoteric surfactants.
[0111]
Preferred examples of the surfactant include polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, glycerin fatty acid partial esters, sorbitan Fatty acid partial esters, pentaerythritol fatty acid partial esters, propylene glycol mono fatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, poly Glycerin fatty acid partial esters, polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acids Nonionic surfactants such as ethanolamides, N, N-bis-2-hydroxyalkylamines, polyoxyethylene alkylamines, triethanolamine fatty acid esters, trialkylamine oxides, fatty acid salts, abietic acid salts, hydroxy Alkane sulfonates, alkane sulfonates, dialkyl sulfosuccinate esters, linear alkyl benzene sulfonates, branched alkyl benzene sulfonates, alkyl naphthalene sulfonates, alkylphenoxy polyoxyethylene propyl sulfonates, polyoxyethylene Alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium salt, N-alkyl sulfosuccinic acid monoamide disodium salt, petroleum sulfonates, sulfated tallow oil Fatty acid alkyl ester sulfate ester salt, alkyl sulfate ester salt, polyoxyethylene alkyl ether sulfate ester salt, fatty acid monoglyceride sulfate ester salt, polyoxyethylene alkylphenyl ether sulfate ester salt, polyoxyethylene styryl phenyl ether sulfate ester salt, alkyl phosphorus Acid ester salts, polyoxyethylene alkyl ether phosphate ester salts, polyoxyethylene alkyl phenyl ether phosphate ester salts, partially saponified styrene / leic anhydride copolymers, and partial saponification of olefin / maleic anhydride copolymers Products, anionic surfactants such as naphthalenesulfonate formalin condensates, alkylamine salts, quaternary ammonium salts such as tetrabutylammonium bromide, Examples include cationic surfactants such as reoxyethylene alkylamine salts and polyethylene polyamine derivatives, and amphoteric surfactants such as carboxybetaines, aminocarboxylic acids, sulfobetaines, aminosulfuric esters, and imidazolines. Among the surfactants listed above, those having polyoxyethylene can be read as polyoxyalkylenes such as polyoxymethylene, polyoxypropylene and polyoxybutylene, and these surfactants are also included.
[0112]
A more preferred surfactant is a fluorosurfactant containing a perfluoroalkyl group in the molecule. Such fluorosurfactants include perfluoroalkyl carboxylates, perfluoroalkyl sulfonates, anionic types such as perfluoroalkyl phosphates, amphoteric types such as perfluoroalkyl betaines, and perfluoroalkyltrimethylammonium salts. Cationic and perfluoroalkylamine oxides, perfluoroalkyl ethylene oxide adducts, perfluoroalkyl group and hydrophilic group-containing oligomers, perfluoroalkyl group and lipophilic group-containing oligomers, perfluoroalkyl groups, hydrophilic groups and lipophilic groups Nonionic types such as group-containing oligomers, perfluoroalkyl groups, and lipophilic group-containing urethanes can be mentioned. Said surfactant can be used individually or in combination of 2 or more types, and is added in 0.001 to 10 weight% in a developing solution, More preferably, it is added in 0.01 to 5 weight%.
[0113]
Various development stabilizers can be used in the developer. Preferred examples thereof include polyethylene glycol adducts of sugar alcohols described in JP-A-6-282079, tetraalkylammonium salts such as tetrabutylammonium hydroxide, phosphonium salts such as tetrabutylphosphonium bromide, and iodonium such as diphenyliodonium chloride. A salt is a preferred example. Further, anionic surfactants or amphoteric surfactants described in JP-A-50-51324, water-soluble cationic polymers described in JP-A-55-95946, and JP-A-56-142528 are described. And water-soluble amphoteric polymer electrolytes that have been used.
[0114]
Furthermore, an organic boron compound to which an alkylene glycol is added as described in JP-A-59-84241, a polyoxyethylene / polyoxypropylene block polymerization type water-soluble surfactant as described in JP-A-60-111246, An alkylenediamine compound substituted with polyoxyethylene / polyoxypropylene disclosed in JP-A-60-129750, a polyethylene glycol having a weight average molecular weight of 300 or more described in JP-A-61-215554, and a cation described in JP-A-63-175858 And a water-soluble ethylene oxide addition compound obtained by adding 4 mol or more of ethylene oxide to an acid or alcohol disclosed in JP-A-2-39157, a water-soluble polyalkylene compound, and the like.
[0115]
If necessary, an organic solvent is further added to the developer. As such an organic solvent, those having a solubility in water of about 10% by weight or less are suitable, and preferably those having a solubility in water of 5% by weight or less are selected. For example, 1-phenylethanol, 2-phenylethanol, 3-phenyl-1-propanol, 4-phenyl-1-butanol, 4-phenyl-2-butanol, 2-phenyl-1-butanol, 2-phenoxyethanol, 2- Benzyloxyethanol, o-methoxybenzyl alcohol, m-methoxybenzyl alcohol, p-methoxybenzyl alcohol, benzyl alcohol, cyclohexanol, 2-methylcyclohexanol, 3-methylcyclohexanol and 4-methylcyclohexanol, N-phenylethanol Examples thereof include amines and N-phenyldiethanolamine.
The content of the organic solvent is 0.1 to 5% by weight with respect to the total weight of the used solution. The amount used is closely related to the amount of surfactant used, and it is preferable to increase the amount of surfactant as the amount of organic solvent increases. This is because the amount of the surfactant is small, and if the amount of the organic solvent is large, the organic solvent is not completely dissolved, and therefore it is impossible to expect good developability.
[0116]
