DE4340339A1 - Thick coating compsn. based on bitumen - Google Patents

Thick coating compsn. based on bitumen

Info

Publication number
DE4340339A1
DE4340339A1 DE19934340339 DE4340339A DE4340339A1 DE 4340339 A1 DE4340339 A1 DE 4340339A1 DE 19934340339 DE19934340339 DE 19934340339 DE 4340339 A DE4340339 A DE 4340339A DE 4340339 A1 DE4340339 A1 DE 4340339A1
Authority
DE
Germany
Prior art keywords
bitumen
thick coating
composition according
coating composition
vol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19934340339
Other languages
German (de)
Inventor
Wolfgang Holland
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HOLLAND PANKERT MONIQUE
Original Assignee
HOLLAND PANKERT MONIQUE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HOLLAND PANKERT MONIQUE filed Critical HOLLAND PANKERT MONIQUE
Priority to DE19934340339 priority Critical patent/DE4340339A1/en
Publication of DE4340339A1 publication Critical patent/DE4340339A1/en
Withdrawn legal-status Critical Current

Abstract

Thick coating compsn. based on bitumen contains blown glass granules made of used glass and/or silicate micro-hollow spheres as filler.

Description

Die Erfindung befaßt sich mit Dickbeschichtungsmassen auf Basis von Bitumen zum Abdichten von Bauteilen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser.The invention is concerned with thick coating compositions based of bitumen for sealing components against soil moisture, non-pressing water and pressing water.

Es ist bekannt, daß Bitumen je nach Beschaffenheit und Herkommen als Klebemasse zum Aufkleben von Fußböden, Fußbodenbelägen und Dachbelägen, als Dichtungs- und Deckaufstrich, zusammen mit Asbestfasern und Steinmehl als Bindemittel und Bitumenmörtel, der gegen Säuren unempfindlich und nicht quellbar ist, als Sperrstoff im Hoch-, Tief- und Wasserbau, als Bitumenpappe zum Imprägnieren und kombiniert mit Lackrohstoffen, wie trocknenden Ölen, Chlorkautschuk, Natur- und Kunstharzen als physikalisch trocknender Bitumenlack zum Isolieren von Bauten und Metallen verwendet wird.It is known that bitumen, depending on the nature and Coming as an adhesive for sticking floors, Flooring and roofing, as sealing and Top coat, together with asbestos fibers and stone powder as Binder and bitumen mortar, which is insensitive to acids and is not swellable, as a barrier material in high, low and Hydraulic engineering, as bitumen cardboard for impregnation and combined with Lacquer raw materials, such as drying oils, chlorinated rubber, natural and synthetic resins as a physically drying bitumen lacquer for Isolation of buildings and metals is used.

Bitumenemulsionen dienen nach Verrühren von heißem flüssigem Bitumen in Wasser unter geringem etwa 1%-igen Emulgatorzusatz, wie Seife, Harz, Ton, vorwiegend zum Straßenbau, aber auch vermischt mit Füllstoffen, wie Asbest und Holzmehl und Styroporkugeln (Schaumstoffkugeln aus Polystyrol), als Isolier- und Dichtungsstoffe. Solche Dichtungsstoffe werden als Dickbeschichtungsmassen, deren Anforderungen durch DIN-Normen festgelegt sind, gehandelt und zum Abdichten von Bauteilen gegen Bodenfeuchte, drückendes Wasser und nichtdrückendes Wasser eingesetzt. Als nachteilig erweist sich hierbei, daß die bekannten handelsüblichen Dickbeschichtungsmassen auf Basis von Bitumen, welche als Füllstoff unter anderem Polystyrolkugeln enthalten, ausschließlich manuell mittels Kelle und Glättspan aufgetragen werden müssen und bei größeren Schichtdicken, im nicht ausgehärteten Zustand zum Ablaufen neigen.Bitumen emulsions are used after stirring hot liquid Bitumen in water with a little about 1% emulsifier added, like soap, resin, clay, mainly for road construction, but also mixed with fillers such as asbestos and wood flour and Styrofoam balls (foam balls made of polystyrene), as insulating and sealants. Such sealants are called Thick coating compositions, their requirements by DIN standards are specified, traded and for sealing components against soil moisture, pressing water and non-pressing  Water used. The disadvantage here is that the known commercial thick coating compositions based on Bitumen, which as a filler includes polystyrene balls included, only manually using a trowel and smoothing chip have to be applied and with thicker layers, in uncured condition tend to run off.

Das Auftragen und Glätten ist, bedingt durch den Zeitaufwand, sehr lohnintensiv. Außerdem sind diese Arbeiten für den Verarbeiter recht unangenehm, da er ständig mit Bitumen verklebten Werkzeugen, Handschuhen und Schutzkleidung agieren muß. Aufgrund dieser Erschwernisse sind die Tagesleistungen entsprechend gering.The application and smoothing is, due to the time required, very wage-intensive. In addition, this work is for the Processors quite uncomfortable since he is constantly using bitumen glued tools, gloves and protective clothing got to. Because of these difficulties, the daily output accordingly low.

