JP2005107112A - Lithographic printing plate original plate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a positive lithographic printing plate original plate having excellent printing durability and chemical resistance. <P>SOLUTION: The lithographic printing plate original plate has on a support a recording layer which contains (A) an alkali-soluble vinyl polymer having a ring structure in a principal chain and also having an active imido group and (B) an IR absorbent, and is capable of forming an image under irradiation with IR. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

  The present invention relates to a lithographic printing plate precursor, and more particularly to a positive lithographic printing plate precursor for so-called direct plate making that can be directly made from a digital signal of a computer or the like.

  In recent years, the development of lasers has been remarkable. In particular, solid-state lasers and semiconductor lasers having a light emitting region from the near infrared to the infrared can easily be obtained with high output and small size. In the field of lithographic printing, these lasers are very useful as an exposure light source for making a plate directly from digital data such as a computer.

  The positive type lithographic printing plate precursor for an infrared laser contains an alkali-soluble binder resin and an IR dye that absorbs light and generates heat as essential components. The IR dye or the like acts as a development inhibitor that substantially reduces the solubility of the binder resin in the developer by interaction with the binder resin in the unexposed area (image area), and in the exposed area (non-image area). The generated heat weakens the interaction between the IR dye and the binder resin and dissolves in an alkaline developer to form a lithographic printing plate.

  Since the image forming ability of such a positive lithographic printing plate precursor for infrared laser depends on the heat generated by infrared laser exposure on the surface of the recording layer, in the vicinity of the support, image formation is caused by diffusion of heat to the support, That is, the amount of heat used for solubilizing the recording layer is reduced, resulting in low sensitivity. Accordingly, there has been a problem that the effect of disappearing the development suppressing ability of the recording layer in the non-image area is not sufficiently obtained, and the difference between the image area and the non-image area becomes small and the highlight reproducibility is insufficient.

  In order to solve the above problem of highlight reproducibility, it is considered to use a recording layer made of a material capable of developing a non-image area more easily, i.e., having a better solubility in an alkaline aqueous solution. However, such a recording layer is chemically weak also in the image area, and is inferior in chemical resistance, such as being easily damaged by a developer, an ink washing solvent used during printing, a plate cleaner, and the like. In the unexposed area, the resin material is excellent in chemical resistance and durability of the film, and after the dissolution inhibiting action is released by exposure, the resin material having the characteristics of excellent developability is eagerly desired. It was.

In order to solve the above problems, it comprises a lower layer excellent in alkali solubility containing a polyvinylphenol resin, and an upper layer that contains a water-insoluble and alkali-soluble resin and an infrared absorber and greatly increases the solubility in an alkaline aqueous solution upon exposure. A lithographic printing plate precursor provided with a recording layer is disclosed (for example, see Patent Document 1). This lithographic printing plate precursor was improved in sensitivity, but was insufficient in chemical resistance. Further, the adhesion between the support and the recording layer is insufficient, and there is a problem that the printing durability is poor.
In addition, various improved techniques have been proposed for the same purpose. For example, an image forming material (for example, an image forming material obtained by laminating a lower layer containing a copolymer having a specific monomer and a photosensitive upper layer on a support (for example, Patent Document 2), and printing plate preparation using a lithographic printing plate precursor obtained by laminating a lower layer containing an alkali-soluble resin and an infrared-sensitive and alkali-resistant upper layer on a hydrophilic support. A method (for example, refer to Patent Document 3) has been proposed. Although the former is excellent in sensitivity and chemical resistance, there is a problem that the film strength of the resin used in the lower layer is insufficient and there is still room for improvement in printing durability. For the latter, the alkali-soluble resin used is chemical resistant. Since the recording layer elutes due to the solvent component contained in the plate cleaner, or the solvent component penetrates to the lower substrate interface, the adhesion between the recording layer and the substrate decreases, and the recording layer peels off. However, it is difficult to achieve both the printing durability depending on the film strength of the lower layer and the chemical resistance.
JP-A-10-250255 JP 11-218914 A Japanese Patent Laid-Open No. 11-194843

  An object of the present invention, which has been made in consideration of the above-mentioned drawbacks of the prior art, is to provide a positive type lithographic printing plate precursor excellent in printing durability and chemical resistance.

  As a result of extensive research, the present inventor has found that the above object can be achieved by using an alkali-soluble vinyl polymer having a specific structure as a recording layer component of a lithographic printing plate precursor, thereby completing the present invention. It came to.

That is, the lithographic printing plate precursor according to the present invention comprises (A) an alkali-soluble vinyl polymer having a ring structure in the main chain and an active imide group (hereinafter referred to as “specific vinyl polymer” as appropriate). And (B) an infrared absorber, and has a recording layer capable of forming an image by irradiation with infrared rays.
In addition, it is preferable that the said (A) specific vinyl polymer has at least one of the following general formula (1) and (2) as the principal chain ring structure.

In general formula (1) or (2), R ¹ and R ² each independently represents a hydrogen atom or a monovalent organic group.

  Further, as a preferred embodiment of the lithographic printing plate precursor according to the present invention, on the support, (A) a lower layer containing a specific vinyl polymer, an upper layer containing an alkali-soluble resin and capable of forming an image by infrared irradiation, And (B) an infrared absorber is contained in at least one of the lower layer and the upper layer of the recording layer. In addition, it is preferable to use novolak resin as alkali-soluble resin contained in the upper layer.

Although the operation of the present invention is not clear, it is presumed as follows.
That is, the (A) specific vinyl polymer used for the recording layer of the lithographic printing plate precursor according to the invention is characterized by having a ring structure in the main chain and an active imide group. A polymer having a ring structure in the main chain is considered to be effective in improving the printing durability because of the rigidity of the formed recording layer due to its rigid structure.
Further, since the active imide group has a high polarity, it is possible to improve the chemical resistance of the recording layer. Furthermore, since the active imide group is an alkali-soluble group, the polymer itself exhibits excellent alkali solubility in the infrared irradiation region (non-image area), but compared with other general alkali-soluble groups. Because of the high pKa, and because the acid group (dissociable proton) part is not on the atom at the end of the side chain but on the atom (inside) in the middle of the side chain, it has high lipophilicity and ink adhesion It is thought that it is excellent in meat property and can maintain a balance with the alkali solubility.

  Further, when the recording layer has a multi-layer structure, which is a preferred embodiment of the present invention, in the image area, that is, in the region where the upper layer of the recording layer exists as an alkali-resistant development layer, the above-described high film strength and chemical resistance are obtained. Works effectively and has excellent printing durability and chemical resistance. In addition, when the upper layer is removed in the non-image area, it is considered that the lower layer quickly dissolves and disperses in the alkali developer due to the original alkali solubility.

  According to the present invention, a positive lithographic printing plate precursor excellent in printing durability and chemical resistance can be provided.

The lithographic printing plate precursor according to the invention comprises (A) a specific vinyl polymer and (B) an infrared absorber on a support, and has a recording layer capable of forming an image by infrared irradiation. And For the purpose of increasing the inhibition (dissolution suppression ability) of the recording layer, it is preferable to further contain (C) a development inhibitor. Particularly when (B) an infrared absorber having no dissolution inhibiting ability is used, the development inhibitor can be an important component for maintaining the alkali resistance of the image area.
Such a recording layer is not particularly limited in its layer structure, and may be a single layer structure or a multilayer structure composed of a plurality of layers having different constituent components. When the recording layer has a multi-layer structure, the component (A) and the component (B) may be contained in any layer, and even if they are contained in the same layer, they are contained in separate layers. It may be.
First, each configuration of the lithographic printing plate precursor according to the invention having a single-layer recording layer will be described in detail sequentially.

[Single layer recording layer]
[(A) Specific vinyl polymer]
The specific vinyl polymer according to the present invention is characterized by having a ring structure in the main chain and an active imide group.
Here, having a ring structure in the main chain means that atoms constituting the main chain are part of the ring structure, and as such a ring structure, the polymer has a ring structure. Any material can be used without limitation as long as the rigidity is improved and the strength of the formed film (recording layer) is increased.

  Especially, it is preferable that the number of rings of the said ring structure is 4-6, and it is especially preferable that the number of members is 5-6. Moreover, it is preferable that a ring structure is an alicyclic structure from the characteristic of the vinyl polymer formed by addition polymerization of a polymerizable double bond, and it is more preferable that it is an alicyclic structure with 5-6 ring members. Further, since the alicyclic structure can be expected to improve rigidity and increase the strength of the film by increasing polarity, it is preferable that the alicyclic structure has a heteroatom as an atom constituting the alicyclic structure. Includes an oxygen atom, a nitrogen atom, and a sulfur atom, and more preferably has an oxygen atom or a nitrogen atom. Particularly preferred examples of the alicyclic structure include structural units represented by the following general formula (1) or general formula (2). The specific vinyl polymer according to the present invention is preferably a polymer containing such a structural unit.

In general formula (1) or (2), R ¹ and R ² each independently represents a hydrogen atom or a monovalent organic group, and preferred organic groups include an alkyl group and an aryl group. In the case of an aryl group, it may be substituted with any substituent. Further, R ¹ and R ² may be introduced with an active imide group described below, which is another characteristic configuration of the specific vinyl polymer. In that case, R ¹ and R ² themselves may be an active imide group, or may have an active imide group as a substituent of the alkyl group or aryl group.

Examples of the alkyl group introduced into R ¹ and R ² include a linear or branched alkyl group having about 1 to 8 carbon atoms. Preferred alkyl groups include a methyl group, an ethyl group, and isopropyl. Group, n-propyl group, n-butyl group, iso-butyl group, tert-butyl group, hexyl group, 2-ethylhexyl group and the like. Among them, ethyl group and n-propyl group are particularly preferable.

As an aryl group introduce | transduced into R < ¹ > and R < ² >, a C6-C10 monocyclic or condensed aryl group etc. are mentioned, for example, Among these, a phenyl group is especially preferable.

  Examples of the substituent that can be introduced into the alkyl group or aryl group include a monovalent substituent having an alkyl group, an alkoxy group, a hydroxyl group, a halogen atom, a cyano group, a nitro group, a carboxy group, and an aminosulfonyl group, Examples thereof include monovalent organic groups having an active imide group, and among these, monovalent substituents having a hydroxyl group and an aminosulfonyl group, and monovalent organic groups having an active imide group are particularly preferable.

The method for introducing a ring structure into the specific vinyl polymer is not particularly limited. For example, by addition polymerization of a polymerizable compound in which a polymerizable double bond is part of the ring structure, such as a maleimide derivative. And a method of introducing a ring structure by a polymer reaction into a vinyl polymer that does not have a ring structure in the main chain, such as a polyvinyl alcohol resin modified with an acetal skeleton typified by polyvinyl butyral. It is done. As the specific vinyl polymer according to the present invention, a polymer having a ring structure introduced by any of these methods can be suitably used.
The specific vinyl polymer according to the present invention needs to have at least one of the above ring structures, and may have two or more of the ring structures.
The copolymerization ratio of the structural unit having the ring structure in the specific vinyl polymer is preferably 10 to 80 mol%, more preferably 15 to 60 mol%, and more preferably 20 to 50 mol%. It is particularly preferred.

The recording layer used in the lithographic printing plate precursor according to the present invention is a specific vinyl polymer that is one of the main components of the recording layer because an image is formed by a change in solubility in an alkaline developer caused by infrared irradiation. Must be soluble in an alkaline developer. In order to express alkali solubility, the specific vinyl polymer according to the present invention has an active imide group as an alkali-soluble group. Incidentally, active imide group, also called substituted sulfonamide-based acid group, _{specifically, -SO 2 NHCOR, -SO 2 NHSO} 2 R, -CONHSO 2 R , and the like.

In the above formula, R represents a hydrocarbon group which may have a substituent. Examples of such a hydrocarbon group include a linear or branched alkyl group having about 1 to 8 carbon atoms, carbon Examples thereof include a monocyclic or condensed ring aryl group having about 6 to 10 carbon atoms, and among them, a branched alkyl group having about 3 to 8 carbon atoms and a phenyl group are particularly preferable.
Examples of the substituent that can be introduced into the hydrocarbon group include an alkyl group, an alkoxy group, a hydroxyl group, a halogen atom, a cyano group, and a nitro group. Preferred examples of the substituent include an alkyl group and a halogen atom. .
The specific vinyl polymer according to the present invention may have one or more of the above active imide groups.

  Since the active imide group represented by these formulas has a high pKa compared to a carboxy group used as an alkali-soluble group of a general alkali-soluble resin, it has a high printing durability, which is a characteristic of a specific vinyl polymer. In addition, it is considered that the oleophilicity of the image portion important as a lithographic printing plate is not impaired while maintaining chemical resistance and imparting alkali solubility. Further, since the acid group (dissociative proton) part is not on the atom at the end of the side chain but on the atom in the middle (inside) of the side chain, it is considered that further improvement in lipophilicity is achieved. .

As a method of introducing such an active imide group into a polymer, a method of copolymerizing a polymerizable monomer having an active imide group, or a method of introducing the active imide group into a vinyl polymer later by a polymer reaction There are no particular restrictions on the method of introduction. In the specific vinyl polymer, each of the ring structure and the active imide group may be present in the same structural unit, or each is present in a different structural unit and is the same by copolymerization. The vinyl polymer may be formed.
In addition, the specific vinyl polymer may have an acid group other than the active imide group as an alkali-soluble group as long as it does not impair the printing durability, chemical resistance, and lipophilicity of the recording layer. Includes a phenolic hydroxyl group, a sulfonamide group, a carboxy group, a sulfonic acid group, a phosphoric acid group, etc. Among them, a phenolic hydroxyl group, a sulfonamide group, and a carboxy group are more preferable, and a phenolic hydroxyl group and a sulfonamide group are particularly preferable. .

The content of all alkali-soluble groups including active imide groups and other acid groups contained in the specific vinyl polymer is preferably 1.0 to 10 meq / g, more preferably 1.5 to 9.0 meq / g. 2.0 to 8.0 meq / g is particularly preferable.
Further, the content of active imide groups in all alkali-soluble groups is preferably 30% or more, more preferably 50% or more, and particularly preferably 75% or more.

  Furthermore, the specific vinyl polymer according to the present invention includes a structural unit other than the structural unit having the ring structure and the structural unit having the alkali-soluble group (active imide group or other acid group). Also good. Such a structural unit can be introduced by copolymerizing the polymerizable monomers (m1) to (m12) described below at the time of vinyl polymer formation. The copolymerization ratio of such a polymerizable monomer is preferably 70 mol% or less, more preferably 60 mol% or less, and particularly preferably 50 mol% or less in the specific vinyl polymer.

(M1) Acrylic acid esters and methacrylic acid esters having an aliphatic hydroxyl group such as 2-hydroxyethyl acrylate or 2-hydroxyethyl methacrylate.
(M2) Alkyl acrylates such as methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, amyl acrylate, hexyl acrylate, octyl acrylate, benzyl acrylate, 2-chloroethyl acrylate, and glycidyl acrylate.
(M3) Alkyl methacrylates such as methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, amyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, 2-chloroethyl methacrylate and glycidyl methacrylate.
(M4) Acrylamide, methacrylamide, N-methylol acrylamide, N-ethyl acrylamide, N-hexyl methacrylamide, N-cyclohexyl acrylamide, N-hydroxyethyl acrylamide, N-phenyl acrylamide, N-nitrophenyl acrylamide, N-ethyl- Acrylamide or methacrylamide such as N-phenylacrylamide.

