DE3338086C1 - Agent and process for neutral sizing - Google Patents

Agent and process for neutral sizing

Info

Publication number
DE3338086C1
DE3338086C1 DE19833338086 DE3338086A DE3338086C1 DE 3338086 C1 DE3338086 C1 DE 3338086C1 DE 19833338086 DE19833338086 DE 19833338086 DE 3338086 A DE3338086 A DE 3338086A DE 3338086 C1 DE3338086 C1 DE 3338086C1
Authority
DE
Germany
Prior art keywords
sizing
agent
water
organic solvent
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19833338086
Other languages
German (de)
Inventor
Erwin Dipl.-Chem. Dr. 6800 Mannheim Hechler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BK Giulini Chemie GmbH
Original Assignee
Giulini Chemie GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Giulini Chemie GmbH filed Critical Giulini Chemie GmbH
Priority to DE19833338086 priority Critical patent/DE3338086C1/en
Application granted granted Critical
Publication of DE3338086C1 publication Critical patent/DE3338086C1/en
Expired legal-status Critical Current

Abstract

The new agent for neutral sizing of paper, cardboard, paperboard and other cellulose-containing materials consists of a stabilised aqueous alkali metal aluminate solution, a sizing component and an organic solvent of only limited miscibility with water. If desired, the organic solvent is used as a mixture with a water-miscible solvent.

Description

Ein wichtiges und seit langem eingesetztes Zusatzmittel bei der Leitung in der Papierindustrie ist bekanntlich Aluminiumsulfat, das die Ausfällung und Fixierung der Leimungskomponente, z. B. Kolophoniumharz, auf der Cellulosefaser bewirkt. Der sich aufgrund der hydrolytischen Spaltung einstellende pH-Wert liegt hierbei jedoch - in Abhängigkeit von der Aluminiumsulfatkonzentration - zwischen 4,2 und etwa 4,8, also im deutlich sauren Bereich. Das kann zu Korrosionserscheinungen an Sieben und Maschinenteilen führen. Außerdem weist so gefertigtes Papier eine geringe Alterungsbeständigkeit und verminderte mechanische Festigkeit auf. Besonders nachteilig wirkt sich der saure pH-Bereich dann aus, wenn Papiere erzeugt werden sollen, die im Strich oder in der Masse Calciumcarbonat, z. B. durch Altpapiereintrag, enthalten, da die Zersetzung des Calciumcarbonats bereits in der Nähe des Neutralpunktes, wenn auch schwach, beginnt. Sowohl die Kohlensäureentwicklung als auch die in Lösung gehenden Calciumionen können zu erheblichen Störungen in der Papiererzeugung führen und die Papierleimung verschlechtern. An important additive that has been used for a long time in management In the paper industry it is well known that aluminum sulphate is responsible for the precipitation and fixation the sizing component, e.g. B. rosin, causes on the cellulose fiber. Of the However, the pH value established due to the hydrolytic cleavage is here - depending on the aluminum sulphate concentration - between 4.2 and about 4.8, so in the clearly acidic range. This can lead to signs of corrosion on the sieves and Lead machine parts. Also has paper made in this way low aging resistance and reduced mechanical strength. Particularly the acidic pH range has a disadvantageous effect when papers are produced should that in the line or in the mass calcium carbonate, z. B. through waste paper entry, because the decomposition of the calcium carbonate is already near the neutral point, albeit weak, begins. Both the evolution of carbonic acid and that in solution Excess calcium ions can lead to considerable disruptions in paper production and deteriorate the paper sizing.

Es hat aus diesem Grunde nicht an Versuchen gefehlt, die in der Papierleimung bei Verwendung von Aluminiumsulfat als Flockungs- und Fixierungsmittel zu beobachtenden Nachteile und Schwierigkeiten zu beheben. For this reason there has been no lack of attempts in paper sizing observed when using aluminum sulfate as a flocculant and fixative Disadvantages and difficulties to be resolved.