A reducing agent can be further added to the developer. This prevents the printing plate from being stained. Preferable organic reducing agents include phenol compounds such as thiosalicylic acid, hydroquinone, metol, methoxyquinone, resorcin, and 2-methylresorcin, and amine compounds such as phenylenediamine and phenylhydrazine. More preferable inorganic reducing agents include sodium, potassium and ammonium salts of inorganic acids such as sulfurous acid, bisulfite, phosphorous acid, hydrogen phosphite, dihydrogen phosphite, thiosulfuric acid and dithionite. A salt etc. can be mentioned.
Among these reducing agents, sulfites are particularly excellent in the antifouling effect. These reducing agents are preferably contained in the range of 0.05 to 5% by weight with respect to the developer at the time of use.
[0117]
An organic carboxylic acid can also be added to the developer. Preferred organic carboxylic acids are aliphatic carboxylic acids and aromatic carboxylic acids having 6 to 20 carbon atoms. Specific examples of the aliphatic carboxylic acid include caproic acid, enanthylic acid, caprylic acid, lauric acid, myristic acid, palmitic acid and stearic acid, and particularly preferred are alkanoic acids having 8 to 12 carbon atoms. . Further, it may be an unsaturated fatty acid having a double bond in the carbon chain or a branched carbon chain. The aromatic carboxylic acid is a compound in which a carboxyl group is substituted on a benzene ring, naphthalene ring, anthracene ring or the like, and specifically includes o-chlorobenzoic acid, p-chlorobenzoic acid, o-hydroxybenzoic acid, p- Hydroxybenzoic acid, o-aminobenzoic acid, p-aminobenzoic acid, 2,4-dihydrobenzoic acid, 2,5-dihydroxybenzoic acid, 2,6-dihydroxybenzoic acid, 2,3-dihydroxybenzoic acid, 3, There are 5-dihydroxybenzoic acid, gallic acid, 1-hydroxy-2-naphthoic acid, 3-hydroxy-2-naphthoic acid, 2-hydroxy-1-naphthoic acid, 1-naphthoic acid, 2-naphthoic acid and the like. Naphthoic acid is particularly effective.
[0118]
The aliphatic and aromatic carboxylic acids are preferably used as sodium salts, potassium salts or ammonium salts in order to enhance water solubility. The content of the organic carboxylic acid in the developer used in the present invention is not particularly limited, but if it is less than 0.1% by weight, the effect is not sufficient, and if it is 10% by weight or more, the effect cannot be further improved. In addition, dissolution may be hindered when other additives are used in combination. Therefore, the preferable addition amount is 0.1 to 10% by weight, and more preferably 0.5 to 4% by weight with respect to the developing solution at the time of use.
[0119]
The developer may further contain a preservative, a colorant, a thickener, an antifoaming agent, a hard water softening agent, and the like, if necessary. Examples of water softeners include polyphosphoric acid and its sodium, potassium and ammonium salts, ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, triethylenetetraminehexaacetic acid, hydroxyethylethylenediaminetriacetic acid, nitrilotriacetic acid, 1,2-diaminocyclohexanetetra Aminopolycarboxylic acids such as acetic acid and 1,3-diamino-2-propanoltetraacetic acid and their sodium, potassium and ammonium salts, aminotri (methylenephosphonic acid), ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylene Phosphonic acid), triethylenetetramine hexa (methylenephosphonic acid), hydroxyethylethylenediaminetri (methylenephosphonic acid) and 1-hydroxy-data-ene-1,1-diphosphonic acid and their sodium salts, potassium salts and ammonium salts.
[0120]
The optimum value of such a hard water softener varies depending on its chelation and the hardness of the hard water used and the amount of hard water. %, More preferably in the range of 0.01 to 0.5% by weight. If the addition amount is less than this range, the intended purpose is not sufficiently achieved. If the addition amount is more than this range, adverse effects on the image area such as color loss will occur. The remaining component of the developer is water. It is advantageous in terms of transportation that the developer is a concentrated solution having a water content less than that in use and is diluted with water when in use. In this case, the degree of concentration is appropriate such that each component does not cause separation or precipitation.
[0121]
The developer described in JP-A-6-282079 can also be used as the developer used in the present invention. This is SiO ₂ / M ₂ Water-soluble ethylene oxide addition obtained by adding 5 mol or more of ethylene oxide to an alkali metal silicate having a molar ratio of O (M represents an alkali metal) of 0.5 to 2.0 and a sugar alcohol having 4 or more hydroxyl groups A developer containing a compound. Sugar alcohols are polyhydric alcohols corresponding to those obtained by reducing aldehyde groups and ketone groups of sugars to form primary and secondary alcohol groups, respectively. Examples of sugar alcohol shells include D, L-trait, erythritol, D, L-arabit, rebit, xylit, D, L-sorbit, D, L-mannit, D, L-exit, D, Examples thereof include L-talit, dulcit, and allozulcit, and di-, tri-, tetra-, penta-, and hexaglycerin condensed with a sugar alcohol. The water-soluble ethylene oxide addition compound can be obtained by adding 5 mol or more of ethylene oxide to 1 mol of the sugar alcohol. Further, propylene oxide may be block-copolymerized in the ethylene oxide addition compound as required within a range where solubility is acceptable. These ethylene oxide addition compounds may be used alone or in combination of two or more.
The addition amount of these water-soluble ethylene oxide addition compounds is suitably 0.001 to 5% by weight, more preferably 0.001 to 2% by weight, based on the developing solution (working solution).
[0122]
