DE3743511A1 - Process for producing thin panels from a cuboid of natural or cast stone, and panel produced by this process - Google Patents

Process for producing thin panels from a cuboid of natural or cast stone, and panel produced by this process

Info

Publication number
DE3743511A1
DE3743511A1 DE19873743511 DE3743511A DE3743511A1 DE 3743511 A1 DE3743511 A1 DE 3743511A1 DE 19873743511 DE19873743511 DE 19873743511 DE 3743511 A DE3743511 A DE 3743511A DE 3743511 A1 DE3743511 A1 DE 3743511A1
Authority
DE
Germany
Prior art keywords
plates
cuboid
carrier layer
panels
natural
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19873743511
Other languages
German (de)
Other versions
DE3743511C2 (en
Inventor
Giancarlo Negri
Josef Spaeth
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE19873743511 priority Critical patent/DE3743511A1/en
Priority to IT8812618A priority patent/IT1229796B/en
Publication of DE3743511A1 publication Critical patent/DE3743511A1/en
Application granted granted Critical
Publication of DE3743511C2 publication Critical patent/DE3743511C2/de
Granted legal-status Critical Current

Abstract

Process for producing thin panels from a cuboid of natural or cast stone, for example of marble, granite, agglomerated marble or the like, and panel produced by this process. In order to be able to produce comparatively large-surface-area panels with a relatively low thickness, along with sufficient inherent rigidity and rupture strength, the present invention proposes the following process: a natural-stone or cast-stone cuboid is first of all split up, in the known manner, into relatively thick, inherently rigid panels. These panels, which are still very thick, are then provided on one or both sides with a backing layer, are then fitted together again to form a cuboid (10a) and are subsequently split up into thin panels (14). The thickness of these panels (14) corresponds to only half of the panels produced in the conventional manner, reduced by the cutting width of the frame-saw blades (12) by means of which the cuboid (10a) is split up again. <IMAGE>

Description

Die vorliegende Erfindung betrifft ein Verfahren zur Her­ stellung von dünnen Platten aus einem Quader aus Natur- oder Kunststein, beispielsweise aus Marmor, Granit, Agglomarmor od.dgl.The present invention relates to a method for manufacturing positioning of thin plates from a natural or artificial stone, for example made of marble, granite, Agglomerate or the like

Die Erfindung betrifft weiterhin eine nach diesem Verfah­ ren hergestellte Platte.The invention further relates to a method according to this ren manufactured plate.

Bislang wird ein Quader aus Natur- oder Kunststein wie etwa Marmor, Granit, Agglormarmor od.dgl. mittels diamant­ bestückter Gatterblätter oder ähnlicher Werkzeuge in ein­ zelne Platten aufgespalten, wobei diese Platten bislang eine relativ große Mindestdicke aufweisen mußten. Dies liegt darin begründet, daß derartige Platten aus Natur- oder Kunststein ab einer gewissen Mindestdicke - bezogen auf die Größe der Grundfläche der einzelnen Platte - dazu neigen, schon aufgrund ihres Eigengewichtes zu zerbre­ chen. Mit anderen Worten können bislang aus einem Quader aus Natur- oder Kunststein nur Platten geschnitten wer­ den, die aufgrund ihrer Dicke ausreichende Eigensteifig­ keit und Bruchfestigkeit gewährleisten, wobei selbst bei den bislang verwirklichten Mindestdicken äußerste Sorg­ falt bei der Handhabung erforderlich ist.So far, a cuboid made of natural or artificial stone such as marble, granite, agglomerated marble or the like. by means of diamond-tipped gate leaves or similar tools, split into individual plates, these plates previously had to have a relatively large minimum thickness. This is due to the fact that such slabs of natural or artificial stone from a certain minimum thickness - based on the size of the base of the individual slab - tend to break due to their own weight. In other words, until now, from a cuboid made of natural or artificial stone, only plates can be cut who guarantee sufficient inherent rigidity and breaking strength due to their thickness, whereby extreme care is required in handling even with the minimum thicknesses previously achieved.

Bei all diesen Überlegungen ist zu bedenken, daß die Ge­ fahr der Zerbrechlichkeit derartiger Platten schon allei­ ne aufgrund ihres Eigengewichtes mit der Größe der Grund­ fläche derartiger Platten wächst.With all these considerations it should be borne in mind that the Ge Already drive the fragility of such plates ne due to their own weight with the size of the reason surface of such plates grows.