Versuche, durch Anhebung des pH-Bereiches, etwa durch Verminderung der Aluminiumsulfatmenge und Ersatz des »eingesparten« Aluminiumsulfats durch ein kationisches Retentionsmittel, haben jedoch nicht den angestrebten Erfolg gezeigt. Der pH-Wert der Fasersuspension konnte damit lediglich auf Werte von ca. 5;0 angehoben werden, da Mindestmengen an Aluminiumsulfat für eine gute Leimung unabdingbar sind.Try increasing the pH range, for example by decreasing it the amount of aluminum sulphate and replacement of the "saved" aluminum sulphate with one cationic retention agent, however, have not shown the desired success. The pH of the fiber suspension could thus only be increased to values of about 5.0 as minimum quantities of aluminum sulphate are essential for good gluing.

Aus der US-PS 35 40 980 ist weiterhin auch bekannt geworden, daß das Aluminiumsulfat ganz oder teilweise durch wasserlösliches Aluminat ersetzt werden kann. From US-PS 35 40 980 it is also known that the aluminum sulfate can be wholly or partially replaced by water-soluble aluminate can.

Dabei wird die zu leimende wäßrige Fasersuspension zunächst mit so viel Aluminatlösung versetzt, bis sich ein pH-Wert von mindestens 9 eingestellt hat. Anschließend wird der pH-Wert mittels einer anorganischen Säure oder eines sauer reagierenden Salzes, z. B.The aqueous fiber suspension to be sized is initially with so a lot of aluminate solution is added until a pH value of at least 9 is established Has. The pH is then adjusted using an inorganic acid or a acidic reacting salt, e.g. B.

Schwefelsäure oder Aluminiumsulfat, auf einen pH-Wert nicht kleiner als 4,5 gesenkt. Das während der Neutralisation erzeugte Aluminiumhydroxyd bewirkt nach Zugabe des Harzleimes die Ausflockung des Aluminiumresinates und die gebildeten Aluminiumionen fixieren das Resinat auf der Faser. Unter den angegebenen Bedingungen führt der teilweise oder vollständige Ersatz des Aluminiumsulfates durch Natriumaluminat zu der gewünschten Erhöhung des pH-Wertes, ohne daß eine Leimungsverschlechterung beobachtet wird.Sulfuric acid or aluminum sulfate, to a pH not less lower than 4.5. The aluminum hydroxide generated during the neutralization causes after adding the resin glue, the flocculation of the aluminum resinate and the resulting Aluminum ions fix the resinate on the fiber. Under the specified conditions leads to the partial or complete replacement of aluminum sulfate by sodium aluminate to the desired increase in pH without deterioration in sizing is observed.

Aluminiumsulfat ist demnach zur Ausflockung von Harzleim und dessen Fixierung an den Cellulosefasern nicht mehr erforderlich, es kann durch Natriumaluminatzugabe und anschließende pH-Wert-Änderung substituiert werden.Aluminum sulfate is therefore used to flocculate resin glue and its Fixation to the cellulose fibers is no longer necessary, it can be done by adding sodium aluminate and subsequent pH change can be substituted.

Ein Nachteil des vorstehenden Verfahrens wird nun darin gesehen, daß es zweistufig ist und beide Verfahrensstufen in hochverdünnten Stoffsuspensionen ablaufen müssen, Nebenreaktionen und Betriebsstörungen sind bei abgeänderten Verfahrensparametern unvermeidlich. A disadvantage of the above method is now seen in that that it is two-stage and both process stages in highly diluted stock suspensions have to take place, side reactions and malfunctions are with modified process parameters inevitable.

In der nicht vorveröffentlichten DE-PS 3245390 wird weiterhin ein Mittel zur Neutralleimung von Papier, Karton, Pappen und anderen cellulosehaltigen Materialien beschrieben, das aus Wasser, einem mit Wasser unbegrenzt mischbaren Lösungsmittel, einer basisch reagierenden Verbindung, einem Alkalialuminat und einer Leimungskomponente besteht. Das Leimungsmittel ist leicht herstellbar, kann unmittelbar in die zu leimende Fasersuspension eingetragen und durch pH-Wert-Einstellung mit Säuren und/oder sauer reagierenden Salzen in Gegenwart eines kationischen Retentionsmittels aktiviert werden. In DE-PS 3245390, which was not previously published, a Agent for the neutral sizing of paper, cardboard, paperboard and other cellulose-containing materials Materials described that consist of water, one that is infinitely miscible with water Solvent, a basic reacting compound, an alkali aluminate and a There is a sizing component. The sizing agent is easy to manufacture and can be used immediately entered into the fiber suspension to be sized and adjusted with the pH value Acids and / or acidic salts in the presence of a cationic retention aid to be activated.

