JP2000007050A - Multi-room container - Google Patents
Multi-room containerInfo
- Publication number
- JP2000007050A JP2000007050A JP10168595A JP16859598A JP2000007050A JP 2000007050 A JP2000007050 A JP 2000007050A JP 10168595 A JP10168595 A JP 10168595A JP 16859598 A JP16859598 A JP 16859598A JP 2000007050 A JP2000007050 A JP 2000007050A
- Authority
- JP
- Japan
- Prior art keywords
- weak seal
- seal portion
- peel strength
- width
- chamber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、輸液等の収容に用
いられる、複数の収容室を有する容器に関し、より詳し
くは、収容室間の隔壁が誤って破損し、各室内の収容物
が混合してしまうのを防止した複室容器に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a container having a plurality of storage chambers used for storing an infusion solution or the like, and more particularly, a partition wall between storage chambers is erroneously damaged, and contents in each chamber are mixed. The present invention relates to a double-chambered container that prevents the occurrence of such a case.
【０００２】[0002]
【従来の技術】近年、例えばアミノ酸を含む輸液とブド
ウ等を含む輸液や、抗生物質とその溶解液等の、混合状
態で保管すると変質するおそれのある薬剤の組合せを１
つの容器内で分離収容することを目的として、図５に示
すような、容易に剥離し得る弱シール部（隔壁）６で区
画された複数の収容室を有するいわゆる複室容器５が広
く用いられつつある。2. Description of the Related Art In recent years, a combination of an infusion solution containing an amino acid and an infusion solution containing grape, an antibiotic and a solution thereof, which may deteriorate when stored in a mixed state, has been developed.
As shown in FIG. 5, a so-called multi-chamber container 5 having a plurality of storage chambers partitioned by a weak seal portion (partition wall) 6 that can be easily peeled is widely used for the purpose of separately housing in one container. It is getting.
【０００３】この複室容器５を用いれば、使用時にいず
れかの収容室３を押圧して弱シール部６を剥離させるこ
とによって各室に収容された薬剤等の収容物を混合させ
ることができ、異種の薬剤を別々の容器に収納する煩わ
しさを解消できる。[0003] If this multi-chamber container 5 is used, one of the storage chambers 3 is pressed at the time of use, and the weak seal portion 6 is peeled off, whereby the contents such as medicines stored in each chamber can be mixed. In addition, the inconvenience of storing different types of drugs in separate containers can be eliminated.
【０００４】弱シール部６は、周縁部４よりも弱く熱融
着することにより形成されるものであって、収容室３を
所定の力以上で押圧すれば剥離するように設計されてお
り、一方で使用時以外には容易に剥離しないように設計
されている必要がある。そこで従来、弱シール部６は、
所定の押圧を加えると始めて剥離し得るような素材を選
択して使用したり、融着条件をコントロールして剥離強
度を適宜調整して形成されていた。さらに従来の複室容
器５は、弱シール部６が使用時以外に誤って剥離するの
を防止するため、当該弱シール部６で容器を２つ折りに
し、その状態で外装袋に収容した製品形態が採られてい
る。[0004] The weak seal portion 6 is formed by heat-sealing weaker than the peripheral edge portion 4 and is designed to be peeled off when the housing chamber 3 is pressed with a predetermined force or more. On the other hand, it must be designed so that it does not easily peel off except during use. Therefore, conventionally, the weak seal portion 6 has
A material which can be peeled off only when a predetermined pressure is applied is selected and used, or the peeling strength is appropriately adjusted by controlling the fusion conditions. Further, in order to prevent the weak seal portion 6 from being accidentally peeled off except during use, the conventional double-chamber container 5 is formed by folding the container in two at the weak seal portion 6 and storing it in an outer bag in that state. Is adopted.
【０００５】ところが、実際の医療現場等では、複室容
器５を外装袋から取り出して、広げた状態で放置または
運搬することがしばしば行われる。その際、複室容器５
を誤って落下してしまうことがあり、左右側周縁部４０
が下になって落下した場合には、収容室３に押圧をかけ
なくても弱シール部６が剥離してしまう問題が生じる。[0005] However, in an actual medical field, it is often performed to take out the multi-chamber container 5 from the outer bag, leave it in an expanded state, or carry it. At that time, the multi-chamber container
May be accidentally dropped, and the left and right peripheral portions 40
If the storage unit 3 falls down, there is a problem that the weak seal portion 6 peels off without applying pressure to the storage chamber 3.
【０００６】[0006]
【発明が解決しようとする課題】実開平３−８５０３８
号公報には、収容室を区画するのに２つの弱シール部を
用いるとともに、弱シール部と交差する方向に強固な接
着部を設けて弱シール部を補強することにより、弱シー
ル部が誤って剥離してしまうのを防止した輸液バックが
開示されている。しかし、この公報においては、輸液バ
ッグの左右の周縁部が下になって落下したときに弱シー
ル部が剥離してしまうことについては何ら考慮されてい
ない。また、使用時に収容室を押圧して弱シール部を剥
離させても、前述の強固な接着部が収容室間の通路を狭
めてしまい、各室の収容物を混合しにくくなる問題もあ
る。[Problems to be Solved by the Invention]
In the publication, two weak seal portions are used to divide the accommodation room, and a strong adhesive portion is provided in a direction crossing the weak seal portion to reinforce the weak seal portion. There is disclosed an infusion bag which prevents peeling off. However, in this publication, no consideration is given to peeling of the weak seal portion when the left and right peripheral edges of the infusion bag fall down and fall. Further, even if the weak seal portion is peeled by pressing the storage chamber during use, the strong adhesive portion narrows the passage between the storage chambers, and there is also a problem that it becomes difficult to mix the stored materials in each chamber.
【０００７】特開平７−２９９１１７号公報には、収容
室を押圧しても弱シール部のうち左右の周縁部に近い両
端部分が充分に剥離せず、その結果各室の収容物の混合
が順調に進まなくなるという問題を防ぐことを目的とし
て、弱シール部の剥離強度をその中央部から両側部に向
って連続的に低下するように設計した輸液バッグが開示
されている。しかし、この公報に開示の輸液バッグで
は、左右の周縁部が下になって落下した場合に弱シール
部がより一層剥離しやすくなる。[0007] Japanese Patent Application Laid-Open No. 7-299117 discloses that even when the storage chamber is pressed, both ends of the weak seal portion near the left and right peripheral portions are not sufficiently peeled off. For the purpose of preventing the problem of not proceeding smoothly, there has been disclosed an infusion bag designed so that the peel strength of the weak seal portion is continuously reduced from the center toward both sides. However, in the infusion bag disclosed in this publication, the weak seal portion is more easily peeled off when the left and right peripheral portions fall down.