Der Erfindung liegt die Aufgabe zugrunde, eine Dickbeschichtungsmasse auf Basis von Bitumen zum Abdichten von Bauteilen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser zu schaffen, die die vorgenannten arbeitstechnischen Nachteile nicht aufweist und die spritzbar ist, d. h. mit einer Spritzpistole aufgetragen werden kann, wobei selbstverständlich auch eine manuelle Auftragung möglich bleibt.The invention has for its object a Thick coating composition based on bitumen for sealing Components against soil moisture, non-pressing water and to create oppressive water that the aforementioned Does not have technical disadvantages and the sprayable is, d. H. can be applied with a spray gun, manual application is of course also possible remains.

Erfindungsgemäß wird diese Aufgabe für eine Dickbeschichtungsmasse auf Basis von Bitumen zum Abdichten von Bauteilen gegen Bodenfeuchte, nichtdrückendes und drückendes Wasser erreicht, die als Füllstoff Blähglasgranulat aus Altglas und/oder silikatische Mikro-Hohlkugeln enthält. Durch die leichten kugelförmigen relativ druckfesten erfindungsgemäßen Zuschlagstoffe in Gestalt von silikatischen Mikro-Hohlkugeln und/oder Blähglasgranulat in der Bitumenmasse ergibt sich eine ausgesprochen leicht förderbare Masse mit sehr geringer innerer und äußerer Reibung, sogenannter Kugellagereffekt, die es erlaubt, über größere Förderweiten mit nur minimalem Temperaturanstieg der Spritzmasse bis zum Pistole gefördert und aufgespritzt zu werden. Die Erfindung ermöglicht die Anwendung des Spritzverfahrens für die erfindungsgemäßen Dickbeschichtungsmassen, wodurch sich gleichmäßigere Schichtdicken ergeben, die auch bei größeren Dicken nicht zum Ablaufen neigen. Damit wird die Tagesleistung um ein Vielfaches erhöht, die Anwendung ist zugleich einfacher und sauberer. Des weiteren wird die Abdichtung sicherer, da Fehlstellen ausgeschlossen werden. Infolge der kugelförmigen Füllstoffe ist auch die Elastizität der erhärteten Abdichtungsschicht geringfügig besser.According to the invention, this task for a Thick coating composition based on bitumen for sealing Components against soil moisture, non-pressing and pressing Water reaches that as a filler expanded glass granulate from waste glass and / or contains siliceous microspheres. Through the light spherical relatively pressure-resistant according to the invention Aggregates in the form of silicate micro hollow spheres and / or expanded glass granulate in the bitumen mass results in a Extremely easily conveyable mass with very little internal and external friction, so-called ball-bearing effect, which it allowed over larger conveying distances with only minimal Temperature rise of the spray mass promoted to the gun and to be sprayed on. The invention enables the application the spraying process for the inventive Thick coating compounds, which makes them more uniform  Layer thicknesses that do not even with larger thicknesses Tend to drain. This makes the daily output many times over increased, the application is simpler and cleaner at the same time. Of furthermore, the sealing becomes more secure because of imperfections be excluded. As a result of the spherical fillers also the elasticity of the hardened sealing layer slightly better.

Vorteilhafte Ausgestaltungen für unterschiedliche Anwendungen der erfindungsgemäßen Dickbeschichtungsmassen sind den kennzeichnenden Merkmalen der Unteransprüche entnehmbar.Advantageous configurations for different applications of the thick coating compositions according to the invention are the characteristic features of the subclaims.

Die Dickbeschichtungsmasse kann auf Basis von Bitumenemulsion sowie Bitumen-Latex-Emulsion mit variablen Latexanteilen oder Bitumen-Kautschuk-Emulsion je nach gewünschter Elastizität ausgeführt werden. Derartige Bitumenemulsionen bzw. Bitumen-Latex-Emulsionen bzw. Bitumen-Kautschuk-Emulsionen oder gegebenenfalls auch in lösungsmittelgelöste Bitumenmassen zur besseren Verarbeitung bei Minustemperaturen sind für Abdichtungszwecke handelsüblich erhältlich (beispielsweise Herstellerfirma VAT Baustofftechnik GmbH, Hamburg).The thick coating compound can be based on bitumen emulsion as well as bitumen latex emulsion with variable latex proportions or Bitumen-rubber emulsion depending on the desired elasticity be carried out. Such bitumen emulsions or Bitumen-latex emulsions or bitumen-rubber emulsions or if necessary also in solvent-dissolved bitumen better processing at minus temperatures are for Sealing purposes commercially available (for example Manufacturing company VAT Baustofftechnik GmbH, Hamburg).

Silikatische Mikro-Hohlkugeln werden auch vielfach als Glaskugeln bezeichnet und weisen einen Durchmesser von 5 bis 300 µm auf. Die Mikro-Hohlkugeln sind mit Stickstoff (30 Vol.-%) und Kohlendioxid (70 Vol.-%) gefüllt und weisen eine mittlere Dichte von 0,7 g/cm³ mit einem mittleren Schüttgewicht von 0,4 g/cm³ auf. Es ist auch möglich, die silikatischen Mikro-Hohlkugeln mit speziellen Kornverteilungen in gröberer Form von 5 bis 300 µ oder feiner mit 5 bis 150 µm oder 5 bis 100 µm zu erhalten. Die Härte der Glaskugeln beträgt nach Mohs 5. Die Wandstärke der Mikro-Hohlkugeln beträgt etwa 1/10 des Durchmessers der Mikro-Hohlkugeln. Sie haben einen Schmelzpunkt von 1200 bis 1350°C und eine maximale Oberflächenfeuchte 0,2%. Derartige silikatische Mikro-Hohlkugeln sind handelsüblich erhältlich.Silicate micro hollow spheres are also widely used as Designated glass balls and have a diameter of 5 to 300 µm. The micro hollow spheres are made with nitrogen (30 vol .-%) and carbon dioxide (70 vol .-%) filled and have an average density of 0.7 g / cm³ with an average Bulk density of 0.4 g / cm³. It is also possible that silicate micro hollow spheres with special grain distributions in coarser form from 5 to 300 µ or finer with 5 to 150 µm or to get 5 to 100 µm. The hardness of the glass balls is according to Mohs 5. The wall thickness of the hollow micro spheres is approximately 1/10 of the diameter of the hollow microspheres. they have one Melting point from 1200 to 1350 ° C and a maximum Surface moisture 0.2%. Such silicate Micro hollow spheres are commercially available.

