DE69615012T2 - Erosions-korrosionsschutzschicht für hochtemperaturbauteile - Google Patents

Erosions-korrosionsschutzschicht für hochtemperaturbauteile

Info

Publication number
DE69615012T2
DE69615012T2 DE69615012T DE69615012T DE69615012T2 DE 69615012 T2 DE69615012 T2 DE 69615012T2 DE 69615012 T DE69615012 T DE 69615012T DE 69615012 T DE69615012 T DE 69615012T DE 69615012 T2 DE69615012 T2 DE 69615012T2
Authority
DE
Germany
Prior art keywords
high temperature
protective layer
corrosion protective
temperature components
erosion corrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE69615012T
Other languages
English (en)
Other versions
DE69615012D1 (de
Inventor
Wolfram Beele
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siemens AG
Original Assignee
Siemens AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Siemens AG filed Critical Siemens AG
Application granted granted Critical
Publication of DE69615012D1 publication Critical patent/DE69615012D1/de
Publication of DE69615012T2 publication Critical patent/DE69615012T2/de
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
    • C23C28/321—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer
    • C23C28/3215—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer at least one MCrAlX layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B18/00—Layered products essentially comprising ceramics, e.g. refractory products
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/04—Interconnection of layers
    • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
    • C23C14/06—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the coating material
    • C23C14/0682—Silicides
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
    • C23C28/3455—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer with a refractory ceramic layer, e.g. refractory metal oxide, ZrO2, rare earth oxides or a thermal barrier system comprising at least one refractory oxide layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
    • C23C4/10—Oxides, borides, carbides, nitrides or silicides; Mixtures thereof
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
    • F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or antivibration means on the blades or the members
    • F01D5/12—Blades
    • F01D5/28—Selecting particular materials; Particular measures relating thereto; Measures against erosion or corrosion
    • F01D5/288—Protective coatings for blades
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12014—All metal or with adjacent metals having metal particles
    • Y10T428/12028—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.]
    • Y10T428/12049—Nonmetal component
    • Y10T428/12056—Entirely inorganic
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12014—All metal or with adjacent metals having metal particles
    • Y10T428/12028—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.]
    • Y10T428/12063—Nonparticulate metal component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12014—All metal or with adjacent metals having metal particles
    • Y10T428/12028—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.]
    • Y10T428/12063—Nonparticulate metal component
    • Y10T428/12069—Plural nonparticulate metal components
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12014—All metal or with adjacent metals having metal particles
    • Y10T428/12028—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.]
    • Y10T428/12063—Nonparticulate metal component
    • Y10T428/12069—Plural nonparticulate metal components
    • Y10T428/12076—Next to each other
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12583—Component contains compound of adjacent metal
    • Y10T428/1259—Oxide
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12611—Oxide-containing component

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • Ceramic Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Turbine Rotor Nozzle Sealing (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
DE69615012T 1995-04-06 1996-04-01 Erosions-korrosionsschutzschicht für hochtemperaturbauteile Expired - Fee Related DE69615012T2 (de)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US08/417,945 US5740515A (en) 1995-04-06 1995-04-06 Erosion/corrosion protective coating for high-temperature components
PCT/EP1996/001432 WO1996031636A1 (en) 1995-04-06 1996-04-01 Erosion/corrosion protective coating for high-temperature components

Publications (2)

Publication Number Publication Date
DE69615012D1 DE69615012D1 (de) 2001-10-11
DE69615012T2 true DE69615012T2 (de) 2002-06-13

Family

ID=23656002

Family Applications (1)

Application Number Title Priority Date Filing Date
DE69615012T Expired - Fee Related DE69615012T2 (de) 1995-04-06 1996-04-01 Erosions-korrosionsschutzschicht für hochtemperaturbauteile

Country Status (13)

Country Link
US (1) US5740515A (de)
EP (1) EP0820535B1 (de)
JP (1) JP3464003B2 (de)
KR (1) KR19980703619A (de)
CN (1) CN1180126C (de)
CZ (1) CZ315797A3 (de)
DE (1) DE69615012T2 (de)
DK (1) DK0820535T3 (de)
ES (1) ES2162048T3 (de)
IN (1) IN187892B (de)
RU (1) RU2167220C2 (de)
UA (1) UA48169C2 (de)
WO (1) WO1996031636A1 (de)