Aufgabe der vorliegenden Erfindung ist es, ein Mittel und ein Verfahren zur Neutralleimung von Papier, Karton und anderen cellulosehaltigen Materialien zu finden, bei denen die vorstehenden Schwierigkeiten und Nachteile eliminert sind, bzw. bereits erzielte Vorteile verbessert werden. The object of the present invention is to provide a means and a method for neutral sizing of paper, cardboard and other cellulose-containing materials to find in which the above difficulties and disadvantages are eliminated, or advantages already achieved are improved.

Gelöst wird die gestellte Aufgabe mit einem Leimungsmittel, das aus einer stabilisierten wäßrigen Alkali-Aluminatlösung, einem organischen Lösungsmittel und einer Leimungskomponente besteht. Es ist dadurch gekennzeichnet, daß es ein mit Wasser nur begrenzt mischbares Lösungsmittel, 40-85 Gew.-% Leimungskomponente, 10 bis 50 Gew.-% Natriumaluminat und 0,2 bis 5 Gew.-% Stabilisator, bezogen auf das Mittelgewicht, enthält. Gemäß einer besonders vorteilhaften Ausführungsform der Erfindung enthält das Neutralleimungsmittel weiterhin ein organisches Lösungsmittel, das sowohl mit dem in Wasser nur begrenzt löslichen organischen Lösungsmittel als auch mit Wasser mischbar ist. Isopropanol, Äthanol, Methanol und Aceton sind solche Lösungsmittel. The task at hand is solved with a sizing agent that consists of a stabilized aqueous alkali aluminate solution, an organic solvent and a sizing component. It is characterized by having a Solvent only limited miscibility with water, 40-85% by weight sizing component, 10 to 50% by weight of sodium aluminate and 0.2 to 5% by weight of stabilizer, based on the middleweight. According to a particularly advantageous embodiment According to the invention, the neutral sizing agent also contains an organic solvent, that both with the only sparingly soluble in water organic solvent as can also be mixed with water. Isopropanol, ethanol, methanol and acetone are such Solvent.

Als mit Wasser begrenzt mischbare organische Lösungsmittel sind alle Mittel geeignet, die für die Leimungskomponente ausgezeichnete Lösungsmittel sind, insbesondere für Kolophoniumharz und Tallharz. Benzol, Diäthyläther und Schwefelkohlenstoff sind z. B. solche Lösungsmittel. Die Leimungskomponenten können mit Maleinsäure- oder Fumarsäure modifiziert sein. Organic solvents with limited miscibility with water are all Suitable agents that are excellent solvents for the sizing component, especially for rosin resin and tall resin. Benzene, diethyl ether and carbon disulfide are z. B. such solvents. The sizing components can be mixed with maleic acid or modified fumaric acid.

Auch andere Leimungskomponenten sind einsetzbar, etwa ungesättigte Fettsäuren mit 12 bis 24 Kohlenstoffatomen, vorteilhafterweise jedoch solche, die vollständig verseift sind.Other sizing components can also be used, such as unsaturated ones Fatty acids with 12 to 24 carbon atoms, but advantageously those which are completely saponified.

Die Stabilisatoren für die Natriumaluminatlösung können alle bekannten Stabilisatoren sein, z. B. basisch reagierende Verbindungen wie Natriumhydroxid oder organische Polyhydroxiverbindungen wie Hexit, Sorbit und Weinsäure. The stabilizers for the sodium aluminate solution can all be known Be stabilizers, e.g. B. basic compounds such as sodium hydroxide or organic polyhydroxy compounds such as hexitol, sorbitol and tartaric acid.