Wird beispielsweise ein Quader mit einer Länge von 2,60 m und einer Höhe von 1,25 m nach bekannten Verfahren in Platten entsprechender Grundfläche aufgespalten, so kön­ nen diese Platten bislang nur in einer Dicke von 20 mm oder darüber hergestellt werden.For example, a cuboid with a length of 2.60 m and a height of 1.25 m by known methods in Split plates of the corresponding base area, so can So far, these plates have only been 20 mm thick or above.

Die Verwendung derartiger Platten beispielsweise als Pa­ neelen zur Wandverkleidung im Innenausbau ist aufgrund der relativ hohen Kosten für Natur- und Kunststein sehr un­ wirtschaftlich, ganz abgesehen davon, daß für derartige Platten stabile Trageinrichtungen geschaffen werden müß­ ten.The use of such plates, for example as Pa neelen to wall cladding in the interior is due the relatively high cost of natural and artificial stone very un economically, not to mention that for such Plates stable support devices must be created ten.

Der vorliegenden Erfindung liegt die Aufgabe zugrunde, ein Verfahren zur Herstellung von dünnen Platten aus einem Quader aus Natur- oder Kunststein, beispielsweise aus Marmor, Granit, Agglomarmor od.dgl. zu entwickeln, nach dem es möglich ist, aus einem entsprechenden Quader Plat­ ten zu fertigen, deren Dicke beträchtlich unter der als bislang nicht als unterschreitbar angesehenen Mindest­ dicke liegt.The present invention is based on the object Process for the production of thin plates from a  Cuboid made of natural or artificial stone, for example made of Marble, granite, agglomerated marble or the like. develop after which is possible from a corresponding cuboid plat to manufacture, the thickness of which is considerably less than that so far not considered to be below the minimum thickness lies.

Die Lösung dieser Aufgabe besteht erfindungsgemäß darin, daß der Quader zunächst in bekannter Weise in relativ dicke, eigensteife Platten aufgespalten wird, danach die einzelnen Platten ein- oder beidseitig mit einer Träger­ schicht versehen, wieder zu einem Quader zusammengefaßt und dann in dünne Platten aufgespalten werden.According to the invention, this object is achieved by that the cuboid is initially known in relative terms thick, rigid plates are split, then the single panels on one or both sides with a support provided layer, again combined into a cuboid and then split into thin plates.

Durch die Aufbringung einer Trägerschicht auf die zunächst hergestellten, insich tragfähigen Platten wird die Mög­ lichkeit eröffnet, diese noch vergleichsweise dicken Plat­ ten neuerlich aufzuspalten, ohne daß die Gefahr besteht, daß die nunmehr hergestellten, relativ dünnen Platten auf­ grund ihres Eigengewichtes zerbrechen. Durch die Träger­ schicht wird den endgültig hergestellten, relativ dünnen Platten derart viel Stabilität gegeben, daß diese Platten praxisgerecht gehandhabt und verarbeitet werden können. Ebensowenig ist eine Bruchgefahr beim Aufspalten der zu­ nächst hergestellten Platten zu rechnen, da durch die beim Aufspalten auf die Platten wirkenden Kräfte durch die Trägerschicht aufgefangen bzw. die dünnen Platten durch die Trägerschicht soweit gestützt werden, daß ein Zerbrechen der dünnen Platten verhindert ist. By applying a backing layer to the initially manufactured, self-supporting plates, the Mög opened, this still relatively thick plat to split again without the risk of that the now manufactured, relatively thin plates break due to their own weight. Through the carrier layer becomes the final manufactured, relatively thin Plates given so much stability that these plates can be handled and processed in a practical manner. Nor is there a risk of breakage when splitting the next plates produced, because of the forces acting on the plates when splitting the carrier layer or the thin plates are supported by the carrier layer so far that a Breakage of the thin plates is prevented.  

Zweckmäßigerweise werden die Platten mit einer Träger­ schicht aus Glasfasern versehen.The plates are expediently provided with a support layer of glass fibers.

Diese Glasfasern werden mittels Kunstharz oder anderen, geeigneten Bindemitteln auf die zunächst noch relativ dicken Platten aufgebracht, so daß sich ein inniger Ver­ bund zwischen der eigentlichen Trägerschicht und dem Mate­ rial aus Natur- oder Kunststein ergibt. Das Kunstharz kann in Poren, Haarrisse od.dgl. eindringen und zu einer zu­ sätzlichen Versteifung der Platten führen.These glass fibers are made using synthetic resin or other suitable binders to the initially still relative thick plates applied, so that an intimate Ver bond between the actual carrier layer and the mate rial from natural or artificial stone. The synthetic resin can in pores, hairline cracks or the like. penetrate and become one too additional stiffening of the plates.