The developer may further contain the above-described various surfactants and organic solvents as necessary for the purpose of promoting developability, dispersing development residue, and improving the ink affinity of the printing plate image area.
[0123]
A lithographic printing plate precursor developed with a developer having such a composition is subjected to post-treatment with a washing water, a rinse solution containing a surfactant, a finisher mainly composed of gum arabic or starch derivatives, or a protective gum solution. The These treatments can be used in various combinations for the post-treatment of the lithographic printing plate precursor according to the invention.
[0124]
In recent years, automatic developing machines for PS plates have been widely used in the stencil and printing industries in order to rationalize and standardize plate making operations. This automatic developing machine is generally composed of a developing section and a post-processing section, and is composed of an apparatus for transporting the PS plate, each processing liquid tank and a spray device, and the exposed PS plate is pumped up while being transported horizontally. Each processing solution is sprayed from a spray nozzle to develop and post-process. In addition, recently, a PS plate is immersed and transported in a processing solution tank filled with a processing solution by a guide roll in the solution, and a small amount of washing water after development is supplied to the plate surface for washing. A method is also known in which the waste water is reused as dilution water for the developer stock solution.
[0125]
In such automatic processing, each processing solution can be processed while being replenished with each replenisher according to the processing amount, operating time, and the like. In addition, a so-called disposable processing method in which processing is performed with a substantially unused processing solution can also be applied.
[0126]
In the lithographic printing plate precursor according to the invention, image portions unnecessary for the lithographic printing plate obtained by image exposure, development, washing and / or rinsing and / or gumming (for example, film edge marks of the original film, etc.) ), Unnecessary image portions are erased. Such erasing is preferably performed by applying an erasing solution as described in, for example, Japanese Patent Publication No. 2-13293 to an unnecessary image portion, leaving it for a predetermined time, and then washing with water. As described in JP-A-59-174842, a method of developing after irradiating an unnecessary image portion with an actinic ray guided by an optical fiber can also be used.
[0127]
The lithographic printing plate obtained from the lithographic printing plate precursor of the present invention as described above can be subjected to a printing process after applying a desensitizing gum if desired, but lithographic printing with a higher printing durability. If you want to make a plate, you will be burned. In the case of burning a lithographic printing plate, before burning, an adjustment as described in JP-B-61-2518, JP-A-55-28062, JP-A-62-31859, JP-A-61-159655 is used. It is preferable to treat with a surface liquid.
As its method, with a sponge or absorbent cotton soaked with the surface-adjusting liquid, it is applied onto a lithographic printing plate, or a method in which the printing plate is immersed and applied in a vat filled with the surface-adjusting liquid, Application by an automatic coater is applied. Further, it is more preferable to make the coating amount uniform with a squeegee or a squeegee roller after coating.
[0128]
The coating amount of the surface conditioning liquid is generally 0.03 to 0.8 g / m. ² (Dry mass) is appropriate. The lithographic printing plate coated with the surface-adjusting solution is dried if necessary, and then heated to a high temperature with a burning processor (for example, burning processor “BP-1300” sold by Fuji Photo Film Co., Ltd.). The In this case, the heating temperature and time are in the range of 180 to 300 ° C. and preferably in the range of 1 to 20 minutes, although depending on the type of components forming the image.
[0129]
The lithographic printing plate that has been burned can be subjected to conventional treatments such as washing and gumming as needed, but a surface-conditioning solution containing a water-soluble polymer compound is used. In such a case, a so-called desensitizing treatment such as gumming can be omitted. The planographic printing plate obtained by such processing is applied to an offset printing machine or the like and used for printing a large number of sheets.
[0130]
【Example】
EXAMPLES Hereinafter, although this invention is demonstrated according to an Example, the scope of the present invention is not limited to these Examples.
[0131]
[Synthesis of polyurethane resin]
<Synthesis Example 1>
In a 500 ml three-necked flask, 125 g of 4,4′-diphenylmethane diisocyanate and 67 g of 2,2-bis (hydroxymethyl) propionic acid were dissolved in 290 ml of dioxane. After adding 1 g of N, N-diethylaniline, the mixture was stirred for 6 hours under reflux of dioxane. After the reaction, the polymer was precipitated little by little into a solution of 4 L of water and 40 cc of acetic acid. This solid was vacuum-dried to obtain 185 g of polyurethane resin (1). The acid content was 2.47 meq / g. When the molecular weight was measured by GPC, the weight average (polystyrene standard) was 28,000.
[0132]
<Synthesis Examples 2-13>
Polyurethane resins (2) to (13) were synthesized in the same manner as in Synthesis Example 1 except that in Example 1 above, the starting materials were changed to the diisocyanate compounds and diol compounds shown in Table 1 below.
[0133]
[Table 1]