Die Herstellung des neuen Leimungsmittels kann in einfacher Weise durch Mischung der Komponenten bei Raumtemperatur durchgeführt werden, und zwar derart, daß in eine Wasservorlage zunächst festes Alkalialuminat oder eine wäßrige Alkalialuminatlösung eingetragen wird. Zur Vermeidung von Ausfällungen und gegebenenfalls Verseifung der Leimungskomponente wird dann ein Stabilisator in fester oder gelöster Form eingetragen. Abschließend werden organisches Lösungsmittel und Leimungskomponente unter Rühren eingetragen. Es wird so lange gerührt, bis vollständige Lösung der Leimungskomponente eingetreten ist. Bezogen auf den gesamten Wirkstoffgehalt, beträgt der Stabilisatorgehalt des neuen Leimungsmittel 0,2 bis 5 Gew.-%, der Natriumaluminatgehalt 10 bis 50 Gew.-% und der Gehalt der Leimungskomponente 40 bis 85 Gew.-%. Die Reihenfolge der Komponentenzugabe ist nicht kritisch. The new sizing agent can be produced in a simple manner be carried out by mixing the components at room temperature, namely in such a way that initially solid alkali aluminate or an aqueous one in a water reservoir Alkali aluminate solution is entered. To avoid precipitations and if necessary Saponification of the sizing component then becomes a solid or dissolved stabilizer Form registered. Finally, the organic solvent and sizing component entered with stirring. It is stirred until the complete dissolution of the Sizing component has occurred. Based on the total active ingredient content, is the stabilizer content of the new sizing agent 0.2 to 5% by weight, the sodium aluminate content 10 to 50% by weight and the content of the sizing component 40 to 85% by weight. The chronological order the addition of components is not critical.

Es kann auch so vorgegangen werden, daß die stabilisierte Natriumaluminatlösung in die Leimharzlösung einfließt Das neue Leimungsmittel kann unmittelbar in die zu leimende Faserstoffsuspension eingetragen werden, und zwar derart, daß es in Mengen von 0,1 bis 10 Gew.-%, bezogen auf den Fasergehalt der Suspension und berechnet als Feststoffgehalt, eingetragen, homogen verteilt und auf den Fasern fixiert wird.It is also possible to proceed in such a way that the stabilized sodium aluminate solution flows into the glue resin solution The new glue can be poured directly into the to be sized pulp suspension are entered, in such a way that it is in Quantities from 0.1 to 10% by weight, based on the fiber content of the suspension and calculated as solids content, entered, homogeneously distributed and fixed on the fibers.

Die Fixierung des Leimungsharzes auf den Fasern kann auf verschiedene Weise erfolgen. So kann das Leimungsmittel nach Vermischung im Pulper oder in einer nachgeschalteten Bütte mittels Säuren und/oder sauer reagierenden Salzen in Gegenwart von kationischen Retentionsmitteln aktiviert werden, wobei die Säure-und/oder Salzmenge so bemessen wird, daß ein pH-Wert von etwa 7 erreicht wird. Als Aktivator können alle organischen und anorganischen Säuren eingesetzt werden, die mit den Aluminiumionen weder unlösliche Salze noch Komplexverbindungen bilden. Bei Neutralisation auf einen pH-Wert von 6,8-7,2 werden mit dem neuen Leimungsmittel vorzügliche Ergebnisse erhalten. The fixing of the sizing resin on the fibers can be done in different ways Way to be done. After mixing in the pulper or in a downstream vat by means of acids and / or acidic salts in the presence are activated by cationic retention agents, the amount of acid and / or salt is dimensioned so that a pH of about 7 is reached. As an activator you can all organic and inorganic acids are used will the form neither insoluble salts nor complex compounds with the aluminum ions. at Neutralization to a pH of 6.8-7.2 will be done with the new sizing agent obtained excellent results.

