ES249049A1 - Procedure for obtaining steel molded to manganese of austenic structure (Machine-translation by Google Translate, not legally binding)
- Google Patents
Procedure for obtaining steel molded to manganese of austenic structure (Machine-translation by Google Translate, not legally binding)
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by IndividualfiledCriticalIndividual
Priority to ES0249049ApriorityCriticalpatent/ES249049A1/en
Publication of ES249049A1publicationCriticalpatent/ES249049A1/en
Method for obtaining manganese-molded steel of austenitic structure, characterized in that, after the iron is subjected to melting in an electric furnace, together with a composition composed of carbon in a concentration ranging from 0.9 to 1.1 percent, silicon in maximum concentration of 0.5 percent, manganese in concentration ranging from 7 to 9 percent, phosphorus in maximum concentration of 0.06 percent and sulfur in concentration also maximum of 0.06 percent, then proceeds to a subsequent special treatment of the resulting material by means of a tempering phase at a temperature of 1,050 degrees, subjecting said material to the action of a muffle furnace or reconcentrator. (Machine-translation by Google Translate, not legally binding)
ES0249049A1959-04-291959-04-29Procedure for obtaining steel molded to manganese of austenic structure (Machine-translation by Google Translate, not legally binding)
ExpiredES249049A1
(en)
A procedure for manufacturing steel in electric oven by replacing scrap by ferreos products (Machine-translation by Google Translate, not legally binding)