IN2014KN01189A - - Google Patents

Info

Publication number
IN2014KN01189A
IN2014KN01189A IN1189KON2014A IN2014KN01189A IN 2014KN01189 A IN2014KN01189 A IN 2014KN01189A IN 1189KON2014 A IN1189KON2014 A IN 1189KON2014A IN 2014KN01189 A IN2014KN01189 A IN 2014KN01189A
Authority
IN
India
Prior art keywords
steel sheet
manganese
silicon
crystal grains
hot rolled
Prior art date
Application number
Inventor
Yoshimasa Funakawa
Tetsuo Yamamoto
Hiroshi Uchomae
Hiroshi Nakano
Taro Kizu
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of IN2014KN01189A publication Critical patent/IN2014KN01189A/en

Abstract

Provided is a high strength hot rolled steel sheet that exhibits little inter coil variability in mechanical properties and excellent stretch flangeability. By mass said steel sheet contains more than 0.010% and no more than 0.06% carbon up to 0.3% silicon up to 0.8% manganese up to 0.03% phosphorus up to 0.02% sulfur up to 0.1% aluminum up to 0.01% nitrogen and 0.05 0.10% titanium with the remainder comprising iron and unavoidable impurities. The amounts of silicon and manganese are minimized the amount of segregation and the like is reduced and strength variation due to inter coil position differences is decreased. The structure of the steel sheet is such that the area fraction of a ferrite phase is at least 95% the mean diameter of ferrite crystal grains is at least 1 µm and TiC with a mean grain diameter of at most 7 nm is dispersed inside the ferrite crystal grains. This results in a high strength hot rolled steel sheet that maintains a yield strength of at least 530 MPa.
IN1189KON2014 2011-12-27 2012-12-14 IN2014KN01189A (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011284685A JP5838796B2 (en) 2011-12-27 2011-12-27 High-strength hot-rolled steel sheet excellent in stretch flangeability and manufacturing method thereof
PCT/JP2012/008003 WO2013099136A1 (en) 2011-12-27 2012-12-14 High-strength hot-rolled steel sheet and manufacturing method therefor

Publications (1)

Publication Number Publication Date
IN2014KN01189A true IN2014KN01189A (en) 2015-10-16

Family

ID=48696684

Family Applications (1)

Application Number Title Priority Date Filing Date
IN1189KON2014 IN2014KN01189A (en) 2011-12-27 2012-12-14

Country Status (7)

Country Link
US (2) US9657382B2 (en)
EP (1) EP2799578B1 (en)
JP (1) JP5838796B2 (en)
KR (1) KR20140103339A (en)
CN (1) CN104024460B (en)
IN (1) IN2014KN01189A (en)
WO (1) WO2013099136A1 (en)

