ES1295179U - Una placa de construcción compuesta principalmente por residuos municipales - Google Patents
Una placa de construcción compuesta principalmente por residuos municipales Download PDFInfo
- Publication number
- ES1295179U ES1295179U ES202231420U ES202231420U ES1295179U ES 1295179 U ES1295179 U ES 1295179U ES 202231420 U ES202231420 U ES 202231420U ES 202231420 U ES202231420 U ES 202231420U ES 1295179 U ES1295179 U ES 1295179U
- Authority
- ES
- Spain
- Prior art keywords
- weight
- municipal waste
- base layer
- construction plate
- polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Placa de construcción compuesta principalmente por residuos municipales, caracterizada por el hecho de estar compuesta de una capa de base (1) y de dos capas de recubrimiento (2), siendo que la capa de base (1) contiene una mezcla triturada comprimida de residuos municipales desintegrados, homogeneizados y compactados, que comprenden entre el 5 y el 65% del peso: celulosa química, entre el 20 y el 75% del peso: PE-LD -polietileno de bajo peso- y/o PE-HD -polietileno de alto peso-, entre el 0,05 y el 15% del peso: PET -tereftalato de polietileno-, entre el 0,05 y el 5% del peso: PA -poliamida-, entre el 0,05 y el 5% del peso: POM -poliacetal-, entre el 0,05 y el 5% del peso: PP -polipropileno-, entre el 0,05 y el 40% del peso: material de fibra de madera y hasta el 5% del peso en partículas de polvo de los residuos municipales resultantes de su desintegración, habiendo pasado los residuos municipales por un tamiz con un diámetro de malla de 10 a 50 mm; siendo que la capa de base (1) está provista de una capa de recubrimiento (2) en cada lado y que al menos una de las capas de recubrimiento (2) está empapelada en el exterior (3).
Description
DESCRIPCIÓN
UNA PLACA DE CONSTRUCCIÓN COMPUESTA PRINCIPALMENTE POR RESIDUOS
MUNICIPALES
ÁREA DE TECNOLOGÍA
La solución técnica es una placa de construcción adecuada para uso en el sector de la construcción. Se compone principalmente de residuos municipales.
SITUACIÓN ACTUAL DE LA TECNOLOGÍA
Hasta ahora se han conocido placas de construcción hechas de material procedente de la madera, unido con cola. Su desventaja es que tienden a absorber la humedad y a hincharse, lo cual conlleva una pérdida de resistencia.
También es conocida la producción de placas de revestimiento a partir de yeso y mezclas de aglomerado y de cemento. Estas placas de construcción se utilizan como placas de revestimiento y debido a su baja resistencia y la alta capacidad de absorción de agua se destinan a usos especiales.
También se conocen placas de construcción fabricadas a partir de un residuo específico postindustrial y post-consumo, que es un envoltorio de papel laminado con al menos una cara recubierta de una película de plástico tipo TETRAPAK. Sin embargo, estos residuos representan solo un pequeño porcentaje del volumen total de residuos y su clasificación es laboriosa y costosa, de modo que se encarece su producción.
Las soluciones existentes son muy complejas y cuanto más complejas, menos económicas.
LA ESENCIA DE LA SOLUCIÓN TÉCNICA
Las desventajas indicadas se eliminan en gran medida mediante la placa de construcción compuesta principalmente por residuos municipales, según la presente solución técnica, cuya esencia reside en que consta de una capa de base y de al menos dos capas de recubrimiento.
La capa de base contiene una mezcla triturada comprimida de residuos municipales desintegrados, homogeneizados y compactados, que primero se tritura, se mezcla y tamiza a
través de un tamiz de malla de 10 a 50 mm. Para la fabricación de la placa de construcción se utilizarán residuos municipales, preferiblemente libres de cenizas grandes, piedras, arcilla y componentes similares que complicarían la producción. Sin embargo, pequeñas cantidades de estas impurezas no causan problemas. Por tanto, se pueden utilizar incluso residuos municipales sin clasificar, lo cual representa una ventaja económica.