(M5) Vinyl ethers such as ethyl vinyl ether, 2-chloroethyl vinyl ether, hydroxyethyl vinyl ether, propyl vinyl ether, butyl vinyl ether, octyl vinyl ether, and phenyl vinyl ether.
(M6) Vinyl esters such as vinyl acetate, vinyl chloroacetate, vinyl butyrate and vinyl benzoate.
(M7) Styrenes such as styrene, α-methylstyrene, methylstyrene, chloromethylstyrene.
(M8) Vinyl ketones such as methyl vinyl ketone, ethyl vinyl ketone, propyl vinyl ketone, and phenyl vinyl ketone.
(M9) Olefins such as ethylene, propylene, isobutylene, butadiene and isoprene.
(M10) N-vinylpyrrolidone, acrylonitrile, methacrylonitrile and the like.
(M11) Unsaturated imides such as maleimide, N-acryloylacrylamide, N-acetylmethacrylamide, N-propionylmethacrylamide, N- (p-chlorobenzoyl) methacrylamide.
(M12) Unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic anhydride and itaconic acid.

  Examples of the specific vinyl polymer that can be suitably used in the present invention are shown below, but the present invention is not limited thereto.

The specific vinyl polymer according to the present invention can be obtained by various known organic synthesis methods. As a typical synthesis method, a vinyl polymer having a ring structure in the main chain has an active imide group by polymer reaction. Examples thereof include a method of introducing an organic group, and a method of copolymerizing a polymerizable monomer having a ring structure and a polymerizable monomer having an active imide group.
As a preferred vinyl polymer used in the method of introducing an organic group having an active imide group into a vinyl polymer having a ring structure in the main chain by polymer reaction, maleimides represented by N-phenylmaleimide derivatives are used as monomers. Examples thereof include vinyl polymers used, polyvinyl butyral derived from polyvinyl alcohols, and polyvinyl formal. In these vinyl polymers having a ring structure in the main chain, a functional group such as a hydroxyl group or an amino group present in the polymer reacts with an organic group having an active imide structure, so that an active imide group is present in the polymer. be introduced. The active imide group may be formed by a reaction for introducing an organic group.
On the other hand, when copolymerizing a polymerizable monomer having a ring structure and a polymerizable monomer having an active imide group, a polymerizable monomer capable of forming a ring structure in the main chain by polymerization, and an active imide A specific vinyl polymer can be obtained by polymerizing a polymerizable monomer having a group with various polymerization means. Moreover, you may use what has both the ring structure and the active imide group in the single polymerizable monomer. Preferable examples of the polymerizable monomer that can be polymerized to form a ring structure in the main chain include maleimides represented by N-phenylmaleimide derivatives.
Although the synthesis method of exemplary compound (P-1) is shown below as a typical synthesis method, the synthesis method of the specific vinyl polymer of this invention is not limited to this.

<Synthesis of specific vinyl polymer (P-1)>
In a 500 ml three-necked flask equipped with a stirrer, a condenser, and a dropping funnel, 19.7 g of p-toluenesulfonyl isocyanate and 100 ml of dichloromethane were added and stirred. To this mixture, 200 ml of a dichloromethane solution of 18.9 g of N- (4-hydroxyphenyl) maleimide was dropped from a dropping funnel over about 30 minutes. After completion of the dropwise addition, heating and refluxing were performed for 5 hours. After the reaction, the reaction solvent was distilled off under reduced pressure, and the residue was washed with hexane, and then recrystallized with a hexane / ethyl acetate mixed solvent to obtain 36.4 g of a monomer (M-1) having the following structure.

  Next, 136 g of dimethyl sulfoxide was placed in a 500 ml three-necked flask equipped with a stirrer and a condenser, and stirred while heating to 80 ° C. in a hot water bath under a nitrogen stream. Here, a mixture of 17.4 g of the monomer (M-1), 1.3 g of methacrylamide, 4.0 g of methyl methacrylate, 136 g of dimethyl sulfoxide and 0.25 g of V-601 (manufactured by Wako Pure Chemical Industries, Ltd.) The solution was added dropwise over 2 hours and 30 minutes. After completion of dropping, the mixture was further stirred at 80 ° C. for 4 hours. After completion of the reaction, 140 g of methanol was added, cooled, poured into 3000 ml of water with stirring, stirred for 60 minutes, filtered, washed with water, and dried to obtain a specific vinyl polymer (P-1) (yield 21.8 g). ). When the weight average molecular weight (polystyrene standard) was measured by gel permeation chromatography, it was 53,000.

The weight average molecular weight of the specific vinyl polymer according to the present invention is preferably about 1,000 to 200,000, preferably about 2,000 to 150,000, from the viewpoint of the strength and alkali solubility of the resin layer to be formed. More preferably, it is particularly preferably about 5,000 to 120,000.
The specific vinyl polymer may be used alone or in combination of two or more.

The content of the specific vinyl polymer in the single-layer recording layer of the lithographic printing plate precursor according to the invention is preferably 50 to 96% by mass and preferably 60 to 93% by mass in the total solid content of the recording layer. More preferred is 65 to 91% by mass. Within this range, the recording layer is excellent in printing durability, chemical resistance and image formability.
The single-layer recording layer according to the present invention may use an alkali-soluble resin other than the specific vinyl polymer. Examples of the alkali-soluble resin that can be used in combination include general alkali-soluble resins that are used in a multi-layer recording layer (upper layer) described later, and among these, novolak resins are preferable. As a ratio which mixes a general alkali-soluble resin, 40 mass% or less of all the alkali-soluble resins is preferable, More preferably, it is 35 mass% or less, Most preferably, it is 30 mass% or less.

[(B) Infrared absorber]
It is necessary to add (B) an infrared absorber to the single-layer recording layer according to the present invention. The infrared absorbent used in the present invention is not particularly limited as long as it is a dye that absorbs infrared light and generates heat, and various dyes known as infrared absorbents can be used. Among them, it is preferable to use an infrared absorbent that has a function of forming an interaction with a binder resin such as the specific vinyl polymer or novolak resin and substantially reducing the solubility of the binder resin in a developer. May be mentioned as having excellent dissolution inhibiting ability.

  As the infrared absorber according to the present invention, commercially available dyes and known ones described in literature (for example, “Dye Handbook” edited by the Society of Synthetic Organic Chemistry, published in 1970) can be used. Specific examples include azo dyes, metal complex azo dyes, pyrazolone azo dyes, anthraquinone dyes, phthalocyanine dyes, carbonium dyes, quinoneimine dyes, methine dyes, and cyanine dyes. In the present invention, among these dyes, those that absorb infrared light or near-infrared light are particularly preferable because they are suitable for use in lasers that emit infrared light or near-infrared light.

  Examples of dyes that absorb such infrared light or near infrared light include, for example, JP-A-58-125246, JP-A-59-84356, JP-A-59-202829, and JP-A-60-78787. Methine dyes described in JP-A-58-173696, JP-A-58-181690, JP-A-58-194595, etc., JP-A-58-112793, Naphthoquinone dyes described in JP-A-58-224793, JP-A-59-48187, JP-A-59-73996, JP-A-60-52940, JP-A-60-63744, etc. Examples thereof include squarylium dyes described in 58-112792 and cyanine dyes described in British Patent 434,875.

Further, near-infrared absorption sensitizers described in US Pat. No. 5,156,938 are also preferably used as dyes, and substituted arylbenzo (thio) pyrylium described in US Pat. No. 3,881,924. Salts, trimethine thiapyrylium salts described in JP-A-57-142645 (US Pat. No. 4,327,169), JP-A-58-181051, 58-220143, 59-41363, 59 -84248, 59-84249, 59-146063, 59-146061, pyrylium compounds described in JP-A-59-216146, cyanine dyes, U.S. Pat. No. 4,283,475 The pentamethine thiopyrylium salt described in No. 5 and the pyrylium compound disclosed in Japanese Patent Publication Nos. 5-13514 and 5-19702 Commercially available products, Eporin Co. Epolight III-178, Epolight III-130, Epolight III-125 and the like are particularly preferably used.
Another particularly preferable example of the dye is a near-infrared absorbing dye described in US Pat. No. 4,756,993 as formulas (I) and (II).

These infrared absorbers may be added to the same layer as the recording layer, or another layer may be provided and added thereto. In the case of a separate layer, it is desirable to add it to a layer adjacent to the recording layer.
Furthermore, when the infrared absorber is a compound having dissolution inhibiting ability, the infrared absorber functions not only as a photothermal conversion function but also as a development inhibitor when added to the same layer as the specific vinyl polymer. Therefore, it is preferable.

  The addition amount of the infrared absorber is preferably about 0.01 to 50% by mass in the total solid content of the single-layer recording layer from the viewpoint of sensitivity and recording layer durability (film properties). It is more preferable to add 0.1 to 10% by mass.

[(C) Development inhibitor]
The recording layer according to the present invention preferably contains (C) a development inhibitor for the purpose of enhancing its inhibition (dissolution inhibiting ability). In particular, when an infrared absorber that does not have dissolution inhibiting ability is used, this development inhibitor can be an important component for maintaining the alkali resistance of the image area.
The development inhibitor used in the present invention forms an interaction with the specific vinyl polymer or other alkali-soluble resin, substantially lowers the solubility of the alkali-soluble resin in the developer in the unexposed area, and The exposed portion is not particularly limited as long as the interaction is weakened and can be soluble in the developer, but quaternary ammonium salts, polyethylene glycol compounds and the like are particularly preferably used. Among the image colorants described below, there are compounds that function as a development inhibitor, and these are also preferred.

Although it does not specifically limit as a quaternary ammonium salt, A tetraalkyl ammonium salt, a trialkyl aryl ammonium salt, a dialkyl diaryl ammonium salt, an alkyl triaryl ammonium salt, a tetraaryl ammonium salt, a cyclic ammonium salt, and a bicyclic ammonium salt are mentioned. .
Specifically, tetrabutylammonium bromide, tetrapentylammonium bromide, tetrahexylammonium bromide, tetraoctylammonium bromide, tetralaurylammonium bromide, tetraphenylammonium bromide, tetranaphthylammonium bromide, tetrabutylammonium chloride, tetrabutylammonium iodide , Tetrastearyl ammonium bromide, lauryl trimethyl ammonium bromide, stearyl trimethyl ammonium bromide, behenyl trimethyl ammonium bromide, lauryl triethyl ammonium bromide, phenyl trimethyl ammonium bromide, 3-trifluoromethylphenyl trimethyl ammonium bromide, benzyl trimethyl ammonium bromide De, dibenzyl dimethyl ammonium bromide, distearyl dimethyl ammonium bromide, tristearyl methyl ammonium bromide, benzyl triethyl ammonium bromide, hydroxyphenyl trimethyl ammonium bromide, N- methyl pyridinium bromide, and the like. In particular, quaternary ammonium salts described in Japanese Patent Application Nos. 2001-226297, 2001-370059, and 2001-398047 are preferable.

  The addition amount of the quaternary ammonium salt is preferably 0.1 to 25% by mass with respect to the total solid content of the single-layer recording layer, from the viewpoint of the development inhibiting effect and the film forming property of the alkali-soluble resin. More preferably, it is 0.5-15 mass%.

Moreover, it does not specifically limit as a polyethyleneglycol compound, The thing of the structure represented with the following general formula (I) is mentioned.
^{R 1 - {- O- (R} 3 -O-) m -R 2} n ··· general formula (I)
In the general formula (I), R ¹ represents a polyhydric alcohol residue or a polyhydric phenol residue, R ² represents a hydrogen atom, an alkyl group having 1 to 25 carbon atoms which may have a substituent, An alkenyl group, an alkynyl group, an alkylyl group, an aryl group or an aryloyl group is represented. R ³ represents an alkylene residue which may have a substituent, m represents an integer of 10 or more on average, and n represents an integer of 1 to 4.

  Examples of the polyethylene glycol compound represented by the general formula (I) include polyethylene glycols, polypropylene glycols, polyethylene glycol alkyl ethers, polypropylene glycol alkyl ethers, polyethylene glycol aryl ethers, polypropylene glycol aryl ethers, Polyethylene glycol alkyl aryl ethers, polypropylene glycol alkyl aryl ethers, polyethylene glycol glycerol esters, polypropylene glycol glycerol esters, polyethylene sorbitol esters, polypropylene glycol sorbitol esters, polyethylene glycol fatty acid esters, polypropylene glycol fatty acid esters, polyethylene glycol Lumpur ethylenediamines, polypropylene glycolated ethylenediamines, polyethylene glycolated diethylenetriamine, and polypropylene glycol diethylenetriamines.

  Specific examples thereof include polyethylene glycol 1000, polyethylene glycol 2000, polyethylene glycol 4000, polyethylene glycol 10000, polyethylene glycol 20000, polyethylene glycol 5000, polyethylene glycol 100000, polyethylene glycol 200000, polyethylene glycol 500000, polypropylene glycol 1500, polypropylene glycol. 3000, polypropylene glycol 4000, polyethylene glycol methyl ether, polyethylene glycol ethyl ether, polyethylene glycol phenyl ether, polyethylene glycol dimethyl ether, polyethylene glycol diethyl ether, polyethylene glycol diphenyl ether Polyethylene glycol lauryl ether, polyethylene glycol dilauryl ether, polyethylene glycol nonyl ether, polyethylene glycol cetyl ether, polyethylene glycol stearyl ether, polyethylene glycol distearyl ether, polyethylene glycol behenyl ether, polyethylene glycol dibehenyl ether, polypropylene glycol methyl ether, Polypropylene glycol ethyl ether, polypropylene glycol phenyl ether, polypropylene glycol dimethyl ether, polypropylene glycol diethyl ether, polypropylene glycol diphenyl ether, polypropylene glycol lauryl ether, polypropylene glycol dilauryl ether Polypropylene glycol nonyl ether, polyethylene glycol acetyl ester, polyethylene glycol diacetyl ester, polyethylene glycol benzoate ester, polyethylene glycol lauryl ester, polyethylene glycol dilauryl ester, polyethylene glycol nonyl acid ester, polyethylene glycol cetylate ester, polyethylene glycol stearoyl ester, polyethylene Glycol distearoyl ester, polyethylene glycol behenate ester, polyethylene glycol dibehenate ester, polypropylene glycol acetyl ester, polypropylene glycol diacetyl ester, polypropylene glycol benzoate ester, polypropylene glycol dibenzoate ester , Polypropylene glycol laurate, polypropylene glycol dilaurate, polypropylene glycol nonyl ester, polyethylene glycol glycerol ether, polypropylene glycol glycerol ether, polyethylene glycol sorbitol ether, polypropylene glycol sorbitol ether, polyethylene glycolated ethylenediamine, polypropylene glycolated ethylenediamine, Examples thereof include polyethylene glycolized diethylenetriamine, polypropylene glycolated diethylenetriamine, and polyethylene glycolated pentamethylenehexamine.

  The addition amount of the polyethylene glycol-based compound is preferably 1 to 25% by mass, and 3 to 15% by mass with respect to the total solid content of the single-layer recording layer, from the viewpoint of the development inhibiting effect and image forming property. It is more preferable.