【０００８】複室容器の研究開発の進歩により、収容室
への弱い押圧によって、あるいは通常の取扱いによって
弱シール部が誤って剥離するという問題に対しては十分
に検討がなされている。しかしながら、前述のように容
器の左右の周縁部が下になって落下するという不慮の事
故に対しては、未だに何らの対策も施されていないのが
現状である。[0008] Advances in the research and development of multi-chamber containers have been thoroughly studied for the problem that the weak seal portion is accidentally peeled off by a weak pressure on the storage chamber or by ordinary handling. However, at present, no countermeasures have been taken against an unexpected accident in which the left and right peripheral portions of the container fall down as described above.
【０００９】そこで本発明の目的は、左右の周縁部から
の衝撃によって弱シール部が誤って剥離することのない
複室容器を提供することである。SUMMARY OF THE INVENTION It is an object of the present invention to provide a multi-chamber container in which a weak seal portion is not erroneously peeled off by impact from left and right peripheral portions.
【００１０】[0010]
【課題を解決するための手段】本発明者らは、上記課題
を解決するために鋭意研究を重ねた結果、弱シール部で
区画された複数の収容室を有する可撓性容器であって、
前記弱シール部が中央部とその両側の側部との少なくと
も３つの部分からなり、弱シール部側部の剥離強度が弱
シール部中央部の剥離強度よりも大きいときは、たとえ
容器の左右の周縁部が下になって落下しても弱シール部
が誤って剥離することのない複室容器が得られるという
全く新たな事実を見出し、本発明を完成するに至った。Means for Solving the Problems The inventors of the present invention have conducted intensive studies to solve the above-mentioned problems, and as a result, have obtained a flexible container having a plurality of storage chambers partitioned by a weak seal portion,
When the weak seal portion is composed of at least three portions of a central portion and side portions on both sides thereof and the peel strength of the weak seal portion side portion is larger than the peel strength of the weak seal portion central portion, even if the left and right sides of the container The present inventors have found a completely new fact that a multi-chamber container in which the weakly sealed portion does not peel off accidentally even when the peripheral portion falls down can be obtained, and have completed the present invention.
【００１１】すなわち本発明の複室容器によれば、複室
容器を使用する際には、収容室を所定の力以上で押圧す
ることによって弱シール部を容易に剥離させ、各室の収
容物を混合することができ、かつ左右の周縁部を下にし
て落下させるなどして、左右周縁部から衝撃を与えたと
きに弱シール部が誤って剥離することがなく、収容物を
分離して収容する状態を維持することができる。That is, according to the multi-chamber container of the present invention, when using the multi-chamber container, the weak seal portion is easily peeled off by pressing the housing chamber with a predetermined force or more, so that the stored material in each chamber can be removed. Can be mixed, and the left and right peripheral parts can be dropped, so that the weak seal part does not accidentally peel off when an impact is applied from the left and right peripheral parts. The state of accommodation can be maintained.
【００１２】本発明の複室容器において、弱シール部中
央部の横幅が弱シール部全体の１０〜８０％であるとき
は、左右の周縁部からの衝撃によって弱シール部が誤っ
て剥離するのを防止する本発明の効果を維持しつつ、使
用時における収容室の押圧によって弱シール部をよりス
ムーズに剥離させることができる。In the multi-chamber container according to the present invention, when the width of the central portion of the weak seal portion is 10 to 80% of the entire weak seal portion, the weak seal portion is erroneously peeled off by impact from the left and right peripheral edges. The weak seal portion can be more smoothly peeled off by pressing the storage chamber during use, while maintaining the effect of the present invention for preventing the problem.
【００１３】また、本発明の複室容器においては、使用
時に収容室を押圧することによって弱シール部を容易に
剥離させることができるとともに、左右の周縁部からの
衝撃で弱シール部が誤って剥離してしまうのを防止する
という本発明の効果をより一層高めるために、弱シール
部側部の剥離強度を弱シール部中央部の剥離強度の１．
２〜５倍とするのが好ましい。In the multi-chamber container according to the present invention, the weak seal portion can be easily peeled off by pressing the storage chamber at the time of use, and the weak seal portion is erroneously made by impact from the right and left peripheral edges. In order to further enhance the effect of the present invention of preventing the peeling, the peel strength at the side of the weak seal portion is set to 1.
It is preferably 2 to 5 times.
【００１４】さらに、本発明の複室容器において、弱シ
ール部が使用時における収容室の押圧によって容易に剥
離するものの、通常の取扱いで誤って剥離することがな
いようにするには、弱シール部中央部の剥離強度を０．
２〜０．７ｋｇｆ／１５ｍｍとするのが好ましい。ま
た、弱シール部が左右の周縁部からの衝撃によって誤っ
て剥離するのを防止するとともに、使用時における収容
室の押圧によって充分に剥離するようにするには、弱シ
ール部側部の剥離強度を０．５〜１．５ｋｇｆ／１５ｍ
ｍとするのが好ましい。Further, in the multi-chamber container of the present invention, although the weak seal portion is easily peeled off by the pressing of the storage chamber during use, in order to prevent the weak seal portion from being erroneously peeled off in ordinary handling, the weak seal portion is required. The peel strength at the center of the part is 0.
It is preferably set to 2 to 0.7 kgf / 15 mm. Further, in order to prevent the weak seal portion from being accidentally peeled off by the impact from the left and right peripheral portions and to sufficiently peel off by pressing the storage chamber during use, the peel strength of the side portion of the weak seal portion is required. 0.5-1.5kgf / 15m
m is preferable.
【００１５】なお本発明において、弱シール部の「剥離
強度」とは、ＪＩＳ−Ｚ０２３８に規定の「袋のヒート
シール強さ試験」に準拠した測定値である。すなわち、
図４(a) に示すように、複室容器５から弱シール部６を
含む幅１５ｍｍの短冊状の試験片７を切取り、次いで同
図(b) に示すように、試験片７のフィルム８を引張試験
機にて逆方向に引張り、弱シール部６が剥離したときの
引張強度（ｋｇｆ／１５ｍｍ）を定速伸長形引張試験機
等によって測定したものである。In the present invention, the "peel strength" of the weakly sealed portion is a measured value based on the "heat seal strength test of bag" specified in JIS-Z0238. That is,
As shown in FIG. 4 (a), a strip-shaped test piece 7 having a width of 15 mm including the weak seal portion 6 is cut out from the multi-chamber container 5, and then, as shown in FIG. Was pulled in a reverse direction by a tensile tester, and the tensile strength (kgf / 15 mm) when the weak seal portion 6 was peeled off was measured by a constant-speed elongation type tensile tester or the like.
【００１６】[0016]
【発明の実施の形態】以下、本発明の複室容器につい
て、図１〜３を参照しつつ詳細に説明する。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a perspective view of a multi-chamber container according to the present invention.