Als Blähglasgranulat wird ein feinporiges Rundgranulat aus Recycling-Glas, das säure- und laugenbeständig und frostbeständig ist, eingesetzt. Die Wasseraufnahme solcher Blähglasgranulate beträgt im Mittel etwa 8 Vol.-%. Das Rundgranulat kann in unterschiedlicher Körnung und Kornverteilung von 0,25 bis 4,0 mm maximal bis 16 mm und entsprechenden Kornrohdichten von 0,75 g/cm³ bis 0,35 g/cm³ erhalten werden. Auch derartiges feinporiges Rundgranulat aus Recycling-Glas ist handelsüblich erhältlich.A fine-pored round granulate is made from expanded glass granulate  Recycled glass that is acid and alkali resistant is frost-resistant. The water intake of such Expanded glass granules are on average about 8% by volume. The Round granules can come in different grain sizes and Grain distribution from 0.25 to 4.0 mm maximum to 16 mm and corresponding grain densities from 0.75 g / cm³ to 0.35 g / cm³ be preserved. Such fine-pored round granules also Recycled glass is commercially available.

Latex ist eine wässerige Dispersion von natürlichen oder synthetischen Polymeren, sie entsteht beispielsweise bei der Emulsionspolimerisation und wird der Bitumenmasse zur Erhöhung der Elastizität zugesetzt. Hierbei werden insbesondere auch wässerige Dispersionen von Synthese-Kautschuk, Polychloropren oder Polystyrolcobutadien als Latex eingesetzt.Latex is an aqueous dispersion of natural or synthetic polymers, it arises, for example, from the Emulsion polymerization and will increase the bitumen mass added to the elasticity. Here in particular also aqueous dispersions of synthetic rubber, polychloroprene or polystyrene cobutadiene used as latex.

Zum Verarbeiten der Dickbeschichtungsmassen auf Basis Bitumen bei Minustemperaturen ist es erforderlich, diese in einem Lösungsmittel, wie Testbenzin, Terpentinöl oder Benzol zu lösen. Darüber hinaus ist es auch möglich, der Dickbeschichtungsmasse auf Basis Bitumen je nach Einsatz ein Bindemittel oder eine hydraulische Härterkomponente in Pulverform, Zement, Steinmehl oder dergleichen zuzugeben. Auch Füllstoffe wie Fasern, beispielsweise Glasfasern, Kunststoffasern oder Stahlfasern, sind je nach Einsatzzweck der Dickbeschichtungsmesser zuzugeben, um gegebenenfalls ihre statischen Eigenschaften zu verbessern.For processing thick coating materials based on bitumen at sub-zero temperatures it is necessary to combine them in one Solvents such as white spirit, turpentine oil or benzene to solve. In addition, it is also possible to Thick coating based on bitumen depending on the application Binder or a hydraulic hardener component in Add powder form, cement, stone powder or the like. Also Fillers such as fibers, for example glass fibers, Plastic fibers or steel fibers are depending on the application Thick coating meter to add their if necessary improve static properties.

Bevorzugt werden die erfindungsgemäßen Dickbeschichtungsmassen so eingestellt, daß sie mit einer Airless-Pumpe oder dergleichen förderbar und mit einer Spritzpistole auftragbar sind.The thick coating compositions according to the invention are preferred set to work with an airless pump or the same can be conveyed and applied with a spray gun are.

Nachfolgend wird die Erfindung an beispielhaften Zusammensetzungen der Dickbeschichtungsmasse für unterschiedliche Anwendungsbereiche erläutert.In the following the invention will be exemplified Thick coating compositions for different areas of application explained.

