FR2252995A2 - Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure - Google Patents

Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure

Info

Publication number
FR2252995A2
FR2252995A2 FR7342852A FR7342852A FR2252995A2 FR 2252995 A2 FR2252995 A2 FR 2252995A2 FR 7342852 A FR7342852 A FR 7342852A FR 7342852 A FR7342852 A FR 7342852A FR 2252995 A2 FR2252995 A2 FR 2252995A2
Authority
FR
France
Prior art keywords
mixt
sintering
prepd
over
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR7342852A
Other languages
French (fr)
Other versions
FR2252995B2 (en
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ACTIVITE ATOM AVANCE
Original Assignee
ACTIVITE ATOM AVANCE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ACTIVITE ATOM AVANCE filed Critical ACTIVITE ATOM AVANCE
Priority to FR7342852A priority Critical patent/FR2252995A2/en
Priority to CH603574A priority patent/CH588426A5/xx
Priority to AU68555/74A priority patent/AU498289B2/en
Priority to DE2422416A priority patent/DE2422416A1/en
Priority to CA199,582A priority patent/CA1028363A/en
Priority to IT2254274A priority patent/IT1022031B/en
Priority to GB2158774A priority patent/GB1438602A/en
Priority to NO741794A priority patent/NO143151C/en
Priority to JP49053953A priority patent/JPS5048004A/ja
Publication of FR2252995A2 publication Critical patent/FR2252995A2/en
Priority to US05/793,341 priority patent/US4119469A/en
Application granted granted Critical
Publication of FR2252995B2 publication Critical patent/FR2252995B2/fr
Granted legal-status Critical Current

Abstract

Insulating ceramics passive to molten corrosive metals, e.g. Al and steel, and resistant to repeated heat-shocks, are prepd. by (1) mixing finely powdered oxides of Gp. III and Gp. IV elements, (2) sintering pt. of powder mixt. under high temp. and press., (3) comminuting sintered matl., (4) mixing comminuted matl. with balance of powder, (5) stirring after adding 0.1-6 wt.% Gp. IA fluoride, and (6) quickly vibrating in a mould, followed by (7) sintering vibrated mixt. without over-press. for 1 to several hrs. at 850-1350 degrees C under a controlled atmos. pref. H2 or a neutral atmos. Porosity of ceramic can be increased by admixing finely powdered mixt. before sintering with >35 wt.% (w.r.t. total mixt) compact grains of Gp. III and IV oxides. Specif. grains and fine powder consists of same oxide, pref. Al2O3, have French standard screen mesh sizes 22 and 17 resp. and are sintered in air at 1350 degrees C.
FR7342852A 1973-05-18 1973-11-30 Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure Granted FR2252995A2 (en)

Priority Applications (10)

Application Number Priority Date Filing Date Title
FR7342852A FR2252995A2 (en) 1973-11-30 1973-11-30 Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure
AU68555/74A AU498289B2 (en) 1973-05-18 1974-05-03 Porous insulating sintered ceramic substances
CH603574A CH588426A5 (en) 1973-05-18 1974-05-03
CA199,582A CA1028363A (en) 1973-05-18 1974-05-09 Controlled porosity insulating ceramics and related sintering process
DE2422416A DE2422416A1 (en) 1973-05-18 1974-05-09 INSULATING CERAMICS WITH CONTROLLED POROSITY AND SINTER MANUFACTURING PROCESS
IT2254274A IT1022031B (en) 1973-11-30 1974-05-10 INSULATING CERAMICS WITH CONTROLLED POROSITY AND THEIR PREPARATION PROCEDURE FOR SINTERING
GB2158774A GB1438602A (en) 1973-05-18 1974-05-15 Method of preparing ceramic substances by sintering
NO741794A NO143151C (en) 1973-05-18 1974-05-16 PROCEDURE FOR THE MANUFACTURE OF CERAMIC INSULATION MATERIAL
JP49053953A JPS5048004A (en) 1973-05-18 1974-05-16
US05/793,341 US4119469A (en) 1973-05-18 1977-05-03 Insulating ceramic substances having controlled porosity and the method for preparing them by sintering