【００１７】〔第１の実施形態〕本発明の第１の実施形
態としては、例えば図１に示すように、２つの収容室３
ａ，３ｂを有する複室容器１が挙げられる。この複室容
器１において、上部収容室３ａと下部収容室３ｂとは弱
シール部２で区画されており、この弱シール部２は、収
容室３ａ，３ｂのいずれかを所定の力以上で押圧するこ
とにより、収容室内の収容物による圧力（例えば、薬剤
による液圧）で剥離する。[First Embodiment] As a first embodiment of the present invention, for example, as shown in FIG.
a, 3b. In this multi-chamber container 1, the upper storage chamber 3a and the lower storage chamber 3b are partitioned by a weak seal portion 2, and the weak seal portion 2 presses any of the storage chambers 3a, 3b with a predetermined force or more. As a result, the film is peeled off by the pressure (for example, the liquid pressure by the medicine) of the stored material in the storage chamber.
【００１８】第１の実施形態において、弱シール部２は
中央部２ｃとその両側の側部２ａ，２ｂとの３つの部分
からなり、その剥離強度は側部２ａ，２ｂの方が中央部
２ｃよりも大きくなるように設定される。In the first embodiment, the weak seal portion 2 is composed of a central portion 2c and side portions 2a and 2b on both sides thereof, and the peel strength of the side portions 2a and 2b is larger at the central portion 2c. Is set to be larger than
【００１９】弱シール部中央部２ｃの横幅は、弱シール
部全体の横幅Ｌの１０〜８０％に設定される。中央部２
ｃの横幅の割合が全体の横幅Ｌに対して１０％を下回る
と、剥離強度の小さい部分が少なくなりすぎて、収容室
への押圧によって弱シール部を容易に剥離させることが
できなくなるおそれがある。逆に、中央部２ｃの横幅の
割合が全体の横幅Ｌに対して８０％を超えると、弱シー
ル部側部２ａ，２ｂの横幅が減少することから、複室容
器１の左右周縁部４０から衝撃を受けたときに弱シール
部２が誤って剥離するおそれがある。中央部２ｃの横幅
の、全体の横幅Ｌに対する割合は、上記範囲の中でも特
に１０〜５０％であるのが好ましく、３０〜５０％であ
るのがより好ましい。The width of the weak seal central portion 2c is set to 10 to 80% of the width L of the entire weak seal. Central part 2
If the ratio of the width of c is less than 10% of the entire width L, there is a possibility that the portion having a small peel strength becomes too small and the weak seal portion cannot be easily peeled off by pressing against the storage chamber. is there. Conversely, if the ratio of the width of the central portion 2c exceeds 80% with respect to the entire width L, the width of the weak seal portion side portions 2a and 2b decreases. When receiving an impact, the weak seal portion 2 may be peeled off by mistake. The ratio of the width of the central portion 2c to the entire width L is particularly preferably 10 to 50%, and more preferably 30 to 50%, in the above range.
【００２０】弱シール部側部２ａ，２ｂの横幅は、それ
ぞれ弱シール部全体の横幅Ｌの１０〜４５％に設定する
のが好ましい。側部２ａ，２ｂのそれぞれの横幅が全体
の横幅Ｌに対して１０％を下回ると、剥離強度の大きい
側部が少なくなりすぎて、左右周縁部４０から衝撃を受
けたときに弱シール部２が誤って剥離するおそれがあ
る。逆に、側部２ａ，２ｂのそれぞれの横幅が全体の横
幅Ｌに対して４５％を超えると、剥離強度の大きい部分
が多くなりすぎて、収容室への押圧によって弱シール部
を容易に剥離させることができなくなるおそれがある。It is preferable that the width of the weak seal portion side portions 2a and 2b is set to 10 to 45% of the width L of the entire weak seal portion. If the lateral width of each of the side portions 2a and 2b is less than 10% of the entire lateral width L, the side portion having a large peel strength becomes too small, and the weak seal portion 2 is provided when receiving an impact from the left and right peripheral portions 40. May be accidentally peeled off. Conversely, if the lateral width of each of the side portions 2a and 2b exceeds 45% of the entire lateral width L, a portion having a large peel strength becomes too large, and the weak seal portion is easily peeled off by pressing the storage chamber. It may not be possible to do so.
【００２１】弱シール部側部２ａ，２ｂの剥離強度は、
弱シール部中央部２ｃの剥離強度の１．２〜５倍である
のが好ましい。側部２ａ，２ｂの剥離強度が中央部２ｃ
の剥離強度の１．２倍よりも小さいと、左右周縁部４０
から衝撃を受けたときに弱シール部２が誤って剥離する
おそれがある。逆に、側部２ａ，２ｂの剥離強度が中央
部２ｃの剥離強度の５倍よりも大きいと、収容室への押
圧によって弱シール部を容易に剥離させることができな
くなるおそれがある。弱シール部側部２ａ，２ｂと中央
部２ｃとの剥離強度は、その比が上記条件を満たすほか
は特に限定されないが、中央部２ｃの剥離強度が０．２
〜０．７ｋｇｆ／１５ｍｍの範囲となるように、側部２
ａ，２ｂの剥離強度が０．５〜１．５ｋｇｆ／１５ｍｍ
の範囲となるようにそれぞれ設定するのが好ましい。The peel strength of the weak seal side portions 2a and 2b is as follows:
The peel strength of the weak seal central portion 2c is preferably 1.2 to 5 times the peel strength. The peel strength of the side parts 2a, 2b is the central part 2c.
If it is smaller than 1.2 times the peel strength of
There is a possibility that the weak seal portion 2 may be erroneously peeled off when an impact is received from the user. Conversely, if the peel strength of the side portions 2a and 2b is greater than five times the peel strength of the central portion 2c, there is a possibility that the weak seal portion cannot be easily peeled off by pressing against the storage chamber. The peel strength between the weak seal portion side portions 2a and 2b and the central portion 2c is not particularly limited, except that the ratio satisfies the above condition, but the peel strength of the central portion 2c is 0.2.
Side part 2 so as to be in a range of 0.7 kgf / 15 mm.
a, 2b peel strength of 0.5 to 1.5 kgf / 15 mm
It is preferable to set each of them so as to fall within the range.
【００２２】弱シール部中央部２ｃの剥離強度が前記範
囲を下回ると弱シール部２が剥離しやすくなり、通常の
取扱いでも各室の収容物の分離収容を維持できなくなる
おそれがある。逆に、中央部２ｃの剥離強度が前記範囲
を超えると、収容室への押圧によって弱シール部を容易
に剥離させることができなくなるおそれがある。中央部
２ｃの剥離強度は、上記範囲の中でも特に０．２〜０．
５ｋｇｆ／１５ｍｍであるのが好ましく、０．３〜０．
４ｋｇｆ／１５ｍｍであるのがより好ましい。If the peel strength of the weak seal central portion 2c is less than the above range, the weak seal 2 tends to peel, and it may not be possible to maintain the separated contents of each chamber even in normal handling. Conversely, if the peel strength of the central portion 2c exceeds the above range, there is a possibility that the weak seal portion cannot be easily peeled off by pressing against the storage chamber. The peel strength of the central portion 2c is particularly preferably in the range of 0.2 to 0.5.