Neben Schwefelsäure und Aluminiumsulfat haben sich auch Ameisensäure und Essigsäure in den durchgeführten Versuchen bestens bewährt. Kationische Retentionsmittel verbessern die Fixierung von Faser- und Füllstoff sowie Leimungsmittel erheblich. Die Menge ist abhängig von der Art des Retentionsmittels. 0,02 bis 0,2 Gew.-%, bezogen auf Stoffansatz, sollten jedoch genügen. In addition to sulfuric acid and aluminum sulfate, formic acid has also been found and acetic acid have proven their worth in the tests carried out. Cationic retention agents improve the fixation of fibers and fillers as well as sizing agents considerably. The amount depends on the type of retention aid. 0.02 to 0.2 wt% based on on substance approach, however, should suffice.

Nach einer anderen Verfahrensvariante kann die Neutralleimung auch derart durchgeführt werden, daß in eine wäßrige Suspension von Cellulosefasern mit einem pH-Wert kleiner 7, insbesondere einem pH-Wert von 6,5 bis 6,9, zunächst ein kationaktives polymeres Retentionsmittel eingetragen und homogen verteilt wird, und daß anschließend soviel Leimungsmittel eingetragen wird, bis ein pH-Wert größer als 7 erreicht ist. In another process variant, neutral sizing can also be used be carried out in such a way that in an aqueous suspension of cellulose fibers with a pH value of less than 7, in particular a pH value of 6.5 to 6.9, initially cation-active polymeric retention agent is introduced and homogeneously distributed, and that then enough sizing agent is added until a pH value is greater than 7 is reached.

Ein pH-Wert von 7,5 bis 8 hat sich gut bewährt. A pH of 7.5 to 8 has proven itself well.

Verwendbare kationaktive Retentionsmittel sind beispielsweise: Polyäthylenimin, kationische Stärke, Polyacrylamid, Polymethacrylamid und quartäre Stickstoffverbindungen. Mengen von 0,1 bis 0,5 Gew.-%, bezogen auf den Fasergehalt der Suspension, reichen zur Erzielung einer guten Masseleimung aus. Cation-active retention agents that can be used are, for example: polyethyleneimine, cationic starch, polyacrylamide, polymethacrylamide and quaternary nitrogen compounds. Quantities from 0.1 to 0.5% by weight, based on the fiber content of the suspension, range to achieve a good cement sizing.

Anhand der beiden nachstehenden Beispiele wird das neue Leimungsmittel noch näher beschrieben. The new sizing agent is based on the two examples below described in more detail.

Beispiel 1 In eine Vorlage, die 690 Gewichtsteile destilliertes Wasser enthält, werden unter Rühren 120 Gewichtsteile mit Weinsäure stabilisierte Natriumaluminatlösung und 25 Gewichtsteile festes Natriumhydroxid eingetragen. Example 1 In a template containing 690 parts by weight of distilled water contains, 120 parts by weight of sodium aluminate solution stabilized with tartaric acid are added with stirring and added 25 parts by weight of solid sodium hydroxide.

Der AkO3-Gehalt beträgt 23,7%. Nach Auflösung des Natriumhydroxids liegt die Temperatur der Lösung bei etwa 35O C. In diese Lösung läßt man 150 Gewichtsteile Benzol einfließen und vermischt anschließend mit 100 Gewichtsteilen gemahlenem Kolophonium sowie 15 Gewichtsteilen mit Maleinsäure umgesetzten Kolophoniumharz. Es wird so lange gerührt, bis sich die beiden Harzkomponenten gelöst haben. Nach dem Abfüllen in Behälter bilden sich 2 Schichten aus. Vor dem Einsatz wird das Leimungsmittel kurz umgerührt und dann sofort eingesetzt Beispiel 2 In ein Rührgefäß, in dem sich 680 Gewichtsteile enthärtetes Wasser befinden, trägt man unter ständigem Rühren 100 Gewichtsteile Natriumaluminatlösung mit einem Al203-Gehalt von 19% ein! Dann werden 50 Gewichtsteile 50%ige Natriumhydroxidlösung zugegeben. The AkO3 content is 23.7%. After dissolving the sodium hydroxide the temperature of the solution is about 350 ° C. 150 parts by weight are allowed into this solution Pour in benzene and then mixed with 100 parts by weight of ground rosin and 15 parts by weight of rosin reacted with maleic acid. It will be like this Stirred for a long time until the two resin components have dissolved. After bottling 2 layers form in the container. Before use, the sizing agent stirred briefly and then used immediately. Example 2 In a stirred vessel in which 680 parts by weight of softened water are located, one carries with constant stirring 100 parts by weight of sodium aluminate solution with an Al203 content of 19%! then 50 parts by weight of 50% sodium hydroxide solution are added.