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
FR7342852A FR2252995A2 (en) 1973-11-30 1973-11-30 Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure

Publications (2)

Publication Number Publication Date
FR2252995A2 true FR2252995A2 (en) 1975-06-27
FR2252995B2 FR2252995B2 (en) 1980-06-20

Family

ID=9128563

Family Applications (1)

Application Number Title Priority Date Filing Date
FR7342852A Granted FR2252995A2 (en) 1973-05-18 1973-11-30 Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure

Country Status (2)

Country Link
FR (1) FR2252995A2 (en)
IT (1) IT1022031B (en)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2497684A1 (en) * 1981-01-09 1982-07-16 Aikoh Co Filtering medium for liq. - comprises sintered body of high alumina bonded with lithium fluoride or oxide
EP0191053A1 (en) * 1984-07-23 1986-08-20 Norton Company Refractory cement
FR2686081A1 (en) * 1992-01-14 1993-07-16 Prod Cellulosiques Isolants PROCESS FOR THE MANUFACTURE OF AN INSULATING REFRACTORY MATERIAL, RIGID AND WITH HIGH OPEN POROSITY, AND MATERIAL THUS OBTAINED.

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2497684A1 (en) * 1981-01-09 1982-07-16 Aikoh Co Filtering medium for liq. - comprises sintered body of high alumina bonded with lithium fluoride or oxide
EP0191053A1 (en) * 1984-07-23 1986-08-20 Norton Company Refractory cement
EP0191053A4 (en) * 1984-07-23 1988-04-06 Norton Co Refractory cement.
FR2686081A1 (en) * 1992-01-14 1993-07-16 Prod Cellulosiques Isolants PROCESS FOR THE MANUFACTURE OF AN INSULATING REFRACTORY MATERIAL, RIGID AND WITH HIGH OPEN POROSITY, AND MATERIAL THUS OBTAINED.
WO1993014045A1 (en) * 1992-01-14 1993-07-22 Produits Cellulosiques Isolants - Procelis Method for the fabrication of a refractory insulating rigid material with high open porosity, and material thus obtained

Also Published As

Publication number Publication date
IT1022031B (en) 1978-03-20
FR2252995B2 (en) 1980-06-20

Similar Documents

Publication Publication Date Title
GB1406571A (en) Method for producing a sintered silicon mitride base ceramic and said ceramic product
GB1126614A (en) Material suitable for casting and process of casting refractory material
FR2229663A1 (en) Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure
FR2252995A2 (en) Insulating ceramic having controlled porosity - prepd. by sinter process comprising final sintering without over-pressure
US3116146A (en) Method for sintering tungsten powder
GB1264087A (en)
JPS5757804A (en) Production of honeycomb-shaped molding made of metal
US4119469A (en) Insulating ceramic substances having controlled porosity and the method for preparing them by sintering
US3679444A (en) Control of shrinkage and growth of silicon oxynitride bodies
JP2786719B2 (en) Method for producing rare earth oxide sintered body
JPS5918165A (en) Manufacture of silicon nitride sintered body
GB1093726A (en) Improvements in and relating to permanent moulds for the casting of metals
US2979399A (en) Preparation of compacts made from uranium and beryllium by sintering
JPS61215253A (en) Chromium oxide base ceramic material
GB1447518A (en) Metal-casting components
Yao et al. Sintering of Tungsten Metal Powder
JPS6380857A (en) Sintered body for crushing instrument
JPS61227908A (en) Preparation of raw material powder for sintered silicon nitride
KR950014356B1 (en) Method of manufacturing composite materials of iron-siliconcarbide
Birchall et al. ADVANCED STRUCTURAL CERAMICS- CRITICAL NEEDS
JP2563782B2 (en) Method for manufacturing silicon carbide based jig for semiconductor manufacturing
JPS61281801A (en) Manufacture of powder metallurgical product
JPS6479009A (en) Aluminium nitride powder
JPH07309669A (en) Low heat-conductive silicon nitride sintered body by direct nitriding method having two kinds of particle distribution and its production
JPS62113769A (en) Manufacture of silicon nitride sintered body