It is preferably 5 kgf / 15 mm, and 0.3 to 0.1 mm.
More preferably, it is 4 kgf / 15 mm.
【００２３】一方、弱シール部側部２ａ，２ｂの剥離強
度が前記範囲を下回ると、左右周縁部４０から衝撃を受
けたときに弱シール部２が誤って剥離するおそれがあ
る。逆に、側部２ａ，２ｂの剥離強度が前記範囲を超え
ると、収容室への押圧によって弱シール部を容易に剥離
させることができなくなるおそれがある。側部２ａ，２
ｂの剥離強度は、上記範囲の中でも特に０．５〜１．０
ｋｇｆ／１５ｍｍであるのが好ましく、０．６〜０．９
ｋｇｆ／１５ｍｍであるのがより好ましい。On the other hand, if the peel strength of the weak seal portion side portions 2a and 2b is less than the above range, the weak seal portion 2 may be erroneously peeled when receiving an impact from the left and right peripheral portions 40. Conversely, if the peel strength of the side portions 2a, 2b exceeds the above range, there is a possibility that the weak seal portion cannot be easily peeled off by pressing against the storage chamber. Sides 2a, 2
The peel strength of b is particularly 0.5 to 1.0 in the above range.
kgf / 15 mm, preferably 0.6 to 0.9 kgf / 15 mm.
kgf / 15 mm is more preferable.
【００２４】弱シール部２の幅Ｗは、弱シール部２に用
いられる材料や、当該弱シール部２の剥離強度等に応じ
て設定されるものであって特に限定されないが、通常３
〜２０ｍｍの範囲で設定される。The width W of the weak seal portion 2 is set according to the material used for the weak seal portion 2 and the peel strength of the weak seal portion 2 and is not particularly limited.
It is set in the range of ２０20 mm.
【００２５】〔第２の実施形態〕本発明の第２の実施形
態としては、例えば図２に示すように、２つの収容室３
０ａ，３０ｂを有する複室容器１０が挙げられる。この
複室容器１０において、上部収容室３０ａと下部収容室
３０ｂとは弱シール部２０で区画されており、この弱シ
ール部２０は、収容室３０ａ，３０ｂのいずれかを所定
の力以上で押圧することにより、収容室内の収容物によ
る圧力で剥離する。[Second Embodiment] As a second embodiment of the present invention, for example, as shown in FIG.
0a, 30b. In this multi-chamber container 10, the upper storage chamber 30a and the lower storage chamber 30b are partitioned by a weak seal portion 20, and this weak seal portion 20 presses any of the storage chambers 30a, 30b with a predetermined force or more. As a result, the film is peeled off by the pressure of the stored material in the storage chamber.
【００２６】第２の実施形態において、弱シール部２０
は中央部２０ｃと、その両側の側部２０ａ，２０ｂと、
さらにその両側の端部２０ｄ，２０ｅとの５つの部分か
らなり、側部２０ａ，２０ｂの剥離強度が中央部２０ｃ
の剥離強度よりも大きくなるように設定される。In the second embodiment, the weak seal portion 20
Is a central portion 20c and side portions 20a and 20b on both sides thereof,
Furthermore, it is composed of five parts with the ends 20d and 20e on both sides, and the peel strength of the side parts 20a and 20b is increased by the center part 20c
Is set so as to be larger than the peel strength.
【００２７】弱シール部中央部２０ｃの横幅は、弱シー
ル部全体の横幅Ｌの１０〜８０％に設定される。中央部
２０ｃの横幅の割合が上記範囲を外れたときには、第１
の実施形態と同様な問題が生じる。中央部２０ｃの横幅
の、全体の横幅Ｌに対する割合は、上記範囲の中でも特
に１０〜５０％であるのが好ましく、３０〜５０％であ
るのがより好ましい。The width of the weak seal central portion 20c is set to 10 to 80% of the width L of the entire weak seal. When the ratio of the width of the central portion 20c is out of the above range, the first
A problem similar to that of the first embodiment occurs. The ratio of the width of the central portion 20c to the entire width L is particularly preferably 10 to 50%, more preferably 30 to 50% in the above range.
【００２８】弱シール部側部２０ａ，２０ｂの横幅は、
それぞれ弱シール部全体の横幅Ｌの５〜４５％に設定さ
れるのが好ましい。側部２０ａ，２０ｂの横幅の割合が
上記範囲を外れたときには、第１の実施形態と同様な問
題が生じる。The width of the weak seal portion side portions 20a and 20b is as follows.
It is preferable that the width is set to 5 to 45% of the width L of the entire weak seal portion. When the width ratio of the side portions 20a and 20b is out of the above range, the same problem as in the first embodiment occurs.
【００２９】弱シール部端部２０ｄ，２０ｅは、収容室
への押圧によって弱シール部を剥離させる際に、剥離強
度の大きい弱シール部側部が完全に剥離せずにその融着
状態が残存してしまうのを防止するために設けられたも
のであって、当該端部２０ｄ，２０ｅのそれぞれの横幅
は、弱シール部全体の横幅Ｌの５％以下、好ましくは
０．１〜５％に設定される。端部２０ｄ，２０ｅのそれ
ぞれの横幅が全体の横幅Ｌの５％を超えると、左右周縁
部４０から衝撃を受けたときに弱シール部２が誤って剥
離してしまい、本発明の効果が得られなくなる。When the weak seal portion is peeled by pressing against the storage chamber, the weak seal portion ends 20d and 20e do not completely peel off the weak seal portion side having a large peel strength, and the fused state remains. The width of each of the ends 20d and 20e is 5% or less, preferably 0.1 to 5% of the width L of the entire weak seal portion. Is set. If the width of each of the end portions 20d and 20e exceeds 5% of the entire width L, the weak seal portion 2 is erroneously peeled off when receiving an impact from the left and right peripheral portions 40, and the effect of the present invention is obtained. Can not be.
【００３０】弱シール部中央部２０ｃの剥離強度は、第
１の実施形態における弱シール部中央部２ｃの剥離強度
と同じ範囲で設定される。また、弱シール部側部２０
ａ，２０ｂの剥離強度も、第１の実施形態における弱シ
ール部側部２ａ，２ｂの剥離強度と同じ範囲で設定され
る。剥離強度がそれぞれの好適範囲から外れたときの問
題点も、第１の実施形態と同様である。The peel strength of the weak seal central portion 20c is set in the same range as the peel strength of the weak seal central portion 2c in the first embodiment. Also, the weak seal portion side 20
The peel strengths of a and 20b are also set in the same range as the peel strength of the weak seal portion side portions 2a and 2b in the first embodiment. Problems when the peel strength deviates from the respective preferred ranges are also the same as in the first embodiment.
【００３１】弱シール部側部２０ａ，２０ｂの剥離強度
は、弱シール部中央部２０ｃの剥離強度の１．２〜５倍
であるのが好ましい。この範囲を外れたときには、第１
の実施形態と同様な問題が生じる。The peel strength of the weak seal portion side portions 20a and 20b is preferably 1.2 to 5 times the peel strength of the weak seal portion central portion 20c. If outside this range, the first
A problem similar to that of the first embodiment occurs.