Versuche haben ergeben, daß mit dem erfindungsgemäßen Ver­ fahren Platten herstellbar sind, die bei gleicher Grund­ fläche um mehr als die Hälfte dünner sind als bislang herstellbare Platten.Experiments have shown that with the Ver drive plates that can be produced for the same reason area is more than half thinner than before producible plates.

Damit ergibt sich, daß aus einem Quader vorgegebener Ab­ messungen nunmehr doppelt so viele Platten gefertigt wer­ den können, wie bislang.This means that from a cuboid predetermined Ab measurements are now twice as many plates manufactured can, as before.

Eine nach dem erfindungsgemäßen Verfahren hergestellte Platte aus Natur- oder Kunststein ist dadurch gekennzeich­ net, daß sie zur Erzielung ausreichender Eigensteifigkeit und Bruchfestigkeit mittels einer Trägerschicht verstärkt ist.A manufactured by the method according to the invention This is characterized by a plate made of natural or artificial stone net that they achieve sufficient inherent rigidity and strengthened by a carrier layer is.

Dabei besteht die Trägerschicht vorzugsweise aus Glasfaser­ material und Kunstharz od.dgl. als Bindemittel. The carrier layer preferably consists of glass fiber material and synthetic resin or the like as a binder.  

Weitere Merkmale der Erfindung sind Gegenstand von wei­ teren Unteransprüchen.Further features of the invention are the subject of white other subclaims.

Anhand der beigefügten Zeichnungen wird das erfindungsge­ mäße Verfahren im folgenden ausführlich erläutert und weiterhin werden unter Bezugnahme auf die Zeichnungen nach dem erfindungsgemäßen Verfahren hergestellte Platten beschrieben.Based on the accompanying drawings, the fiction, The following detailed procedures and continue with reference to the drawings plates produced by the method according to the invention described.

Im einzelnen zeigt:In detail shows:

Fig. 1 eine schematische Darstellung eines Qua­ ders aus Natur- oder Kunststein, der mit­ tels eines Gatters in noch relativ dicke Platten aufgespalten wird, Fig. 1 is a schematic representation of a Qua DERS of natural or artificial stone, which is cleaved with means of a gate in relatively thick plates,

Fig. 2 eine im wesentlichen der Fig. 1 entspre­ chende Darstellung bei der erneuten Auf­ spaltung der nach dem Verfahrensschritt gemäß Fig. 1 hergestellten Platten, Fig. 2 is a substantially FIG. 1 entspre sponding representation of the re-cleavage on the plates prepared by the process step shown in FIG. 1,

Fig. 3 die in Fig. 2 mit III bezeichnete Einzel­ heit in stark vergrößerter Darstellung, Fig. 3 in Fig. 2 indicated by III in detail a greatly enlarged representation,

Fig. 4 eine der Fig. 3 entsprechende Darstellung nach einem weiteren Ausführungsbeispiel der Erfindung, Fig. 4 is a FIG. 3 representation corresponding to a further embodiment of the invention,

Fig. 5 eine schematisch und im Schnitt dargestell­ te Aufspaltung einer Platte gemäß Ausfüh­ rungsbeispiel nach Fig. 3, Fig. 5 is a schematically and in section dargestell te splitting a disk according to exporting approximately example of FIG. 3,

Fig. 6 eine der Fig. 5 entsprechende Darstellung der Aufspaltung einer Platte nach dem Aus­ führungsbeispiel gemäß Fig. 4. Fig. 6 is a Fig. 5 illustration corresponding to the resolution of a plate according to the off operation example of FIG. 4.

In Fig. 1 ist mit dem Bezugszeichen 10 ein Quader aus Natur- oder Kunststein, beispielsweise aus Marmor, Granit, Agglomarmor od.dgl. bezeichnet, der in eine Vielzahl von dünnen Platten aufgeteilt werden soll.In Fig. 1, the reference numeral 10 is a cuboid made of natural or artificial stone, for example made of marble, granite, agglomerated marble or the like. referred to, which is to be divided into a plurality of thin plates.

