HU213641B - Glass product with ability pulling fiber from it, procedure for making insulating glass-fiber and the insulating glass-fiber - Google Patents
Glass product with ability pulling fiber from it, procedure for making insulating glass-fiber and the insulating glass-fiber Download PDFInfo
- Publication number
- HU213641B HU213641B HU9201735A HU9201735A HU213641B HU 213641 B HU213641 B HU 213641B HU 9201735 A HU9201735 A HU 9201735A HU 9201735 A HU9201735 A HU 9201735A HU 213641 B HU213641 B HU 213641B
- Authority
- HU
- Hungary
- Prior art keywords
- weight
- glass
- fiber
- sio
- composition
- Prior art date
Description
A találmány tárgya üvegkészítmény és felhasználása. Találmányunk olyan bór-trioxid-mentes üvegkészítményre vonatkozik, amelyből szálat lehet húzni, vonatkozik továbbá egy szálhúzó eljárásra a találmány szerinti készítményekből, mechanikusan ötvözött vagy oxid-diszperzióval erősített ötvözetből készült szálhúzógépben, valamint vonatkozik a találmány szerinti készítményekből előállított üvegszál szigetelőanyagokra is.
Számos üvegkészítmény ismeretes, amelyből centrifugális szálhúzóval üvegszál állítható elő. Ezek a készítmények általában tartalmaznak bór-trioxidot, annak érdekében, hogy megfelelő hőmérséklet/viszkozitás tulajdonságokkal rendelkezzenek, amelynek révén az üveg szabadon át tud haladni a centrifugális szálhúzó fal nyílásain, elegendően alacsony hőmérsékleten a szálhúzó berendezés túlzott korróziójának és eróziójának megelőzésére. A bór-trioxid alkalmazásával együtt jár az a probléma, hogy a bór illékony az üvegolvasztó tartályból elillanva környezetszennyezési problémákat okozhat. Ezenkívül hajlamos a regenerátorokra kondenzálni is, amelyeket így eldugítja és megakadályozza az ilyen berendezéseknek az olajtüzelésű üvegolvasztó tartályok termikus hatékonyságának javítására való felhasználását.
A GB 2 041 910. sz. szabadalmi leírásban javasolják a bór-trioxid mennyiségének csökkentését vagy teljes elhagyását, aminek az a következménye, hogy megemelkedik a likvidusz hőmérséklet és nagyobb az alumínium—oxid vagy bárium-oxid tartalom. Ezeket a csökkentett bór-trioxid tartalmú készítményeket gyakorlatilag lehetetlen az ismert szálhúzó eljárásokkal ipari méretekben szállá feldolgozni. Javasolnak ugyan egy új eljárást, amely egy új kialakítású szálhúzót alkalmaz, azonban a gyakorlatban az ilyen szálhúzók korróziója, amennyiben ezeket hagyományos ötvözetekből készítik, elfogadhatatlanul magas. Az ezen szabadalmi leírás szerinti készítmények tartóssága pedig elfogadhatatlanul alacsony.
Az EP-A-0413254. számú szabadalmi leírásban olyan síküveggyártásra alkalmas üveget ismertetnek, amelynek különleges összetételében a kálcium-oxid és a magnézium-oxid mennyiségét és egymáshoz viszonyított arányát szigorúan meghatározzák.
Az EP-A-0399320. számú szabadalmi leírásban csökkentett rákkeltő hatással rendelkező szálat állítanak elő oly módon, hogy az átlagos rostátmérőt csökkentik. Az üvegkészitményben bór-trioxid is van.
Az US-5,03 0,594. számú szabadalmi leírásban (1991. július 9-én hozták nyilvánosságra) Fe2O3-mal kék színűre színezett síküveget ismertetnek.
A 4,396,722. számú amerikai egyesült államokbeli szabadalmi leírásban szálhúzásra alkalmas bórmentes üveget állítanak elő úgy, hogy nagy mennyiségű (4,1-10 tömeg%) vas-oxidot alkalmaznak.
A 4,713,359. számú amerikai egyesült államokbeli szabadalmi leírásban infravörös sugárzást elnyelő üveget állítanak elő úgy, hogy az összetételben foszfor-pentoxidot szerepeltetnek.
A 4,203,746. számú amerikai egyesült államokbeli szabadalmi leírásban üvegszál-előállítási eljárást ismertetnek.
