JP2001107544A - 内装材の目地施工方法 - Google Patents

内装材の目地施工方法

Info

Publication number
JP2001107544A
JP2001107544A JP28647899A JP28647899A JP2001107544A JP 2001107544 A JP2001107544 A JP 2001107544A JP 28647899 A JP28647899 A JP 28647899A JP 28647899 A JP28647899 A JP 28647899A JP 2001107544 A JP2001107544 A JP 2001107544A
Authority
JP
Japan
Prior art keywords
joint
resin
constructing
cutting
construction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP28647899A
Other languages
English (en)
Inventor
Hidejiro Tanaka
秀二郎 田中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toli Corp
Original Assignee
Toli Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toli Corp filed Critical Toli Corp
Priority to JP28647899A priority Critical patent/JP2001107544A/ja
Publication of JP2001107544A publication Critical patent/JP2001107544A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【課題】溶接棒よりも接着性と施工仕上がりの優れた目
地の施工方法が求められた。 【解決手段】本発明は、床材の目地施工方法において、
目地にホットメルト樹脂を溶融し盛り上げ充填した後に
冷却し、盛り上げ部分を切除することを特徴とする床材
の目地施工方法、により滑らかな表面と充分な接着性、
良好な作業性の目地の施工方法を得た。

Description

【発明の詳細な説明】
【０００１】
【発明の属する技術分野】本発明は継ぎ目の美しい内装
材の目地施工方法に関する。
【０００２】
【従来の技術】従来から目地施工には溶接棒が使用され
る。このうち、ＰＶＣ溶接棒は、塩ビ製品には良好な接
着力が得られるが、ＰＶＣ以外の材料の床材には接着し
ない。またホットメルト溶接棒では、リノリユームや非
塩ビ製床材には良好に接着するが、冷えると固くなり、
美麗な切削仕上げは困難であった。また溶接棒は熱風溶
接機で施工するが、作業が滞るとＰＶＣ溶接棒の場合は
溶接機内部で黒焦げになり、ホットメルト溶接棒の場合
は溶接機内部で飴状に溶融して詰まり、トラブルの原因
になった。更に目地棒で部分的な補修を行う時も、補修
部分前後の数１０cm分を折角良好な状態の目地部分をわ
ざわざ切除して目地施工しなければならなかった。
【０００３】特公平５−３９２２２号公報には,ホット
メルト樹脂による目地施工の開示はなく、硬化型樹脂を
用いて目地施工を行っている。硬化型樹脂の場合は切断
のタイミングが少し遅れると樹脂が非常に硬くなり、な
お切断のタイミングが遅かった。
【０００４】
【発明が解決しようとする課題】本願発明は、施工後の
目地が美しく、強度も十分で、作業能率もよい床材、壁
材、巾木等の内装材の目地施工方法に関する。
【０００５】
【課題を解決するための手段】本願発明は、内装材の目
地施工方法において、目地に軟化点が７０〜１３０℃の
ホットメルト（以下ＨＭと略す）樹脂を溶融し盛り上げ
充填した後に冷却し、盛り上げ部分を切除することを特
徴とする内装材の目地施工方法、を要旨とする。
【０００６】本願発明に使用する樹脂はＨＭ樹脂が好適
で、加熱により容易に溶融され、目地に充填される。Ｈ
Ｍ樹脂としては軟化点が７０〜１３０℃、または１８０
℃での溶融粘度が５０００〜２００００ｃｐｓが望まし
い。このようなＨＭ樹脂としては、エチレン−酢酸ビニ