In addition, when measures are taken to increase such inhibition (dissolution suppression ability), the sensitivity decreases. In this case, it is effective to add a lactone compound to the recording layer to suppress the sensitivity decrease. It is. The lactone compound reacts with the lactone compound when the developer penetrates into the exposed area, that is, the recording layer in the area where the inhibition is released. It is considered that the sensitivity is improved by promoting the dissolution of the recording layer in the partial area. In the unexposed area, this lactone compound forms an interaction with a polar group in the alkali-soluble resin, for example, a hydroxyl group in the novolak resin, and is stable in the film together with a bulky structure having a ring. Therefore, even when an alkaline developer is contacted with the surface of the unexposed area, the rapid opening of the lactone ring during the development process is suppressed, so that the development resistance of the region is reduced. Absent. Since this interaction is more easily released by exposure or heating than the suppression effect by the development inhibitor, the ring-opening reaction of the lactone compound in the exposed area is performed quickly.
Such a lactone compound is not particularly limited, and examples thereof include compounds represented by the following general formula (LI) and general formula (L-II).

In general formula (LI) and general formula (L-II), X ¹ , X ² , X ³ and X ⁴ are divalent nonmetallic atoms or nonmetallic atomic groups constituting the ring, It can be the same or different. Moreover, these may each independently have a substituent. Furthermore, at least one of X ¹ , X ² and X ^{3 in} the general formula (LI) and at least one of X ¹ , X ² , X ³ and X ^{4 in} the general formula (L-II) is: The substituent is preferably an electron-withdrawing substituent or a substituent substituted with an electron-withdrawing group.

  A preferred nonmetallic atom or nonmetallic atomic group is an atom or atomic group selected from a methylene group, a sulfinyl group, a carbonyl group, a thiocarbonyl group, a sulfonyl group, a sulfur atom, an oxygen atom, and a selenium atom, and more preferably, It is an atomic group selected from a methylene group, a carbonyl group and a sulfonyl group.

  In this specification, the electron-withdrawing substituent refers to a group in which Hammett's substituent constant σp takes a positive value. For Hammett's substituent constants, see Journal of Medicinal Chemistry, 1973, Vol. 16, no. 11, 1207-1216 etc. can be referred to. Examples of electron-withdrawing groups in which Hammett's substituent constant σp takes a positive valence include halogen atoms [fluorine atoms (σp value: 0.06), chlorine atoms (σp value: 0.23), bromine atoms (σp value). : 0.23), iodine atom (σp value: 0.18)], trihaloalkyl group [tribromomethyl (σp value: 0.29), trichloromethyl (σp value: 0.33), trifluoromethyl (σp Value: 0.54)], cyano group (σp value: 0.66), nitro group (σp value: 0.78), aliphatic / aryl or heterocyclic sulfonyl group [for example, methanesulfonyl (σp value: 0. 72)], aliphatic / aryl or heterocyclic acyl groups [for example, acetyl (σp value: 0.50), benzoyl (σp value: 0.43)], alkynyl groups [for example, C≡CH (σp value: 0) .23)], Aliphatic Ali Or a heterocyclic oxycarbonyl group [for example, methoxycarbonyl (σp value: 0.45), phenoxycarbonyl (σp value: 0.44)], carbamoyl group (σp value: 0.36), sulfamoyl group (σp value: 0.57), sulfoxide groups, heterocyclic groups, oxo groups, phosphoryl groups and the like.

Preferred electron withdrawing groups include amide groups, azo groups, nitro groups, fluoroalkyl groups having 1 to 5 carbon atoms, nitrile groups, alkoxycarbonyl groups having 1 to 5 carbon atoms, and acyl groups having 1 to 5 carbon atoms. , An alkylsulfonyl group having 1 to 9 carbon atoms, an arylsulfonyl group having 6 to 9 carbon atoms, an alkylsulfinyl group having 1 to 9 carbon atoms, an arylsulfinyl group having 6 to 9 carbon atoms, and an arylcarbonyl group having 6 to 9 carbon atoms , A thiocarbonyl group, a fluorine-containing alkyl group having 1 to 9 carbon atoms, a fluorine-containing aryl group having 6 to 9 carbon atoms, a fluorine-containing allyl group having 3 to 9 carbon atoms, an oxo group, and a group selected from a halogen element. More preferably, a nitro group, a fluoroalkyl group having 1 to 5 carbon atoms, a nitrile group, an alkoxycarbonyl group having 1 to 5 carbon atoms, an acyl group having 1 to 5 carbon atoms, a carbon number 6 9 arylsulfonyl group, an arylcarbonyl group having 6 to 9 carbon atoms, an oxo group, and a halogen element.
Specific examples of the compounds represented by formulas (LI) and (L-II) are shown below, but the present invention is not limited to these compounds.

The addition amount of the compound represented by the general formula (LI) and the general formula (L-II) is based on the total solid content of the single-layer recording layer from the viewpoint of the effectiveness of the addition and the effect of image formation. 0.1-10 mass% is preferable, Furthermore, 0.2-6 mass% is more preferable.
Any one lactone compound may be used in the present invention, or two or more lactone compounds may be used in combination. In addition, when two or more compounds of the general formula (LI) or two or more compounds of the general formula (L-II) are used, they should be used in any ratio as long as the total addition amount is within the above range. Can do.

  In addition, substances that are thermally decomposable, such as onium salts, o-quinonediazide compounds, aromatic sulfone compounds, aromatic sulfonic acid ester compounds, and that substantially reduce the solubility of alkali-soluble resins when not decomposed. Is preferably used from the viewpoint of improving the inhibition of the image portion in the developer.

  Examples of the onium salt used in the present invention include diazonium salts, ammonium salts, phosphonium salts, iodonium salts, sulfonium salts, selenonium salts, arsonium salts, and the like. I. Schlesinger, Photogr. Sci. Eng. , 18, 387 (1974), T.A. S. Balet al, Polymer, 21, 423 (1980), diazonium salts described in JP-A-5-158230, U.S. Pat. Nos. 4,069,055, 4,069,056, and JP-A-3-140140. Ammonium salts described in the specification, D.I. C. Necker et al, Macromolecules, 17, 2468 (1984), C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988), U.S. Pat. Nos. 4,069,055 and 4,069,056,

  J. et al. V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), Chem. & Eng. News, Nov. 28, p31 (1988), European Patent No. 104,143, US Pat. Nos. 5,041,358, 4,491,628, JP-A-2-150848 and JP-A-2-296514. Iodonium salts, J.M. V. Crivello et al, Polymer J. et al. 17, 73 (1985), J. Am. V. Crivello et al. J. et al. Org. Chem. 43, 3055 (1978); R. Watt et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 22, 1789 (1984), J. Am. V. Crivello et al, Polymer Bull. , 14, 279 (1985),

  J. et al. V. Crivello et al, Macromolecules, 14 (5), 1141 (1981), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. 17, 2877 (1979), European Patents 370,693, 233,567, 297,443, 297,442, U.S. Pat. Nos. 4,933,377, 3,902,114 No. 4,491,628, No. 4,760,013, No. 4,734,444, No. 2,833,827, German Patent No. 2,904,626, No. 3,604 The sulfonium salt described in No. 580 and No. 3,604,581,

J. et al. V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 17, 1047 (1979), a selenonium salt described in C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988).
Of these onium salts, a diazonium salt is particularly preferable. Particularly suitable diazonium salts include those described in JP-A-5-158230.

  The counter ion of the onium salt includes tetrafluoroboric acid, hexafluorophosphoric acid, triisopropylnaphthalenesulfonic acid, 5-nitro-o-toluenesulfonic acid, 5-sulfosalicylic acid, 2,5-dimethylbenzenesulfonic acid, 2,4,6-trimethylbenzenesulfonic acid, 2-nitrobenzenesulfonic acid, 3-chlorobenzenesulfonic acid, 3-bromobenzenesulfonic acid, 2-fluorocaprylnaphthalenesulfonic acid, dodecylbenzenesulfonic acid, 1-naphthol-5-sulfone Examples include acid, 2-methoxy-4-hydroxy-5-benzoyl-benzenesulfonic acid, and paratoluenesulfonic acid. Of these, particularly preferred are alkyl aromatic sulfonic acids such as hexafluorophosphoric acid, triisopropylnaphthalenesulfonic acid and 2,5-dimethylbenzenesulfonic acid.

Suitable quinonediazides include o-quinonediazide compounds. The o-quinonediazide compound used in the present invention is a compound having at least one o-quinonediazide group, which increases alkali solubility by thermal decomposition, and compounds having various structures can be used. That is, o-quinonediazide assists the solubility of the upper layer by both the effect of losing the inhibition as a development inhibitor due to thermal decomposition and the change of o-quinonediazide itself into an alkali-soluble substance.
Examples of such o-quinonediazide compounds include J. Org. The compounds described in pages 339 to 352 of “Light-Sensitive Systems” (John Wiley & Sons. Inc.) by Korser can be used, and in particular, o-quinonediazide reacted with various aromatic polyhydroxy compounds or aromatic amino compounds. The sulfonic acid esters or sulfonic acid amides are preferred. Further, benzoquinone (1,2) -diazide sulfonic acid chloride or naphthoquinone- (1,2) -diazide-5-sulfonic acid chloride and pyrogallol-acetone resin as described in JP-B-43-28403 Esters of benzoquinone- (1,2-diazide sulfonic acid chloride or naphthoquinone- (1,2) -diazide-5 described in US Pat. Nos. 3,046,120 and 3,188,210 Esters of sulfonic acid chloride and phenol-formaldehyde resin are also preferably used.

  Further, an ester of naphthoquinone- (1,2) -diazido-4-sulfonic acid chloride and phenol formaldehyde resin or cresol-formaldehyde resin, naphthoquinone- (1,2) -diazido-4-sulfonic acid chloride and pyrogallol-acetone resin, Similarly, the esters are also preferably used. Other useful o-quinonediazide compounds are reported and known in numerous patents. For example, JP-A-47-5303, JP-A-48-63802, JP-A-48-63803, JP-A-48-96575, JP-A-49-38701, JP-A-48-13354, Japanese Patent Publication Nos. 41-11222, 45-9610, 49-17474, U.S. Pat. Nos. 2,797,213, 3,454,400, 3,544,323, 3,573,917, 3,674,495, 3,785,825, British Patents 1,227,602, 1,251,345, 1,267, No. 005, No. 1,329,888, No. 1,330,932, German Patent No. 854,890, and the like.

The addition amount of the o-quinonediazide compound is preferably in the range of 0.1 to 8% by mass, more preferably 0.2 to 5% by mass, based on the total solid content of the single-layer recording layer. These compounds can be used alone, but may be used as a mixture of several kinds.
Moreover, you may include the alkali-soluble resin by which at least one part of Unexamined-Japanese-Patent No. 11-288089 was esterified.

Further, for the purpose of enhancing the inhibition of the surface of the recording layer and the scratch resistance of the surface, the perfluoroalkyl having 3 to 20 carbon atoms in the molecule as described in JP-A-2000-187318 is also disclosed. It is preferable to use a polymer having a (meth) acrylate monomer having 2 or 3 groups as a polymerization component.
The addition amount is preferably 0.5 to 15% by mass, more preferably 1 to 10% by mass, based on the total solid content of the single-layer recording layer.

[Other additives]
In forming the single-layer recording layer according to the present invention, various additives can be further added as necessary in addition to the above essential components as long as the effects of the present invention are not impaired.

<Development accelerator>
For the purpose of improving sensitivity, acid anhydrides, phenols, and organic acids may be added to the single-layer recording layer according to the present invention.
As the acid anhydrides, cyclic acid anhydrides are preferable. Specific examples of the cyclic acid anhydrides include phthalic anhydride, tetrahydrophthalic anhydride, and hexahydrophthalic anhydride described in US Pat. No. 4,115,128. Acid, 3,6-endooxy-tetrahydrophthalic anhydride, tetrachlorophthalic anhydride, maleic anhydride, chloromaleic anhydride, α-phenylmaleic anhydride, succinic anhydride, pyromellitic anhydride and the like can be used. Examples of the acyclic acid anhydride include acetic anhydride.

  Examples of phenols include bisphenol A, 2,2′-bishydroxysulfone, p-nitrophenol, p-ethoxyphenol, 2,4,4′-trihydroxybenzophenone, 2,3,4-trihydroxybenzophenone, 4- Examples include hydroxybenzophenone, 4,4 ′, 4 ″ -trihydroxytriphenylmethane, 4,4 ′, 3 ″, 4 ″ -tetrahydroxy-3,5,3 ′, 5′-tetramethyltriphenylmethane. .

Examples of organic acids include sulfonic acids, sulfinic acids, alkyl sulfates, phosphonic acids, phosphate esters, and carboxylic acids described in JP-A-60-88942 and JP-A-2-96755. Specifically, p-toluenesulfonic acid, dodecylbenzenesulfonic acid, p-toluenesulfinic acid, ethyl sulfate, phenylphosphonic acid, phenylphosphinic acid, phenyl phosphate, diphenyl phosphate, benzoic acid, isophthalic acid, adipic acid , P-toluic acid, 3,4-dimethoxybenzoic acid, phthalic acid, terephthalic acid, 4-cyclohexene-1,2-dicarboxylic acid, erucic acid, lauric acid, n-undecanoic acid, ascorbic acid and the like.
The proportion of the acid anhydride, phenols and organic acids in the total solid content of the single-layer recording layer is preferably 0.05 to 20% by mass, more preferably 0.1 to 15% by mass, and particularly preferably 0. .1 to 10% by mass.

<Surfactant>
In order to improve the coating property and to improve the stability of the processing with respect to the developing conditions, the single layer type recording layer according to the present invention is disclosed in Japanese Patent Application Laid-Open Nos. 62-251740 and 3-208514. Nonionic surfactants as described, amphoteric surfactants as described in JP-A-59-121044, JP-A-4-13149, and siloxanes as described in EP950517 Fluorine-containing monomer copolymers as described in JP-A-62-170950, JP-A-11-288093, and Japanese Patent Application No. 2001-247351 can be added.

  Specific examples of the nonionic surfactant include sorbitan tristearate, sorbitan monopalmitate, sorbitan trioleate, stearic acid monoglyceride, polyoxyethylene nonylphenyl ether and the like. Specific examples of amphoteric activators include alkyldi (aminoethyl) glycine, alkylpolyaminoethylglycine hydrochloride, 2-alkyl-N-carboxyethyl-N-hydroxyethylimidazolinium betaine and N-tetradecyl-N, N-betaine. Type (for example, trade name “Amorgen K” manufactured by Daiichi Kogyo Co., Ltd.).

As the siloxane compound, a block copolymer of dimethylsiloxane and polyalkylene oxide is preferable. Specific examples include DBE-224, DBE-621, DBE-712, DBP-732, DBP-534, manufactured by Chisso Corporation. And polyalkylene oxide-modified silicones such as Tego Glide 100 manufactured by Tego, Germany.
The proportion of the nonionic surfactant and amphoteric surfactant in the total solid content of the single-layer recording layer is preferably 0.01 to 15% by mass, more preferably 0.1 to 5.0% by mass, and still more preferably. Is 0.5-2.0 mass%.

<Bake-out agent / colorant>
To the single-layer recording layer according to the present invention, a printing-out agent for obtaining a visible image immediately after heating by exposure, or a dye or pigment as an image colorant can be added.
A representative example of the printing-out agent is a combination of a compound that releases an acid by heating by exposure (photoacid releasing agent) and an organic dye that can form a salt. Specifically, combinations of o-naphthoquinonediazide-4-sulfonic acid halides and salt-forming organic dyes described in JP-A-50-36209 and JP-A-53-8128, 36223, 54-74728, 60-3626, 61-143748, 61-151644, and 63-58440, and trihalomethyl compounds and salt-forming organic dyes Can be mentioned. Such trihalomethyl compounds include oxazole-based compounds and triazine-based compounds, both of which have excellent temporal stability and give clear printout images.