Families Citing this family (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5838796B2 (en) * 2011-12-27 2016-01-06 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in stretch flangeability and manufacturing method thereof
US10301698B2 (en) 2012-01-31 2019-05-28 Jfe Steel Corporation Hot-rolled steel sheet for generator rim and method for manufacturing the same
JP5637225B2 (en) * 2013-01-31 2014-12-10 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in burring workability and manufacturing method thereof
JP5821864B2 (en) * 2013-01-31 2015-11-24 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in burring workability and manufacturing method thereof
JP6036756B2 (en) * 2013-08-30 2016-11-30 Ｊｆｅスチール株式会社 High strength hot rolled steel sheet and method for producing the same
ES2791757T3 (en) * 2013-12-19 2020-11-05 Nippon Steel Corp Hot-dip coated steel sheet with a Zn-Al-Mg based system that has excellent workability and method of manufacturing it
JP6349865B2 (en) * 2014-03-28 2018-07-04 Ｊｆｅスチール株式会社 Hot-rolled steel sheet and manufacturing method thereof
BR112017003147A2 (en) * 2014-08-25 2017-11-28 Tata Steel Ijmuiden Bv low-alloy, high-strength cold-rolled steel
BR112018000633A2 (en) * 2015-07-31 2018-09-18 Nippon Steel & Sumitomo Metal Corporation high-strength hot-rolled steel sheet
CN105177467A (en) * 2015-08-31 2015-12-23 铜陵市大明玛钢有限责任公司 Configuration of hot-rolled steel plate and manufacturing process thereof
CN105369162A (en) * 2015-12-16 2016-03-02 常熟市凯波冶金建材机械设备厂 Anti-explosion gas turbine housing
GB2546809B (en) * 2016-02-01 2018-05-09 Rolls Royce Plc Low cobalt hard facing alloy
GB2546808B (en) * 2016-02-01 2018-09-12 Rolls Royce Plc Low cobalt hard facing alloy
CA3034549A1 (en) * 2016-09-22 2018-03-29 Tata Steel Ijmuiden B.V. A method of producing a hot-rolled high-strength steel with excellent stretch-flange formability and edge fatigue performance
WO2019026739A1 (en) * 2017-07-31 2019-02-07 Ｊｆｅスチール株式会社 Steel sheet for crown cap, crown cap, and method for manufacturing steel sheet for crown cap
US10633726B2 (en) * 2017-08-16 2020-04-28 The United States Of America As Represented By The Secretary Of The Army Methods, compositions and structures for advanced design low alloy nitrogen steels
CN108165881A (en) * 2018-01-08 2018-06-15 哈尔滨工程大学 A kind of 800MPa grades of more characteristic hot rolled steel plates and preparation method thereof
HUE052103T2 (en) * 2018-01-23 2021-04-28 Ssab Technology Ab Hot rolled steel and process for the production of hot rolled steel
WO2020039979A1 (en) * 2018-08-23 2020-02-27 Ｊｆｅスチール株式会社 Hot rolled steel plate and manufacturing method thereof
CN109797336B (en) * 2019-01-17 2020-04-21 武汉钢铁有限公司 Tubeless rim steel with thickness of 9-11 mm and production method thereof
CN112522587B (en) * 2019-09-19 2022-07-19 宝山钢铁股份有限公司 High-hole-expansion steel based on scrap steel raw material and production method thereof
KR102846338B1 (en) * 2020-08-27 2025-08-14 닛폰세이테츠 가부시키가이샤 hot rolled steel plate
WO2024096073A1 (en) * 2022-11-02 2024-05-10 日本製鉄株式会社 Hot-rolled coil
CN116377338B (en) * 2022-12-05 2024-11-12 钢铁研究总院有限公司 A kind of alloy and its preparation method and application

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3539545B2 (en) * 1998-12-25 2004-07-07 Ｊｆｅスチール株式会社 High-tensile steel sheet excellent in burring property and method for producing the same
JP3433687B2 (en) * 1998-12-28 2003-08-04 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in workability and method for producing the same
JP3990549B2 (en) 2001-06-05 2007-10-17 新日本製鐵株式会社 High stretch flangeability steel sheet with excellent shape freezing property and method for producing the same
US6669789B1 (en) * 2001-08-31 2003-12-30 Nucor Corporation Method for producing titanium-bearing microalloyed high-strength low-alloy steel
JP3821036B2 (en) * 2002-04-01 2006-09-13 住友金属工業株式会社 Hot rolled steel sheet, hot rolled steel sheet and cold rolled steel sheet
JP3775337B2 (en) 2002-04-26 2006-05-17 Ｊｆｅスチール株式会社 High formability, high-tensile hot-rolled steel sheet with excellent material uniformity, manufacturing method and processing method thereof
JP3821042B2 (en) 2002-04-30 2006-09-13 Ｊｆｅスチール株式会社 High-formability high-tensile steel sheet with excellent strength stability and method for producing and processing the same
JP3821043B2 (en) * 2002-04-30 2006-09-13 Ｊｆｅスチール株式会社 Hot-dip galvanized high-strength hot-rolled steel sheet with excellent weldability, manufacturing method and processing method thereof
JP4160839B2 (en) 2003-02-19 2008-10-08 新日本製鐵株式会社 High formability and high strength hot-rolled steel sheet with low shape anisotropy and small anisotropy and method for producing the same
JP2005054255A (en) 2003-08-06 2005-03-03 Jfe Steel Kk High-strength hot-rolled steel sheet for CRT frame, method for manufacturing the same, and CRT frame
EP1918396B1 (en) * 2005-08-05 2014-11-12 JFE Steel Corporation High-tension steel sheet and process for producing the same
JP4575893B2 (en) 2006-03-20 2010-11-04 新日本製鐵株式会社 High strength steel plate with excellent balance of strength and ductility
JP2007308771A (en) 2006-05-19 2007-11-29 Nippon Steel Corp High strength steel plate with excellent shape freezing properties
JP2010053434A (en) * 2008-08-29 2010-03-11 Nakayama Steel Works Ltd High strength hot rolled thin steel sheet having excellent ductility and method for producing the same
JP5458641B2 (en) * 2009-04-21 2014-04-02 Ｊｆｅスチール株式会社 Carbide dispersion steel
JP4998755B2 (en) * 2009-05-12 2012-08-15 Ｊｆｅスチール株式会社 High strength hot rolled steel sheet and method for producing the same
JP5338525B2 (en) * 2009-07-02 2013-11-13 新日鐵住金株式会社 High yield ratio hot-rolled steel sheet excellent in burring and method for producing the same
JP5278226B2 (en) 2009-07-29 2013-09-04 新日鐵住金株式会社 Alloy-saving high-strength hot-rolled steel sheet and manufacturing method thereof
JP5609786B2 (en) * 2010-06-25 2014-10-22 Ｊｆｅスチール株式会社 High-tensile hot-rolled steel sheet excellent in workability and manufacturing method thereof
JP5765080B2 (en) * 2010-06-25 2015-08-19 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in stretch flangeability and manufacturing method thereof
JP5838796B2 (en) * 2011-12-27 2016-01-06 Ｊｆｅスチール株式会社 High-strength hot-rolled steel sheet excellent in stretch flangeability and manufacturing method thereof