A 4 402 767. sz. amerikai egyesült államokbeli szabadalmi leírás új szálhúzó berendezést előállító eljárást ismertet, amellyel mechanikusan ötvözött vagy oxid-diszperzióval erősített ötvözetet készítenek, meleg megmunkálás, edzés és forró alakítás kombinálásával. Ezekről a szálhúzókról azt állítják, hogy kitünően ellenállnak az olvasztott üveg támadásával szemben, és hogy egészen nagy hőmérsékleteknél, például még 1315 °Cnál is képesek üvegszálat és ásvány gyapotot előállítani. Az üvegszál-előállításról a leírás nem tartalmaz részleteket.
Találmányunk feladata olyan bór-trioxid-mentes üvegkészítmények meghatározása, amelyek rendelkeznek a szükséges tartóssággal és használhatók nagy hőmérsékleten dolgozó szálhúzó berendezésekben, mint amilyeneket például az US 4 402 767. sz. szabadalmi leírásban ismertetnek. Habár a bór-trioxid hiánya az üveg vizes tartósságának romlását okozza, találtunk egy olyan összetétel-tartományt, amelyre ez a tartósság kielégítő.
| Találmány tárgya tehát bór-trioxid-mentes üvegkészítmény, amely szálhúzásra alkalmas, melyre jellemező, hogy a következő komponenseket tartalmazza: | |
| SiO2 | 66-73 tömeg% |
| ai2ó3 | 0,8-5 tömeg% |
| R2O=Na2O+K2O | 14-17,5 tömeg% |
| CaO | 6,5-12 tömeg% |
| SiO2+Al2O3 | 69-74 tömeg% |
| Az ilyen üvegek viszkozitása egészen 1200 °C-ig 100 Pa.s vagy kevesebb és a Műszaki Könyvkiadó: Szilikátipari kézikönyv: 82.,83.,571. oldalakon 1982., Bp. likvidusza legalább 130 °C-kal a 100 Pa.s-hoz tartozó hőmérséklet alatti. A készítmény tartalmazhat a fentieken kívül 0-2 tömeg% Fe2O3-at, 0-5 tömeg% MgO-t, 0-0,6 tömeg% | |
| SO3-at is. | |
| Előnyösek azok | a készítmények, amelyek összetétele |
| a következő: SiO2 | 67-72,4 tömeg% |
| SiO7 | 67-72,4 tömeg% |
| A12Ó3 | 1-4 tömeg% |
| r2o | 14,5-17 tömeg% |
| K2O | 0,5-2 tömeg% |
| Na,0 | 13,5-16,5 tömeg% |
| CaÖ | 7-11,2 tömeg% |
| Fe2O3 | 0,1-2,5 tömeg% |
| MgO | 0,2-4,4 tömeg% |
| SiO2+Al2O3 | 70-73,7 tömeg% |
Különösen előnyösek azok a készítmények, amelyek
| összetétele a következő: | |
| SiO2 | 67-70 tömeg% |
| ai2o3 | 2-4 tömeg% |
| Na2O | 14-15,5 tömeg% |
| K20 | 0,5-1,5 törneg% |
| MgO | 3-4,5 tömeg% |
| CaO | 7-8,5 tömeg0/» |
| Fe2O3 | 0,3-2 tömeg% |
| SÓ3 | 0-0,3 tömeg% |
| SiO2+Al2O3 | 70-72 tömeg% |
| Na2O+K2O | 15-16,5 tömeg% |
HU 213 641 Β
Az alacsony likviduszhőmérséklethez (Szilikátipari Kézikönyv, Műszaki Könyvkiadó, Bp. 1982., 83. o.) magas Na2O tartalom szükséges, azonban az MgO előnyösen szűk tartománya lehetővé teszi az Na2O minimális értéken tartását, ily módon a tartósság optimális és közben a likvidusz legalább 160 °C-kal a 100 Pa.s likviditási hőmérséklet alatt van, amely utóbbi előnyösen 1170 °C alatti.
Találmányunkat a továbbiakban példákkal illusztráljuk. Alacsony SO3, K2O és Fe2O3 tartalmat regisztráltunk ezekben a példákban minimális tartalomként. Valójában ezek a nyersanyagokban vannak jelen, ilyen alacsony mennyiségben, mint szennyezések és nem befolyásolják lényegesen az üvegszálak tulajdonságait. A példákra vonatkozó részleteket és a tartóssági vizsgálat eredményét az 1. táblázatban tüntetjük fel. Megjegyezzük, hogy a 18. példa találmányunk oltalmi körén kívül esik, mivel az összetételben szereplő alacsony alumínium-oxid tartalom miatt a készítmény tartóssága nem kielégítő.