In die klare Lösung läßt man ein Gemisch, bestehend aus 75 Gewichtsteilen Ethanol und 25 Gewichtsteilen Benzol, einfließen. Nach Verteilung des Gemisches in der Natriumaluminatlösung verrührt man 70 Gewichtsteile mit Maleinsäure umgesetztes Kolophoniumharz und 40 Gewichtsteile einer Ölfettsäure in dem Rührgefäß. Es wird so lange gerührt, bis sich die Festsubstanzen gelöst haben. Der Ansatz wird abgefüllt und kurz vor Anwendung zur Erzielung einer guten Vermischung kräftig gerührt. A mixture consisting of 75 parts by weight is allowed to enter the clear solution Ethanol and 25 parts by weight of benzene are poured in. After distributing the mixture 70 parts by weight of maleic acid are stirred in the sodium aluminate solution Rosin resin and 40 parts by weight of an oleic fatty acid in the stirring vessel. It will Stirred until the solids have dissolved. The approach is bottled and vigorously stirred shortly before use to achieve good mixing.

Claims (26)

Patentansprüche: 1. Mittel, bestehend aus Wasser, organischem Lösungsmittel, einer basisch reagierenden Verbindung, einem Alkalialuminat und einer Leimungskomponente zur Neutralleimung von Papier, Karton, Pappen und anderen cellulosehaltigen Materialien durch Ausfällung der Leimungskomponente mit Natriumaluminat, dadurch ;gekennzeichnet, daßes ein mit Wasser,ri egFënzt mischbares Lösungsmittel, 40 - 85 -Gew,o- Leimungskomponente, 10 bis 50 Gew.-% Natriumaluminat und 0,2 bis 5 Gew.-% Stabilisator, bezogen auf das Mittelgewicht, enthält. Claims: 1. Agent consisting of water, organic solvent, a basic reacting compound, an alkali aluminate and a sizing component for neutral sizing of paper, cardboard, cardboard and other cellulose-containing materials by precipitation of the sizing component with sodium aluminate, characterized; characterized, that it is a solvent which is slightly miscible with water, 40 - 85 weight, o-sizing component, 10 to 50% by weight of sodium aluminate and 0.2 to 5% by weight of stabilizer, based on the middleweight. 2. Mittel nach Anspruch 1, dadurch gekennzeichnet, daß es als Leimungskomponente Kolophoniumharz enthält. 2. Means according to claim 1, characterized in that it is used as a sizing component Contains rosin resin. 3. Mittel nach Anspruch 1, dadurch gekennzeichnet, daß es als Leimungskomponente Tallharz enthält. 3. Means according to claim 1, characterized in that it is used as a sizing component Contains tall resin. 4. Mittel nach dem Anspruch 2 oder 3, dadurch gekennzeichnet, daß es ein mit Maleinsäure oder Fumarsäure modifiziertes Leimungsharz enthält. 4. Means according to claim 2 or 3, characterized in that it contains a sizing resin modified with maleic acid or fumaric acid. 5. Mittel nach Anspruch 1, dadurch gekennzeichnet, daß es als Leimungskomponente eine gesättigte oder ungesättigte Fettsäure mit 12 bis 24 Kohlenstoffatomen enthält. 5. Agent according to claim 1, characterized in that it is used as a sizing component contains a saturated or unsaturated fatty acid having 12 to 24 carbon atoms. 6. Mittel nach Anspruch 5 dadurch gekennzeichnet, daß es als Leimungskomponente mindestens eine vollständig verseifte Fettsäure enthält. 6. Agent according to claim 5, characterized in that it is used as a sizing component Contains at least one completely saponified fatty acid. 7. Mittel nach den Ansprüchen 1 bis 6, dadurch gekennzeichnet, daß es als organisches Lösungsmittel für die Leimungskomponente weiterhin ein organisches Lösungsmittel enthält, das mit Wasser unbegrenzt mischbar ist. 7. Agent according to claims 1 to 6, characterized in that it continues to be an organic solvent as the organic solvent for the sizing component Contains solvents that are infinitely miscible with water. 