[0134]
[Table 2]

[0135]
[Example 1]
[Production of support]
0.24 mm thick aluminum plate (Si: 0.06 mass%, Fe: 0.30 mass%, Cu: 0.014 mass%, Mn: 0.001 mass%, Mg: 0.001 mass%, Zn : 0.001% by mass, Ti: 0.03% by mass, the balance being Al and an inevitable impurity aluminum alloy), the following surface treatment was continuously performed.
[0136]
An electrochemical surface roughening treatment was continuously performed using an alternating voltage of 60 Hz. The electrolytic solution at this time was a nitric acid 10 g / liter aqueous solution (containing 5 g / liter of aluminum ions and 0.007 mass% of ammonium ions) at a temperature of 80 ° C. After washing with water, the aluminum plate was etched at 32 ° C. with a caustic soda concentration of 26 mass% and an aluminum ion concentration of 6.5 mass%, and the aluminum plate was 0.20 g / m. ² Dissolved and washed with water by spray. Thereafter, a desmut treatment by spraying was performed with a 25% by weight aqueous solution of sulfuric acid having a temperature of 60 ° C. (containing 0.5% by weight of aluminum ions), and washing with water by spraying was performed.
[0137]
Anodization was performed using an anodizing apparatus of a two-stage power supply electrolytic treatment method. Sulfuric acid was used as the electrolytic solution supplied to the electrolysis unit. Then, water washing by spraying was performed. The final oxide film amount is 2.7 g / m ² Met.
The aluminum support obtained by the anodizing treatment is immersed in a treatment tank of 1 mass% aqueous solution of sodium silicate No. 3 at a temperature of 30 ° C. for 10 seconds for alkali metal silicate treatment (silicate treatment). It was. Then, water washing by spraying was performed.
On the aluminum support after the alkali metal silicate treatment obtained as described above, an undercoat solution having the following composition was applied and dried at 80 ° C. for 15 seconds to form a coating film. The coating amount after drying is 15 mg / m ² Met.
[0138]
<Undercoat liquid composition>
・ The following compound 0.3g
・ Methanol 100g
・ Water 1g
[0139]
[Chemical formula 5]