As the image colorant, other dyes can be used in addition to the aforementioned salt-forming organic dyes. Examples of suitable dyes including salt-forming organic dyes include oil-soluble dyes and basic dyes. Specifically, Oil Yellow # 101, Oil Yellow # 103, Oil Pink # 312, Oil Green BG, Oil Blue BOS, Oil Blue # 603, Oil Black BY, Oil Black BS, Oil Black T-505 (above Orient Chemical Industry) Co., Ltd.), Victoria Pure Blue, Crystal Violet Lactone, Crystal Violet (CI42555), Methyl Violet (CI42535), Ethyl Violet, Rhodamine B (CI145170B), Malachite Green (CI42000), Methylene Blue (CI522015), and the like. it can. The dyes described in JP-A-62-293247 are particularly preferred.
These dyes can be added in a proportion of 0.01 to 10% by mass, preferably 0.1 to 3% by mass, based on the total solid content of the single-layer recording layer.

<Plasticizer>
A plasticizer may be added to the single-layer recording layer according to the present invention in order to impart flexibility and the like of the coating film. For example, butylphthalyl, polyethylene glycol, tributyl citrate, diethyl phthalate, dibutyl phthalate, dihexyl phthalate, dioctyl phthalate, tricresyl phosphate, tributyl phosphate, trioctyl phosphate, tetrahydrofurfuryl oleate, acrylic acid or methacrylic acid These oligomers and polymers are used.
These plasticizers can be added in a proportion of 0.5 to 10% by mass, preferably 1.0 to 5% by mass, based on the total solid content of the single-layer recording layer.

<WAX agent>
In the single-layer recording layer according to the present invention, a compound that lowers the static friction coefficient of the surface can be added for the purpose of imparting scratch resistance. Specifically, US Pat. No. 6,117,913 or Japanese Patent Application Nos. 2001-261627, 2002-032904, and 2002-165854 previously proposed by the applicant of the present application. And compounds having an ester of a long-chain alkyl carboxylic acid as described in the above.
As the amount added, the proportion of the total solid content of the single-layer recording layer is preferably 0.1 to 10% by mass, and more preferably 0.5 to 5% by mass.

[Multilayer recording layer]
Next, a planographic printing plate precursor having a recording layer composed of a plurality of layers each having a different constituent component will be described when the recording layer of the planographic printing plate precursor of the present invention has a multilayer structure.
The (A) specific vinyl polymer and (B) infrared absorber, which are essential components of the recording layer in the present invention, may be contained in the same layer or in separate layers. The lithographic printing plate precursor having a multilayered recording layer which is a preferred embodiment in the invention includes (A) a lower layer containing a specific vinyl polymer, an upper layer containing an alkali-soluble resin and capable of forming an image by infrared irradiation. And a recording layer containing (B) an infrared absorber in at least one of the lower layer and the upper layer of the recording layer. Hereinafter, such a preferable multilayer recording layer will be described in detail.

[(A) Lower layer containing specific vinyl polymer]
The lower layer according to the present invention is characterized by containing the above-mentioned (A) specific vinyl polymer. The specific vinyl polymer used here is not particularly limited as long as it has a ring structure in the main chain and an active imide group as described above.
The content of the specific vinyl polymer in the lower layer of such a multilayer recording layer is preferably 50 to 100% by mass, more preferably 60 to 98% by mass in the total solid content of the lower recording layer, It is particularly preferably 65 to 95% by mass. Within this range, the printing layer is excellent in printing durability, chemical resistance, and image formability.

In the lower layer of the multi-layer recording layer, only such a specific vinyl polymer may be used as a binder resin, but from the viewpoint of improving film properties, in addition to the specific vinyl polymer, a range that does not impair the effects of the present invention. Other resins can be used in combination. Since the lower layer itself needs to express alkali solubility, particularly in the non-image area, it is necessary to select a resin that does not impair this property. From this viewpoint, examples of the resin that can be used in combination include alkali-soluble resins other than the specific vinyl polymer. As for the alkali-soluble resin that can be used in combination with the specific vinyl polymer, a general alkali-soluble resin described later can be used as an upper layer component. Among these, for example, polyamide resins, resins containing epoxy groups, polyvinyl acetal resins, acrylic resins, methacrylic resins, polystyrene resins, novolac phenolic resins, polyurethane resins and the like can be preferably exemplified.
As a ratio which mixes general alkali-soluble resin, 40 mass% or less of all the alkali-soluble resins contained in a lower layer is preferable, 35 mass% or less is more preferable, It is especially preferable that it is 30 mass% or less.

  Moreover, as a component contained in the lower layer based on this invention, an infrared absorber and another additive can be further used as needed. Examples of other additives include development accelerators, surfactants, printout / coloring agents, plasticizers, and WAX agents. The details of these components are the same as those described as components of the upper layer described later.

[Upper layer containing an alkali-soluble resin and capable of forming an image by infrared irradiation]
The upper layer according to the present invention contains an alkali-soluble tree and can form an image by irradiation with infrared rays.

(Alkali-soluble resin)
The alkali-soluble resin that can be used for the upper layer in the present invention is not particularly limited as long as it has a property of dissolving when contacted with an alkaline developer, but an acidic group is present on the main chain and / or side chain in the polymer. It is preferably a homopolymer to be contained, a copolymer thereof, or a mixture thereof. Moreover, the above-mentioned specific vinyl polymer can also be added to the upper layer.
Examples of the alkali-soluble resin having such an acidic group include (1) phenolic hydroxyl group, (2) sulfonamide group, (3) active imide group, (4) carboxylic acid group, and (5) phosphoric acid group. Examples thereof include polymer compounds having any functional group in the molecule, and among them, a polymer compound having (1) a phenolic hydroxyl group, (2) a sulfonamide group, and (3) an active imide group is particularly preferable. Examples of such a polymer compound include the following, but the present invention is not limited thereto.

  (1) Examples of the polymer compound having a phenolic hydroxyl group include phenol formaldehyde resin, m-cresol formaldehyde resin, p-cresol formaldehyde resin, m- / p-mixed cresol formaldehyde resin, phenol / cresol (m-, p Any of-or m- / p-mixing) may be used. Examples thereof include novolak resins such as mixed formaldehyde resins and pyrogallol acetone resins. In addition to this, a polymer compound having a phenolic hydroxyl group in the side chain is preferably used as the polymer compound having a phenolic hydroxyl group. As a polymer compound having a phenolic hydroxyl group in the side chain, a polymerizable monomer comprising a low molecular compound having at least one phenolic hydroxyl group and at least one polymerizable unsaturated bond is homopolymerized, or other polymerization is performed on the monomer. And a high molecular compound obtained by copolymerizing a functional monomer.

  Examples of the polymerizable monomer having a phenolic hydroxyl group include acrylamide, methacrylamide, acrylic acid ester, methacrylic acid ester, and hydroxystyrene having a phenolic hydroxyl group. Specifically, N- (2-hydroxyphenyl) acrylamide, N- (3-hydroxyphenyl) acrylamide, N- (4-hydroxyphenyl) acrylamide, N- (2-hydroxyphenyl) methacrylamide, N- (3- Hydroxyphenyl) methacrylamide, N- (4-hydroxyphenyl) methacrylamide, o-hydroxyphenyl acrylate, m-hydroxyphenyl acrylate, p-hydroxyphenyl acrylate, o-hydroxyphenyl methacrylate, m-hydroxyphenyl methacrylate, p-hydroxy Phenyl methacrylate, o-hydroxystyrene, m-hydroxystyrene, p-hydroxystyrene, 2- (2-hydroxyphenyl) ethyl acrylate, 2- (3-hydroxyphenyl) Preferable are til acrylate, 2- (4-hydroxyphenyl) ethyl acrylate, 2- (2-hydroxyphenyl) ethyl methacrylate, 2- (3-hydroxyphenyl) ethyl methacrylate, 2- (4-hydroxyphenyl) ethyl methacrylate, etc. Can be used. Such resins having a phenolic hydroxyl group may be used in combination of two or more. Furthermore, as described in US Pat. No. 4,123,279, phenol and formaldehyde having an alkyl group having 3 to 8 carbon atoms as a substituent, such as t-butylphenol formaldehyde resin and octylphenol formaldehyde resin, These copolymers may be used in combination.

(2) Examples of the alkali-soluble resin having a sulfonamide group include polymer compounds obtained by homopolymerizing a polymerizable monomer having a sulfonamide group or copolymerizing the monomer with another polymerizable monomer. The polymerizable monomer having a sulfonamide group includes one or more sulfonamide groups —NH—SO ₂ — in which at least one hydrogen atom is bonded on a nitrogen atom and one or more polymerizable unsaturated bonds in one molecule. And a polymerizable monomer comprising a low molecular weight compound. Among them, a low molecular compound having an acryloyl group, an allyl group, or a vinyloxy group, and a substituted or monosubstituted aminosulfonyl group or a substituted sulfonylimino group is preferable.

(3) The alkali-soluble resin having an active imide group is preferably one having an active imide group in the molecule, and the polymer compound has one unsaturated bond polymerizable with the active imide group in each molecule. Examples thereof include a polymer compound obtained by homopolymerizing a polymerizable monomer comprising the above-described low molecular weight compound, or copolymerizing the monomer with another polymerizable monomer.
As such a compound, specifically, N- (p-toluenesulfonyl) methacrylamide, N- (p-toluenesulfonyl) acrylamide and the like can be preferably used.

  (4) As an alkali-soluble resin having a carboxylic acid group, for example, a minimum structural unit derived from a compound having at least one carboxylic acid group and polymerizable unsaturated group in the molecule is used as a main constituent component. A polymer can be mentioned.

  (5) As an alkali-soluble resin having a phosphoric acid group, for example, a minimum structural unit derived from a compound having at least one phosphoric acid group and a polymerizable unsaturated group in the molecule is used as a main constituent component. A polymer can be mentioned.

  As the alkali-soluble resin used in the upper layer according to the present invention, two or more kinds of the polymerizable monomer having a phenolic hydroxyl group, the polymerizable monomer having a sulfonamide group, and the polymerizable monomer having an active imide group are polymerized. It is preferable to be a high molecular compound. Although there is no restriction | limiting in the copolymerization ratio of the said polymerizable monomer, and the combination of a polymerizable monomer, Especially the polymerizable monomer which has a sulfonamide group in the polymerizable monomer which has a phenolic hydroxyl group, and / or the polymerizable property which has an active imide group When monomers are copolymerized, the compounding polymerization ratio of these components is preferably in the range of 50:50 to 5:95, and particularly preferably in the range of 40:60 to 10:90.

Furthermore, as the alkali-soluble resin used in the upper layer, one or more kinds selected from the polymerizable monomer having a phenolic hydroxyl group, the polymerizable monomer having a sulfonamide group, or the polymerizable monomer having an active imide group are used. In addition to the polymerizable monomer, a polymer compound obtained by copolymerizing another polymerizable monomer is preferable. As a copolymerization ratio in this case, it is preferable that the monomer which provides alkali solubility is included 10 mol% or more from a viewpoint of developability, and what contains 20 mol% or more is more preferable.
Examples of other polymerizable monomers that can be used here include the compounds listed in the following (m1) to (m12), but the present invention is not limited thereto.

(M1) Acrylic acid esters and methacrylic acid esters having an aliphatic hydroxyl group such as 2-hydroxyethyl acrylate or 2-hydroxyethyl methacrylate.
(M2) Alkyl acrylates such as methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, amyl acrylate, hexyl acrylate, octyl acrylate, benzyl acrylate, 2-chloroethyl acrylate, and glycidyl acrylate.
(M3) Alkyl methacrylates such as methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, amyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, 2-chloroethyl methacrylate and glycidyl methacrylate.
(M4) Acrylamide, methacrylamide, N-methylol acrylamide, N-ethyl acrylamide, N-hexyl methacrylamide, N-cyclohexyl acrylamide, N-hydroxyethyl acrylamide, N-phenyl acrylamide, N-nitrophenyl acrylamide, N-ethyl- Acrylamide or methacrylamide such as N-phenylacrylamide.

(M5) Vinyl ethers such as ethyl vinyl ether, 2-chloroethyl vinyl ether, hydroxyethyl vinyl ether, propyl vinyl ether, butyl vinyl ether, octyl vinyl ether, and phenyl vinyl ether.
(M6) Vinyl esters such as vinyl acetate, vinyl chloroacetate, vinyl butyrate and vinyl benzoate.
(M7) Styrenes such as styrene, α-methylstyrene, methylstyrene, chloromethylstyrene.
(M8) Vinyl ketones such as methyl vinyl ketone, ethyl vinyl ketone, propyl vinyl ketone, and phenyl vinyl ketone.
(M9) Olefins such as ethylene, propylene, isobutylene, butadiene and isoprene.
(M10) N-vinylpyrrolidone, acrylonitrile, methacrylonitrile and the like.
(M11) Unsaturated imides such as maleimide, N-acryloylacrylamide, N-acetylmethacrylamide, N-propionylmethacrylamide, N- (p-chlorobenzoyl) methacrylamide.
(M12) Unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic anhydride and itaconic acid.

The alkali-soluble resin used in the upper layer according to the present invention is a homopolymer or copolymer of a polymerizable monomer having a phenolic hydroxyl group, a polymerizable monomer having a sulfonamide group, or a polymerizable monomer having an active imide group. In this case, those having a weight average molecular weight of 2,000 or more and a number average molecular weight of 500 or more are preferred. More preferably, the weight average molecular weight is 5,000 to 300,000, the number average molecular weight is 800 to 250,000, and the dispersity (weight average molecular weight / number average molecular weight) is 1.1 to 10. .
In particular, when the alkali-soluble resin used in the upper layer according to the present invention is a phenol formaldehyde resin or a cresol aldehyde resin, the weight average molecular weight is 500 to 20,000 and the number average molecular weight is 200 to 10 1,000 is preferred.

As the alkali-soluble resin used for the upper layer, a resin having a phenolic hydroxyl group is desirable because it causes strong hydrogen bonding in the unexposed area and some hydrogen bonds are easily released in the exposed area. Among the resins having a functional hydroxyl group, a novolak resin is particularly preferable.
In the present invention, two or more kinds of alkali-soluble resins having different dissolution rates in an alkaline aqueous solution may be mixed and used, and the mixing ratio in that case is arbitrary. The alkali-soluble resin suitable for mixing with the resin having a phenolic hydroxyl group is preferably an acrylic resin because of its low compatibility with a resin having a phenolic hydroxyl group, and more preferably a sulfoamide group. It is an acrylic resin.

  The content of the alkali-soluble resin relative to the total solid content of the upper layer is preferably used in an addition amount of 50 to 98% by mass from the viewpoints of durability and sensitivity of the recording layer.