Los residuos municipales usados contienen un porcentaje de peso según la siguiente composición:
Celulosa química de 5 a 65%
PE-LD - polietileno de bajo peso
y/o PE-HD - polietileno de alto peso de 20 a 75%
PET - tereftalato de polietileno de 0,05 a 15%
PA - poliamida de 0,05 a 5%
POM - poliacetal de 0,05 a 5%
PP - polipropileno de 0,05 a 5%
Material de fibra de madera de 0,05 a 40%
Partículas de polvo de los residuos municipales hasta el 5%
A partir de residuos municipales se fabrica mediante prensado en caliente la capa base, que ya se está recubriendo por ambos lados con una capa durante el proceso de prensado. Al menos una de las capas de recubrimiento llevará aplicado un papel en su exterior. La capa de recubrimiento añade resistencia al compactado, así como apariencia y suavidad a la placa de construcción.
Es significativo que la capa de recubrimiento sea una película a base de polietileno PE-HD o polietileno PE-LD.
La solución técnica también se basa en que la capa base de la placa de construcción contiene un relleno antibacteriano.
Es significativo que el grosor de la placa de construcción es de 6 a 25 mm.
También es significativo que la placa de construcción toma la forma de un rectángulo de entre 500 y 5000 mm de largo y 500 y 3000 mm de ancho.
Es significativo que los bordes de la placa de construcción están recubiertos con una capa protectora contra la humedad y/o el moho, consistente en una impregnación hidrófuga y/o antibacteriana.
También es significativo que sus bordes están provistos de cinta protectora.
Para ir finalizando, pero no por ello menos significativo, es que la placa de construcción está provista en uno o en ambos lados de molduras continuas y/o molduras en distribución de baldosas, cuya profundidad es hasta 5 mm.
Por último, es significativo que el peso específico de la placa de construcción sea de 750-1150 kg/m3.
DESCRIPCIÓN DE LOS GRÁFICOS
La solución técnica se explicará con más detalle mediante dibujos que muestran una placa de construcción compuesta principalmente por residuos municipales según esta solución técnica.
La fig. 1 muestra una sección a través de la placa de construcción. Se observa una capa de base, compuesta principalmente por residuos municipales, y una capa de recubrimiento inferior y superior. La capa de recubrimiento superior además está cubierta con una capa de papel.
La fig. 2 muestra un plano de planta de la placa de construcción. Se muestran las molduras continuas que conforman la placa, así como las tiras protectoras de las que están provistos todos sus bordes.
La fig. 3 muestra un plano de planta de la placa de construcción. Se muestran las molduras en distribución de baldosas que conforman la placa.
EJEMPLOS DE REALIZACIÓN DE LA SOLUCIÓN TÉCNICA
El objetivo es producir placas de construcción que sean sencillas y económicas de fabricar. A la vez, el objetivo también es eliminar residuos municipales de forma barata. Por tanto, se decide fabricar placas de construcción compuestas principalmente por residuos municipales según esta solución técnica.
Para la producción de la capa base 1 de la placa de construcción se utilizan residuos municipales con la siguiente composición en porcentaje en peso:
Celulosa química 41%
PE-LD - polietileno de bajo peso 12%
y/o PE-HD - polietileno de alto peso 19%
PET - tereftalato de polietileno 4%
PA - poliamida 3%
POM - poliacetal 4%
PP - polipropileno 1%
Material de fibra de madera 13%
Partículas de polvo de los residuos municipales 3%
Además, para la realización de las capas de recubrimiento 2, se recubre por ambos lados la capa base 1 -la placa de construcción- con una película de PE-HD de 1 mm de espesor, formando las capas de recubrimiento 2.