Beispiel 1example 1

Basismasse ist eine Bitumen-Latex-Emulsion, handelsüblich, die je nach gewünschter Elastizität mit variablem Latexanteil einsetzbar ist, beispielsweise die VAT-Eubit-Dickbeschichtung der Firma VAT Baustofftechnik GmbH, ohne Füllstoffe. Der Basismasse werden 20 Vol.-%, bezogen auf die Basismasse, an Mikro-Hohlkugeln der Körnung 5 bis 300 µm sowie 10 Vol.-%, bezogen auf die Basismasse, an Blähglasgranulat der Körnung 0,25 bis 1,00 mm zugegeben. Die Füllstoffanteile können variiert werden, allerdings beeinträchtigt ein zu hoher Anteil zwangsläufig die Dichtigkeit. Die vorangehend hergestellte Dickbeschichtungsmasse mit Bitumen-Latex-Emulsion, Mikro-Hohlkugeln und Blähglasgranulat ist eine airless-spritzbare Abdichtungsemulsionsmasse. Durch die leichten kugelförmigen relativ druckfesten Zuschlagstoffe in der Emulsion und der hervorragenden Kornverteilung in der Masse ergibt sich eine ausgesprochen leicht förderbare Masse mit sehr geringer innerer und äußerer Reibung (Kugellagereffekt), die es erlaubt, auch über größere Förderweiten mit minimalem Temperaturanstieg der spritzbaren Masse bis zur Pistole gefördert und aufgespritzt zu werden.Base mass is a bitumen-latex emulsion, commercially available that with variable latex content depending on the desired elasticity can be used, for example the VAT-Eubit thick coating from VAT Baustofftechnik GmbH, without fillers. Of the Base mass are 20 vol .-%, based on the base mass Micro hollow spheres with a grain size of 5 to 300 µm and 10 vol.%, based on the base mass, on expanded glass granules of the grain size 0.25 to 1.00 mm added. The filler proportions can can be varied, but too high a proportion inevitably the tightness. The one previously made Thick coating with bitumen-latex emulsion, Micro hollow spheres and expanded glass granulate is one airless sprayable sealing emulsion. Through the light spherical relatively pressure resistant aggregates in the emulsion and the excellent grain distribution in the mass results in an extremely easily conveyable mass with very low internal and external friction (ball bearing effect) that it allowed, even over larger conveying distances with minimal Temperature increase of the sprayable mass up to the gun to be promoted and sprayed on.

Die gemäß Beispiel hergestellte airless-spritzbare Abdichtungsemulsionsmasse kann für Abdichtungen gegen Bodenfeuchte, nichtdrückendes Wasser sowie mit Gewebeeinlage gegen drückendes Wasser eingesetzt werden.The airless sprayable manufactured according to the example Sealing emulsion mass can be used for sealing against Soil moisture, non-pressing water and with fabric insert against pressurized water.

Beispiel 2Example 2

Als Basismasse ist wiederum eine Bitumen-Latex-Emulsion mit je nach gewünschter Elastizität variablem Latex-Anteil vorgesehen, wie in Beispiel 1. Dieser Basismasse werden 100 Vol.-%, bezogen auf die Basismasse an Mikro-Hohlkugeln der Körnung 5 bis 300 µm sowie 15 Vol.-%, bezogen auf die Basismasse, an Blähglasgranulat einer ausgesuchten Körnung von entweder 0,25 bis 0,5 mm oder 0,5 bis 1,0 mm oder 1,0 bis 2,0 mm zugegeben.A bitumen-latex emulsion with each is again the base mass variable latex content according to the desired elasticity, as in Example 1. 100% by volume of this base mass are obtained on the base mass of micro hollow spheres with a grain size of 5 to 300 µm and 15% by volume, based on the base mass Expanded glass granules with a selected grain size of either 0.25 up to 0.5 mm or 0.5 to 1.0 mm or 1.0 to 2.0 mm added.

Die der Basismasse zugefügten Mikro-Hohlkugeln beeinflussen die Fließfähigkeit der Basismasse nur geringfügig. Durch die Zugabe von Blähglasgranulat läßt sich die Basismasse bis zur Pasteusität auffüllen. Es sind dann Schichtdicken von mehreren Zentimetern auftragbar, ohne daß sie ablaufen. Allerdings beeinflußt eine zu hohe Zugabe von Blähglasgranulat die Verarbeitbarkeit, da dann die Masse zu schnell erhärtet. Aufgrund des Kugellagereffektes der Zuschlagstoffe ist die Verarbeitbarkeit hervorragend.The micro hollow spheres added to the base mass influence the Flowability of the base mass only marginally. By the encore  of expanded glass granulate, the base mass can be used up to Fill up pasteusity. Then there are layer thicknesses of several Can be applied centimeters without expiring. Indeed affects an excessive addition of expanded glass granules Processability, because then the mass hardens too quickly. Due to the ball bearing effect of the aggregates, the Processability excellent.

Die gemäß Beispiel hergestellte Dickbeschichtungsmasse kann für Isolierungen, insbesondere von Feuchträumen, Abdichtungen und Verspachtelungen von Fehlstellen, zum Beispiel vor dem Anbringen der Spritzabdichtung, eingesetzt werden.The thick coating mass produced according to the example can be used for Insulations, especially damp rooms, seals and Filling of imperfections, for example before Attach the spray seal.

