DE69708541D1 - Verfahren zur Aluminisierung einer Superlegierung - Google Patents

Verfahren zur Aluminisierung einer Superlegierung

Info

Publication number
DE69708541D1
DE69708541D1 DE69708541T DE69708541T DE69708541D1 DE 69708541 D1 DE69708541 D1 DE 69708541D1 DE 69708541 T DE69708541 T DE 69708541T DE 69708541 T DE69708541 T DE 69708541T DE 69708541 D1 DE69708541 D1 DE 69708541D1
Authority
DE
Germany
Prior art keywords
aluminizing
superalloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE69708541T
Other languages
English (en)
Other versions
DE69708541T2 (de
Inventor
Rodney George Wing
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chromalloy United Kingdom Ltd
Rolls Royce PLC
Original Assignee
Chromalloy United Kingdom Ltd
Rolls Royce PLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GBGB9615474.5A external-priority patent/GB9615474D0/en
Priority claimed from GBGB9626191.2A external-priority patent/GB9626191D0/en
Application filed by Chromalloy United Kingdom Ltd, Rolls Royce PLC filed Critical Chromalloy United Kingdom Ltd
Publication of DE69708541D1 publication Critical patent/DE69708541D1/de
Application granted granted Critical
Publication of DE69708541T2 publication Critical patent/DE69708541T2/de
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C10/00—Solid state diffusion of only metal elements or silicon into metallic material surfaces
    • C23C10/28—Solid state diffusion of only metal elements or silicon into metallic material surfaces using solids, e.g. powders, pastes
    • C23C10/34—Embedding in a powder mixture, i.e. pack cementation
    • C23C10/58—Embedding in a powder mixture, i.e. pack cementation more than one element being diffused in more than one step
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/028—Including graded layers in composition or in physical properties, e.g. density, porosity, grain size

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Physical Vapour Deposition (AREA)
  • Chemical Vapour Deposition (AREA)
DE69708541T 1996-07-23 1997-07-14 Verfahren zur Aluminisierung einer Superlegierung Expired - Fee Related DE69708541T2 (de)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB9615474.5A GB9615474D0 (en) 1996-07-23 1996-07-23 A method of platinum alluminising a superalloy
GBGB9626191.2A GB9626191D0 (en) 1996-12-18 1996-12-18 A metheod of aluminising a superalloy

Publications (2)

Publication Number Publication Date
DE69708541D1 true DE69708541D1 (de) 2002-01-10
DE69708541T2 DE69708541T2 (de) 2002-05-08

Family

ID=26309743

Family Applications (1)

Application Number Title Priority Date Filing Date
DE69708541T Expired - Fee Related DE69708541T2 (de) 1996-07-23 1997-07-14 Verfahren zur Aluminisierung einer Superlegierung

Country Status (9)

Country Link
US (1) US6080246A (de)
EP (1) EP0821076B1 (de)
JP (1) JP3996978B2 (de)
AU (1) AU713624B2 (de)
CA (1) CA2211149A1 (de)
DE (1) DE69708541T2 (de)
IL (1) IL121313A (de)
RU (1) RU2188250C2 (de)
UA (1) UA46752C2 (de)