ルコポリマー（ＥＶＡ）、ポリエチレン、ポリプロピレ
ン、ポリエステル、ポリアミド、熱可塑性エラストマー
等の床材との親和性のある樹脂が好適である。このよう
な条件に合った樹脂は、ＨＭガンから円滑に押し出さ
れ、切断作業が容易となる。なお上記ＨＭ樹脂には例え
ば、ポリウレタン樹脂、アクリル系樹脂を若干添加して
変性させてもよい。上記ＨＭ樹脂には、顔料または１０
％以下の炭酸カルシウム、タルク、酸化チタン等の無機
充填剤が含有されてもよい。
【０００７】「図１」は一部切り欠いた施工状態の図で
あり、１は床材、２は目地である。床材としては、リノ
リユーム、ＰＶＣ、ＥＶＡ、その他のポリオレフィン系
合成樹脂床材が利用される。特にリノリユーム床材の目
地施工において、本願発明は有効である。
【０００８】直径５〜３０ｍｍ、長さ５〜４０ｃｍの棒
状のＨＭ樹脂３を導入口に入れ、ヒーター等の加熱手段
４により加熱溶融された状態で、ガン引き金を引くこと
により前進し、溶融状態でガン先端５から押し出され
６、床材間の目地内部７に充填されるとともに目地の上
に盛り上げ状８に形成される。この盛り上げ部８が冷却
されると、ナイフ９で切り取る。 なおＨＭ樹脂として
ペレット状でも良い。
【０００９】「図２」は盛り上げ部分の切断図である。
ＨＭに顔料を添加することにより、透明性を押さえて、
違和感をなくし、また少量の充填剤を添加することによ
り、ナイフ９とＨＭ樹脂１０のへばり付きをなくし、切
削性を向上させた。このように接着強度が強く、切削面
も平滑なＨＭ樹脂目地１１ができる。
【００１０】目地２及び床材シート端部１、１’の表面
が平滑なＨＭ樹脂で覆われる。このときのショアーＤ硬
度が３０〜７０であり、この硬度では、カッター、ナイ
フ、包丁等の通常の施工道具で容易に切断できる。一度
目地部分を切除して樹脂目地１１を形成した後、さらに
精細な削除即ち仕上げカットを行ってもよい。
【００１１】ＨＭ樹脂を床材継ぎ目に溶融充填すること
により、目地部分がしっかり接着し、かつ盛り上がり部
分をスムーズに切削する事ができ、能率的で、しかも美
しい仕上がりができた。
【００１２】
【実施例】
【実施例１】厚さ２．０ｍｍＰＶＣシート床材の０．１
０ｍｍの目地部分に、軟化点８５℃ 、１８０℃の粘度
７８００ｃｐｓのＥＶＡに顔料、５部の炭酸カルシウム
充填材を配合したＨＭ棒をＨＭガンで に溶融押し出し
し、上記目地に盛り上げ充填した。冷却後、盛り上げ充
填部はカッターで容易に切削できた。目地部分は滑らか
で、ガラス光沢のテカリもなく綺麗に仕上がった。目地
にＨＭ樹脂は充分含浸し、目地は床材の使用に充分耐え
るものであった。
【００１３】
【実施例２】実施例１と同じ厚さのリノリユーム床材の
目地に、実施例１と同じＨＭ樹脂をＨＭガンで充填して
目地施工を行った。従来のリノリユーム施工と比べ、一
段と仕上げが美しかった。
【００１４】
【発明の効果】目地部分の切断面が滑らかである。目地
内にＨＭ樹脂が充填され、充分な接着力が得られる。リ
ノリユームの目地施工が円滑かつ美麗にできた。盛り上
がったＨＭ樹脂は容易に切削でき施工能率が高い。少量
の充填材を添加することにより、切削性がよい。目地部
の部分補修も簡単に出来た。
【図面の簡単な説明】
【図１】 本発明施工状態例を示す断面図である。
【図２】施工された目地部分を示す断面図である。
【符号の説明】
１ 床材 ２ 目地 ３、６、１０ ＨＭ樹脂 ９ ナイフ

Claims (4)

    【特許請求の範囲】
  1. 【請求項１】床材の目地施工方法において、目地にホッ
    トメルト樹脂を溶融し盛り上げ充填した後に冷却し、盛
    り上げ部分を切除することを特徴とする床材の目地施工
    方法。
  2. 【請求項２】樹脂の軟化点が７０〜１３０℃である請求
    項１の施工方法。
  3. 【請求項３】樹脂の溶融粘度が１８０℃で５０００〜２
    ００００ｃｐｓである請求項１〜２の施工方法。
  4. 【請求項４】ホットメルト樹脂が、エチレン−酢酸ビニ
    ルコポリマー、ポリエチレン、ポリプロピレンのうちの
    １種である請求項１〜３の施工方法。
JP28647899A 1999-10-07 1999-10-07 内装材の目地施工方法 Pending JP2001107544A (ja)