((B) infrared absorber)
In the lithographic printing plate precursor having the multilayer type recording layer of the present invention, it is necessary to add an infrared absorber to at least one of the lower layer and the upper layer of the recording layer. As such an infrared absorber, the same infrared absorber as that used in the single-layer recording layer can be used.
These infrared absorbers may be added to the lower layer, the upper layer, or both the upper and lower layers, but are preferably added to the upper layer of the recording layer or the vicinity thereof from the viewpoint of sensitivity. In particular, it is preferable to add an infrared absorber having dissolution inhibiting ability to the same layer as the alkali-soluble resin in the upper layer, so that the unexposed area can have alkali solubility resistance at the same time as high sensitivity. .
On the other hand, when added to the lower layer, it is possible to realize further higher sensitivity. When an infrared absorber is added to both the upper layer and the lower layer, the same compound may be used, or different compounds may be used.
These infrared absorbers may be added to the same layer as the upper and lower recording layers, or may be added to another layer provided. In the case of a separate layer, it is desirable to add it to a layer adjacent to the recording layer.

  As the addition amount of the infrared absorber, from the viewpoint of sensitivity and durability (film properties) of the recording layer when added to the upper layer, it is 0.01 to 30% by mass, preferably 0.1%, based on the total solid content of the upper layer. It can be added at a ratio of ˜20% by mass, particularly preferably 1.0 to 10% by mass.

  On the other hand, when adding to a lower layer, it is 0-20 mass% with respect to a lower layer total solid, Preferably it is 0-10 mass%, Most preferably, it can add in the ratio of 0-5 mass%. When an infrared absorber is added to the lower layer, the solubility of the lower layer decreases if an infrared absorber having dissolution inhibiting ability is used. On the other hand, the infrared absorber generates heat during infrared laser exposure, and the solubility of the lower layer is improved by heat. Therefore, the compound to be added and the addition amount should be selected in consideration of these balances. In the region of 0.2 to 0.3 μm in the vicinity of the support, it is difficult to obtain the effect of improving the solubility due to heat, for example, the heat generated during exposure diffuses to the support. In some cases, the decrease in sensitivity may cause a decrease in sensitivity. Therefore, even within the range of the addition amount shown above, such an addition amount that the dissolution rate in the lower layer developer (25 ° C. to 30 ° C.) is lower than 30 nm / sec is not preferable.

((C) Development inhibitor)
The upper layer according to the present invention preferably contains a development inhibitor for the purpose of enhancing its inhibition (dissolution inhibiting ability). In particular, when an infrared absorber that does not have dissolution inhibiting ability is used, this development inhibitor can be an important component for maintaining the alkali resistance of the image area.
As the development inhibitor used for the multi-layer recording layer, the same development inhibitor as the component (C) described above as the component of the single-layer recording layer can be used. For example, quaternary ammonium salts, polyethylene glycol compounds and the like are preferably used. Among the image colorants described below, there are compounds that function as a development inhibitor, and these are also preferred.

As the quaternary ammonium salt, those similar to the quaternary ammonium salts mentioned as the development inhibitor for the single-layer recording layer can be used.
The addition amount of the quaternary ammonium salt is preferably 0.1 to 50% by mass and 1 to 30% by mass with respect to the total solid content of the upper layer from the viewpoint of the development inhibiting effect and the film forming property of the alkali-soluble resin. % Is more preferable.

As the polyethylene glycol compound, those similar to the polyethylene glycol compounds mentioned as the development inhibitor for the single-layer recording layer can be used.
The addition amount of the polyethylene glycol compound is preferably from 0.1 to 50% by mass, and preferably from 1 to 30% by mass, based on the total solid content of the upper layer, from the viewpoints of development inhibition effect and image forming property. More preferred.

The lactone compound is also effective for obtaining the same effect as that of the single-layer recording layer, and the same compounds as those mentioned for the single-layer recording layer can be used.
Among such lactone compounds, the addition amount of the compounds represented by the general formula (LI) and the general formula (L-II) that are particularly preferably used includes the effectiveness of addition and the effect of image forming properties. From a viewpoint, 0.1-50 mass% is preferable with respect to the upper-layer total solid, Furthermore, 1-30 mass% is more preferable.

In addition, substances that are thermally decomposable, such as onium salts, o-quinonediazide compounds, aromatic sulfone compounds, aromatic sulfonic acid ester compounds, and that substantially reduce the solubility of alkali-soluble resins when not decomposed. Is preferably used from the viewpoint of improving the inhibition of the image portion in the developer.
As the onium salt, those similar to the onium salts mentioned as the development inhibitor for the single-layer recording layer can be used.
As the o-quinonediazides, those similar to the o-quinonediazides mentioned as the development inhibitor for the single-layer recording layer can be used.
The addition amount of the o-quinonediazide compound is preferably in the range of 1 to 50% by mass, more preferably 5 to 30% by mass, and particularly preferably 10 to 30% by mass with respect to the total solid content of the upper layer.

Further, for the purpose of enhancing the inhibition of the surface of the recording layer and the scratch resistance of the surface, the perfluoroalkyl having 3 to 20 carbon atoms in the molecule as described in JP-A-2000-187318 is also disclosed. It is preferable to use a polymer having a (meth) acrylate monomer having 2 or 3 groups as a polymerization component.
As addition amount, 0.1-10 mass% is preferable with respect to upper layer total solid, More preferably, it is 0.5-5 mass%.

(Other additives)
In forming the lower layer and the upper layer of the polymerization type recording layer, in addition to the above essential components, various additives can be further added as necessary as long as the effects of the present invention are not impaired. The additives listed below may be added only to the lower layer, may be added only to the upper layer, or may be added to both layers.

<Development accelerator>
A development accelerator may be added to the upper layer and / or the lower layer as the recording layer according to the present invention for the purpose of improving sensitivity. As such a development accelerator, the acid anhydrides, phenols, and organic acids mentioned as the development accelerator for the single-layer recording layer can be used.
The proportion of the acid anhydride, phenols, and organic acids in the total solid content of the lower or upper layer is preferably 0.05 to 20% by mass, more preferably 0.1 to 15% by mass, and particularly preferably 0. 1 to 10% by mass.

<Surfactant>
A surfactant can be added to the upper layer and / or the lower layer, which are recording layers according to the present invention, in order to improve the coating properties and to increase the stability of the processing with respect to the development conditions. As such a surfactant, the nonionic surfactants and amphoteric surfactants exemplified as the surfactant for the single-layer recording layer can be used.
The ratio of the nonionic surfactant and the amphoteric surfactant to the total solid content of the lower layer or upper layer is preferably 0.01 to 15% by mass, more preferably 0.1 to 5.0% by mass, and still more preferably 0. .5 to 2.0% by mass.

<Bake-out agent / colorant>
To the upper layer and / or the lower layer, which is the recording layer according to the present invention, a print-out agent for obtaining a visible image immediately after heating by exposure, or a dye or pigment as an image colorant can be added.
As such a print-out agent or image colorant, the same print-out agents or image colorants as those mentioned for the single-layer recording layer can be used.
These dyes can be added in a proportion of 0.01 to 10% by mass, preferably 0.1 to 3% by mass, based on the total solid content of the lower layer or upper layer.

<Plasticizer>
A plasticizer may be added to the upper layer and / or the lower layer, which are recording layers according to the present invention, in order to impart flexibility of the coating film. As such a plasticizer, the same plasticizers as those mentioned for the single-layer recording layer can be used.
These plasticizers can be added in a proportion of 0.5 to 10% by mass, preferably 1.0 to 5% by mass, based on the total solid content of the lower layer or the upper layer.

<WAX agent>
In the upper layer according to the present invention, for the purpose of imparting resistance to scratches, a compound that reduces the static friction coefficient of the surface can be added. As such a compound, those similar to the WAX agent exemplified in the single-layer recording layer can be used. The addition amount is preferably 0.1 to 10% by mass, more preferably 0.5 to 5% by mass in the upper layer.

[Formation of recording layer]
The recording layer of the lithographic printing plate precursor according to the present invention (single layer type recording layer or lower layer or upper layer of the multi-layer type recording layer) is usually prepared by dissolving the above-mentioned components in a solvent to form a recording layer coating solution. It can form by apply | coating on.
Solvents used here include ethylene dichloride, cyclohexanone, methyl ethyl ketone, methanol, ethanol, propanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, 2-methoxyethyl acetate, 1-methoxy-2-propyl acetate, dimethoxy Examples include ethane, methyl lactate, ethyl lactate, N, N-dimethylacetamide, N, N-dimethylformamide, tetramethylurea, N-methylpyrrolidone, dimethyl sulfoxide, sulfolane, γ-butyrolactone, and toluene. It is not limited. These solvents are used alone or in combination.

In particular, in the multilayer recording layer, it is preferable that the lower layer and the upper layer are formed by separating the two layers in principle.
As a method for forming the two layers separately, for example, a method using a difference in solvent solubility between a component contained in the lower layer and a component contained in the upper layer, or after applying the upper layer, a solvent is rapidly used. For example, a method of drying and removing.
Hereinafter, although these methods are explained in full detail, the method of apply | coating two layers separately is not limited to these.

  As a method of utilizing the difference in solvent solubility between the component contained in the lower layer and the component contained in the upper layer, a solvent system in which any of the components contained in the lower layer is insoluble is used when the upper layer coating solution is applied. Is. Thereby, even if it carries out 2 layer application | coating, it becomes possible to isolate | separate each layer clearly and to make a coating film. For example, as the lower layer component, a component insoluble in a solvent such as methyl ethyl ketone or 1-methoxy-2-propanol that dissolves the alkali-soluble resin that is the upper layer component is selected, and the lower layer is applied using a solvent system that dissolves the lower layer component. -It is possible to form two layers by drying and then dissolving the upper layer component mainly composed of alkali-soluble resin with methyl ethyl ketone, 1-methoxy-2-propanol, etc., and applying and drying.

  Next, after applying the second layer (upper layer), as a method of drying the solvent very quickly, a method of blowing high-pressure air from a slit nozzle installed substantially perpendicular to the running direction of the web, heating with steam, etc. The method of giving thermal energy as conduction heat from the lower surface of the web from the roll (heating roll) supplied inside the medium, or a combination of these methods can be mentioned.

  Moreover, in order to provide a new function, the upper layer and the lower layer may be partially miscible in a range where the effects of the present invention are sufficiently exhibited. Such a method can be achieved by adjusting the degree of any of the above methods using the difference in solvent solubility and the method of drying the solvent very quickly after coating the second layer.

The concentration of the above-described components (total solid content including additives) in the recording layer coating solution coated on the support is preferably 1 to 50% by mass.
Various methods can be used as the coating method, and examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.
In particular, when applying the upper layer in the multilayer recording layer, it is desirable that the upper layer application method is a non-contact type in order to prevent damage to the lower layer. Further, although it is a contact type, it is possible to use bar coater coating as a method generally used for solvent-based coating, but it is desirable to perform coating by forward rotation in order to prevent damage to the lower layer.

In the single-layer recording layer, the coating amount of the recording layer component after drying is preferably in the range of 0.7 to 4.0 g / m ² , more preferably 0, from the viewpoint of sensitivity and printing durability. The range is from 8 to 3.0 g / m ² .

In the multi-layer recording layer, the coating amount of the lower layer component after drying is preferably in the range of 0.5 to 4.0 g / m ² , more preferably 0.6, from the viewpoint of sensitivity and printing durability. It is in the range of ˜2.5 g / m ² .
The coating amount of the upper layer component after drying is preferably in the range of 0.05 to 1.0 g / m ² , and more preferably 0.08 to 0.08 from the viewpoint of sensitivity, development latitude, scratch resistance, and the like. The range is 0.7 g / m ² .
The coating amount after drying combining the lower layer and the upper layer is preferably in the range of 0.6 to 4.0 g / m ² , more preferably from the viewpoint of sensitivity, image reproducibility, printing durability, and the like. in the range of 0.7 to 2.5 g / m ^2.

[Support]
The support used in the lithographic printing plate precursor according to the present invention is not particularly limited as long as it is a dimensionally stable plate having the required strength and durability. For example, paper, plastic (for example, Paper laminated with polyethylene, polypropylene, polystyrene, etc., metal plate (eg, aluminum, zinc, copper, etc.), plastic film (eg, cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, Cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), paper laminated with a metal as described above, or vapor-deposited paper, or a plastic film.

  Among them, in the present invention, a polyester film or an aluminum plate is preferable, and among them, an aluminum plate that has good dimensional stability and is relatively inexpensive is particularly preferable. A suitable aluminum plate is a pure aluminum plate or an alloy plate containing aluminum as a main component and containing a trace amount of different elements, and may be a plastic film on which aluminum is laminated or vapor-deposited. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is at most 10% by mass.

Particularly suitable aluminum in the present invention is pure aluminum, but completely pure aluminum is difficult to produce in the refining technique, and may contain slightly different elements.
Thus, the composition of the aluminum plate applied to the present invention is not specified, and conventionally known and used aluminum plates can be appropriately used. The thickness of the aluminum plate used in the present invention is about 0.1 mm to 0.6 mm, preferably 0.15 mm to 0.4 mm, and particularly preferably 0.2 mm to 0.3 mm.

Such an aluminum plate may be subjected to surface treatment such as roughening treatment or anodizing treatment, if necessary. Hereinafter, such a surface treatment will be briefly described.
Prior to roughening the aluminum plate, a degreasing treatment with, for example, a surfactant, an organic solvent, or an alkaline aqueous solution for removing rolling oil on the surface is performed as desired. The surface roughening treatment of the aluminum plate is performed by various methods. For example, a method of mechanically roughening, a method of electrochemically dissolving and roughening a surface, and a method of selectively dissolving a surface chemically. This is done by the method of As the mechanical method, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used. Further, as an electrochemical surface roughening method, there is a method of performing alternating current or direct current in hydrochloric acid or nitric acid electrolyte. Further, as disclosed in JP-A-54-63902, a method in which both are combined can also be used.
The aluminum plate roughened as described above is subjected to an alkali etching treatment and neutralization treatment as necessary, and then subjected to an anodizing treatment if desired in order to enhance the water retention and wear resistance of the surface. As the electrolyte used for the anodizing treatment of the aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, phosphoric acid, oxalic acid, chromic acid, or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.

The treatment conditions for anodization vary depending on the electrolyte used, and thus cannot be specified in general. In general, however, the electrolyte concentration is 1 to 80% by mass solution, the liquid temperature is 5 to 70 ° C., and the current density is 5 to 60 A / dm ^2. A voltage of 1 to 100 V and an electrolysis time of 10 seconds to 5 minutes are suitable. When the amount of the anodized film is less than 1.0 g / m ² , the printing durability is insufficient, or the non-image part of the lithographic printing plate is easily damaged, and the ink adheres to the damaged part during printing. So-called “scratch dirt” is likely to occur.
After the anodizing treatment, the aluminum surface is subjected to a hydrophilic treatment if necessary.

  The hydrophilization treatment used in the present invention is disclosed in US Pat. Nos. 2,714,066, 3,181,461, 3,280,734 and 3,902,734. There are alkali metal silicate (such as aqueous sodium silicate) methods. In this method, the support is immersed in an aqueous sodium silicate solution or electrolytically treated. In addition, it is disclosed in potassium fluoride zirconate disclosed in Japanese Patent Publication No. 36-22063 and US Pat. Nos. 3,276,868, 4,153,461, and 4,689,272. A method of treating with polyvinylphosphonic acid is used.

