ES331184A1 - A process for the manufacture of refractory bricks, especially not calcinated, of magnesite-chromium and of chrome-magnesium. (Machine-translation by Google Translate, not legally binding) - Google Patents

A process for the manufacture of refractory bricks, especially not calcinated, of magnesite-chromium and of chrome-magnesium. (Machine-translation by Google Translate, not legally binding)

Info

Publication number
ES331184A1
ES331184A1 ES0331184A ES331184A ES331184A1 ES 331184 A1 ES331184 A1 ES 331184A1 ES 0331184 A ES0331184 A ES 0331184A ES 331184 A ES331184 A ES 331184A ES 331184 A1 ES331184 A1 ES 331184A1
Authority
ES
Spain
Prior art keywords
chromium
magnesite
translation
manufacture
machine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
ES0331184A
Other languages
Spanish (es)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
OSTERREICHISCH - AMERIKANISCHE MAGNESIT AG
Osterreichisch Amerikanische Magnesit AG
Original Assignee
OSTERREICHISCH - AMERIKANISCHE MAGNESIT AG
Osterreichisch Amerikanische Magnesit AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by OSTERREICHISCH - AMERIKANISCHE MAGNESIT AG, Osterreichisch Amerikanische Magnesit AG filed Critical OSTERREICHISCH - AMERIKANISCHE MAGNESIT AG
Publication of ES331184A1 publication Critical patent/ES331184A1/en
Expired legal-status Critical Current

Abstract

A process for the manufacture of refractory bricks, especially uncalcined, of magnesite-chromium and chromium-magnesite using a sintered material (simultaneous sintering) which is obtained without fusion by joint calcination of materials containing chromium oxide, especially chromite, with magnesia, optionally sintered magnesia or other natural or synthetic magnesium compounds that provide magnesium oxide when calcined, at temperatures of at least 1,700º C, preferably above 1,750º C, and in which the periclase and chromite particles are directly bonded between each other, characterized in that the sintered material in granulated form is mixed with 3 to 9%, preferably 4.5 to 5.5%, of tar and/or fish, especially hard fish or bitumen, or possibly similar mixtures of high hydrocarbons. molecular weight, and is configured in bricks. (Machine-translation by Google Translate, not legally binding)
ES0331184A 1965-10-07 1966-09-14 A process for the manufacture of refractory bricks, especially not calcinated, of magnesite-chromium and of chrome-magnesium. (Machine-translation by Google Translate, not legally binding) Expired ES331184A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
AT906765A AT263610B (en) 1965-10-07 1965-10-07 Process for the production of refractory, in particular unfired, magnesite chromium and chromium magnesite bricks

Publications (1)

Publication Number Publication Date
ES331184A1 true ES331184A1 (en) 1967-07-01

Family

ID=3610913

Family Applications (1)

Application Number Title Priority Date Filing Date
ES0331184A Expired ES331184A1 (en) 1965-10-07 1966-09-14 A process for the manufacture of refractory bricks, especially not calcinated, of magnesite-chromium and of chrome-magnesium. (Machine-translation by Google Translate, not legally binding)

Country Status (7)

Country Link
AT (1) AT263610B (en)
BE (1) BE686224A (en)
DE (1) DE1646837C2 (en)
ES (1) ES331184A1 (en)
GB (1) GB1112735A (en)
NL (1) NL6613689A (en)
NO (1) NO116795B (en)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2638458B2 (en) * 1976-08-26 1978-08-24 Magnesital-Feuerfest Gmbh, 4200 Oberhausen Unfired, refractory masses or stones for metallurgical vessels, based on chrome ore, sintered magnesia and hard pitch as a carbon-containing binder
DE4409078C1 (en) * 1994-03-17 1995-02-02 Veitsch Radex Ag Refractory brick
CN110746173B (en) * 2019-11-25 2022-03-25 和县明生环保材料有限责任公司 Preparation method of baking-free brick with good freezing resistance
CN111689768B (en) * 2020-06-28 2021-03-19 广西蒙娜丽莎新材料有限公司 Co-firing method of whole-body ink-jet black golden flower fully-polished brick and common archaized brick

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE667691C (en) * 1934-01-21 1938-11-18 Arthur Sprenger Refractory mass
DE891826C (en) * 1951-01-20 1953-10-01 Oesterr Amerikan Magnesit Process for the production of refractory material by melting magnesia

Also Published As

Publication number Publication date
DE1646837C2 (en) 1974-08-08
GB1112735A (en) 1968-05-08
BE686224A (en) 1967-02-01
NL6613689A (en) 1967-04-10
NO116795B (en) 1969-05-19
AT263610B (en) 1968-07-25
DE1646837B1 (en) 1971-08-26

Similar Documents

Publication Publication Date Title
ES331184A1 (en) A process for the manufacture of refractory bricks, especially not calcinated, of magnesite-chromium and of chrome-magnesium. (Machine-translation by Google Translate, not legally binding)
Gutt et al. Studies of the role of calcium sulphate in the manufacture of Portland cement clinker
ES311765A1 (en) A procedure for the manufacture of magnesia calcinated on the basis of low porosity. (Machine-translation by Google Translate, not legally binding)
ES372370A1 (en) A particles kaolin based ceramic tile containing granite felospar and hard alumin
ES331244A1 (en) A process for the manufacture of magnesite-chrome and chrome-magnesite bricks refractory and calcinated. (Machine-translation by Google Translate, not legally binding)
GB1001928A (en) Tar-bonded basic refractories
ES377265A1 (en) Process of manufacturing refractory magnesia-chrome and chrome-magnesia bricks
ES325388A1 (en) A procedure for the manufacture of bricks and refractory masses not calcinated. (Machine-translation by Google Translate, not legally binding)
ES413829A1 (en) Fired refractory brick
SU389059A1 (en) CHARGE FOR FIRE FIGHTING? SIG1 -.- ZNAYAPATENT | 10-TSH; .-: GOGSh: BIBLIO; : ^ - IA I
GB1300714A (en) Refractories with a non-aqueous bond
ES393962A1 (en) Producing refractory material
GB1058615A (en) Process for the manufacture of ceramic products
SU431137A1 (en) MINE
GB430036A (en) Improvements in and relating to the production of refractory material and bodies
ES330178A1 (en) Procedure for the manufacture of molded bodies. (Machine-translation by Google Translate, not legally binding)
GB1130383A (en) Refractory composition for use in repairing furnaces
SU771064A1 (en) Refractory mass
GB1428641A (en) Sintering inhibitor for fused mgo grain
GB1137831A (en) Refractory materials
ES312058A1 (en) A procedure for the manufacture of refractory bricks. (Machine-translation by Google Translate, not legally binding)
ES438144A1 (en) A method for the production of refractory bodies. (Machine-translation by Google Translate, not legally binding)
GB1407240A (en) Refractory shapes
ES374899A1 (en) A procedure to produce magnesia calcinated in a substantially complete mode, with high density and low porosity. (Machine-translation by Google Translate, not legally binding)
FR2233297A1 (en) Pure synthetic mullite prodn - as powder or shaped bodies