Nincs elfogadott nemzetközi vizsgálati eljárás annak megállapítására, hogy egy üvegkészítmény alkalmas-e szigetelőanyag célú üvegszál előállítására. Általánosan elfogadottá vált az ISO 719. sz. laboratóriumi áruvizsgálat alkalmazása, mivel ez hasznos útmutatást ad arra vonatkozólag, hogy az üveg vizes tartóssága és időjárásállósága megfelel-e. Ebben a vizsgálatban 2 g üvegszemcsét desztillált vízzel kezelünk 60 percig 98 °C-on és az extrahált alkálifém-tartalmat 0,01 mólos sósavoldattal titráljuk. A tartósságot az extrahált alkálifém-oxid mennyiségében fejezzük ki 1 g üvegre vonatkoztatva, a semlegesítéshez szükséges sav mennyiségéből számítva. Az üveggyapot számára megfelelő osztály az ISO 3. sz. osztály, 62-264 ug alkálifém-oxid/gramm tartományban, valamint a 4. osztály 265-620 ug/g tartományban. Az üveggyapot előnyösen a 3. osztályba esik, de egy jó 4-es osztályú készítmény is elfogadható, mivel a szigetelőképesség mind az üveg, mind a gyanta kötőanyag függvénye, és léteznek olyan kötőanyagok, amelyek a nagyobb alkálifém-leadású üvegekhez alkalmazhatók. A 3. osztályba tartozó összetétel tehát jó, a 4. osztályba tartozó elfogadható, de nem minősíthető ugyanolyan jónak.
1. táblázat
| Példa | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 |
| SiO21% | 70 | 69 | 68 | 67 | 70 | 69 | 67 | 67 | 69 | 68,5 | 69 | 68 | 72,4 | 70 |
| A12O, t% | 1 | 2 | 3 | 4 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 1,3 | 3 |
| SiÓ2+Al2O31% | 71 | 71 | 71 | 71 | 73 | 72 | 70 | 70 | 72 | 71,5 | 72 | 71 | 73,7 | 73 |
| Fe2O31% | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 0,3 | 1,3 | 0,1 | 0,3 |
| CaO t% | 8 | 8 | 8 | 8 | 8 | 8 | 8 | 9 | 7 | 8 | 7,5 | 7,5 | 11,2 | 8,3 |
| MgO t% | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 0,2 | 3,9 |
| Na2O t% | 15,5 | 15,5 | 15,5 | 15,5 | 13,5 | 14,5 | 16,5 | 15,5 | 15,5 | 15 | 15 | 15 | 14 | 13,5 |
| K2O t% | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 0,5 | 0,9 |
| R2O t% | 16,5 | 16,5 | 16,5 | 16,5 | 14,5 | 15,5 | 17,5 | 16,5 | 16,5 | 16 | 16 | 16 | 14,5 | 14,4 |
| SÖ31% | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 |
| Tlog 3 | 1146 | 1150 | 1155 | 1159 | 1191 | 1173 | 1136 | 1142 | 1166 | 1163 | 1169 | 1163 | 1170 | 1195 |
| likvidusz °C | 952 | 964 | 982 | 1002 | 1012 | 1002 | 980 | 1018 | 950 | 990 | 966 | 1000 | 1018 | 1018 |
| Pg R2O/g© | 307 | 270 | 260 | 248 | 186 | 251 | 406 | 285 | 298 | 258 | 259 | 253 | 286 | 231 |
| osztály | 4 | 4 | 3 | 3 | 3 | 3 | 4 | 4 | 4 | 3 | 3 | 4 | 4 | 3 |
| 1. | táblázat folytatása | |||||||||||||
| Példa | 15 | 16 | 17 | 18 | 19 | 20 | 21 | 22 | 23 | 24 | 25 | 26 | 27 | 28 |
