DE4103773C1 - Structural sealant yielding improved adhesivity - comprises a primer contg. water-glass, saponification resistant polymer, water, dyes, pigments and thickeners and a sealing thick layer contg. bitumen

Info

Publication number: DE4103773C1
Application number: DE19914103773
Authority: DE
Inventors: Klaus 4354 Datteln De Wichmann
Original assignee: Heinrich Hahne & Co Kg 4354 Datteln De GmbH
Current assignee: Heinrich Hahne & Co Kg 4354 Datteln De GmbH
Priority date: 1991-02-08
Filing date: 1991-02-08
Publication date: 1992-06-11
Anticipated expiration: 2011-02-09

Abstract

Structural sealant comprises a primer which can be applied on to fully-joined masonry, e.g, lime sandstone, concrete block, aerated concrete, concrete and plater; and a sealing thick layer, pref. a bitumen-rubber thick coating, which can be applied on the primer. The improvement is that the primer comprises 3-25 wt. % solid waterglass, 2-25 wt. % of a polymer providing a saponification-resistant polymer dispersion, 40-94 wt. % water and 1-10 wt. % usual additives, pref. dyes, pigments, de-foamers, stabilisers, hydropobing agents or thickeners. ADVANTAGE - Improved adhesion of the structural seal on the masonry is obtd. (Dwg.0/0)

Description

Die Erfindung bezieht sich auf eine Bauwerksabdichtung aus einer Grundierung, die auf vollfugiges Mauerwerk, z. B. Kalk sandstein, Betonstein, Gasbeton, Beton, Putz ud.dgl. auf bringbar ist und einer abdichtenden Bitumen-Kautschuk-Dick beschichtung, die auf die Grundierung aufbringbar ist.The invention relates to a building waterproofing a primer based on solid masonry, e.g. B. Lime sandstone, concrete block, gas concrete, concrete, plaster and the like. on can be brought and a sealing bitumen rubber thick coating that can be applied to the primer.

Aus der DE-OS 21 63 010 ist es bekannt, daß Bauwerke sowohl durch Verkieselungsverfahren auf Kieselsäure-Basis als auch durch Bitumen-Latex-Kombinationen abdichtbar sind.From DE-OS 21 63 010 it is known that buildings both by silicification processes based on silica as can also be sealed with bitumen-latex combinations.

Die DE-OS 37 10 405 zeigt eine bitumenhaltige elastomermodi fizierte Emulsion, die als Dichtungsbelag mit oder ohne Haftverbund zum Untergrund verwendet werden kann. Hierbei wird ein Voranstrich, z. B. ein bituminöser Kaltanstrich, als Grundierung auf den Untergrund aufgebracht.DE-OS 37 10 405 shows a bituminous elastomer modes fected emulsion, which as a sealant with or without Adhesive bond to the surface can be used. Here a primer, e.g. B. a bituminous cold paint, applied as a primer to the substrate.

Die DE-OS 29 13 263 zeigt, daß die Abdichtung eines Mauer werks durch Verkieselung mit Wasserglas erreichbar ist. DE-OS 29 13 263 shows that the sealing of a wall can be reached by silicification with water glass.

Aus der DE-OS 25 26 514 ist es bekannt, auf einen Bauwerks träger eine Grundierung aus lösungsmittelhaltigen, alkali festen Kunstharzgemischen aufzubringen, bevor eine handels übliche Abdichtung auf den vorbehandelten Träger aufgetragen wird.From DE-OS 25 26 514 it is known on a building a primer made of solvent-based, alkali to apply solid synthetic resin mixtures before a trade usual seal applied to the pretreated carrier becomes.

Bei den eingangs geschilderten Bauwerksabdichtungen werden im Stand der Technik zwei Typen von Grundierungen verwendet. Zum einen dient als Grundierungsmittel das für die Dickbeschichtung verwendete Material selbst, welches etwa in einem Verhältnis von 1 : 10 mit Wasser verdünnt wird. Darüber hinaus ist es ge bräuchlich, eine sog. Verkieselung zu verwenden, die ihrer seits im Verhältnis 1 : 1 mit Wasser verdünnt ist.In the case of the building seals described above, in Prior art used two types of primers. To the one serves as a primer for thick coating used material itself, which is roughly in a ratio 1:10 is diluted with water. In addition, it is ge customary to use a so-called silicification, their is diluted 1: 1 with water.

Um mittels dieser bekannten Grundierungen eine feste und den Dichtigkeitsanforderungen genügende Verbindung zwischen der Dickbeschichtung und dem Mauerwerk herzustellen, muß zum einen sichergestellt werden, daß auf dem unbehandelten Mauerwerk möglichst wenig Staub od. dgl. abgelagert ist, was angesichts der bei einem normalen Baubetrieb herrschenden Bedingungen vergleichsweise schwierig ist, und zum anderen muß das unbehandelte Mauerwerk möglichst wenig naß bzw. mög lichst trocken sein, wobei mit zunehmender Nässe des unbe handelten Mauerwerks die Haftung der auf dieses aufgebrach ten Bauwerksabdichtung stark nachläßt.In order to have a solid and by means of these known primers connection between the tightness requirements the thick coating and the masonry on the one hand ensure that the untreated Masonry as little dust or the like is deposited, what given the prevailing in normal construction operations Conditions is comparatively difficult, and secondly the untreated masonry must be as wet or as little as possible be as dry as possible, with increasing wetness of the unbe acted masonry liability on this building waterproofing deteriorates significantly.