Dieser Quader 10 wird in einem ersten Verfahrensschritt, der symbolisch in Fig. 1 gezeigt ist, in bekannter Weise in relativ dicke, eigensteife Platten 11 aufgespalten, und zwar mittels bekannter Werkzeuge in Form von Gatter­ blättern 12, die letztendlich auch als diamantbestückte Sägeblätter bezeichnet werden könnten.In a first method step, which is symbolically shown in FIG. 1, this cuboid 10 is split in a known manner into relatively thick, inherently rigid plates 11 , specifically by means of known tools in the form of a gate 12 , which are ultimately also referred to as diamond-tipped saw blades could.

Während des eigentlichen Auseinandersägens des Quaders 10 wird im Schneidenbereich der Gatterblätter 12 Wasser zuge­ führt zwecks Kühlung und Schlammabtragung.During the actual sawing apart of the cuboid 10 12 water is supplied in the cutting area of the gate leaves for the purpose of cooling and sludge removal.

Durch das Aufspalten des Quaders 10 im ersten Verfahrens­ schritt in eigensteife Platten 11 werden noch relativ dicke Platten 11 erzeugt, die jeweils für sich gesehen ohne Bruchgefahr aufgrund ihres Eigengewichtes gehand­ habt werden können. By splitting of the box 10 in the first process step is still relatively thick plates 11 are produced, that can each be seen to be without risk of breaking due to its own weight in gehand have inherently rigid plates. 11

In einem nächsten Verfahrensschritt werden die noch rela­ tiv dicken Platten 11 nun mit einer Trägerschicht verse­ hen, so wie dies beispielsweise aus Fig. 3 hervorgeht. Hier sind mit dem Bezugszeichen 13 die erwähnten Träger­ schichten bezeichnet, wobei diese vorteilhafterweise aus Glasfasern bestehen und mittels eines Kunstharzes oder eines anderen geeigneten Bindemittels auf die Platten 11 aufgebracht werden.In a next process step, the still relatively thick plates 11 are now provided with a carrier layer, as can be seen, for example, from FIG. 3. Here, the support layers mentioned are designated by the reference numeral 13 , these advantageously consisting of glass fibers and being applied to the plates 11 by means of a synthetic resin or another suitable binder.

Beim Ausführungsbeispiel nach Fig. 3 dient jede Träger­ schicht 13 gleichzeitig zum Verbinden zweier Platten 11, die gemäß dem ersten Verfahrensschritt nach Fig. 1 aus dem Quader 10 gebildet worden sind. Aus den Platten 11 entsteht somit wiederum ein vollständiger Quader 10 a, so wie dies in Fig. 2 gezeigt ist. Dieser Quader 10 a besteht letztendlich aus den Platten 11, die untereinander wieder verbunden sind durch die Trägerschichten 13. Diese "Ver­ bundplatten" sind in Fig. 2 sowie in Fig. 3 zur Unter­ scheidung von den noch nicht miteinander verbundenen Plat­ ten 11 mit dem Bezugszeichen 11 a versehen. Wie sich nun aus Fig. 3 besonders deutlich ergibt, werden diese Plat­ ten 11 a erneut aufgespalten, und zwar wiederum mittels der Gatterblätter 12. Dadurch entstehen relativ dünne Platten 14, deren Dicke jeweils nur noch die Hälfte der Dicke der Platten 11 - abzüglich der Schnittbreite der Gatterblätter 12 - entspricht, wenn man einmal von der in Fig. 3 übertrieben dargestellten Dicke der Trägerschich­ ten 13 absieht.In the exemplary embodiment according to FIG. 3, each carrier layer 13 serves at the same time for connecting two plates 11 , which were formed from the cuboid 10 according to the first method step according to FIG. 1. A complete cuboid 10 a thus again arises from the plates 11 , as shown in FIG. 2. This cuboid 10 a ultimately consists of the plates 11 , which are connected to one another again by the carrier layers 13 . These "Ver bundplatten" are in Fig. 2 and in Fig. 3 to differentiate from the not yet connected Plat th 11 with the reference numeral 11 a . As can be seen particularly clearly from FIG. 3, these plates 11 a are split again, again by means of the gate leaves 12 . This results in relatively thin plates 14 , the thickness of which is only half the thickness of the plates 11 - minus the cutting width of the gate leaves 12 - if one disregards the thickness of the carrier layers 13 shown in FIG. 3 exaggerated.