【００３２】弱シール部端部２０ｄ，２０ｅの剥離強度
は、中央部２０ｃの剥離強度と同程度に、より詳しくは
０．２〜０．７ｋｇｆ／１５ｍｍに設定される。端部２
０ｄ，２０ｅの剥離強度が前記範囲を下回ると当該端部
２０ｄ，２０ｅが剥離しやすくなる。特に、左右周縁部
４０から衝撃を受けたときに誤って剥離してしまい、本
発明の効果が得られなくなる。逆に、端部２０ｄ，２０
ｅの剥離強度が前記範囲を超えると、弱シール部側部が
完全に剥離せずにその融着状態が残存してしまうのを防
止するという効果が得られない。The peel strength of the weak seal portion ends 20d and 20e is set to be substantially the same as the peel strength of the central portion 20c, more specifically, 0.2 to 0.7 kgf / 15 mm. End 2
If the peel strength of 0d, 20e falls below the above range, the end portions 20d, 20e are easily peeled. In particular, when an impact is applied from the left and right peripheral portions 40, they are erroneously peeled off, and the effect of the present invention cannot be obtained. Conversely, ends 20d, 20
When the peel strength of e exceeds the above range, the effect of preventing the weak seal portion side portion from completely peeling and preventing the fused state from remaining cannot be obtained.
【００３３】弱シール部２０の幅Ｗは、弱シール部２０
に用いられる材料や、当該弱シール部２０の剥離強度等
に応じて設定されるものであって特に限定されないが、
通常３〜２０ｍｍの範囲で設定される。The width W of the weak seal portion 20 is
Is set according to the peel strength of the weak seal portion 20 and the material used for the weak seal portion 20.
Usually, it is set in a range of 3 to 20 mm.
【００３４】〔第３の実施形態〕本発明の第３の実施形
態としては、例えば図３に示すように、２つの収容室３
１ａ，３１ｂを有する複室容器１１が挙げられる。この
複室容器１１において、上部収容室３１ａと下部収容室
３１ｂとは弱シール部２１で区画されており、この弱シ
ール部２１は、収容室３１ａ，３１ｂのいずれかを所定
の力以上で押圧することにより、収容室内の収容物によ
る圧力で剥離する。[Third Embodiment] As a third embodiment of the present invention, for example, as shown in FIG.
The multi-chamber container 11 having 1a and 31b is exemplified. In this multi-chamber container 11, the upper storage chamber 31a and the lower storage chamber 31b are partitioned by a weak seal portion 21, and the weak seal portion 21 presses one of the storage chambers 31a, 31b with a predetermined force or more. As a result, the film is peeled off by the pressure of the stored material in the storage chamber.
【００３５】第３の実施形態において、弱シール部２１
は中央部２１ｃとその両側の側部２１ａ，２１ｂとの３
つの部分からなり、その剥離強度は側部２１ａ，２１ｂ
の方が中央部２１ｃよりも大きくなるように設定され
る。In the third embodiment, the weak seal portion 21
Is the center portion 21c and the side portions 21a and 21b on both sides thereof.
And the peel strength of the side portions 21a, 21b
Is set to be larger than the central portion 21c.
【００３６】また、第３の実施形態においては、左右周
縁部４０から衝撃を受けたときに弱シール部２１が誤っ
て剥離するのを防止するという観点から、弱シール部側
部２１ａ，２１ｂの幅Ｗを弱シール部中央部２１ｃの幅
Ｗよりも１０〜１００％、好ましくは３０〜６０％大き
く設定する。なお、弱シール部２１の幅Ｗは、弱シール
部２１に用いられる材料や、当該弱シール部２１の剥離
強度等に応じて設定されるものであって特に限定されな
いが、通常弱シール部側部２１ａ，２１ｂの幅Ｗが３〜
２０ｍｍの範囲で設定される。Further, in the third embodiment, from the viewpoint of preventing the weak seal portion 21 from being accidentally peeled off when receiving an impact from the left and right peripheral portions 40, the weak seal portion side portions 21a, 21b are formed. The width W is set to be 10 to 100%, preferably 30 to 60% larger than the width W of the weak seal central portion 21c. The width W of the weak seal portion 21 is set according to the material used for the weak seal portion 21 and the peel strength of the weak seal portion 21 and is not particularly limited. The width W of the portions 21a and 21b is 3 to
It is set within a range of 20 mm.
【００３７】弱シール部中央部２１ｃの横幅は弱シール
部全体の横幅Ｌの１０〜８０％に設定される。中央部２
１ｃの横幅の割合が上記範囲を外れたときには、第１の
実施形態と同様な問題が生じる。中央部２１ｃの横幅
の、全体の横幅Ｌに対する割合は、上記範囲の中でも特
に１０〜５０％であるのが好ましく、３０〜５０％であ
るのがより好ましい。The width of the weak seal central portion 21c is set to 10 to 80% of the width L of the entire weak seal. Central part 2
When the width ratio of 1c is out of the above range, the same problem as in the first embodiment occurs. The ratio of the width of the central portion 21c to the entire width L is particularly preferably 10 to 50%, more preferably 30 to 50% in the above range.
【００３８】弱シール部側部２１ａ，２１ｂの横幅はそ
れぞれ全体の横幅Ｌの１０〜４５％に設定するのが好ま
しい。側部２１ａ，２１ｂの横幅の割合が上記範囲を外
れたときには、第１の実施形態と同様な問題が生じる。The width of the weak seal portion side portions 21a and 21b is preferably set to 10 to 45% of the entire width L. When the width ratio of the side portions 21a and 21b is out of the above range, the same problem as in the first embodiment occurs.
【００３９】弱シール部側部２１ａ，２１ｂの剥離強度
は、弱シール部中央部２１ｃの剥離強度の１．２〜５倍
であるのが好ましい。この範囲を外れたときには、第１
の実施形態と同様な問題が生じる。The peel strength of the weak seal portion side portions 21a and 21b is preferably 1.2 to 5 times the peel strength of the weak seal central portion 21c. If outside this range, the first
A problem similar to that of the first embodiment occurs.
【００４０】弱シール部中央部２１ｃの剥離強度は、第
１の実施形態における弱シール部中央部２ｃの剥離強度
と同じ範囲で設定される。また、弱シール部側部２１
ａ，２１ｂの剥離強度も、第１の実施形態における弱シ
ール部側部２ａ，２ｂの剥離強度と同じ範囲で設定され
る。剥離強度がそれぞれの好適範囲から外れたときの問
題点も、第１の実施形態と同様である。The peel strength of the weak seal central part 21c is set in the same range as the peel strength of the weak seal central part 2c in the first embodiment. Also, the weak seal portion side 21
The peel strength of the a and 21b is also set in the same range as the peel strength of the weak seal portion side portions 2a and 2b in the first embodiment. Problems when the peel strength deviates from the respective preferred ranges are also the same as in the first embodiment.