| SiO2 t% | 68 | 68 | 68,5 | 71 | 68 | 69 | 68 | 67 | 66 | 66 | 66 | 70 | 69,5 | 70,5 |
| A12Ó31% | 4 | 3 | 3 | 0 | 3 | 3 | 3 | 3 | 3 | 4 | 4 | 2 | 2 | 3 |
| SiO2+Al2O31% | 72 | 71 | 71,5 | 71 | 71 | 72 | 71 | 70 | 69 | 70 | 70 | 72 | 71,5 | 73,5 |
| Fe2O31% | 0,3 | 1,9 | 0,3 | 0,3 | 0,3 | 0,3 | 1,3 | 2,3 | 3,3 | 2,5 | 2,5 | 0,5 | 0,5 | 0,3 |
| CaO t% | 7,5 | 8 | 7,6 | 8 | 8 | 7,5 | 7,5 | 7,5 | 7,5 | 7,8 | 6,8 | 8,5 | 8,5 | 8 |
| MgO t% | 3,5 | 3,9 | 4,4 | 4 | 4 | 4 | 4 | 4 | 4 | 3 | 4 | 4 | 4 | 4 |
| Na2O t% | 15,5 | 14 | 15 | 15,5 | 15,5 | 15 | 15 | 15 | 15 | 15,5 | 15 | 14,5 | 14 | 13 |
| K2O t% | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1,5 | 0,5 | 1,5 | 1 |
| R2O t% | 16,5 | 15 | 16 | 16,5 | 16,5 | 16 | 16 | 16 | 16 | 16,5 | 16,5 | 15 | 15,5 | 14 |
| SÖ31% | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0,2 | 0 | 0 | 0,2 |
| Tlog 3 | 1158 | 1170 | 1165 | 1142 | 1154 | 1170 | 1164 | 1157 | 1150 | 1150 | 1164 | 1166 | 1165 | |
| likvidusz °C | 996 | 1026 | 1006 | 940 | 981 | 974 | 994 | 1002 | 1024 | 1010 | 1014 | 1006 | 1005 | |
| Pg R2O/g® | 256 | 195 | 251 | 474 | 251 | 259 | 253 | 236 | 239 | 240 | 206 | 261 | 229 | 186 |
| osztály 3 3 3 4 3 3 ®alkálifém-oxid mennyisége lg üvegre vonatkoztatva | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 3 |
Claims (4)
- SZABADALMI IGÉNYPONTOK1. Bór-trioxid-mentes üvegkészítmények, amelyek
szálhúzásra alkalmasak, azzal jellemezve, hogy a következő komponenseket tartalmazzák: S1O7 ai203 R2O=Na?O+K?O CaO SiO2+Al2O3 66-73 tömeg% 0,8-5 tömeg% 14-17,5 tömeg% 6,5-12 tömeg% 69-74 tömeg% 2. Az 1. igénypont szerinti készítmények, azzal jellemezve, hogy tartalmaznak még legfeljebb 2,5 tömeg% Fe2O3-at, legfeljebb 5 tömeg% MgO-t és legfeljebb 0,6 tömeg% SO3-at is. 3. Az 1. vagy 2. igénypont szerinti készítmények, azzal jellemezve, hogy összetételük a következő: SiO2 67-72,4 tömeg% A12O3 ÍR tömeg% r2ó 14,5-17 tömeg% K2O 0,5-2 tömeg% Na2O 13,5-16,5 tömeg% CaÖ 7-11,2 tömeg% Fe2O3 0,1-2,5 tömeg% MgO 0,2R,4 tömeg%SiO2+Al2O3 70-73,7 tömeg% - 4. A 3. igénypont szerinti készítmények, azzaljelle-
mezve, hogy összetételük a következő: SiO2 67-70 tömeg% A12O3 2R tömeg% Na2O 14-15,5 tömeg% K2O 0,5-1,5 tömeg% MgO 3R,5 tömeg% CaO 7-8,5 tömeg% Fe2O3 0,3-2 tömeg% SO3 0-0,3 tömeg% SiO2+Al2O3 70-72 tömeg% Na2O+K2O 15-16,5 tömeg% - 5. Eljárás szigetelő hatású, az 1-4. igénypontok bármelyike szerinti összetételű üvegszálak előállítására, azzal jellemezve, hogy az olvasztott üvegből nagy hőmérsékleten mechanikusan ötvözött vagy oxid-diszperzióval erősített ötvözetből készült szálhúzó berendezésben szálat húzunk.
- 6. Szigetelő hatású üvegszálak, azzal jellemezve, hogy összetételük az ÍR. igénypontok bármelyike szerinti.