Der Erfindung liegt die Aufgabe zugrunde, die gattungsgemäße Bauwerksabdichtung derart weiterzubilden, daß die Haftung der Bauwerksabdichtung am Mauerwerk erheblich verbessert ist, wo bei darüber hinaus eine Verschlechterung der Haftungseigen schaften, insbesondere aufgrund von auf dem unbehandelten Mauerwerk vorhandenem Staub od. dgl. oder aufgrund von Feuch tigkeit bzw. Nässe des unbehandelten Mauerwerks reduziert bzw. ausgeschlossen sein sollen.The invention has for its object the generic Building sealing in such a way that the liability of Building waterproofing on masonry is significantly improved where in addition, deterioration in liability shaft, especially due to the untreated Masonry existing dust or the like or due to moisture activity or wetness of the untreated masonry reduced or should be excluded.

Diese Aufgabe wird erfindungsgemäß gelöst durch eine Abdichtung gemäß der Merkmale des Anspruches 1.This object is achieved according to the invention by a seal according to the features of claim 1.

Besonders günstige Haftungseigenschaften zwischen der Dick beschichtung und dem Mauerwerk ergeben sich, wenn der feste Wasserglasgehalt der Grundierung zwischen 5-15 Gew.-% und der feste Polymergehalt der Grundierung zwischen 3-10 Gew.-% beträgt.Particularly favorable adhesion properties between the thick coating and masonry arise when the solid Water glass content of the primer between 5-15% by weight and the solid polymer content of the primer between 3-10 % By weight.

Als Wasserglaslösung läßt sich üblicherweise auf dem ent sprechenden Fachgebiet verwendete Kaliwasserglaslösung ver wenden. As a water glass solution can usually on the ent Potash water glass solution used in the specialist field turn.

Um eine klare Unterscheidung zwischen mit Grundierungsmittel behandeltem Mauerwerk und unbehandeltem Mauerwerk zu ermög lichen, kann als Additiv ein Farbstoff bzw. ein Farbpigment der Grundierung zugesetzt werden, so daß die behandelte Mauerwerksfläche aufgrund ihrer unterschiedlichen Einfärbung von der unbehandelten Mauerwerksfläche in einfacher Weise unterschieden werden kann. Darüber hinaus können zur Ver einfachung der Aufbringung der Grundierung, zur Verbesserung ihrer Haltbarkeit, zur Verbesserung ihrer wasserabstoßenden Eigenschaften und zur Verbesserung ihrer Aushärtungseigen schaften Entschäumer, Konservierungsmittel, Hydrophobierungs mittel, Stabilisierungsmittel und/oder Verdickungsmittel als Additive zugesetzt werden.To make a clear distinction between using primer treated masonry and untreated masonry Lichen, a dye or a pigment can be used as an additive be added to the primer so that the treated Masonry surface due to their different coloring from the untreated masonry surface in a simple way can be distinguished. In addition, ver simplifying the application of the primer, for improvement their durability, to improve their water-repellent Properties and to improve their curing properties defoamers, preservatives, water repellents agents, stabilizers and / or thickeners as Additives are added.

Das erfindungsgemäße Grundierungsmittel wirkt chemisch und physikalisch zur Verbesserung der staubbindenden, verfestigen den und wasserabweisenden Eigenschaften der Bauwerksabdich tung, ohne daß die Diffusionsfähigkeit des Untergrunds wesent lich beeinträchtigt würde. Der unter baustellenüblichen Be dingungen an den mineralischen Baustoffoberflächen anhaften de Staub, z. B. Abrieb, Zement- und Quarzstäube, wird sicher eingebunden und somit fester Bestandteil der Bauwerksab dichtung bzw. der Grundierung. Die Baustoffoberflächen wer den durch silikatische Bindungen millimetertief verfestigt und ergeben so eine sichere, tragfähige Unterlage für die nachfolgende Bitumen-Kautschuk-Dickbeschichtung. Die Anwen dung der erfindungsgemäßen Grundierung führt zu einer was serabweisenden Oberflächenzone von einigen Millimetern Tiefe. The primer according to the invention acts chemically and physically to improve dust-binding, solidify the and water-repellent properties of the building seal tion without the diffusibility of the subsoil essential would be affected. The under construction site custom conditions adhere to the mineral building material surfaces de dust, e.g. B. abrasion, cement and quartz dust will be safe integrated and thus an integral part of the structure seal or the primer. The building material surfaces who solidified to the millimeter by silicate bonds and thus result in a secure, stable base for the subsequent bitumen rubber thick coating. The users tion of the primer according to the invention leads to what Serum-repellent surface zone a few millimeters deep.

