GB373017A - Process and apparatus for the heat treatment of bodies produced at high temperatures - Google Patents
Process and apparatus for the heat treatment of bodies produced at high temperaturesInfo
- Publication number
- GB373017A GB373017A GB23236/31A GB2323631A GB373017A GB 373017 A GB373017 A GB 373017A GB 23236/31 A GB23236/31 A GB 23236/31A GB 2323631 A GB2323631 A GB 2323631A GB 373017 A GB373017 A GB 373017A
- Authority
- GB
- United Kingdom
- Prior art keywords
- temperature
- per cent
- cooling
- alloy
- maintained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Alloy steels containing a precipitation hardening element, e.g. Cu Ti B Zr during cooling from a high temperature, e.g. the working temperature, are maintained at a predetermined temperature (200-800 DEG C.) to increase the hardness and strength by precipitation hardening. The cooling apparatus may be as described in Specification 358,785. In the case of copper alloy, the alloy is allowed to cool from its production temperature to 500 DEG C. and then maintained at 500 DEG C. for a few hours. The parts may be fed in on a conveyer to the cooling bed with insulated bottom and heat protecting hood. The sections may be covered with sand &c. as desired. After hardening rapid cooling by air, steam, or water may be used and gas burners and fresh air inlets for heating or cooling any part locally is provided, e.g. a steel containing 0,17 per cent C, 0,38 per cent Si, 1,2 per cent Mn, and 0,75 per cent Cu was slowly cooled from the rolling temperature down to 450 DEG and kept there for 20 hours and was then quickly cooled to hand temperature.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE373017X | 1930-08-23 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB373017A true GB373017A (en) | 1932-05-19 |
Family
ID=6335549
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB23236/31A Expired GB373017A (en) | 1930-08-23 | 1931-08-18 | Process and apparatus for the heat treatment of bodies produced at high temperatures |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB373017A (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2871117A (en) * | 1956-07-18 | 1959-01-27 | Union Carbide Corp | Low alloy ferritic steel for high temperature application |
-
1931
- 1931-08-18 GB GB23236/31A patent/GB373017A/en not_active Expired
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2871117A (en) * | 1956-07-18 | 1959-01-27 | Union Carbide Corp | Low alloy ferritic steel for high temperature application |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB936872A (en) | Improvements in or relating to a process of heat treating austenitic stainless steel and austenitic stainless steels whenever prepared by the aforesaid process | |
GB373017A (en) | Process and apparatus for the heat treatment of bodies produced at high temperatures | |
GB924948A (en) | Temper resistant steels and die blocks made therefrom | |
JPS55131126A (en) | Production of modified by low alloy containing boron high tensile steel plate | |
GB375792A (en) | Improvements relating to processes for improving iron-boron alloys | |
GB782356A (en) | Improvements in or relating to the manufacture of steel bars | |
GB669118A (en) | Heat treatment of strip metal | |
SU432212A1 (en) | METHOD OF THERMAL TREATMENT OF LARGE-SIZE PRODUCTS FROM STEELS OF MARTENIETIC AND MARTENSITO-FERRITE CLASSES | |
JPS54104425A (en) | Heat treating method for high chromium white cast iron | |
GB666265A (en) | Improvements in or relating to alloy steel | |
SU749914A1 (en) | Method of thermal treatment of high-streength corrosion-resistant martensite steels | |
SU55345A1 (en) | High-speed chrome-molybdenum-vanadium steel | |
US1086459A (en) | Process for the manufacture of armor-plates. | |
GB386665A (en) | Improvements in the manufacture of hardened iron and steel alloy articles | |
GB643367A (en) | Improvements in or relating to the thermal treatment of steel and products thereof | |
GB1062754A (en) | Process for producing steel pipes for low temperatures | |
SU988884A1 (en) | Method for heat treating stainless martensite-ageing steels | |
SU423857A1 (en) | METHOD OF HEAT TREATMENT OF STEEL PRODUCTS | |
SU28020A1 (en) | The method of processing of white cast iron | |
GB781027A (en) | Improved process for the manufacture of piston rings | |
GB768207A (en) | Improvements in or relating to the production of cast iron | |
SU73280A1 (en) | The method of manufacturing cast or forged rolls for direct rolling | |
GB385584A (en) | Process for the production of phosphor-steels | |
SU151366A1 (en) | Durable cast iron | |
GB473331A (en) | Improvements in and relating to the heat treatment of austenitic nickel-chromium steels |