DK200401839A - Beton- og mörteladditiv, fremgangsmåde til fremstilling af dette og dels anvendelse, samt beton eller mörtel indeholdende dette - Google Patents
Beton- og mörteladditiv, fremgangsmåde til fremstilling af dette og dels anvendelse, samt beton eller mörtel indeholdende dette Download PDFInfo
- Publication number
- DK200401839A DK200401839A DK200401839A DKPA200401839A DK200401839A DK 200401839 A DK200401839 A DK 200401839A DK 200401839 A DK200401839 A DK 200401839A DK PA200401839 A DKPA200401839 A DK PA200401839A DK 200401839 A DK200401839 A DK 200401839A
- Authority
- DK
- Denmark
- Prior art keywords
- concrete
- mortar
- clay
- group
- additive
- Prior art date
Description
PATENTKRAV 1. Fremgangsmåde til fremstilling af et additiv til beton eller mørtel, hvorved en lerart omfattende lermineraler udvalgt fra smectitgruppen, vermiculitgruppen, og/eller chloritgruppen opslæmmes i vand i en mængde på 5-30, fortrinsvis 8-20 og mere fore¬ trukket 10-12 vægt% tørstof under omrøring og justering af pH til 6,5-8, fortrinsvis 7, til opnåelse af en konsistens, der er afpasset efter det doseringsudstyr, som anvendes til dosering af additivet ved blanding af beton eller mørtel, hvorefter blandingen henstår under omrøring til modning i 1-7 døgn, fortrinsvis 1-2 døgn, før anvendelse. 2. Fremgangsmåde ifølge krav 1, hvorved nævnte lerart indeholder 50-90, for¬ trinsvis 60-80, mere foretrukket 70-75 og specielt ca. 75 vægt% lermineraler udvalgt fra smectitgruppen, vermiculitgruppen og/eller chloritgruppen. 3. Fremgangsmåde ifølge krav 2, hvorved lermineraleme især er udvalgt fra smectitgruppen. 4. Fremgangsmåde ifølge krav 3, hvorved en væsentlig del af lermineralet, såsom 90-50, fortrinsvis 80-60 og især ca. 70 vægt%, er montmorillonit. 5. Fremgangsmåde ifølge krav 4, hvorved lerarten er et bentonit, især calcium- bentonit. 6. Fremgangsmåde ifølge krav 5, hvorved pH-værdien efter behov indstilles med svovlsyre, myresyre eller phosphorsyre eller med calciumhydroxid, natriumhydroxid eller natriumcarbonat. 7. Additiv til beton eller mørtel, omfattende en i 1-7 døgn, fortrinsvis 1-2 døgn, modnet og stabiliseret vandig opslæmning med en konsistens, der er afpasset efter det doseringsudstyr, som anvendes til dosering af additivet ved blanding af beton eller mørtel, og med et pH på 6,5-8, fortrinsvis 7, og indeholdende 5-30, fortrinsvis 8-20 og mere foretrukket 10-12 vægt% tørstof af en lerart omfattende lermineraler udvalgt fra smectitgruppen, vermiculitgruppen og/eller chloritgruppen. 8. Additiv ifølge krav 7, hvor nævnte lerart indeholder 50-90, fortrinsvis 60-80, mere foretrukket 70-75 og specielt ca. 75 vægt% lermineraler udvalgt ffa smectitgrup- pen, vermiculitgruppen og/eller chloritgruppen. 9. Additiv ifølge krav 8, hvor lermineraleme især er udvalgt fra smectitgruppen. 10. Additiv, hvor en væsentlig del af lermineralet, såsom 90-50, fortrinsvis 80-60 og især ca. 70 vægt%, er montmorillonit. 11. Additiv ifølge krav 10, hvor lerarten er et bentonit, især calciumbentonit. 12. Anvendelse af et additiv til beton eller mørtel, omfattende en i 1-7 døgn, for¬ trinsvis 1-2 døgn, modnet og stabiliseret vandig opslæmning med en konsistens, der er afpasset efter det doseringsudstyr, som anvendes til dosering af additivet ved blanding af beton eller mørtel, og med et pH på 6,5-8, fortrinsvis 7, og indeholdende 5-30, for¬ trinsvis 8-20 og mere foretrukket 10-12 vægt% tørstof af en lerart, omfattende lermine¬ raler udvalgt fra smectitgruppen, vermiculitgruppen og/eller chloritgruppen, i en mængde på 0,1-0,4, fortrinsvis 0,2-0,3 og især ca. 0,25 vægt% beregnet på tørstof¬ mængden af lerarten i forhold til pulvermængden (bindemiddelmængden) i betonen el¬ ler mørtlen. 13. Anvendelse ifølge krav 12, hvor nævnte lerart indeholder 50-90, fortrinsvis 60- 80, mere foretrukket 70-75 og specielt ca. 75 vægt% lermineraler udvalgt fra smectit¬ gruppen, vermiculitgruppen og/eller chloritgruppen. 14. Anvendelse ifølge krav 13, hvor lermineralet især er udvalgt fra smectitgrup¬ pen. 15. Anvendelse ifølge krav 14, hvor en væsentlig del af lermineralet, såsom 90-50, fortrinsvis 80-60 og især ca. 70 vægt%, er montmorillonit. 16. Anvendelse ifølge krav 15, hvor lerarten er bentonit, især calciumbentonit. 17. Beton, omfattende et additiv bestående af en i 1-7 døgn, fortrinsvis 1-2 døgn, modnet og stabiliseret vandig opslæmning med en konsistens, der er afpasset efter det doseringsudstyr, som anvendes til dosering af additivet ved blanding af beton eller mørtel, og med et pH på 6,5-8, fortrinsvis 7, og indeholdende 5-30, fortrinsvis 8-20 og mere foretrukket 10-12 vægt% tørstof af en lerart omfattende lermineraler udvalgt fra smectitgruppen, vcrmiculitgruppen og/eller chloritgruppen, foruden i beton eller mørtel sædvanligt anvendte komponenter valgt fra gruppen bestående af cement, andre tilsæt¬ ninger med puzzolaneffekt, såsom flyveaske og mikrosilica, sten, sand, fine mineralske stoffer uden puzzolaneffekt, additiver, såsom plastiflceringsmidler, superplastifice- ringsmidler og luftindblandingsmidler, samt vand, idet mængden af lerarten beregnet på tørstofindholdet deraf udgør 0,1-0,4, fortrinsvis 0,2-0,3 og især ca. 0,25 vægt% i forhold til pulvermængden (bindemiddelmængden) i betonen eller mørtlen. 18. Beton ifølge krav 17, hvor nævnte lerart indeholder 50-90, fortrinsvis 60-80, mere foretrukket 70-75 og specielt ca. 75 vægt% lermineraler udvalgt fra smectitgrup¬ pen, vermiculitgruppen og/eller chloritgruppen. 19. Beton ifølge krav 18, hvor lermineraleme er udvalgt fra smectitgruppen. 20. Beton ifølge krav 19, hvor en væsentlig del af lermineralet, såsom 90-50, for¬ trinsvis 80-60 og især ca. 70 vægt%, er montmorillonit. 21. Additiv ifølge krav 20, hvor lerarten er et bentonit, især calciumbentonit.