(Undercoat layer)
In the lithographic printing plate precursor according to the invention, an undercoat layer can be provided between the support and the recording layer, if necessary.
Various organic compounds are used as the undercoat layer component. For example, phosphonic acids having an amino group such as carboxymethylcellulose, dextrin, gum arabic, 2-aminoethylphosphonic acid, phenylphosphonic acid which may have a substituent, Organic phosphonic acids such as naphthylphosphonic acid, alkylphosphonic acid, glycerophosphonic acid, methylenediphosphonic acid and ethylenediphosphonic acid, optionally substituted phenylphosphoric acid, naphthylphosphoric acid, alkylphosphoric acid and glycerophosphoric acid Organic phosphoric acid, optionally substituted phenylphosphinic acid, naphthylphosphinic acid, organic phosphinic acids such as alkylphosphinic acid and glycerophosphinic acid, amino acids such as glycine and β-alanine, and hydrochloride of triethanolamine Hydroxy groups such as Selected from hydrochloride of the amine to be, but may be used by mixing two or more.

  The undercoat layer preferably contains a compound having an onium group. The compounds having an onium group are described in detail in JP-A Nos. 2000-10292 and 2000-108538. In addition, a compound selected from the group of polymer compounds having a structural unit represented by poly (p-vinylbenzoic acid) in the molecule can also be used. Specific examples of these polymer compounds include a copolymer of p-vinylbenzoic acid and vinylbenzyltriethylammonium salt, a copolymer of p-vinylbenzoic acid and vinylbenzyltrimethylammonium chloride, and the like. .

This organic undercoat layer can be provided by the following method. That is, a method in which a solution obtained by dissolving the above organic compound in water or an organic solvent such as methanol, ethanol, methyl ethyl ketone, or a mixed solvent thereof is applied on an aluminum plate and dried, and water, methanol, ethanol, methyl ethyl ketone, etc. In this method, an aluminum plate is immersed in a solution in which the above organic compound is dissolved in the above organic solvent or a mixed solvent thereof to adsorb the above compound, followed by washing with water or the like and drying to provide an organic undercoat layer. In the former method, a solution having a concentration of 0.005 to 10% by mass of the organic compound can be applied by various methods. In the latter method, the concentration of the solution is 0.01 to 20% by mass, preferably 0.05 to 5% by mass, the immersion temperature is 20 to 90 ° C., preferably 25 to 50 ° C., and the immersion time is 0.1 second to 20 minutes, preferably 2 seconds to 1 minute. The solution used for this can be adjusted to a pH range of 1 to 12 with basic substances such as ammonia, triethylamine, potassium hydroxide, and acidic substances such as hydrochloric acid and phosphoric acid. A yellow dye can also be added to improve the tone reproducibility of the image recording material.
The coverage of the organic undercoat layer, from the viewpoint of printing durability, 2 to 200 mg / m ² are suitable, and preferably from 5 to 100 mg / m ^2.
The lithographic printing plate precursor produced as described above is imagewise exposed and then developed.

(Back coat layer)
A back coat layer is provided on the back surface of the support of the lithographic printing plate precursor according to the invention, if necessary. Such a back coat layer comprises a metal oxide obtained by hydrolysis and polycondensation of an organic polymer compound described in JP-A-5-45885 and an organic or inorganic metal compound described in JP-A-6-35174. A coating layer is preferably used. Among these coating layers, silicon alkoxy compounds such as Si (OCH ₃ ) ₄ , Si (OC ₂ H ₅ ) ₄ , Si (OC ₃ H ₇ ) ₄ , and Si (OC ₄ H ₉ ) ₄ are available at a low price. The coating layer of the metal oxide obtained therefrom is particularly preferable because of its excellent developer resistance.

〔exposure〕
The actinic ray light source used for image exposure of the lithographic printing plate precursor according to the present invention is preferably a light source having an emission wavelength in the near infrared to infrared region, and a solid laser or a semiconductor laser is particularly preferred.

[Development processing]
The developer that can be applied to the development processing of the lithographic printing plate precursor according to the invention is a developer having a pH in the range of 9.0 to 14.0, preferably in the range of 12.0 to 13.5. A conventionally known alkaline aqueous solution can be used as the developer (hereinafter referred to as developer including the replenisher). For example, sodium silicate, potassium, tribasic sodium phosphate, potassium, ammonium, dibasic sodium phosphate, potassium, ammonium, sodium carbonate, potassium, ammonium, sodium bicarbonate, potassium, Examples include inorganic alkali salts such as ammonium, sodium borate, potassium, ammonium, sodium hydroxide, ammonium, potassium, and lithium. Moreover, monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropylamine, diisopropylamine, triisopropylamine, n-butylamine, monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, Organic alkali agents such as ethyleneimine, ethylenediamine, and pyridine are listed. These alkaline aqueous solutions may be used individually by 1 type, and may use 2 or more types together.

  Among the above alkaline aqueous solutions, one of the developers exhibiting the effect of the present invention contains one containing an alkali silicate as a base, or an alkali silicate mixed with a silicon compound in a base, The so-called “silicate developer” is an aqueous solution having a pH of 12 or more, and another more preferable developer does not contain an alkali silicate and contains a non-reducing sugar (an organic compound having a buffering action) and a base. “Non-silicate developer”.

In the former, the aqueous solution of alkali metal silicate is represented by the ratio of silicon oxide SiO ₂ which is a component of silicate to alkali metal oxide M ₂ O (generally expressed as a molar ratio of [SiO ₂ ] / [M ₂ O]. ) And the density, the developing property can be adjusted. For example, as disclosed in JP-A-54-62004, the molar ratio of SiO ₂ / Na ₂ O is 1.0 to 1.5 (that is, [SiO ₂ ] / [Na ₂ O] is 1.0 to 1.5), and an aqueous solution of sodium silicate having a SiO ₂ content of 1 to 4 mass% is disclosed in JP-B-57-7427. As described, [SiO ₂ ] / [M] is 0.5 to 0.75 (ie, [SiO ₂ ] / [M ₂ O] is 1.0 to 1.5), and SiO ₂ The developer is based on gram atoms of all alkali metals present in the developer. A manner containing potassium at least 20%, aqueous solution of an alkali metal silicate is preferably used.

  A so-called “non-silicate developer” that does not contain an alkali silicate and contains a non-reducing sugar and a base is also preferable for application to the development of the lithographic printing plate precursor according to the invention. When the development processing of the lithographic printing plate precursor is performed using this developer, the surface of the recording layer is not deteriorated and the thickness of the recording layer can be maintained in a better state.

  The main component of the developer is preferably composed of at least one compound selected from non-reducing sugars and at least one base, and the pH of the solution is in the range of 9.0 to 13.5. Such non-reducing sugars are saccharides that do not have a free aldehyde group or ketone group and do not exhibit reducing properties, and are trehalose-type oligosaccharides in which reducing groups are bonded to each other, and glycosides in which a reducing group of saccharides and non-saccharides are bonded. It is classified into sugar alcohols reduced by hydrogenating the body and saccharides, and any of them is preferably used. Trehalose type oligosaccharides include saccharose and trehalose. Examples of glycosides include alkyl glycosides, phenol glycosides, mustard oil glycosides, and the like. Examples of the sugar alcohol include D, L-arabit, rebit, xylit, D, L-sorbit, D, L-mannit, D, L-exit, D, L-talit, zulsiit and allozulcit. Furthermore, maltitol obtained by hydrogenation of a disaccharide and a reduced form (reduced water candy) obtained by hydrogenation of an oligosaccharide are preferably used. Among these, sugar alcohol and saccharose are particularly preferred non-reducing sugars, and D-sorbite, saccharose, and reduced syrup are particularly preferred because they have a buffering action in an appropriate pH region and are inexpensive.

  These non-reducing sugars can be used singly or in combination of two or more, and the proportion of the non-reducing sugar in the developer is preferably 0.1 to 30% by mass from the viewpoint of buffering effect and developability, Preferably, it is 1-20 mass%.

  A conventionally known alkaline agent can be used as the base to be combined with the non-reducing sugar. For example, sodium hydroxide, potassium hydroxide, lithium hydroxide, trisodium phosphate, tripotassium phosphate, triammonium phosphate, disodium phosphate, dipotassium phosphate, diammonium phosphate, sodium carbonate, potassium carbonate, Examples include inorganic alkali agents such as ammonium carbonate, sodium hydrogen carbonate, potassium hydrogen carbonate, ammonium hydrogen carbonate, sodium borate, potassium borate, and ammonium borate. Moreover, monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropylamine, diisopropylamine, triisopropylamine, n-butylamine, monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, Organic alkali agents such as ethyleneimine, ethylenediamine, and pyridine are also used.

These alkali agents are used alone or in combination of two or more. Among these, sodium hydroxide and potassium hydroxide are preferable because the pH can be adjusted in a wide pH range by adjusting these amounts relative to the non-reducing sugar. Further, trisodium phosphate, tripotassium phosphate, sodium carbonate, potassium carbonate and the like are preferable because they have a buffering action.
These alkali agents are added so that the pH of the developer is in the range of 9.0 to 13.5, and the addition amount is determined by the desired pH, the type and addition amount of the non-reducing sugar, and more preferable pH. The range is 10.0 to 13.2.

Further, an alkaline buffer composed of a weak acid other than sugars and a strong base can be used in combination with the developer. As the weak acid used as such a buffer, one having a dissociation constant (pKa) of 10.0 to 13.2 is preferable.
Such a weak acid is selected from those described in IONATION CONSTANTS OF ORGANIC ACIDS IN AQUEOUS SOLUTION published by Pergamon Press, for example, 2,2,3,3-tetrafluoropropanol-1 (PKa12.74) , Alcohols such as trifluoroethanol (12.37) and trichloroethanol (12.24), aldehydes such as pyridine-2-aldehyde (12.68) and pyridine-4-aldehyde (12.05) , Salicylic acid (13.0), 3-hydroxy-2-naphthoic acid (12.84), catechol (12.6), gallic acid (12.4), sulfosalicylic acid (11.7) 3,4-dihydroxysulfonic acid (12) 2), 3,4-dihydroxybenzoic acid (11.94), 1,2,4-trihydroxybenzene (11.82), hydroquinone (11.56), pyrogallol (11.34), o -Compounds having phenolic hydroxyl groups such as cresol (10.33), resorcinol (11.27), p-cresol (10.27), m-cresol (10.09), 2-butanone oxime ( 12.45), acetoxime (12.42), 1,2-cycloheptanedione dioxime (12.3), 2-hydroxybenzaldehyde oxime (12.10), dimethylglyoxime (11.9) ), Ethanediamide dioxime (11.37), oximes such as acetophenone oxime (11.35), adenosine (12.5 6) Nucleic acid-related substances such as inosine (12.5), guanine (12.3), cytosine (12.2), hypoxanthine (12.1), xanthine (11.9), etc. Diethylaminomethylphosphonic acid (12.32), 1-amino-3,3,3-trifluorobenzoic acid (12.29), isopropylidenediphosphonic acid (12.10), 1,1-ethylidene Diphosphonic acid (11.54), 1,1-ethylidene diphosphonic acid 1-hydroxy (11.52), benzimidazole (12.86), thiobenzamide (12.8), picoline thioamide (same as above) Weak acids such as 12.55) and barbituric acid (12.5).

  Of these weak acids, sulfosalicylic acid and salicylic acid are preferred. As the base to be combined with these weak acids, sodium hydroxide, ammonium, potassium and lithium are preferably used. These alkali agents are used alone or in combination of two or more. The above various alkali agents are used by adjusting the pH within a preferable range by the concentration and combination.

  Various surfactants and organic solvents can be added to the developer as necessary for the purpose of promoting developability, dispersing development residue, and improving the ink affinity of the printing plate image area. Preferred surfactants include anionic, cationic, nonionic and amphoteric surfactants.

  Preferred examples of the surfactant include polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, glycerin fatty acid partial esters, sorbitan Fatty acid partial esters, pentaerythritol fatty acid partial esters, propylene glycol mono fatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, poly Glycerin fatty acid partial esters, polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acids Nonionic surfactants such as ethanolamides, N, N-bis-2-hydroxyalkylamines, polyoxyethylene alkylamines, triethanolamine fatty acid esters, trialkylamine oxides, fatty acid salts, abietic acid salts, hydroxy Alkane sulfonates, alkane sulfonates, dialkyl sulfosuccinate esters, linear alkyl benzene sulfonates, branched alkyl benzene sulfonates, alkyl naphthalene sulfonates, alkylphenoxy polyoxyethylene propyl sulfonates, polyoxyethylene Alkylsulfophenyl ether salts, N-methyl-N-oleyl taurine sodium salt, N-alkylsulfosuccinic acid monoamide disodium salt, petroleum sulfonates, sulfated tallow oil Fatty acid alkyl ester sulfate ester salt, alkyl sulfate ester salt, polyoxyethylene alkyl ether sulfate ester salt, fatty acid monoglyceride sulfate ester salt, polyoxyethylene alkylphenyl ether sulfate ester salt, polyoxyethylene styryl phenyl ether sulfate ester salt, alkyl phosphorus Acid ester salts, polyoxyethylene alkyl ether phosphoric acid ester salts, polyoxyethylene alkyl phenyl ether phosphoric acid ester salts, partially saponified products of styrene / leic anhydride copolymer, partial saponification of olefin / maleic anhydride copolymer Products, anionic surfactants such as naphthalenesulfonate formalin condensates, alkylamine salts, quaternary ammonium salts such as tetrabutylammonium bromide, Examples thereof include cationic surfactants such as reoxyethylene alkylamine salts and polyethylene polyamine derivatives, and amphoteric surfactants such as carboxybetaines, aminocarboxylic acids, sulfobetaines, aminosulfuric esters, and imidazolines. Among the surfactants listed above, those having polyoxyethylene can be read as polyoxyalkylenes such as polyoxymethylene, polyoxypropylene and polyoxybutylene, and these surfactants are also included.

  A more preferred surfactant is a fluorosurfactant containing a perfluoroalkyl group in the molecule. Such fluorosurfactants include perfluoroalkyl carboxylates, perfluoroalkyl sulfonates, anionic types such as perfluoroalkyl phosphates, amphoteric types such as perfluoroalkyl betaines, and perfluoroalkyltrimethylammonium salts. Cationic and perfluoroalkyl amine oxides, perfluoroalkyl ethylene oxide adducts, perfluoroalkyl group and hydrophilic group-containing oligomers, perfluoroalkyl group and lipophilic group-containing oligomers, perfluoroalkyl groups, hydrophilic groups and lipophilic groups Nonionic types such as group-containing oligomers, perfluoroalkyl groups, and lipophilic group-containing urethanes can be mentioned. Said surfactant can be used individually or in combination of 2 or more types, and is added in 0.001-10 mass% in a developing solution, More preferably, it is added in 0.01-5 mass%.

  Various development stabilizers can be used in the developer. Preferred examples thereof include polyethylene glycol adducts of sugar alcohols described in JP-A-6-282079, tetraalkylammonium salts such as tetrabutylammonium hydroxide, phosphonium salts such as tetrabutylphosphonium bromide, and iodonium such as diphenyliodonium chloride. A salt is a preferred example. Furthermore, anionic surfactants or amphoteric surfactants described in JP-A-50-51324, water-soluble cationic polymers described in JP-A-55-95946, and JP-A-56-142528 are described. And water-soluble amphoteric polymer electrolytes that have been used.

  Furthermore, an organic boron compound to which an alkylene glycol is added as described in JP-A-59-84241, a polyoxyethylene / polyoxypropylene block polymerization type water-soluble surfactant as described in JP-A-60-111246, An alkylenediamine compound substituted with polyoxyethylene / polyoxypropylene disclosed in JP-A-60-129750, a polyethylene glycol having a weight average molecular weight of 300 or more described in JP-A-61-215554, and a cation described in JP-A-63-175858 And a fluorine-containing surfactant having a functional group, a water-soluble ethylene oxide addition compound obtained by adding 4 mol or more of ethylene oxide to an acid or alcohol disclosed in JP-A-2-39157, and a water-soluble polyalkylene compound.