8. Mittel nach den Ansprüchen 1 bis 7, dadurch gekennzeichnet, daß es als mit Wasser begrenzt mischbares organisches Lösungsmittel einen Kohlenwasserstoff, insbesondere Benzol, enthält. 8. Composition according to claims 1 to 7, characterized in that it is a hydrocarbon as an organic solvent with limited miscibility with water, especially benzene. 9. Mittel nach den Ansprüchen 1 bis 7, dadurch gekennzeichnet, daß es als mit Wasser begrenzt mischbares organisches Lösungsmittel Diäthyläther enthält. 9. Means according to claims 1 to 7, characterized in that it contains diethyl ether as an organic solvent which is limitedly miscible with water. 10. Mittel nach den Ansprüchen 1 bis 7, dadurch gekennzeichnet, daß es als mit Wasser begrenzt mischbares Lösungsmittel Schwefelkohlenstoff enthält. 10. Means according to claims 1 to 7, characterized in that it contains carbon disulfide as a solvent with limited miscibility with water. 11. Mittel nach den Ansprüchen 7 bis 10, dadurch gekennzeichnet, daß es als mit Wasser unbegrenzt mischbares organisches Lösungsmittel einen Alkohol, insbesondere Isopropanol, enthält. 11. Means according to claims 7 to 10, characterized in that that, as an organic solvent that is infinitely miscible with water, it is an alcohol, especially isopropanol. 12. Mittel nach den Ansprüchen 7 bis 10, dadurch gekennzeichnet, daß es als mit Wasser unbegrenzt mischbares Lösungsmittel Aceton enthält. 12. Means according to claims 7 to 10, characterized in that that it contains acetone as a solvent which is infinitely miscible with water. 13. Mittel nach den Ansprüchen 1-12, dadurch gekennzeichnet, daß es als Stabilisator eine basisch reagierende Verbindung, insbesondere Natriumhydroxid, enthält. 13. Means according to claims 1-12, characterized in that it is a basic compound, especially sodium hydroxide, as a stabilizer, contains. 14. Mittel nach den Ansprüchen 1 bis 12, dadurch gekennzeichnet, daß es als Stabilisator eine organische Polyhydroxiverbindung enthält. 14. Agent according to claims 1 to 12, characterized in that that it contains an organic polyhydroxy compound as a stabilizer. 15. Mittel nach Anspruch 14, dadurch gekennzeichnet, daß es als Stabilisator einen Hexit, insbesondere Sorbit, enthält. 15. Composition according to claim 14, characterized in that it is used as a stabilizer contains a hexitol, especially sorbitol. 16. Verfahren zur Neutralleimung von Papier, Karton, Pappe und anderen cellulosehaltigen Materialien, dadurch gekennzeichnet, daß das Leimungsmittel gemäß den vorstehenden Ansprüchen in Mengen von 0,1 bis 10 Gew.-O/o, bezogen auf den Fasergehalt der Suspension und berechnet als Feststoffgehalt, in die Fasersuspension eingetragen, homogen verteilt und auf den Fasern fixiert wird. 16. Process for the neutral sizing of paper, cardboard, paperboard and others cellulose-containing materials, characterized in that the sizing agent according to the preceding claims in amounts of 0.1 to 10% by weight, based on the fiber content of the suspension and calculated as the solids content, entered into the fiber suspension, homogeneously distributed and fixed on the fibers. 17. Verfahren nach Anspruch 16, dadurch gekennzeichnet, daß das Leimungsmittel durch Aktivierung in Gegenwart eines kationischen Retentionsmittel auf den Fasern fixiert wird. 17. The method according to claim 16, characterized in that the sizing agent by activation in the presence of a cationic retention agent on the fibers is fixed. 18. Verfahren nach Anspruch 17, dadurch gekennzeichnet, daß die Aktivierung durch Neutralisation mit anorganischen oder organischen Säuren auf einen pH-Wert von 6,8 bis 7,2 durchgeführt wird. 18. The method according to claim 17, characterized in that the activation by neutralization with inorganic or organic acids to a pH value from 6.8 to 7.2. 