Beispiel 3Example 3

Als Basismasse wird eine Bitumenemulsion, die eventuell Fasern enthält, eingesetzt. Der Basismasse wird als Füllstoff Blähglasgranulat einer Körnung von 1,0 bis 2,0 mm in einer Menge von 50 Vol.-%, bezogen auf die Basismasse, zugegeben. Des weiteren wird eine hydraulische Härterkomponente in Pulverform, beispielsweise Portland-Zement, zugegeben. Auf diese Weise wird ein bituminöser Kleber erhalten. Das zugefügte Blähglasgranulat saugt sich mit der Basismasse an den zu verklebenden Bauteilen fest, bedingt durch seine Fähigkeit, bis zu 8 Vol.-% Wasser aufzunehmen, die in der Anfangsphase am größten ist. Auf diese Weise können beispielsweise Styroporplatten, ob bituminiert oder thermisch verschweißt, wenn sie einmal mittels des Klebers an eine Fläche angedrückt sind, selbst in der noch nicht erhärteten erfindungsgemäßen Klebermasse nur noch mit Bruch in der Platte entfernt werden.A bitumen emulsion, possibly fibers, is used as the base mass contains, used. The base mass is used as a filler Expanded glass granules with a grain size of 1.0 to 2.0 mm in one Amount of 50 vol .-%, based on the base mass, added. Of another is a hydraulic hardener component in powder form, for example Portland cement added. That way received a bituminous glue. The added expanded glass granulate sucks with the base mass on the components to be glued solid, due to its ability to hold up to 8 vol% water record, which is greatest in the initial phase. To this For example, polystyrene plates, whether bituminized or thermally welded once using the adhesive are pressed against a surface, even in that not yet hardened adhesive composition according to the invention only with a break in be removed from the plate.

Der gemäß Beispiel herstellbare bituminöse Kleber kann zur Verklebung von Styroporplatten als Drainplatten oder Wärmedämmung sowie von anderen Materialien, wie Verbundplatten, Rigipsplatten, Faserplatten oder dergleichen, eingesetzt werden. Es ist auch die Verlegung von Fliesen auf zuvor bituminös abgedichteten Wänden und Böden mit Hilfe des bituminösen Klebers möglich. The bituminous adhesive that can be produced according to the example can be used for Gluing styrofoam plates as drain plates or Thermal insulation and other materials, such as composite panels, Plasterboard, fiberboard or the like used become. It is also laying tiles on top of it bituminous sealed walls and floors with the help of bituminous adhesive possible.  

Beispiel 4Example 4

Als Basismasse wird eine lösungsmittelgelöste Bitumenmasse eingesetzt, die gegebenenfalls je nach Anforderung mit Faseranteilen gefüllt ist, um eine leicht thixotrope Einstellung zu erhalten. Dieser Basismasse werden silikatische Mikro-Hohlkugeln der Körnung 5 bis 300 µm in einer Menge von 50 Vol.-%, bezogen auf die Basismasse, zugegeben. Des weiteren wird Blähglasgranulat der Körnung 0,25 bis 1,0 mm in einer Menge von 50 Vol.-%, bezogen auf die Basismasse, zugegeben.A solvent-dissolved bitumen mass is used as the base mass used, if necessary, depending on the requirement Fiber content is filled to be a slightly thixotropic Get attitude. This base mass will be silicatic Micro hollow spheres with a grain size of 5 to 300 µm in an amount of 50 Vol .-%, based on the base mass, added. Furthermore expanded glass granules with a grain size of 0.25 to 1.0 mm in one Amount of 50 vol .-%, based on the base mass, added.

Die Füllstoffanteile können variiert werden, jedoch beeinträchtigt ein zu hoher Anteil die Dichtigkeit der herzustellenden Masse. Die gemäß Beispiel hergestellte Dickbeschichtungsmasse ist spritzbar. Durch die leichten kugelförmigen relativ druckfesten Zuschlagstoffe in der Bitumenmasse ergibt eine ausgesprochen leicht förderbare Masse mit sehr geringer innerer und äußerer Reibung (Kugellagereffekt), die es erlaubt, über größere Förderweiten mit nur minimalen Temperaturanstieg der Spritzmasse bis zur Spritzpistole gefördert und aufgespritzt zu werden.The filler proportions can be varied, however too high a proportion affects the tightness of the mass to be produced. The one produced according to the example Thick coating is sprayable. Because of the light spherical relatively pressure-resistant aggregates in the Bitumen mass results in an extremely easily conveyable mass with very little internal and external friction (Ball bearing effect), which allows it over longer conveying distances with only a minimal increase in temperature of the molding compound up to Spray gun to be promoted and sprayed on.

Die lösungsmittelhaltige Bitumenspritzmasse ist nicht ganz so umweltfreundlich wie die Spritzmassen auf Emulsionsbasis, sie sind jedoch auch bei Minustemperaturen zu verarbeiten.The solvent-based bitumen spray compound is not quite so environmentally friendly like the emulsion-based spray compounds, they however, they can also be processed at sub-zero temperatures.

Die Dickbeschichtungsmassen gemäß Beispiel werden für Abdichtungen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser eingesetzt, wobei sie insbesondere bei niedrigen Außentemperaturen im Spritzverfahren als Abdichtungsschicht aufgetragen werden können.The thick coating compositions according to the example are for Seals against soil moisture, non-pressing water and pressurized water used, in particular when low outside temperatures in the spray process as Sealing layer can be applied.

Beispiel 5Example 5

Als Basismasse ist eine lösungsmittelhaltige Bitumen-Kautschuk- Masse vorgesehen, die je nach Anforderung mit Faseranteilen in leicht thixotroper Einstellung vorgesehen wird. Derartige Massen sind, wie auch die vorgenannten, handelsüblich erhältlich, beispielsweise von der Firma VAT Baustofftechnik GmbH unter der Produktbezeichnung "Eukatekt". A solvent-based bitumen rubber Mass provided, depending on the requirement with fiber in slightly thixotropic adjustment is provided. Such Masses, like the aforementioned, are commercially available available, for example from VAT Baustofftechnik GmbH under the product name "Eukatekt".  