Families Citing this family (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001521990A (ja) * 1997-11-03 2001-11-13 シーメンス アクチエンゲゼルシヤフト ＭｏＳｉ２含有層を製造するためのガスジェットＰＶＤ法
US6060177A (en) * 1998-02-19 2000-05-09 United Technologies Corporation Method of applying an overcoat to a thermal barrier coating and coated article
US6299988B1 (en) 1998-04-27 2001-10-09 General Electric Company Ceramic with preferential oxygen reactive layer
US6485848B1 (en) 1998-04-27 2002-11-26 General Electric Company Coated article and method of making
US6284390B1 (en) * 1998-06-12 2001-09-04 United Technologies Corporation Thermal barrier coating system utilizing localized bond coat and article having the same
WO2000025005A1 (de) * 1998-10-22 2000-05-04 Siemens Aktiengesellschaft Erzeugnis mit wärmedämmschicht sowie verfahren zur herstellung einer wärmedämmschicht
US6517960B1 (en) 1999-04-26 2003-02-11 General Electric Company Ceramic with zircon coating
US6444271B2 (en) * 1999-07-20 2002-09-03 Lockheed Martin Corporation Durable refractory ceramic coating
US6265080B1 (en) * 1999-12-22 2001-07-24 United Technologies Corporation Pest resistant molybdenum disilicide type materials
US20030152814A1 (en) * 2002-02-11 2003-08-14 Dinesh Gupta Hybrid thermal barrier coating and method of making the same
US7157151B2 (en) * 2002-09-11 2007-01-02 Rolls-Royce Corporation Corrosion-resistant layered coatings
EP1541810A1 (de) * 2003-12-11 2005-06-15 Siemens Aktiengesellschaft Verwendung einer Wärmedämmschicht für ein Bauteil einer Dampfturbine und eine Dampfturbine
EP1541808A1 (de) * 2003-12-11 2005-06-15 Siemens Aktiengesellschaft Turbinenbauteil mit Wärmedämmschicht und Erosionsschutzschicht
EP1734145A1 (de) * 2005-06-13 2006-12-20 Siemens Aktiengesellschaft Schichtsystem für ein Bauteil mit Wärmedämmschicht und metallischer Erosionsschutzschicht, Verfahren zur Herstellung und Verfahren zum Betreiben einer Dampfturbine
US8512871B2 (en) * 2006-05-30 2013-08-20 United Technologies Corporation Erosion barrier for thermal barrier coatings
US7989020B2 (en) * 2007-02-08 2011-08-02 Honeywell International Inc. Method of forming bond coating for a thermal barrier coating
FR2960970B1 (fr) * 2010-06-03 2015-02-20 Snecma Mesure de l'endommagement d'une barriere thermique d'aube de turbine
US20110297138A1 (en) * 2010-06-08 2011-12-08 Laughery Harry E Cover for use with a furnace during a heating operation
EP2474414A1 (de) * 2011-01-06 2012-07-11 Siemens Aktiengesellschaft Legierung, Schutzschicht und Bauteil
UA110643C2 (uk) 2011-04-13 2016-01-25 Роллс-Ройс Корпорейшн Стійкий до високотемпературної корозії диск або роздільник газової турбіни і спосіб отримання стійкого до викосотемпературної корозії покриття
FR2978931B1 (fr) * 2011-08-10 2014-05-09 Snecma Procede de realisation d'un renfort de protection du bord d'attaque d'une pale
US20130216798A1 (en) * 2012-02-17 2013-08-22 General Electric Company Coated article and process of coating an article
EP2767616A1 (de) 2013-02-15 2014-08-20 Alstom Technology Ltd Turbomaschinenkomponente mit einem erosions- und korrosionsbeständigen Beschichtungssystem und Verfahren zur Herstellung solch einer Komponente
CN103758580B (zh) * 2014-01-26 2016-06-22 石智勇 旋喷定子反冲透平机
EP2918705B1 (de) 2014-03-12 2017-05-03 Rolls-Royce Corporation Beschichtungs mit Diffusionssperrschicht mit Iridium und Oxidschicht und Beschichtungsverfahren
CN105750515A (zh) * 2016-04-26 2016-07-13 江苏省沙钢钢铁研究院有限公司 一种小容量母合金浇铸系统
US10329926B2 (en) * 2016-05-09 2019-06-25 United Technologies Corporation Molybdenum-silicon-boron with noble metal barrier layer
CN107365151B (zh) * 2016-05-12 2021-01-01 中国科学院宁波材料技术与工程研究所 一种致密亚微米晶β″‐Al2O3制品、其制备方法与应用
FR3067391B1 (fr) * 2017-06-12 2020-12-04 Safran Revetement anti-cmas a efficacite renforcee
CN107882639B (zh) * 2017-11-03 2019-09-03 西安航天动力研究所 一种隔热罩
US11692274B2 (en) 2019-12-05 2023-07-04 Raytheon Technologies Corporation Environmental barrier coating with oxygen-scavenging particles having barrier shell
CN114015992B (zh) * 2021-11-01 2022-05-20 重庆嘉陵特种装备有限公司 一种适用于钛合金表面抗高温氧化隔热涂层及其制备方法