Dies bedeutet, daß durch die doppelte Aufspaltung äußerst dünne Platten 14 hergestellt werden können, die durch die Trägerschichten 13 eine derart hohe Eigensteifigkeit und Stabilität aufweisen, daß diese dünnen Platten 14 ohne Bruchgefahr in herkömmlicher Weise verarbeitet werden können.This means that extremely thin plates 14 can be produced by the double splitting, which have such a high inherent rigidity and stability through the carrier layers 13 that these thin plates 14 can be processed in a conventional manner without risk of breakage.

Die Platten 14 gemäß Ausführungsbeispiel nach Fig. 3 könnten als Sandwichplatten bezeichnet werden, bei denen sich zu beiden Seiten der jeweiligen Trägerschicht Natur- oder Kunststein befindet.The plates 14 according to the exemplary embodiment according to FIG. 3 could be referred to as sandwich plates, in which there is natural or artificial stone on both sides of the respective carrier layer.

In Fig. 4 ist dargestellt, daß auch eine andere Vorgehens­ weise möglich ist.In Fig. 4 it is shown that a different approach is possible.

Bei diesem Ausführungsbeispiel sind die Platten 11, wie sie gemäß Verfahrensschritt nach Fig. 1 hergestellt wer­ den, beidseitig mit einer Trägerschicht 13 versehen. Auch diese beidseitig beschichteten Platten werden nunmehr wieder zu einem Quader zusammengestellt und dann erneut aufgespalten durch die Gatterblätter 12, wobei in diesem Falle Platten 14 a von geringer Dicke hergestellt werden, die dann an einer Außenseite mit der Trägerschicht 13 versehen sind.In this embodiment, the plates 11 , as produced in accordance with the method step according to FIG. 1, are provided on both sides with a carrier layer 13 . These plates, which are coated on both sides, are now put together again to form a cuboid and then split again by the gate leaves 12 , in which case plates 14 a of small thickness are produced, which are then provided on the outside with the carrier layer 13 .

Die Trägerschicht 13 ist somit im Gegensatz zum Ausfüh­ rungsbeispiel nach Fig. 3 in jedem Falle sichtbar, was aber in vielen Anwendungsfällen insofern nicht störend ist, als derartige Platten 14 a als Verkleidungselemente mit der Trägerschicht 13 hinten liegend verarbeitet wer­ den. The backing layer 13 is thus in contrast to the exporting approximately example of FIG. 3 in each case visible, but in many applications so far is not disturbing, processed as such plates 14 a and lining elements to the support layer 13 at rear who the.

Die Fig. 5 und 6 zeigen noch einmal die Möglichkeiten der Herstellung von Platten 14 bzw. 14 a nach den Ausführungs­ beispielen der Fig. 3 bzw. 4. FIGS. 5 and 6 again show the possibilities of the production of panels 14 and 14 a to the execution examples of FIGS. 3 and 4 respectively.

Durch das erfindungsgemäße Verfahren werden somit Platten 14 bzw. 14 a hergestellt, die sich durch eine praxisge­ rechte Stabilität auszeichnen, obgleich sie gegenüber be­ kannten Platten um mehr als die Hälfte dünner sind, was im Endergebnis den Vorteil mit sich bringt, daß die erfin­ dungsgemäßen Platten 14 oder 14 a erheblich leichter und auch erheblich kostengünstiger sind als bislang herstell­ bare, doppelt so dicke Platten.By the method according to the invention plates 14 and 14 a are thus produced, which are characterized by a practical right stability, although they are more than half thinner than known plates, which in the end results in the advantage that the inventions according to the invention Plates 14 or 14 a are considerably lighter and also considerably cheaper than previously produced, twice as thick plates.

Es wurde schon eingangs darauf hingewiesen, daß die Anwen­ dung des erfindungsgemäßen Verfahrens zur Herstellung von relativ großen Platten bei einer vergleichsweise geringen Mindestdicke dient. Da bei Materialien wie Natur- oder Kunststein in Form von Marmor, Granit, Agglomarmor od.dgl. aufgrund der diesen Materialien eigenen Imponderabilien konkrete Maßangaben bezüglich des Verhältnisses von Dicke der Platten zur Grundfläche der Platten nicht möglich sind, sei hier noch einmal ausdrücklich betont, daß die Verstärkung der Platten 14 oder 14 a durch die Träger­ schichten 13 dazu dient, Platten 14 bzw. 14 a mit solch geringer Mindestdicke zu fertigen, die ohne die Verwen­ dung von Trägerschichten 13 zu einem Zerbrechen dieser Platten schon alleine aufgrund des Eigengewichtes führen würde.It has already been mentioned at the outset that the application of the method according to the invention is used to produce relatively large plates at a comparatively small minimum thickness. Since materials such as natural or artificial stone in the form of marble, granite, agglomerate marble or the like. due to these materials own imponderables specific dimensions regarding the ratio of the thickness of the plates to the base of the plates are not possible, it should be emphasized again here that the reinforcement of the plates 14 or 14 a by the carrier layers 13 serves to plates 14 and 14 respectively 14 a with such a small minimum thickness to be produced, which would lead to the breakage of these plates alone due to their own weight without the use of carrier layers 13 .