Der Basismasse werden Mikro-Hohlkugeln mit einem Durchmesser von 5 bis 300 µm in einer Menge von 100 Vol.-%, bezogen auf die Basismasse, sowie Blähglasgranulat der Körnung 0,25 bis 0,5 mm in einer Menge von 25 Vol.-%, bezogen auf die Basismasse, und einer Körnung von 0,5 bis 1,0 mm in einer Menge von 25 Vol.-%, bezogen auf die Basismasse, zugegeben.The base mass will be micro hollow spheres with a diameter from 5 to 300 µm in an amount of 100% by volume, based on the Base mass, as well as expanded glass granules with a grain size of 0.25 to 0.5 mm in an amount of 25 vol .-%, based on the base mass, and a grain size of 0.5 to 1.0 mm in an amount of 25% by volume, based on the base mass, added.

Die gemäß Beispiel erhaltene lösungsmittelhaltige Bitumen-Kautschuk-Dickbeschichtungsmasse ist spachtelfähig. Die Zuschlagstoffe in der aufeinander abgestimmten Sieblinie ergeben in Verbindung mit der Basismasse eine sehr homogene standfeste Masse, die sich, bedingt durch die kugelförmigen Zuschlagstoffe, hervorragend verarbeiten läßt.The solvent-containing obtained according to the example Bitumen rubber thick coating compound can be filled. The Aggregates in the coordinated sieve line result in a very homogeneous combination with the base mass stable mass, due to the spherical shape Aggregates, excellent processing.

Auch diese lösungsmittelhaltige Bitumen-Kautschuk-Dickbeschichtungsmasse läßt sich bei Minustemperaturen verarbeiten. Mit ihr können dickschichtige Abdichtungen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser hergestellt werden.This also contains solvents Bitumen rubber thick coating compound can be used Process minus temperatures. With it can thick layers Seals against soil moisture, non-pressing water and pressurized water.

Beispiel 6Example 6

Als Basismasse wird eine Bitumenemulsion eingesetzt, der als hydraulisches Bindemittel Portland-Zement zugegeben wird. Als Füllstoffe werden Mikro-Hohlkugeln und Blähglasgranulat in Sieblinien bis zu einer Korngröße von 16 mm je nach erforderlicher Schichtdicke zugegeben.A bitumen emulsion is used as the base mass hydraulic binder Portland cement is added. When Fillers are used in hollow microspheres and expanded glass granules Screen lines up to a grain size of 16 mm depending on required layer thickness added.

Mit der vorgenannten Dickbeschichtungsmasse, die gegebenenfalls in der Bitumenemulsion auch Latexanteile aufweisen kann, kann ein bituminöser Leichtestrich hergestellt werden. Der Leichtestrich hat je nach Korngröße im ausgetrockneten Zustand eine Rohdichte von 310 bis 700 kg/m³. Werden der Emulsion Latexanteile zugegeben, so härtet das System hartgummiartig aus.With the aforementioned thick coating compound, which if necessary may also have latex components in the bitumen emulsion a bituminous light screed can be produced. Of the Depending on the grain size, light screed has dried out a bulk density of 310 to 700 kg / m³. Be the emulsion If latex is added, the system hardens like a rubber out.

Der Leichtestrich weist eine Wärmeleitfähigkeit von ca. 0,12 W/mk bis 0,25 W/mk auf. Bei höherer Zementzugabe verringert sich die Wärmeleitfähigkeit, dafür erhöht sich die Druckfestigkeit.The light screed has a thermal conductivity of approx. 0.12 W / mk to 0.25 W / mk. With higher cement addition  the thermal conductivity decreases, but the increases Compressive strength.

Der erfindungsgemäße bituminöse Leichtestrich kann als dämpfender Zwischenestrich unter Betonplatten, welche Schwingungen von Maschinen ausgesetzt sind, eingesetzt werden. Er ist auch als Leichtfüllung zwischen Balken bei Altbausanierungen, als Gefälleestrich auf Dachkonstruktionen, als Wärmedämmschicht unter Estrichen, als belegbaren Estrich (nur bei höherer Zementzugabe) für Platten-, Holz- oder andere Aufbauten einsetzbar.The bituminous light screed according to the invention can be used as damping screed under concrete slabs, which Machine vibrations are used. It is also used as a light filling between beams Old building renovations, as a screed on roof structures, as a thermal insulation layer under screed, as a verifiable screed (only with higher cement addition) for slabs, wood or others Superstructures can be used.

Claims (17)