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2763919A (en) * 1950-07-28 1956-09-25 Thompson Prod Inc Coated refractory body
US2878554A (en) * 1955-09-16 1959-03-24 Rand Dev Corp Method and coating for protection of molybdenum and its alloys
US3574572A (en) * 1964-04-14 1971-04-13 United Aircraft Corp Coatings for high-temperature alloys
US3595633A (en) * 1964-04-14 1971-07-27 United Aircraft Corp Coatings for high-temperature alloys
US3383235A (en) * 1965-03-29 1968-05-14 Little Inc A Silicide-coated composites and method of making them
US3540863A (en) * 1968-01-22 1970-11-17 Sylvania Electric Prod Art of protectively metal coating columbium and columbium - alloy structures
US4055705A (en) * 1976-05-14 1977-10-25 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Thermal barrier coating system
US4321311A (en) * 1980-01-07 1982-03-23 United Technologies Corporation Columnar grain ceramic thermal barrier coatings
US4321310A (en) * 1980-01-07 1982-03-23 United Technologies Corporation Columnar grain ceramic thermal barrier coatings on polished substrates
US4439470A (en) * 1980-11-17 1984-03-27 George Kelly Sievers Method for forming ternary alloys using precious metals and interdispersed phase
US5035957A (en) * 1981-11-27 1991-07-30 Sri International Coated metal product and precursor for forming same
DE3325251A1 (de) * 1983-07-13 1985-01-24 Brown, Boveri & Cie Ag, 6800 Mannheim Verfahren zum pruefen und nachbessern von auf bauelementen aufgetragenen schutzschichten
US4889776A (en) * 1987-08-17 1989-12-26 Barson Corporation Refractory metal composite coated article
US5262245A (en) * 1988-08-12 1993-11-16 United Technologies Corporation Advanced thermal barrier coated superalloy components
US5087477A (en) * 1990-02-05 1992-02-11 United Technologies Corporation Eb-pvd method for applying ceramic coatings
US5238752A (en) * 1990-05-07 1993-08-24 General Electric Company Thermal barrier coating system with intermetallic overlay bond coat
US5401307A (en) * 1990-08-10 1995-03-28 Siemens Aktiengesellschaft High temperature-resistant corrosion protection coating on a component, in particular a gas turbine component
DE69122461T2 (de) * 1990-08-11 1997-02-27 Johnson Matthey Plc Beschichteter Gegenstand
US5472487A (en) * 1991-01-18 1995-12-05 United Technologies Corporation Molybdenum disilicide based materials with reduced coefficients of thermal expansion
JP2697469B2 (ja) * 1992-04-03 1998-01-14 株式会社日立製作所 ガスタービン動翼，静翼と燃焼器ライナ及び製造法

Also Published As

Publication number Publication date
RU2167220C2 (ru) 2001-05-20
IN187892B (de) 2002-07-20
US5740515A (en) 1998-04-14
WO1996031636A1 (en) 1996-10-10
ES2162048T3 (es) 2001-12-16
CZ315797A3 (cs) 1998-03-18
CN1185183A (zh) 1998-06-17
JPH11506500A (ja) 1999-06-08
EP0820535B1 (de) 2001-09-05
JP3464003B2 (ja) 2003-11-05
UA48169C2 (uk) 2002-08-15
CN1180126C (zh) 2004-12-15
KR19980703619A (ko) 1998-12-05
EP0820535A1 (de) 1998-01-28
DE69615012D1 (de) 2001-10-11
DK0820535T3 (da) 2002-01-07

Similar Documents

Publication Publication Date Title
DE69615012D1 (de) Erosions-korrosionsschutzschicht für hochtemperaturbauteile
DE69732046D1 (de) Schutzbeschichtung für hochtemperatur
ATE205238T1 (de) Wasserverdünnbare beschichtungszusammensetzung für korrosionsschutz
ATA21697A (de) Korrosionsinhibierende überzugszusammensetzung für metalle
DE69636785D1 (de) Isolierungssystem für hohe Temperaturen
DE69519858D1 (de) Voreinspritzung für gasturbinenanlagen
DE69634562D1 (de) Hochreine zusammensetzung für ofenteile
AU1166095A (en) High temperature corrosion inhibitor
DE59703794D1 (de) Oxidationsschutzschicht für refraktärmetalle
DE59508512D1 (de) Korrosionsschutz für mikromechanische Metallschichten
DE69801301T2 (de) Schutzfolie für Anstrichfolie
DE69219773T2 (de) Korrosionsschutz für metalloberflächen
FI956211A0 (fi) Suojapäällystys teräsosia varten
DE69624971T2 (de) Fäulnisverhinderndes Überzugsmittel für Turbomaschinen
DE69528697T2 (de) Splitterschutzbeschichtung für panzerfahrzeuge
NO976059L (no) Termisk beskyttende sammensetninger
DE69518341T2 (de) Schutzschicht für Bildelemente
DE69700339D1 (de) Beschichtungsabschirmung für PVD-Vorrichtung
DE69717515D1 (de) Wärmeisolatorschicht für Feststoffraketenmotor
ATA208693A (de) Korrosionsschutzverfahren für verbrennungsanlagen
DE69400043T2 (de) Hitzebeständige Schicht für farbstoffgebendes Element
DE9418369U1 (de) Isoliermantel für Rohrleitungen
DE69329599D1 (de) Thermoplastische korrosionsschutzschicht für metalle
DE29507796U1 (de) Kälteversorgungssystem für weitverzweigt angeordnete Verbraucher
DE29519453U1 (de) Beschichtung für metallische Oberflächen

Legal Events

Date Code Title Description
8364 No opposition during term of opposition
8339 Ceased/non-payment of the annual fee