【００４１】上記第１〜第３の実施形態の説明では、い
ずれも収容室が２室である複室容器を例示して説明した
が、本発明においては収容室が３室以上であってもよ
い。この場合、それぞれの収容室における少なくとも１
つの隔壁が、隣接する収容室と上記第１〜第３の実施形
態に示す弱シール部で区画されていればよい。In the above first to third embodiments, a multi-chamber container having two accommodation chambers has been described as an example. However, in the present invention, even if the number of accommodation chambers is three or more, Good. In this case, at least one
It suffices that one partition is partitioned by the adjacent storage chamber and the weak seal portion described in the first to third embodiments.
【００４２】また、弱シール部の剥離強度は、側部、中
央部および端部内でそれぞれの所定の強度範囲を満足し
ていれば必ずしも均一である必要はなく、弱シール部の
中央部から側部にかけて剥離強度が高くなるように連続
的に変化していてもよい。The peel strength of the weak seal portion is not necessarily required to be uniform as long as it satisfies the respective predetermined strength ranges in the side portion, the center portion, and the end portion. It may be continuously changed so that the peel strength increases over the part.
【００４３】〔複室容器本体〕本発明の複室容器の本体
は、従来の複室容器と同様に、医療用として許容された
プラスチック（ポリマー、エラストマーを含む）のフィ
ルムを用いて、公知の成形方法により成形される。[Multi-chamber container main body] The multi-chamber container main body of the present invention is made of a known plastic (including polymers and elastomers) film as in the conventional multi-chamber container using a known film. It is molded by a molding method.
【００４４】上記フィルムには、例えばブロー成形法、
インフレーション法、Ｔダイ法等の、従来公知の種々の
方法により成形されたものを使用することができる。The above-mentioned film is formed by, for example, a blow molding method.
Those molded by various conventionally known methods such as an inflation method and a T-die method can be used.
【００４５】上記プラスチックとしては、特にポリエチ
レン、ポリプロピレン等のポリオレフィンが、優れた成
形性を有しており、かつ安全性が確立していることから
好適に用いられる。As the above-mentioned plastic, in particular, polyolefins such as polyethylene and polypropylene are preferably used because they have excellent moldability and safety has been established.
【００４６】ポリエチレンは、エチレンのホモポリマー
のほかに、プロピレン、１−ブテン、４−メチル−１−
ペンテン等のα−オレフィンとの共重合体であってもよ
く、これらの共重合体は直鎖状、分岐鎖状のいずれであ
ってもよい。また、本発明に用いられるポリエチレン
は、高密度であるか低密度であるかを問わず、広い範囲
から適宜選択できるが、柔軟性や透明性の観点から、直
鎖状で低密度のポリエチレンを主材料として使用するの
が好ましい。Polyethylene is not only a homopolymer of ethylene but also propylene, 1-butene, 4-methyl-1-
Copolymers with α-olefins such as pentene may be used, and these copolymers may be linear or branched. Further, the polyethylene used in the present invention can be appropriately selected from a wide range, regardless of whether it is high-density or low-density.From the viewpoint of flexibility and transparency, linear and low-density polyethylene is used. It is preferably used as the main material.
【００４７】ポリプロピレンは、プロピレンのホモポリ
マーのほかに、エチレン、１−ブテン等のオレフィンを
少量（一般に１０重量％以下、好ましくは５重量％以
下）含むの共重合体であってもよい。中でも、医療用容
器に汎用されているグレードのものを用いるのが好適で
ある。さらに、ポリ１−ブテンやポリ４−メチル−１−
ペンテン等のポリオレフィンも適宜使用することができ
る。The polypropylene may be a copolymer containing a small amount (generally 10% by weight or less, preferably 5% by weight or less) of an olefin such as ethylene or 1-butene in addition to a propylene homopolymer. Among them, it is preferable to use a grade commonly used for medical containers. Furthermore, poly 1-butene and poly 4-methyl-1-
Polyolefins such as pentene can also be used as appropriate.
【００４８】上記ポリオレフィンは、単独で用いてもよ
く、混合樹脂として用いてもよい。特に、例えばポリエ
チレンとポリプロピレンや、密度の異なるポリエチレン
同士の混合樹脂を採用すれば、弱シール部の形成が容易
になる。The above-mentioned polyolefins may be used alone or as a mixed resin. In particular, for example, if a mixed resin of polyethylene and polypropylene or polyethylene having different densities is employed, the formation of the weak seal portion is facilitated.
【００４９】また、本発明の複室容器の本体は、多層構
造のプラスチックから形成されたものであってもよい。Further, the main body of the multi-chamber container of the present invention may be formed of a multilayer plastic.
【００５０】〔弱シール部の形成方法〕本発明の複室容
器における周縁部は、現在一般に普及している手段、例
えばヒートシールバーによる熱融着等によって形成され
る。[Method of Forming Weakly Sealed Part] The peripheral part of the multi-chamber container of the present invention is formed by a means that is currently widely used, for example, heat fusion using a heat seal bar.
【００５１】本発明の複室容器における弱シール部は、
従来の複室容器で採用されている方法と同様の方法によ
って形成することが適用できる。すなわち、例えば(i)
複室容器を構成するフィルムのうち、弱シール部におけ
る容器内側（多層フィルムで複室容器を作成する場合に
は当該多層フィルムの最内層）に、ポリエチレン−ポリ
プロピレン混合樹脂等の混合樹脂を使用したり、(ii)弱
シールを形成する部分に上記混合樹脂のテープを挟んだ
状態で熱融着したり、(iii) 弱シール部の熱融着温度
を、周縁部を熱融着させる際の温度（通常の完全融着温
度）よりも低く設定したりする方法などが挙げられる。The weak seal portion in the multi-chamber container of the present invention
The formation by the same method as that employed in the conventional multi-chamber container can be applied. That is, for example, (i)
Among the films constituting the multi-chamber container, a mixed resin such as a polyethylene-polypropylene mixed resin is used on the inside of the container at the weakly sealed portion (in the case of forming a multi-chamber container with a multilayer film, the innermost layer of the multilayer film). Or (ii) heat-sealing with the mixed resin tape sandwiched in the portion forming the weak seal, or (iii) adjusting the heat-sealing temperature of the weak seal portion to heat-sealing the peripheral portion. And a method of setting the temperature lower than the temperature (normal perfect fusion temperature).
【００５２】弱シール部の剥離強度を、当該弱シール部
の中心部と側部とで部分的に異なるものとするには、例
えば(1) ヒートシールバーの温度を部分的に変える、
(2) ヒートシールバーのクリアランスを、シム（薄板）
等を噛ませることによって部分的に変える、(3) 通常の
ヒートシールの方法により一旦弱シール部を形成し、こ
の弱シール部のうち剥離強度を高く設定する箇所を部分
的に再度ヒートシールする等の方法が挙げられる。To make the peel strength of the weak seal portion partially different between the center portion and the side portion of the weak seal portion, for example, (1) the temperature of the heat seal bar is partially changed.