[0140]
[Formation of recording layer]
On the web-like support obtained as described above, the coating amount for the lower layer coating solution 1 having the following composition is 0.85 g / m. ² After coating with a bar coater, it was dried at 160 ° C. for 44 seconds, and immediately cooled with cold air of 17 to 20 ° C. until the temperature of the support became 35 ° C.
Thereafter, the upper layer coating liquid 1 having the following composition was applied in an amount of 0.22 g / m. ² After coating with a bar coater so as to be dried, it was dried at 148 ° C. for 25 minutes, and further slowly cooled with a wind of 20 to 26 ° C. to prepare a lithographic printing plate precursor of Example 1.
[0141]

[0142]
[Chemical 6]

[0143]

[0144]
[Chemical 7]

[0145]
[Examples 2 to 13]
Example 2 In the same manner as in Example 1, except that the polyurethane resin (1) used in the lower layer coating solution 1 in Example 1 was changed to the polyurethane resins (2) to (13) obtained in the above synthesis examples. ~ 13 planographic printing plate precursors were prepared.
[0146]
[Comparative Example 1]
The polyurethane resin (1) used in the lower layer coating solution 1 in Example 1 was prepared by using N- (4-aminosulfonylphenyl) methacrylamide / acrylonitrile / methyl methacrylate (36/34/30: weight average molecular weight 50000, acid value). A lithographic printing plate precursor of Comparative Example 1 was produced in the same manner as in Example 1 except that it was changed to 2.65).
[0147]
[Evaluation of planographic printing plate precursor]
(Evaluation of printing durability)
The exposure energy was changed for the lithographic printing plate precursors of Examples 1 to 13 and the lithographic printing plate precursor of Comparative Example 1 using a Trend setter manufactured by Creo, and a test pattern was drawn in an image form. Thereafter, development was performed using an automatic developing machine LP-940H (manufactured by Fuji Photo Film Co., Ltd.) charged with a developer DT-2 manufactured by Fuji Photo Film Co., Ltd. (diluted to a conductivity of 43 mS / cm). Development was performed at a temperature of 30 ° C. and a development time of 12 seconds. This was continuously printed using a printer Lithron manufactured by Komori Corporation. At this time, the number of sheets that can be printed while maintaining a sufficient ink density was measured visually to evaluate the printing durability. The larger the number, the better the printing durability. The results are shown in Table 3 below.
[0148]
(Evaluation of chemical resistance)
The lithographic printing plate precursors of Examples 1 to 13 and the lithographic printing plate precursor of Comparative Example 1 were exposed, developed and printed in the same manner as in the evaluation of printing durability. At this time, every time 5,000 sheets were printed, a process of wiping the plate surface with a cleaner (manufactured by Fuji Photo Film Co., Ltd., multi-cleaner) was added to evaluate chemical resistance. The larger the number, the better the chemical resistance. The results are shown in Table 3 below.
[0149]
[Table 3]

[0150]
As is apparent from Table 3, the lithographic printing plate precursors of Examples 1 to 13 using the polyurethane resin according to the present invention as a lower layer component were confirmed to be excellent in printing durability and chemical resistance. It was. In particular, with respect to the polyurethane resin having an aromatic skeleton in the polymer, even better results were obtained in both printing durability and chemical resistance than in the other examples.
On the other hand, the lithographic printing plate precursor of Comparative Example 1 that did not use the polyurethane resin according to the present invention as a lower layer component was confirmed to be significantly inferior in both printing durability and chemical resistance as compared with the examples. It was done.
[0151]
Example 14
In the production of the support of Example 1, the same undercoating and recording layer (lower layer / upper layer) as in Example 1 were provided, except that the silicate treatment was not performed after the anodic oxidation treatment. A printing plate precursor was prepared.
[0152]
(Evaluation of printing durability and chemical resistance)
Evaluation of printing durability and chemical resistance was carried out in the same manner as in Example 1 except that silicate developer DP-4 (28 ° C.) manufactured by Fuji Photo Film Co., Ltd. diluted 6-fold was used as the developer. went.
As a result, the printing durability was 200,000 sheets and the chemical resistance was 180,000 sheets. The same number of printed sheets as in Example 1 was obtained. As a result, the lithographic printing plate precursor using the substrate not subjected to the hydrophilic treatment by silicate was developed by silicate development in the same manner as in Examples 1 to 13 in which the lithographic printing plate precursor using the silicate-treated substrate was developed with a non-silicate developer. Also in Example 14 developed with the liquid, it was confirmed that excellent printing durability and chemical resistance, which are the effects of the present invention, were obtained.
[0153]
【The invention's effect】
According to the present invention, a positive lithographic printing plate precursor which can be directly made by scanning exposure based on a digital signal and has excellent printing durability and chemical resistance can be obtained.

Claims (1)

A recording layer comprising: a lower layer containing a water-insoluble and alkali-soluble polyurethane resin on a support; and an upper layer containing a water-insoluble and alkali-soluble resin and a development inhibitor and having increased solubility in an alkaline aqueous solution upon exposure. And a lithographic printing plate precursor comprising an infrared absorber in at least one of a lower layer and an upper layer of the recording layer.