If necessary, an organic solvent is further added to the developer. As such an organic solvent, those having a solubility in water of about 10% by mass or less are suitable, and are preferably selected from those having 5% by mass or less. For example, 1-phenylethanol, 2-phenylethanol, 3-phenyl-1-propanol, 4-phenyl-1-butanol, 4-phenyl-2-butanol, 2-phenyl-1-butanol, 2-phenoxyethanol, 2- Benzyloxyethanol, o-methoxybenzyl alcohol, m-methoxybenzyl alcohol, p-methoxybenzyl alcohol, benzyl alcohol, cyclohexanol, 2-methylcyclohexanol, 3-methylcyclohexanol and 4-methylcyclohexanol, N-phenylethanol Examples thereof include amines and N-phenyldiethanolamine.
Content of the organic solvent is 0.1-5 mass% with respect to the total mass of a use liquid. The amount used is closely related to the amount of surfactant used, and it is preferable to increase the amount of surfactant as the amount of organic solvent increases. This is because the amount of the surfactant is small, and if the amount of the organic solvent is large, the organic solvent is not completely dissolved, and therefore it is impossible to expect good developability.

A reducing agent can be further added to the developer. This prevents the printing plate from being stained. Preferable organic reducing agents include phenol compounds such as thiosalicylic acid, hydroquinone, metol, methoxyquinone, resorcin, and 2-methylresorcin, and amine compounds such as phenylenediamine and phenylhydrazine. More preferable inorganic reducing agents include sodium, potassium and ammonium salts of inorganic acids such as sulfurous acid, bisulfite, phosphorous acid, hydrogen phosphite, dihydrogen phosphite, thiosulfuric acid and dithionite. A salt etc. can be mentioned.
Among these reducing agents, sulfites are particularly excellent in the antifouling effect. These reducing agents are preferably contained in the range of 0.05 to 5% by mass with respect to the developing solution at the time of use.

  An organic carboxylic acid can also be added to the developer. Preferred organic carboxylic acids are aliphatic carboxylic acids and aromatic carboxylic acids having 6 to 20 carbon atoms. Specific examples of the aliphatic carboxylic acid include caproic acid, enanthylic acid, caprylic acid, lauric acid, myristic acid, palmitic acid and stearic acid, and particularly preferred are alkanoic acids having 8 to 12 carbon atoms. . Further, it may be an unsaturated fatty acid having a double bond in the carbon chain or a branched carbon chain. The aromatic carboxylic acid is a compound in which a carboxyl group is substituted on a benzene ring, naphthalene ring, anthracene ring or the like, and specifically includes o-chlorobenzoic acid, p-chlorobenzoic acid, o-hydroxybenzoic acid, p- Hydroxybenzoic acid, o-aminobenzoic acid, p-aminobenzoic acid, 2,4-dihydrobenzoic acid, 2,5-dihydroxybenzoic acid, 2,6-dihydroxybenzoic acid, 2,3-dihydroxybenzoic acid, 3, There are 5-dihydroxybenzoic acid, gallic acid, 1-hydroxy-2-naphthoic acid, 3-hydroxy-2-naphthoic acid, 2-hydroxy-1-naphthoic acid, 1-naphthoic acid, 2-naphthoic acid and the like. Naphthoic acid is particularly effective.

  The aliphatic and aromatic carboxylic acids are preferably used as sodium salts, potassium salts or ammonium salts in order to enhance water solubility. The content of the organic carboxylic acid in the developer used in the present invention is not particularly limited, but if it is less than 0.1% by mass, the effect is not sufficient, and if it is 10% by mass or more, the effect cannot be further improved. In addition, dissolution may be hindered when other additives are used in combination. Therefore, the preferable addition amount is 0.1 to 10% by mass, and more preferably 0.5 to 4% by mass with respect to the developing solution at the time of use.

  If necessary, the developer may further contain a preservative, a colorant, a thickener, an antifoaming agent, a hard water softening agent, and the like. Examples of water softeners include polyphosphoric acid and its sodium, potassium and ammonium salts, ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, triethylenetetraminehexaacetic acid, hydroxyethylethylenediaminetriacetic acid, nitrilotriacetic acid, 1,2-diaminocyclohexanetetra Aminopolycarboxylic acids such as acetic acid and 1,3-diamino-2-propanoltetraacetic acid and their sodium, potassium and ammonium salts, aminotri (methylenephosphonic acid), ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylene Phosphonic acid), triethylenetetramine hexa (methylenephosphonic acid), hydroxyethylethylenediaminetri (methylenephosphonic acid) and 1-hydro The lower edge 1,1-diphosphonic acid and their sodium salts, potassium salts and ammonium salts.

  The optimum value of such a hard water softener varies depending on its chelation and the hardness of the hard water used and the amount of hard water. %, More preferably in the range of 0.01 to 0.5 mass%. If the addition amount is less than this range, the intended purpose is not sufficiently achieved. If the addition amount is more than this range, adverse effects on the image area such as color loss will occur. The remaining component of the developer is water. It is advantageous in terms of transportation that the developer is a concentrated solution having a water content less than that in use and is diluted with water when in use. In this case, the degree of concentration is appropriate such that each component does not cause separation or precipitation.

The developer described in JP-A-6-282079 can also be used as the developer used in the present invention. This is because 5 mol or more of ethylene oxide is added to an alkali metal silicate having a molar ratio of SiO ₂ / M ₂ O (M represents an alkali metal) of 0.5 to 2.0 and a sugar alcohol having 4 or more hydroxyl groups. A developer containing a water-soluble ethylene oxide addition compound obtained in this manner. Sugar alcohols are polyhydric alcohols corresponding to those obtained by reducing aldehyde groups and ketone groups of sugars to form primary and secondary alcohol groups, respectively. Examples of sugar alcohol shells include D, L-trait, erythritol, D, L-arabit, rebit, xylit, D, L-sorbit, D, L-mannit, D, L-exit, D, L-talit, dulcite, allozulcit, and the like, and di-, tri-, tetra-, penta-, and hexaglycerin condensed with a sugar alcohol are also included. The water-soluble ethylene oxide addition compound can be obtained by adding 5 mol or more of ethylene oxide to 1 mol of the sugar alcohol. Further, propylene oxide may be block-copolymerized to the ethylene oxide addition compound as required within a range where solubility is acceptable. These ethylene oxide addition compounds may be used alone or in combination of two or more.
0.001-5 mass% is suitable for the addition amount of these water-soluble ethylene oxide addition compounds with respect to a developing solution (use liquid), More preferably, it is 0.001-2 mass%.

  The developer may further contain the above-described various surfactants and organic solvents as needed for the purpose of promoting developability, dispersing development residue, and improving ink affinity of the printing plate image area.

  A lithographic printing plate precursor developed with a developer having such a composition is subjected to post-treatment with a washing water, a rinse solution containing a surfactant, a finisher mainly composed of gum arabic or starch derivatives, or a protective gum solution. The These treatments can be used in various combinations for the post-treatment of the lithographic printing plate precursor according to the invention.

  In recent years, automatic developing machines for PS plates have been widely used in the stencil and printing industries in order to rationalize and standardize plate making operations. This automatic developing machine is generally composed of a developing unit and a post-processing unit, and includes an apparatus for conveying the PS plate, each processing liquid tank and a spray device, and the exposed PS plate is pumped up while being transported horizontally. Each processing solution is sprayed from a spray nozzle to develop and post-process. In addition, recently, a PS plate is immersed and transported in a processing solution tank filled with a processing solution by a guide roll in the solution, and a small amount of washing water after development is supplied to the plate surface for washing. A method is also known in which the waste water is reused as dilution water for the developer stock solution.

  In such automatic processing, each processing solution can be processed while being replenished with each replenisher according to the processing amount, operating time, and the like. In addition, a so-called disposable processing method in which processing is performed with a substantially unused processing solution can also be applied.

  In the lithographic printing plate precursor according to the invention, image portions unnecessary for the lithographic printing plate obtained by image exposure, development, washing and / or rinsing and / or gumming (for example, film edge marks of the original film, etc.) ), Unnecessary image portions are erased. Such erasing is preferably performed by applying an erasing solution as described in, for example, Japanese Patent Publication No. 2-13293 to an unnecessary image portion, leaving it for a predetermined time, and then washing with water. As described in JP-A-59-174842, a method of developing after irradiating an unnecessary image portion with an actinic ray guided by an optical fiber can also be used.

The lithographic printing plate obtained from the lithographic printing plate precursor of the present invention as described above can be subjected to a printing process after applying a desensitizing gum if desired, but lithographic printing with a higher printing durability. If you want to make a plate, you will be burned. In the case of burning a lithographic printing plate, before burning, an adjustment as described in JP-B-61-2518, JP-A-55-28062, JP-A-62-31859, JP-A-61-159655 is used. It is preferable to treat with a surface liquid.
As its method, with a sponge or absorbent cotton soaked with the surface-adjusting liquid, it is applied onto a lithographic printing plate, or a method in which the printing plate is immersed and applied in a vat filled with the surface-adjusting liquid, Application by an automatic coater is applied. Further, it is more preferable to make the coating amount uniform with a squeegee or a squeegee roller after coating.

In general, the amount of surface-adjusting solution applied is suitably 0.03 to 0.8 g / m ² (dry mass). The lithographic printing plate coated with the surface-adjusting liquid is dried if necessary, and then heated to a high temperature with a burning processor (for example, burning processor “BP-1300” sold by Fuji Photo Film Co., Ltd.). Is done. In this case, the heating temperature and time are in the range of 180 to 300 ° C. and preferably in the range of 1 to 20 minutes, although depending on the type of components forming the image.

  The lithographic printing plate that has been burned can be subjected to conventional treatments such as washing and gumming as needed, but a surface-conditioning solution containing a water-soluble polymer compound is used. In such a case, a so-called desensitizing treatment such as gumming can be omitted. The lithographic printing plate obtained by such processing is applied to an offset printing machine or the like and used for printing a large number of sheets.

  EXAMPLES Hereinafter, although this invention is demonstrated according to an Example, the scope of the present invention is not limited to these Examples.

[Examples 1 to 4]
[Production of support]
<Aluminum plate>
Si: 0.06 mass%, Fe: 0.30 mass%, Cu: 0.025 mass%, Mn: 0.001 mass%, Mg: 0.001 mass%, Zn: 0.001 mass%, Ti: It contains 0.03% by mass, and the balance is prepared by using an aluminum alloy of Al and inevitable impurities. After the molten metal treatment and filtration, an ingot having a thickness of 500 mm and a width of 1200 mm is obtained by a DC casting method. Produced. After the surface was shaved with a chamfering machine with an average thickness of 10 mm, it was kept soaked at 550 ° C. for about 5 hours, and when the temperature dropped to 400 ° C., rolling with a thickness of 2.7 mm using a hot rolling mill A board was used. Furthermore, after performing heat processing using a continuous annealing machine at 500 degreeC, it finished by cold rolling to 0.24 mm in thickness, and obtained the aluminum plate of JIS1050 material. The obtained aluminum had an average crystal grain size with a minor axis of 50 μm and a major axis of 300 μm. After making this aluminum plate width 1030mm, it used for the surface treatment shown below.

<Surface treatment>
In the surface treatment, the following various treatments (a) to (k) were continuously performed. In addition, after each process and water washing, the liquid was drained with the nip roller.
(A) Mechanical surface roughening treatment While supplying a suspension of a polishing agent (pumice) having a specific gravity of 1.12 and water as a polishing slurry liquid to the surface of the aluminum plate, mechanical roughening is performed by a rotating nylon brush. Surface treatment was performed. The average particle size of the abrasive was 30 μm, and the maximum particle size was 100 μm. The material of the nylon brush was 6 · 10 nylon, the hair length was 45 mm, and the hair diameter was 0.3 mm. The nylon brush was planted so as to be dense by making a hole in a stainless steel tube having a diameter of 300 mm. Three rotating brushes were used. The distance between the two support rollers (φ200 mm) at the bottom of the brush was 300 mm. The brush roller was pressed until the load of the drive motor for rotating the brush became 7 kW plus with respect to the load before the brush roller was pressed against the aluminum plate. The rotating direction of the brush was the same as the moving direction of the aluminum plate. The rotation speed of the brush was 200 rpm.

(B) Alkali etching treatment The aluminum plate obtained above was subjected to an etching treatment by spraying using an aqueous solution having a caustic soda concentration of 2.6% by mass, an aluminum ion concentration of 6.5% by mass and a temperature of 70 ° C. / M ² dissolved. Then, water washing by spraying was performed.

(C) Desmutting treatment The desmutting treatment was performed by spraying with a 1% by mass aqueous solution of nitric acid at a temperature of 30 ° C. (containing 0.5% by mass of aluminum ions), and then washed with water by spraying. The nitric acid aqueous solution used for the desmut treatment was a waste liquid from a process of performing an electrochemical surface roughening treatment using alternating current in a nitric acid aqueous solution.

(D) Electrochemical roughening treatment An electrochemical roughening treatment was carried out continuously using an alternating voltage of 60 Hz. The electrolytic solution at this time was a 10.5 g / L aqueous solution of nitric acid (containing 5 g / L of aluminum ions and 0.007% by mass of ammonium ions) at a liquid temperature of 50 ° C. AC power supply waveform is 0.8 msec until the current value reaches the peak from zero, duty ratio is 1: 1, and trapezoidal rectangular wave alternating current is used to perform electrochemical surface roughening treatment with the carbon electrode as the counter electrode. went. Ferrite was used for the auxiliary anode.
The current density was 30 A / dm ² at the peak current value, and the amount of electricity was 220 C / dm ² in terms of the total amount of electricity when the aluminum plate was the anode. 5% of the current flowing from the power source was shunted to the auxiliary anode. Then, water washing by spraying was performed.

(E) Alkaline etching treatment The aluminum plate was subjected to etching treatment at 32 ° C. using an aqueous solution having a caustic soda concentration of 26% by mass and an aluminum ion concentration of 6.5% by mass to dissolve the aluminum plate by 0.50 g / m ² . Removes the smut component mainly composed of aluminum hydroxide that was generated when electrochemical roughening treatment was performed using the alternating current of the previous stage, and also melted the edge part of the generated pit to smooth the edge part. did. Then, water washing by spraying was performed.

(F) Desmut treatment Desmut treatment was performed by spraying with a 15% by weight aqueous solution of nitric acid at a temperature of 30 ° C. (containing 4.5% by weight of aluminum ions), and then washed with water by spraying. The nitric acid aqueous solution used in the desmut was the waste liquid from the step of electrochemical surface roughening using alternating current in the nitric acid aqueous solution.

(G) Electrochemical roughening treatment An electrochemical roughening treatment was performed continuously using an alternating voltage of 60 Hz. The electrolytic solution at this time was a hydrochloric acid 5.0 g / L aqueous solution (containing 5 g / L of aluminum ions) at a temperature of 35 ° C. The AC power supply waveform is subjected to electrochemical surface roughening using a carbon electrode as a counter electrode, using a trapezoidal trapezoidal wave alternating current with a time until the current value reaches a peak from zero for 0.8 msec, a duty ratio of 1: 1. went. Ferrite was used for the auxiliary anode.
The current density was 25 A / dm ² at the peak current value, and the amount of electricity was 50 C / dm ² in terms of the total amount of electricity when the aluminum plate was the anode. Then, water washing by spraying was performed.