(2) Clear the heat seal bar with a shim (thin plate)
(3) A weak seal portion is once formed by a normal heat sealing method, and a portion of the weak seal portion where the peel strength is set high is partially heat-sealed again. And the like.
【００５３】また、容器の内壁を上記のように混合樹脂
とする代わりに、同様の混合樹脂から成形したテープを
弱シール部形成部に挟んだ状態で熱融着を行うことによ
っても形成できる。Further, instead of using the mixed resin for the inner wall of the container as described above, the container can be formed by heat-sealing a tape molded from the same mixed resin while sandwiching the tape between the weak seal portion forming portions.
【００５４】[0054]
【実施例】以下、実施例および比較例を挙げて本発明を
説明する。The present invention will be described below with reference to examples and comparative examples.
【００５５】〔多層フィルムの成形〕下記の樹脂Ａ〜Ｅ
を用いて、Ｔダイ法により多層フィルムを成形した。[Formation of multilayer film] The following resins A to E
Was used to form a multilayer film by the T-die method.
【００５６】樹脂Ａ〜Ｅはそれぞれ次のとおりである。 ・樹脂Ａ：直鎖状ポリエチレン（エチレン・１−ブテン
共重合体）〔密度０．９４ｇ／ｃｍ3 、メルトフローレ
ート（ＭＦＲ）２．１ｇ／１０分（１９０℃）〕 ・樹脂Ｂ：直鎖状ポリエチレン（エチレン・１−ブテン
共重合体）〔密度０．９２ｇ／ｃｍ3 、ＭＦＲ２．１ｇ
／１０分（１９０℃）〕 ・樹脂Ｃ：エチレン・１−ブテン共重合体エラストマー
〔密度０．８８５ｇ／ｃｍ3 、ＭＦＲ０．５ｇ／１０分
（１９０℃）〕 ・樹脂Ｄ：直鎖状ポリエチレン（エチレン・１−ブテン
共重合体）〔密度０．９６２ｇ／ｃｍ3 、ＭＦＲ１５ｇ
／１０分（１９０℃）〕 ・樹脂Ｅ：アイソタクチックポリプロピレン（エチレン
含量５重量％以下）〔密度０．９１ｇ／ｃｍ3 、ＭＦＲ
４０ｇ／１０分（２３０℃）〕 多層フィルムの層構成は次のとおりである。 ・第１層（外層）：樹脂Ａ単独からなる厚さ２０μｍの
層 ・第２層（中間層）：樹脂Ｂ４５重量％、樹脂Ｃ５０重
量％および樹脂Ｄ５重量％の混合樹脂からなる厚さ２０
０μｍの層 ・第３層（内層）：樹脂Ａ８０重量％および樹脂Ｅ２０
重量％の混合樹脂からなる厚さ３０μｍの層 〔複室容器の製造〕 実施例１ 上記多層フィルム２枚を当該フィルムの第３層を内側に
して重ね、ヒートシールによって弱シール部２を熱融着
させることにより、図１に示す形状の複室容器１を製造
した。弱シール部２は、全体の横幅Ｌのうち、中央部２
ｃの横幅を３０％、側部２ａ，２ｂの横幅をそれぞれ３
５％となるように設定した。The resins A to E are as follows.・ Resin A: linear polyethylene (ethylene / 1-butene copolymer) [density 0.94 g / cm 3 , melt flow rate (MFR) 2.1 g / 10 min (190 ° C.)] ・ Resin B: linear Polyethylene (ethylene / 1-butene copolymer) [density 0.92 g / cm 3 , MFR 2.1 g
/ 10 min (190 ° C.)] Resin C: ethylene / 1-butene copolymer elastomer [density 0.885 g / cm 3 , MFR 0.5 g / 10 min (190 ° C.)] Resin D: linear polyethylene ( Ethylene / 1-butene copolymer) [density 0.962 g / cm 3 , MFR 15 g
/ 10 min (190 ° C.)] Resin E: isotactic polypropylene (ethylene content 5% by weight or less) [density 0.91 g / cm 3 , MFR
40 g / 10 min (230 ° C.)] The layer constitution of the multilayer film is as follows. The first layer (outer layer): a layer made of resin A alone and having a thickness of 20 μm. The second layer (intermediate layer): a thickness 20 made of a mixed resin of 45% by weight of resin B, 50% by weight of resin C and 5% by weight of resin D.
0 μm layer Third layer (inner layer): 80% by weight of resin A and resin E20
Example 1 Production of a multi-chamber container Two layers of the above multilayer film were laminated with the third layer of the film inside, and the weakly sealed portion 2 was heat-sealed by heat sealing. Thus, the multi-chamber container 1 having the shape shown in FIG. 1 was manufactured. The weak seal portion 2 has a central portion 2 of the entire width L.
c is 30%, and the side portions 2a and 2b are 3% each.
It was set to be 5%.
【００５７】ヒートシールの条件は、周縁部４，４０が
１６０℃で３秒間、弱シール部２が１３５℃で４秒間と
した。弱シール部２の側部２ａ，２ｂに対応する箇所に
は厚さ約２５μｍのシムを噛ませて、当該箇所のヒート
シールバーのクリアランスを部分的に変えて熱融着を行
った。こうして得られた複室容器１の弱シール部２の剥
離強度は、中央部２ｃが０．４ｋｇｆ／１５ｍｍ、側部
２ａ，２ｂが１．０ｋｇｆ／１５ｍｍであった。The conditions for heat sealing were as follows: the peripheral portions 4 and 40 were at 160 ° C. for 3 seconds, and the weak seal portions 2 were at 135 ° C. for 4 seconds. A portion corresponding to the side portions 2a and 2b of the weak seal portion 2 was bitten with a shim having a thickness of about 25 μm, and heat sealing was performed by partially changing the clearance of the heat seal bar at the portion. The peel strength of the weak seal portion 2 of the multi-chamber container 1 thus obtained was 0.4 kgf / 15 mm at the central portion 2c and 1.0 kgf / 15 mm at the side portions 2a and 2b.
【００５８】比較例１ 上記多層フィルム２枚を当該フィルムの第３層を内側に
して重ね、ヒートシールによって弱シール部６を熱融着
させることにより、図５に示す形状の複室容器５を製造
した。COMPARATIVE EXAMPLE 1 The above-mentioned two multilayer films were stacked with the third layer of the film inside, and the weakly sealed portion 6 was heat-sealed by heat sealing to form a multi-chamber container 5 having the shape shown in FIG. Manufactured.
【００５９】ヒートシールの条件は、周縁部４，４０が
１６０℃で３秒間、弱シール部６が１３５℃で４秒間と
した。The conditions for heat sealing were as follows: the peripheral portions 4 and 40 were at 160 ° C. for 3 seconds, and the weak seal portions 6 were at 135 ° C. for 4 seconds.