19. Verfahren nach Anspruch 17, dadurch gekennzeichnet, daß die Aktivierung durch Neutralisation mit sauer reagierenden Salzen durchgeführt wird. 19. The method according to claim 17, characterized in that the activation is carried out by neutralization with acidic salts. 20. Verfahren nach Anspruch 18, dadurch gekennzeichnet, daß die Aktivierung mit Schwefelsäure oder Ameisensäure durchgeführt wird. 20. The method according to claim 18, characterized in that the activation is carried out with sulfuric acid or formic acid. 21. Verfahren nach Anspruch 19, dadurch gekennzeichnet, daß die Aktivierung mit Aluminiumsulfat durchgeführt wird. 21. The method according to claim 19, characterized in that the activation is carried out with aluminum sulfate. 22. Verfahren nach Anspruch 16, dadurch gekennzeichnet, daß man in eine wäßrige Suspension von Cellulosefasern mit einem pH-Wert kleiner 7, insbesondere einem pH-Wert von 6,5 bis 6,9, zunächst ein kationaktives polymeres Retentionsmittel einträgt und darin homogen verteilt und anschließend soviel Leimungsmittel einträgt, bis ein pH-Wert größer 7 erreicht ist. 22. The method according to claim 16, characterized in that in an aqueous suspension of cellulose fibers with a pH value less than 7, in particular a pH of 6.5 to 6.9, initially a cationic polymeric retention agent enters and homogeneously distributed therein and then enters as much sizing agent as until a pH value greater than 7 is reached. 23. Verfahren nach Anspruch 22, dadurch gekennzeichnet, daß man soviel Leimungsmittel in die wäßrige Suspension einträgt, bis ein pH-Wert von 7,5 bis 8 erreicht ist. 23. The method according to claim 22, characterized in that there is so much Introduces sizing agent into the aqueous suspension until a pH value of 7.5 to 8 is reached. 24. Verfahren nach den Ansprüchen 22 und 23, dadurch gekennzeichnet, daß man als kationaktives Retentionsmittel Polyäthylenimin, kationische Stärke, Polyacrylamid, Polymethacrylamid und/oder eine quartäre Stickstoffverbindung in die wäßrige Suspension einträgt. 24. The method according to claims 22 and 23, characterized in that that the cationic retention agent is polyethyleneimine, cationic starch, Polyacrylamide, polymethacrylamide and / or a quaternary nitrogen compound in the aqueous suspension enters. 25. Verfahren nach den Ansprüchen 22 bis 24, dadurch gekennzeichnet, daß man das aktive Retentionsmittel in Mengen von 0,1 bis 0,5 Gew.-%, bezogen auf den Fasergehalt der wäßrigen Suspension, einträgt. 25. The method according to claims 22 to 24, characterized in that that the active retention aid in amounts of 0.1 to 0.5 wt .-%, based on the fiber content of the aqueous suspension enters. 26. Verfahren nach den Ansprüchen 22 bis 25, dadurch gekennzeichnet, daß man das Leimungsmittel in Mengen von 0,1 bis 10 Gew.-%, bezogen auf den Fasergehalt der Suspension und berechnet als Feststoffgehalt, einträgt. 26. The method according to claims 22 to 25, characterized in that that the sizing agent in amounts of 0.1 to 10 wt .-%, based on the fiber content of the suspension and calculated as the solids content. Gegenstand der vorliegenden Erfindung ist ein Masseleimungsmittel für Papier, Karton, Pappe und andere cellulosehaltige Materialien im neutralen Bereich, sowie ein einstufiges Verfahren zur Masseleimung mit diesem Mittel. The present invention relates to an engine sizing agent for paper, cardboard, cardboard and other cellulose-containing materials in the neutral range, as well as a one-step process for glue sizing with this agent.
DE19833338086 1983-10-20 1983-10-20 Agent and process for neutral sizing Expired DE3338086C1 (en)