Los residuos municipales se trituran y se tamizan a través de un tamiz de malla de 40 mm. A continuación, se mezcla y se le añade un relleno antibacteriano. Seguidamente, se extiende sobre la lámina de PE-HD, de modo que la altura de la capa de residuos municipales sea de 20 a 24 mm. Los residuos municipales así estratificados se cubren a continuación con una segunda capa de recubrimiento 2, también una lámina de PE-HD, y se prensan a una temperatura de 200 °C a una presión de 0,5 N/mm2. El molde está provisto de salientes en ambos lados para que al prensar el producto se formen las molduras en distribución de baldosas 5. Las molduras 5 refuerzan el producto. Tras el moldeado se recubren ambas capas de recubrimiento 2 de la lámina PE-HD con papel 3, que se pega sobre ellas. El producto fabricado de esta manera tiene un grosor de 15 mm y se recorta al formato elegido, es decir, 400 mm x 300 mm. Los bordes del producto están recubiertos contra la humedad y el moho con una capa protectora de impregnación líquida adecuada, hidrófuga y antibacteriana. Posteriormente, los bordes del producto se cubren con una cinta protectora de película de 4 PE-HD. La placa de construcción elaborada de esta manera tiene un peso específico de 950 kg/m3.
POSIBILIDAD DE USO INDUSTRIAL
Esta solución técnica puede aprovecharse en la industria de la construcción como material de construcción. También encuentra uso en la gestión de almacenes y en otros sectores industriales que utilicen placas de construcción estándares. Destaca por suficiente rigidez, resistencia mecánica, es higiénicamente segura y asequible. Al mismo tiempo, su producción elimina residuos municipales no deseados.
Claims (10)
1. Placa de construcción compuesta principalmente por residuos municipales, caracterizada por el hecho de estar compuesta de una capa de base (1) y de dos capas de recubrimiento (2), siendo que la capa de base (1) contiene una mezcla triturada comprimida de residuos municipales desintegrados, homogeneizados y compactados, que comprenden
entre el 5 y el 65% del peso: celulosa química,
entre el 20 y el 75% del peso: PE-LD —polietileno de bajo peso- y/o PE-HD —polietileno de alto peso-,
entre el 0,05 y el 15% del peso: PET —tereftalato de polietileno—,
entre el 0,05 y el 5% del peso: PA —poliamida—,
entre el 0,05 y el 5% del peso: POM —poliacetal—,
entre el 0,05 y el 5% del peso: PP —polipropileno—,
entre el 0,05 y el 40% del peso: material de fibra de madera
y hasta el 5% del peso en partículas de polvo de los residuos municipales resultantes de su desintegración, habiendo pasado los residuos municipales por un tamiz con un diámetro de malla de 10 a 50 mm; siendo que la capa de base (1) está provista de una capa de recubrimiento (2) en cada lado y que al menos una de las capas de recubrimiento (2) está empapelada en el exterior (3).
2. La placa de construcción según la reivindicación 1 se caracteriza por el hecho de ser la capa de recubrimiento (2) de polietileno PE-HD o de polietileno PE-LD.
3. La placa de construcción según la reivindicación 1 o 2 se caracteriza por el hecho de que la capa base (1) contiene relleno antibacteriano.
4. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que la capa base (1) está provista contra la humedad y el moho, por una o por ambas caras, de una impregnación hidrófuga y/o antibacteriana.
5. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que el espesor de la placa es de 6 a 25 mm.
6. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que tiene la forma de un rectángulo de entre 500 y 5000 mm de largo y 500 y 3
000 mm de ancho.
7. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que sus bordes están provistos de una capa protectora contra la humedad y/o el moho realizado por una impregnación hidrófuga y/o antibacteriana.
8. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que sus bordes están provistos de cinta protectora (4).
9. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que está provista en uno o en ambos lados de molduras continuas (5) y/o molduras en distribución de baldosas (5), cuya profundidad es hasta 5 mm.
10. La placa de construcción, según alguna de las reivindicaciones anteriores, se caracteriza por el hecho de que su peso específico es de 750-1150 kg/m3.