【００６０】こうして得られた複室容器５の弱シール部
６の剥離強度は０．４ｋｇｆ／１５ｍｍであって、弱シ
ール部６全体で均一であった。The peel strength of the weak seal portion 6 of the multi-chamber container 5 thus obtained was 0.4 kgf / 15 mm, and was uniform throughout the weak seal portion 6.
【００６１】〔複室容器の性能試験〕上記実施例および
比較例で得られた複室容器１，５の収容室３のうち、上
側の収容室３ａに水６００ｍｌと、下側の収容室３ｂに
水１２００ｍｌを充填した。[Performance test of double-chamber container] Of the storage chambers 3 of the multi-chamber containers 1 and 5 obtained in the above Examples and Comparative Examples, 600 ml of water was placed in the upper storage chamber 3a and 3d in the lower storage chamber 3b. Was filled with 1200 ml of water.
【００６２】次いで、下側の収容室３ｂを押圧すること
により弱シール部２，６の開封を行ったところ、実施例
１および比較例１の双方ともに３５ｋｇｆの押力で弱シ
ール部を剥離させることができた。また、いずれの複室
容器も、押圧時に周縁部４，４０は破損しなかった。Next, when the weak seal portions 2 and 6 were opened by pressing the lower housing chamber 3b, the weak seal portions were peeled off with a pressing force of 35 kgf in both Example 1 and Comparative Example 1. I was able to. In addition, the peripheral portions 4 and 40 were not damaged when pressed in any of the multi-chamber containers.
【００６３】さらに、実施例１および比較例１の複室容
器各１００袋について前述のように水を充填した後、複
室容器の左右周縁部４０のいずれか一方を下にして１ｍ
の高さから落下させたところ、実施例１では弱シール部
２が開封したものは１袋も無かったのに対し、比較例１
では１００袋中４８袋について弱シール部６の剥離が生
じた。Further, after filling the water in each of the 100 bags of the multi-compartment containers of Example 1 and Comparative Example 1 as described above, 1 m of the left and right peripheral portions 40 of the multi-compartment container was set at 1 m.
When the bag was dropped from the height of Example 1, there was no bag in which the weak seal portion 2 was opened in Example 1, whereas in Comparative Example 1
In this case, peeling of the weak seal portion 6 occurred in 48 bags out of 100 bags.
【００６４】上記結果より、本発明の複室容器は、側面
方向からの落下に対しても十分耐え得る上、弱シール部
の開封性は損なわれないことがわかった。From the above results, it was found that the double-chamber container of the present invention can sufficiently withstand dropping from the side direction and that the openability of the weak seal portion is not impaired.
【００６５】[0065]
【発明の効果】以上詳述したように、本発明によれば、
収容室を所定の力以上で押圧したときには、弱シール部
を容易に剥離させて各室の収容物を混合することがで
き、一方で左右の周縁部を下にして落下させるなど、左
右周縁部から衝撃を受けたときに弱シール部が誤って剥
離することがなく、収容物を分離して収容する状態を維
持することのできる複室容器を得ることができる。As described in detail above, according to the present invention,
When the storage chamber is pressed with a predetermined force or more, the weak seal portion can be easily peeled and the contents of each chamber can be mixed, while the left and right peripheral parts are dropped with the left and right peripheral parts down. A weakly sealed portion does not accidentally peel off when receiving an impact from the container, and a multi-chamber container capable of maintaining a state in which the contents are separated and stored can be obtained.
【００６６】かかる本発明の複室容器は、アミノ酸を含
む輸液とブドウ等を含む輸液や、抗生物質とその溶解液
等の、混合状態で保管すると変質するおそれのある薬剤
用の容器として好適である。The multi-chamber container of the present invention is suitable as a container for a drug that may be deteriorated when stored in a mixed state, such as an infusion solution containing amino acids and an infusion solution containing grape, or an antibiotic and a solution thereof. is there.
【図１】複室容器の一実施形態を示す正面図である。FIG. 1 is a front view showing an embodiment of a multi-chamber container.
【図２】複室容器の他の実施形態を示す正面図である。FIG. 2 is a front view showing another embodiment of the multi-chamber container.
【図３】複室容器の他の実施形態を示す正面図である。FIG. 3 is a front view showing another embodiment of a multi-chamber container.
【図４】同図(a) および(b) は弱シール部の剥離強度の
測定方法を示す模式図である。FIGS. 4A and 4B are schematic views showing a method for measuring the peel strength of a weak seal portion.
【図５】従来の複室容器を示す正面図である。FIG. 5 is a front view showing a conventional multi-chamber container.
１，１０，１１ 複室容器 ２，２０，２１ 弱シール部 ２ａ，２０ａ，２１ａ 側部 ２ｂ，２０ｂ，２１ｂ 側部 ２ｃ，２０ｃ，２１ｃ 中央部 ３ 収容室 ３ａ，３０ａ，３１ａ 収容室 ３ｂ，３０ｂ，３１ｂ 収容室 ４，４０ 周縁部 Ｌ 弱シール部の横幅 1, 10, 11 Multi-chamber container 2, 20, 21 Weak seal part 2a, 20a, 21a Side part 2b, 20b, 21b Side part 2c, 20c, 21c Central part 3 Storage room 3a, 30a, 31a Storage room 3b, 30b , 31b Storage chamber 4, 40 Peripheral part L Width of weak seal part
Claims (5)
する可撓性容器であって、前記弱シール部が中央部とそ
の両側の側部との少なくとも３つの部分からなり、弱シ
ール部側部の剥離強度が弱シール部中央部の剥離強度よ
りも大きいことを特徴とする複室容器。1. A flexible container having a plurality of storage chambers partitioned by a weak seal portion, wherein the weak seal portion comprises at least three portions: a central portion and side portions on both sides thereof. A multi-chamber container wherein the peel strength at the side of the part is greater than the peel strength at the center of the weak seal.
の１０〜８０％である請求項１記載の複室容器。2. The multi-chamber container according to claim 1, wherein the width of the central portion of the weak seal portion is 10 to 80% of the entire weak seal portion.
中央部の剥離強度の１．２〜５倍である請求項１または
２記載の複室容器。3. The multi-chamber container according to claim 1, wherein the peel strength at the side of the weak seal portion is 1.2 to 5 times the peel strength at the central portion of the weak seal portion.
０．７ｋｇｆ／１５ｍｍである請求項３記載の複室容
器。4. The peel strength at the central portion of the weak seal portion is 0.2 to
The multi-chamber container according to claim 3, which has a weight of 0.7 kgf / 15 mm.
５ｋｇｆ／１５ｍｍである請求項３記載の複室容器。5. The peel strength at the side of the weak seal portion is 0.5 to 1.
The double-chamber container according to claim 3, which has a weight of 5 kgf / 15 mm.