1. Dickbeschichtungsmassen auf Basis von Bitumen zum Abdichten von Bauteilen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser, enthaltend als Füllstoff Blähglasgranulat aus Altglas und/oder silikatische Mikro-Hohlkugeln.1. Thick coating compositions based on bitumen for sealing of components against soil moisture, non-pressing water and pressing water containing as a filler Expanded glass granulate from waste glass and / or silicate Micro hollow spheres. 2. Dickbeschichtungsmassen nach Anspruch 1, dadurch gekennzeichnet, daß silikatische Mikro-Hohlkugeln mit einer Korngröße von 5 bis 300 µm und einer Mohshärte von 5 als Füllstoff eingesetzt sind.2. thick coating compositions according to claim 1, characterized in that silicate micro hollow spheres with a grain size of 5 to 300 µm and a Mohs hardness of 5 are used as filler. 3. Dickbeschichtungsmasse nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß als Blähglasgranulat ein feinporiges Rundgranulat aus Recycling-Glas mit einer Wasseraufnahme von 5 bis 9 Vol.-% und einer Körnung von 0,25 bis 4,0 min mit einer Kornrohdichte von 0,75 g/cm³ bis 0,35 g/cm³, das säure- und laugenbeständig ist, eingesetzt ist.3. thick coating composition according to claim 1 or 2, characterized in that as expanded glass granules fine-pored round granulate made from recycled glass with a Water absorption of 5 to 9 vol .-% and a grain size of 0.25 to 4.0 min with a grain density of 0.75 g / cm³ to 0.35 g / cm³, which is acid and alkali resistant, used is. 4. Dickbeschichtungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß als Basismasse eine Bitumenemulsion eingesetzt ist.4. thick coating composition according to claim 1, characterized in that as a base mass Bitumen emulsion is used. 5. Dickbeschichtungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß als Basismasse eine Bitumen-Latex-Emulsion eingesetzt ist.5. thick coating composition according to claim 1, characterized in that as a base mass Bitumen latex emulsion is used. 6. Dickbeschichtungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß als Basismasse eine lösungsmittelgelöste Bitumenmasse verwendet ist. 6. thick coating composition according to claim 1, characterized in that as a base mass solvent-dissolved bitumen mass is used.   7. Dickbeschichtungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß als Basismasse eine lösungsmittelgelöste Bitumen-Kautschuk-Masse verwendet ist.7. thick coating composition according to claim 1, characterized in that as a base mass solvent-based bitumen rubber compound is used. 8. Dickbeschichtungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß in der Bitumenmasse zusätzlich Fasern, wie Glasfasern, Kunststoffasern und/oder ein Bindemittel, wie Steinmehl, enthalten sind.8. thick coating composition according to claim 1, characterized in that additionally in the bitumen mass Fibers such as glass fibers, plastic fibers and / or a Binders such as stone powder are included. 9. Dickbeschichtungsmasse nach Anspruch 5, dadurch gekennzeichnet, daß die Bitumen-Latex-Emulsion bis zu 100 Vol.-%, bezogen auf das Volumen der Bitumen-Latex-Emulsion, Mikro-Hohlkugeln und bis zu 50 Vol .-%, bezogen auf das Volumen der Bitumen-Latex-Emulsion, Blähglasgranulat enthält, wobei die Summe von Mikro-Hohlkugeln und Blähglasgranulat maximal 120 Vol.-% beträgt.9. thick coating composition according to claim 5, characterized in that the bitumen latex emulsion up to 100 vol .-%, based on the volume of the Bitumen latex emulsion, micro hollow spheres and up to 50 Vol .-%, based on the volume of the bitumen-latex emulsion, Contains expanded glass granules, the sum of Micro hollow spheres and expanded glass granules maximum 120 vol .-% is. 10. Dickbeschichtungsmasse nach Anspruch 4, dadurch gekennzeichnet, daß der Bitumenemulsion eine hydraulische Härterkomponente in Pulverform zugegeben ist.10. thick coating composition according to claim 4, characterized in that the bitumen emulsion hydraulic hardener component is added in powder form. 11. Dickbeschichtungsmasse nach Anspruch 6 oder 7, dadurch gekennzeichnet, daß als Lösungsmittel für das Bitumen Testbenzin oder Terpentinöl oder Benzol verwendet ist.11. thick coating composition according to claim 6 or 7, characterized in that as a solvent for the Bitumen white spirit or turpentine oil or benzene is used is. 12. Dickbeschichtungsmasse nach Anspruch 5, dadurch gekennzeichnet, daß die Bitumen-Latex-Emulsion 15 bis 25 Vol.-%, bezogen auf die Bitumen-Latex-Emulsion, an Mikro-Hohlkugeln der Körnung 5 bis 300 µm und 5 bis 15 Vol .-%, bezogen auf die Bitumen-Latex-Emulsion, an Blähglasgranulat der Körnung 0,25 bis 1,00 mm enthält, so daß sie zum Herstellen einer Abdichtungsschicht durch Spritzen gegen Bodenfeuchtigkeit, nichtdrückendes Wasser sowie mit Gewebeeinlage gegen drückendes Wasser einsetzbar ist. 12. thick coating composition according to claim 5, characterized in that the bitumen-latex emulsion 15th up to 25 vol .-%, based on the bitumen latex emulsion Micro hollow spheres with a grain size of 5 to 300 µm and 5 to 15 Vol .