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1036850A4 (de) * 1998-06-15 2003-05-02 Mitsubishi Heavy Ind Ltd Einkristall-legierung auf nickelbasis mit beschichtungsfilm zur verhinderung vonkristallisationsbruch
DE69821945T2 (de) 1998-11-10 2005-07-14 Alstom Technology Ltd Gasturbineteil
US6305077B1 (en) * 1999-11-18 2001-10-23 General Electric Company Repair of coated turbine components
US6830827B2 (en) 2000-03-07 2004-12-14 Ebara Corporation Alloy coating, method for forming the same, and member for high temperature apparatuses
US6843861B2 (en) * 2002-02-08 2005-01-18 General Electric Company Method for preventing the formation of secondary reaction zone in susceptible articles, and articles prepared by the method
US6929868B2 (en) 2002-11-20 2005-08-16 General Electric Company SRZ-susceptible superalloy article having a protective layer thereon
US6921582B2 (en) * 2002-12-23 2005-07-26 General Electric Company Oxidation-resistant coatings bonded to metal substrates, and related articles and processes
GB2401117A (en) * 2003-05-01 2004-11-03 Rolls Royce Plc A method of preventing aluminising and a mask to prevent aluminising
CN100554495C (zh) * 2003-05-30 2009-10-28 石川岛播磨重工业株式会社 反应抑制涂布方法
US7604726B2 (en) 2004-01-07 2009-10-20 Honeywell International Inc. Platinum aluminide coating and method thereof
FR2881439B1 (fr) * 2005-02-01 2007-12-07 Onera (Off Nat Aerospatiale) Revetement protecteur pour superalliage monocristallin
US8123872B2 (en) 2006-02-22 2012-02-28 General Electric Company Carburization process for stabilizing nickel-based superalloys
US7544424B2 (en) 2006-11-30 2009-06-09 General Electric Company Ni-base superalloy having a coating system containing a stabilizing layer
US7416790B2 (en) 2006-12-08 2008-08-26 General Electric Company Coating systems containing rhodium aluminide-based layers
US7989020B2 (en) * 2007-02-08 2011-08-02 Honeywell International Inc. Method of forming bond coating for a thermal barrier coating
US8968528B2 (en) * 2008-04-14 2015-03-03 United Technologies Corporation Platinum-modified cathodic arc coating
US8124246B2 (en) * 2008-11-19 2012-02-28 Honeywell International Inc. Coated components and methods of fabricating coated components and coated turbine disks
EP2239346A1 (de) 2009-04-09 2010-10-13 Siemens Aktiengesellschaft Schlickerzusammensetzung um eine Superlegierungskomponente zu aluminisieren
WO2010138096A1 (en) 2009-05-26 2010-12-02 Siemens Aktiengesellschaft Layered coating system with a mcralx layer and a chromium rich layer and a method to produce it
FR2961528B1 (fr) * 2010-06-18 2012-07-20 Snecma Procede d'aluminisation d'une surface avec depot prealable d'une couche de platine et de nickel
US8636890B2 (en) 2011-09-23 2014-01-28 General Electric Company Method for refurbishing PtAl coating to turbine hardware removed from service
JP5857794B2 (ja) * 2012-02-27 2016-02-10 株式会社Ihi 拡散層付き金属材料ならびにその製造方法
EP2937438A1 (de) * 2014-04-22 2015-10-28 Siemens Aktiengesellschaft Beschichtete Turbinenkomponente und Verfahren zur Bildung einer Beschichtung auf einer Turbinenkomponente
GB201707986D0 (en) 2017-05-18 2017-07-05 Rolls Royce Plc Coating for a nickel-base superalloy
US11970953B2 (en) * 2019-08-23 2024-04-30 Rtx Corporation Slurry based diffusion coatings for blade under platform of internally-cooled components and process therefor
FR3101643B1 (fr) * 2019-10-08 2022-05-06 Safran Piece d'aeronef en superalliage comprenant du rhenium et/ou du ruthenium et procede de fabrication associe
US11686208B2 (en) 2020-02-06 2023-06-27 Rolls-Royce Corporation Abrasive coating for high-temperature mechanical systems

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2207198B1 (de) * 1972-10-23 1976-08-20 Onera (Off Nat Aerospatiale)
US4528215A (en) * 1973-01-31 1985-07-09 Alloy Surfaces Company, Inc. Diffusion aluminizing of cobalt-base superalloys
US3999956A (en) * 1975-02-21 1976-12-28 Chromalloy American Corporation Platinum-rhodium-containing high temperature alloy coating
US3979273A (en) * 1975-05-27 1976-09-07 United Technologies Corporation Method of forming aluminide coatings on nickel-, cobalt-, and iron-base alloys
US4101714A (en) * 1977-03-31 1978-07-18 General Electric Company High temperature oxidation resistant dispersion strengthened nickel-chromium alloys
GB2009251B (en) * 1977-12-01 1982-08-18 Rolls Royce Coated metal part and the method of applying coating
US4820362A (en) * 1979-03-30 1989-04-11 Alloy Surfaces Company, Inc. Metal diffusion and composition
US4310574A (en) * 1980-06-20 1982-01-12 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Method of protecting a surface with a silicon-slurry/aluminide coating
US4374183A (en) * 1980-06-20 1983-02-15 The United States Of America As Represented By The Administrator, National Aeronautics And Space Administration Silicon-slurry/aluminide coating
US4526814A (en) * 1982-11-19 1985-07-02 Turbine Components Corporation Methods of forming a protective diffusion layer on nickel, cobalt, and iron base alloys
US5077141A (en) * 1984-12-06 1991-12-31 Avco Corporation High strength nickel base single crystal alloys having enhanced solid solution strength and methods for making same
DE3571149D1 (en) * 1985-03-13 1989-07-27 Gen Electric Yttrium and yttrium-silicon bearing nickel-base superalloys especially useful as compatible coatings for advanced superalloys
FR2638174B1 (fr) * 1988-10-26 1991-01-18 Onera (Off Nat Aerospatiale) Procede de protection de surface de pieces metalliques contre la corrosion a temperature elevee, et piece traitee par ce procede
US5498484A (en) * 1990-05-07 1996-03-12 General Electric Company Thermal barrier coating system with hardenable bond coat
US5139824A (en) * 1990-08-28 1992-08-18 Liburdi Engineering Limited Method of coating complex substrates
US5057196A (en) * 1990-12-17 1991-10-15 General Motors Corporation Method of forming platinum-silicon-enriched diffused aluminide coating on a superalloy substrate
US5334263A (en) * 1991-12-05 1994-08-02 General Electric Company Substrate stabilization of diffusion aluminide coated nickel-based superalloys
DE69304397T2 (de) * 1992-04-29 1997-01-16 Walbar Inc Verbessertes Verfahren zur Diffusionsbeschichtung und Produkte
GB9210683D0 (en) * 1992-05-19 1992-07-08 Rolls Royce Plc Multiplex aluminide-silicide coating
GB9218858D0 (en) * 1992-09-05 1992-10-21 Rolls Royce Plc High temperature corrosion resistant composite coatings
EP0654542B1 (de) * 1993-11-19 1999-03-31 Walbar Inc. Verbessertes Verfahren für eine mit Platingruppen-Silicid modifizierte Aluminid-Beschichtung und Produkte
US5650235A (en) * 1994-02-28 1997-07-22 Sermatech International, Inc. Platinum enriched, silicon-modified corrosion resistant aluminide coating
GB9426257D0 (en) * 1994-12-24 1995-03-01 Rolls Royce Plc Thermal barrier coating for a superalloy article and method of application
US5716720A (en) * 1995-03-21 1998-02-10 Howmet Corporation Thermal barrier coating system with intermediate phase bondcoat
US6066405A (en) * 1995-12-22 2000-05-23 General Electric Company Nickel-base superalloy having an optimized platinum-aluminide coating