(H) Alkaline etching treatment An aluminum plate was subjected to an etching treatment at 32 ° C. using an aqueous solution having a caustic soda concentration of 26 mass% and an aluminum ion concentration of 6.5 mass%, and the aluminum plate was dissolved at 0.10 g / m ² . Removes the smut component mainly composed of aluminum hydroxide generated when electrochemical surface roughening treatment was performed using alternating current in the previous stage, and also melted the edge part of the generated pit to smooth the edge part. did. Then, water washing by spraying was performed.

(I) Desmutting treatment A desmutting treatment by spraying was performed with a 25% by weight aqueous solution of sulfuric acid at a temperature of 60 ° C. (containing 0.5% by weight of aluminum ions), followed by washing with water by spraying.

(J) Anodizing treatment Anodizing treatment is performed using an anodizing apparatus (first and second electrolysis section length 6 m, first and second feeding section length 3 m, first and second feeding section length 2.4 m each). It was. Sulfuric acid was used as the electrolytic solution supplied to the first and second electrolysis units. All electrolytes had a sulfuric acid concentration of 50 g / L (containing 0.5 mass% of aluminum ions) and a temperature of 20 ° C. Then, water washing by spraying was performed. The final oxide film amount was 2.7 g / m ² .

(K) Alkali metal silicate treatment An aluminum support obtained by anodizing treatment was immersed in a treatment tank of a 1% by mass aqueous solution of sodium silicate No. 3 at a temperature of 30 ° C. for 10 seconds. Acid salt treatment (silicate treatment) was performed. Thereafter, washing with water using well water was performed to obtain a support subjected to a surface silicate hydrophilization treatment. On the aluminum support after the alkali metal silicate treatment obtained as described above, an undercoat solution having the following composition was applied and dried at 80 ° C. for 15 seconds to form a coating film. The coating amount of the coating film after drying was 12 mg / m ² .

<Undercoat liquid composition>
・ The following compound 0.3g
・ Methanol 100g
・ Water 1g

[Formation of recording layer (multilayer)]
The lower layer coating solution 1 having the following composition was coated on the obtained undercoated support with a bar coater so that the coating amount after drying was 0.85 g / m ² , and then dried at 160 ° C. for 44 seconds, and immediately after 17 to The support was cooled to 20 ° C. with cold air at 20 ° C.
Thereafter, the coating liquid 1 for the upper layer having the following composition was coated on a bar coater so that the coating amount after drying was 0.25 g / m ² , dried at 148 ° C. for 25 seconds, and further slowly cooled with air at 20 to 26 ° C. Then, lithographic printing plate precursors of Examples 1 to 4 were produced.

<Lower layer coating solution 1>
・ Specific vinyl polymer 2.133g listed in Table 1 below
・ Cyanine dye A (the following structure) 0.134 g
・ 4,4'-bishydroxyphenylsulfone 0.126g
・ Tetrahydrophthalic anhydride 0.190g
・ 0.008 g of p-toluenesulfonic acid
・ 3-Methoxy-4-diazodiphenylamine
Hexafluorophosphate 0.032g
・ The ethyl violet counter ion is changed to 6-hydroxynaphthalenesulfonic acid 0.0781 g
・ Polymer 1 (the following structure) 0.035g
・ Methyl ethyl ketone 25.41g
・ 1-methoxy-2-propanol 12.97g
・ Γ-butyrolactone 13.18g

<Upper layer coating solution 1>
・ M, p-cresol novolak 0.348g
(M / p ratio = 6/4, weight average molecular weight 4700,
Contains 0.8% by mass of unreacted cresol)
-Polymer 3 (the following structure MEK 30% solution) 0.1403g
・ Cyanine dye A (the above structure) 0.0192 g
・ Polymer 1 (the above structure) 0.015 g
-Polymer 2 (the following structure) 0.00328g
1- (4-Methylbenzyl) -1-phenylpiperidinium 5-benzoyl-4-hydroxy
2-methoxybenzenesulfonate 0.004g
・ Surfactant (polyoxyethylene sorbite fatty acid ester HLB8.5, GO-4 manufactured by Nikko Chemicals Co., Ltd.) 0.008 g
・ Methyl ethyl ketone 6.79g
・ 1-methoxy-2-propanol 13.07 g

[Comparative Example 1]
A lithographic printing plate precursor of Comparative Example 1 was prepared in the same manner as in Example 1 except that the lower layer coating solution 1 in Example 1 was changed to a lower layer coating solution 2 having the following composition not containing a specific vinyl polymer.

<Lower layer coating solution 2>
・ Acrylonitrile / Methyl methacrylate /
Methacrylic acid copolymer 2.133 g
(35/45/20: weight average molecular weight 50,000,
Acid value 2.65 meq / g)
・ Cyanine dye A (the above structure) 0.134 g
・ 4,4'-bishydroxyphenylsulfone 0.126g
・ Tetrahydrophthalic anhydride 0.190g
・ 0.008 g of p-toluenesulfonic acid
・ 3-Methoxy-4-diazodiphenylamine
Hexafluorophosphate 0.032g
・ The ethyl violet counter ion is changed to 6-hydroxynaphthalenesulfonic acid 0.0781 g
・ Polymer 1 (the above structure) 0.035 g
・ Methyl ethyl ketone 25.41g
・ 1-methoxy-2-propanol 12.97g
・ Γ-butyrolactone 13.18g

[Comparative Example 2]
A lithographic printing plate precursor of Comparative Example 2 was prepared in the same manner as in Example 1 except that the lower layer coating solution 1 in Example 1 was changed to the lower layer coating solution 3 having the following composition not containing a specific vinyl polymer.

<Lower layer coating solution 3>
・ The following resin (PC) 2.133 g
・ Cyanine dye A (the above structure) 0.124 g
・ 4,4'-bishydroxyphenylsulfone 0.126g
・ Tetrahydrophthalic anhydride 0.190g
・ 0.008 g of p-toluenesulfonic acid
・ 3-Methoxy-4-diazodiphenylamine
Hexafluorophosphate 0.032g
・ The ethyl violet counter ion is changed to 6-hydroxynaphthalenesulfonic acid 0.0781 g
・ Polymer 1 (the above structure) 0.035 g
・ Methyl ethyl ketone 25.41g
・ 1-methoxy-2-propanol 12.97g
・ Γ-butyrolactone 13.18g

[Evaluation of planographic printing plate precursor]
(Evaluation of printing durability)
The test patterns were drawn in the form of images by changing the exposure energy of the lithographic printing plate precursors of Examples 1 to 4 and the lithographic printing plate precursors of Comparative Examples 1 and 2 using a Trendsetter VX manufactured by Creo. Thereafter, development was performed at a developing temperature of 30 ° C. using a PS processor LP940H manufactured by Fuji Photo Film Co., Ltd. charged with a developer DT-2 manufactured by Fuji Photo Film Co., Ltd. (diluted to a conductivity of 43 mS / cm). Development was performed in 12 seconds. This was continuously printed using a printer Lithron manufactured by Komori Corporation. At this time, the number of sheets that can be printed while maintaining a sufficient ink density was measured visually to evaluate the printing durability. The larger the number, the better the printing durability. The results are shown in Table 1 below.

(Evaluation of chemical resistance)
The lithographic printing plate precursors of Examples 1 to 4 and the lithographic printing plate precursors of Comparative Examples 1 and 2 were exposed, developed and printed in the same manner as in the evaluation of printing durability. At this time, every time 5,000 sheets were printed, a process of wiping the plate surface with a cleaner (manufactured by Fuji Photo Film Co., Ltd., multi-cleaner) was added to evaluate chemical resistance. The larger the number, the better the chemical resistance. The results are shown in Table 1 below.

(Evaluation of ink fillability)
In the chemical resistance evaluation, after the plate surface cleaning operation at the time when 50,000 sheets were printed, further wiping was performed, and printing was resumed. From the restart of printing, ink was supplied to the image area, and the ink inking property was evaluated by the number of printed sheets until a stable printed matter was obtained. The results are shown in Table 1 below.

  According to the results of Table 1 above, Examples 1 to 4 of the lithographic printing plate precursor using the specific vinyl polymer (A), which is a characteristic component of the present invention, as the lower layer component use (A) the specific vinyl polymer. It was found that compared to the lithographic printing plate precursors of Comparative Examples 1 and 2 that were not present, the printing durability, chemical resistance, and ink landing property were excellent.

[Examples 5 to 7]
[Production of support]
An aluminum plate (material: JIS A 1050) having a thickness of 0.3 mm is etched for 10 seconds at a caustic soda concentration of 30 g / l, an aluminum ion concentration of 10 g / l, a liquid temperature of 60 ° C., washed with running water, and washed with 10 g / l nitric acid. After neutralizing and washing with water. Using an alternating current of a sine wave under the condition of applied voltage Va = 20 V, an electric current of 500 C / dm ² in an aqueous solution having a hydrogen chloride concentration of 15 g / l, an aluminum ion concentration of 10 g / l, and a liquid temperature of 30 ° C. The surface was subjected to an electrochemical surface roughening treatment in an amount and washed with water, followed by an etching treatment for 10 seconds at a caustic soda concentration of 30 g / l, an aluminum ion concentration of 10 g / l and a liquid temperature of 40 ° C., and then washed with running water. Next, it was desmutted in a sulfuric acid aqueous solution having a sulfuric acid concentration of 15% by mass and a liquid temperature of 30 ° C., and washed with water. Furthermore, in a 10% by mass sulfuric acid aqueous solution at a liquid temperature of 20 ° C., an anodizing treatment was performed under a condition of a current density of 6 A / dm ² by direct current so that the amount of the anodized film was 2.5 g / m ² , and washing with water. , Dried. Then, it processed for 10 second at 30 degreeC with 2.5 mass% sodium silicate aqueous solution, and produced the board | substrate. The centerline average roughness (Ra) of the substrate was measured using a needle having a diameter of 2 μm and found to be 0.48 μm. On the silicate-treated aluminum substrate obtained as described above, an undercoat solution having the following composition was applied and dried at 80 ° C. for 15 seconds to form a coating film. The coating amount of the coating film after drying was 17 mg / m ² .

<Undercoat liquid composition>
・ The following compound 0.3g
・ Methanol 100g
・ Water 1g

[Formation of recording layer (single layer)]
On the support obtained above, the recording layer (single layer) coating liquid 1 having the following composition was applied and dried so that the coating amount after drying was 1.45 g / m ² to form a recording layer. The planographic printing plate precursors of Examples 5 to 7 were obtained.

<Recording layer (single layer) coating solution 1>
・ Novolak resin 0.5g
(M / p-cresol (6/4), weight average molecular weight 7,000,
Unreacted cresol 0.5% by mass)
・ 1.0 g of specific vinyl polymers listed in Table 2
・ Cyanine dye A (the above structure) 0.15 g
・ Phthalic anhydride 0.05g
・ 0.002 g of p-toluenesulfonic acid
・ Ethyl violet counter ion made into 6-hydroxy-β-naphthalenesulfonic acid 0.02 g
・ Fluorine polymer 0.015g
(Megafuck F-176 (solid content 20%),
Dainippon Ink & Chemicals, Inc.)
・ Fluoropolymer 0.035g
(Megafuck MCF-312 (solid content 30%),
Dainippon Ink & Chemicals, Inc.)
・ Lauryl stearate 0.03g
・ Γ-Butyrolactone 8.5g
・ 3.5 g of 1-methoxy-2-propanol

[Comparative Example 3]
[Formation of recording layer]
A recording layer is formed by applying and drying a recording layer (single layer) coating liquid 2 having the following composition on an undercoated support similar to that of Example 5 so that the coating amount after drying is 1.6 g / m ^2. Thus, a planographic printing plate precursor of Comparative Example 3 was obtained.

<Recording layer (single layer) coating solution 2>
・ Novolak resin 0.5g
(M / p-cresol (6/4), weight average molecular weight 7,000,
Unreacted cresol 0.5% by mass)
・ Acrylonitrile / ethyl acrylate /
Methacrylic acid copolymer 1.0 g
(35/55/10: weight average molecular weight 50,000, acid value 2.65 meq / g)
・ Cyanine dye A (the above structure) 0.15 g
・ Phthalic anhydride 0.05g
・ 0.002 g of p-toluenesulfonic acid
-Ethyl violet counter ion converted to 6-hydroxy-β-naphthalenesulfonic acid 0.02 g
・ Fluorine polymer 0.015g
(Megafuck F-176 (solid content 20%),
Dainippon Ink & Chemicals, Inc.)
・ Fluoropolymer 0.035g
(Megafuck MCF-312 (solid content 30%),
Dainippon Ink & Chemicals, Inc.)
・ Lauryl stearate 0.03g
・ Γ-Butyrolactone 8.5g
・ 3.5 g of 1-methoxy-2-propanol

[Evaluation of lithographic printing plate precursor (printing durability, chemical resistance, ink deposition)]
The lithographic printing plate precursors of Examples 5 to 7 and Comparative Example 3 were exposed, developed and printed in the same manner as in Example 1. Furthermore, printing durability, chemical resistance, and ink landing property were evaluated in the same manner. The results are shown in Table 2 below.

  According to the results in Table 2 above, Examples 5 to 7 of the lithographic printing plate precursor using the specific vinyl polymer (A), which is a characteristic component of the present invention, as the lower layer component use (A) the specific vinyl polymer. It was found that compared with the lithographic printing plate precursor of Comparative Example 3 that was not present, the printing durability, chemical resistance, and ink landing property were excellent.

Example 8
In the production of the support of Example 1, the same undercoating and recording layer (lower layer / upper layer) as those of Example 1 were provided except that the silicate treatment was not performed after the anodic oxidation treatment. A printing plate precursor was prepared.

(Evaluation of printing durability and chemical resistance)
The resulting lithographic printing plate precursor of Example 8 was exposed in the same manner as in Example 1, and the development temperature was 28 ° C. using a PS processor LP940H manufactured by Fuji Photo Film Co., Ltd., charged with the following alkaline developer A. Development was carried out at a development time of 30 seconds. Thereafter, printing durability and chemical resistance were evaluated in the same manner as in Example 1.

<Alkali developer A composition>
・ SiO ₂ / K ₂ O 4.0 mass%
(K ₂ O / SiO ₂ = 1/1 (molar ratio))
・ Citric acid 0.5% by mass
・ Polyethylene glycol modified sorbitol 1.0% by mass
(Average 30 unit adduct)
・ Water 50.0 mass%

  As a result, the printing durability was 160,000 sheets, and the chemical resistance was 150,000 sheets. The same number of printed sheets as in Example 1 was obtained. Thus, the lithographic printing plate precursor using the substrate not subjected to the hydrophilization treatment with the silicate was treated with the silicate developer as in Example 1 in which the lithographic printing plate precursor using the silicate-treated substrate was developed with a non-silicate developer. In developed Example 8, it was confirmed that excellent printing durability and chemical resistance were obtained.

Claims (1)

On the support, it contains (A) an alkali-soluble vinyl polymer having a ring structure in the main chain and an active imide group, and (B) an infrared absorber, and image formation is possible by infrared irradiation. A lithographic printing plate precursor having a flexible recording layer.