ES355811A1 - A method of constructing or repairing refractory linings or lining bodies - Google Patents
A method of constructing or repairing refractory linings or lining bodiesInfo
- Publication number
- ES355811A1 ES355811A1 ES355811A ES355811A ES355811A1 ES 355811 A1 ES355811 A1 ES 355811A1 ES 355811 A ES355811 A ES 355811A ES 355811 A ES355811 A ES 355811A ES 355811 A1 ES355811 A1 ES 355811A1
- Authority
- ES
- Spain
- Prior art keywords
- lining
- sawdust
- constructing
- refractory linings
- lining bodies
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
A refractory material having the following percentage composition by weight. Sintered magnesia 2À0-6À0 mm. 15%, 0-0À7 mm. 60%, 0-0À1 mm. 20%, disodium phosphate 5%, together with between 6 and 12%, preferably 10% of water is used to form a refractory lining or lining body or a repair for such a lining or lining body. A porous coating of the following composition, sintered magnesia 2À5-5À0 mm. 10%, 0-0À7 mm. 55%, 0-0À1 mm. 15%, sawdust 15%, disodium phosphate 5% is then applied to its top surface, the sawdust being burnt out to form the pores. Alternatively a foaming agent, a granular plastics material or an inorganic fibrous material may replace the sawdust. The pre-forming substances may comprise between 10 and 20% by weight of the coating mass.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AT724467A AT274872B (en) | 1967-08-04 | 1967-08-04 | Process for building up or repairing refractory linings or lining bodies |
Publications (1)
Publication Number | Publication Date |
---|---|
ES355811A1 true ES355811A1 (en) | 1969-12-16 |
Family
ID=3594095
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES355811A Expired ES355811A1 (en) | 1967-08-04 | 1968-07-05 | A method of constructing or repairing refractory linings or lining bodies |
Country Status (5)
Country | Link |
---|---|
AT (1) | AT274872B (en) |
DE (1) | DE1771654A1 (en) |
ES (1) | ES355811A1 (en) |
FR (1) | FR1582587A (en) |
GB (1) | GB1223048A (en) |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2523993C3 (en) * | 1975-05-30 | 1985-08-08 | Sumitomo Metal Industries, Ltd., Osaka | Refractory repair material for blast furnaces |
SE430883B (en) * | 1976-09-27 | 1983-12-19 | Quigley Co | PROCEDURE TO SEPARATE AND EXTEND THE LIFE OF BASIC ELVENTIVE CALLS IN BASIC OXYGEN Ovens |
DE3119548C1 (en) * | 1981-05-16 | 1982-12-09 | Chamotte- u. Tonwerk Kurt Hagenburger, 6719 Hettenleidelheim | Wear layer of a metallurgical vessel lined with permanent lining with a layer not sintered towards the permanent lining |
US4400335A (en) * | 1981-12-15 | 1983-08-23 | Hoganas Ab | Process for repairing refractory linings |
DE3306423A1 (en) * | 1983-02-24 | 1984-08-30 | Didier-Werke Ag, 6200 Wiesbaden | UNBURNED FIRE-RESISTANT COMPONENT IN THE FORM OF A PLATE FOR THE LOST LINING OF METALLURGICAL VESSELS |
FR2671796B1 (en) * | 1991-01-17 | 1994-01-07 | Vesuvius France Sa | INSULATING MONOLITH REFRACTORY MATERIAL - PRODUCTION PROCESS AND PART ACCORDING TO THE PROCESS. |
-
1967
- 1967-08-04 AT AT724467A patent/AT274872B/en active
-
1968
- 1968-06-21 DE DE19681771654 patent/DE1771654A1/en active Pending
- 1968-07-05 ES ES355811A patent/ES355811A1/en not_active Expired
- 1968-08-01 GB GB36775/68A patent/GB1223048A/en not_active Expired
- 1968-08-02 FR FR1582587D patent/FR1582587A/fr not_active Expired
Also Published As
Publication number | Publication date |
---|---|
AT274872B (en) | 1969-10-10 |
FR1582587A (en) | 1969-10-03 |
GB1223048A (en) | 1971-02-17 |
DE1771654A1 (en) | 1972-02-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES377475A1 (en) | Wear resistant, textured resinous compositions | |
GB1292156A (en) | Furnace and float tanks walls and parts thereof | |
DK233486A (en) | FIRE-PROPERTY WOOD-CONTAINING COMPOSITION MATERIALS, PARTS IN THE FORM OF PLATES, AND PROCEDURES FOR MANUFACTURING THIS | |
ES355811A1 (en) | A method of constructing or repairing refractory linings or lining bodies | |
SE7906086L (en) | PROCEDURE FOR THE PREPARATION OF POWDER-EASY, LIQUID FLUIDIZABLE SULFUR SULFUR MIXTURE | |
ES419437A1 (en) | Method of repairing refractory walls and a gunning composition for use in the method | |
SE7507228L (en) | PROCEDURE FOR THE PRODUCTION OF WITH A HYDRAULIC BINDER PREFERREDLY CEMENT, BOUND WOODEN MATERIALS, SPECIAL PLATE. | |
DE3063483D1 (en) | Combustible compositions and process for their production | |
ES460941A1 (en) | Cementitous composition | |
GB1216171A (en) | Method of manufacturing flat or curved units, wall panels or the like | |
ATE93763T1 (en) | STRUCTURING A MOLD SURFACE. | |
NL176088B (en) | METHOD FOR USING A STEEL CONVERTER AND A STEEL CONVERTER TO BE USED WITH THIS | |
GB1141073A (en) | A non-slip surface and method for making same | |
GB701802A (en) | Improvements relating to the manufacture of bricks or blocks, slabs and the like | |
GB380369A (en) | Improvements in or relating to bricks, tiles and the like | |
GB1160029A (en) | A New and Improved Cement Composition | |
ES451052A1 (en) | Porous lightweight particulate aggregates and process of manufacture | |
US3563790A (en) | Open-top porous container having sealed exterior surface | |
SE8105208L (en) | HEATING OR LIKE WITH ELLASTIC FOOD | |
US2460347A (en) | Protection of furnaces from slag | |
NL7103187A (en) | Low density aggregates for cement compsn | |
SU479623A1 (en) | Fire retardant wood coating | |
GB888857A (en) | Improvements in or relating to a composition suitable for lining casting moulds and hot tops | |
GB1085977A (en) | Refractory and method of making | |
GB485511A (en) | Improvements relating to the manufacture of plastic bricks, blocks, slabs, tiles and the like |