Also Published As

Publication number Publication date
US20170218474A1 (en) 2017-08-03
CN104024460A (en) 2014-09-03
US20140363696A1 (en) 2014-12-11
JP2013133497A (en) 2013-07-08
EP2799578B1 (en) 2017-11-22
WO2013099136A1 (en) 2013-07-04
US9657382B2 (en) 2017-05-23
US10533236B2 (en) 2020-01-14
CN104024460B (en) 2016-06-22
EP2799578A1 (en) 2014-11-05
JP5838796B2 (en) 2016-01-06
EP2799578A4 (en) 2016-01-27
KR20140103339A (en) 2014-08-26

Similar Documents

Publication Publication Date Title
IN2014KN01189A (en)
IN2014KN00887A (en)
WO2012127125A8 (en) Hot-rolled steel sheet and associated production method
MX363636B (en) High-strength steel sheet having excellent processability and paint bake hardenability, and method for producing same.
IN2014CN04330A (en)
IN2014KN01170A (en)
MX2013002627A (en) Grain-oriented magnetic steel sheet and process for producing same.
IN2014DN00268A (en)
MX2016013898A (en) Hot-rolled steel sheet for tailored rolled blank, tailored rolled blank, and method for producing these.
MX2015001071A (en) Cold-rolled steel sheet, electrolytic zinc-coated cold-rolled steel sheet, hot-dip zinc-coated cold-rolled steel sheet, alloyed hot-dip zinc-coated cold-rolled steel sheet, and methods for producing said steel sheets.
MX365792B (en) Automotive chassis part made from high strength formable hot rolled steel sheet.
MX340869B (en) Hot-rolled steel.
MX2015009431A (en) 780 mpa class cold rolled dual-phase strip steel and manufacturing method thereof.
IN2014KN01297A (en)
IN2014MN01636A (en)
MY183438A (en) High-strength cold-rolled steel sheet and method for manufacturing the same
IN2014MN00819A (en)
MX390334B (en) COLD-ROLLED STEEL SHEET AND METHOD FOR MANUFACTURING SAME.
MY192691A (en) High yield ratio type high strenght steel sheet having high strength and a high yield ratio with excellent formability
IN2014DN06146A (en)
MY171985A (en) High strength cold rolled steel sheet having yield strength with low planar anisotropy, and method for manufacturing the same
MX377319B (en) STEEL SHEET FOR NITRIDING AND METHOD FOR PRODUCTION THEREOF.
MY153967A (en) High-strength hot rolled steel sheet having good formability and method for manufacturing the same
MY177836A (en) Low yield ratio high-strength hot-dip galvanized steel sheet, low yield ratio high-strength hot-dip galvannealed steel sheet, method for manufacturing low yield ratio highstrength hot-dip galvanized steel sheet, and method for manufacturing low yield ratio high-strength hot-dip galvannealed steel sheet
TWI504756B (en) Manufacture method of high strength and high ductility steel