Ein so grundierter Baustoff vermindert die Gefahr des Hinter laufens der Abdichtung durch Wasser. Kapillarwasser kann nicht mehr bis zur Haftzone der Abdichtung gelangen. Die Saug fähigkeit des Untergrundes wird reduziert, die abdichtende Dickbeschichtung härtet gleichmäßiger und spannungsärmer durch. Durch die gute Diffusionsfähigkeit der erfindungsge mäßen Grundierung kann ein Abtrocknen der abdichtenden Dick beschichtung auch in dem Untergrund stattfinden. Dies ist besonders wichtig bei einkomponentigen Materialien, die sich ausschließlich durch Trocknung verfestigen. Die erfindungs gemäße Grundierung ist bei ein- und zweikomponentigen ab dichtenden Dickbeschichtungen auf allen saugfähigen minera lischen Untergründen anwendbar. Die Grundierung läßt sich auf trockenen und vorübergehend feuchten Flächen anwenden.A building material primed in this way reduces the risk of the rear running the seal through water. Capillary water can no longer reach the seal's adhesive zone. The suction The ability of the substrate is reduced, the sealing Thick coating hardens more evenly and less stress by. Due to the good diffusibility of the fiction moderate primer can dry off the sealing thick coating also take place in the subsurface. This is particularly important for single-component materials that are solidify only by drying. The fiction proper primer is off with one and two component sealing thick coatings on all absorbent minera applicable substrates. The primer can be opened Apply dry and temporarily damp surfaces.

Bei der Anbringung einer Bitumen-Kautschuk-Dickbeschichtung auf staubigem Kalksandstein lassen sich mit der erfindungs gemäßen Grundierung Haftkräfte erzielen, die um ca. 38% höher als bei der Verwendung einer Verkieselung und um ca. 47% höher als bei der Verwendung einer 1 : 10-Verdünnung des Dickbe schichtungsmaterials liegen. Bei der Anbringung einer Bitu men-Kautschuk-Dickbeschichtung auf vergleichsweise Gasbeton stein lassen sich mit der erfindungsgemäßen Grundierung Haf tungskräfte erzielen, die um 156% bzw. um 56% höher lie gen als bei der Verwendung einer Verkieselung oder einer 1 : 10-Verdünnung des Dickbeschichtungsmaterials liegen.When applying a bitumen rubber thick coating on dusty sand-lime brick with the invention according to primer achieve adhesive forces that are about 38% higher than when using silicification and about 47% higher than when using a 1:10 dilution of the Dickbe layering material. When attaching a Bitu men rubber thick coating on comparatively gas concrete can be stone with the primer Haf achievements that were 156% and 56% higher, respectively than when using a silicification or a 1:10 dilution of the thick coating material.

Nur bei einer beträchtlich über das übliche Maß hinausge henden Verschmutzung an der Baustoffoberfläche muß diese vor dem Aufbringen der Grundierung entfernt werden, z. B. durch Abfegen oder Abspülen. Die erfindungsgemäße Grundierung kann gestrichen, gerollt oder gespritzt werden. Bei stark staubigen Baustoffoberflächen empfiehlt es sich, zur Auf bringung der Grundierung eine Bürste oder einen Besen zu verwenden, um so eine gute Einbindung des Staubes zu er reichen. Die nachfolgende Dickbeschichtung kann bereits aufgetragen werden, wenn die Grundierung mattfeucht aufge trocknet ist. Längere Trockenzeiten haben keinen nachteiligen Einfluß auf die Haftung.Only with a considerably larger than usual Soiling on the surface of the building material must be be removed before applying the primer, e.g. B. by sweeping or rinsing. The primer according to the invention can be painted, rolled or sprayed. With strong dusty building material surfaces, it is recommended to open apply a brush or broom to the primer use, so that the dust is well integrated pass. The subsequent thick coating can already can be applied when the primer is applied with a damp cloth is drying. Longer drying times have no disadvantage Influence on liability.

Je nach Saugfähigkeit des Untergrunds werden ca. 150-250 g/ Quadratmeter Grundierungsmittel benötigt.Depending on the absorbency of the surface, approx. 150-250 g / Square meters of primer required.

Claims

1. Building waterproofing, consisting of a primer that on solid brickwork, z. B. sand-lime brick, concrete block, gas concrete, concrete, plaster can be applied, and a thick sealing coating, preferably a bituminous rubber thick coating, which can be brought onto the primer, characterized in that the primer consists of 3-25% by weight solid water glass, from 2-25% by weight of a saponification-resistant polymer dispersion resulting polymer, 40-94% by weight of water and from 1-10% by weight of conventional additives.

2. Building waterproofing according to claim 1, wherein the primer 5-15 wt .-% solid water glass.

3. Building waterproofing according to claim 1 or 2, wherein the Primer has 3-10 wt .-% polymer.

4. Building sealing according to one of claims 1-3, in which Potash water glass solution is provided as the water glass solution.

5. Building sealing according to one of claims 1-4, in which as additives dyes, color pigments, defoamers, con preservatives, water repellents, stabilizing agents tel and / or thickeners are provided.