-%, based on the bitumen latex emulsion Contains expanded glass granules with a grain size of 0.25 to 1.00 mm, see above that they use to make a sealing layer Splash against soil moisture, non-pressing water and can be used with fabric inlay against pressing water is.   13. Dickbeschichtungsmasse nach Anspruch 5, dadurch gekennzeichnet, daß die Bitumen-Latex-Emulsion bis zu 100 Vol.-%, bezogen auf die Bitumen-Latex-Emulsion, an Mikro-Hohlkugeln der Körnung 5 bis 300 µm und 10 bis 20 Vol.-%, bezogen auf die Bitumen-Latex-Emulsion, an Blähgranulat der Körnungen 0,25 bis 0,5 mm bis 0,5 bis 1,0 mm bzw. 1,0 bis 2,0 mm enthält, so daß sie zum Herstellen von Isolierungen von Feuchträumen, Verspachtelungen und Abdichtungen einsetzbar ist.13. thick coating composition according to claim 5, characterized in that the bitumen latex emulsion up to 100 vol .-%, based on the bitumen latex emulsion Micro hollow spheres with a grain size of 5 to 300 µm and 10 to 20 Vol .-%, based on the bitumen latex emulsion Expandable granules with grain sizes from 0.25 to 0.5 mm to 0.5 to Contains 1.0 mm or 1.0 to 2.0 mm, so that they for Manufacture of damp room insulation, Filling and sealing can be used. 14. Dickbeschichtungsmasse nach Anspruch 4, dadurch gekennzeichnet, daß die Bitumenemulsion 40 bis 60 Vol.-%, bezogen auf die Bitumenemulsion, Blähglasgranulat von 1,0 bis 2,0 mm Korngröße und eine hydraulische Härterkomponente in Pulverform sowie gegebenenfalls Fasern enthält, so daß sie als Klebemasse zum Verkleben von Fliesen, Platten, Verbundplatten, Styroporplatten als Drainplatten oder Wärmedämmung, Rigipsplatten, Faserplatten einsetzbar ist.14. thick coating composition according to claim 4, characterized in that the bitumen emulsion 40 to 60 vol .-%, based on the bitumen emulsion, Expanded glass granules of 1.0 to 2.0 mm grain size and one hydraulic hardener component in powder form as well optionally contains fibers so that they act as an adhesive for gluing tiles, panels, composite panels, Styrofoam panels as drain panels or thermal insulation, Plasterboard, fiberboard can be used. 15. Dickbeschichtungsmasse nach Anspruch 6, dadurch gekennzeichnet, daß die lösungsmittelhaltige Bitumenmasse in leicht thixotroper Einstellung 40 bis 60 Vol.-%, bezogen auf die lösungsmittelgelöste Bitumenmasse, an Mikro-Hohlkugeln der Körnung 5 bis 300 µm und 60 bis 40 Vol.-%, bezogen auf die lösungsmittelgelöste Bitumenmasse, an Blähglasgranulat der Körnung 0,25 bis 1,0 mm sowie gegebenenfalls Fasern enthält, so daß sie zur Herstellung von Abdeckschichten durch Spritzen auch bei Minustemperaturen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser einsetzbar ist.15. thick coating composition according to claim 6, characterized in that the solvent-based Bitumen mass in a slightly thixotropic setting 40 to 60 Vol .-%, based on the solvent-dissolved bitumen mass, on micro hollow spheres with a grain size of 5 to 300 µm and 60 to 40 vol .-%, based on the solvent solution Bitumen mass, on expanded glass granules with a grain size of 0.25 to 1.0 mm and optionally contains fibers, so that they for Production of cover layers by spraying also at Freezing temperatures against soil moisture, non-pressing Water and pressurized water can be used. 16. Dickbeschichtungsmasse nach Anspruch 7, dadurch gekennzeichnet, daß die lösungsmittelhaltige Bitumen-Kautschukmasse spachtelfähig leicht thixotrop eingestellt ist und 80 bis 110 Vol.-%, bezogen auf die lösungsmittelhaltige Bitumen-Kautschukmasse, an Mikro-Hohlkugeln der Körnung 5 bis 300 µm und je 20 bis 30 Vol.-%, bezogen auf die lösungsmittelhaltige Bitumen-Kautschukmasse, an Blähglasgranulat der Körnung 0,25 bis 0,5 mm und der Körnung 0,5 bis 1,0 mm enthält sowie gegebenenfalls Fasern enthält, so daß dickschichtige Abdichtungen bei Minustemperaturen gegen Bodenfeuchte, nichtdrückendes Wasser und drückendes Wasser herstellbar sind.16. thick coating composition according to claim 7, characterized in that the solvent-based Bitumen rubber compound can be trowelled and slightly thixotropic is set and 80 to 110 vol .-%, based on the solvent-based bitumen rubber compound Micro hollow spheres with a grain size of 5 to 300 µm and 20 to  30 vol .-%, based on the solvent-based Bitumen rubber compound, on expanded glass granulate of the grain Contains 0.25 to 0.5 mm and the grain size 0.5 to 1.0 mm and optionally contains fibers, so that thick layers Seals at minus temperatures against soil moisture, non-pressing water and pressing water can be produced are. 17. Dickbeschichtungsmasse nach Anspruch 4, dadurch gekennzeichnet, daß ein Leichtestrich mit einer Rohdichte von 310 bis 700 kg/m³ im ausgetrockneten Zustand aus einer Bitumenemulsion, Zement als Bindemittel und Mikro-Hohlkugeln und Blähglasgranulat in Sieblinien bis zu einer Korngröße von 16 mm, gegebenenfalls unter Zusatz von Latex, herstellbar ist.17. thick coating composition according to claim 4, characterized in that a light screed with a Bulk density from 310 to 700 kg / m³ in the dried state from a bitumen emulsion, cement as a binder and Micro hollow spheres and expanded glass granules in sieve lines up to a grain size of 16 mm, optionally with the addition of Latex, is producible.
DE19934340339 1993-11-26 1993-11-26 Thick coating compsn. based on bitumen Withdrawn DE4340339A1 (en)