Also Published As

Publication number Publication date
CA2211149A1 (en) 1998-01-23
EP0821076B1 (de) 2001-11-28
AU713624B2 (en) 1999-12-09
UA46752C2 (uk) 2002-06-17
JP3996978B2 (ja) 2007-10-24
JPH10168556A (ja) 1998-06-23
US6080246A (en) 2000-06-27
EP0821076A1 (de) 1998-01-28
RU2188250C2 (ru) 2002-08-27
IL121313A0 (en) 1998-01-04
AU3014497A (en) 1998-01-29
IL121313A (en) 2001-03-19
DE69708541T2 (de) 2002-05-08

Similar Documents

Publication Publication Date Title
DE69708541T2 (de) Verfahren zur Aluminisierung einer Superlegierung
DE69413346D1 (de) Verfahren zur Beschichtung einer Abzweigeleitung
DE69414496T2 (de) Verfahren zur Beschichtung einer Abzweigeleitung
DE69634194D1 (de) Verfahren zur bearbeitung einer oberfläche
DE69621335D1 (de) Verfahren zur herstellung einer membranhaltenden mikrostruktur
DE794839T1 (de) Verfahren zur beschichtung einer oberfläche
DE69823027D1 (de) Verfahren zur herstellung einer waschmittelzusammensetzung
DE69828198D1 (de) Verfahren zur herstellung einer thermoplastischen beschichtung
ATE353030T1 (de) Verfahren zur herstellung eines beschichteten katalysators
DE69502849D1 (de) Verfahren zur Herstellung einer versiegelbaren Dichtung
DE59607996D1 (de) Verfahren zur generierung einer contone-map
DE69801560T2 (de) Verfahren zur herstellung einer katalysatorzusammenstellung
DE69701890T2 (de) Verfahren zur herstellung einer abbindenden zusammensetzung
DE59710734D1 (de) Verfahren zur Regelung einer Gasturbogruppe
DE69701731T2 (de) Verfahren zur herstellung einer waschmittelzusammensetzung
DE69304509T2 (de) Verfahren zur Beschichtung einer Abzweigeleitung
DE19782013T1 (de) Verfahren zur Herstellung eines Strukturgliedes
DE69826249D1 (de) Verfahren zur aktivierungssicherung einer v5 schnittstelle
ATA170197A (de) Verfahren zur anpassung eines brennerbeheizten heizgerätes
DE59703321D1 (de) Verfahren zur Herstellung einer Beschichtung
DE69535398D1 (de) Verfahren zur herstellung einer d-n-carbamoyl-alpha-aminosäure
DE59808395D1 (de) Verfahren zur herstellung einer gebauten nockenwelle
DE69709398D1 (de) Verfahren zur herstellung einer waschmittelzusammensetzung
DE59712795D1 (de) Verfahren zur Prüfung einer Vielzahl von Produkten
DE948435T1 (de) Verfahren zur herstellung einer anzeige

Legal Events

Date Code Title Description
8364 No opposition during term of opposition
8339 Ceased/non-payment of the annual fee