Claims (8)

1. Verfahren zur Herstellung von dünnen Platten aus einem Quader aus Natur- oder Kunststein, beispielsweise aus Marmor, Granit, Agglomarmor od.dgl., dadurch gekennzeichnet, daß der Quader (10) zunächst in bekannter Weise in relativ dicke, eigen­ steife Platten (11) aufgespalten wird, danach die ein­ zelnen Platten (11) ein- oder beidseitig mit einer Trägerschicht (13) versehen, wieder zu einem Quader (10 a) zusammengefaßt und dann in dünne Platten (14, 14 a) aufgespalten werden.1. A process for the production of thin plates of a parallelepiped made of natural or artificial stone, such as marble, granite, or the like Agglomarble., Characterized in that the cuboid (10) first thickness in a known manner relative inherently rigid plates ( 11 ) is split, then the individual plates ( 11 ) provided on one or both sides with a carrier layer ( 13 ), combined again into a cuboid ( 10 a ) and then split into thin plates ( 14 , 14 a ). 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Platten (11) mit einer Trägerschicht (13) aus Glasfasern versehen werden.2. The method according to claim 1, characterized in that the plates ( 11 ) are provided with a carrier layer ( 13 ) made of glass fibers. 3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß die Trägerschicht (13) aus Glasfasern mittels eines Kunstharzes oder eines anderen, geeigneten Bindemit­ tels mit den Platten (11) verbunden wird.3. The method according to claim 2, characterized in that the carrier layer ( 13 ) made of glass fibers by means of a synthetic resin or another suitable binder with the plates ( 11 ) is connected. 4. Verfahren nach einem oder mehreren der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Platten (11) mittels der Trägerschicht (13) vor der erneuten Auf­ spaltung wieder miteinander verbunden werden.4. The method according to one or more of claims 1 to 3, characterized in that the plates ( 11 ) by means of the carrier layer ( 13 ) are joined together again before splitting again. 5. Nach dem Verfahren nach einem oder mehreren der Pa­ tentansprüche 1 bis 4 hergestellte Platte aus Natur- oder Kunststein, beispielsweise aus Marmor, Granit, Agglomarmor od.dgl., dadurch gekennzeichnet, daß diese Platte (14, 14 a) zur Erzielung ausreichender Eigensteifigkeit und Bruchfestigkeit mittels einer Trägerschicht (13) verstärkt ist.5. According to the method according to one or more of Pa tent Claims 1 to 4 plate made of natural or artificial stone, such as marble, granite, agglomerate or the like., Characterized in that this plate ( 14 , 14 a ) to achieve sufficient Intrinsic stiffness and breaking strength is reinforced by means of a carrier layer ( 13 ). 6. Verfahren nach Anspruch 5, dadurch gekennzeichnet, daß die Trägerschicht (13) aus Glasfasermaterial und Kunst­ harz od.dgl. als Bindemittel besteht.6. The method according to claim 5, characterized in that the carrier layer ( 13 ) made of glass fiber material and synthetic resin or the like. exists as a binder. 7. Verfahren nach Anspruch 5 oder 6, dadurch gekennzeich­ net, daß die Trägerschicht (13) in der Mitte der Plat­ te (14) angeordnet ist.7. The method according to claim 5 or 6, characterized in that the carrier layer ( 13 ) in the middle of the plate te ( 14 ) is arranged. 8. Verfahren nach Anspruch 5 oder 6, dadurch gekennzeich­ net, daß die Trägerschicht (13) auf einer Außenseite der Platte (14 a) angeordnet ist.8. The method according to claim 5 or 6, characterized in that the carrier layer ( 13 ) on an outside of the plate ( 14 a ) is arranged.
DE19873743511 1987-12-22 1987-12-22 Process for producing thin panels from a cuboid of natural or cast stone, and panel produced by this process Granted DE3743511A1 (en)